Patent Grant
9446959
The present invention relates to a synthetic amorphous silica powder with high purity and a method for producing the same, which silica powder is suitable as a raw material for manufacturing a synthetic silica glass product such as a piping, crucible, or the like to be used in a high temperature and reduced pressure environment in a semiconductor industry and the like.
Conventionally, crucibles, jigs, and the like to be used for single crystal production in semiconductor application have been manufactured from a quartz powder as a raw material obtained by pulverizing and purifying a natural quartz, quartz sand, or the like. However, the natural quartz, quartz sand, or the like contains various metal impurities which are not completely removed therefrom even by the purification treatment, so that the thus obtained raw material has not been fully satisfied in purity. In turn, progression of high integration of semiconductors has led to a more enhanced quality demand for single crystals as materials for the semiconductors, so that crucibles, jigs, and the like to be used for producing the single crystals are also demanded to have high purities, respectively. As such, attention has been directed to a synthetic silica glass product obtained by adopting, as a raw material, a synthetic amorphous silica powder with high purity instead of a natural quartz, quartz sand, or the like.
As a method for producing such a synthetic amorphous silica powder with high purity, there has been disclosed a method where silicon tetrachloride with high purity is hydrolyzed with water, and the generated silica gel is dried, sized, and fired, to obtain a synthetic amorphous silica powder (see Patent Document 1, for example). Further, methods have been disclosed each configured to hydrolyze an alkoxysilane such as silicate in the presence of acid and alkali to thereby gelate, and to dry and pulverize the obtained gel, followed by firing to thereby obtain a synthetic amorphous silica powder (see Patent Documents 2 and 3, for example). The synthetic amorphous silica powders produced by the methods described in the Patent Documents 1 to 3, respectively, are highly pure as compared to a natural quartz, quartz sand, and the like, thereby exemplarily enabling to: decrease entrained levels of impurities in synthetic silica glass products such as crucibles, jigs, and the like manufactured from such synthetic amorphous silica powders as raw materials, respectively; and enhance performances of the products, respectively.
However, those synthetic silica glass products manufactured from the synthetic amorphous silica powders as raw materials produced by the methods described in the Patent Documents 1 to 3, respectively, each have a drawback that the applicable synthetic silica glass product generates gas bubbles or the gas bubbles are expanded when the synthetic silica glass product is used in a high temperature and reduced pressure environment, in a manner to considerably deteriorate the performance of the synthetic silica glass product.
For example, crucibles for pulling up silicon single crystals are each used in an environment at a high temperature of about 1,500° C. and at a reduced pressure of about 7,000 Pa, such that the considerable deterioration of a performance of the crucible due to the aforementioned generation or expansion of gas bubbles has been a problem affecting a quality of a single crystal to be pulled up.
Against the above problem to be brought about upon usage in a high temperature and reduced pressure environment, it is conceivable to conduct such a countermeasure to lower a concentration of those impurities in a synthetic amorphous silica powder which possibly act as gas components: by applying a heat treatment to a synthetic amorphous silica powder obtained by hydrolysis of silicon tetrachloride, to thereby decrease respective concentrations of hydroxyl group and chlorine in the synthetic amorphous silica powder; or, by applying a heat treatment to a synthetic amorphous silica powder obtained from alkoxysilane by a sol-gel method, to thereby decrease respective concentrations of hydroxyl group and carbon in the synthetic amorphous silica powder.
However, even by the above countermeasure, it is impossible to sufficiently restrict generation or expansion of gas bubbles in a synthetic silica glass product to be used in a high temperature and reduced pressure environment.
It is therefore an object of the present invention to provide a synthetic amorphous silica powder and a method for producing the same, which silica powder overcomes the conventional problem and is suitable as a raw material for manufacturing a synthetic silica glass product which is less in amount of generation or degree of expansion of gas bubbles even upon usage of the product in a high temperature and reduced pressure environment.
The first aspect of the present invention is characterized in a synthetic amorphous silica powder obtained by applying a spheroidizing treatment to a granulated silica powder, and by subsequently cleaning and drying it so that the synthetic amorphous silica powder has an average particle diameter D50 of 10 to 2,000 μm; characterized in that the synthetic amorphous silica powder has:
The second aspect of the present invention resides in an invention based on the first aspect, characterized in that the synthetic amorphous silica powder is obtained by applying the spheroidizing treatment to the granulated silica powder after firing it; and
The third aspect of the present invention resides in an invention based on the second aspect, characterized in that the granulated silica powder is a silica powder obtained by: hydrolyzing silicon tetrachloride to produce a siliceous gel; drying the siliceous gel to turn it into a dry powder; pulverizing particles of the dry powder; and then classifying the pulverizedly obtained particles; and
The fourth aspect of the present invention resides in an invention based on the second aspect, characterized in that the granulated silica powder is a silica powder obtained by: hydrolyzing an organic silicon compound to produce a siliceous gel; drying the siliceous gel to turn it into a dry powder; pulverizing particles of the dry powder; and then classifying the pulverizedly obtained particles; and
The fifth aspect of the present invention resides in an invention based on the second aspect, characterized in that the granulated silica powder is a silica powder obtained by: using a fumed silica to produce a siliceous gel; drying the siliceous gel to turn it into a dry powder; pulverizing particles of the dry powder; and then classifying the pulverizedly obtained particles; and
The sixth aspect of the present invention resides in a method for producing a synthetic amorphous silica powder, comprising, in the recited order:
The seventh aspect of the present invention resides in an invention based on the sixth aspect, characterized in that the granulating step is a step for: hydrolyzing silicon tetrachloride to produce a siliceous gel; drying the siliceous gel to turn it into a dry powder; pulverizing particles of the dry powder; and then classifying the pulverizedly obtained particles, to obtain a silica powder having an average particle diameter D50 of 10 to 3,000 μm.
The eighth aspect of the present invention resides in a method for producing a synthetic amorphous silica powder, which is an invention based on the sixth aspect, characterized in that the granulating step is a step for: hydrolyzing an organic silicon compound to produce a siliceous gel; drying the siliceous gel to turn it into a dry powder; pulverizing particles of the dry powder; and then classifying the pulverizedly obtained particles, to obtain a silica powder having an average particle diameter D50 of 10 to 3,000 μm.
The ninth aspect of the present invention resides in a method for producing a synthetic amorphous silica powder, which is an invention based on the sixth aspect, characterized in that wherein the granulating step is a step for: using a fumed silica to produce a siliceous gel; drying the siliceous gel to turn it into a dry powder; pulverizing particles of the dry powder; and then classifying the pulverizedly obtained particles, to obtain a silica powder having an average particle diameter D50 of 10 to 3,000 μm.
The tenth aspect of the present invention resides in a method for producing a synthetic amorphous silica powder, comprising, in the recited order:
The eleventh aspect of the present invention resides in an invention based on the tenth aspect, characterized in that, when the granulating step is a step for: hydrolyzing silicon tetrachloride to produce a siliceous gel; drying the siliceous gel to turn it into a dry powder; pulverizing particles of the dry powder; and then classifying the pulverizedly obtained particles, to obtain a silica powder having an average particle diameter D50 of 10 to 3,000 μm,
The twelfth aspect of the present invention resides in an invention based on the tenth aspect, characterized in that, when the granulating step is a step for: hydrolyzing an organic silicon compound to produce a siliceous gel; drying the siliceous gel to turn it into a dry powder; pulverizing particles of the dry powder; and then classifying the pulverizedly obtained particles, to obtain a silica powder having an average particle diameter D50 of 10 to 3,000 μm,
The thirteenth aspect of the present invention resides in an invention based on the tenth aspect, characterized in that, when the granulating step is a step for: using a fumed silica to produce a siliceous gel; drying the siliceous gel to turn it into a dry powder; pulverizing particles of the dry powder; and then classifying the pulverizedly obtained particles, to obtain a silica powder having an average particle diameter D50 of 10 to 3,000 μm,
The synthetic amorphous silica powder according to the first aspect of the present invention is a synthetic amorphous silica powder obtained by applying a spheroidizing treatment to a granulated silica powder, and by subsequently cleaning and drying it so that the synthetic amorphous silica powder has an average particle diameter D50 of 10 to 2,000 μm;
Thus, by using this synthetic amorphous silica powder to manufacture a synthetic silica glass product, gas components adsorbed onto surfaces of particles of a raw powder are less in amount and gas components inside the powder particles are also less in amount, thereby enabling to reduce an amount of generation or degree of expansion of gas bubbles.
The synthetic amorphous silica powder according to the second aspect of the present invention is obtained by applying the spheroidizing treatment to the granulated silica powder after firing it; wherein the synthetic amorphous silica powder satisfies one or both of the conditions that it has a carbon concentration less than 2 ppm and that it has a chlorine concentration less than 2 ppm. Thus, by using this synthetic amorphous silica powder to manufacture a synthetic silica glass product, gas components adsorbed onto surfaces of particles of a raw powder are less in amount and gas components inside the powder are also less in amount, thereby enabling to reduce an amount of generation or degree of expansion of gas bubbles. Particularly, in case of this synthetic amorphous silica powder, firing is conducted before applying the spheroidizing treatment to the powder, so that gas components to be adsorbed onto surfaces of powder particles and gas components inside the powder are extremely decreased in amount, thereby further enhancing an effect for reducing an amount of generation or degree of expansion of gas bubbles in the synthetic silica glass product.
In case of the synthetic amorphous silica powder according to the third aspect of the present invention, the granulated silica powder is a silica powder obtained by: hydrolyzing silicon tetrachloride to produce a siliceous gel; drying the siliceous gel to turn it into a dry powder; pulverizing particles of the dry powder; and then classifying the pulverizedly obtained particles; whereby it accomplishes that it has a carbon concentration less than 2 ppm.
In case of this synthetic amorphous silica powder, the material obtained by reacting silicon tetrachloride in a liquid is used as the silica powder which is the raw powder, so that the carbon concentration can be reduced, thereby enhancing an effect for reducing an amount of generation or degree of expansion of gas bubbles in a synthetic silica glass product.
In case of the synthetic amorphous silica powder according to the fourth aspect of the present invention, the granulated silica powder is a silica powder obtained by: hydrolyzing an organic silicon compound to produce a siliceous gel; drying the siliceous gel to turn it into a dry powder; pulverizing particles of the dry powder; and then classifying the pulverizedly obtained particles; whereby it accomplishes that it has a chlorine concentration less than 2 ppm.
In case of this synthetic amorphous silica powder, the material obtained from the organic silicon compound such as tetramethoxysilane is used as the silica powder which is the raw powder, so that the chlorine concentration can be reduced, thereby enhancing an effect for reducing an amount of generation or degree of expansion of gas bubbles in a synthetic silica glass product.
In case of the synthetic amorphous silica powder according to the fifth aspect of the present invention, the granulated silica powder is a silica powder obtained by: using a fumed silica to produce a siliceous gel; drying the siliceous gel to turn it into a dry powder; pulverizing particles of the dry powder; and then classifying the pulverizedly obtained particles; thereby achieving that the synthetic amorphous silica powder has a carbon concentration less than 2 ppm and a chlorine concentration less than 2 ppm.
In case of this synthetic amorphous silica powder, the granulated silica powder is further restricted in both of carbon concentration and chlorine concentration by using a fumed silica as a silica powder as a raw powder, as compared to a granulated silica powder which uses, as a raw powder, a silica powder obtained by reacting a chlorine-based silicon compound in a liquid or a silica powder obtained from an organic silicon compound such as tetramethoxysilane; thereby further enhancing an effect for reducing an amount of generation or degree of expansion of gas bubbles in the synthetic silica glass product.
In the method for producing a synthetic amorphous silica powder according to the sixth to ninth aspects of the present invention, the siliceous gel is produced by hydrolyzing silicon tetrachloride, the siliceous gel is produced by hydrolyzing an organic silicon compound such as tetramethoxysilane, or the siliceous gel is produced by using a fumed silica, for example. The method is characterized in that it comprises in the recited order:
The synthetic amorphous silica powder is less in inevitable gas adsorption amount and less in gas components inside the powder particles by virtue of experience of the above steps, thereby enabling to expediently produce a synthetic amorphous silica powder which is preferably usable as a raw material of a synthetic silica glass product.
In the method for producing a synthetic amorphous silica powder according to the tenth to thirteenth aspects of the present invention, the siliceous gel is produced by hydrolyzing silicon tetrachloride, the siliceous gel is produced by hydrolyzing an organic silicon compound such as tetramethoxysilane, or the siliceous gel is produced by using a fumed silica, for example. The method is characterized in that it comprises in the recited order:
The synthetic amorphous silica powder is less in inevitable gas adsorption amount and less in gas components inside the powder particles by virtue of experience of the above steps, thereby enabling to expediently produce a synthetic amorphous silica powder which is preferably usable as a raw material of a synthetic silica glass product. Particularly, this production method is configured to provide the firing step under the predetermined conditions before the spheroidizing step, in a manner to remarkably decrease amounts of gas components to be otherwise adsorbed onto surfaces of powder particles and gas components to be otherwise present within the powder particles, thereby enabling to produce a synthetic amorphous silica powder which is higher in an effect for reducing an amount of generation or degree of expansion of gas bubbles in the synthetic silica glass product.
The modes for carrying out the present invention will be explained hereinafter based on the accompanying drawings.
The synthetic amorphous silica powder according to a first embodiment of the present invention is obtained by applying a spheroidizing treatment to a granulated silica powder, and by subsequently cleaning and drying it. Further, the synthetic amorphous silica powder is characterized in that it has: a quotient of greater than 1.35 and not more than 1.75 obtained by dividing a BET specific surface area of the powder by a theoretical specific surface area calculated from an average particle diameter D50; a real density of 2.10 to 2.20 g/cm3; an intra-particulate porosity of 0 to 0.05; a circularity of 0.50 to 0.75; and an unmolten ratio of greater than 0.25 and not more than 0.60.
Further, the synthetic amorphous silica powder according to the second embodiment of the present invention is a synthetic amorphous silica powder, which is obtained by applying a spheroidizing treatment to a granulated silica powder after firing it. Thus, the synthetic amorphous silica powder satisfies one or both of the conditions that it has a carbon concentration less than 2 ppm and that it has a chlorine concentration less than 2 ppm.
Conceivable as a main source of generation or expansion of gas bubbles in a synthetic silica glass product such as a crucible for pulling up a silicon single crystal at a high temperature and a reduced pressure, is a gas adsorbed onto surfaces of particles of a raw powder, which has been used for manufacturing a product. Namely, upon manufacturing a synthetic silica glass product, gas components adsorbed onto surfaces of particles of the raw powder are desorbed therefrom upon melting of the particles as one step of manufacturing. Further, the thus desorbed gas components are left in the synthetic silica glass product, in a manner to act as a source of generation or expansion of gas bubbles.
It is typical, for a silica powder to be used as a raw material of a synthetic silica glass product, that the powder is passed through a pulverizing step, so that the silica powder contains numerous particles in indeterminate forms (pulverized powder particle forms), respectively, as shown in
As such, the synthetic amorphous silica powder of the present invention is made to have a quotient in the above range obtained by dividing a BET specific surface area of the powder by a theoretical specific surface area calculated from the average particle diameter D50, by applying the spheroidizing treatment to the powder. The BET specific surface area is a value measured by a BET three-point method. Further, it is possible to calculate a theoretical specific surface area of particles from the following equation (1), supposing that the particles are true spheres, respectively, and surfaces thereof are smooth. In the equation (1), D represents a diameter of a particle, and ρ represents a real density.
Theoretical specific surface area=6/(D×ρ) (1)
In the present specification, the theoretical specific surface area of a powder is a value calculated from a theoretical real density, by assuming that D is an average particle diameter D50 of the powder, and p is a real density of 2.20 g/cm3 in the above equation (1). Namely, the theoretical specific surface area of a powder is calculated from the following equation (2).
Theoretical specific surface area of powder=2.73/D50 (2)
Larger quotients obtained by dividing BET specific surface areas by theoretical specific surface areas calculated from average particle diameters D50, lead to larger specific surface areas, thereby increasing inevitable gas adsorption amounts. When the value is 1.35 or less, moldability of the synthetic silica glass product such as quartz crucible lowers. On the other hand, when it exceeds 1.75, the effects for reducing amounts of generation or degrees of expansion of gas bubbles are small. Quotients obtained by dividing BET specific surface areas by theoretical specific surface areas calculated from average particle diameters D50 is preferably in a range of 1.40 to 1.60.
Further, the synthetic amorphous silica powder has a circularity of 0.50 or more and 0.75 or less. The circularity means that powder particles approachingly resemble real spheres as the circularity approaches 1.00, and the circularity is calculated from the following equation (3).
Circularity=4πS/L2 (3)
In the equation (3), S represents an area of a particle in a projection view, and L represents a perimeter of the particle in the projection view. In the present specification, the circularity of the powder is an average value of circularities of 200 powder particles calculated from the equation (3). Circularities of powder less than 0.50 lead to lower effects for reducing amounts of generation or degrees of expansion of gas bubbles. Circularities of powder more than 0.75 lead to lower moldability of the synthetic silica glass product such as quartz crucible. In the above, the circularity of the powder is preferably within a range of 0.60 to 0.70. Also, the unmolten ratio of the synthetic amorphous silica is greater than 0.25 and not more than 0.60. The unmolten ratio of the powder means a rate of the angular powder particles in the above-mentioned 200 powder particles of the particle image in the projection view. The unmolten ratio of not more than 0.25 leads to lower moldability of the synthetic silica glass product such as quartz crucible. On the other hand, the unmolten ratio of greater than 0.60 leads to lower effects for reducing amounts of generation or degrees of expansion of gas bubbles. In the above, the non-dissolution rate of the powder is preferably within a range of 0.30 to 0.40.
Moreover, considering a single particle of the synthetic amorphous silica powder, it is preferable that the particle is free of presence of interior spaces therein such as voids, closed cracks, and the like. Namely, a space(s) present inside the particle of synthetic amorphous silica powder act(s) as a source of generation or expansion of gas bubbles in a synthetic silica glass product. As such, the real density is to be 2.10 g/cm3 or more, and preferably 2.15 to 2.20 g/cm3. The real density means an average value of real densities obtained by conducting a real density measurement three times in conformity to JIS R7212: Testing Methods for Carbon Blocks, (d) Measurement of absolute specific gravity. Further, the intra-particulate porosity is to be 0.05 or less, preferably 0.01 or less. The intra-particulate porosity means an average value calculated from the following equation (4) based on 50 powder particles, by measuring a cross-sectional area of each particle, and an area of a space in the particle, if present, upon observing the cross section of the particle by a SEM (scanning electron microscope):
Intra-particulate porosity=total area of spaces in particles/total cross-sectional area of particles (4)
In turn, the average particle diameter D50 of the synthetic amorphous silica powder is to be 10 to 2,000 μm, and preferably within a range of 50 to 1,000 μm. This is because, average particle diameters smaller than the lower limit value lead to smaller spaces among powder particles such that gases present in the spaces scarcely leave therefrom and thus smaller gas bubbles are likely to be left there, while average particle diameters exceeding the upper limit value lead to excessively larger spaces among powder particles such that larger gas bubbles are likely to be left there. In the above, the average particle diameter D50 is particularly preferably within a range of 80 to 600 μm. In the present specification, the average particle diameter D50 means an average value of medians of particle distributions in volume basis measured three times. The bulk density of the synthetic amorphous silica powder is preferably 1.00 g/cm3 or more. This is because, bulk densities smaller than the lower limit value lead to excessively larger spaces among powder particles such that larger gas bubbles are likely to be left there, while bulk densities exceeding the upper limit value lead to smaller spaces among powder particles such that gases present in the spaces scarcely leave therefrom and thus smaller gas bubbles are likely to be left there. In the above, the bulk density is particularly preferably within a range of 1.20 to 1.50 g/cm3.
To uniformalize meltabilities of powders, it is preferable that each powder has a broad diffraction peak and no crystalline silica powder particles are recognized therein when the powder is measured by a powder X-ray diffractometry using a Cu—Kα ray. This is because, amorphous silica is different from crystalline silica in behavior of melting, in such a tendency that melting of the crystalline silica is belatedly started; so that gas bubbles are likely to be left in a synthetic silica glass product or the like when the synthetic silica glass product is manufactured by using a synthetic amorphous silica powder containing amorphous and crystalline silicas in a mixed manner.
So as to decrease amounts of impurities entrained in a synthetic silica glass product or so as to improve a performance of the product, the synthetic amorphous silica powder is to preferably have such an impurity concentration that concentrations are less than 1 ppm, respectively, for elements belonging to the 1A group except for a hydrogen atom, 2A to 8 groups, 1B to 3B groups, 4B group except for carbon and silicon, 5B group, 6B group except for oxygen, and 7B group except for chlorine. In the above, the impurity concentrations are particularly preferably less than 0.05 ppm, respectively. Further, to restrict generation or expansion of gas bubbles in a synthetic silica glass product at a high temperature and a reduced pressure, it is preferable that a hydroxyl group, chlorine, and carbon, which possibly act as gas components are 60 ppm or less, 5 ppm or less, and 5 ppm or less, respectively, in concentration.
Particularly, in case of the synthetic amorphous silica powder according to the second embodiment of the present invention, firing is conducted before applying the spheroidizing treatment to the powder, so that gas components to be adsorbed onto surfaces of powder particles and gas components inside the particles are extremely decreased in amount, thereby further enhancing an effect for reducing an amount of generation or degree of expansion of gas bubbles in a synthetic silica glass product. Namely, it is possible for the granulated silica powder to satisfy one or both of the conditions that it has a chlorine concentration less than 2 ppm and that it has a carbon concentration less than 2 ppm, by firing the silica powder under a predetermined condition.
When the granulated silica powder, i.e., the raw powder, is a silica powder obtained by: hydrolyzing silicon tetrachloride to produce a siliceous gel; drying the siliceous gel to turn it into a dry powder; pulverizing particles of the dry powder; and then classifying the pulverizedly obtained particles; the synthetic amorphous silica powder is made to have a carbon concentration less than 2 ppm by conducting firing thereof under predetermined conditions before the spheroidizing treatment. This is because, the silica powder is low in carbon concentration as compared to a silica powder obtained by using an organic silicon compound such as tetramethoxysilane, so that the synthetic amorphous silica powder obtained by using the former silica powder as a raw powder is relatively decreased in concentration of residual carbon.
Further, when the granulated silica powder is a silica powder obtained by: hydrolyzing an organic silicon compound to produce a siliceous gel; drying the siliceous gel to turn it into a dry powder; pulverizing particles of the dry powder; and then classifying the pulverizedly obtained particles; the synthetic amorphous silica powder is made to have a chlorine concentration less than 2 ppm by conducting firing thereof under predetermined conditions before the spheroidizing treatment. This is because, the silica powder is low in chlorine concentration as compared to a silica powder obtained by reacting a chlorine-based silicon compound in a liquid, so that the synthetic amorphous silica powder obtained by using the former silica powder as a raw powder is relatively decreased in concentration of residual chlorine.
Moreover, when the granulated silica powder is a silica powder obtained by: using a fumed silica to produce a siliceous gel; drying the siliceous gel to turn it into a dry powder; pulverizing particles of the dry powder; and then classifying the pulverizedly obtained particles; the synthetic amorphous silica powder is made to have a carbon concentration less than 2 ppm and a chlorine concentration less than 2 ppm by conducting firing thereof under predetermined conditions before the spheroidizing treatment. Namely, the synthetic amorphous silica powder obtained by using a silica powder obtained by reacting a raw powder with a chlorine-based silicon compound in a liquid, is likely to become relatively high in concentration of residual chlorine. Further, the synthetic amorphous silica powder obtained by using an organic silicon compound as a raw powder, is likely to become relatively high in concentration of residual carbon. In turn, the fumed silica is low in both of chlorine concentration and carbon concentration as compared to the above-described two types of silica powders, so that the synthetic amorphous silica powder obtained by using the fumed silica as a raw powder is extremely decreased in both of chlorine concentration and carbon concentration. This further enhances also an effect for reducing an amount of generation or degree of expansion of gas bubbles in a synthetic silica glass product.
The synthetic amorphous silica powder of the present invention contains numerous agglomerated multiple particles having been melted and spheroidized as shown in
Next will be explained a method for producing the synthetic amorphous silica powder of the present invention. The method for producing a synthetic amorphous silica powder according to a first embodiment of the present invention is conducted as shown in
The silica powder to be used as a raw material of the synthetic amorphous silica powder of the present invention is obtainable by the following methods, for example. As a first method, ultrapure water in an amount equivalent to 45 to 80 mols is firstly prepared per 1 mol of silicon tetrachloride. The prepared ultrapure water is charged into a vessel, and then the carbon tetrachloride is added thereinto, with stirring while keeping the temperature at 20 to 45° C. in an atmosphere of nitrogen, argon, or the like, thereby hydrolyzing the silicon tetrachloride. After addition of the silicon tetrachloride, stirring is continued for 0.5 to 6 hours, thereby producing a siliceous gel. At this time, it is preferable to set the stirring speed within a range of 100 to 300 rpm. Next, the siliceous gel is transferred into a container for drying which is brought into a drier, and the siliceous gel is dried for 12 to 48 hours at a temperature of 200° C. to 300° C. while flowing nitrogen, argon, or the like through within the drier preferably at a flow rate of 10 to 20 L/min, thereby obtaining a dry powder. This dry powder is then taken out of the drier, and pulverized by a crusher such as a roll crusher. In case of adopting a roll crusher, pulverizing is conducted by appropriately adjusting a roll gap to 0.2 to 2.0 mm and a roll revolution speed to 3 to 200 rpm. Finally, the pulverized particles of the dry powder are classified by using a vibrating screen or the like, thereby obtaining a silica powder having an average particle diameter D50 of 10 to 3,000 μm, preferably 70 to 1,300 μm.
As a second method, 0.5 to 3 mols of ultrapure water and 0.5 to 3 mols of ethanol are prepared per 1 mol of tetramethoxysilane as an organic silicon compound. The prepared ultrapure water and ethanol are charged into a vessel, and then the tetramethoxysilane is added thereinto, with stirring while keeping the temperature at 60° C. in an atmosphere of nitrogen, argon, or the like, thereby hydrolyzing the tetramethoxysilane. After addition of the tetramethoxysilane, stirring is continued for 5 to 120 minutes, and 1 to 50 mols of ultrapure water is further added thereinto per 1 mol of tetramethoxysilane, followed by continued stirring for 1 to 12 hours, thereby producing a siliceous gel. At this time, it is preferable to set the stirring speed within a range of 100 to 300 rpm. Next, the siliceous gel is transferred into a container for drying which is brought into a drier, and the siliceous gel is dried for 6 to 48 hours at a temperature of 200° C. to 300° C. while flowing nitrogen, argon, or the like through within the drier preferably at a flow rate of 10 to 20 L/min, thereby obtaining a dry powder. This dry powder is then taken out of the drier, and pulverized by a crusher such as a roll crusher. In case of adopting a roll crusher, pulverizing is conducted by appropriately adjusting a roll gap to 0.2 to 2.0 mm and a roll revolution speed to 3 to 200 rpm. Finally, the pulverized particles of the dry powder are classified by using a vibrating screen or the like, thereby obtaining a silica powder having an average particle diameter D50 of 10 to 3,000 μm, preferably 70 to 1,300 μm.
As a third method, 3.0 to 35.0 mols of ultrapure water is firstly prepared per 1 mol of fumed silica having an average particle diameter D50 of 0.007 to 0.030 μm and a specific surface area of 50 to 380 m2/g. The prepared ultrapure water is charged into a vessel, and then the fumed silica is added thereinto, with stirring while keeping the temperature at 10 to 30° C. in an atmosphere of nitrogen, argon, or the like. After addition of the fumed silica, stirring is continued for 0.5 to 6 hours, thereby producing a siliceous gel. At this time, it is preferable to set the stirring speed within a range of 10 to 50 rpm. Next, the siliceous gel is transferred into a container for drying which is brought into a drier, and the siliceous gel is dried for 12 to 48 hours at a temperature of 200° C. to 300° C. while flowing nitrogen, argon, or the like through within the drier preferably at a flow rate of 1 to 20 L/min, thereby obtaining a dry powder. This dry powder is then taken out of the drier, and pulverized by a crusher such as a roll crusher. In case of adopting a roll crusher, pulverizing is conducted by appropriately adjusting a roll gap to 0.2 to 2.0 mm and a roll revolution speed to 3 to 200 rpm. Finally, the pulverized particles of the dry powder are classified by using a vibrating screen or the like, thereby obtaining a silica powder having an average particle diameter D50 of 10 to 3,000 μm, preferably 70 to 1,300 μm.
While the thus obtained silica powder by granulation in the above manner is to be subjected to a spheroidizing treatment under conditions to be described later, firing is to be conducted under predetermined conditions as shown in
The spheroidization of the silica powder obtained by any one of the first to third methods, or the spheroidization of the silica powder obtained by firing the above obtained silica powder under the above conditions, is attained by a spheroidizing treatment based on thermal plasma. In the spheroidizing treatment based on thermal plasma, it is possible to use an apparatus shown in
Because silica powder particles after the spheroidizing treatment have surfaces carrying those fine particles attached thereto which have once evaporated into the argon-oxygen plasma, ultrasonic cleaning is conducted such that the spheroidized silica powder particles after the spheroidizing step and ultrapure water are put into a cleaning vessel. Since the fine particles are migrated into the ultrapure water after the ultrasonic cleaning, filtration is conducted by a filter having a coarse mesh. This operation is conducted repetitively until fine particles of the silica powder are fully filtered out.
For drying the silica powder after the cleaning step, the powder is firstly put into a container for drying, and then the container for drying is brought into a drier. Then, drying is preferably conducted by flowing nitrogen, argon, or the like at a flow rate of 1 to 20 L/min through within the drier, and by holding the powder at a temperature of 100° C. to 400° C. for 3 to 48 hours.
Through the above steps, the synthetic amorphous silica powder of the present invention is obtained. This synthetic amorphous silica powder is less in inevitable gas adsorption amount, so that the powder is preferably usable as a raw material of a synthetic silica glass product. Particularly, according to the production method according to the second embodiment of the present invention, the firing step under the predetermined conditions is provided before the spheroidizing treatment step, thereby enabling to remarkably decrease amounts of gas components to be otherwise adsorbed onto surfaces of powder particles and gas components to be otherwise present within the powder particles.
Next, Examples of the present invention will be explained in detail, together with Comparative Examples.
Firstly, ultrapure water was prepared in an amount equivalent to 55.6 mols, per 1 mol of silicon tetrachloride. This ultrapure water was brought into a vessel, and then the silicon tetrachloride was added thereinto, with stirring while keeping the temperature at 25° C. in an atmosphere of nitrogen, thereby hydrolyzing the silicon tetrachloride. After addition of the silicon tetrachloride, stirring was continued for 3 hours, thereby producing a siliceous gel. At this time, the stirring speed was set to be 150 rpm. Next, the siliceous gel was transferred into a container for drying which was brought into a drier, and the siliceous gel was dried for 18 hours at a temperature of 250° C. while flowing nitrogen through within the drier at a flow rate of 15 L/min, thereby obtaining a dry powder. This dry powder was then taken out of the drier, and pulverized by a roll crusher. At this time, pulverizing was conducted by adjusting a roll gap to 0.2 mm and a roll revolution speed to 50 rpm. The pulverized particles of the dry powder were classified by using a vibrating screen having openings of 100 μm and a vibrating screen having openings of 150 μm, thereby obtaining a silica powder having an average particle diameter D50 of 127 μm.
Subsequently, the apparatus 30 shown in
After the spheroidizing treatment, the powder and ultrapure water were put into a cleaning vessel, to conduct ultrasonic cleaning. After conducting the ultrasonic cleaning, filtration was conducted by a filter having openings of 50 μm. This operation was conducted repetitively until fine particles attached onto surfaces of the silica powder particles were fully filtered out.
Finally, the cleaned powder was charged into a container for drying, and drying was conducted by flowing nitrogen at a flow rate of 10 L/min through within the drier, and by holding the powder at a temperature of 200° C. for 48 hours, thereby obtaining a synthetic amorphous silica powder.
Firstly, 1 mol of ultrapure water and 1 mol of ethanol were prepared per 1 mol of tetramethoxysilane. The prepared ultrapure water and ethanol were charged into a vessel, and then the tetramethoxysilane was added thereinto, with stirring while keeping the temperature at 60° C. in an atmosphere of nitrogen, thereby hydrolyzing the tetramethoxysilane. After addition of the tetramethoxysilane, stirring was continued for 60 minutes, and 25 mols of ultrapure water was further added thereinto per 1 mol of tetramethoxysilane, followed by continued stirring for 6 hours, thereby producing a siliceous gel. At this time, the stirring speed was set to be 100 rpm. Next, the siliceous gel was transferred into a container for drying which was brought into a drier, and the siliceous gel was dried for 24 hours at a temperature of 200° C. while flowing nitrogen through within the drier at a flow rate of 20 L/min, thereby obtaining a dry powder. This dry powder was then taken out of the drier, and pulverized by a roll crusher. At this time, pulverizing was conducted by adjusting a roll gap to 0.2 mm and a roll revolution speed to 55 rpm. The pulverized particles of the dry powder were classified by using a vibrating screen having openings of 100 μm and a vibrating screen having openings of 175 μm, thereby obtaining a silica powder having an average particle diameter D50 of 135 μm.
Subsequently, the apparatus 30 shown in
After the spheroidizing treatment, the powder and ultrapure water were put into a cleaning vessel, to conduct ultrasonic cleaning. After conducting the ultrasonic cleaning, filtration was conducted by a filter having openings of 50 μm. This operation was conducted repetitively until fine particles attached onto surfaces of the silica powder particles were fully filtered out.
Finally, the powder after cleaning was charged into a container for drying, and drying was conducted by flowing argon at a flow rate of 10 L/min through within the drier, and by holding the powder at a temperature of 300° C. for 12 hours, thereby obtaining a synthetic amorphous silica powder.
Firstly, 13 mols of ultrapure water was prepared per 1 mol of fumed silica having an average particle diameter D50 of 0.020 μm and a specific surface area of 90 m2/g. The prepared ultrapure water was charged into a vessel, and then the fumed silica was added thereinto, with stirring while keeping the temperature at 25° C. in an atmosphere of nitrogen. After addition of the fumed silica, stirring was continued for 3 hours, thereby producing a siliceous gel. At this time, the stirring speed was set to be 30 rpm. Next, the siliceous gel was transferred into a container for drying which was brought into a drier, and the siliceous gel was dried for 12 hours at a temperature of 300° C. while flowing nitrogen through within the drier at a flow rate of 10 L/min, thereby obtaining a dry powder. This dry powder was then taken out of the drier, and pulverized by a roll crusher. At this time, pulverizing was conducted by adjusting a roll gap to 0.5 mm and a roll revolution speed to 30 rpm. The pulverized particles of the dry powder were classified by using a vibrating screen having openings of 400 μm and a vibrating screen having openings of 550 μm, thereby obtaining a silica powder having an average particle diameter D50 of 484 μm.
Subsequently, the apparatus 30 shown in
After the spheroidizing treatment, the powder and ultrapure water were put into a cleaning vessel, to conduct ultrasonic cleaning. After conducting the ultrasonic cleaning, filtration was conducted by a filter having openings of 200 μm. This operation was conducted repetitively until fine particles attached onto surfaces of the silica powder particles were fully filtered out.
Finally, the powder after cleaning was charged into a container for drying, and drying was conducted by flowing nitrogen at a flow rate of 20 L/min through within the drier, and by holding the powder at a temperature of 200° C. for 36 hours, thereby obtaining a synthetic amorphous silica powder.
Firstly, ultrapure water was prepared in an amount equivalent to 70.5 mols, per 1 mol of silicon tetrachloride. This ultrapure water was brought into a vessel, and then the silicon tetrachloride was added thereinto, with stirring while keeping the temperature at 35° C. in an atmosphere of argon, thereby hydrolyzing the silicon tetrachloride. After addition of the silicon tetrachloride, stirring was continued for 3 hours, thereby producing a siliceous gel. At this time, the stirring speed was set to be 150 rpm. Next, the siliceous gel was transferred into a container for drying which was brought into a drier, and the siliceous gel was dried for 24 hours at a temperature of 300° C. while flowing nitrogen through within the drier at a flow rate of 10 L/min, thereby obtaining a dry powder. This dry powder was then taken out of the drier, and pulverized by a roll crusher. At this time, pulverizing was conducted by adjusting a roll gap to 0.9 mm and a roll revolution speed to 20 rpm. The pulverized particles of the dry powder were classified by using a vibrating screen having openings of 800 μm and a vibrating screen having openings of 1000 μm, thereby obtaining a silica powder having an average particle diameter D50 of 927 μm.
Subsequently, the apparatus 30 shown in
After the spheroidizing treatment, the powder and ultrapure water were put into a cleaning vessel, to conduct ultrasonic cleaning. After conducting the ultrasonic cleaning, filtration was conducted by a filter having openings of 600 μm. This operation was conducted repetitively until fine particles attached onto surfaces of the silica powder particles were fully filtered out.
Finally, the cleaned powder was charged into a container for drying, and drying was conducted by flowing argon at a flow rate of 10 L/min through within the drier, and by holding the powder at a temperature of 300° C. for 24 hours, thereby obtaining a synthetic amorphous silica powder.
Firstly, ultrapure water was prepared in an amount equivalent to 55.6 mols, per 1 mol of silicon tetrachloride. This ultrapure water was brought into a vessel, and then the silicon tetrachloride was added thereinto, with stirring while keeping the temperature at 25° C. in an atmosphere of nitrogen, thereby hydrolyzing the silicon tetrachloride. After addition of the silicon tetrachloride, stirring was continued for 3 hours, thereby producing a siliceous gel. At this time, the stirring speed was set to be 150 rpm. Next, the siliceous gel was transferred into a container for drying which was brought into a drier, and the siliceous gel was dried for 18 hours at a temperature of 250° C. while flowing nitrogen through within the drier at a flow rate of 15 L/min, thereby obtaining a dry powder. This dry powder was then taken out of the drier, and pulverized by a roll crusher. At this time, pulverizing was conducted by adjusting a roll gap to 0.2 mm and a roll revolution speed to 50 rpm. The pulverized particles of the dry powder were classified by using a vibrating screen having openings of 100 μm and a vibrating screen having openings of 175 μm, thereby obtaining a silica powder having an average particle diameter D50 of 136 μm.
Subsequently, the apparatus 30 shown in
After the spheroidizing treatment, the powder and ultrapure water were put into a cleaning vessel, to conduct ultrasonic cleaning. After conducting the ultrasonic cleaning, filtration was conducted by a filter having openings of 50 μm. This operation was conducted repetitively until fine particles attached onto surfaces of the silica powder particles were fully filtered out.
Finally, the cleaned powder was charged into a container for drying, and drying was conducted by flowing nitrogen at a flow rate of 10 L/min through within the drier, and by holding the powder at a temperature of 200° C. for 48 hours, thereby obtaining a synthetic amorphous silica powder.
Firstly, ultrapure water was prepared in an amount equivalent to 55.6 mols, per 1 mol of silicon tetrachloride. This ultrapure water was brought into a vessel, and then the silicon tetrachloride was added thereinto, with stirring while keeping the temperature at 25° C. in an atmosphere of nitrogen, thereby hydrolyzing the silicon tetrachloride. After addition of the silicon tetrachloride, stirring was continued for 3 hours, thereby producing a siliceous gel. At this time, the stirring speed was set to be 150 rpm. Next, the siliceous gel was transferred into a container for drying which was brought into a drier, and the siliceous gel was dried for 18 hours at a temperature of 250° C. while flowing nitrogen through within the drier at a flow rate of 15 L/min, thereby obtaining a dry powder. This dry powder was then taken out of the drier, and pulverized by a roll crusher. At this time, pulverizing was conducted by adjusting a roll gap to 0.2 mm and a roll revolution speed to 50 rpm. The pulverized particles of the dry powder were classified by using a vibrating screen having openings of 50 μm and a vibrating screen having openings of 150 μm, thereby obtaining a silica powder having an average particle diameter D50 of 113 μm.
Subsequently, the apparatus 30 shown in
After the spheroidizing treatment, the powder and ultrapure water were put into a cleaning vessel, to conduct ultrasonic cleaning. After conducting the ultrasonic cleaning, filtration was conducted by a filter having openings of 35 μm. This operation was conducted repetitively until fine particles attached onto surfaces of the silica powder particles were fully filtered out.
Finally, the cleaned powder was charged into a container for drying, and drying was conducted by flowing nitrogen at a flow rate of 10 L/min through within the drier, and by holding the powder at a temperature of 200° C. for 48 hours, thereby obtaining a synthetic amorphous silica powder.
Firstly, 1 mol of ultrapure water and 1 mol of ethanol were prepared per 1 mol of tetramethoxysilane. The prepared ultrapure water and ethanol were charged into a vessel, and then the tetramethoxysilane was added thereinto, with stirring while keeping the temperature at 60° C. in an atmosphere of nitrogen, thereby hydrolyzing the tetramethoxysilane. After addition of the tetramethoxysilane, stirring was continued for 60 minutes, and 25 mols of ultrapure water was further added thereinto per 1 mol of tetramethoxysilane, followed by continued stirring for 6 hours, thereby producing a siliceous gel. At this time, the stirring speed was set to be 100 rpm. Next, the siliceous gel was transferred into a container for drying which was brought into a drier, and the siliceous gel was dried for 24 hours at a temperature of 200° C. while flowing nitrogen through within the drier at a flow rate of 20 L/min, thereby obtaining a dry powder. This dry powder was then taken out of the drier, and pulverized by a roll crusher. At this time, pulverizing was conducted by adjusting a roll gap to 0.2 mm and a roll revolution speed to 55 rpm. The pulverized particles of the dry powder were classified by using a vibrating screen having openings of 75 μm and a vibrating screen having openings of 150 μm, thereby obtaining a silica powder having an average particle diameter D50 of 126 μm.
Subsequently, the apparatus 30 shown in
After the spheroidizing treatment, the powder and ultrapure water were put into a cleaning vessel, to conduct ultrasonic cleaning. After conducting the ultrasonic cleaning, filtration was conducted by a filter having openings of 50 μm. This operation was conducted repetitively until fine particles attached onto surfaces of the silica powder particles were fully filtered out.
Finally, the cleaned powder was charged into a container for drying, and drying was conducted by flowing argon at a flow rate of 10 L/min through within the drier, and by holding the powder at a temperature of 300° C. for 12 hours, thereby obtaining a synthetic amorphous silica powder.
Firstly, 13 mols of ultrapure water was prepared per 1 mol of fumed silica having an average particle diameter D50 of 0.020 μm and a specific surface area of 90 m2/g. The prepared ultrapure water was charged into a vessel, and then the fumed silica was added thereinto, with stirring while keeping the temperature at 25° C. in an atmosphere of nitrogen. After addition of the fumed silica, stirring was continued for 3 hours, thereby producing a siliceous gel. At this time, the stirring speed was set to be 30 rpm. Next, the siliceous gel was transferred into a container for drying which was brought into a drier, and the siliceous gel was dried for 12 hours at a temperature of 300° C. while flowing nitrogen through within the drier at a flow rate of 10 L/min, thereby obtaining a dry powder. This dry powder was then taken out of the drier, and pulverized by a roll crusher. At this time, pulverizing was conducted by adjusting a roll gap to 0.5 mm and a roll revolution speed to 30 rpm. The pulverized particles of the dry powder were classified by using a vibrating screen having openings of 350 μm and a vibrating screen having openings of 550 μm, thereby obtaining a silica powder having an average particle diameter D50 of 440 μm.
Subsequently, the apparatus 30 shown in
After the spheroidizing treatment, the powder and ultrapure water were put into a cleaning vessel, to conduct ultrasonic cleaning. After conducting the ultrasonic cleaning, filtration was conducted by a filter having openings of 250 μm. This operation was conducted repetitively until fine particles attached onto surfaces of the silica powder particles were fully filtered out.
Finally, the cleaned powder was charged into a container for drying, and drying was conducted by flowing nitrogen at a flow rate of 20 L/min through within the drier, and by holding the powder at a temperature of 200° C. for 36 hours, thereby obtaining a synthetic amorphous silica powder.
Firstly, 13 mols of ultrapure water was prepared per 1 mol of fumed silica having an average particle diameter D50 of 0.020 μm and a specific surface area of 90 m2/g. The prepared ultrapure water was charged into a vessel, and then the fumed silica was added thereinto, with stirring while keeping the temperature at 25° C. in an atmosphere of nitrogen. After addition of the fumed silica, stirring was continued for 3 hours, thereby producing a siliceous gel. At this time, the stirring speed was set to be 30 rpm. Next, the siliceous gel was transferred into a container for drying which was brought into a drier, and the siliceous gel was dried for 12 hours at a temperature of 300° C. while flowing nitrogen through within the drier at a flow rate of 10 L/min, thereby obtaining a dry powder. This dry powder was then taken out of the drier, and pulverized by a roll crusher. At this time, pulverizing was conducted by adjusting a roll gap to 0.5 mm and a roll revolution speed to 30 rpm. The pulverized particles of the dry powder were classified by using a vibrating screen having openings of 400 μm and a vibrating screen having openings of 600 μm, thereby obtaining a silica powder having an average particle diameter D50 of 480 μm.
Subsequently, the apparatus 30 shown in
After the spheroidizing treatment, the powder and ultrapure water were put into a cleaning vessel, to conduct ultrasonic cleaning. After conducting the ultrasonic cleaning, filtration was conducted by a filter having openings of 200 μm. This operation was conducted repetitively until fine particles attached onto surfaces of the silica powder particles were fully filtered out.
Finally, the cleaned powder was charged into a container for drying, and drying was conducted by flowing nitrogen at a flow rate of 20 L/min through within the drier, and by holding the powder at a temperature of 200° C. for 36 hours, thereby obtaining a synthetic amorphous silica powder.
Firstly, 13 mols of ultrapure water was prepared per 1 mol of fumed silica having an average particle diameter D50 of 0.020 μm and a specific surface area of 90 m2/g. The prepared ultrapure water was charged into a vessel, and then the fumed silica was added thereinto, with stirring while keeping the temperature at 25° C. in an atmosphere of nitrogen. After addition of the fumed silica, stirring was continued for 3 hours, thereby producing a siliceous gel. At this time, the stirring speed was set to be 30 rpm. Next, the siliceous gel was transferred into a container for drying which was brought into a drier, and the siliceous gel was dried for 24 hours at a temperature of 250° C. while flowing nitrogen through within the drier at a flow rate of 10 L/min, thereby obtaining a dry powder. This dry powder was then taken out of the drier, and pulverized by a roll crusher. At this time, pulverizing was conducted by adjusting a roll gap to 0.5 mm and a roll revolution speed to 40 rpm. The pulverized particles of the dry powder were classified by using a vibrating screen having openings of 400 μm and a vibrating screen having openings of 625 μm, thereby obtaining a silica powder having an average particle diameter D50 of 492 μm.
Subsequently, the apparatus 30 shown in
After the spheroidizing treatment, the powder and ultrapure water were put into a cleaning vessel, to conduct ultrasonic cleaning. After conducting the ultrasonic cleaning, filtration was conducted by a filter having openings of 200 μm. This operation was conducted repetitively until fine particles attached onto surfaces of the silica powder particles were fully filtered out.
Finally, the cleaned powder was charged into a container for drying, and drying was conducted by flowing argon at a flow rate of 20 L/min through within the drier, and by holding the powder at a temperature of 250° C. for 36 hours, thereby obtaining a synthetic amorphous silica powder.
Firstly, ultrapure water was prepared in an amount equivalent to 55.6 mols, per 1 mol of silicon tetrachloride. This ultrapure water was brought into a vessel, and then the silicon tetrachloride was added thereinto, with stirring while keeping the temperature at 25° C. in an atmosphere of nitrogen, thereby hydrolyzing the silicon tetrachloride. After addition of the silicon tetrachloride, stirring was continued for 3 hours, thereby producing a siliceous gel. At this time, the stirring speed was set to be 150 rpm. Next, the siliceous gel was transferred into a container for drying which was brought into a drier, and the siliceous gel was dried for 18 hours at a temperature of 250° C. while flowing nitrogen through within the drier at a flow rate of 15 L/min, thereby obtaining a dry powder. This dry powder was then taken out of the drier, and pulverized by a roll crusher. At this time, pulverizing was conducted by adjusting a roll gap to 1.0 mm and a roll revolution speed to 75 rpm. The pulverized particles of the dry powder were classified by using a vibrating screen having openings of 800 μm and a vibrating screen having openings of 1,200 μm, thereby obtaining a silica powder having an average particle diameter D50 of 937 μm.
Subsequently, the apparatus 30 shown in
After the spheroidizing treatment, the powder and ultrapure water were put into a cleaning vessel, to conduct ultrasonic cleaning. After conducting the ultrasonic cleaning, filtration was conducted by a filter having openings of 700 μm. This operation was conducted repetitively until fine particles attached onto surfaces of the silica powder particles were fully filtered out.
Finally, the cleaned powder was charged into a container for drying, and drying was conducted by flowing argon at a flow rate of 10 L/min through within the drier, and by holding the powder at a temperature of 250° C. for 36 hours, thereby obtaining a synthetic amorphous silica powder.
Firstly, ultrapure water was prepared in an amount equivalent to 55.6 mols, per 1 mol of silicon tetrachloride. This ultrapure water was brought into a vessel, and then the silicon tetrachloride was added thereinto, with stirring while keeping the temperature at 25° C. in an atmosphere of nitrogen, thereby hydrolyzing the silicon tetrachloride. After addition of the silicon tetrachloride, stirring was continued for 3 hours, thereby producing a siliceous gel. At this time, the stirring speed was set to be 150 rpm. Next, the siliceous gel was transferred into a container for drying which was brought into a drier, and the siliceous gel was dried for 48 hours at a temperature of 200° C. while flowing argon through within the drier at a flow rate of 15 L/min, thereby obtaining a dry powder. This dry powder was then taken out of the drier, and pulverized by a roll crusher. At this time, pulverizing was conducted by adjusting a roll gap to 0.8 mm and a roll revolution speed to 50 rpm. The pulverized particles of the dry powder were classified by using a vibrating screen having openings of 704 μm and a vibrating screen having openings of 1,000 μm, thereby obtaining a silica powder having an average particle diameter D50 of 855 μm.
Subsequently, the apparatus 30 shown in
After the spheroidizing treatment, the powder and ultrapure water were put into a cleaning vessel, to conduct ultrasonic cleaning. After conducting the ultrasonic cleaning, filtration was conducted by a filter having openings of 600 μm. This operation was conducted repetitively until fine particles attached onto surfaces of the silica powder particles were fully filtered out.
Finally, the cleaned powder was charged into a container for drying, and drying was conducted by flowing nitrogen at a flow rate of 10 L/min through within the drier, and by holding the powder at a temperature of 200° C. for 48 hours, thereby obtaining a synthetic amorphous silica powder.
Firstly, ultrapure water was prepared in an amount equivalent to 55.6 mols, per 1 mol of silicon tetrachloride. This ultrapure water was brought into a vessel, and then the silicon tetrachloride was added thereinto, with stirring while keeping the temperature at 25° C. in an atmosphere of nitrogen, thereby hydrolyzing the silicon tetrachloride. After addition of the silicon tetrachloride, stirring was continued for 3 hours, thereby producing a siliceous gel. At this time, the stirring speed was set to be 150 rpm. Next, the siliceous gel was transferred into a container for drying which was brought into a drier, and the siliceous gel was dried for 18 hours at a temperature of 250° C. while flowing nitrogen through within the drier at a flow rate of 15 L/min, thereby obtaining a dry powder. This dry powder was then taken out of the drier, and pulverized by a roll crusher. At this time, pulverizing was conducted by adjusting a roll gap to 0.2 mm and a roll revolution speed to 50 rpm. The pulverized particles of the dry powder were classified by using a vibrating screen having openings of 50 μm and a vibrating screen having openings of 150 μm, thereby obtaining a silica powder having an average particle diameter D50 of 100 μm.
Finally, the crushed powder was charged into a container for firing, and the container for firing was brought into a firing furnace, and firing was conducted by flowing nitrogen at a flow rate of 10 L/min through within the firing furnace, and by holding the powder at a temperature of 1,200° C. for 48 hours, thereby obtaining a synthetic amorphous silica powder. This silica powder not conducting the spheroidizing treatment is made Comparative Example 9.
Firstly, 1 mol of ultrapure water and 1 mol of ethanol were prepared per 1 mol of tetramethoxysilane. The prepared ultrapure water and ethanol were charged into a vessel, and then the tetramethoxysilane was added thereinto, with stirring while keeping the temperature at 60° C. in an atmosphere of nitrogen, thereby hydrolyzing the tetramethoxysilane. After addition of the tetramethoxysilane, stirring was continued for 60 minutes, and 25 mols of ultrapure water was further added thereinto per 1 mol of tetramethoxysilane, followed by continued stirring for 6 hours, thereby producing a siliceous gel. At this time, the stirring speed was set to be 100 rpm. Next, the siliceous gel was transferred into a container for drying which was brought into a drier, and the siliceous gel was dried for 24 hours at a temperature of 200° C. while flowing nitrogen through within the drier at a flow rate of 20 L/min, thereby obtaining a dry powder. This dry powder was then taken out of the drier, and pulverized by a roll crusher. At this time, pulverizing was conducted by adjusting a roll gap to 0.6 mm and a roll revolution speed to 100 rpm. The pulverized particles of the dry powder were classified by using a vibrating screen having openings of 550 μm and a vibrating screen having openings of 650 μm, thereby obtaining a silica powder having an average particle diameter D50 of 590 μm.
Finally, the pulverized powder was charged into a container for firing, and the container for firing was brought into a firing furnace, and firing was conducted by flowing argon at a flow rate of 10 L/min through within the firing furnace, and by holding the powder at a temperature of 1,200° C. for 48 hours, thereby obtaining a synthetic amorphous silica powder. This silica powder not conducting the spheroidizing treatment is made Comparative Example 10.
Firstly, 13 mols of ultrapure water was prepared per 1 mol of fumed silica having an average particle diameter D50 of 0.020 μm and a specific surface area of 90 m2/g. The prepared ultrapure water was charged into a vessel, and then the fumed silica was added thereinto, with stirring while keeping the temperature at 25° C. in an atmosphere of nitrogen. After addition of the fumed silica, stirring was continued for 3 hours, thereby producing a siliceous gel. At this time, the stirring speed was set to be 30 rpm. Next, the siliceous gel was transferred into a container for drying which was brought into a drier, and the siliceous gel was dried for 12 hours at a temperature of 300° C. while flowing nitrogen through within the drier at a flow rate of 10 L/min, thereby obtaining a dry powder. This dry powder was then taken out of the drier, and pulverized by a roll crusher. At this time, pulverizing was conducted by adjusting a roll gap to 0.9 mm and a roll revolution speed to 150 rpm. The pulverized particles of the dry powder were classified by using a vibrating screen having openings of 854 μm and a vibrating screen having openings of 950 μm, thereby obtaining a silica powder having an average particle diameter D50 of 895 μm.
Finally, the pulverized powder was charged into a container for firing, and the container for firing was brought into a firing furnace, and firing was conducted by flowing argon at a flow rate of 10 L/min through within the firing furnace, and by holding the powder at a temperature of 1,200° C. for 48 hours, thereby obtaining a synthetic amorphous silica powder. This silica powder not conducting the spheroidizing treatment is made Comparative Example 11.
Firstly, 13 mols of ultrapure water was prepared per 1 mol of fumed silica having an average particle diameter D50 of 0.020 μm and a specific surface area of 90 m2/g. The prepared ultrapure water was charged into a vessel, and then the fumed silica was added thereinto, with stirring while keeping the temperature at 25° C. in an atmosphere of nitrogen. After addition of the fumed silica, stirring was continued for 3 hours, thereby producing a siliceous gel. At this time, the stirring speed was set to be 30 rpm. Next, the siliceous gel was transferred into a container for drying which was brought into a drier, and the siliceous gel was dried for 12 hours at a temperature of 300° C. while flowing nitrogen through within the drier at a flow rate of 10 L/min, thereby obtaining a dry powder. This dry powder was then taken out of the drier, and pulverized by a roll crusher. At this time, pulverizing was conducted by adjusting a roll gap to 0.2 mm and a roll revolution speed to 50 rpm. The pulverized particles of the dry powder were classified by using a vibrating screen having openings of 100 μm and a vibrating screen having openings of 175 μm, thereby obtaining a silica powder having an average particle diameter D50 of 132 μm.
The granulated powder was put into a quartz vessel and subjected to firing in the atmospheric air at 1,300° C. for 72 hours, thereby obtaining a silica powder having an average particle diameter D50 of 91 μm.
Subsequently, the apparatus 30 shown in
After the spheroidizing treatment, the powder and ultrapure water were put into a cleaning vessel, to conduct ultrasonic cleaning. After conducting the ultrasonic cleaning, filtration was conducted by a filter having openings of 50 μm. This operation was conducted repetitively until fine particles attached onto surfaces of the silica powder particles were fully filtered out.
Finally, the powder after cleaning was charged into a container for drying, then the container for drying was brought into a drier, and drying was conducted by flowing nitrogen at a flow rate of 20 L/min through within the drier, and by holding the powder at a temperature of 100° C. for 48 hours, thereby obtaining a synthetic amorphous silica powder.
Firstly, 25 mols of ultrapure water was prepared per 1 mol of fumed silica having an average particle diameter D50 of 0.007 μm and a specific surface area of 300 m2/g. The prepared ultrapure water was charged into a vessel, and then the fumed silica was added thereinto, with stirring while keeping the temperature at 25° C. in an atmosphere of nitrogen. After addition of the fumed silica, stirring was continued for 3 hours, thereby producing a siliceous gel. At this time, the stirring speed was set to be 50 rpm. Next, the siliceous gel was transferred into a container for drying which was brought into a drier, and the siliceous gel was dried for 12 hours at a temperature of 300° C. while flowing argon through within the drier at a flow rate of 20 L/min, thereby obtaining a dry powder. This dry powder was then taken out of the drier, and pulverized by a roll crusher. At this time, pulverizing was conducted by adjusting a roll gap to 0.2 mm and a roll revolution speed to 50 rpm. The pulverized particles of the dry powder were classified by using a vibrating screen having openings of 100 μm and a vibrating screen having openings of 175 μm, thereby obtaining a silica powder having an average particle diameter D50 of 136 μm.
The granulated powder was put into a quartz vessel and subjected to firing in the atmospheric air at 1,200° C. for 72 hours, thereby obtaining a silica powder having an average particle diameter D50 of 95 μm.
Subsequently, the apparatus 30 shown in
After the spheroidizing treatment, the powder and ultrapure water were put into a cleaning vessel, to conduct ultrasonic cleaning. After conducting the ultrasonic cleaning, filtration was conducted by a filter having openings of 50 μm. This operation was conducted repetitively until fine particles attached onto surfaces of the silica powder particles were fully filtered out.
Finally, the powder after cleaning was charged into a container for drying, then the container for drying was brought into a drier, and drying was conducted by flowing argon at a flow rate of 20 L/min through within the drier, and by holding the powder at a temperature of 200° C. for 36 hours, thereby obtaining a synthetic amorphous silica powder.
Firstly, 7 mols of ultrapure water was prepared per 1 mol of fumed silica having an average particle diameter D50 of 0.012 μm and a specific surface area of 200 m2/g. The prepared ultrapure water was charged into a vessel, and then the fumed silica was added thereinto, with stirring while keeping the temperature at 30° C. in an atmosphere of nitrogen. After addition of the fumed silica, stirring was continued for 6 hours, thereby producing a siliceous gel. At this time, the stirring speed was set to be 50 rpm. Next, the siliceous gel was transferred into a container for drying which was brought into a drier, and the siliceous gel was dried for 48 hours at a temperature of 250° C. while flowing nitrogen through within the drier at a flow rate of 20 L/min, thereby obtaining a dry powder. This dry powder was then taken out of the drier, and pulverized by a roll crusher. At this time, pulverizing was conducted by adjusting a roll gap to 0.5 mm and a roll revolution speed to 30 rpm. The pulverized particles of the dry powder were classified by using a vibrating screen having openings of 375 μm and a vibrating screen having openings of 5754 μm, thereby obtaining a silica powder having an average particle diameter D50 of 461 μm.
The granulated powder was put into a quartz vessel and subjected to firing in the atmospheric air at 1,100° C. for 72 hours, thereby obtaining a silica powder having an average particle diameter D50 of 322 μm.
Subsequently, the apparatus 30 shown in
After the spheroidizing treatment, the powder and ultrapure water were put into a cleaning vessel, to conduct ultrasonic cleaning. After conducting the ultrasonic cleaning, filtration was conducted by a filter having openings of 100 μm. This operation was conducted repetitively until fine particles attached onto surfaces of the silica powder particles were fully filtered out.
Finally, the powder after cleaning was charged into a container for drying, then the container for drying was brought into a drier, and drying was conducted by flowing nitrogen at a flow rate of 20 L/min through within the drier, and by holding the powder at a temperature of 120° C. for 48 hours, thereby obtaining a synthetic amorphous silica powder.
Firstly, 8 mols of ultrapure water was prepared per 1 mol of fumed silica having an average particle diameter D50 of 0.030 μm and a specific surface area of 50 m2/g. The prepared ultrapure water was charged into a vessel, and then the fumed silica was added thereinto, with stirring while keeping the temperature at 30° C. in an atmosphere of nitrogen. After addition of the fumed silica, stirring was continued for 6 hours, thereby producing a siliceous gel. At this time, the stirring speed was set to be 40 rpm. Next, the siliceous gel was transferred into a container for drying which was brought into a drier, and the siliceous gel was dried for 48 hours at a temperature of 250° C. while flowing nitrogen through within the drier at a flow rate of 10 L/min, thereby obtaining a dry powder. This dry powder was then taken out of the drier, and pulverized by a roll crusher. At this time, pulverizing was conducted by adjusting a roll gap to 0.9 mm and a roll revolution speed to 30 rpm. The pulverized particles of the dry powder were classified by using a vibrating screen having openings of 800 μm and a vibrating screen having openings of 1,000 μm, thereby obtaining a silica powder having an average particle diameter D50 of 895 μm.
The granulated powder was put into a quartz vessel and subjected to firing in the atmospheric air at 1,400° C. for 72 hours, thereby obtaining a silica powder having an average particle diameter D50 of 625 μm.
Subsequently, the apparatus 30 shown in
After the spheroidizing treatment, the powder and ultrapure water were put into a cleaning vessel, to conduct ultrasonic cleaning. After conducting the ultrasonic cleaning, filtration was conducted by a filter having openings of 200 μm. This operation was conducted repetitively until fine particles attached onto surfaces of the silica powder particles were fully filtered out.
Finally, the powder after cleaning was charged into a container for drying, then the container for drying was brought into a drier, and drying was conducted by flowing nitrogen at a flow rate of 20 L/min through within the drier, and by holding the powder at a temperature of 400° C. for 48 hours, thereby obtaining a synthetic amorphous silica powder.
Firstly, ultrapure water was prepared in an amount equivalent to 60 mols, per 1 mol of silicon tetrachloride. This ultrapure water was brought into a vessel, and then the silicon tetrachloride was added thereinto, with stirring while keeping the temperature at 25° C. in an atmosphere of nitrogen, thereby hydrolyzing the silicon tetrachloride. After addition of the silicon tetrachloride, stirring was continued for 4 hours, thereby producing a siliceous gel. At this time, the stirring speed was set to be 250 rpm. Next, the siliceous gel was transferred into a container for drying which was brought into a drier, and the siliceous gel was dried for 24 hours at a temperature of 250° C. while flowing nitrogen through within the drier at a flow rate of 10 L/min, thereby obtaining a dry powder. This dry powder was then taken out of the drier, and pulverized by a roll crusher. At this time, pulverizing was conducted by adjusting a roll gap to 0.2 mm and a roll revolution speed to 150 rpm. The pulverized particles of the dry powder were classified by using a vibrating screen having openings of 200 μm and a vibrating screen having openings of 100 μm, thereby obtaining a silica powder having an average particle diameter D50 of 143 μm.
The granulated powder was put into a quartz vessel and subjected to firing in the atmospheric air at 1,250° C. for 48 hours, thereby obtaining a silica powder having an average particle diameter D50 of 98 μm.
Subsequently, the apparatus 30 shown in
After the spheroidizing treatment, the powder and ultrapure water were put into a cleaning vessel, to conduct ultrasonic cleaning. After conducting the ultrasonic cleaning, filtration was conducted by a filter having openings of 50 μm. This operation was conducted repetitively until fine particles attached onto surfaces of the silica powder particles were fully filtered out.
Finally, the powder after cleaning was charged into a container for drying, which was then brought into a drier, and drying was conducted by flowing argon at a flow rate of 15 L/min through within the drier, and by holding the powder at a temperature of 400° C. for 36 hours, thereby obtaining a synthetic amorphous silica powder.
Firstly, 0.5 mol of ultrapure water and 0.5 mol of ethanol were prepared per 1 mol of tetramethoxysilane. The prepared ultrapure water and ethanol were charged into a vessel, and then the tetramethoxysilane was added thereinto, with stirring while keeping the temperature at 60° C. in an atmosphere of nitrogen, thereby hydrolyzing the tetramethoxysilane. After addition of the tetramethoxysilane, stirring was continued for 120 minutes, and 20 mols of ultrapure water was further added thereinto per 1 mol of tetramethoxysilane, followed by continued stirring for 6 hours, thereby producing a siliceous gel. At this time, the stirring speed was set to be 150 rpm. Next, the siliceous gel was transferred into a container for drying which was brought into a drier, and the siliceous gel was dried for 24 hours at a temperature of 250° C. while flowing nitrogen through within the drier at a flow rate of 10 L/min, thereby obtaining a dry powder. This dry powder was then taken out of the drier, and pulverized by a roll crusher. At this time, pulverizing was conducted by adjusting a roll gap to 0.2 mm and a roll revolution speed to 60 rpm. The pulverized particles of the dry powder were classified by using a vibrating screen having openings of 75 μm and a vibrating screen having openings of 250 μm, thereby obtaining a silica powder having an average particle diameter D50 of 132 μm.
The granulated powder was put into a quartz vessel and subjected to firing in the atmospheric air at 1,350° C. for 48 hours, thereby obtaining a silica powder having an average particle diameter D50 of 91 μm.
Subsequently, the apparatus 30 shown in
After the spheroidizing treatment, the powder and ultrapure water were put into a cleaning vessel, to conduct ultrasonic cleaning. After conducting the ultrasonic cleaning, filtration was conducted by a filter having openings of 50 μm. This operation was conducted repetitively until fine particles attached onto surfaces of the silica powder particles were fully filtered out.
Finally, the powder after cleaning was charged into a container for drying, and drying was conducted by flowing nitrogen at a flow rate of 5 L/min through within the drier, and by holding the powder at a temperature of 400° C. for 6 hours, thereby obtaining a synthetic amorphous silica powder.
Firstly, 13 mols of ultrapure water was prepared per 1 mol of fumed silica having an average particle diameter D50 of 0.020 μm and a specific surface area of 90 m2/g. The prepared ultrapure water was charged into a vessel, and then the fumed silica was added thereinto, with stirring while keeping the temperature at 30° C. in an atmosphere of nitrogen. After addition of the fumed silica, stirring was continued for 3 hours, thereby producing a siliceous gel. At this time, the stirring speed was set to be 30 rpm. Next, the siliceous gel was transferred into a container for drying which was brought into a drier, and the siliceous gel was dried for 12 hours at a temperature of 300° C. while flowing nitrogen through within the drier at a flow rate of 10 L/min, thereby obtaining a dry powder. This dry powder was then taken out of the drier, and pulverized by a roll crusher. At this time, pulverizing was conducted by adjusting a roll gap to 0.2 mm and a roll revolution speed to 80 rpm. The pulverized particles of the dry powder were classified by using a vibrating screen having openings of 75 μm and a vibrating screen having openings of 175 μm, thereby obtaining a silica powder having an average particle diameter D50 of 132 μm.
The granulated powder was put into a quartz vessel and subjected to firing in the atmospheric air at 1,280° C. for 72 hours, thereby obtaining a silica powder having an average particle diameter D50 of 92 μm.
Subsequently, the apparatus 30 shown in
After the spheroidizing treatment, the powder and ultrapure water were put into a cleaning vessel, to conduct ultrasonic cleaning. After conducting the ultrasonic cleaning, filtration was conducted by a filter having openings of 50 μm. This operation was conducted repetitively until fine particles attached onto surfaces of the silica powder particles were fully filtered out.
Finally, the powder after cleaning was charged into a container for drying, then the container for drying was brought into a drier, and drying was conducted by flowing argon at a flow rate of 10 L/min through within the drier, and by holding the powder at a temperature of 200° C. for 24 hours, thereby obtaining a synthetic amorphous silica powder.
Firstly, 25 mols of ultrapure water was prepared per 1 mol of fumed silica having an average particle diameter D50 of 0.007 μm and a specific surface area of 300 m2/g. The prepared ultrapure water was charged into a vessel, and then the fumed silica was added thereinto, with stirring while keeping the temperature at 25° C. in an atmosphere of nitrogen. After addition of the fumed silica, stirring was continued for 3 hours, thereby producing a siliceous gel. At this time, the stirring speed was set to be 50 rpm. Next, the siliceous gel was transferred into a container for drying which was brought into a drier, and the siliceous gel was dried for 12 hours at a temperature of 300° C. while flowing argon through within the drier at a flow rate of 20 L/min, thereby obtaining a dry powder. This dry powder was then taken out of the drier, and pulverized by a roll crusher. At this time, pulverizing was conducted by adjusting a roll gap to 0.2 mm and a roll revolution speed to 40 rpm. The pulverized particles of the dry powder were classified by using a vibrating screen having openings of 75 μm and a vibrating screen having openings of 175 μm, thereby obtaining a silica powder having an average particle diameter D50 of 139 μm.
The granulated powder was put into a quartz vessel and subjected to firing in the atmospheric air at 1,200° C. for 72 hours, thereby obtaining a silica powder having an average particle diameter D50 of 97 μm.
Subsequently, the apparatus 30 shown in
After the spheroidizing treatment, the powder and ultrapure water were put into a cleaning vessel, to conduct ultrasonic cleaning. After conducting the ultrasonic cleaning, filtration was conducted by a filter having openings of 50 μm. This operation was conducted repetitively until fine particles attached onto surfaces of the silica powder particles were fully filtered out.
Finally, the powder after cleaning was charged into a container for drying, then the container for drying was brought into a drier, and drying was conducted by flowing nitrogen at a flow rate of 10 L/min through within the drier, and by holding the powder at a temperature of 200° C. for 48 hours, thereby obtaining a synthetic amorphous silica powder.
Firstly, 25 mols of ultrapure water was prepared per 1 mol of fumed silica having an average particle diameter D50 of 0.007 μm and a specific surface area of 300 m2/g. The prepared ultrapure water was charged into a vessel, and then the fumed silica was added thereinto, with stirring while keeping the temperature at 25° C. in an atmosphere of argon. After addition of the fumed silica, stirring was continued for 3 hours, thereby producing a siliceous gel. At this time, the stirring speed was set to be 50 rpm. Next, the siliceous gel was transferred into a container for drying which was brought into a drier, and the siliceous gel was dried for 12 hours at a temperature of 300° C. while flowing argon through within the drier at a flow rate of 20 L/min, thereby obtaining a dry powder. This dry powder was then taken out of the drier, and pulverized by a roll crusher. At this time, pulverizing was conducted by adjusting a roll gap to 0.2 mm and a roll revolution speed to 50 rpm. The pulverized particles of the dry powder were classified by using a vibrating screen having openings of 100 μm and a vibrating screen having openings of 200 μm, thereby obtaining a silica powder having an average particle diameter D50 of 146 μm.
The granulated powder was put into a quartz vessel and subjected to firing in the atmospheric air at 1,300° C. for 24 hours, thereby obtaining a silica powder having an average particle diameter D50 of 102 μm.
Subsequently, the apparatus 30 shown in
After the spheroidizing treatment, the powder and ultrapure water were put into a cleaning vessel, to conduct ultrasonic cleaning. After conducting the ultrasonic cleaning, filtration was conducted by a filter having openings of 50 μm. This operation was conducted repetitively until fine particles attached onto surfaces of the silica powder particles were fully filtered out.
Finally, the powder after cleaning was charged into a container for drying, then the container for drying was brought into a drier, and drying was conducted by flowing nitrogen at a flow rate of 5 L/min through within the drier, and by holding the powder at a temperature of 350° C. for 12 hours, thereby obtaining a synthetic amorphous silica powder.
Firstly, 25 mols of ultrapure water was prepared per 1 mol of fumed silica having an average particle diameter D50 of 0.007 μm and a specific surface area of 300 m2/g. The prepared ultrapure water was charged into a vessel, and then the fumed silica was added thereinto, with stirring while keeping the temperature at 25° C. in an atmosphere of nitrogen. After addition of the fumed silica, stirring was continued for 3 hours, thereby producing a siliceous gel. At this time, the stirring speed was set to be 50 rpm. Next, the siliceous gel was transferred into a container for drying which was brought into a drier, and the siliceous gel was dried for 12 hours at a temperature of 300° C. while flowing argon through within the drier at a flow rate of 20 L/min, thereby obtaining a dry powder. This dry powder was then taken out of the drier, and pulverized by a roll crusher. At this time, pulverizing was conducted by adjusting a roll gap to 0.2 mm and a roll revolution speed to 60 rpm. The pulverized particles of the dry powder were classified by using a vibrating screen having openings of 75 μm and a vibrating screen having openings of 175 μm, thereby obtaining a silica powder having an average particle diameter D50 of 132 μm.
The granulated powder was put into a quartz vessel and subjected to firing in the atmospheric air at 1,250° C. for 49 hours, thereby obtaining a silica powder having an average particle diameter D50 of 99 μm.
Subsequently, the apparatus 30 shown in
After the spheroidizing treatment, the powder and ultrapure water were put into a cleaning vessel, to conduct ultrasonic cleaning. After conducting the ultrasonic cleaning, filtration was conducted by a filter having openings of 50 μm. This operation was conducted repetitively until fine particles attached onto surfaces of the silica powder particles were fully filtered out.
Finally, the powder after cleaning was charged into a container for drying, then the container for drying was brought into a drier, and drying was conducted by flowing nitrogen at a flow rate of 5 L/min through within the drier, and by holding the powder at a temperature of 350° C. for 12 hours, thereby obtaining a synthetic amorphous silica powder.
Firstly, 7 mols of ultrapure water was prepared per 1 mol of fumed silica having an average particle diameter D50 of 0.012 μm and a specific surface area of 200 m2/g. The prepared ultrapure water was charged into a vessel, and then the fumed silica was added thereinto, with stirring while keeping the temperature at 30° C. in an atmosphere of nitrogen. After addition of the fumed silica, stirring was continued for 6 hours, thereby producing a siliceous gel. At this time, the stirring speed was set to be 50 rpm. Next, the siliceous gel was transferred into a container for drying which was brought into a drier, and the siliceous gel was dried for 48 hours at a temperature of 250° C. while flowing nitrogen through within the drier at a flow rate of 20 L/min, thereby obtaining a dry powder. This dry powder was then taken out of the drier, and pulverized by a roll crusher. At this time, pulverizing was conducted by adjusting a roll gap to 0.4 mm and a roll revolution speed to 30 rpm. The pulverized particles of the dry powder were classified by using a vibrating screen having openings of 350 μm and a vibrating screen having openings of 500 μm, thereby obtaining a silica powder having an average particle diameter D50 of 456 μm.
The granulated powder was put into a quartz vessel and subjected to firing in the atmospheric air at 1,100° C. for 72 hours, thereby obtaining a silica powder having an average particle diameter D50 of 319 μm.
Subsequently, the apparatus 30 shown in
After the spheroidizing treatment, the powder and ultrapure water were put into a cleaning vessel, to conduct ultrasonic cleaning. After conducting the ultrasonic cleaning, filtration was conducted by a filter having openings of 100 μm. This operation was conducted repetitively until fine particles attached onto surfaces of the silica powder particles were fully filtered out.
Finally, the powder after cleaning was charged into a container for drying, then the container for drying was brought into a drier, and drying was conducted by flowing argon at a flow rate of 10 L/min through within the drier, and by holding the powder at a temperature of 200° C. for 24 hours, thereby obtaining a synthetic amorphous silica powder.
Firstly, 7 mols of ultrapure water was prepared per 1 mol of fumed silica having an average particle diameter D50 of 0.012 μm and a specific surface area of 200 m2/g. The prepared ultrapure water was charged into a vessel, and then the fumed silica was added thereinto, with stirring while keeping the temperature at 30° C. in an atmosphere of nitrogen. After addition of the fumed silica, stirring was continued for 6 hours, thereby producing a siliceous gel. At this time, the stirring speed was set to be 50 rpm. Next, the siliceous gel was transferred into a container for drying which was brought into a drier, and the siliceous gel was dried for 48 hours at a temperature of 250° C. while flowing nitrogen through within the drier at a flow rate of 20 L/min, thereby obtaining a dry powder. This dry powder was then taken out of the drier, and pulverized by a roll crusher. At this time, pulverizing was conducted by adjusting a roll gap to 0.4 mm and a roll revolution speed to 30 rpm. The pulverized particles of the dry powder were classified by using a vibrating screen having openings of 375 μm and a vibrating screen having openings of 525 μm, thereby obtaining a silica powder having an average particle diameter D50 of 442 μm.
The granulated powder was put into a quartz vessel and subjected to firing in the atmospheric air at 1,200° C. for 24 hours, thereby obtaining a silica powder having an average particle diameter D50 of 308 μm.
Subsequently, the apparatus 30 shown in
After the spheroidizing treatment, the powder and ultrapure water were put into a cleaning vessel, to conduct ultrasonic cleaning. After conducting the ultrasonic cleaning, filtration was conducted by a filter having openings of 100 μm. This operation was conducted repetitively until fine particles attached onto surfaces of the silica powder particles were fully filtered out.
Finally, the powder after cleaning was charged into a container for drying, then the container for drying was brought into a drier, and drying was conducted by flowing argon at a flow rate of 20 L/min through within the drier, and by holding the powder at a temperature of 250° C. for 48 hours, thereby obtaining a synthetic amorphous silica powder.
Firstly, 8 mols of ultrapure water was prepared per 1 mol of fumed silica having an average particle diameter D50 of 0.030 μm and a specific surface area of 50 m2/g. The prepared ultrapure water was charged into a vessel, and then the fumed silica was added thereinto, with stirring while keeping the temperature at 30° C. in an atmosphere of nitrogen. After addition of the fumed silica, stirring was continued for 6 hours, thereby producing a siliceous gel. At this time, the stirring speed was set to be 40 rpm. Next, the siliceous gel was transferred into a container for drying which was brought into a drier, and the siliceous gel was dried for 48 hours at a temperature of 250° C. while flowing nitrogen through within the drier at a flow rate of 10 L/min, thereby obtaining a dry powder. This dry powder was then taken out of the drier, and pulverized by a roll crusher. At this time, pulverizing was conducted by adjusting a roll gap to 0.9 mm and a roll revolution speed to 30 rpm. The pulverized particles of the dry powder were classified by using a vibrating screen having openings of 700 μm and a vibrating screen having openings of 1,000 μm, thereby obtaining a silica powder having an average particle diameter D50 of 891 μm.
The granulated powder was put into a quartz vessel and subjected to firing in the atmospheric air at 1,400° C. for 72 hours, thereby obtaining a silica powder having an average particle diameter D50 of 623 μm.
Subsequently, the apparatus 30 shown in
After the spheroidizing treatment, the powder and ultrapure water were put into a cleaning vessel, to conduct ultrasonic cleaning. After conducting the ultrasonic cleaning, filtration was conducted by a filter having openings of 150 μm. This operation was conducted repetitively until fine particles attached onto surfaces of the silica powder particles were fully filtered out.
Finally, the powder after cleaning was charged into a container for drying, then the container for drying was brought into a drier, and drying was conducted by flowing argon at a flow rate of 20 L/min through within the drier, and by holding the powder at a temperature of 250° C. for 48 hours, thereby obtaining a synthetic amorphous silica powder.
Firstly, 8 mols of ultrapure water was prepared per 1 mol of fumed silica having an average particle diameter D50 of 0.030 μm and a specific surface area of 50 m2/g. The prepared ultrapure water was charged into a vessel, and then the fumed silica was added thereinto, with stirring while keeping the temperature at 30° C. in an atmosphere of nitrogen. After addition of the fumed silica, stirring was continued for 6 hours, thereby producing a siliceous gel. At this time, the stirring speed was set to be 40 rpm. Next, the siliceous gel was transferred into a container for drying which was brought into a drier, and the siliceous gel was dried for 48 hours at a temperature of 250° C. while flowing nitrogen through within the drier at a flow rate of 10 L/min, thereby obtaining a dry powder. This dry powder was then taken out of the drier, and pulverized by a roll crusher. At this time, pulverizing was conducted by adjusting a roll gap to 0.9 mm and a roll revolution speed to 30 rpm. The pulverized particles of the dry powder were classified by using a vibrating screen having openings of 700 μm and a vibrating screen having openings of 1,000 μm, thereby obtaining a silica powder having an average particle diameter D50 of 877 μm.
The granulated powder was put into a quartz vessel and subjected to firing in the atmospheric air at 1,300° C. for 48 hours, thereby obtaining a silica powder having an average particle diameter D50 of 614 μm.
Subsequently, the apparatus 30 shown in
After the spheroidizing treatment, the powder and ultrapure water were put into a cleaning vessel, to conduct ultrasonic cleaning. After conducting the ultrasonic cleaning, filtration was conducted by a filter having openings of 200 μm. This operation was conducted repetitively until fine particles attached onto surfaces of the silica powder particles were fully filtered out.
Finally, the powder after cleaning was charged into a container for drying, then the container for drying was brought into a drier, and drying was conducted by flowing argon at a flow rate of 10 L/min through within the drier, and by holding the powder at a temperature of 200° C. for 24 hours, thereby obtaining a synthetic amorphous silica powder.
Firstly, ultrapure water was prepared in an amount equivalent to 60 mols, per 1 mol of silicon tetrachloride. This ultrapure water was brought into a vessel, and then the carbon tetrachloride was added thereinto, with stirring while keeping the temperature at 30° C. in an atmosphere of nitrogen, thereby hydrolyzing the silicon tetrachloride. After addition of the silicon tetrachloride, stirring was continued for 4 hours, thereby producing a siliceous gel. At this time, the stirring speed was set to be 250 rpm. Next, the siliceous gel was transferred into a container for drying which was brought into a drier, and the siliceous gel was dried for 24 hours at a temperature of 250° C. while flowing nitrogen through within the drier at a flow rate of 10 L/min, thereby obtaining a dry powder. This dry powder was then taken out of the drier, and pulverized by a roll crusher. At this time, pulverizing was conducted by adjusting a roll gap to 0.2 mm and a roll revolution speed to 150 rpm. The pulverized particles of the dry powder were classified by using a vibrating screen having openings of 75 μm and a vibrating screen having openings of 200 μm, thereby obtaining a silica powder having an average particle diameter D50 of 144 μm.
The granulated powder was put into a quartz vessel and subjected to firing in the atmospheric air at 1,250° C. for 48 hours, thereby obtaining a silica powder having an average particle diameter D50 of 101 μm.
Subsequently, the apparatus 30 shown in
After the spheroidizing treatment, the powder and ultrapure water were put into a cleaning vessel, to conduct ultrasonic cleaning. After conducting the ultrasonic cleaning, filtration was conducted by a filter having openings of 50 μm. This operation was conducted repetitively until fine particles attached onto surfaces of the silica powder particles were fully filtered out.
Finally, the powder after cleaning was charged into a container for drying, which was then brought into a drier, and drying was conducted by flowing nitrogen at a flow rate of 10 L/min through within the drier, and by holding the powder at a temperature of 200° C. for 36 hours, thereby obtaining a synthetic amorphous silica powder.
Firstly, 1 mol of ultrapure water and 1 mol of ethanol were prepared per 1 mol of tetramethoxysilane. The prepared ultrapure water and ethanol were charged into a vessel, and then the tetramethoxysilane was added thereinto, with stirring while keeping the temperature at 60° C. in an atmosphere of nitrogen, thereby hydrolyzing the tetramethoxysilane. After addition of the tetramethoxysilane, stirring was continued for 60 minutes, and 25 mols of ultrapure water was further added thereinto per 1 mol of tetramethoxysilane, followed by continued stirring for 6 hours, thereby producing a siliceous gel. At this time, the stirring speed was set to be 100 rpm. Next, the siliceous gel was transferred into a container for drying which was brought into a drier, and the siliceous gel was dried for 24 hours at a temperature of 200° C. while flowing nitrogen through within the drier at a flow rate of 20 L/min, thereby obtaining a dry powder. This dry powder was then taken out of the drier, and pulverized by a roll crusher. At this time, pulverizing was conducted by adjusting a roll gap to 0.2 mm and a roll revolution speed to 60 rpm. The pulverized particles of the dry powder were classified by using a vibrating screen having openings of 75 μm and a vibrating screen having openings of 200 μm, thereby obtaining a silica powder having an average particle diameter D50 of 136 μm.
The granulated powder was put into a quartz vessel and subjected to firing in the atmospheric air at 1,250° C. for 48 hours, thereby obtaining a silica powder having an average particle diameter D50 of 95 μm.
Subsequently, the apparatus 30 shown in
After the spheroidizing treatment, the powder and ultrapure water were put into a cleaning vessel, to conduct ultrasonic cleaning. After conducting the ultrasonic cleaning, filtration was conducted by a filter having openings of 50 μm. This operation was conducted repetitively until fine particles attached onto surfaces of the silica powder particles were fully filtered out.
Finally, the powder after cleaning was charged into a container for drying, which was then brought into a drier, and drying was conducted by flowing nitrogen at a flow rate of 10 L/min through within the drier, and by holding the powder at a temperature of 200° C. for 36 hours, thereby obtaining a synthetic amorphous silica powder.
Measured for the powders obtained in Examples 1 to 10 and Comparative Examples 1 to 21, were an average particle diameter D50, a BET specific surface area, a theoretical specific surface area, a quotient represented by “BET specific surface area/theoretical specific surface area”, a real density, an intra-particulate porosity, a circularity, and a unmolten ratio, by those methods to be described hereinafter. These results are listed in Table 3 or Table 4.
(i) Average particle diameter D50: this was obtained by calculating an average value of medians of particle distributions in volume basis measured three times by Laser Diffraction/Scattering Particle Size Distribution Analyzer (Model Name: HORIBA LA-950).
(ii) BET specific surface area: this was measured by a BET three-point method by using a measuring apparatus (QUANTACHROME AUTOSORB-1 MP). The BET three-point method is configured to obtain a gradient A from adsorbed nitrogen amounts at three points of relative pressure, thereby obtaining a specific surface area value based on a BET equation. Measurement of adsorbed nitrogen amounts was conducted under conditions of 150° C. for 60 minutes.
(iii) Theoretical specific surface area: this was calculated from the following equation (2), assuming that D represents an average particle diameter D50 of a powder, and ρ represents a real density of 2.2 g/cm3 in the following equation (1):
Theoretical specific surface area=6/(D×ρ) (1)
Theoretical specific surface area of powder=2.73/D50 (2)
(iv) Quotient of “BET specific surface area/theoretical specific surface area”: this was calculated from the specific surface area and the theoretical specific surface area measured and obtained in the above manners, respectively.
(v) Real density: this was calculated as an average value of real densities obtained by conducting a real density measurement three times in conformity to JIS R7212: Testing Methods for Carbon Blocks, (d) Measurement of absolute specific gravity.
(vi) Intra-particulate porosity: the obtained powder was embedded in a resin which was then ground to expose cross sections of powder particles. The cross sections of powder particles were observed by a SEM (scanning electron microscope). Further, the intra-particulate porosity was calculated from the following equation (4), by measuring cross-sectional areas of 50 powder particles, and areas of spaces in the particles, if present:
Intra-particulate porosity=total area of spaces in particles/total cross-sectional area of particles (4)
(vii) Circularity: this was measured two times by a particle size/shape distribution measuring device (PITA-1 manufactured by SEISHIN ENTERPRISE Co., Ltd.) shown in
Circularity=4πS/L2 (3)
(viii) Unmolten ratio: in the above-mentioned 200 powder particles of the particle image in the projection view, a rate of the angular powder particles shown in
<Evaluation 1>
Impurity concentrations of the powders obtained in Examples 1 to 10 and Comparative Examples 1 to 21 were analyzed or measured by the following methods (1) to (5). The results thereof are listed in the following Table 5 or Table 6.
(i) Na, K, Ca, Fe, Al, and P: Each powder was thermally decomposed with hydrofluoric acid and sulfuric acid, in a manner to prepare a constant-volume liquid by using dilute nitric acid after thermal condensation, followed by conduction of analysis by a High-Frequency Inductive Coupling Plasma Mass Spectrometer (Model Name: SPQ9000 of SII NanoTechnology Inc.).
(ii) B: Each powder was thermally decomposed with hydrofluoric acid, in a manner to prepare a constant-volume liquid by using ultrapure water after thermal condensation, followed by conduction of analysis by a High-Frequency Inductive Coupling Plasma Mass Spectrometer (Model Name: SPQ9000 of SII NanoTechnology Inc.)
(iii) C: Added to each powder were iron, tungsten, and tin as combustion improvers, to thereby conduct analysis by a high-frequency furnace combustion-infrared absorption method (Model Name: HORIBA EMIA-920V).
(iv) Cl: Each synthetic amorphous silica powder was mixed with ultrapure water, in a manner to cause Cl to leach out of the former into the latter, under ultrasonic waves. The synthetic amorphous silica powder and the leach solution were separated from each other by a centrifuge, and the separated leach solution was subjected to conduction of analysis by ion chromatography (Model Name: Dionex DX-500).
(v) OH: Measurement therefor was conducted by a peak height near 3,660 cm−1 by Fourier Transformation Infrared spectrophotometer (Model Name: ThermoFischer Nicolet 4700FT-IR).
As apparent from Table 5, it is seen that the powders of Examples 1 to 4 were each relatively low in concentration of hydroxyl group and carbon which possibly act as gas components acting as sources of generation or expansion of gas bubbles in a synthetic silica glass product at a high temperature and a reduced pressure, as compared to the powders of Comparative Examples 1 to 11.
As apparent from Table 6, it is seen that: the synthetic amorphous silica powders each adopting a powder as a raw material obtained by reacting silicon tetrachloride in a liquid, were less than 2 ppm in carbon concentration; the synthetic amorphous silica powders each adopting a powder as a raw material obtained from an organic silicon compound, were less than 2 ppm in chlorine concentration; and the synthetic amorphous silica powders each adopting a powder as a raw material obtained from fumed silica, were less than 2 ppm in carbon concentration and less than 2 ppm in chlorine concentration.
<Comparative Test and Evaluation 2>
The powders obtained in Examples 1 to 10 and Comparative Examples 1 to 21 were used to fabricate rectangular parallelepiped block materials of length 20 mm×width 20 mm×height 40 mm, respectively, in a manner to evaluate the number of gas bubbles caused in each block material. These results are listed in the following Table 7 or Table 8. Specifically, each block material was fabricated by: introducing the applicable powder into a carbon crucible; heating it by a carbon heater to 2,200° C. in a vacuum atmosphere at 2.0×104 Pa; and holding it for 48 hours. Conducted for this block material was a heat treatment at a temperature of 1,600° C. for 48 hours in a vacuum atmosphere of 5.0×102 Pa. After the heat treatment, the block material was cut out at a height of 20 mm to expose a cross section of length 20 mm×width 20 mm which was then ground, in a manner to evaluate the number of gas bubbles observed in a region having a depth of 2 mm from the surface (cross section) of the block material, and a width of 2 mm.
<Comparative Test and Evaluation 3>
Into a mold for producing a quartz crucible having a diameter of 16 inches were filled about 8 mm of natural quartz powder and about 2.5 mm of each powder obtained in Examples 1 to 10 and Comparative Examples 1 to 21. An arc electrode was so provided that the tip of the electrode was located at the position (the same level as the upper end surface of the mold) 400 mm upward from the bottom surface of the mold which is on the center axis of the mold. The quartz powder was melted by passing the current to the arc electrode with a power of 200 kw for 5 minutes while rotating the mold with a predetermined rate. Then, the arc electrode was descended by 200 mm, and the quartz in the vicinity of the center of the bottom of the mold was selectively heated by passing the current with the same electric power for 8 minutes while reducing the pressure from the mold side during passing the current for 6 minutes.
The obtained quartz crucible was cut and the sectional surface was polished. With regard to the amorphous silica layer formed by the powder obtained in Examples 1 to 10 and Comparative Examples 1 to 21, each of the thickness at the portion 10 cm from the upper end of the quartz crucible was measured by a microscope. These results are shown in the following Table 7 or Table 8. In Table 7 and Table 8, the thickness of the amorphous silica layer is preferably as close as 2.5 mm.
As apparent from Table 7, it is seen that the blocks fabricated by using the powders of Examples 1 to 4, respectively, were remarkably decreased in the number of caused gas bubbles, as compared to the blocks fabricated by using the powders of Comparative Examples 9 to 11 without subjecting to a spheroidizing treatment, respectively.
Further, it is seen that, comparing Examples 1 to 4 with Comparative Examples 1 to 8, Examples 1 to 4 were remarkably decreased in the number of caused gas bubbles as compared to Comparative Examples 2 to 4, 6 and 8 though these Examples and Comparative Examples were each subjected to a spheroidizing treatment. On the other hand, whereas Comparative Examples 1, 5 and 7 were remarkably decreased in the number of caused gas bubbles, as compared with Examples 1 to 4, the thickness of the amorphous silicon layer was markedly thin, thus the amorphous silica layer with a desired thickness could not be formed.
As apparent from Table 1 to Table 8, it is seen that the blocks fabricated by using the powders of Examples 5 to 10 which were fired under predetermined conditions before spheroidizing treatments, respectively, were further decreased in the number of caused gas bubbles with the thickness of the amorphous silicon layer, as compared to the blocks fabricated by using the powders of Examples 1 to 4 without subjecting to firing, respectively.
Further, comparing Examples 5 to 8 with Comparative Examples 13 to 15, 17 and 19, Example 9 with Comparative Example 20, and Example 10 with Comparative Example 21, it is seen therefrom that Examples 5 to 8, Example 9, and Example 10 were remarkably decreased in the number of caused gas bubbles, as compared to Comparative Examples 13 to 15, 17 and 19, Comparative Example 20, and Comparative Example 21, though these Examples and Comparative Examples were each subjected to a spheroidizing treatment. On the other hand, Comparative Examples 12, 16 and 18 were remarkably decreased in the number of caused gas bubbles, as compared to Examples 5 to 8, but the thicknesses of the amorphous silica layers were markedly thin and the amorphous silica layer having a desired thickness could not be formed. It is seen therefrom that the synthetic amorphous silica powders of the present invention are each remarkably enhanced in effect for reducing an amount of generation or degree of expansion of gas bubbles, and are improved in moldability, so that the powders are each suitable as a raw material for manufacturing a synthetic silica glass product.
The synthetic amorphous silica powder of the present invention is preferably usable as a raw material for manufacturing a synthetic silica glass product such as a crucible, jig, and the like to be used for single crystal production in semiconductor application.
| Number | Date | Country | Kind |
|---|---|---|---|
| 2011-064451 | Mar 2011 | JP | national |
| 2011-064456 | Mar 2011 | JP | national |
| Filing Document | Filing Date | Country | Kind | 371c Date |
|---|---|---|---|---|
| PCT/JP2012/055059 | 2/29/2012 | WO | 00 | 11/22/2013 |
| Publishing Document | Publishing Date | Country | Kind |
|---|---|---|---|
| WO2012/128005 | 9/27/2012 | WO | A |
| Number | Name | Date | Kind |
|---|---|---|---|
| 8883110 | Ueda | Nov 2014 | B2 |
| 9120678 | Ueda | Sep 2015 | B2 |
| 20050129603 | Szillat et al. | Jun 2005 | A1 |
| 20100178509 | Schumacher et al. | Jul 2010 | A1 |
| 20120299207 | Ueda | Nov 2012 | A1 |
| Number | Date | Country |
|---|---|---|
| 2522627 | Nov 2012 | EP |
| 2522630 | Nov 2012 | EP |
| 62-176928 | Aug 1987 | JP |
| 03-275527 | Dec 1991 | JP |
| 04-075848 | Mar 1992 | JP |
| 06-287012 | Oct 1994 | JP |
| 2004-225135 | Aug 2004 | JP |
| 2005-162593 | Jun 2005 | JP |
| 2005-531475 | Oct 2005 | JP |
| 2011-157261 | Aug 2011 | JP |
| 200922896 | Jun 2009 | TW |
| WO-2011083710 | Jul 2011 | WO |
| Entry |
|---|
| Office Action dated Mar. 27, 2015, issued for the Taiwan Patent Application No. 101109323 and English translation thereof. |
| Supplementary European Search Report dated Jul. 22, 2014, issued for the European patent application No. 12761100.2. |
| International Search Report dated Jun. 12, 2012, issued for PCT/JP2012/055059. |
| Number | Date | Country | |
|---|---|---|---|
| 20140065423 A1 | Mar 2014 | US |