Synthetic microspheres and methods of making same

Abstract

A synthetic microsphere having a low alkali metal oxide content and methods of forming the microsphere and its components are provided. The synthetic microsphere is substantially chemically inert and thus a suitable replacement for natural cenospheres, particularly in caustic environments such as cementitious mixtures. The synthetic microsphere can be made from an agglomerate precursor that includes an aluminosilicate material, such as fly ash, a blowing agent such as sugar, carbon black, and silicon carbide, and a binding agent. The synthetic microsphere is produced when the precursor is fired at a pre-determined temperature profile so as to form either solid or hollow synthetic microspheres depending on the processing conditions and/or components used.

Description

BACKGROUND OF THE INVENTION

[0002] 1. Field of the Invention

[0003] Embodiments of this invention generally relate to synthetic microspheres and processes for manufacturing the microspheres. These embodiments have been developed primarily to provide a cost-effective alternative to commercially available cenospheres.

[0004] 2. Description of the Related Art

[0005] Any discussion of the prior art throughout the specification should in no way be considered as an admission that such prior art is widely known or forms part of common general knowledge in the field.

[0006] Cenospheres are spherical inorganic hollow microparticles found in fly ash, which is typically produced as a by-product in coal-fired power stations. Cenospheres typically make up around 1%-2% of the fly ash and can be recovered or “harvested” from fly ash. These harvested cenospheres are widely available commercially. The composition, form, size, shape and density of cenospheres provide particular benefits in the formulation and manufacture of many low-density products.

[0007] One of the characterizing features of cenospheres is their exceptionally high chemical durability. This exceptionally high chemical durability is understood to be largely due to the very low content of alkali metal oxides, particularly sodium oxide, in their composition. Accordingly, low-density composites produced from harvested cenospheres usually have the desirable properties of high strength to weigh ratio and chemical inertness. Chemical inertness is especially important in Portland cement applications, where relative chemical inertness plays an important role in achieving highly durable cementitious products. Thus, harvested cenospheres have proven to be especially useful in building products and in general applications where they may come into contact with corrosive environments where high chemical durability is desirable.

[0008] Despite the known utility of harvested cenospheres, their widespread use has been limited to a large extent by their cost and availability. The recovery of cenospheres in large quantities from fly ash is a labor intensive and expensive process. Although it is possible to increase the recovery of cenospheres from fly ash by modifying the collection process, the cost of improved recovery does not make this economically viable.

[0009] It may also be possible to alter combustion conditions in power stations to increase the yield of cenospheres in fly ash. However, combustion conditions in power stations are optimized for coal-burning rather than cenosphere production. It is not economically viable to increase the yield of cenosphere production at the expense of coal-burning efficiency.

[0010] Several methods for producing synthetic microspheres have also been developed and are described in the prior art. Early methods for manufacturing hollow glass microspheres involved combining sodium silicate and borax with a suitable foaming agent, drying and crushing the mixture, adjusting the size of the crushed particles and subsequently firing the particles. However, these methods suffer from the use of expensive starting materials such as borax. Hence, the resulting microspheres are necessarily expensive. In addition, the product has poor chemical durability due to the presence of a relatively high percentage of sodium oxide in the resulting glass composition.

[0011] U.S. Pat. No. 3,752,685 describes a method of producing glass microspheres from Shirasu, a naturally occurring volcanic rock. Upon heating at 800 to 1000° C., finely divided Shirasu forms hollow glass microspheres. However, this method relies on the provision of Shirasu, which is not a widely available starting material.

[0012] U.S. Pat. No. 3,365,315 describes a method of producing glass microspheres from glass beads by heating in the presence of water vapor at a temperature of about 1200° C. This method requires the exclusive use of pre-formed amorphous glasses as the starting raw materials.

[0013] U.S. Pat. No. 2,978,340 describes a method of forming glass microspheres from discrete, solid particles consisting essentially of an alkali metal silicate. The microspheres are formed by heating the alkali metal silicate at a temperature in the range of 1000-2500° F. in the presence of a gasifying agent, such as urea or Na2CO3. Again, these alkali silicate microspheres suffer from poor chemical durability due to a high percentage of alkali metal oxides.

[0014] U.S. Pat. No. 2,676,892 describes a method of forming microspheres from a Macquoketa clay shale by heating particles of the shale to a temperature of 2500-3500° F. The resulting product undesirably has an open pore structure leading to a relatively high water absorption in an aqueous cementitious environment.

[0015] U.S. Pat. No. 2001/0043996 (equivalent of EP-A-1156021) describes a spray combustion process for forming hollow microspheres having a diameter of from 1 to 20 microns. However, this process is unsuitable for making hollow microspheres having a diameter similar to that of known cenospheres, which is typically about 200 microns. In spray combustion processes as described in the reference, rapid steam explosion ruptures larger particles thereby preventing formation of hollow microspheres greater than about 20 microns in diameter.

[0016] Hence, from the foregoing, it will be appreciated that there is a need for low-cost synthetic microspheres with properties similar to those of natural microspheres harvested from fly ash. There is also a need for synthetic microspheres with acceptable chemical durability suitable for incorporation into fiber cement compositions. To this end, there is a particular need for a low-cost, high yield process of producing synthetic microspheres from commonly available raw materials. It is an object of the present invention to overcome or ameliorate at least one of the disadvantages of the prior art, or to provide a useful alternative.

SUMMARY OF THE INVENTION

[0017] Unless the text clearly requires otherwise, throughout the description and the claims, the words “comprise”, “comprising”, and the like are to be construed in an inclusive sense as opposed to an exclusive or exhaustive sense; that is to say, in the sense of “including, but not limited to”.

[0018] As used herein, the term “synthetic hollow microsphere” or “synthetic microsphere” means a microsphere synthesized as a primary target product of a synthetic process. The term does not include harvested cenospheres which are merely a by-product of burning coal in coal-fired power stations.

[0019] Although the term “microsphere” is used throughout the specification, it will be appreciated that this term is intended to include any substantially spherical microparticle, including microparticles that are not true geometric spheres.

[0020] As used herein, the term “preparing an agglomerate precursor” means a synthetic preparation of an agglomerate precursor by combining the various constituents, for example, by a method described below.

[0021] As used herein, the term “primary component” means that this component is the major constituent of the agglomerate precursor, in the sense that the amount of primary component exceeds the amount of any other individual constituent.

[0022] In one aspect, the preferred embodiments of the present invention provide a synthetic microsphere having a synthetic, substantially spherical wall, a particle diameter, of greater than about 30 microns, and an alkali metal oxide content of less than about 10 wt. %, preferably between about 2 to 10 wt. %, based on the weight of the microsphere. Preferably, the synthetic microsphere comprises a pre-determined amount of at least one aluminosilicate material and at least one pre-selected chemical. In some embodiments, the at least one pre-selected chemical acts as a binding agent.

[0023] In certain preferred embodiments, the substantially spherical wall defines at least one inner void, wherein the at least one inner void is synthetically formed by a pre-determined amount of at least one blowing agent and preferably has a volume of between about 30-95% of the aggregate volume of the microsphere. The at least one blowing agent can be selected from the group consisting of powdered coal, carbon black, graphite, carbonaceous polymeric organics, oils, sugar, starch, polymeric organic oils, polyvinyl alcohol, carbonates, silicon carbide, sulfates, nitrides, nitrates, glycol, glycerine, and combinations thereof.

[0024] Moreover, the synthetic, substantially spherical wall of the microsphere preferably has a make-up comprising an aluminosilicate material and the binding agent. The binding agent can be selected from the group consisting of alkali metal silicates, alkali metal aluminosilicates, alkali metal borates, alkali or alkaline earth metal carbonates, alkali or alkaline earth metal nitrates, alkali or alkaline earth metal nitrites, boric acid, alkali or alkaline earth metal sulfates, alkali or alkaline earth metal phosphates, alkali or alkaline earth metal hydroxides, sugar, starch, ultra fine fly ash, Class C fly ash, Class F fly ash, colloidal silica, inorganic silicate cements, organic polymers, and combinations thereof.

[0025] In one embodiment, the synthetic microsphere has one or more of the following properties: a particle diameter of between about 30 to 1000 microns, an aspect ratio of between about 0.8 and 1, a wall thickness of between about 1 to 100 microns of the microsphere radius, a particle density of between about 0.1 and 2 g/cm3, and/or a bulk density of less than about 1.4 g/cm3. Moreover, the synthetic microsphere is preferably formulated to be substantially chemically inert in a caustic environment having a pH of about 12-14.

[0026] In another aspect, the preferred embodiments of the present invention provide a synthetic microsphere having an outer wall defining a substantially enclosed synthetically formed cavity. Preferably, the microsphere has an average particle diameter of greater than about 30 microns and comprises a material formed with a pre-selected formulation, wherein the formulation is configured to provide the microsphere with an alkali metal oxide content of less than about 10 wt. % based on the weight of the microsphere.

[0027] In one embodiment, the pre-selected formulation comprises about 30 to 80 wt. % SiO2, about 2 to 45 wt. % Al2O3, up to about 30 wt. % divalent metal oxide, and up to about 10 wt. % monovalent metal oxide, and up to about 20 wt. % of one or more metal oxides. Moreover, the microsphere can also have one or more of the following properties: about 1 to 10 wt. % sodium oxide and/or an average particle diameter of between about 50 to 300 microns and/or the mass ratio of silica to alumina is greater than unity. In certain embodiments, the aluminosilicate material is derived from fly ash and is preferably calcined.

[0028] In yet another aspect, the preferred embodiments of the present invention provide a plurality of synthetic microspheres having an alkali metal oxide content of less than about 10 wt. % based on the total weight of the microspheres. Preferably, the microspheres are formulated from aluminosilicate particles, wherein the particles have a pre-selected size range. In one embodiment, the average particle diameter is between about 0.01 to 50 microns.

[0029] In yet another aspect, the preferred embodiments of the present invention provide a formulation for forming a synthetic microsphere. The formulation preferably comprises a primary component comprising at least one aluminosilicate component having a particle diameter pre-selected to form a microsphere with a particle diameter greater than about 30 microns and at least one chemical, wherein the at least one chemical comprises a binding agent that substantially binds the primary component together so as to form a precursor to make the microspheres. Moreover, the primary component and the at least one chemical each having a sufficiently low or no alkali metal oxide content so as to maintain the alkali metal oxide content of the synthetic microsphere to less than about 10 wt. %.

[0030] In one embodiment, the formulation further comprises a blowing agent, wherein the blowing agent can be combined with the primary component and the binding agent in a manner such that when activated, the blowing agent releases a gas that expands the precursor so as to form a substantially spherical wall enclosing the cavity therein. In one embodiment, the primary component comprises fly ash and the blowing agent is selected from the group consisting of carbon black, powdered coal, sugar, and silicon carbide.

[0031] From the foregoing, it will be appreciated that certain aspects of the preferred embodiments provide a synthetic microsphere that is substantially chemically inert and can be used as a substitute for natural harvested cenospheres. In particular, certain embodiments of the microspheres are configured with physical properties, such as particle diameter, aspect ratio and density, that are substantially the same as the cenospheres. These and other objects and advantages of the preferred embodiments of the present invention will become more apparent from the following description taken in conjunction with the following drawings.

BRIEF DESCRIPTION OF THE DRAWINGS

[0032] FIG. 1 illustrates a phase equilibrium diagram for binary system Na2O—SiO2, the composition being expressed as a weight percentage of SiO2;

[0033] FIG. 2 is a schematic illustration of one preferred method of producing the agglomerate precursor of one embodiment of the present invention;

[0034] FIG. 3 is a scanning electron micrograph of synthetic hollow microspheres obtained from Example 1 (Sample 1);

[0035] FIG. 4 is a scanning electron micrograph of synthetic hollow microspheres obtained from Example 1 (Sample 2);

[0036] FIG. 5 is a scanning electron micrograph of synthetic hollow microspheres obtained from Example 1 (Sample 3);

[0037] FIG. 6 is a scanning electron micrograph of synthetic hollow microspheres obtained from Example 2 (Sample 4);

[0038] FIG. 7 is a scanning electron micrograph of synthetic hollow microspheres obtained from Example 2 (Sample 5);

[0039] FIG. 8 is a scanning electron micrograph of synthetic hollow microspheres obtained from Example 2 (Sample 6);

[0040] FIG. 9 is a scanning electron micrograph of synthetic hollow microspheres obtained from Example 3 (Sample 7);

[0041] FIG. 10 is a scanning electron micrograph of synthetic hollow microspheres obtained from Example 4 (Sample 12);

[0042] FIG. 11 is a scanning electron micrograph of synthetic hollow microspheres obtained from Example 4 (Sample 13);

[0043] FIG. 12 is a scanning electron micrograph of synthetic hollow microspheres obtained from Example 5;

[0044] FIG. 13 is a scanning electron micrograph of synthetic hollow microspheres obtained from Example 5;

[0045] FIG. 14 is a scanning electron micrograph of synthetic hollow microspheres obtained from Example 5;

[0046] FIG. 15 is a scanning electron micrograph of synthetic hollow microspheres obtained from Example 6;

[0047] FIG. 16 is a scanning electron micrograph of synthetic hollow microspheres obtained from Example 6;

[0048] FIG. 17 is a scanning electron micrograph of synthetic hollow microspheres obtained from Example 7.

DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

[0049] Reference will now be made to the drawings wherein like numerals refer to like parts throughout. As described hereinbelow, the preferred embodiments of the present invention provide a chemically durable, synthetic microsphere having properties and characteristics similar to natural cenospheres harvested from fly ash. The preferred embodiments also provide a method for manufacturing the microspheres, including raw material composition and processing, and uses for the microspheres in various applications, including fiber cement products.

[0050] Synthetic Microspheres

[0051] The synthetic microsphere as described herein generally comprises a substantially spherical outer wall and a substantially enclosed cavity or void defined by the wall, resembling the general configuration of harvested cenospheres. However, it will be appreciated that the synthetic microspheres of certain embodiments can be substantially solid. In certain preferred embodiments, the synthetic microsphere has one or more of the following characteristics, which are also generally characteristics of harvested cenospheres:

[0052] an aspect ratio of between about 0.8 and 1;

[0053] (i) a void volume of between about 30 and 95%, based on the total volume of the microsphere;

[0054] (ii) a wall thickness of between about 1 to 100 microns and/or 5 and 50% of the microsphere radius;

[0055] (iii) a composition comprising about 30 to 85% SiO2, about 2 to 45 wt. %, preferably about 6 to 40 wt. %, Al2O3, up to about 30 wt. % divalent metal oxides such as MgO, CaO, SrO, and BaO, about 4 to 10 wt. % monovalent metal oxides such as Na2O, K2O, and up to about 20 wt. % of other metal oxides, including metal oxides which exist in multiple oxidation states such as TiO2 and Fe2O3;

[0056] (iv) a silica to alumina ratio which is greater than about 1;

[0057] (v) an average diameter of between about 40 and 500 microns, more preferably between about 50 and 300 microns;

[0058] (vi) an outer wall thickness of between about 1 and 50 microns, preferably between about 1 and 30 microns, more preferably between about 2.5 and 20 microns;

[0059] (vii) a particle density of between about 0.1 and 20 g/cm3, more preferably between about 0.2 and 1.5 g/cm3, and more preferably between about 0.4 and 1 g/cm3; or

[0060] (viii) a bulk density of less than about 1.4 g/cm3, preferably less than about 1 g/cm3.

[0061] In one embodiment, the synthetic microsphere comprises an aluminosilicate material having an average particle diameter of between about 30 to 1000 microns and an alkali metal oxide content of less than about 10 wt. %, preferably between about 2 to 10 wt. %, based on the total weight of the microsphere. In one preferred embodiment, the total alkali metal oxide content is in the range of about 3 to 9 wt. %, more preferably about 4 to 8 wt. % based on the total weight of the microsphere. In some embodiments, the total alkali metal oxide content of the synthetic microsphere is in the range of about 4 to 6 wt. %, based on the total weight of the microsphere.

[0062] The synthetic microsphere may contain several alkali metal oxides, typically a combination of sodium oxide Na2O and potassium oxide K2O, which make up the total alkali metal content. The majority of the sodium oxide in the synthetic microspheres is typically derived from binding agents (e.g. sodium silicate) used in forming the microspheres as will be described in greater detail below. In one embodiment, the amount of sodium oxide in the synthetic microsphere is preferably in the range of about 2 to 10 wt. %, more preferably about 3 to 9 wt. %, more preferably about 4 to 8 wt. %, and more preferably about 4 to 7 wt. %, based on the total weight of the microsphere. The amount of potassium oxide in the synthetic hollow microspheres is preferably less than about 3 wt. %, more preferably less than about 2 wt. %, and more preferably less than about 1.5 wt. %, based on the total weight of the microsphere.

[0063] In certain embodiments, the synthetic microsphere further comprises one or more chemicals used to form the microspheres. For example, the make-up of the wall of the synthetic microsphere may include a binding agent that will be described in greater detail below. Moreover, the synthetic hollow microsphere may also comprise residual amounts of a blowing agent used to form the microsphere as will also be described in greater detail below.

[0064] The synthetic microspheres of the preferred embodiments have several advantages over microspheres known in the prior art. Firstly, the synthetic microspheres comprise an aluminosilicate material. Aluminosilicates are inexpensive and widely available throughout the world, for example from a large variety of rocks, clays and minerals and also from waste by-products, particularly bottom ash and fly ash. It is particularly advantageous that the synthetic microspheres can be prepared from fly ash. Secondly, the presence of only moderate quantities of alkali metal oxide provides the microspheres with acceptably high chemical durability and can be used in the same situations as known cenospheres. For example, synthetic microspheres according to preferred forms of the present invention can withstand highly caustic environments and harsh autoclaving conditions as typical of some fiber cement manufacturing processes. By contrast, synthetic microspheres produced according to methods known in the prior art generally contain high amounts of alkali metal oxides and thus have unacceptable low chemical durability.

[0065] Furthermore, an average particle diameter of between about 30 and 1000 microns for the synthetic microspheres of the preferred embodiments is advantageous. Particles of this size are known to be relatively safe is building and other materials. When very small particles (e.g. less than about 30 microns) are used in building and other materials, the risk of particulates entering the human respiratory system is greatly increased. This is highly undesirable since it is known that the entry of particulates into the respiratory system is responsible for many potentially fatal diseases, which have been well documented. The risk is increased when composite building materials incorporating the small particles are disturbed, for example, by cutting operations. Hence, the larger average particle diameter of the synthetic microspheres of the embodiments described herein permits the microspheres to be used safely in a range of applications.

[0066] As will be described in greater detail below, the synthetic hollow microsphere of certain preferred embodiments can be formed by first preparing an agglomerate precursor, wherein the agglomerate precursor comprises a primary component, a binding agent, and a blowing agent and then firing the precursor at a predetermined temperature profile sufficient to seal the surface of the precursor and activate the blowing agent thereby forming a synthetic hollow microsphere.

[0067] Agglomerate Precursor

[0068] In certain embodiments, the agglomerate precursor is generally a substantially solid agglomerate mixture comprising a primary component, a binding agent and a blowing agent. Preferably, the amount of primary component comprises about 40 wt. % or more based on the total weight of the agglomerate precursor, more preferably about 50 wt. % or more, more preferably about 70 wt. % or more, more preferably about 80 wt. % or more, and more preferably about 90 wt. % or more. Preferably, the amount of blowing agent comprises about 0.05 to 10 wt. %, based on the total weight of the agglomerate precursor, more preferably about 0.1 to 6 wt. %, more preferably about 0.2 to 4 wt. %. The exact amount of blowing agent will depend on the composition of the primary component, the type of blowing agent and the required density of the final microsphere.

[0069] The preferred ratio of primary component to blowing agent will vary, depending on the composition of each of the ingredients. Typically, the ratio of primary component to blowing agent is in the range of about 1000:1 to 10:1, more preferably about 700:1 to 15:1, and more preferably about 500:1 to 20:1.

[0070] Preferably, the agglomerate precursor has a water content of about 10 wt. % or less, more preferably about 5 wt. % or less, and more preferably about 3 wt. % or less. The agglomerate precursor is substantially dry, although a small amount of moisture may be present in the agglomerate precursor after a solution-based process for forming the precursor, which is to be described in greater detail below. A small amount of water may also help to bind particles in the agglomerate together, especially in cases where particles in the agglomerate precursor are water-reactive. In some embodiments, when the agglomerate precursor has greater than about 10 wt. % water, such as for example 14 wt. %., it was found that the agglomerate tend to burst into fines during the firing process.

[0071] Moreover, the agglomerate precursor preferably has a total alkali metal oxide content of 10 wt. % or less, and typically in the range of about 3 to 10 wt. %, about 4 to 10 wt. % or about 5 to 10 wt. %. A total alkali metal oxide content of about 10 wt. % or less is advantageous, because microspheres formed from such agglomerate precursors will still have acceptably high chemical durability suitable for most applications.

[0072] Preferably, the agglomerate is particulate, having an average agglomerate particle diameter in the range of about 10 to 1000 microns, more preferably about 30 to 1000 microns, more preferably about 40 to 500 microns, and more preferably about 50 to 300 microns.

[0073] Primary Component

[0074] In certain preferred embodiments, the primary component of the agglomerate precursor comprises a low alkali material. The “low alkali material” refers to a material having an alkali metal oxide content of about 10 wt. % or less, more preferably about 8 wt. % or less, and more preferably about 5 wt. % or less. However, in some embodiments, relative high alkali materials may still be included in the primary component. The relative high alkali materials may be combined with low alkali primary component(s) so that the resulting primary component still has a sufficiently low overall alkali metal oxide content. Accordingly, waste glass powders, such as soda lime glasses (sometimes referred to as cullet) having an alkali content of up to 15 wt. % may be included in the primary component. However, when combined with other low alkali primary component(s), the overall alkali concentration of the primary component should be about 10 wt. % or less.

[0075] Hitherto, it was believed that relatively large amounts of alkali metal oxides were required to act as a fluxing agent in forming glass microspheres from alkali metal silicates (see, for example, U.S. Pat. No 3,365,315). However, the present inventors have found a method to form synthetic microspheres from commonly available sources of low alkali content aluminosilicate raw materials without the need for large quantities of additional alkali metal oxides. This will be described in greater detail below.

[0076] Aluminosilicate materials are well known to the person skilled in the art. Generally, these are materials having a large component (e.g., greater than about 50 wt. %, preferably greater than about 60 wt. %) of silica (SiO2) and alumina (Al2O3). The amounts of silica and alumina will vary depending on the source and may even vary within the same source. Fly ash, for example, will contain varying amounts of silica and alumina depending on the type of coal used and combustion conditions. However, the skilled person will readily understand those materials classed as “aluminosilicates”.

[0077] In one embodiment, the primary component of the precursor comprises at least one aluminosilicate material, preferably about 80 wt. % or more, or about 90 wt. % or more, based on the weight of the primary component. Typically, aluminosilicate materials for use in the embodiments of the present invention have a composition of about 30 to 85 wt. % SiO2; about 2 to 45 wt. % (preferably about 6 to 45 wt. %) Al2O3; up to about 30 wt. % (preferably up to about 15 wt. %) divalent metal oxides (e.g. MgO, CaO, SrO, BaO); up to about 10 wt. % monovalent metal oxides (e.g. Li2O, Na2O, K2O); and up to about 20 wt. % of other metal oxides, including metal oxides which exist in multiple oxidation states (e.g. TiO2, Fe2O3, etc.) Preferably, the mass ratio of silica (SiO2) to alumina (Al2O3) is greater than about 1 in the aluminosilicate materials used in certain embodiments of the present invention.

[0078] Methods of the present embodiments are not limited to any particular source of aluminosilicate material. However, the primary component preferably comprises at least one aluminosilicate material selected from fly ash (e.g. Type F fly ash, Type C fly ash, etc.), bottom ash, blast-furnace slag, paper ash, basaltic rock, andesitic rock, feldspars, aluminosilicate clays (e.g. kaolinite clay, illite clay, bedalite clay, betonite clay, china, fire clays, etc.) obsidian, diatomaceous earth, volcanic ash, volcanic rocks, silica sand, silica fume, bauxite, volcanic glasses, geopolymers and combinations thereof. More preferably, the primary component comprises fly ash and/or basaltic rock.

[0079] The aluminosilicate material may be either calcined or non-calcined. The term “calcined” means that the aluminosilicate material has been heated in air to a predetermined calcination temperature for a predetermined duration so as to either oxidize or pre-react certain component(s) of the aluminosilicate material. Calcination of the aluminosilicate material may be advantageous in certain embodiments of the present invention since the blowing (expansion) process of the microspheres can be sensitive to the redox state of multivalent oxide(s) present in the aluminosilicate material. Without wishing to be bound by theory, it is believed that activation of the blowing agent is influenced by the release of oxygen from the multivalent oxide(s) present in the aluminosilicate material (e.g., by redox reaction). As an example, a carbonaceous blowing agent may be oxidized to CO2 by ferric oxide (Fe2O3), which is in turn reduced to ferrous oxide (FeO). The release of CO2 from the blowing agent expands the microspheres. Hence, by pre-calcining the aluminosilicate material in air, the relative amount of ferric oxide is increased, which is then used as a source of oxygen for blowing agents to produce more gas, thereby lowering the density of the microspheres.

[0080] In addition, calcination can promote pre-reaction of oxide components and/or cause partial vitrification in the aluminosilicate material, which may be beneficial in the production of high quality synthetic microspheres.

[0081] Fly ash is a particularly preferred aluminosilicate primary component due to its low cost and availability. In one preferred form of the invention, the primary component comprises about 5 wt. % or more fly ash, and more preferably about 10 wt. % fly ash or more, based on the total amount of primary component. In another preferred form, the primary component comprises about 50 wt. % fly ash or more, more preferably about 70 wt. % fly ash or more, and more preferably about 90 wt. % fly ash or more, based on the total amount of primary component. In some embodiments of the present invention, the primary component may be substantially all fly ash. Fly ash may also be used in the form of a fly ash geopolymer, which is formed when fly ash is contacted with an aqueous solution of a metal hydroxide such as sodium hydroxide NaOH or potassium hydroxide KOH. Fly ash geopolymers are well known in the art.

[0082] In certain embodiments, at least one of the aluminosilicate material used preferably comprises an amorphous phase and is either partially or wholly amorphous. In general, a vitrified material is substantially amorphous.

[0083] In certain embodiments, at least one of the aluminosilicate material used preferably has an average primary particle diameter in the range of about 0.01 to 100 microns, more preferably about 0.01 to 100 microns, more preferably about 0.05 to 50 microns, more preferably about 0.1 to 25 microns, and more preferably about 0.2 to 10 microns. Preferred particle diameters may be achieved by appropriate grinding and classification. All types of grinding, milling, and overall size reduction techniques that are used in ceramic industry can be used in embodiments of the present invention. Without limiting to other methods of size reduction used for brittle solids, preferred methods according to embodiments of the present invention are ball milling (wet and dry), high energy centrifugal milling, jet milling, and attrition milling. If more than one aluminosilicate material is to be used, then the multitude of ingredients can be co-ground together. In one method of the present invention, the blowing agent and, optionally the binding agent as will be described in greater detail below, are added to the aluminosilicate material before the milling process. For example all the ingredients can be co-ground together (e.g. in a wet ball mill), which then substantially eliminates the aqueous mixing.

[0084] In an alternative embodiment of the present invention, the primary component may include waste material(s) and/or other glass-forming material(s) in addition to the at least one aluminosilicate material. Typical waste materials or other glass-forming material which may be used in this alternative embodiment include waste glasses (e.g. soda lime glasses, borosilicate glasses or other waste glasses), waste ceramics, kiln dust, waste fiber cement, concrete, incineration ash, or combinations thereof. The total amount of waste material and/or other glass-forming material may be up to about 50 wt. % (e.g. up to about 40 wt. %, up to about 30 wt. %, or up to about 20 wt. %), based on the weight of the primary component. As stated above, it is preferred that the total amount of alkali metal oxide in the primary component mixture of this type to still be less than about 10 wt. %.

[0085] Blowing Agent

[0086] The blowing agent used in embodiments of the present invention is a substance which, when heated, liberates a blowing gas by one or more of combustion, evaporation, sublimation, thermal decomposition, gasification or diffusion. The blowing gas may be, for example, CO2, CO, O2, H2O, N2, N2O, NO, NO2, SO2, SO3, or mixtures thereof. Preferably, the blowing gas comprises CO2 and/or CO.

[0087] Preferably, the blowing agent is selected from powdered coal, carbon black, activated carbon, graphite, carbonaceous polymeric organics, oils, carbohydrates (e.g. sugar, starch, etc.) PVA (polyvinyl alcohol), carbonates, carbides (e.g. silicon carbide, aluminum carbide, and boron carbide, etc.), sulfates, sulfides, nitrides (e.g. silicon nitride, boron nitride, aluminum nitride, etc.), nitrates, amines, polyols, glycols, glycerine or combinations thereof. Carbon black, powdered coal, sugar and silicon carbide are particularly preferred blowing agents.

[0088] Preferably, and particularly if the blowing agent is non-water soluble, the blowing agent has an average particle diameter in the range of about 0.01 to 10 microns, more preferably about 0.5 to 8 microns, and more preferably about 1 to 5 microns.

[0089] Binding Agent

[0090] In preferred embodiment, the agglomerate precursor comprises a binding agent (or binder). The primary function of the binding agent is to bind the particles in the agglomerate together. In some embodiments, the binding agent may act initially to bind particles of the agglomerate together during formation of the agglomerate precursor, and then act as a blowing agent during subsequent firing process.

[0091] In general, any chemical substance that is reactive and/or adheres with the aluminosilicate primary component can be used as the binding agent. The binding agent may be any commercially available material used as a binder in the ceramic industry. Preferably, the binding agent is selected from alkali metal silicates (e.g. sodium silicate), alkali metal aluminosilicate, alkali metal borates (e.g. sodium tetraborate), alkali or alkaline earth metal carbonates, alkali or alkaline earth metal nitrates, alkali or alkaline earth metal nitrites, boric acid, alkali or alkaline earth metal sulfates, alkali or alkaline earth metal phosphates, alkali or alkaline earth metal hydroxides (e.g. NaOH, KOH, or Ca(OH)2), carbohydrates (e.g. sugar, starch, etc.), colloidal silica, inorganic silicate cements, Portland cement, alumina cement, lime-based cement, phosphate-based cement, organic polymers (e.g. polyacrylates) or combinations thereof. In some cases, fly ash, such as ultrafine, Type C or Type F fly ash, can also act as a binding agent.

[0092] The binding agent and blowing agent are typically different from each other, although in some cases (e.g. sugar, starch, etc.) the same substance may have dual blowing/binding agent properties.

[0093] The term “binder” or “binding agent”, as used herein, includes all binding agents mentioned above, as well as the in situ reaction products of these binding agents with other components in the agglomerate. For example, an alkali metal hydroxide (e.g. NaOH) will react in situ with at least part of the aluminosilicate material to produce an alkali metal aluminosilicate. Sodium hydroxide may also form sodium carbonate when exposed to ambient air containing CO2, the rate of this process increasing at higher temperatures (e.g. 400° C.). The resulting sodium carbonate can react with the aluminosilicate material to form sodium aluminosilicate.

[0094] In certain preferred embodiments, the amount of binding agent is in the range of about 0.1 to 50 wt. % based on the total weight of the agglomerate precursor, more preferably about 0.5 to 40 wt. % and more preferably about 1 to 30 wt. %.

[0095] It has been unexpectedly found that the properties of the binder or binding agent, and in particular its melting point, affect the properties of the resulting microspheres. Without wishing to be bound by theory, it is understood by the present inventors that the binder is responsible for forming a molten skin around the agglomerate precursor during or prior to activation of the blowing agent in the firing step as will be described in greater detail below. Hence, in a preferred form of the present invention, the binding agent has a melting point which is lower than the melting point of the whole agglomerate precursor. Preferably, the binding agent has a melting point which is less than about 1200° C., more preferably less than about 1100° C., and more preferably less than about 1000° C. (e.g. 700 to 1000° C.).

[0096] It has also been unexpectedly found that the degree of crystallinity in the binder phase can have a pronounced effect on the formation kinetics of the molten skin. The degree of crystallinity at a given temperature may be readily determined from the phase diagram of oxides present in the mixture. For example, in a simple binary system of SiO2 and Na2O, there are three eutectic points, with the lowest one having a liquidus temperature of about 790° C. and a SiO2 to Na2O ratio of about 3. As sodium oxide concentration is increased, the liquidus temperature increases sharply, to about 1089° C. at a SiO2:Na2O ratio of about 1:1. This is illustrated in FIG. 1, which provides a phase diagram of SiO2—Na2O. Most other alkali metal oxides behave similarly to sodium oxide. For example, the K2O—SiO2 system has also several eutectic points, with the lowest at about 750° C. occurring at a SiO2 to K2 O ratio of about 2.1. Similarly, Li2O has several eutectic points with one at 1028° C. and a ratio of about 4.5.

[0097] In standard glass technology, sodium oxide is known to be a strong fluxing agent. Its addition to silicate glasses lowers the melting point and viscosity of the glass. For example, in a typical soda lime glass composition, there is about 15 wt. % sodium oxide, which lowers the melting temperature of SiO2 from about 1700° C. to less than about 1400° C. However, in melting commercial glasses, enough time is given for the melt to reach the equilibrium concentration throughout the glass mass, normally in the order of hours or longer. Thus, in standard glass technology, sufficient sodium oxide and/or other fluxing agents are added so that the whole melt has the requisite viscosity-temperature characteristics.

[0098] However, without wishing to be bound by theory, it is understood by the present inventors that, under the fast reaction kinetics of firing (with a temperature increase as fast as 2000° C./second), one of the important requirements for rapid formation of a molten skin around the agglomerate precursor is rapid melting of the binder component. Hence, it is preferred that the binder (present as, for example, sodium silicate or sodium aluminosilicate) has a eutectic or near eutectic composition. Preferably, the binder is sodium silicate having a SiO2:Na2O ratio in the range of about 5:1 to about 1:1, more preferably about 4:1 to about 1.5:1, more preferably about 3.5:1 to about 2:1. It will be appreciated that other alkali metal oxides (e.g. Li2O and K2O) can have the same effect in the binder. However, Na2O is preferred due to its low cost.

[0099] It was unexpectedly found that when sodium silicate with an about 1:1 ratio of SiO2:Na2O was used as binder to formulate the agglomerate precursor, relatively dense microspheres with a particle density of about 1 g/cm3 resulted. However, sodium silicate binder with a SiO2:Na2O ratio of about 3:1 resulted in microspheres having a lower density of about 0.7 g/cm3. In both cases, the overall concentration of Na2O relative to the agglomerate was substantially the same. Under the principles of traditional glass-making technology, it would have been expected that there would be little or no difference in the final products when using the same amount of fluxing agent. However, the present inventors have found that using a eutectic or near eutectic composition in the binder, a molten skin is formed rapidly during firing, and low density microspheres result, irrespective of the total amount of fluxing agent in the agglomerate.

[0100] Equally unexpected, it was found that sodium hydroxide showed substantially the same trend. Sodium oxide, when used as a binder, reacts with silica present in aluminosilicate powders to form a compound of sodium silicate. As more sodium hydroxide is added, the ratio of silica to sodium oxide is lowered, resulting in binders with progressively higher melting temperatures.

[0101] Furthermore, the properties of the synthetic microspheres may also be dependent on the drying temperature of the agglomerate, and to some extent, the pressure. For example, a high drying temperature favors formation of sodium silicate having a lower SiO2:Na2O ratio, thereby giving a binder having a higher melting temperature. For example, about 5 wt. % of NaOH was found to be an appropriate amount of binder for forming low density microspheres when the agglomerate was dried at about 50° C. However, a substantially identical formulation resulted in higher density microspheres when the agglomerate was dried at about 400° C. It was surprisingly found that, when the agglomerate was dried at about 400° C., a lower concentration of NaOH (e.g. about 2-3 wt. %) was required to produce low density microspheres.

[0102] Traditionally, it was believed that a relatively high amount (e.g. 15 wt. %) of sodium oxide was necessary in glass-making technology to act as a fluxing agent. However, in certain embodiments of the present invention, it was surprisingly found that relatively high amounts of sodium oxide are actually less preferred.

[0103] The agglomerate precursor may also include surfactants, which assist in dispersion of the agglomerate precursor components into an aqueous solution or paste. The surfactants may be anionic, cationic or non-ionic surfactants.

[0104] As described the above, once the agglomerate precursor is formed, it is fired at a predetermined temperature profile sufficient to seal the surface of the precursor and activate the blowing agent.

[0105] Methods of Forming the Synthetic Microspheres

[0106] As described above, the synthetic microspheres of certain preferred embodiments can be formed by first combining the primary component with a binding agent and a blowing agent so as to form an agglomerate precursor in a manner to be described in greater detail below. For the formation of substantially solid microspheres, the blowing agent can be left out. The agglomerate precursor is then fired at a pre-determined temperature profile sufficient to activate the blowing agent to release a blowing gas, thereby forming a microsphere with at lease one substantially enclosed void. In embodiments for forming solid synthetic microspheres, the agglomerate precursor is fired at a pre-determined temperature profile that will adequately combine the primary component with the binding agent.

[0107] In certain preferred embodiments, the temperature profile used in the firing step substantially fuses the precursor into a melt, reduces the viscosity of the melt, seals the surface of the precursor and promotes expansive formation of gas within the melt to form bubbles. The temperature profile preferably should maintain the melt at a temperature and time sufficient to allow gas bubbles to coalesce and form a primary void. After foaming or formation of the primary void, the newly expanded particles are rapidly cooled, thus forming hollow glassy microspheres. In one embodiment, the temperature profile is preferably provided by a furnace having one or more temperature zones, such as a drop tube furnace, a vortex type furnace, a fluidized bed furnace or a fuel fired furnace, with upward or downward draft air streams. A fuel fired furnace used in certain preferred embodiments of the present invention includes furnace types in which agglomerated precursors are introduced directly into one or a multitude of combustion zones, to cause expansion or blowing of the particles. This is a preferred type of furnace, since the particles benefit by direct rapid heating to high temperatures, which is desirable. The heat source may be electric or provided by burning fossil fuels, such as natural gas or fuel oil. One preferred method of heating is by combustion of natural gas, since this is more economical than electric heating and cleaner than burning fuel oil.

[0108] Typically, the peak firing temperature in the firing step is in the range of about 600 to 2500° C., more preferably about 800 to 2000° C., more preferably about 1000 to 1500° C., and more preferably about 1100 to 1400° C. However, it will be appreciated that the requisite temperature profile will typically depend on the type of aluminosilicate primary component and blowing agent used. Preferably, the exposure time to the peak firing temperatures described above will be for a period of about 0.05 to 20 seconds, more preferably about 0.1 to 10 seconds.

[0109] Method of Forming Azzlomerate Precursor

[0110] As described above, preferred embodiments of the present invention also provide methods of preparing an agglomerate precursor that is suitable for forming a synthetic hollow microsphere therefrom. FIG. 2 provides a schematic illustration of one preferred method 200 of forming the agglomerate precursor.

[0111] As shown, in FIG. 2, the method 200 begins with Step 202, which comprises providing a primary component of a predetermined size. Preferably, the primary component comprises at least one aluminosilicate material. Preferably, the amount of primary component is greater than about 40 wt. % based on the total dry weight of the agglomerate precursor. Preferably, the amount of blowing agent is less than about 10 wt. % based on the total dry weight of the agglomerate precursor. Further preferred forms of the primary component and blowing agent are described above.

[0112] As shown in FIG. 2, the method 200 continues with Step 204, which comprises mixing the primary component with a blowing agent in water. In certain preferred embodiments, a binding agent is additionally mixed with the primary component and the blowing agent in Step 204. Preferably, the amount of binding agent is in the range of about 0.1 to 50 wt. %, based on the total dry weight of the agglomerate precursor. Further preferred forms of the binding agent are described above.

[0113] Other additives (e.g. surfactants) may also be added in the mixing Step 204, as appropriate. Surfactants may used to assist with mixing, suspending and dispersing the particles. Typically, Step 204 provides an aqueous dispersion or paste, which is dried in subsequent steps. Mixing can be performed by any conventional means, such that those used to blend ceramic powders. Examples of preferred mixing techniques include, but are not limited to, agitated tanks, ball mills, single and twin screw mixers, and attrition mills.

[0114] Subsequent to the mixing process in Step 204, the method 200 continues with Step 206, in which the mixture is dried. Drying may be performed at a temperature in the range of about 30 to 600° C. and may occur over a period of up to about 48 hours, depending on the drying technique employed. Any type of dryer customarily used in industry to dry slurries and pastes may be used. Drying may be performed in a batch process using, for example, a stationary dish or container. Alternatively, drying may be performed in a fluid bed dryer, rotary dryer, rotating tray dryer, spray dryer or flash dryer. Alternatively, drying may also be performed using a microwave oven. It will be readily appreciated that the optimum drying period will depend on the type of drying method employed.

[0115] When drying is performed in a stationary dish or container, it is preferred that the drying temperature is initially not set too high in order to avoid water in the mixture boiling violently and thus spewing solids out of the drying container. In this case, the drying temperature, at least initially, is preferably in the range of about 30 to 100° C., and more preferably about 40 to 80° C. to avoid initial, rapid boiling of water. However, after initial evaporation of water, the drying temperature may be increased to temperatures up to about 350° C., which completes the drying process more speedily.

[0116] As shown in FIG. 2, the method 200 of forming the agglomerate precursor further includes Step 208, which comprises comminuting the dried mixture from Step 206 to form agglomerate precursor particles of a predetermined particle diameter range. However, in some embodiments, the drying Step 206 and comminuting Step 208 may be performed in a single step. Preferably, the dried mixture is comminuted to provide agglomerate precursor particles having an average particle diameter in the range of about 10 to 1000 microns, more preferably about 30 to 1000 microns, more preferably about 40 to 500 microns, and more preferably about 50 to 300 microns. The particle diameter of the agglomerate precursor will affect the particle diameter of the resultant synthetic hollow microsphere, although the degree of correspondence will, of course, only be approximate.

[0117] It is preferred that preferred embodiments of the present invention provide synthetic hollow microspheres having a controlled particle diameter distribution. Accordingly, the comminuted agglomerate precursor may be classified to a predetermined particle diameter distribution. Alternatively, a controlled particle diameter distribution in the agglomerate precursor may be achieved by the use of spray dryer in the drying Step 206. Spray drying has the additional advantage of allowing a high throughput of material and fast drying times. Hence, in one preferred embodiment of the present invention, the drying Step 206 is performed using a spray dryer. Spray dryers are described in a number of standard textbooks (e.g. Industrial Drying Equipment, C. M. van't Land; Handbook of Industrial Drying 2nd Edition, Arun S. Mujumbar) and will be well known to the skilled person. The use of a spray dryer in the present invention has been found to substantially eliminate the need for any sizing/classification of the agglomerate precursor.

[0118] Preferably, the aqueous slurry feeding the spray dryer comprises about 20 to 90 wt. % solids, more preferably about 25 to 75 wt. % solids, and more preferably about 60 to 70 wt. % solids. In addition to the agglomerate ingredients described above, the slurry may contain further processing aids or additives to improve mixing, flowability or droplet formation in the spray dryer. Suitable additives are well known in the spray drying art. Examples of such additives are sulphonates, glycol ethers, hydrocarbons, cellulose ethers and the like. These may be contained in the aqueous slurry in an amount ranging from about 0 to 5 wt. %.

[0119] In the spray drying process, the aqueous slurry is typically pumped to an atomizer at a predetermined pressure and temperature to form slurry droplets. The atomizer may be, for example, an atomizer based on a rotating disc (centrifugal atomization), a pressure nozzle (hydraulic atomization), or a two-fluid pressure nozzle wherein the slurry is mixed with another fluid (pneumatic atomization). The atomizer may also be subjected to cyclic mechanical or sonic pulses. The atomization may be performed from the top or from the bottom of the dryer chamber. The hot drying gas may be injected into the dryer co-current or counter-current to the direction of the spraying.

[0120] The atomized droplets of slurry are dried in the spray dryer for a predetermined residence time. Typically, the residence time in the spray dryer is in the range of about 0.1 to 10 seconds, with relatively long residence times of greater than about 2 seconds being generally more preferred. Preferably, the inlet temperature in the spray dryer is in the range of about 300 to 600° C. and the outlet temperature is in the range of about 100 to 220° C.

[0121] Use of Synthetic Hollow Microspheres

[0122] The synthetic hollow microspheres according preferred embodiments of the present invention may be used in a wide variety of applications, for example, in filler applications, modifier applications, containment applications or substrate applications. The scope of applications is much greater than that of harvested cenospheres due to the low cost and consistent properties of synthetic microspheres.

[0123] Synthetic microspheres according to the present invention may be used as fillers in composite materials, where they impart properties of cost reduction, weight reduction, improved processing, performance enhancement, improved machinability and/or improved workability. More specifically, the synthetic microspheres may be used as fillers in polymers (including thermoset, thermoplastic, and inorganic geopolymers), inorganic cementitious materials (including material comprising Portland cement, lime cement, alumina-based cements, plaster, phosphate-based cements, magnesia-based cements and other hydraulically settable binders), concrete systems (including precise concrete structures, tilt up concrete panels, columns, suspended concrete structures etc.), putties (e.g. for void filling and patching applications), wood composites (including particleboards, fibreboards, wood/polymer composites and other composite wood structures), clays, and ceramics. One particularly preferred use of the microspheres according to the present invention is in fiber cement building products.

[0124] The synthetic microspheres may also be used as modifiers in combination with other materials. By appropriate selection of size and geometry, the microspheres may be combined with certain materials to provide unique characteristics, such as increased film thickness, improved distribution, improved flowability etc. Typical modifier applications include light reflecting applications (e.g. highway markers and signs), industrial explosives, blast energy absorbing structures (e.g. for absorbing the energy of bombs and explosives), paints and powder coating applications, grinding and blasting applications, earth drilling applications (e.g. cements for oil well drilling), adhesive formulations and acoustic or thermal insulating applications.

[0125] The synthetic microspheres may also be used to contain and/or store other materials. Typical containment applications include medical and medicinal applications (e.g. microcontainers for drugs), micro-containment for radioactive or toxic materials, and micro-containment for gases and liquids.

[0126] The synthetic microspheres may also be used in to provide specific surface activities in various applications where surface reactions are used (i.e. substrate applications). Surface activities may be further improved by subjecting the synthetic microspheres to secondary treatments, such as metal or ceramic coating, acid leaching etc. Typical substrate applications include ion exchange applications (for removing contaminants from a fluid), catalytic applications (in which the surface of the microsphere is treated to serve as a catalyst in synthetic, conversion or decomposition reactions), filtration (where contaminants are removed from gas or liquid streams), conductive fillers or RF shielding fillers for polymer composites, and medical imaging.

[0127] In one embodiment, the synthetic microspheres of preferred embodiments of the present invention are incorporated in a building material. The synthetic microspheres can be incorporated in a composite building material as an additive, low density filler, and/or the like. In one embodiment, the synthetic hollow microspheres are incorporated in a cementitious material. Due in large part to the low alkali metal oxide content (e.g. less than 10 wt. %) of the synthetic microspheres, the microspheres are substantially chemically inert when in contact with the caustic cementitious material.

[0128] The synthetic microspheres of preferred embodiments can be incorporated in a building material formulation comprising a hydraulic binder, one or more fibers (e.g cellulose fibers) Advantageously, the synthetic microspheres can serve as a substitute for harvested cenospheres in all applications because of the synthetic microspheres have substantially the same properties as the cenospheres.

[0129] However, in certain embodiments, the synthetic microspheres can be manufactured with properties that are superior to that of harvested cenospheres. For example, in some embodiments, the average aspect ratio of the synthetic microspheres is closer to 1 than the average aspect ratio of natural cenospheres, thus providing a microsphere that is more spherical. Moreover, in some embodiments, the average standard deviation of the wall thickness of the synthetic hollow microspheres is less than that of cenospheres, which provides a product with a more uniform appearance. These improved properties are achieved through controlling the processing conditions and raw material in manufacturing the microspheres.

[0130] The following examples illustrate some preferred methods of making the synthetic hollow microspheres of preferred embodiments of the present invention.

EXAMPLE 1

[0131] This example illustrates a method of making synthetic microspheres from formulations comprising fly ash, sodium silicate, and sugar.

[0132] Three samples were made by mixing a type F fly ash (ground to an average size of about 5.4 microns) with a commercial grade sodium silicate solution (SiO2/Na2O is about 3.22, about 40% solid content), a commercial grade sugar, and water. The amounts of ingredients are given in Table 1. The composition of fly ash is given in Table 2. The mixtures were blended into homogeneous slurry, poured into a flat dish and allowed to solidify at room temperature for about 5 minutes.

[0133] The resulting products were further dried at about 50° C. for about 20 hours, after which they were ground and sieved to obtain powders within a size range of about 106 to 180 microns. In the next step, for each sample, the powders were fed into a vertical heated tube furnace at an approximate feed rate of about 0.14 grams/min. The gas flow inside the tube furnace was about 1 litre of air plus 3 litres of nitrogen per minute. The constant temperature zone of the furnace was adjusted to provide residence times from less than a second to approximately a few seconds at the peak firing temperatures. The foamed microspheres were collected on a funnel shaped collecting device covered with a fine mesh screen positioned at the bottom part of the furnace. A mild suction was applied to the end of funnel to aid in collecting the microspheres. The products were characterized for particle density (e.g. apparent density), percent of water flotation, and approximate particle diameter distribution. The results for various firing temperatures and residence times are summarized in Table 3. FIGS. 3 to 5 show the cross sections of the products.

TABLE 1
		Sodium silicate
Sample No.	Fly ash	solution	Sugar	Water
1	93.1	58.0	3.6	7.0
2	104.8	29.1	3.6	19.2
3	108.0	21.0	3.6	21.0
All masses are in grams

[0134]

TABLE 2
LOI	SiO2	Al2O3	Fe2O3	CaO	MgO	SO3	Na2O	K2O	TiO2	Mn2O3	P2O5	Total
0.39	50.63	21.14	7.62	12.39	3.61	0.66	0.63	1.27	1.30	0.17	0.14	99.95
All amounts are in percentage of weight

[0135]

	TABLE 3
	Residence	Apparent	Water	Size of
Sample	Temperature	time	density	float	microspheres
No.	(degree C.)	(second)	(g/cm3)	(%)	(micron)
1	1300	0.6-1.1	0.64	81	100-275
1	1300	0.8-1.5	0.78
2	1300	0.6-1.1	0.87	55	110-240
3	1300	0.6-1.1	1.05		75-225

EXAMPLE 2

[0136] This example illustrates a method of making synthetic microspheres from formulations comprising fly ash, sodium silicate, and carbon black.

[0137] Three samples were made by mixing a type F fly ash (ground to an average size of about 5.4 microns) with a commercial grade sodium silicate solution (SiO2/Na2O is about 3.22, about 40% solid content), a commercial grade carbon black, and water. The amounts of ingredients are given in Table 4. The composition of fly ash is given in Table 2. Each mixture was blended into homogeneous slurry, poured into a flat dish and allowed to solidify at room temperature for about 5 minutes. The resulting products were further dried at about 50° C. for about 20 hours, after which they were ground and sieved to obtain powders within a size range of 106 to 180 microns. In the next step, for each sample, the powders were fed into a vertical heated tube furnace at an approximate feed rate of about 0.14 grams/min. The gas flow inside the tube furnace is about 1 litre of air plus 3 litres of nitrogen per minute. The constant temperature zone of the furnace was adjusted to provide residence times from less than a second to approximately a few seconds at the peak firing temperatures. The foamed microspheres were collected on a funnel shaped collecting device covered with a fine mesh screen positioned at the bottom part of the furnace. A mild suction was applied to the end of funnel to aid in collecting the microspheres. The products were characterized for particle density (e.g. apparent density), percent of water floatation, and approximate particle diameter distribution. The results for various firing temperatures and residence times are summarized in Table 5. FIGS. 6 to 8 show the cross sections of the products.

TABLE 4
		Sodium silicate
Sample No.	Fly ash	solution	Carbon black	Water
4	95.0	59.0	1.2	7.1
5	100.8	45.0	1.2	18.4
6	106.8	30.0	1.2	30.1
All masses are in grams

[0138]

	TABLE 5
	Residence	Apparent	Water	Size of
Sample	Temperature	time	density	float	microspheres
No.	(degree C.)	(second)	(g/cm3)	(%)	(micron)
4	1300	0.6-1.1	0.87	70	100-275
5	1300	0.6-1.1	0.75	71	100-275
6	1300	0.6-1.1	0.86	67	110-260

EXAMPLE 3

[0139] This example illustrates a method of making synthetic microspheres form formulations comprising fly ash, sodium hydroxide, and carbon black.

[0140] Three samples were made by mixing a type F fly ash (ground to an average size of about 5.4 microns) with a commercial grade solid sodium hydroxide (flakes), a commercial grade carbon black, and water. The amounts of ingredients are given in Table 6. The composition of fly ash is given in Table 2. Each mixture was blended into homogeneous slurry, poured into a flat dish and allowed to solidify at room temperature for about 5 minutes. The resulting products were further dried at about 50° C. for about 20 hours, after which it was ground and sieved to obtain powders within a size range of about 106 to 180 microns. In the next step, the powders were fed into a vertical heated tube furnace at an approximate feed rate of about 0.14 grams/min. The gas flow inside the tube furnace is about 1 litre of air plus 3 litres of nitrogen per minute. The constant temperature zone of the furnace was adjusted to provide residence times from less than a second to approximately few seconds at the peak firing temperatures. The foamed microspheres were collected on a funnel shaped collecting device covered with a fine mesh screen positioned at the bottom part of the furnace. A mild suction was applied to the end of funnel to aid in collecting the microspheres. The products were characterized for particle density (e.g. apparent density), percent of water floatation, and approximate particle diameter distribution. The results are summarized in Table 7. FIG. 9 shows the cross section of the product obtained from Sample 7.

TABLE 6
Sample No.	Fly ash	Sodium hydroxide	Carbon black	Water
7	112.8	6.0	1.2	39.5
8	116.4	2.4	1.2	46.6
9	117.6	1.2	1.2	47.0
All masses are in grams

[0141]

	TABLE 7
	Residence	Apparent	Water	Size of
Sample	Temperature	time	density	float	microspheres
No.	(degree C.)	(second)	(g/cm3)	(%)	(micron)
7	1300	0.6-1.1	0.65	77	85-290
8	1300	0.6-1.1	0.76
9	1300	0.6-1.1	0.78	66

EXAMPLE 4

[0142] This example illustrates a method to make synthetic microspheres form formulations consisting of fly ash, basalt, sodium hydroxide, and carbon black.

[0143] About 94 grams of a type F fly ash and basalt co-ground to an average size of about 1 micron were mixed with about 5 grams of solid sodium hydroxide (flakes), about 1 gram of a commercial grade carbon black, and about 38 ml of water. Several samples were made by changing the proportions of basalt to fly ash as shown in Table 8. The compositions of fly ash and basalt are given in Tables 2 and 9 respectively. Each mixture was blended into an homogeneous slurry, poured into a flat dish and allowed to solidify at room temperature for about 5 minutes. The resulting product was further dried at about 50° C. for about 20 hours, after which it was ground and sieved to obtain powders within a size range of about 106 to 180 microns. In the next step, the powders were fed into a vertical heated tube furnace at an approximate feed rate of about 0.14 grams/min. The gas flow inside the tube furnace is about 1 litre of air plus 3 litres of nitrogen per minute. The constant temperature zone of the furnace was adjusted to provide residence times from less than a second to approximately few seconds at the peak firing temperatures. The foamed microspheres were collected on a funnel shaped collecting device covered with a fine mesh screen positioned at the bottom part of the furnace. A mild suction was applied to the end of funnel to aid in collecting the microspheres. The products were characterized for particle density (e.g. apparent density), percent of water floatation, and approximate particle diameter distribution. The results are summarized in Table 10. FIGS. 10 and 11 show the cross section of the products of Samples 12 and 13 respectively.

TABLE 8
Sample	Fly		Sodium	Carbon
No.	ash	Basalt	hydroxide	black	Water
10	75.2	18.8	5.0	1.0	38.0
11	56.4	37.6	5.0	1.0	38.0
12	37.6	56.4	5.0	1.0	38.0
13	18.8	75.2	5.0	1.0	38.0
All masses are in grams

[0144]

TABLE 9
LOI	SiO2	Al2O3	Fe2O3	CaO	MgO	SO3	Na2O	K2O	TiO2	Mn2O3	P2O5	Total
0	46.13	15.81	9.50	9.50	9.60	0	2.78	1.53	2.38	0.25	0.59	98.07
All amounts are in percentage of weight

[0145]

	TABLE 10
	Residence	Apparent	Water	Size of
Sample	Temperature	time	density	float	microspheres
No.	(degree C.)	(second)	(g/cm3)	(%)	(micron)
10	1300	0.8-1.5	0.76	62
11	1300	0.8-1.5	0.77	63
12	1300	0.8-1.5	0.76	65	100-250
13	1300	0.8-1.5	1.00	44	100-225

EXAMPLE 5

[0146] This example illustrates a method to make synthetic microspheres form a formulation comprising basalt, sodium hydroxide, and silicon carbide.

[0147] About 93.5 grams of basalt ground to an average size of about 1 micron was mixed with about 5 grams of a commercial grade solid sodium hydroxide (flakes), about 1.5 grams of a commercial grade silicon carbide, and about 37.4 ml of water. The composition of basalt is given in table 9. The mixture was blended into homogeneous slurry, poured into a flat dish and allowed to solidify at room temperature for about 5 minutes. The resulting product was further dried at about 50° C. for about 20 hours, after which it was ground sieved to obtain powders within a size range of about 106 to 180 microns. In the next step, the powders were fed into a vertical heated tube furnace at an approximate feed rate of about 0.14 grams/min. The gas flow inside the tube furnace is about 1 litre of air plus 3 litres of nitrogen per minute. The constant temperature zone of the furnace was adjusted to provide residence times from less than a second to approximately few seconds at the peak firing temperatures. The foamed microspheres were collected on a funnel shaped collecting device covered with a fine mesh screen positioned at the bottom part of the furnace. A mild suction was applied to the end of funnel to aid in collecting the microspheres. The products were charaterized for particle density (e.g. apparent density), percent of water floatation, and approximate particle diameter distribution. The results for various firing temperatures and residence times are summarized in Table 11. FIGS. 12-14 show the cross section of the products.

TABLE 11
			Water	Size of
Temperature	Residence	Apparent density	float	microspheres
(degree C.)	time (second)	(g/cm3)	(%)	(micron)
1300	0.6-1.1	0.61
1250	0.6-1.1	0.56	86	130-260
1200	0.6-1.1	0.59		85-195
1150	0.6-1.1	1.21		105-240

EXAMPLE 6

[0148] This example illustrates a method to make synthetic microspheres form a formulation comprising fly ash, sodium hydroxide, and silicon carbide.

[0149] About 93.5 grams of a type F fly ash ground to an average size of about 1.3 microns was mixed with about 5 grams of solid sodium hydroxide (flakes), about 1.5 grams of a commercial grade silicon carbide, and about 37.4 ml of water. The composition of the fly ash is given in Table 2. The mixture was blended into homogeneous slurry, poured into a flat dish and allowed to solidify at room temperature for about 5 minutes. The resulting product was further dried at about 50° C. for about 20 hours, after which it was ground and sieved to obtain powders within a size range of about 106 to 180 microns. In the next step, the powders were fed into a vertical heated tube furnace at an approximate feed rate of about 0.14 grams/min. The gas flow inside the tube furnace is about 1 litre of air plus 3 litres of nitrogen per minute. The constant temperature zone of the furnace was adjusted to provide residence times from less than a second to approximately few seconds at the peak firing temperatures. The foamed microspheres were collected on a funnel shaped collecting device covered with a fine mesh screen positioned at the bottom part of the furnace. A mild suction was applied to the end of funnel to aid in collecting the microspheres. The products were characterized for particle density (e.g. apparent density), percent of water floatation, and approximate particle diameter distribution. The results for various firing temperatures and residence times are summarized in Table 12. FIGS. 15 and 16 show the cross section of the products.

TABLE 12
LOI	SiO2	Al2O3	Fe2O3	CaO	MgO	SO3	Na2O	K2O	TiO2	Mn2O3	P2O5	Total
0.40	61.53	17.91	4.72	7.30	2.91	0.40	2.16	1.39	0.86	0.08	0.28	99.94
All amounts are in percentage of weight

[0150]

TABLE 12
			Water	Size of
Temperature	Residence	Apparent density	float	microspheres
(degree C.)	time (second)	(g/cm3)	(%)	(micron)
1400	0.6-1.1	0.52	83
1300	0.6-1.1	0.49	96	130-280
1250	0.6-1.1	0.58		105-220

EXAMPLE 7

[0151] This example illustrates a method to make synthetic microspheres form a formulation comprising fly ash, sodium hydroxide, silicon carbide as a primary blowing agent and carbon black a secondary blowing agent.

[0152] About 93.8 grams of a type F fly ash ground to an average size of about 1.3 microns was mixed with about 5 grams of solid sodium hydroxide (flakes), about 0.2 grams of a commercial grade silicon carbide, about 1 gram of commercial grade carbon black, and about 37.5 ml of water. The composition of the fly ash is given in Table 2. The mixture was blended into homogeneous slurry, poured into a flat dish and allowed to solidify at room temperature for about 5 minutes. The resulting product was further dried at about 50° C. for about 20 hours, after which it was ground and sieved to obtain powders within a size range of about 106 to 180 microns. In the next step, the powders were fed into a vertical heated tube furnace at an approximate feed rate of about 0.14 grams/min. The gas flow inside the tube furnace is about 1 litre of air plus 3 litres of nitrogen per minute. The constant temperature zone of the furnace was adjusted to provide residence times from less than a second to approximately few seconds at the peak firing temperatures. The foamed microspheres were collected on a funnel shaped collecting device covered with a fine mesh screen positioned at the bottom part of the furnace. A mild suction was applied to the end of funnel to aid in collecting the microspheres. The products were characterized for particle density (e.g. apparent density), percent of water floatation, and approximate particle diameter distribution. The result is summarized in Table 13. FIG. 17 shows the cross section of the product.

TABLE 12
			Water	Size of
Temperature	Residence	Apparent density	float	microspheres
(degree C.)	time (second)	(g/cm3)	(%)	(micron)
1300	0.6-1.1	0.65	82	105-220

EXAMPLE 8

[0153] The compositions (percentage of weight) of synthetic microspheres (“A” and “B”) according to one preferred embodiment of the present invention were compared with a sample of commercially available harvested cenospheres. The results are shown in Table 13.

TABLE 13
	Harvested	Synthetic	Synthetic
Major Oxides	Cenosphere	Microsphere “A”	Microsphere “B”
SiO2	62.5	58.9	65.8
Al2O3	25.2	17.1	12.8
Fe2O3	3.7	4.5	3.3
CaO	1.1	7.0	5.2
MgO	1.7	2.8	2.0
Na2O	1.1	5.2	6.8
K2O	1.9	1.3	1.0
SO3	0.5	0.4	0.3
Others	2.3	2.8	2.8

EXAMPLE 9

[0154] This example shows typical spray drying conditions used to produce agglomerate precursors in certain preferred embodiments of the present invention.

[0155] Dryer: Bowen Engineering, Inc. No 1 Ceramic Dryer fitted with a two-fluid nozzle type 59-BS

[0156] Air nozzle pressure: about 20 psi

[0157] Cyclone vacuum: about 4.5

[0158] Inlet/Outlet temperature: about 550° C./120° C.

[0159] Chamber vacuum: about 1.6

[0160] Slurry solids: about 50%

[0161] Agglomerate precursors produced using these spray drying conditions had a suitable average particle diameter and particle diameter distribution for forming synthetic hollow microspheres therefrom.

[0162] It will be appreciated that embodiments of the present invention have been described by way of example only and the modifications of detail within the scope of the invention will be readily apparent to those skilled in the art.

[0163] One preferred method of the present invention advantageously provides a means for producing microspheres in high yield from widely available and inexpensive starting materials, such as fly ash, natural rocks and minerals. Hence, the method, in its preferred forms, reduces the overall cost of producing microspheres, and consequently increases the scope for their use, especially in the building industry where the use of presently available cenospheres is relatively limited due to their prohibitive cost and low availability. Hitherto, it was not believed that hollow microspheres could be formed synthetically from waste aluminosilicate materials, such as fly ash.

[0164] A further advantage of one embodiment of the present invention, in its preferred form, is that the microspheres produced may be tailor-made to suit a particular purpose. For example, the size, density and composition of the microspheres may be modified, as required, by modifying the relative amounts of ingredients and/or the temperature profile/exposure time during formation.

[0165] Still a further advantage of one embodiment of the present invention, in its preferred form, is that the microspheres produced have acceptably high chemical durability and can withstand, for example, a highly caustic environment of pH about 12-14 for up to about 48 hours. Thus, microspheres produced according to one preferred embodiment of the present invention can withstand aqueous cementitious environments, such as Portland cement paste.

[0166] Moreover, in most cases, fiber cement products are cured for up to 24 hours in an autoclave that is maintained at temperatures as high as 250° C. Microspheres produced according to one preferred embodiment of the present invention lose minimal amount of mass to dissolution, such as by leaching of silica, retain their shape, and continue to have high mechanical strength in fiber cement products, even after exposure to harsh autoclaving conditions.

[0167] Although the foregoing descriptions of certain preferred embodiments of the present invention have shown, described and pointed out some fundamental novel features of the invention, it will be understood that various omissions, substitutions, and changes in the form of the detail of the apparatus as illustrated as well as the uses thereof, may be made by those skilled in the art, without departing from the spirit of the invention. Consequently, the scope of the present invention should not be limited to the foregoing discussions.

Claims

1. A synthetic microsphere, comprising: a synthetic, substantially spherical wall; wherein the microsphere has a particle diameter of greater than about 30 microns, wherein the microsphere comprises a pre-determined amount of at least one aluminosilicate material and at least one pre-selected chemical, wherein the microsphere has an alkali metal oxide content of less than about 10 wt. %, based on the weight of the microsphere.

2. The synthetic microsphere of claim 1, wherein the substantially spherical wall defines at least one inner void, wherein the at least one inner void is synthetically formed by a pre-determined amount of a blowing agent.

3. The synthetic microsphere of claim 2, wherein the blowing agent is selected from the group consisting of powdered coal, carbon black, graphite, carbonaceous polymeric organics, oils, sugar, starch, polymeric organic oils, polyvinyl alcohol, carbonates, carbides, sulfates, sulfides, nitrides, nitrates, glycol, glycerine, and combinations thereof.

4. The synthetic microsphere of claim 2, wherein the at least one inner void has a volume of between about 30-95% of the aggregate volume of the microsphere.

5. The synthetic microsphere of claim 1, wherein the synthetic substantially spherical wall has a make-up comprising an aluminosilicate material and the at least one pre-selected chemical, wherein the at least one pre-selected chemical acts as a binding agent.

6. The synthetic microsphere of claim 5, wherein the at least one pre-selected binding agent is selected from the group consisting of alkali metal silicates, alkali metal aluminosilicates, alkali metal borates, alkali or alkaline earth metal carbonates, alkali or alkaline earth metal nitrates, alkali or alkaline earth metal nitrites, boric acid, alkali or alkaline earth metal sulfates, alkali or alkaline earth metal phosphates, alkali or alkaline earth metal hydroxides, sugar, starch, ultra fine fly ash, Class C fly ash, Class F fly ash, colloidal silica, inorganic silicate cements, organic polymers, and combinations thereof.

7. The synthetic microsphere of claim 1, wherein the alkali metal oxide content of the microsphere is between about 2 to 10 wt. %.

8. The synthetic microsphere of claim 1, wherein the microsphere is formulated to be substantially chemically inert in a caustic environment having a pH of about 12-14.

9. The synthetic microsphere of claim 1, wherein the particle diameter of the microsphere is between about 30 to 1000 microns.

10. The synthetic microsphere of claim 1, further comprising an aspect ratio of between about 0.8 and 1.

11. The synthetic microsphere of claim 1, further comprising a wall thickness of between about 1 to 100 microns.

12. The synthetic microsphere of claim 1, wherein the particle density of the microsphere is between about 0.1 and 2 g/cm3.

13. The synthetic microsphere of claim 1, wherein the bulk density of the microsphere is less than about 1.4 g/cm3.

14. The synthetic microsphere of claim 1, further comprising a composition of about 30 to 85 wt. % SiO2, about 2 to 45 wt. % Al2O3, and up to about 30 wt. % divalent material oxides, and up to about 20 wt. % of one or more metal oxides.

15. A synthetic microsphere comprising an outer wall defining a substantially enclosed synthetically formed cavity, wherein the microsphere comprises a material formed with a pre-selected formulation, wherein the formulation is configured to provide the microsphere with an alkali metal oxide content of less than about 10 wt. % based on the weight of the microsphere, wherein the average particle diameter of the synthetic microsphere is greater than about 30 microns.

16. The synthetic microsphere of claim 15, wherein the pre-selected formulation comprises an aluminosilicate material.

17. The synthetic microsphere of claim 16, wherein the pre-selected formulation comprises about 30 to 80 wt. % SiO2, about 2 to 45 wt. % Al2O3, up to about 30 wt. % divalent metal oxide, up to about 10 wt. % monovalent metal oxide, and up to about 20 wt. % of one or more metal oxides.

18. The synthetic microsphere of claim 15, wherein the microsphere comprises about 1 to 10 wt. % sodium oxide.

19. The synthetic microsphere of claim 15, wherein the mass ratio of silica to alumina is greater than unity.

20. The synthetic microsphere of claim 15, wherein the average particle diameter of the microsphere is between about 30 and 1000 microns.

21. The synthetic microsphere of claim 15, wherein the average particle diameter of the microsphere is between about 50 and 300 microns.

22. The synthetic microsphere of claim 16, wherein the aluminosilicate material is calcined.

23. The synthetic microsphere of claim 16, wherein the aluminosilicate material is derived from fly ash.

24. A plurality of synthetic microspheres comprising an alkali metal oxide content of less than about 10 wt. % based on the total weight of the microspheres, wherein the synthetic microspheres are formulated to have a pre-selected average particle diameter of greater than about 30 microns.

25. The synthetic microspheres of claim 24, wherein the synthetic microspheres are formulated from aluminosilicate particles, wherein the particles have a pre-selected size range.

26. The synthetic microspheres of claim 25, wherein the aluminosilicate particles have a pre-selected average particles size range of about 0.01 to 50 microns.

27. The synthetic microspheres of claim 24, wherein each synthetic microsphere has a substantially spherical outer wall defining a synthetically formed, substantially enclosed cavity therein.

28. A formulation for forming a synthetic microsphere, comprising: a primary component comprising at least one aluminosilicate component having a particle diameter pre-selected to form a microsphere with a particle diameter greater than about 30 microns; at least one chemical, wherein the at least one chemical comprises a binding agent that substantially binds the particles of the primary component together so as to form a precursor to make the synthetic microspheres; wherein the primary component and the at least one chemical each having a sufficiently low or no alkali metal oxide content so as to maintain the alkali metal oxide content of the synthetic microsphere to less than about 10 wt. %.

29. The formulation of claim 28, further comprising a blowing agent, wherein the blowing agent can be combined with the primary component and the binding agent in a manner such that when activated, the blowing agent releases a gas that expands the precursor so as to form a substantially spherical wall enclosing a cavity therein.

30. The formulation of claim 29, wherein the primary component comprises fly ash and the blowing agent is selected from the group consisting of carbon black, powdered coal, sugar, silicon carbide.

31. The formulation of claim 29, wherein the primary component comprises basalt and the blowing agent is selected from the group consisting of carbon black, powdered coal, sugar, and silicon carbide.

32. The formulation of claim 28, wherein the at least one chemical is selected from the group consisting of alkali metal silicate, alkali metal aluminosilicate, alkali metal borate, alkali or alkaline earth metal carbonates, alkali or alkaline earth metal nitrite, boric acid, alkali or alkaline earth metal sulfates, alkali or alkaline earth metal nitrate, alkali or alkaline earth metal phosphates, alkali or alkaline earth metal hydroxides, sugar, starch, ultra fine fly ash, class C fly ash, class F fly ash, colloidal silica, inorganic silicate cements, organic polymers and combinations thereof.

33. The formulation of claim 29, wherein the blowing agent is substantially the same as the binding agent.