Systems And Methods Of Deriving Peak Fracture Strain Values Of Metal Experiencing Fracture Failure

Abstract

Systems and methods of deriving peak fracture strain values of a metal experiencing fracture failure from measured data obtained in a specimen test are disclosed. Metal fracture failure criteria, a measurement characteristic length in a specimen test and characteristics of a neck formed in the metal are received in a computer system. The metal fracture failure criteria contain respective measured critical strain value and average fracture strain value in various loading conditions. The characteristics of the neck include the neck's width and a profile of strain distribution within the neck's width. Respective peak fracture strain values are calculated for various loading conditions using a formula based on the profile of strain distribution, the neck's width, and measured critical strain value and average fracture strain value. Peak fracture strain values can be used in a numerical simulation of sheet metal deformation for more accurately predicting structural behaviors of metal.

Description

FIELD

The present invention generally relates to computer-aided engineering analysis, more particularly to methods and systems for deriving peak fracture strain values of a metal experiencing fracture failure from measured data obtained in a physical or numerically-simulated specimen test.

BACKGROUND

Computer aided engineering (CAE) has been used for supporting engineers in many tasks. For example, in a structure or engineering product design procedure, CAE analysis, particularly finite element analysis (FEA), has often been employed to predict structural behavior (e.g., stresses, displacements, etc.) under various simulated loading conditions (e.g., static or dynamic).

In order to numerically simulate metal necking and fracture failure in finite element analysis, metal failure criteria are specified by users. Prior art approaches have been developed from metal specimen test (either physical or numerically-simulated). Before the metal develops a neck, the strain is homogeneous throughout the specimen; therefore the measured strain values including the critical (necking) strain value are constant. The critical necking strain value is the highest strain value before necking starts. From thereon, the strain becomes non-uniform and concentrates within the neck. As a result, the measured fracture strain value is an average value over a measurement characteristic length (i.e., strain gauge or a finite element representing the strain gauge). Due to the measurement dependency of the average fracture strain values, these prior art approaches often cause confusions and difficulties for preparing input data and lead to incorrect simulation because users need to prepare the failure criteria based on these artificial and ad hoc requirement.

It would therefore be desirable to have improved methods and systems for deriving peak fracture strain values of a metal experiencing fracture failure from measured data obtained in a physical or numerically-simulated specimen test.

BRIEF SUMMARY

This section is for the purpose of summarizing some aspects of the present invention and to briefly introduce some preferred embodiments. Simplifications or omissions may be made to avoid obscuring the purpose of the section. Such simplifications or omissions are not intended to limit the scope of the present invention.

Systems and methods of deriving peak fracture strain values of a metal experiencing fracture failure from measured data obtained in a specimen test are disclosed. Metal fracture failure criteria in forms of a loading path diagram, a measurement characteristic length in a specimen test and characteristics of a neck formed in the metal are received in a computer system. The metal fracture failure criteria contain respective measured critical strain value and average fracture strain value in various loading conditions between uni-tension and bi-axial tension. The characteristics of the neck including the neck's width and a profile of strain distribution within the neck's width. Respective peak fracture strain values are calculated for various loading conditions using a formula based on the profile of strain distribution, the neck's width, the measured critical strain value and the average fracture strain value. The average fracture strain is based on the measurement characteristic length. Peak fracture strain values can be used in a numerical simulation of sheet metal deformation for more accurately predicting structural behaviors of metal.

Objects, features, and advantages of the present invention will become apparent upon examining the following detailed description of an embodiment thereof, taken in conjunction with the attached drawings.

BRIEF DESCRIPTION OF THE DRAWINGS

These and other features, aspects, and advantages of the present invention will be better understood with regard to the following description, appended claims, and accompanying drawings as follows:

FIG. 1 is a flowchart illustrating an example process of deriving peak fracture strain values of a metal experiencing fracture failure, according to an embodiment of the present invention;

FIG. 2 is a diagram showing a stress-strain relationship of an example metal, according to an embodiment of the present invention;

FIG. 3 shows an example loading path diagram containing measured critical strain value and average fracture strain value obtained in a physical or numerically-simulated specimen test of a metal of interest in accordance with an embodiment of the present invention;

FIG. 4 is a set of schematic diagrams showing various stages of an example physical or numerically-simulated specimen test, according to an embodiment of the present invention;

FIG. 5 is a diagram showing an example profile of strain distribution between critical strain and fracture strain in accordance with an embodiment of the present invention;

FIG. 6 is a diagram showing an alternative example profile of strain distribution between critical strain and fracture strain in accordance with an embodiment of the present invention;

FIG. 7 is a diagram showing derived peak fracture strain values along with measured data in the loading path diagram in accordance with one embodiment of the present invention; and

FIG. 8 is a functional block diagram showing salient components of an exemplary computer, in which an embodiment of the present invention may be implemented.

DETAILED DESCRIPTION

In the following description, numerous specific details are set forth in order to provide a thorough understanding of the present invention. However, it will become obvious to those skilled in the art that the present invention may be practiced without these specific details. The descriptions and representations herein are the common means used by those experienced or skilled in the art to most effectively convey the substance of their work to others skilled in the art. In other instances, well-known methods, procedures and components have not been described in detail to avoid unnecessarily obscuring aspects of the present invention.

Reference herein to “one embodiment” or “an embodiment” means that a particular feature, structure, or characteristic described in connection with the embodiment can be included in at least one embodiment of the invention. The appearances of the phrase “in one embodiment” in various places in the specification are not necessarily all referring to the same embodiment, nor are separate or alternative embodiments mutually exclusive of other embodiments. Further, the order of blocks in process flowcharts or diagrams representing one or more embodiments of the invention do not inherently indicate any particular order nor imply any limitations in the invention.

Embodiments of the present invention are discussed herein with reference to FIGS. 1-8. However, those skilled in the art will readily appreciate that the detailed description given herein with respect to these figures is for explanatory purposes as the invention extends beyond these limited embodiments.

Referring first to FIG. 1, it is a flowchart illustrating an example process 100 of deriving peak fracture strain values of a metal experiencing fracture failure according to one embodiment of the present invention. Process 100 is preferably implemented in software and understood with other figures.

Process 100 starts at action 102 by receiving a set of metal fracture failure criteria in forms of a loading path diagram (e.g., loading path diagram 300 in FIG. 3) in a computer system (e.g., computer system 800 of FIG. 8) having an application module installed thereon. The loading path diagram contains respective measured critical strain value and average fracture strain value in various loading conditions or strain directions obtained in a physical or numerically-simulated specimen test. In one embodiment, the loading conditions range over uni-tension and bi-axial tension.

A measurement characteristic length used in the specimen test and the neck's characteristics are also received in the computer system. The characteristic length used in a physical specimen test is the original length of a strain gauge used for measurement. The characteristic length in a numerically-simulated specimen test is the dimension of the finite element used for numerically representing the strain gauge. The neck's characteristics include the neck's width and a profile of the strain distribution within the neck. (e.g., see FIGS. 5-6).

FIG. 2 shows an example stress-strain curve 200, which may be used for determining post-yielding structural behaviors including necking and fracture, according to one embodiment of the present invention. The curve 200 has a vertical axis representing stress 204 and a horizontal axis for strain 202. Material has two regions: elastic 212 and plastic 214. Plastic region 214 is further divided into three categories: yielding 215, strain hardening 216 and necking 217. At the top end of the elastic region of the stress-strain curve 200 is a yielding point 220, to which the yielding stress corresponds. The critical strain 232 corresponds to the ultimate strength point 222 (i.e., onset of necking 217) and the fracture strain 234 corresponds to the fracture location 224.

FIG. 3 shows an example set of metal fracture failure criteria in forms of a loading path diagram 300, according to an embodiment of the present invention. The loading path diagram 300 has two axes: a vertical axis representing strain values in major strain (ε₁) direction and a horizontal axis representing strain values in minor strain (ε₂) direction. The metal fracture failure criteria contain respective measured critical strain values 332 and measured average fracture strain values 334 in various loading conditions or strain directions obtained in a physical or numerically-simulated specimen test. In physical specimen test, a strain gauge is used for measuring the data. In numerically-simulated specimen test, finite element analysis can be used for predicting the data. For example, a bi-axial tension loading is illustrated as a dotted line marked by (ε₂=ε₁). A uni-tension loading is shown as a dotted line marked by (ε₂=−ε₁/2).

FIG. 4 is a set of schematic diagrams showing various stages of an example physical or numerically-simulated specimen test of a metal of interest in accordance with one embodiment of the present invention. For the purpose of the present invention, the larger positive strain (i.e., stretch by tension) of the two computed strain values is referred to as a major strain. The other is referred to as the minor strain, which can be positive (under tension) or negative (under compression).

In this example, the specimen is under tension (shown as two hollow arrows) in its major strain direction (i.e., the vertical direction in the loading path diagram 300). The characteristic length l_g 412 is the original dimension of a strain gauge 410 or a finite element representing the strain gauge 410 used for measurement of strain values.

The metal is stretched by additional length to the deformed length l₁ 414 at the ultimate strength point right before the necking stage. Also shown in FIG. 4 is the neck width w 404, which is obtained/measured. At this point, the metal experiences the critical strain ε_c. The metal is further stretched to the final length l₁+dw 416 before fracture occurs, and the neck width is increased to a final width w+dw 406.

FIG. 5 is a diagram showing a first example (triangular) profile 510 of strain distribution between critical strain value ε_c 514 corresponding to the ultimate strength of the metal and peak fracture strain value ε_f 512 corresponding to the metal stretched right before the fracture in accordance with an embodiment of the present invention. The final width w+dw 516 at the base of the profile 510 is the length of the neck before facture occurs. The area of the triangular profile 510 is (w+dw)*(ε_f−ε_c)/2.

Obtained from the specimen test (either physical or numerically-simulated), the average fracture strain value ε_M is an average strain value over the characteristic length l_g for measurement. ε_M can be expressed as follows:

$\begin{array}{cc}{\varepsilon }_c=\ln \frac{l_1}{l_g}& \left(1\right)\\ l_1=l_ge^{{\varepsilon }_c}& \left(2\right)\\ \ln \frac{\mathrm{dw}}{w}=\frac{{\varepsilon }_f-{\varepsilon }_c}{2}& \left(3\right)\\ \mathrm{dw}={\mathrm{we}}^{\left({\varepsilon }_f-{\varepsilon }_c\right)/2}& \left(4\right)\\ {\varepsilon }_M=\ln \frac{l_1+\mathrm{dw}}{l_g}& \left(5\right)\\ {\varepsilon }_M=\ln \left[e^{{\varepsilon }_c}+\frac{w}{l_g}e^{\left({\varepsilon }_f-{\varepsilon }_c\right)/2}\right]& \left(6\right)\end{array}$

In order to calculate the peak fracture strain value ε_f from the measured data (i.e., l_g, w, ε_M, ε_c), a formula based on the first example profile is determined as follows:

$\begin{array}{cc}{\varepsilon }_f={\varepsilon }_c+2\ln \left[\frac{l_g}{w}\left(e^{{\varepsilon }_M}-e^{{\varepsilon }_c}\right)\right]& \left(7\right)\end{array}$

In an alternative embodiment, a second example (curved) profile 610 of strain values is shown in FIG. 6. The curved profile 610 has a peak representing the peak fracture strain value ε_f 612 while the base representing the critical strain value ε_c 614. The length at the base is the final width w+dw 616 of the neck before fracture. The area under the curved profile needs to be calculated to determine a different formula for deriving the peak facture strain values from the measured data.

Referring back to process 100, at action 104, respective peak fracture strain values for various loading conditions are calculated using the relevant formula. For a triangular shaped profile of strain distribution, equation (7) is used.

FIG. 7 a diagram showing derived peak fracture strain values along with measured data in the loading path diagram in accordance with one embodiment of the present invention. For any loading condition (shown as a line with triple arrows) between bi-axial tension (ε₂=ε₁) and uni-tension (ε₂=−ε₁/2) conditions, peak fracture strain 736 can be calculated/derived from the measured data including average fracture strain 734 and measured critical strain 732. The peak fracture strain values 736 can be used in a numerical simulation of sheet metal deformation for more accurately predicting structural behaviors of metal. The structural behaviors include failure of the metal based on the peak fracture strain value under a particular loading condition.

According to one aspect, the present invention is directed towards one or more computer systems capable of carrying out the functionality described herein. An example of a computer system 800 is shown in FIG. 8. The computer system 800 includes one or more processors, such as processor 804. The processor 804 is connected to a computer system internal communication bus 802. Various software embodiments are described in terms of this exemplary computer system. After reading this description, it will become apparent to a person skilled in the relevant art(s) how to implement the invention using other computer systems and/or computer architectures.

Computer system 800 also includes a main memory 808, preferably random access memory (RAM), and may also include a secondary memory 810. The secondary memory 810 may include, for example, one or more hard disk drives 812 and/or one or more removable storage drives 814, representing a floppy disk drive, a magnetic tape drive, an optical disk drive, etc. The removable storage drive 814 reads from and/or writes to a removable storage unit 818 in a well-known manner. Removable storage unit 818, represents a floppy disk, magnetic tape, optical disk, etc. which is read by and written to by removable storage drive 814. As will be appreciated, the removable storage unit 818 includes a computer usable storage medium having stored therein computer software and/or data.

In alternative embodiments, secondary memory 810 may include other similar means for allowing computer programs or other instructions to be loaded into computer system 800. Such means may include, for example, a removable storage unit 822 and an interface 820. Examples of such may include a program cartridge and cartridge interface (such as that found in video game devices), a removable memory chip (such as an Erasable Programmable Read-Only Memory (EPROM), Universal Serial Bus (USB) flash memory, or PROM) and associated socket, and other removable storage units 822 and interfaces 820 which allow software and data to be transferred from the removable storage unit 822 to computer system 800. In general, Computer system 800 is controlled and coordinated by operating system (OS) software, which performs tasks such as process scheduling, memory management, networking and I/O services.

There may also be a communications interface 824 connecting to the bus 802. Communications interface 824 allows software and data to be transferred between computer system 800 and external devices. Examples of communications interface 824 may include a modem, a network interface (such as an Ethernet card), a communications port, a Personal Computer Memory Card International Association (PCMCIA) slot and card, etc. The computer 800 communicates with other computing devices over a data network based on a special set of rules (i.e., a protocol). One of the common protocols is TCP/IP (Transmission Control Protocol/Internet Protocol) commonly used in the Internet. In general, the communication interface 824 manages the assembling of a data file into smaller packets that are transmitted over the data network or reassembles received packets into the original data file. In addition, the communication interface 824 handles the address part of each packet so that it gets to the right destination or intercepts packets destined for the computer 800. In this document, the terms “computer program medium” and “computer usable medium” are used to generally refer to media such as removable storage drive 814, and/or a hard disk installed in hard disk drive 812. These computer program products are means for providing software to computer system 800. The invention is directed to such computer program products.

The computer system 800 may also include an input/output (I/O) interface 830, which provides the computer system 800 to access monitor, keyboard, mouse, printer, scanner, plotter, and alike.

Computer programs (also called computer control logic) are stored as application modules 806 in main memory 808 and/or secondary memory 810. Computer programs may also be received via communications interface 824. Such computer programs, when executed, enable the computer system 800 to perform the features of the present invention as discussed herein. In particular, the computer programs, when executed, enable the processor 804 to perform features of the present invention. Accordingly, such computer programs represent controllers of the computer system 800.

In an embodiment where the invention is implemented using software, the software may be stored in a computer program product and loaded into computer system 800 using removable storage drive 814, hard drive 812, or communications interface 824. The application module 806, when executed by the processor 804, causes the processor 804 to perform the functions of the invention as described herein.

The main memory 808 may be loaded with one or more application modules 806 that can be executed by one or more processors 804 with or without a user input through the I/O interface 830 to achieve desired tasks. In operation, when at least one processor 804 executes one of the application modules 806, the results are computed and stored in the secondary memory 810 (i.e., hard disk drive 812). The status of the calculations of peak fracture strain values is reported to the user via the I/O interface 830 either in a text or in a graphical representation.

Although the present invention has been described with reference to specific embodiments thereof, these embodiments are merely illustrative, and not restrictive of, the present invention. Various modifications or changes to the specifically disclosed exemplary embodiments will be suggested to persons skilled in the art. For example, whereas two-dimensional finite elements have been shown and described for the present invention, other types of finite elements may be used to achieve the same, for example, one-dimensional finite element (beam element) or three-dimensional finite element (solid element). Generally, there is one major strain value and two minor strain values in a three-dimensional finite element. In summary, the scope of the invention should not be restricted to the specific exemplary embodiments disclosed herein, and all modifications that are readily suggested to those of ordinary skill in the art should be included within the spirit and purview of this application and scope of the appended claims.

Claims

1. A method of deriving peak fracture strain values of a metal experiencing fracture failure from measured data obtained in a specimen test, the method comprising: receiving, in a computer system having an application module installed thereon, a set of metal fracture failure criteria in forms of a loading path diagram, a measurement characteristic length in a specimen test of the metal and characteristics of a neck formed in the metal, the metal fracture failure criteria containing respective measured critical strain value and average fracture strain value in various loading conditions, the characteristics of the neck including the neck's width and a profile of strain distribution within the neck's width, wherein the average fracture strain value is based on the measurement characteristic length; andcalculating, with the application module, respective peak fracture strain values for each of the loading conditions using a formula based on the profile of strain distribution within the neck's width, the neck's width, the measured critical strain value and the average fracture strain value; whereby the peak fracture strain values are used in a numerical simulation of sheet metal deformation for more accurately predicting structural behaviors of metal.

2. The method of claim 1, wherein the measured critical strain value and the average fracture strain value are between uni-tension and biaxial tension conditions.

3. The method of claim 1, wherein said specimen test of metal comprises a physical specimen test and the measurement characteristic length is a strain gauge's length.

4. The method of claim 1, wherein said specimen test of metal comprises a numerically-simulated specimen test and the measurement characteristic length is a finite element's dimension that represents a strain gauge.

5. The method of claim 1, wherein said profile comprises a triangular profile.

6. The method of claim 5, wherein said formula is as follows:

7. The method of claim 6, wherein the structural behaviors include necking and fracture failure of the metal based on the peak fracture strain value under a particular loading condition.

8. The method of claim 1, wherein said profile comprises one or more curves.

9. A system for deriving peak fracture strain values of a metal experiencing fracture failure from measured data obtained in a specimen test, the system comprising: an input/output (I/O) interface;a memory for storing computer readable code for an application module;at least one processor coupled to the memory, said at least one processor executing the computer readable code in the memory to cause the application module to perform operations of:receiving a set of metal fracture failure criteria in forms for a loading path diagram, a measurement characteristic length in a specimen test of the metal and characteristics of a neck formed in the metal, the metal fracture failure criteria containing respective measured critical strain value and average fracture strain value in various loading conditions, the characteristics of the neck including the neck's width and a profile of strain distribution within the neck's width, wherein the average fracture strain value is based on the measurement characteristic length; andcalculating respective peak fracture strain values for each of the loading conditions using a formula based on the profile of strain distribution within the neck's width, the neck's width, the measured critical strain value and the average fracture strain value; whereby the peak fracture strain values are used in a numerical simulation of sheet metal deformation for more accurately predicting structural behaviors of metal.

10. The system of claim 9, wherein the measured critical strain value and the average fracture strain value are between uni-tension and biaxial tension conditions.

11. The system of claim 9, wherein said specimen test of metal comprises a physical specimen test and the measurement characteristic length is a strain gauge's length.

12. The system of claim 9, wherein said specimen test of metal comprises a numerically-simulated specimen test and the measurement characteristic length is a finite element's dimension that represents a strain gauge.

13. The system of claim 9, wherein said profile comprises a triangular profile.

14. The method of claim 13, wherein said formula is as follows:

15. The system of claim 14, wherein the structural behaviors include necking and fracture failure of the metal based on the peak fracture strain value under a particular loading condition.

16. A non-transitory computer readable storage medium containing computer instructions for deriving peak fracture strain values of a metal experiencing fracture failure from measured data obtained in a specimen test, said computer instructions when executed on a computer system cause the computer system to perform operations of: receiving, in a computer system having an application module installed thereon, a set of metal fracture failure criteria in forms for a loading path diagram, a measurement characteristic length in a specimen test of the metal and characteristics of a neck formed in the metal, the metal fracture failure criteria containing respective measured critical strain value and average fracture strain value in various loading conditions, the characteristics of the neck including the neck's width and a profile of strain distribution within the neck's width, wherein the average fracture strain value is based on the measurement characteristic length; andcalculating, with the application module, respective peak fracture strain values for each of the loading conditions using a formula based on the profile of strain distribution within the neck's width, the neck's width, the measured critical strain value and the average fracture strain value; whereby the peak fracture strain values are used in a numerical simulation of sheet metal deformation for more accurately predicting structural behaviors of metal.

17. The non-transitory computer readable storage medium of claim 16, wherein the measured critical strain value and the average fracture strain value are between uni-tension and biaxial tension conditions.

18. The non-transitory computer readable storage medium of claim 16, wherein said specimen test of metal comprises a physical specimen test and the measurement characteristic length is a strain gauge's length.

19. The non-transitory computer readable storage medium of claim 16, said specimen test of metal comprises a numerically-simulated specimen test and the measurement characteristic length is a finite element's dimension that represents a strain gauge.

20. The non-transitory computer readable storage medium of claim 16, wherein said profile comprises a triangular profile and wherein said formula is as follows: