Claims
- 1. A hose made by the process which comprises (1) extruding a rubber composition into the form of a tube, wherein the rubber composition is comprised of (a) a polyethylene/polypropylene alloy comprised of (i) low melt index polyethylene having a melt index which is within the range of about 0.05 g/10 minutes to about 1.5 g/10 minutes and (ii) polypropylene, wherein the polypropylene is homogeneously dispersed throughout the polyethylene in the polypropylene/polyethylene alloy, (b) an EPDM rubber, (c) carbon black, (d) at least one curative, (e) zinc oxide, (f) a processing oil and (g) stearic acid; (2) shaping the tube into the geometric form desired for the hose; and (3) curing the rubber composition at a temperature within the range of 130.degree. C. to 210.degree. C. to produce the hose; wherein said hose has a burst strength of at least 140 pounds per square inch and wherein said hose is void of fabric reinforcement.
- 2. A hose as specified in claim 1 wherein said hose has a Shore A hardness of no more than about 88.
- 3. A hose as specified in claim 2 wherein the thermoplastic is a polyethylene/polypropylene alloy and wherein the amount of alloy is sufficient for there to be from about 2 phr to about 30 phr of polypropylene in the rubber composition based upon the total amount of EPDM rubber in the composition.
- 4. A hose as specified in claim 2 wherein the rubber composition contains from about 80 phr to about 150 phr of carbon black, from about 20 phr to about 90 phr of processing oil, from about 1 phr to about 10 phr of zinc oxide, from about 0.25 phr to about 5 phr of stearic acid, from about 0.2 phr to about 6 phr of sulfur and from about 1 phr to about 12 phr of accelerator.
- 5. A hose as specified in claim 4 wherein the rubber composition is cured at a temperature which is within the range of about 140.degree. C. to about 200.degree. C.
- 6. A hose as specified in claim 2 wherein the rubber composition is extruded into the form of a tube utilizing a spiral mandrel die.
- 7. A hose as specified in claim 2 wherein the thermoplastic is polyethylene/polypropylene alloy and wherein the rubber composition contains from about 3 phr to about 30 phr of polypropylene, from about 100 phr to about 130 phr of carbon black, from about 30 phr to about 70 phr of processing oil, from about 3 phr to about 8 phr of zinc oxide, from about 0.5 phr to about 4 phr of stearic acid, from about 0.3 phr to about 4 phr of sulfur and from about 2.5 phr to about 10 phr of accelerators.
- 8. A hose as specified in claim 2 wherein the rubber composition contains from about 4 phr to about 30 phr of polypropylene, from about 110 phr to about 125 phr of carbon black, from about 40 phr to about 50 phr of processing oil, from about 4 phr to about 6 phr of zinc oxide, from about 1 phr to about 3 phr of stearic acid, from about 0.5 phr to about 2 phr of sulfur and from about 4 phr to about 8 phr of accelerator.
- 9. A hose as specified in claim 7 wherein the accelerator is comprised of a combination of mercaptobenzothiazole, tetramethylthiuram disulfide and zinc dibutyldithiocarbamate.
- 10. A hose as specified in claim 9 wherein said rubber composition is cured at a temperature which is within the range of about 170.degree. C. to about 195.degree. C.
- 11. A hose as specified in claim 10 wherein said hose has a burst strength of at least 150 pounds per square inch and a Shore A hardness of no more than about 85.
- 12. A hose made by the process which comprises injection molding a rubber composition into the desired geometric form for the hose at a temperature which is within the range of 130.degree. C. to 210.degree. C., wherein the rubber composition is comprised of (a) a polypropylene/polyethylene alloy comprised of (i) a low melt index polyethylene having a melt index which is within the range of about 0.05 g/10 minutes to about 1.5 g/10 minutes and (ii) polypropylene, wherein the polypropylene is homogeneously dispersed throughout the polyethylene in the polypropylene/polyethylene alloy, (b) an EPDM rubber, (c) carbon black, (d) at least one curative, (e) zinc oxide, (f) a processing oil and (g) stearic acid; (2) shaping the tube into the geometric form desired for the hose; and (3) curing the rubber composition at a temperature within the range of 130.degree. C. to 210.degree. C. to produce the hose; wherein said hose has a burst strength of at least 140 pounds per square inch and wherein said hose is void of fabric reinforcement.
- 13. A hose as specified in claim 12 wherein said hose has a Shore A hardness of no more than about 88.
- 14. A hose as specified in claim 13 wherein the amount of alloy is sufficient for there to be from about 2 phr to about 50 phr of polypropylene in the rubber composition based upon the total amount of EPDM rubber in the composition.
- 15. A hose as specified in claim 14 wherein the rubber composition contains from about 80 phr to about 150 phr of carbon black, from about 20 phr to about 90 phr of processing oil, from about 1 phr to about 10 phr of zinc oxide, from about 0.25 phr to about 5 phr of stearic acid, from about 0.2 phr to about 6 phr of sulfur and from about 1 phr to about 12 phr of accelerator.
- 16. A hose as specified in claim 15 wherein the rubber composition contains from about 3 phr to about 30 phr of polypropylene, from about 100 phr to about 130 phr of carbon black, from about 30 phr to about 70 phr of processing oil, from about 3 phr to about 8 phr of zinc oxide, from about 0.5 phr to about 4 phr of stearic acid, from about 0.3 phr to about 4 phr of sulfur and from about 2.5 phr to about 10 phr of accelerators.
- 17. A hose as specified in claim 15 wherein the rubber composition contains from about 4 phr to about 30 phr of polypropylene derived from polyethylene/polypropylene alloy, from about 110 phr to about 125 phr of carbon black, from about 40 phr to about 50 phr of processing oil, from about 4 phr to about 6 phr of zinc oxide, from about 1 phr to about 3 phr of stearic acid, from about 0.5 phr to about 2 phr of sulfur and from about 4 phr to about 8 phr of accelerator.
- 18. A hose as specified in claim 17 wherein said hose has a burst strength of at least 150 pounds per square inch and a Shore A hardness of no more than about 85.
Parent Case Info
This application is a divisional application of application Ser. No. 08/767,555, filed Dec. 16, 1996, now U.S. Pat. No. 5,762,850.
US Referenced Citations (4)
Divisions (1)
|
Number |
Date |
Country |
Parent |
767555 |
Dec 1996 |
|