1. Field of the invention
The invention relates generally to thermal interface materials and manufacturing methods thereof; and more particularly to a kind of thermal interface material which conducts heat by using carbon nanotubes, and a manufacturing method thereof.
2. Description of Related Art
Electronic components such as semiconductor chips are becoming progressively smaller, while at the same time heat dissipation requirements thereof are increasing. Commonly, a thermal interface material is utilized between the electronic component and a heat sink in order to dissipate heat generated by the electronic component.
A conventional thermal interface material is obtained by diffusing particles with a high heat conduction coefficient in a base material. The particles can be graphite, boron nitride, silicon oxide, alumina, silver, or other metals. However, a heat conduction coefficient of the thermal interface material is now considered to be too low for many contemporary applications, because it cannot adequately meet the heat dissipation requirements of modern electronic components.
A new kind of thermal interface material has recently been developed. The thermal interface material is obtained by fixing carbon fibers with polymer. The carbon fibers are distributed directionally, and each carbon fiber can provide a heat conduction path. A heat conduction coefficient of this kind of thermal interface material is relatively high. However, the heat conduction coefficient of the thermal interface material is inversely proportional to a thickness thereof, and the thickness is required to be greater than 40 micrometers. In other words, the heat conduction coefficient is limited to a certain value corresponding to a thickness of 40 micrometers. The value of the heat conduction coefficient cannot be increased, because the thickness cannot be reduced.
An article entitled “Unusually High Thermal Conductivity of Carbon Nanotubes” and authored by Savas Berber (page 4613, Vol. 84, Physical Review Letters 2000) discloses that a heat conduction coefficient of a carbon nanotube can be 6600 W/mK (watts/milliKelvin) at room temperature.
U.S. Pat. No. 6,407,922 discloses another kind of thermal interface material. The thermal interface material is formed by injection molding, and has a plurality of carbon nanotubes incorporated in a matrix material. A first surface of the thermal interface material engages with an electronic device, and a second surface of the thermal interface material engages with a heat sink. The second surface has a larger area than the first surface, so that heat can be uniformly spread over the larger second surface.
However, the thermal interface material formed by injection molding is relatively thick. This increases a bulk of the thermal interface material and reduces its flexibility. Furthermore, the carbon nanotubes are disposed in the matrix material randomly and multidirectionally. This means that heat does not necessarily spread uniformly through the thermal interface material. In addition, heat does not necessarily spread directly from a first surface of the thermal interface material engaged with an electronic device to a second surface of the thermal interface material engaged with a heat sink.
A new thermal interface material which overcomes the above-mentioned problems and a method for manufacturing such material are desired.
Accordingly, an object of the present invention is to provide a thermal interface material having a reduced thickness, good flexibility and excellent heat conduction.
Another object of the present invention is to provide a method for manufacturing the above-described thermal interface material.
To achieve the first of the above-mentioned objects, the present invention provides a thermal interface material comprising a silver colloid base and an array of carbon nanotubes disposed in the silver colloid base uniformly. The silver colloid base comprises silver particles, boron nitride particles and polysynthetic oils. The silver colloid base has a first surface, and a second surface opposite to the first surface. The carbon nanotubes are substantially parallel to each other, and extend from the first surface to the second surface.
To achieve the second of the above-mentioned objects, a method for manufacturing the thermal interface material comprises the steps of:
Unlike in a conventional thermal interface material, the carbon nanotubes of the thermal interface material of the present invention are disposed in the silver colloid base uniformly and directionally. Thus, each carbon nanotube of the thermal interface material can provide a heat conduction path in a direction perpendicular to a main heat absorbing surface of the thermal interface material. This ensures that the thermal interface material has a high heat conduction coefficient.
Other objects, advantages and novel features of the invention will become more apparent from the following detailed description when taken in conjunction with the accompanying drawings, in which:
Referring to
The catalyst film 12 is oxidized to obtain catalyst particles (not shown). Then, the substrate 11 with the catalyst particles disposed thereon is placed in a reaction furnace (not shown), and a carbon source gas is provided in the reaction furnace at a temperature of 700–1000° C. to grow the array of carbon nanotubes 22. The carbon source gas can be acetylene or ethene. A height of the array of carbon nanotubes 22 can be controlled by controlling the growth time thereof. The height of the array of carbon nanotubes 22 is generally in the range from 1 to 100 micrometers. In the preferred embodiment, the height of the array of carbon nanotubes 22 is about 100 micrometers. Details of the method for growing the array of carbon nanotubes 22 can be found in pages 512–514, Vol. 283, Science 1999, and in pages 11502–11503, Vol. 123, J. Am. Chem. Soc. 2001. Moreover, U.S. Pat. No. 6,350,488 discloses a method for mass synthesis of arrays of carbon nanotubes. These three publications are incorporated herein by reference.
Referring to
It is understood that the above-described embodiment is intended to illustrate rather than limit the invention. Variations may be made to the embodiment without departing from the spirit of the invention. Accordingly, it is appropriate that the appended claims be construed broadly and in a manner consistent with the scope of the invention.
Number | Date | Country | Kind |
---|---|---|---|
92136527 A | Dec 2003 | TW | national |
Number | Name | Date | Kind |
---|---|---|---|
5026748 | Adams et al. | Jun 1991 | A |
5052481 | Horvath et al. | Oct 1991 | A |
5094769 | Anderson et al. | Mar 1992 | A |
5989459 | Nguyen et al. | Nov 1999 | A |
6350488 | Lee et al. | Feb 2002 | B1 |
6407922 | Eckblad et al. | Jun 2002 | B1 |
20050161210 | Zhong et al. | Jul 2005 | A1 |
20050269726 | Matabayas | Dec 2005 | A1 |
Number | Date | Country | |
---|---|---|---|
20050136248 A1 | Jun 2005 | US |