Patent Application
20120107662
1. Field of the Invention
The present invention relates to a thermal management matrix for an electrochemical cell array including a plurality of electrochemical cell elements, the matrix including layers of expanded graphite with different densities in the form of a sandwich-like structure.
2. Description of the Related Art
The need for thermal management systems to improve Li-ion battery performance, extend battery life and reduce the risks of thermal runaway are well known. Different systems have been developed to address these problems. One present technology differs from the others in that they use PCM (Phase Change Material) infiltrated graphite as a passive solution, to dissipate heat from individual cells in multi-cell modules. This solution is particularly effective where thermal problems are intermittent or “transient”. Other active systems developed for comparison use fluid circulating in metal jackets to dissipate heat and effectively control steady-state thermal conditions. Another advantage of active systems is that they can heat as well as cool the modules, which is important in areas with extreme seasonal temperature changes.
As mentioned above, a PCM/graphite system offers the advantage of a passive system, with no moving parts (pumps, temperature sensors, seals, controls, etc.) to fail. They are simple and relatively inexpensive. The thermal anisotropy inherent in the molded graphite blocks manufactured using expanded graphite worms effectively transfers heat from the Li-ion cells towards the perimeter of the modules where it can be dissipated. A disadvantage of the system is that once the PCM/graphite becomes “saturated” with heat, it retains it for a long period of time. PCM is the primary weight component of the “compound” and, if paraffin based, is flammable.
Metal systems (machined, formed, extruded) can be complex, heavy, expensive and require many more components (fittings, fixtures, thermal interface materials, etc.) to be effective. Differences in CTE (Coefficient of Thermal Expansion) between the metal (aluminum) and the cells, presents additional engineering challenges. These systems typically have their own fluid circulation systems, further increasing space and weight.
EP 1 972 675 A2 and U.S. Pat. No. 7,235,301 B2 disclose latent heat storage material comprising at least one phase change material and expanded graphite. No sandwich structure of the thermal management matrix is disclosed herein.
What is needed in the art is an enhanced thermal management system to improve Li-ion battery performance, extend battery life and reduce the risks of a thermal runaway, thereby overcoming the disadvantages of the state of the art.
The present invention provides a thermal management matrix for an electrochemical cell array. More specifically the present invention provides a thermal management matrix for an electrochemical cell array including a plurality of electrochemical cell elements, the thermal management matrix at least in part enveloping the electrochemical cell array and in thermal contact therewith. The thermal management matrix according to the present invention includes mainly expanded graphite, arranged in the form of a block-like structure. The block includes at least one layer of expanded graphite having a higher in-plane thermal conductivity than the in-plane thermal conductivity of the layers neighboring the layer with the higher in-plane thermal conductivity.
According to one embodiment of the present invention, at least two layers of expanded graphite with higher thermal conductivity may be present and/or the layers may be parallel to each other.
According to a second embodiment of the present invention, the at least one layer of expanded graphite with higher thermal conductivity may be present in the form of a foil.
According to a third embodiment of the present invention, the at least one layer of expanded graphite with higher thermal conductivity may be arranged either parallel to the longitudinal direction of the electrochemical cell elements or orthogonal to the longitudinal direction of the electrochemical cell elements.
According to a fourth embodiment of the present invention, the at least one layer with higher in-plane thermal conductivity may have an in-plane thermal conductivity in the range of approximately 100 to 600 W/mK and the in-plane thermal conductivity of the other layers have an in-plane thermal conductivity in the range of approximately 4 to 50 W/mK.
According to a fifth embodiment of the present invention, the at least one layer of expanded graphite with higher in-plane thermal conductivity has a higher density than the layers with the lower in-plane thermal conductivity. In that context, the at least one layer with higher density has a density, for example, in the range of approximately 0.5 to 2.0 g/cm3 and the density of the other layers have, for example, a density in the range of approximately 0.05 to 0.5 g/cm3.
According to the present invention the thermal conductivity of the layers of the block may be higher either in the orthogonal or the parallel direction.
The parts of the thermal management matrix enveloping the electrochemical cell array, and in thermal contact therewith, may further be coated with one or more phase change materials(s). According to the present invention at least the expanded graphite neighboring the layer with higher in-plane thermal conductivity may be infiltrated with phase change materials.
Further, the at least one layer of expanded graphite with higher in-plane thermal conductivity may be arranged orthogonal to the longitudinal direction of the electrochemical cell elements, and the at least one layer neighboring the layer with the higher in-plane thermal conductivity formed out of two modules may have multiple circular grooves equal to half the diameter of the electrochemical cell elements. The two modules in an assembled form then may envelope the electrochemical cell array.
The present invention further provides a process for producing a thermal management matrix from expanded graphite. A first embodiment of the process for producing a thermal management matrix from expanded graphite, according to the present invention, includes the following steps:
a) producing a planar pre-formed piece from expanded graphite having an in-plane thermal conductivity in the range of approximately 4 to 50 W/mK;
b) placing a layer of a foil of compressed expanded graphite having an in-plane thermal conductivity in the range of approximately 100 to 600 W/mK on top of the produced planar pre-formed piece of step a);
c) repeating steps a) and b) and finally a), until the desired thickness of the block is formed; and
d) boring out holes adapted in size to envelope the electrochemical cell elements.
The expanded graphite used in step a) may be infiltrated with one or more phase change material(s) prior to use in step a). Further, in the context of the process according to the present invention, the finally formed block may be coated with one or more phase change material(s). The formed borings may further be coated with one or more phase change material(s).
The desired thickness of the block formed may be higher than the electrochemical cell elements to be enveloped and the process include the further steps performed after step d):
e) inserting the electrochemical cell elements into the hole provided in step d); and
f) compressing the block of pre-formed expanded graphite together with the inserted electrochemical cell elements to form an intimate contact of the expanded graphite material with the outer surface of the electro-chemical cell elements.
The present invention further provides a second embodiment of a process for producing a thermal management matrix from expanded graphite which includes the following steps:
a) providing a layer of a foil of compressed expanded graphite having an in-plane thermal conductivity in the range of approximately 100 to 600 W/mK;
b) producing two pre-formed pieces from expanded graphite having an in-plane thermal conductivity in the range of approximately 4 to 50 W/mK, the pre-formed pieces including semi-circular grooves equal to approximately one-half the diameter of the electrochemical cell element;
c) placing together the two pre-formed pieces obtained in step a) in such a manner that cylindrical envelopes are formed out of the semi-circular grooves;
d) placing the assembly of step c) with one planar side on top of the layer provided in step a);
e) placing a layer of a foil of compressed expanded graphite having an in-plane thermal conductivity in the range of approximately 100 to 600 W/mK on top of the other planar side of the assembly obtained in step c); and
f) repeating steps b), c) and e) until the desired thick-ness of the block is formed.
The expanded graphite used in step b) may be infiltrated with the phase change materials prior to use in step b). Additionally, the finally formed block may be coated with the phase change materials. Further, the formed cylindrical envelopes may be coated with phase change materials.
The above-mentioned and other features and advantages of this invention, and the manner of attaining them, will become more apparent and the invention will be better understood by reference to the following description of embodiments of the invention taken in conjunction with the accompanying drawings, wherein:
Corresponding reference characters indicate corresponding parts throughout the several views. The exemplifications set out herein illustrate embodiments of the invention and such exemplifications are not to be construed as limiting the scope of the invention in any manner.
Modular cylindrical cell battery systems typically consist of multiple rows of cylindrical cells. To increase power, the systems just multiply the number of rows to meet different power requirements. As the modules are combined, air cooling becomes less effective and liquid cooling is required. In the art it has been attempted to convert the original machined aluminum design to an extruded aluminum version to reduce cost, but it is difficult to maintain desired tolerances and the interface issue remains. Graphite is a potentially attractive option because it is non-flammable, light weight and has good thermal conductivity. Thermal conductivity is also anisotropic, helping to move heat from the core to liquid cooled cold-plates which are attached to the sides of the modules. PCM/graphite, as stated above, may be less desirable when the thermal load is steady-state, not transient.
The present invention uses expanded graphite to form layers that are stacked on each other in order to form a block-like system or structure that can be of any suitable size to embed an electrochemical cell. The layers used include at least two different in-plane thermal conductivity properties. One of the layers has a higher in-plane thermal conductivity than the layers neighboring the layer with the higher in-plane thermal conductivity. These layers are, for example, in the form of a foil made from expanded graphite. This foil includes a higher in-plane thermal conductivity and acts like a highway for dissipating heat from the electrochemical cells to cooling plates that are, for example, arranged at the outer surfaces of the block-like structure. In this way, an effective cooling and an advantageous thermal management within the matrix is achieved. By arranging the layers in accordance with the present invention, the thermal management matrix shows superior properties over the systems known in the art.
To carry out the present invention, expanded graphite is used in the form of a foil having a thermal conductivity in the range of approximately 100 to 600 W/mK in-plane and in the range of approximately 2 to 50 W/mK through-plane and a density of the foil is in the range of approximately 0.5 to 2.0 g/cm3. Further, expanded graphite is used in the form of a pre-compact having a thermal conductivity in the range of approximately 4 to 50 W/mK in-plane and in the range of approximately 2 to 8 W/mK through-plane and the density of the foil is in the range of approximately 0.05 to 0.5 g/cm3. But it will be apparent to a skilled artesian that expanded graphite may be also used that deviates from the given ranges and may lead to an embodiment of the present invention that is within the scope of the claims and the present description.
The present invention may be embodied in a variety of different structures.
Referring now to
Referring now to
The blocks can be made to whatever thickness is desired, simply by adding more layers. Holes for the cells are then cut out of the block to suit the cell pattern of the module. The blocks can be made thicker than the desired finished thickness of the module and compressed to finished size during assembly. This compression step increases the density and thermal conductivity of the block, and also forces intimate contact between the graphite and the cells, eliminating the need for thermal interface materials and further simplifying assembly. Expanded graphite is able to compress and recover, to maintain contact with the cells due to expansion and contraction during thermal cycling.
According to the present needs in certain environments the matrix may be treated with phase change materials (PCM). If, for example, full infiltration of PCM throughout the block is not required, a light dip may be necessary to limit free graphite particles. As an alternative, an external coating (lacquer, rubber, silicone, etc.) could limit free particles and encapsulate the “block”.
For applications that require full PCM infiltration, the pre-compact/foil blocks with holes cut in them, will accept the PCM faster and minimize the amount of PCM required. In the art it is described to mold a block from graphite worms, infiltrate the whole block with PCM, then machine out the cell holes wasting graphite and PCM. By contrast, the present invention uses foil sheets between the layers of pre-compact and bores out the cell holes prior to PCM infiltration. The graphite “holes” can be recycled for other applications. Area weight uniformity and hence density and thermal conductivity, are easier to control according to the method of the present invention.
According to a second embodiment of the present invention, molded pieces of pre-compact are used to create a modular design.
In other words, in this embodiment of the present invention, multiple semi-circular grooves 6 equal to approximately one-half the diameter of the Li-ion cells in the stack, are molded into sheets of pre-compact to form one-half of module 20. Thickness can be adjusted by the number of pre-compact layers 20, 3 used and shape can easily be changed to accommodate the shape of the cell (cylindrical, prismatic, etc.). According to this embodiment of the present invention, two half modules 20 would be assembled to surround and support the Li-ion cells. Graphite foil 3 is positioned between pre-compact modules 20 to convey heat laterally and vertically, increasing heat transfer from the core and cooling the interior cells in a stack. The molded graphite modules are then banded together or constrained through other means, in the stack assembly process. This embodiment of the present invention provides all the advantages of modularity, such as scalability, cost reduction from damage/scrap through reduction of the size of individual pieces, lower tooling costs, etc. and simplifies the manufacturing process. For all of these reasons, this embodiment of the present invention is a very attractive solution of the problem as given above.
As already indicated, it is important to use suitable expanded graphite in order to carry out the invention. Exemplary expanded graphite includes Ecophit® L, supplied by SGL Group, Germany. The expanded graphite has an in-plane thermal conductivity between approximately 6.5 and approximately 25 W/mK and a density between approximately 0.05 and 0.2 g/cm3 and is easily further compressible. Expanded graphite with higher density in the form of a foil that can be used according to the present invention includes Sigraflex® foil, supplied also by SGL Group. The named foil has an in-plane thermal conductivity between approximately 180 and 200 W/mK and a density range from 0.7 to 1.3 g/cm3.
The process for the production of moldings of expanded graphite is known in the art. U.S. Pat. No. 7,520,953 B2 describes a suitable process and is herewith incorporated by reference.
Suitable phase change materials are also known in the art. EP 1 972 675 A2 and US 2009/0004556 A1 disclose suitable PCM useful in the context and the sense of the present invention and are incorporated herein by reference.
The thermal management matrix according to the present invention has the advantage of being easily adaptable to a great variety of electrochemical cell elements. The matrix shows anisotropic heat dissipation and is easy to produce.
While this invention has been described with respect to at least one embodiment, the present invention can be further modified within the spirit and scope of this disclosure. This application is therefore intended to cover any variations, uses, or adaptations of the invention using its general principles. Further, this application is intended to cover such departures from the present disclosure as come within known or customary practice in the art to which this invention pertains and which fall within the limits of the appended claims.