These notes are further entered into the record for this CIP and based on research conducted by the Applicant and Inventor.
It has been noted that plasticizers lower the melting point. Of the system and therefore we can remove filler. The filler can be removed because the plasticizer works as a binder and therefore the filler is no longer needed. Further is noted that the. The melting point is now 430 degrees Fahrenheit, as opposed to 500 degrees Fahrenheit. The new formulation works like a fiberglass filler.
It's further advantageous that PET is much cheaper than resin. Currently less than 20% the cost of residence. So, there's an economic benefit to using PET as opposed to resin. This application is pressing the case that the invention is deserving of patent protection even without using recycled plastics. Consider the use of virgin plastics as novel standing on its own merits.
The present invention relates to paint compositions in general, and to a road marking paint composition.
Road marking paints and thermal compounds are typically utilized for marking lanes, pedestrians' crossings, etc. on roads. Essential components of conventional melt-bonding (or hot melt) road marking paint include a thermoplastic resin (binder), a pigment, glass beads, and a filler.
Melt-bonding road marking compounds typically come in a powder form. Before application, the road marking paint powder is initially melted in a hot melt kettle. The molten road marking paint can then be applied (typically via spraying) onto a road surface to form the desired shape for road markings. The road marking paint coated on the road surface will be cooled and solidified in a few minutes.
The road marking compounds is required to have properties such as fast drying, wear resistance, and diffusive reflectivity, and strong peel strength after solidification.
The present disclose provides an improved composition for melt-bonding road marking compounds.
Essential components of conventional melt-bonding road marking paint include a thermoplastic resin, a pigment along with a plasticizer, a silica in the form of glass beads, and a filler.
Thermoplastic resins allow the road marking paint to be fast-drying and strongly adhesive to a road surface. Two most common pigment colors are white and yellow. White pigments are mainly titanium dioxide, zinc oxide, and lithophone. Yellow pigment is mainly heat resistant yellow lead. The fillers ensure mechanical strength, wear resistance, and color of paint coating. Glass beads, which are generally colorless and transparent, provide light refraction, focusing and directional reflection. Dispensed throughout the road paint coating surface, glass beads can reflect car light back to drivers' eyes to improve visibility of road markings.
Disclosed herein is an improved composition for a melt-bonding road marking paint 130, as discussed below.
A method of manufacture for an improved composition for melt-bonding road marking compound is disclosed. Comprising preparing a PET component from pulverized plastic. Combining said PET component, a pigment component, a filler component, a silica component and a binder component to form a road marking compound. Melting said road marking compound form said melt-bonding road marking compound. Selecting an amount of said PET component to maximize PET in said melt-bonding road marking compound while ensuring said melt-bonding road marking compound remains liquid for application to a road surface.
A method of manufacture for an improved composition for melt-bonding road marking compound is disclosed. Comprising preparing a PET component from pulverized plastic. Combining said PET component, a pigment component, a filler component, a silica component and a binder component to form a road marking compound. Melting said road marking compound form said melt-bonding road marking compound.
A method of manufacture for an improved composition for melt-bonding road marking compound is disclosed. Comprising combining a PET component, a pigment component, a filler component, a silica component and a binder component to form a road marking compound. Melting said road marking compound form said melt-bonding road marking compound. Selecting an amount of said PET component to maximize PET in said melt-bonding road marking compound while ensuring said melt-bonding road marking compound remains liquid for application to a road surface.
The following description is presented to enable any person skilled in the art to make and use the invention as claimed and is provided in the context of the particular examples discussed below, variations of which will be readily apparent to those skilled in the art. In the interest of clarity, not all features of an actual implementation are described in this specification. It will be appreciated that in the development of any such actual implementation (as in any development project), design decisions must be made to achieve the designers' specific goals (e.g., compliance with system-and business-related constraints), and that these goals will vary from one implementation to another. It will also be appreciated that such development effort might be complex and time-consuming, but would nevertheless be a routine undertaking for those of ordinary skill in the field of the appropriate art having the benefit of this disclosure. Accordingly, the claims appended hereto are not intended to be limited by the disclosed embodiments, but are to be accorded their widest scope consistent with the principles and features disclosed herein.
In one embodiment, said method of manufacture 100 can comprise a first step 102 comprising preparing a PET component 122 from pulverized plastic; second step 104 can comprise combining said PET component 122, a pigment component 126, a filler component 128, a silica component 118 and a binder component 120 to form a road marking compound 116; and third step 106 can comprise melting said road marking compound 116 form melt-bonding road marking compound 130.
Said method of manufacture 100 can further comprise fourth step 108 can comprise heating said road marking compound 116 to 400-425° F. to form a melted mixture 124.
Once prepared in said method of manufacture 100, said melt-bonding road marking compound 130 can be applied as said melted mixture 124 through a pump and air atomization to a road surface.
One feature of said method of manufacture 100, as discussed below, is the selection of inputs of said filler component 128 and said PET component 122 to ensure fluidity of said melt-bonding road marking compound 130 and maximizing the inclusion of said PET component 122.
Said PET component 122 can comprise Polyethylene terephthalate (or poly(ethylene terephthalate). Also known as PETE, or the obsolete PETP or PET-P), is the most common thermoplastic polymer resin of the polyester family and is used in fibers for clothing, containers for liquids and foods, and thermoforming for manufacturing, and in combination with glass fiber for engineering resins. It can include other polyethylene compounds or plastics, as is known in the art.
The parent application to this filing (Ser. No. 17/705,326) (incorporated by reference) discusses the formulation of a road marking paint. Likewise, (Ser. No. 18/169,360) (incorporated by reference) discusses recycled material.
One limitation of maximizing PET can comprise the side effect of losing liquid fluidity should too much or too large an input PET be used for said PET component 122. By maximizing PET, said melt-bonding road marking compound 130 can increase durability while enhancing the environmental benefits of said melt-bonding road marking compound 130.
Said method of manufacture 100 can further comprise said first step 202 comprising selecting an amount of said PET component 122 to maximize PET in said melt-bonding road marking compound 130 while ensuring said melt-bonding road marking compound 130 remains liquid for application to a road surface.
Said first table 300 can comprise a components column 302, an example material column 304, a low percentage by weight column 306, and a high percentage by weight column 308. In one embodiment, said low percentage by weight column 306 and said high percentage by weight column 308 can comprise lower and upper limits of each component as described in said components column 302, respectively. In one embodiment, a formulation of said melt-bonding road marking compound 130 can comprise said method of manufacture 100 by weight as a combination of components selected among said components column 302.
Said first table 300 can comprise a composition of said melt-bonding road marking compound 130 in a white color, in in percentages by weight.
In accordance with one embodiment of the present invention, polyethylene terephthalate (PET or PETE) is utilized as said PET component 122 for manufacturing said melt-bonding road marking compound 130. PET is a polymer resin of the polyester family. In addition, being an additive, PET also replace the certain amount of thermoplastic resin, glass beads and filler needed to be employed in conventional melt-bonding paint compositions. For example, the percentage of PET used in the paint composition may replace the same amount of silica glass beads and or calcium carbonate filler.
Components of white color of said melt-bonding road marking compound 130 include said silica component 118, said binder component 120, said PET component 122, said pigment component 126, and said filler component 128.
Wherein, said pigment component 126 can comprise a white pigment from a rutile titanium dioxide that meets the ASTM D 476, Type II or V standard. A maximum of 17% of the total white pigment content may be ASTM D 476 Type I anatase titanium dioxide. When washed free of resins by solvent washing, pigments should meet U.S. Standard Sieve Number 200.
Said silica component 118 can comprise glass beads which can comprise an index of refraction between 1.50 and 1.53 at 25° C. Glass beads should meet the requirement of AASHTO M247 Type 1.
Said filler component 128 can comprise calcium carbonate of 95% purity.
Said binder component 120 can comprise a mixture of thermoplastic resins, at least one of which is a solid at room temperature. At least ⅓ of the binder composition can comprise a maleic-modified glyceryl ester of rosin, and not less than 8% by weight of the entire material composition.
As discussed above, said second table 400 can comprise columns 302-308 just as said first table 300.
Said second table 400 can comprise a composition of said melt-bonding road marking compound 130 in a yellow color, in in percentages by weight.
Components of yellow color of said melt-bonding road marking compound 130 can include said silica component 118, said binder component 120, said PET component 122, said pigment component 126, and said filler component 128.
Said pigment component 126 can comprise a lead and chromate free, organic yellow pigment that is heat-resistant, such as C.I. Pigment Yellow 83, opaque version.
Said silica component 118 can comprise glass beads should have an index of refraction between 1.50 and 1.53 at 25° C. Glass beads should meet the requirement of AASHTO M247 Type 1.
Said filler component 128 can comprise calcium carbonate of 95% purity.
Said binder component 120 can comprise a mixture of thermoplastic resins, at least one of which is a solid at room temperature. At least ⅓ of the binder composition is a maleic-modified glyceryl ester of rosin, and not less than 8% by weight of the entire material composition.
Said PET component 122 can comprise PET formed pulverizing clear plastic into micron size beads.
As has been described, the present invention provides an improved composition of said melt-bonding road marking compound 130.
While the invention has been particularly shown and described with reference to a preferred embodiment, it will be understood by those skilled in the art that various changes in form and detail may be made therein without departing from the spirit and scope of the invention.
Said third table 500 can comprise a graduation of PET chart related to the size and mass of said PET component 122.
Said third table 500 illustrates four columns: viz., A US Sieve number 502, a bead diameter 504 in microns, a mass percentage low 506 and a mass percentage high 508. Wherein, said mass percentage low 506 and said mass percentage high 508 are understood to represent a range of percentages.
In one embodiment, said PET component 122 can comprise glass beads, can be substantially clear, and substantially spherical.
Said PET component 122 can comprise AASHTO M247-11 TYPE 1 glass beads and can be tested in accordance to ASTM D1214 and AASHTO PP-74-13.
In one embodiment, said method of manufacture 100 can comprise optimizing said bead diameter 504 of said PET component 122 to ensure said melt-bonding road marking compound 130 can flow through screens and nozzles in a typical road paint application equipment.
In one embodiment, said PET component 122 can comprise said bead diameter 504 of 400-750 microns.
Said method of manufacture 100 can further comprise optimizing a portion of said PET component 122 in said melt-bonding road marking compound 130 to maximize PET in said melt-bonding road marking compound 130 while ensuring said melt-bonding road marking compound 130 remains liquid for application to a road surface. One feature of said method of manufacture 100 can comprise reducing said filler component 128 and increasing said PET component 122 to improve wearability of said melt-bonding road marking compound 130 on the road.
Various changes in the details of the illustrated operational methods are possible without departing from the scope of the following claims. Some embodiments may combine the activities described herein as being separate steps. Similarly, one or more of the described steps may be omitted, depending upon the specific operational environment the method is being implemented in. It is to be understood that the above description is intended to be illustrative, and not restrictive. For example, the above-described embodiments may be used in combination with each other. Many other embodiments will be apparent to those of skill in the art upon reviewing the above description. The scope of the invention should, therefore, be determined with reference to the appended claims, along with the full scope of equivalents to which such claims are entitled. In the appended claims, the terms “including” and “in which” are used as the plain-English equivalents of the respective terms “comprising” and “wherein.”
The following summary of the original claims serves as the preferred embodiment(s) of this disclosure.
Said method of manufacture 100 for an improved composition for said melt-bonding road marking compound 130 can comprise preparing said PET component 122 from pulverized plastic. Combining said PET component 122, said pigment component 126, said filler component 128, said silica component 118 and said binder component 120 to form said road marking compound 116. Melting said road marking compound 116 form said melt-bonding road marking compound 130. Selecting an amount of said PET component 122 to maximize PET in said melt-bonding road marking compound 130 while ensuring said melt-bonding road marking compound 130 remains liquid for application to a road surface.
Said method of manufacture 100 for an improved composition for said melt-bonding road marking compound 130 can comprise preparing said PET component 122 from pulverized plastic. Combining said PET component 122, said pigment component 126, said filler component 128, said silica component 118 and said binder component 120 to form said road marking compound 116. Melting said road marking compound 116 form said melt-bonding road marking compound 130. Selecting an amount of said PET component 122 to maximize PET in said melt-bonding road marking compound 130 while ensuring said melt-bonding road marking compound 130 remains liquid for application to a road surface.
Said melt-bonding road marking compound 130 comprises, as a percentage by weight: said silica component 118 comprising 30-45% glass beads, said filler component 128 comprising 20-42% calcium carbonate, said binder component 120 comprising 18-23% thermoplastic resins, and said PET component 122 comprising 1-20% polyethylene terephthalate.
Said method of manufacture 100 for an improved composition for said melt-bonding road marking compound 130 can comprise preparing said PET component 122 from pulverized plastic. Combining said PET component 122, said pigment component 126, said filler component 128, said silica component 118 and said binder component 120 to form said road marking compound 116. Melting said road marking compound 116 form said melt-bonding road marking compound 130.
Selecting an amount of said PET component 122 to maximize PET in said melt-bonding road marking compound 130 while ensuring said melt-bonding road marking compound 130 remains liquid for application to a road surface.
Said PET component 122 comprises glass beads, can be substantially clear, and substantially spherical.
Said PET component 122 comprises glass beads. Said method of manufacture 100 comprises optimizing said bead diameter 504 of said PET component 122 to ensure said melt-bonding road marking compound 130 can flow through screens and nozzles in a typical road paint application equipment.
Said PET component 122 comprises said bead diameter 504 of 400-750 microns.
Said melt-bonding road marking compound 130 comprises, as a percentage by weight: said silica component 118 comprising 30-45% glass beads, said filler component 128 comprising 20-42% calcium carbonate, said binder component 120 comprising 18-23% thermoplastic resins, and said PET component 122 comprising 1-20% polyethylene terephthalate.
Said pigment component 126 comprising 8-15% titanium dioxide.
Said pigment component 126 comprising 1-1.5% chrome yellow 83.
Melting said road marking compound 116 into said melted mixture 124 comprises heating said road marking compound 116 to 400-425° F.
Said binder component 120 includes maleic-modified glyceryl ester of rosin.
Said pigment component 126 can be titanium dioxide.
Said pigment component 126 can be C.I. Pigment Yellow 83.
Said filler component 128 can be calcium carbonate.
Said method of manufacture 100 for an improved composition for said melt-bonding road marking compound 130 can comprise combining said PET component 122, said pigment component 126, said filler component 128, said silica component 118 and said binder component 120 to form said road marking compound 116. Melting said road marking compound 116 form said melt-bonding road marking compound 130. Selecting an amount of said PET component 122 to maximize PET in said melt-bonding road marking compound 130 while ensuring said melt-bonding road marking compound 130 remains liquid for application to a road surface.
Preparing said PET component 122 from PET from pulverized plastic.
Said pigment component 126 comprising 8-15% titanium dioxide.
Said pigment component 126 comprising 1-1.5% chrome yellow 83.
Parts List:
This application claims benefit to and incorporates by reference: U.S. nonprovisional utility patent application Ser. No. 17/705,326 filed 2022 Mar. 27, and Ser. No. 18/169,360 filed 2023 Feb. 15. This application is a continuation-in-part to each of these filings.
| Number | Date | Country | |
|---|---|---|---|
| Parent | 18169360 | Feb 2023 | US |
| Child | 18500813 | US |