Patent Application
20230249272
The following relates to systems and methods for soldering, and in particular to a thermal treatment operation which is applied for preconditioning and/or restoration of a solder joint.
Historically, lead (Pb) containing solders, for example, tin-lead (Sn—Pb) solders, were used in the manufacture of electronics. However, lead and many lead alloys are toxic. Due to increasingly strict worldwide environmental regulations, lead solders are increasingly being replaced with less toxic lead-free solder counterparts that also exhibit low melting points and sufficient conductivity for electronics applications.
Lead-free solders containing alloys of tin (Sn) with silver (Ag) and/or copper (Cu) have been adopted by industry to replace the lead-containing solders. SAC 305 is an example of a tin-silver-copper alloy solder that is widely used in industry. The composition of SAC305 is 96.5% tin, 3% silver and 0.5% copper.
It is commonly known that the solder properties of both Sn—Pb alloys and their replacement Sn—Ag—Cu alloys, such as SAC305, degrade over time. The primary reason for property degradation in Sn—Pb solder is grain growth, whereas in SAC305, the second phase (intermetallic) coarsening results in degradation of the solder properties over time.
Early lead free solders typically required processing temperatures higher than those historically used for production with tin-lead solders. These early lead-free solders therefore required the use of specialized circuit board materials that could withstand the higher temperatures. Lead-free solders comprising alloys of tin (Sn), silver (Ag), copper (Cu) and bismuth (Bi) have been developed for low-temperature solder applications that do not require specialized circuit board materials. Examples of such low temperature lead free solders are described in US 2015/0258636. It has been found that individual lead-free solder joints formed using these alloys are typically composed of a few or even only one Sn-rich grain. As a result, failure of the solder joint may result when cleavage by crack propagation along the grain boundary occurs in response to impact or stress accumulation on the joint. Therefore, the typical grain structure of solder joints formed from tin, silver, copper and bismuth alloys results in unpredictable electronic solder joint reliability, with a wide distribution of lifetimes in the field.
Another problem encountered with lead-free solder joints formed using alloys of tin, silver, copper and bismuth is that the Bi particles are unevenly distributed in the microstructure. The failure mechanism described above, of cleavage by crack propagation along a grain in response to impact or stress accumulation in the joint, is exacerbated by the brittleness of the precipitates.
The failure mechanisms resulting from the few large Sn grains and the uneven distribution of Bi particles may be summarized as failure due to unreliable solder joints caused by segregation of large, hard Bi and intermetallic compound (IMC) particles around unidirectional anisotropic Sn grains. The deformation behavior of as-cast lead-free solder joints in relation to grain size and orientation is described by Tae-Jyu Lee, Bieler and Arfaei. (Tae-Kyu Lee, Bite Zhou, Lauren Blair, Kuo-Chuan Liu, and Thomas R. Bieler, Sn—Ag—Cu Solder Joint Microstructure and Orientation Evolution as a Function of Position and Thermal Cycles in Ball Grid Arrays Using Orientation Imaging Microscopy, Journal of Electronic Materials, DOI: 10.1007/s11664-010-1348-4, 2010 TMS; R. J. Coyle, K. Sweatman and B. Arfaei, Thermal Fatigue Evaluation of Pb-Free Solder Joints: Results, Lessons Learned, and Future Trends, JOM, October 2015.)
It is possible to increase the number of grains of Sn in lead-free electronic solder joints through the use of aluminum (Al) as an additional alloying element. The alloys with Al have a trend to nucleate more Sn grains. However, the structure still consists of a low number of grains compared to Sn—Pb isotropic solder joints. (Iver E. Anderson, Jason W. Walleser, Joel L. Harringa, Fran Laabs and Alfred Kracher, Nucleation Control and Thermal Aging Resistance of Near-Eutectic Sn—Ag—Cu—X Solder Joints by Alloy Design, Journal of Electronic Materials, Vol. 38, No. 12, 2009.) Therefore, alternative solutions to the problem of the number of Sn grains are still needed.
The segregation of Bi particles and the impact of this phenomenon on solder joint reliability have not yet attracted significant research attention. Therefore, solutions to this problem are needed.
Annealing of lead-tin and lead-tin-antimony solders to improve solder stability is described by B.T. Lampe; “Room Temperature Aging Properties of Some Solder Alloys Welding Research Supplement,” October 1976; p330-340 (“Lampe”). Lampe describes changes in the microstructure observed in the lead-containing alloys over a period of aging at room temperature, and found that heating at 200° F. could produce similar characteristics in a tin-lead-antimony alloy, but at a faster rate. Lampe also found that the annealing at 200° F. resulted in a somewhat higher shear strength and hardness in the final stabilized product.
In another study, heat treatment is used to artificially accelerate aging of solder alloys to study the properties of the solder alloys and to predict field behavior over time. In mainstream applications of Sn-based Pb-free solder, properties such as hardness and number of thermal cycles to failure degrade over time. This property degradation is caused by microstructure degradation related to the second phase particles coarsening as described by T. K. Lee. (Tae-Kyu Lee, Hongtao Ma, Kuo-Chuan Liu and Jie Xue, Impact of Isothermal Aging on Long-Term Reliability of Fine-Pitch Ball Grid Array Packages with Sn—Ag—Cu Solder Interconnects: Surface Finish Effects, Journal of Electronic Materials, Vol. 39, No. 12, 2010.)
Beneficial changes in the microstructure of Sn—Zn—Cu alloys by annealing at elevated temperatures for extended time periods was reported by Klasik. (A. Klasik et al. “Relationship Between Mechanical Properties of Lead-Free Solder and Their Heat Treatment Parameters” Journal of Materials Engineering and Performance, vol. 21(5) May 2012, p620-628.) These microstructural changes, observed after heating at elevated temperatures for time periods of from 168 to 24 hours, result in the improvement of the mechanical strength.
It has been found that solder joints (interconnects) in an assembly can be conditioned to improve the solder joint properties. In one aspect the conditioning treatment can improve the solder joint properties by the formation of smaller bismuth particles that are more evenly distributed in the solder joint.
In one aspect there is provided a method for conditioning a solder joint comprising:
In an embodiment of the method the lead free solder joint comprises at least 2 weight percent of Bi. In another embodiment the lead free solder joint further includes Ag and/or Cu. The balance or remainder of the lead free solder joint is Sn.
In another embodiment of the method, the step of heating the assembly to a temperature near the solvus temperature involves heating the assembly to a temperature in the range of up to 15° C. below the solvus temperature and up to 40° C. above the solvus temperature. The solvus temperature for a solder composition may be experimentally determined by methods known in the art, for example, DSC.
Conditioning of the solder joint may occur as part of the initial manufacturing process or may take place after a period of use of the assembly under field conditions. In the case where the conditioning occurs during the manufacturing process (preconditioning) the conditioning step will occur at a point after the step of reflow to form the solder joint and before the assembly is used in the field. Other processing or testing steps may occur in the manufacturing process before or after the conditioning step. In the case where the conditioning occurs after the use of the assembly under field conditions (restoration or reconditioning) the assembly will have had some period of use before the conditioning process is applied. The period of use will depend on factors such as the type of solder, the application that the assembly is used for, and the environment where it is used.
In another aspect there is provided a process for preparing an electronic assembly comprising:
Embodiments will now be described by way of example only with reference to the appended drawings wherein:
The following relates generally to soldering processes and more specifically to lead-free solder containing bismuth. As described below, it has been found that a thermal treatment or processing operation can be applied to such solders to create a more reliable grain-refined solder joint with an even distribution of bismuth across the solder joint. The thermal treatment step can be incorporated into electronic assembly manufacturing, e.g., of circuit boards having soldered components.
As is known in the art, a standard electronics assembly soldering process includes the following steps, which have been implemented in various applications for a long period of time:
It has been determined that for lead-free solders containing bismuth, an additional thermal treatment step can be applied after the initial solder joint formation step, known as reflow, to improve the solder joint properties.
In the process exemplified in
It has also been found that the principles described herein can also be used for the restoration of acceptable solder joint properties after a period of time and possible use has elapsed. For example, restoration may be done after several years of product service. A similar thermal treatment step can be applied to a previously prepared solder joint containing a lead-free bismuth containing alloy. The thermal treatment step applied for “restoration” can be used to restore a more reliable grain-refined solder joint with even distribution of Bi across the solder joint, as part of a restoration and refurbishment process, after the solder interconnect structure has coarsened over time in service.
In a particular aspect the particles of Bismuth in a bismuth containing lead-free solder joint after conditioning treatment will be smaller and more evenly distributed than the particles before conditioning.
In a particular embodiment, the lead-free solder alloy containing bismuth further contains tin. In still a further embodiment the solder alloy includes one or more of silver and copper. In a further embodiment, the solder has a bismuth concentration between about 1 and about 10 weight percent. In a further embodiment the bismuth concentration is equal to or greater than 2 weight percent. In a particular embodiment, the bismuth concentration is between about 2 and about 7 weight percent. In another embodiment, the composition of lead-free bismuth containing solder has from 0 to 5% Ag, 0 to 1% Cu and 1 to 10% Bi with the remainder being Sn (percentages are weight percent). In a further embodiment the composition of lead-free bismuth containing solder has from >0 to 5% Ag, >0 to 1% Cu and from about 2 to 7% Bi with the remainder being Sn (percentages are weight percent).
The term “pinning” as used herein refers to the action of a point defect which may be a second phase precipitate in a material which acts as a barrier to movement of a dislocation in the crystal structure.
The term “intermetallic compound” or “IMC” is a solid-state compound exhibiting metallic bonding, defined stoichiometry and ordered crystal structure.
The term “creep” or “creep rate” as used herein means the tendency of a solid material to move slowly or deform permanently under the influence of mechanical stresses, and is measured by techniques such as nano-indentation.
The thermal treatment step 16 is described in more detail below, making reference to
It is generally known that solder interconnects with desirable mechanical properties can be achieved by using a material having a homogeneous structure with small grains of ductile matrix and an evenly distributed second phase pinning the grain boundaries. These features strengthen the solder material by acting as a barrier which prevents a dislocation which may occur in the material from traveling through a lattice when a relatively small stress is applied.
It has been recognized that individual lead-free solder interconnects (solder joints) are typically composed of a few or even only one Sn-rich grain.
The method of conditioning and in particular thermal treatment step 16 described herein is aimed at converting the as-cast microstructure of the lead-free bismuth-containing alloys having large Sn dendrites (one or several grains in a solder joint) and segregated, relatively large Bi particles in the interdendritic spaces, into the desired more reliable structure having many small Sn grains and more evenly distributed Bi particles.
The overall performance of lead-free solder interconnects is dictated by the properties of β-Sn, which exhibits a significant anisotropic nature due to its special body-centered tetragonal (BCT) crystal structure with lattice parameters of a = 0.5632 nm, c = 0.3182 nm, and c/a = 0.547. Therefore, the small number of grains in an interconnect and the significant inherent anisotropic nature of the thermomechanical properties of β-Sn make Pb-free solder interconnects behave differently from their Sn—Pb counterparts, and the crystallographic orientation of each individual grain plays a very important role in dictating the overall thermomechanical performance. The stress state and strain history of every joint is different, because the orientation and boundary conditions are different.
These anisotropic interconnects can result in at worst, unpredictable performance, and at best, electronic solder joint reliability with a wide distribution of lifetimes in the field. The specific failure mechanism that is known to occur is early life solder joint cleavage by crack propagation along a grain in response to impact or stress accumulation in the joint.
It has also been recognized that after solidification of a lead-free bismuth-containing solder joint, the Bi particles are unevenly distributed in the microstructure as illustrated in
The preconditioning and restoration treatments shown in
The thermal treatment step 16 is utilized to address the aforementioned issue with random crystal orientations and uneven microstructures. The thermal treatment step 16 addresses this issue by obtaining a solder joint having many small randomly oriented grains with more uniformly distributed Bi particles. The resulting microstructure is somewhat similar to Sn-Pb.
The recrystallization process can significantly change the crystallographic orientation and microstructure, and therefore, the mechanical properties of the bismuth-containing, lead-free solder interconnects.
According to the dispersion strengthening theory, the presence of second-phase particles can reinforce the solder matrix and inhibit the localized softening and deformation in the recrystallized region, improving the overall mechanical performance of lead-free solder interconnects.
The SEM image in
Table 1 shows the compositions of a variety of alloys that were investigated indicating the percent weight of the components. Where the percentage of Sn is not defined in the composition, Sn is assumed to make up the balance of the composition. SnPb and SAC305 were used as standards for comparison. Different thermal treatments were performed on the alloy compositions both above the temperature of Bi dissolution in Sn (above solvus) and below the temperature of Bi dissolution in Sn (below solvus). The solvus temperature for each alloy containing Bi was experimentally determined using DSC (differential scanning calorimetry) and microstructural analysis. By way of example,
Table 2 describes the thermal treatment parameters applied to various soldering alloys; the compositions of the alloys tested are defined in Table 1. (The “+” symbol indicates that the alloy has been tested under the condition described in the left hand columns.) The solvus line for the lead-free alloys can be found in
Data from the experiments described in Table 2 have shown that the desirable results of grain refinement and more even distribution of small Bi particles may be achieved by heating the alloys above solvus or to a temperature in the proximity of solvus. The experimental data showed that with exposure for more than 24 hours at temperatures above solvus or with exposure for 100 hours or more at temperatures below solvus good results in terms of grain refinement and more even distribution of small Bi particles is achieved.
It has been found that by employing multiple cycles of heating and cooling, the amount of time required to achieve the desired results of grain refinement and more even Bi particle distribution can be dramatically reduced. While experimental trials using as many as 8 heating cycles were carried out, it was found that even using as few as two cycles with 10 minutes dwell at a temperature above solvus results in a structure with small grains with different orientation.
Accordingly, a thermal treatment method has been discovered that can improve solder joints made from Pb-free alloys containing Bi. In a particular embodiment the heating temperature will be a temperature on or near the solvus line for the composition. A temperature near the solvus temperature may include temperatures up to about 15° C. below the solvus, up to 10° C. below the solvus or up to 5° C. below the solvus. In a further embodiment, a temperature near the solvus may include temperatures up to about 40° C. above the solvus, up to about 30° C. above the solvus temperature, up to 20° C. above the solvus, up to 10° C. above the solvus or up to 5° C. above the solvus.
In a further aspect the Pb-free bismuth containing alloy is an alloy comprising at least 2%Bi by weight. In yet another aspect the alloy has from about 0 to about 5% Ag, about 0 to about 1% Cu and about 1 to about 10% Bi with the remainder being Sn (percentages are weight percent). In a further embodiment the composition of lead-free bismuth containing solder has from >0 to about 5% Ag, >0 to about 1% Cu and from about 2 to about 7% Bi with the remainder being Sn (percentages are weight percent).
In still a further aspect the temperature for the thermal treatment whether for annealing or cyclic treatment will be selected such that it does not exceed a temperature which would damage other aspects of the circuit board of which the solder forms a part during the selected time duration of the heating.
In a particular aspect the thermal treatment step 16 includes the following additional sub-steps after the reflow:
The compositions are defined with respect to their weight percentages with Sn making up the balance of the composition.
Preconditioning may be done for several minutes or several hours and up to several days, in order to achieve full dissolution of the Bi particles and even distribution of the Bi across all grains in the solder joint. The time and temperature duration is dependent on the selected Bi-containing alloy. For example, Violet alloy requires up to 50 hours of thermal treatment for full Bi dissolution. Pre-conditioning (or reconditioning) under non-optimized conditions, for example, at a temperature or for a time that is not optimal may result in partial dissolution which may also provide Bi particle size and/or particle distribution which is improved over samples that have not undergone a thermal treatment step. Preconditioning or reconditioning under non-optimized conditions may still provide solder interconnects having acceptable properties depending on the application.
In practice the time and temperature for the annealing or heat cycling step may be selected to provide suitable conditioning results and may also be adapted or conformed to other manufacturing requirements. For example, temperatures in a range from about 25° C. to about 180° C., from about 25° C. to about 160° C., from about 25° C. to about 130° C., from about 75° C. to about 180° C., from about 75° C. to about 160° C., or from about 75° C. to about 130° C. may be used. In another example, the temperature may be 125±15° C. or 120±5° C. The time for a single step annealing process may, for example, range from about 10 minutes to about 300 hours, from about 10 minutes to about 100 hours, from about 10 minutes to about 50 hours, from about 10 minutes to about 24 hours, from about 2 hours to about 50 hours or from about 2 hours to about 24 hours. The time duration for one cycle of a multicycle heating process may be from about 5 min to about 8 hours.
Solder joint recrystallization from anisotropically oriented large grains to a grain structure of many small grains isotropically oriented (non-oriented) has been found to result in improved solder joint reliability due to improved creep and fatigue behaviour and improved global modulus.
The interim indicator of solder joint improvement is hardness, which is known to correlate to solder joint reliability. In contrast to the SnAgCu (SAC) alloy, which loses its hardness over time at room and elevated temperature, alloys with Bi are stable and keep constant hardness under the same conditions.
It has been found therefore that alloys of Sn(Ag)CuBi, as shown in
The reliability of these alloys in this respect has already been published. A summary of the findings on the reliability studies of SnAgCuBi alloy can be found in the reference, Journal of Microelectronics and Electronic Packaging (2015) 12, 1-29.
Bismuth containing alloys formed excellent joints on organic solderability preservative (OSP) finish. The interfacial intermetallic layer was comparable to SnPb solders in thickness and shape, and thinner than in SAC305. The solder composition Sn2.25Ag0.5Cu6Bi (Violet), is compatible not only with OSP but also with electroless nickel immersion gold (ENIG) and electroless nickel electroless palladium immersion gold (ENEPIG), and forms excellent solder joints with uniform intermetallic layers on both BGA and leaded components.
All combinations of alloys tested (Paul (Sn3.4Ag4.8Bi) Violet, Orchid (Sn2Ag7Bi), SAC305, and SnPb), surface finishes (OSP, ENIG, and ENEPIG), and board laminate (normal and high glass transition (Tg)) passed the aerospace ATC qualification requirement of 1,000 cycles of 55° C. to 125° C. There was no solder joint failure on both high gloss and normal Tg boards up to 3,010 cycles for Pb-free lower melt (Paul, Violet, and Orchid) and SAC305 alloys. All three experimental alloys (i.e., Paul, Violet, and Orchid) showed excellent performance in harsh-environment thermal cycling.
The vibration failure analysis was based on 1 million cycles at 2G and 5G, for failures found by resistance monitoring. The lowest failure rate found was for Violet at both the 2-G and 5-G levels; the failure rates were better than for SnAgCu solder alloys.
The microstructure improvement over time at 125° C. is shown in
Currently the electronics industry standards governing the use of soldering materials focus on the use of approved solder metal alloys, acceptable contaminant levels, and appropriate flux materials under appropriate manufacturing conditions. Specific process parameters for high reliability are not addressed. The relevant electronic industry IPC standards are listed below.
The standards include IPC J-STD-001 Requirements for Soldered Electrical and Electronic Assemblies, J-STD-001xS Space Hardware Addendum, J-STD-004, J-STD-005 Requirements for Soldering Pastes, J-STD-006 Requirements for Electronic Grade Solder Alloys and Fluxed and Non-Fluxed Solid Solders for Electronic Soldering Applications, IPC-A-610 Acceptability of Electronic Assemblies, IPC/WHMA-A-620 Space Hardware Addendum Space Applications Electronic Hardware Addendum for IPC/WHMA-A-620.]
The thermal process parameters for each material are different and may be experimentally determined and verified.
The thermal treatment process described above may be used in the electronics assembly manufacturing processes.
With respect to the application of the thermal treatment step 16 to restoration, it has also been recognized that lead-free solder interconnect microstructures experience coarsening over time. Sn grain size increases and Bi or other precipitants get bigger and form solid rims around grain boundaries. These properties are degrading to the function of the solder joint.
The thermal treatment step 16 allows one to restore the microstructure and properties of lead-free alloys with solid solution and precipitation hardening.
Heating the assembly to a temperature near the solvus, allows Bi particles to be dissolved in Sn. For example, the assembly can be heated to about 65° to 100° C., for about 15 to 30 min. Following the heating step, the material is allowed to cool. During cooling, new small particles will precipitate evenly in the Sn matrix, which will improve thermomechanical properties.
Further evidence of the improvement of mechanical properties by the conditioning treatment after aging in the field is provided by creep rate experimental data.
For simplicity and clarity of illustration, where considered appropriate, reference numerals may be repeated among the figures to indicate corresponding or analogous elements. In addition, numerous specific details are set forth in order to provide a thorough understanding of the examples described herein. However, it will be understood by those of ordinary skill in the art that the examples described herein may be practiced without these specific details. In other instances, well-known methods, procedures and components have not been described in detail so as not to obscure the examples described herein. Also, the description is not to be considered as limiting the scope of the examples described herein.
It will be appreciated that the examples and corresponding diagrams used herein are for illustrative purposes only. Different configurations and terminology can be used without departing from the principles expressed herein.
The steps or operations in the flow charts and diagrams described herein are just for example. There may be many variations to these steps or operations without departing from the principles discussed above. For instance, the steps may be performed in a differing order, or steps may be added, deleted, or modified.
Although the above principles have been described with reference to certain specific examples, various modifications thereof will be apparent to those skilled in the art as outlined in the appended claims.
The disclosures of all prior art recited or described herein are hereby incorporated by reference in their entirety.
The present application is a continuation of U.S. Pat. Application No. 16/100,747, filed Aug. 10, 2018, which in turn was a continuation of PCT Application No. PCT/CA2017/050164 filed on Feb. 10, 2017, which claims priority to U.S. Provisional Application No. 62/294,065 filed on Feb. 11, 2016, all of which are hereby incorporated herein by reference.
| Number | Date | Country | |
|---|---|---|---|
| 62294065 | Feb 2016 | US |
| Number | Date | Country | |
|---|---|---|---|
| Parent | 16100747 | Aug 2018 | US |
| Child | 17953315 | US | |
| Parent | PCT/CA2017/050164 | Feb 2017 | WO |
| Child | 16100747 | US |