This application claims priority to and the benefit of Korean Patent Application No. 10-2012-0157577, filed in the Korean Intellectual Property Office on Dec. 28, 2012, and Korean Patent Application No. 10-2013-0037003, filed in the Korean Intellectual Property Office on Apr. 4, 2013, the entire disclosure of each of which is incorporated herein by reference.
Thermoplastic resin compositions and articles including the same are disclosed.
Acrylate-styrene-acrylonitrile (ASA) resins have excellent weatherability and thus are widely used in building materials, exterior part materials for vehicles, and the like. However, the ASA resins can have poor impact resistance. To improve impact resistance, ASA resins are often used in the form of a composition including a rubber polymer. In such a case, the ASA resin compositions require a large amount of the rubber polymer in order to be applicable for uses requiring a high level of impact strength. Such a large amount of the rubber polymer, however, may result in poor heat resistance, which can limit their use in applications requiring a high level of heat resistance such as exterior part materials for vehicles.
In an attempt to provide an alternative, a method of enhancing heat resistance and impact resistance by alloying the ASA resin with a polycarbonate (PC) resin that has excellent heat resistance has been proposed. The PC/ASA resin is often used for a radiator grill for vehicles. However, unlike the PC resin having a high refractive index, the ASA resin has a relatively low level of refractive index. Thus, when the ASA resin is combined with the PC resin, the resulting resin composition may provide a molded product having poor coloring properties, which can limit its use in various products.
One embodiment provides a thermoplastic resin composition that can exhibit enhanced coloring properties of PC/ASA resins. Another embodiment provides a molded product including the resin composition.
According to one embodiment, a thermoplastic resin composition includes: (A) a polycarbonate resin; (B) an acrylate-styrene-acrylonitrile (ASA) graft copolymer; (C) a random copolymer of an alkyl(meth)acrylate, an aromatic vinyl compound, and a vinyl cyanide compound; and (D) a copolymer of an aromatic methacrylate and a monofunctional unsaturated monomer.
The thermoplastic resin composition may include (A) about 40 to about 70% by weight of a polycarbonate resin; (B) about 20 to about 40% by weight of an acrylate-styrene-acrylonitrile (ASA) graft copolymer; (C) about 9 to about 29% by weight of a random copolymer of an alkyl(meth)acrylate, an aromatic vinyl compound, and a vinyl cyanide compound; and (D) greater than or equal to about 0.1% by weight and less than about 10% by weight of a copolymer of an aromatic methacrylate and a monofunctional unsaturated monomer. In the thermoplastic resin composition, the sum of the amounts of the random copolymer (C) of an alkyl(meth)acrylate, an aromatic vinyl compound, and a vinyl cyanide compound and the copolymer (D) of an aromatic methacrylate and a monofunctional unsaturated monomer is less than about 30% by weight based on the total weight of the composition.
In the thermoplastic resin composition, the amount of the alkyl(meth)acrylate compound in the random copolymer (C) of an alkyl(meth)acrylate, an aromatic vinyl compound, and a vinyl cyanide compound may range from about 50% by weight to about 89% by weight based on the total weight of the random copolymer (C) of an alkyl(meth)acrylate, an aromatic vinyl compound, and a vinyl cyanide compound.
In the random copolymer (C) of an alkyl(meth)acrylate, an aromatic vinyl compound, and a vinyl cyanide compound, the alkyl(meth)acrylate compound may include methyl acrylate, ethyl acrylate, methyl methacrylate, and/or ethyl methacrylate, the aromatic vinyl compound may include styrene, α-methylstyrene, and/or p-methylstyrene, and the vinyl cyanide compound may include acrylonitrile and/or methacrylonitrile.
The copolymer (D) of an aromatic vinyl compound and a monofunctional unsaturated monomer may include a copolymer of an aromatic methacrylate represented by Chemical Formula 1 and a monofunctional unsaturated monomer or a mixture thereof:
wherein m is an integer of 0 to 10, Y is a single bond, —O—, or —S—, and Ar is phenyl, methyl phenyl, methyl ethyl phenyl, propyl phenyl, methoxy phenyl, cyclohexyl phenyl, chloro phenyl, bromo phenyl, phenyl phenyl, or benzyl phenyl.
In the thermoplastic resin composition, the monofunctional unsaturated monomer in the copolymer (D) of an aromatic vinyl compound and a monofunctional unsaturated monomer can include a (meth)acrylic acid ester, an unsaturated carboxylic acid, an acid anhydride, an ester containing a hydroxyl group, and/or a (meth)acrylamide.
In the thermoplastic resin composition, the copolymer (D) of an aromatic vinyl compound and a monofunctional unsaturated monomer can have a weight average molecular weight of about 3,000 g/mol to about 30,000 g/mol.
In another embodiment, a molded product including the thermoplastic resin composition is provided.
The PC/ASA resin composition includes a random copolymer of an alkyl(meth)acrylate, an aromatic vinyl compound, and a vinyl cyanide compound, and a copolymer of an aromatic methacrylate and a monofunctional unsaturated monomer. A molded product preparing using the same can have enhanced coloring properties.
The present invention will be described more fully hereinafter in the following detailed description of the invention, in which some but not all embodiments of the invention are described. Indeed, this invention may be embodied in many different forms and should not be construed as limited to the embodiments set forth herein; rather, these embodiments are provided so that this disclosure will satisfy applicable legal requirements.
As used herein, when a specific definition is not otherwise provided, the term “(meth)acrylate” refers to an acrylate and/or methacrylate, the term “(meth)acrylic acid” refers to acrylic acid and/or methacrylic acid, and the term “(meth)acrylamide” refers to acrylamide and/or methacrylamide. As used herein, when a specific definition is not otherwise provided, the term “alkyl” refers to C1 to C30 alkyl, for example, C1 to C20 alkyl.
As used herein, when a specific definition is not otherwise provided, the term “copolymerization” refers to block copolymerization, random copolymerization, graft copolymerization, and/or alternating copolymerization, and the term “copolymer” refers to a block copolymer, a random copolymer, a graft copolymer, and/or an alternating copolymer.
A thermoplastic resin composition according to one embodiment includes: (A) a polycarbonate resin; (B) an acrylate-styrene-acrylonitrile (ASA) graft copolymer; (C) a random copolymer of an alkyl(meth)acrylate, an aromatic vinyl compound, and a vinyl cyanide compound; and (D) a copolymer of an aromatic methacrylate and a monofunctional unsaturated monomer.
(A) Polycarbonate (PC) resin
In the thermoplastic resin composition, the polycarbonate is a polyester having a carbonate bond. The type of polycarbonate is not particularly limited and any polycarbonate available in the field of resin compositions may be used.
For example, the polycarbonate resin may be prepared by reacting a diphenol with a compound selected from the group consisting of phosgene, a halogen formate, a carbonate ester, and combinations thereof. Examples of the diphenols may include, but are not limited to, hydroquinone, resorcinol, 4,4′-dihydroxydiphenyl, 2,2-bis(4-hydroxyphenyl)propane, 2,4-bis(4-hydroxyphenyl)-2-methylbutane, 1,1-bis(4-hydroxyphenyl)cyclohexane, 2,2-bis(3-chloro-4-hydroxyphenyl)propane, 2,2-bis(3,5-dichloro-4-hydroxyphenyl)propane, and the like, and combinations thereof.
The polycarbonate resin may have a weight average molecular weight (Mw) of about 5,000 g/mol to about 200,000 g/mol, for example about 5,000 g/mol to about 40,000 g/mol, for mechanical properties and moldability.
The polycarbonate resin may be a copolymer or mixture of copolymers prepared from two or more diphenols. The polycarbonate resin may also include a linear polycarbonate resin, a branched polycarbonate resin, a polyester carbonate copolymer, and the like, or a combination thereof.
The linear polycarbonate resin may include a bisphenol-A based polycarbonate resin. The branched polycarbonate resin may include one produced by reacting a multi-functional aromatic compound such as trimellitic anhydride, trimellitic acid, and the like with one or more diphenols and a carbonate. A repeating unit derived from the multi-functional aromatic compound may be included in an amount of about 0.05 to about 2 mol % based on the total weight of repeating units of the polycarbonate resin. The polyester carbonate copolymer resin may include one produced by reacting a difunctional carboxylic acid with one or more diphenols and a carbonate. The carbonate may include a diaryl carbonate such as diphenyl carbonate and ethylene carbonate.
The thermoplastic resin composition may include the polycarbonate resin (A) in an amount of about 40 wt % to about 70 wt %, for example about 50 wt % to about 60 wt %, based on the total weight of the thermoplastic resin composition. In some embodiments, the thermoplastic resin composition may include the polycarbonate resin in an amount of about 40, 41, 42, 43, 44, 45, 46, 47, 48, 49, 50, 51, 52, 53, 54, 55, 56, 57, 58, 59, 60, 61, 62, 63, 64, 65, 66, 67, 68, 69, or 70wt %. Further, according to some embodiments of the present invention, the amount of the polycarbonate resin can be in a range from about any of the foregoing amounts to about any other of the foregoing amounts.
(B) Graft Copolymer of Acrylate-Styrene-Acrylonitrile (ASA)
The graft copolymer of acrylate-styrene-acrylonitrile (ASA) is a core-shell type copolymer prepared by graft-polymerizing an acrylate rubber copolymer with a styrene monomer and an acrylonitrile monomer. The types of the ASA graft copolymers used in the thermoplastic resin composition are not particularly limited and may be properly chosen as necessary without undue experimentation by the skilled artisan.
The ASA graft copolymer may be prepared by any methods known in the art. By way of a non-limiting example, an acrylate rubber polymer can be prepared, and a styrene monomer and an acrylonitrile monomer can be graft-copolymerized to form at least one layer of a shell on the core including at least one layer of the acrylate rubber polymer being formed thereon.
The acrylate rubber polymer may be prepared using an acrylate monomer as a main monomer. Examples of the acrylate monomer may include without limitation ethyl acrylate, butyl acrylate, 2-ethylhexyl acrylate, hexyl acrylate, and the like, and combinations thereof. The acrylate monomer may be copolymerized with at least one other monomer that may undergo radical polymerization. In the copolymerization, the other monomer that may undergo radical polymerization can be used in an amount of about 5 to about 30 wt %, for example about 10 to about 20 wt %, based on the total weight of the acrylate rubber polymer.
Examples of the styrene monomer included in the shell may include without limitation styrene, α-methylstyrene, p-methylstyrene, and the like, and combinations thereof.
Examples of the acrylonitrile monomer may include without limitation acrylonitrile, methacrylonitrile, and the like, and combinations thereof.
In a non-limiting example, the ASA graft copolymer may be a double core-shell type ASA graft copolymer produced by preparing a butyl acrylate rubber copolymer having a double core structure including an inner core of a copolymer of butyl acrylate and styrene and an outer core of a butyl acrylate polymer, and conducting graft polymerization of an acrylonitrile monomer and a styrene monomer onto the butyl acrylate rubber copolymer of the double core structure via emulsion polymerization.
The ASA graft copolymer may include the acrylate rubber polymer in an amount of about 30 to about 70 parts by weight, for example about 40 to about 60 parts by weight, based on about 100 parts by weight of the ASA graft copolymer. In some embodiments, the ASA graft copolymer may include the acrylate rubber polymer in an amount of about 30, 31, 32, 33, 34, 35, 36, 37, 38, 39, 40, 41, 42, 43, 44, 45, 46, 47, 48, 49, 50, 51, 52, 53, 54, 55, 56, 57, 58, 59, 60, 61, 62, 63, 64, 65, 66, 67, 68, 69, or 70 parts by weight. Further, according to some embodiments of the present invention, the amount of the acrylate rubber polymer can be in a range from about any of the foregoing amounts to about any other of the foregoing amounts.
The ASA graft copolymer may include the styrene monomer and the acrylonitrile monomer in an amount of about 30 to about 70 parts by weight, for example about 40 to about 60 parts by weight, based on about 100 parts by weight of the ASA graft copolymer. In some embodiments, the ASA graft copolymer may include the styrene monomer and the acrylonitrile monomer in an amount of about 30, 31, 32, 33, 34, 35, 36, 37, 38, 39, 40, 41, 42, 43, 44, 45, 46, 47, 48, 49, 50, 51, 52, 53, 54, 55, 56, 57, 58, 59, 60, 61, 62, 63, 64, 65, 66, 67, 68, 69, or 70 parts by weight. Further, according to some embodiments of the present invention, the amount of the styrene monomer and the acrylonitrile monomer can be in a range from about any of the foregoing amounts to about any other of the foregoing amounts.
The shell may include the styrene monomer in an amount of about 50 to about 80% by weight, for example about 60 to about 70% by weight, based on the total weight of the shell. In some embodiments, the shell may include the styrene monomer in an amount of 50, 51, 52, 53, 54, 55, 56, 57, 58, 59, 60, 61, 62, 63, 64, 65, 66, 67, 68, 69, 70, 71, 72, 73, 74, 75, 76, 77, 78, 79, or 80% by weight. Further, according to some embodiments of the present invention, the amount of the styrene monomer can be in a range from about any of the foregoing amounts to about any other of the foregoing amounts.
The shell may include the acrylonitrile monomer in an amount of about 20 to about 50% by weight, for example, about 30 to about 40% by weight, based on the total weight of the shell. In some embodiments, the shell may include the acrylonitrile monomer in an amount of about 20, 21, 22, 23, 24, 25, 26, 27, 28, 29, 30, 31, 32, 33, 34, 35, 36, 37, 38, 39, 40, 41, 42, 43, 44, 45, 46, 47, 48, 49, or 50% by weight. Further, according to some embodiments of the present invention, the amount of the acrylonitrile monomer can be in a range from about any of the foregoing amounts to about any other of the foregoing amounts.
The thermoplastic resin composition may include the ASA graft copolymer in an amount of about 20 to about 40% by weight, for example about 20 to about 30% by weight, based on the total weight of the resin composition. In some embodiments, the thermoplastic resin composition may include the ASA graft copolymer in an amount of about 20, 21, 22, 23, 24, 25, 26, 27, 28, 29, 30, 31, 32, 33, 34, 35, 36, 37, 38, 39, or 40% by weight. Further, according to some embodiments of the present invention, the amount of the the ASA graft copolymer can be in a range from about any of the foregoing amounts to about any other of the foregoing amounts.
(C) Random Copolymer Including an Alkyl(Meth)Acrylate Compound, an Aromatic Vinyl Compound, and a Vinyl Cyanide Compound
The thermoplastic resin composition includes a random copolymer including an alkyl(meth)acrylate compound, an aromatic vinyl compound, and a vinyl cyanide compound.
Examples of the alkyl(meth)acrylate compound may include without limitation methyl acrylate, ethyl acrylate, methyl methacrylate, ethyl methacrylate, and the like, and combinations thereof.
Examples of the aromatic vinyl compound may include without limitation styrene, C1 to C4 alkyl substituted styrene such as α-methylstyrene, halogen substituted styrene, and the like, and combinations thereof.
Examples of the vinyl cyanide compound may include without limitation acrylonitrile, methacrylonitrile, and the like, and combinations thereof.
The random copolymer may include the alkyl(meth)acrylate compound in an amount of about 50 to about 89% by weight, for example about 60 to about 80% by weight, based on the total weight of the random copolymer (C). In some embodiments, the random copolymer may include the alkyl(meth)acrylate compound in an amount of about 50, 51, 52, 53, 54, 55, 56, 57, 58, 59, 60, 61, 62, 63, 64, 65, 66, 67, 68, 69, 70, 71, 72, 73, 74, 75, 76, 77, 78, 79, 80, 81, 82, 83, 84, 85, 86, 87, 88, or 89% by weight. Further, according to some embodiments of the present invention, the amount of the alkyl(meth)acrylate compound can be in a range from about any of the foregoing amounts to about any other of the foregoing amounts.
When the amount of the alkyl(meth)acrylate compound is within the above range, the thermoplastic resin composition including the random copolymer (C) may have significantly enhanced coloring properties and improved weatherability without having a negative influence on other properties of the resin such as heat resistance, flowability, and the like.
The random copolymer may include the aromatic vinyl compound in an amount of about 10 to about 30% by weight, based on the total weight of the random copolymer (C). In some embodiments, the random copolymer may include the aromatic vinyl compound in an amount of about 10, 11, 12, 13, 14, 15, 16, 17, 18, 19, 20, 21, 22, 23, 24, 25, 26, 27, 28, 29, or 30% by weight. Further, according to some embodiments of the present invention, the amount of the aromatic vinyl compound can be in a range from about any of the foregoing amounts to about any other of the foregoing amounts.
The random copolymer may include the vinyl cyanide compound in an amount of about 1 to about 20% by weight, based on the total weight of the random copolymer (C). In some embodiments, the random copolymer may include the vinyl cyanide compound in an amount of about 1, 2, 3, 4, 5, 6, 7, 8, 9, 10, 11, 12, 13, 14, 15, 16, 17, 18, 19, or 20% by weight. Further, according to some embodiments of the present invention, the amount of the vinyl cyanide compound can be in a range from about any of the foregoing amounts to about any other of the foregoing amounts.
The random copolymer (C) may have a weight average molecular weight of about 10,000 to about 200,000 g/mol, for example, about 50,000 to about 150,000 g/mol.
Without wishing to be bound any theory of the invention, the random copolymer (C) is currently believed to enhance the coloring properties of the molded product prepared from the resin composition based on the following reasons. When a resin composition including the polycarbonate resin and the ASA graft copolymer is melt-kneaded and extruded, domains of the ASA graft copolymer are dispersed in the polycarbonate matrix. The random copolymer (C) may be included in the domains of the ASA graft copolymer. In comparison with a copolymer of an aromatic vinyl monomer and a vinyl cyanide monomer having no alkyl(meth)acrylate compound, the random copolymer (C) includes about 50 to about 89% by weight of the alkyl(meth)acrylate compound and thus the difference of the refractive index between the ASA graft copolymer and the random copolymer (C) can be significantly decreased. When the random copolymer (C) is used together with (D) a copolymer of an aromatic methacrylate and a mono-functional unsaturated monomer, the compatibility between the polycarbonate and other components may be improved in the resulting resin composition, and at the same time, the difference of the refractive index in the domains including the ASA graft copolymer may be minimized. As a result, it can become possible for the resulting resin composition to have greatly enhanced coloring properties with minimal or no negative influences on other properties such as heat resistance, flowability, mechanical strength, and the like.
The thermoplastic resin composition may include the random copolymer (C) including the alkyl(meth)acrylate compound, the aromatic vinyl compound, and the vinyl cyanide compound in an amount of about 9 to about 29% by weight, for example about 10 to about 20% by weight, based on the total weight of the thermoplastic resin composition. In some embodiments, the thermoplastic resin composition may include the random copolymer (C) including the alkyl(meth)acrylate compound, the aromatic vinyl compound, and the vinyl cyanide compound in an amount of about 9, 10, 11, 12, 13, 14, 15, 16, 17, 18, 19, 20, 21, 22, 23, 24, 25, 26, 27, 28, or 29% by weight. Further, according to some embodiments of the present invention, the amount of the random copolymer (C) can be in a range from about any of the foregoing amounts to about any other of the foregoing amounts.
(D) Copolymers Including an Aromatic Methacrylate and a Mono-Functional Unsaturated Monomer
The thermoplastic resin composition includes (D) a copolymer including an aromatic methacrylate and a mono-functional unsaturated monomer. The copolymer (D) of the aromatic methacrylate and the mono-functional unsaturated monomer may include a copolymer of an aromatic methacrylate represented by Chemical Formula 1 and a monofunctional unsaturated monomer or a mixture thereof:
wherein m is an integer of 0 to 10, Y is a single bond, —O—, or —S—, and Ar is phenyl, methyl phenyl, methyl ethyl phenyl, propyl phenyl, methoxy phenyl, cyclohexyl phenyl, chloro phenyl, bromo phenyl, phenyl phenyl, or benzyl phenyl.
Examples of the aromatic methacrylate may include without limitation phenoxy methacrylate, 2-ethylphenoxy methacrylate, benzyl methacrylate, phenyl methacrylate, 2-ethylthiophenyl methacrylate, 2-phenylethyl methacrylate, 3-phenyl propyl methacrylate, 4-phenylbutyl methacrylate, and the like, and combinations thereof.
Examples of the mono-functional unsaturated monomer may include without limitation (meth)acrylic acid esters, unsaturated carboxylic acids, acid anhydrides, hydroxyl group-containing esters, (meth)acrylamide monomers, and the like, and combinations thereof. Specific examples of the monofunctional unsaturated monomer may include, but are not limited to, methacrylic acid esters such as methyl methacrylate, ethyl methacrylate, propyl methacrylate, butyl methacrylate, and benzyl methacrylate; acrylic acid esters such as methyl acrylate, ethyl acrylate, propyl acrylate, butyl acrylate, and 2-ethyl hexyl acrylate; unsaturated carboxylic acids such as acrylic acid and methacrylic acid; acid anhydrides such as maleic anhydride; hydroxyl group containing esters such as 2-hydroxyethyl acrylate, 2-hydroxypropyl acrylate, and monoglycerol acrylate; and (meth)acrylamides such as acrylamide and methacrylamide.
The copolymer (D) including the aromatic methacrylate and the mono-functional unsaturated monomer may be prepared by co-polymerizing about 20 to about 60% by weight, for example about 20 to about 40% by weight, of the aromatic methacrylate, and about 40 to about 80% by weight, for example about 60 to about 80% by weight, of the mono-functional unsaturated monomer based on the total weight of the copolymer (D). The copolymer may be polymerized via bulk polymerization, emulsion polymerization, and suspension polymerization as known in the art.
In some embodiments, the copolymer (D) may include the aromatic methacrylate in an amount of about 20, 21, 22, 23, 24, 25, 26, 27, 28, 29, 30, 31, 32, 33, 34, 35, 36, 37, 38, 39, 40, 41, 42, 43, 44, 45, 46, 47, 48, 49, 50, 51, 52, 53, 54, 55, 56, 57, 58, 59, or 60% by weight. Further, according to some embodiments of the present invention, the amount of the aromatic methacrylate can be in a range from about any of the foregoing amounts to about any other of the foregoing amounts.
In some embodiments, the copolymer (D) may include the mono-functional unsaturated monomer in an amount of about 40, 41, 42, 43, 44, 45, 46, 47, 48, 49, 50, 51, 52, 53, 54, 55, 56, 57, 58, 59, 60, 61, 62, 63, 64, 65, 66, 67, 68, 69, 70, 71, 72, 73, 74, 75, 76, 77, 78, 79, or 80% by weight. Further, according to some embodiments of the present invention, the amount of the mono-functional unsaturated monomer can be in a range from about any of the foregoing amounts to about any other of the foregoing amounts.
The copolymer (D) of the aromatic methacrylate and the mono-functional unsaturated monomer may act as a compatibilizer that can facilitate the uniform mixing of the polycarbonate and other components (e.g., the ASA graft copolymer and the like) in the thermoplastic resin compositions. In this context, the copolymer (D) of the aromatic methacrylate and the mono-functional unsaturated monomer may have a weight average molecular weight of about 3,000 to about 30,000 g/mol, for example about 5,000 to about 20,000 g/mol, and as another example about 8,000 to about 15,000 g/mol.
The thermoplastic resin composition includes the copolymer (D) including the aromatic methacrylate and the mono-functional unsaturated monomer (as the compatibilizer) together with the random copolymer (C) including the alkyl(meth)acrylate compound, the aromatic vinyl compound, and the vinyl cyanide compound so that the difference in the refractive index between the components can be reduced and the compatibility therebetween may be enhanced. Therefore, the resin composition may provide a molded product having significantly enhanced coloring properties with minimal or no loss of thermal properties such as heat resistance and mechanical strength such as impact resistance.
The thermoplastic resin composition may include the copolymer (D) including the aromatic methacrylate and the mono-functional unsaturated monomer in an amount of greater than or equal to about 0.1% by weight and less than about 10% by weight, for example about 0.1 to about 5% by weight, based on the total weight of the resin composition. In some embodiments, the thermoplastic resin composition may include the copolymer (D) including the aromatic methacrylate and the mono-functional unsaturated monomer in an amount of about 0.1, 0.2, 0.3, 0.4, 0.5, 0.6, 0.7, 0.8, 0.9, 1, 2, 3, 4, 5, 6, 7, 8, or 9% by weight. Further, according to some embodiments of the present invention, the amount of the copolymer (D) can be in a range from about any of the foregoing amounts to about any other of the foregoing amounts.
The sum of the amounts of the random copolymer (C) of the alkyl(meth)acrylate compound, the aromatic vinyl compound, and the vinyl cyanide compound and the copolymer (D) of the aromatic methacrylate and the mono-functional unsaturated monomer may be less than about 30% by weight, for example about 25% by weight, based on the total weight of the resin composition. Within such a range, the resulting resin composition may prepare a molded product having greatly improved coloring properties with minimal or no loss in heat resistance, mechanical properties, and the like.
In addition to the components (A) to (D), the thermoplastic resin composition may further include at least one other additive for the purpose of improving injection moldability and achieving better balance among the properties as necessary for its final use. Examples of the additive may include, but are not limited to, a flame retardant, a surfactant, a nucleating agent, a coupling agent, a filler, a plasticizer, an impact reinforcing agent, a lubricant, an antibacterial agent, a release agent, a heat stabilizer, an antioxidant, a light stabilizer, an inorganic additive, a coloring agent, a stabilizer, a lubricating agent, an antistatic agent, a dye, a pigment, a flame proofing agent, and the like. The additive may be used alone or in a combination of two or more additives. The additive may be used in an appropriate amount such that it does not have an adverse effect on the properties of the thermoplastic resin composition. For example, the additive may be included in an amount of less than or equal to about 20 parts by weight based on about 100 parts by weight of the resin composition of components (A) to (D), but it is not limited thereto.
According to another embodiment, a molded product including the aforementioned thermoplastic resin composition is provided. The molded product may be produced in any known various methods such as injection molding, extrusion molding, and the like.
Not only can the molded product have excellent mechanical properties and excellent heat resistance, but it also can possess good weatherability and highly enhanced coloring properties. Therefore, the molded product may be advantageously used in materials for various electronic and electric parts intended for outdoor uses, building materials, sports equipment, parts for vehicles, and the like. By way of non-limiting examples, the molded product may be used in satellite antennas, kayak paddles, sash joiners and profiles, door panels, radiator grills for vehicles, side mirror housings, and the like, but it is not limited thereto.
The following examples illustrate this disclosure in more detail, however it is understood that this disclosure is not limited by these examples.
Each component as set forth in Table 1 is melted and kneaded in an amount recited in Table 1, and is extruded to prepare a composition in the form of pellets. The extrusion is conducted using a twin screw extruder having L/D of 29 and a diameter of 45 mm. The barrel temperature is 230° C.
A resin composition is produced in the form of pellets in the same manner as set forth in Example 1, except for using the components and the polymers as recited in Table 1.
Tests For Properties
The pellets prepared in accordance with Examples 1 to 3 and Comparative Examples 1 to 7 are dried at 80° C. for 6 hours and prepared as a test piece using a 6 oz injection molding machine at a cylinder temperature of 240° C. and a mold temperature 60° C. For each of the test pieces, impact strength, color, and L value are measured and the flow index of dried pellets is measured in accordance with the following manners. The results are compiled in Table 2.
(1) Impact Strength
The notched Izod impact strength is measured for a ⅛″ specimen in accordance with ASTM D 256A.
(2) Flow Index (MI, Melt Flow Index)
Flow index is measured using dried pellets at a temperature of 250° C. under a 10 kg load in accordance with ISO 1133.
(3) Colors
For a test piece of L 90 mm×W 50 mm×T 2.0 mm, a dark black color impression is measured by the naked eye in accordance with the following standards: ⊚=excellent, °=good, Δ=normal, X=poor, XX=very poor
(4) L Value
For a test piece of L 90 mm×W 50 mm×T 2.0 mm, the L value is measured using a CM-3600D spectrophotometer (from Konica Minolta Inc.) in accordance with the SCI (specular component included) standard. Higher L values mean higher brightness, brighter colors, and lower coloring properties.
The results of Table 1 and Table 2 confirm that the pellets and test pieces prepared from the resin compositions of Examples 1 to 3 have excellent impact strength and flow index and achieve significant improvements in the colors and the L values, indicating that they have excellent coloring properties.
In contrast, the coloring properties (the colors and the L values) are significantly poor and/or the impact strength or the flow index are greatly reduced in case of the comparative examples, wherein the styrene-acrylonitrile copolymer of (C-1) or (C-2) is used instead of the copolymer of methyl methacrylate-styrene-acrylonitrile (C-3) (see Comparative Examples 1 and 2), wherein the copolymer (C-3) is used but the copolymer of phenyl methacrylate-methyl methacrylate (D-1) is not used (see Comparative Example 3), wherein an excess amount of the copolymer (D-1) is used (see Comparative Example 4), or wherein the copolymer (D-1) is used but the copolymer (C-3) is not used (see Comparative Example 5). In addition, when polymethylmethacrylate is used instead of a copolymer of phenylmethacrylate-methylmethacrylate, the impact strength, the flow index, and the coloring properties (the color and the L value) are greatly worsened.
Many modifications and other embodiments of the invention will come to mind to one skilled in the art to which this invention pertains having the benefit of the teachings presented in the foregoing descriptions. Therefore, it is to be understood that the invention is not to be limited to the specific embodiments disclosed and that modifications and other embodiments are intended to be included within the scope of the appended claims. Although specific terms are employed herein, they are used in a generic and descriptive sense only and not for purposes of limitation, the scope of the invention being defined in the claims.
| Number | Date | Country | Kind |
|---|---|---|---|
| 10-2012-0157577 | Dec 2012 | KR | national |
| 10-2013-0037003 | Apr 2013 | KR | national |
| Number | Name | Date | Kind |
|---|---|---|---|
| 4006272 | Sakaguchi et al. | Feb 1977 | A |
| 4027073 | Clark | May 1977 | A |
| 4034013 | Lane | Jul 1977 | A |
| 4045514 | Iwahashi et al. | Aug 1977 | A |
| 4139600 | Rollmann et al. | Feb 1979 | A |
| 4180494 | Fromuth et al. | Dec 1979 | A |
| 4287315 | Meyer et al. | Sep 1981 | A |
| 4303772 | Novicky | Dec 1981 | A |
| 4393153 | Hepp | Jul 1983 | A |
| 4400333 | Neefe | Aug 1983 | A |
| 4694031 | Morita et al. | Sep 1987 | A |
| 4745029 | Kambour | May 1988 | A |
| 4788251 | Brown et al. | Nov 1988 | A |
| 4803235 | Okada | Feb 1989 | A |
| 4880875 | Wassmuth et al. | Nov 1989 | A |
| 4906202 | Germ | Mar 1990 | A |
| 4906696 | Fischer et al. | Mar 1990 | A |
| 5025066 | DeRudder et al. | Jun 1991 | A |
| 5061558 | Fischer et al. | Oct 1991 | A |
| 5068285 | Laughner | Nov 1991 | A |
| 5124402 | Laughner et al. | Jun 1992 | A |
| 5189091 | Laughner | Feb 1993 | A |
| 5196480 | Seitz et al. | Mar 1993 | A |
| 5200492 | Ohnaga et al. | Apr 1993 | A |
| 5219915 | McKee et al. | Jun 1993 | A |
| 5280070 | Drzewinski et al. | Jan 1994 | A |
| 5284916 | Drzewinski | Feb 1994 | A |
| 5292809 | Drzewinski et al. | Mar 1994 | A |
| 5308894 | Laughner | May 1994 | A |
| 5369154 | Laughner | Nov 1994 | A |
| 5441997 | Walsh et al. | Aug 1995 | A |
| 5449557 | Liebler et al. | Sep 1995 | A |
| 5470658 | Gasca et al. | Nov 1995 | A |
| 6060538 | Gallucci | May 2000 | A |
| 6252002 | Yamada et al. | Jun 2001 | B1 |
| 6486251 | Patel | Nov 2002 | B1 |
| 6545089 | DeRudder et al. | Apr 2003 | B1 |
| 6646068 | Chisholm et al. | Nov 2003 | B2 |
| 6653391 | Weber et al. | Nov 2003 | B1 |
| 6835775 | Breulmann et al. | Dec 2004 | B2 |
| 7294659 | Yatake | Nov 2007 | B2 |
| 7345112 | You et al. | Mar 2008 | B2 |
| 7385013 | Kobayashi et al. | Jun 2008 | B2 |
| 7547736 | Yang et al. | Jun 2009 | B2 |
| 7732515 | Jang et al. | Jun 2010 | B2 |
| 7960464 | Kobayashi et al. | Jun 2011 | B2 |
| 8044143 | Park et al. | Oct 2011 | B2 |
| 20020042483 | Vanderbilt | Apr 2002 | A1 |
| 20030032725 | Gaggar et al. | Feb 2003 | A1 |
| 20050159533 | Nabeshima et al. | Jul 2005 | A1 |
| 20050171297 | Koevoets et al. | Aug 2005 | A1 |
| 20050239949 | Nakamura et al. | Oct 2005 | A1 |
| 20060004154 | DeRudder et al. | Jan 2006 | A1 |
| 20060030647 | Ebeling et al. | Feb 2006 | A1 |
| 20060051587 | Mori et al. | Mar 2006 | A1 |
| 20060100307 | Uerz et al. | May 2006 | A1 |
| 20060135690 | Juikar et al. | Jun 2006 | A1 |
| 20070265371 | Takahashi et al. | Nov 2007 | A1 |
| 20080009571 | Pixton et al. | Jan 2008 | A1 |
| 20080153954 | Arpin | Jun 2008 | A1 |
| 20080242789 | Zhu et al. | Oct 2008 | A1 |
| 20090012222 | Duijzings et al. | Jan 2009 | A1 |
| 20090080079 | Kogure et al. | Mar 2009 | A1 |
| 20090118402 | Jang et al. | May 2009 | A1 |
| 20090209696 | Lee et al. | Aug 2009 | A1 |
| 20090275678 | Kumazawa et al. | Nov 2009 | A1 |
| 20100010172 | Hong et al. | Jan 2010 | A1 |
| 20100029855 | Matsuoka et al. | Feb 2010 | A1 |
| 20100113648 | Niessner et al. | May 2010 | A1 |
| 20100152357 | Kwon et al. | Jun 2010 | A1 |
| 20100160529 | Lee et al. | Jun 2010 | A1 |
| 20100160532 | Park et al. | Jun 2010 | A1 |
| 20100168272 | Park et al. | Jul 2010 | A1 |
| 20100197827 | Kim et al. | Aug 2010 | A1 |
| 20100240831 | Kim et al. | Sep 2010 | A1 |
| 20100256288 | Kim et al. | Oct 2010 | A1 |
| 20110009524 | Kwon et al. | Jan 2011 | A1 |
| 20110021677 | Kwon et al. | Jan 2011 | A1 |
| 20110040019 | Kwon et al. | Feb 2011 | A1 |
| 20110160380 | Kwon et al. | Jun 2011 | A1 |
| 20120065318 | Park et al. | Mar 2012 | A1 |
| 20120129989 | Kim et al. | May 2012 | A1 |
| 20130131258 | Kwon et al. | May 2013 | A1 |
| Number | Date | Country |
|---|---|---|
| 1285858 | Feb 2001 | CN |
| 19845317 | Apr 2000 | DE |
| 69829099 | Dec 2005 | DE |
| 0033393 | Aug 1981 | EP |
| 0114288 | Aug 1984 | EP |
| 0180417 | May 1986 | EP |
| 0246620 | May 1987 | EP |
| 0376616 | Jul 1990 | EP |
| 0528462 | Feb 1993 | EP |
| 0755977 | Jan 1997 | EP |
| 0787769 | Aug 1997 | EP |
| 1010725 | Jun 2000 | EP |
| 2204412 | Jul 2010 | EP |
| 53-134799 | Nov 1978 | JP |
| 57-125241 | Aug 1982 | JP |
| 58-196250 | Nov 1983 | JP |
| 62-268612 | Nov 1987 | JP |
| 04-023856 | Jan 1992 | JP |
| 04-359954 | Dec 1992 | JP |
| 05-098136 | Apr 1993 | JP |
| 05-125260 | May 1993 | JP |
| 05-194829 | Aug 1993 | JP |
| 06-122771 | May 1994 | JP |
| 06-136212 | May 1994 | JP |
| 06-313089 | Nov 1994 | JP |
| 07-026101 | Jan 1995 | JP |
| 10-060241 | Mar 1998 | JP |
| 10-060242 | Mar 1998 | JP |
| 10-219026 | Aug 1998 | JP |
| 10-226748 | Aug 1998 | JP |
| 11-129246 | May 1999 | JP |
| 11-181168 | Jul 1999 | JP |
| 11-279385 | Oct 1999 | JP |
| 2000-212293 | Aug 2000 | JP |
| 2000-265001 | Sep 2000 | JP |
| 2000-327992 | Nov 2000 | JP |
| 2001-049072 | Feb 2001 | JP |
| 2002-080676 | Mar 2002 | JP |
| 2003-525335 | Aug 2003 | JP |
| 2003-313392 | Nov 2003 | JP |
| 2005-220173 | Aug 2005 | JP |
| 2006-249292 | Sep 2006 | JP |
| 2006-257284 | Sep 2006 | JP |
| 2006-342246 | Dec 2006 | JP |
| 2007-077222 | Mar 2007 | JP |
| 2008-013702 | Jan 2008 | JP |
| 10-1996-0001023 | Jan 1996 | KR |
| 10-1996-0001025 | Jan 1996 | KR |
| 1996-0007611 | Jun 1996 | KR |
| 10-1998-0004915 | Jun 1998 | KR |
| 10-1998-027070 | Jul 1998 | KR |
| 1998-055579 | Sep 1998 | KR |
| 10-1999-0018287 | Mar 1999 | KR |
| 10-0201985 | Mar 1999 | KR |
| 10-1999-0029495 | Apr 1999 | KR |
| 10-1999-0054644 | Jul 1999 | KR |
| 10-2000-0038719 | Jul 2000 | KR |
| 10-2000-0048033 | Jul 2000 | KR |
| 10-2001-0032100 | Apr 2001 | KR |
| 10-2001-0070975 | Jul 2001 | KR |
| 10-2003-0034796 | May 2003 | KR |
| 10-0384377 | Nov 2003 | KR |
| 2004-0079118 | Sep 2004 | KR |
| 10-0454799 | Jan 2005 | KR |
| 10-2005-0032100 | Apr 2005 | KR |
| 10-0514272 | Sep 2005 | KR |
| 10-2005-0109049 | Nov 2005 | KR |
| 10-2006-0035002 | Apr 2006 | KR |
| 10-0581437 | May 2006 | KR |
| 10-0696329 | Mar 2007 | KR |
| 10-0709878 | Apr 2007 | KR |
| 10-2007-0070686 | Jul 2007 | KR |
| 10-2007-0072372 | Jul 2007 | KR |
| 10-0767428 | Oct 2007 | KR |
| 10-2008-0062975 | Jul 2008 | KR |
| 10-2008-0063054 | Jul 2008 | KR |
| 10-2008-0090459 | Oct 2008 | KR |
| 10-0871436 | Nov 2008 | KR |
| 10-2009-0020642 | Feb 2009 | KR |
| 10-2009-0030511 | Mar 2009 | KR |
| 10-0886348 | Mar 2009 | KR |
| 10-2009-0038507 | Apr 2009 | KR |
| 10-2010-0045830 | May 2010 | KR |
| 10-2008-124708 | Jun 2010 | KR |
| 10-2010-0071715 | Jun 2010 | KR |
| 10-0988999 | Oct 2010 | KR |
| 10-2011-0079488 | Jul 2011 | KR |
| 10-2012-0029156 | Mar 2012 | KR |
| 10-2012-0031532 | Apr 2012 | KR |
| 10-1143239 | May 2012 | KR |
| 10-2011-0077805 | May 2013 | KR |
| 02088044 | Nov 2002 | WO |
| 2005075554 | Aug 2005 | WO |
| 2007119920 | Oct 2007 | WO |
| 2007140101 | Dec 2007 | WO |
| 2008039017 | Apr 2008 | WO |
| 2008081791 | Jul 2008 | WO |
| 2009078593 | Jun 2009 | WO |
| 2009078602 | Jun 2009 | WO |
| 2009113762 | Sep 2009 | WO |
| 2009116722 | Sep 2009 | WO |
| 2009128601 | Oct 2009 | WO |
| 2011013882 | Feb 2011 | WO |
| Entry |
|---|
| Kwon et al., electronic translation of KR 10-2008124708, Jun. 2010. |
| Kang, et al., “PC/ASA blends having enhanced interfacial and mechanical properties,” Korea-Australia Rheology Journal, vol. 18, No. 1, Mar. 2006 pp. 1-8. |
| Taiwanese Office Action in commonly owned Taiwanese Application No. 96136059 issued on May 5, 2011, pp. 1-9. |
| English Translation of Taiwanese Office Action in commonly owned Taiwanese Application No. 96136059 issued on May 5, 2011, pp. 1-5. |
| European Search Report in commonly owned European Application No. 07808474 dated Sep. 28, 2011, pp. 1-4. |
| International Preliminary Report on Patentability in commonly owned International Application No. PCT/KR2007/004743, dated Mar. 31, 2009, pp. 1-5. |
| International Search Report in commonly owned International Application No. PCT/KR2007/004743, dated Jan. 4, 2008, pp. 1-2. |
| Office Action in commonly owned U.S. Appl. No. 12/413,630 mailed Jun. 23, 2009, pp. 1-9. |
| Final Office Action in commonly owned U.S. Appl. No. 12/413,630 mailed Dec. 7, 2009, pp. 1-9. |
| Advisory Action in commonly owned U.S. Appl. No. 12/413,630 mailed Apr. 9, 2010, pp. 1-3. |
| French Search Report and Written Opinion in commonly owned French Application No. 0959193 dated May 27, 2010, pp. 1-5. |
| Office Action in commonly owned U.S. Appl. No. 12/640,343 mailed Aug. 29, 2011, pp. 1-7. |
| Office Action in commonly owned U.S. Appl. No. 12/640,343 mailed Feb. 22, 2012, pp. 1-13. |
| Final Office Action in commonly owned U.S. Appl. No. 12/640,343 mailed Jun. 5, 2012, pp. 1-12. |
| Office Action in commonly owned U.S. Appl. No. 12/641,752 mailed Jan. 10, 2011, pp. 1-10. |
| Notice of Allowance in commonly owned U.S. Appl. No. 12/641,752 mailed Jul. 20, 2011, pp. 1-9. |
| International Search Report in commonly owned International Application No. PCT/KR2009/007917 dated Aug. 24, 2010, pp. 1-9. |
| English-translation of Abstract for Korean Publication No. 1998-055579, published Sep. 25, 1998, pp. 1. |
| Igranox 1076, SpecialChem, Ciba, now part of BASF, 2012 Retrieved online<http://www.specialchem4adhesives.com>, pp. 1. |
| Office Action in commonly owned U.S. Appl. No. 13/362,068 mailed Apr. 6, 2012, pp. 1-24. |
| European Search Report in commonly owned European Application No. 08862371 dated Dec. 7, 2010, pp. 1-6. |
| International Search Report in commonly owned International Application No. PCT/KR2008/006870, dated May 28, 2009, pp. 1-2. |
| Office Action in commonly owned U.S. Appl. No. 12/631,018 mailed Nov. 8, 2011, pp. 1-10. |
| Chinese Office Action in commonly owned Chinese Application No. 200910211954 dated Jun. 23, 2011, pp. 1-5. |
| English translation of Chinese Office Action in commonly owned Chinese Application No. 200910211954 dated Jun. 23, 2011, pp. 1-5. |
| Katrizky et al., “Correlation and Prediction of the Refractive Indices of Polymers by QSPR”, Journal of Chemical Information and Computer Sciences, pp. 1171-1176, (1998). |
| Office Action in commonly owned U.S. Appl. No. 12/642,904 mailed Dec. 14, 2011, pp. 1-9. |
| European Search Report in commonly owned European Application No. 09180634 dated Feb. 2, 2010, pp. 1-3. |
| Xu, “Predicition of Refractive Indices of Linear Polymers by a four-descriptor QSPR model”, Polymer, 45 (2004) pp. 8651-8659. |
| European Search Report in commonly owned European Application No. 10196806 dated Apr. 27, 2011, pp. 1-5. |
| European Search Report in commonly owned European Application No. 08873425.6 dated May 29, 2012, pp. 1-5. |
| International Search Report in commonly owned International Application No. PCT/KR2008/007157, dated May 28, 2009, pp. 1-2. |
| Office Action in commonly owned U.S. Appl. No. 12/792,176 mailed Nov. 16, 2011, pp. 1-12. |
| International Search Report in commonly owned International Application No. PCT/KR2008/007825, dated Aug. 28, 2009, pp. 1-2. |
| Office Action in commonly owned U.S. Appl. No. 12/880,209 mailed Feb. 16, 2011, pp. 1-10. |
| Final Office Action in commonly owned U.S. Appl. No. 12/880,209 mailed Jul. 29, 2011, pp. 1-9. |
| Advisory Action in commonly owned U.S. Appl. No. 12/880,209 mailed Nov. 4, 2011, pp. 1-4. |
| International Search Report in commonly owned International Application No. PCT/KR2008/007820 dated Jul. 28, 2009, pp. 1-2. |
| Final Office Action in commonly owned U.S. Appl. No. 12/792,176 mailed Apr. 19, 2012, pp. 1-10. |
| Chinese Search Report in commonly owned Chinese Application No. 200980159831.0 dated Dec. 17, 2012, pp. 1-2. |
| International Search Report in commonly owned International Application No. PCT/KR2009/007944 dated Aug. 13, 2010, pp. 1-6. |
| Full English Translation of JP 04-359953. |
| Full English Translation of JP 04-359954. |
| Number | Date | Country | |
|---|---|---|---|
| 20140187719 A1 | Jul 2014 | US |