Claims
- 1. A color filter comprising
- a transparent substrate;
- a transparent electrically conductive layer supported by the substrate in the form of spaced and substantially parallel electrode stripes;
- a thin film with a thickness of from about 0.4 to 1.1 .mu.m consisting of at least two different organic pigments and optionally including dopant material for increasing the electrical conductivity of the thin film, disposed on the conductive layer, the organic pigments being substantially insoluble in water, the thin film of organic pigments deposited on the conductive layer by electrolysis from a solution containing a redox reactive surfactant in which the organic pigments are colloidally dispersed, the two different pigments of the thin film each having different wavelength transmittance properties and a primary particle size of from 0.005 to 0.5 .mu.m.
- 2. The color filter of claim 1, wherein the transparent substrate is formed from one of glass or plastic.
- 3. The color filter of claims 1, wherein the conductive layer is selected from the group consisting of layers of indiumtin oxide, tin oxide and combinations thereof.
- 4. The color filter of claim 1, wherein the organic pigments are selected from the group consisting of a phthalocyanine pigments, anthraquinone pigments, thioindigo pigments, perylene pigments, quinacridone pigments, dioxazine pigments, isoindolinone pigments, quinophthalone pigments, perinone pigment, nitro pigments, nitroso pigments, azo complex salt pigments, condensed azo pigments, benzoimidazolone pigments, metal complex pigments, aniline black, daylight fluorescent pigments, diketopyrrolopyrrole pigments and combinations thereof.
- 5. The color filter of claim 1, wherein the organic pigments have a hydrophilic surface nature that was converted into a hydrophobic surface nature.
- 6. The color filter of claim 1, wherein the surfactant is oxidizable or reducible by electrolysis and includes a metallocene group having a general formula ##STR8## a hydrophobic end group in which M is a metal selected from the group consisting of Cr, Ti, Fe, V, Co, Ni, Ru, Os and Pd.
- 7. The color filter of claim 6, wherein M is a metal selected from the group consisting of Cr and Ti.
- 8. The color filter of claim 1, wherein the thin film includes a halogen containing dopant material.
- 9. The color filter of claim 1, wherein a light shielding film is disposed on the substrate between the stripes.
- 10. The color filter of claim 9, wherein the light-shielding film includes pigment and photosetting resin which will set upon exposure with light.
- 11. The color filter of claim 1, wherein the parallel electrode stripes of the conductive layer are not electrically coupled to each other.
- 12. The color filter of claim 1, wherein the substrate, conductive layer and thin film are constructed and arranged for use in a liquid crystal display.
- 13. The color filter of claim 1, wherein the spaced parallel stripes are arranged in groups, each group including at least one stripe having a different color thin film than the other stripes of the group; at least one stripe of the group of a different length than the other stripes of the group; the thin films being disposed on less than the entire length of each stripe; and insulating material present on at least a portion of one of the stripes.
- 14. The color filter of claim 1, wherein the organic pigments are selected from the group consisting of organic pigments with a hydrophobic surface nature and organic pigments with a hydrophilic surface nature.
- 15. A color filter for a liquid crystal display, comprising:
- a transparent substrate;
- a transparent electrically conductive layer disposed on a portion of the substrate in the form of three groups of substantially parallel electrode stripes;
- a red thin film on a first group of stripes, a green thin film on a second group of stripes and a blue thin film on a third group of stripes, each thin film including at least two organic pigments having different light transmittance properties, the thin films having been disposed on the stripes by electrolysis from at least one solution containing a surfactant that is oxidizable or reducible, in which the organic pigments are colloidally dispersed, the organic pigments being substantially insoluble in water; the pigments having a primary particle size of between about 0.005 and 0.5 .mu.m; and the thin films being about 0.4 to 1.1 .mu.m thick
- 16. The color filter of claim 15, wherein the thin films of the same color are not on adjacent electrode stripes.
- 17. The color filter of claim 16, including light shielding material selectively disposed on the substrate to prevent light from passing through the filter without passing through the thin films.
- 18. The color filter of claim 15, wherein at least one of the groups of stripes is a different length than the other groups of stripes and at least one of the groups of stripes includes insulating material disposed thereon.
- 19. The color filter of claim 15, wherein the thin film includes dopant material for increasing the electrical conductivity of the thin film.
- 20. The color filter of claim 15, wherein the thin film includes a halogen containing dopant material.
- 21. A color filter, comprising a transparent substrate; at least two groups of substantially parallel transparent electrode stripes; at least two groups of differently colored thin film organic pigment layers having a thickness from about 0.4 to 1.1 .mu.m, each group of differently colored thin films being on an associated group of electrodes, the groups of differently colored thin film layers being at least two groups selected from (a) red layers having an essential light transmission wavelength range substantially between 600 and 700 nm (b) blue layers having an essential light transmission wavelength in the range from about 450 to 500 nm or and (c) green layers having an essential light transmission wavelength range between about 500 and 550 nm, to form at least two groups of differently colored transparent electrode stripes; the thin film organic pigment layers being formed from pigments having a primary particle size between about 0.005 and 0.5 .mu.m, the pigment layers being deposited from a colloidal dispersion of said organic pigments in an aqueous micelle solution of a redox reactive surfactant.
- 22. The color filter of claim 21, wherein the filter includes a red layer formed from a red pigment and a yellow pigment in a ratio of red pigment to yellow pigment of about 8:2.
- 23. The color filter of claim 21, wherein the filter includes a green layer formed from a green pigment and a yellow pigment in a ratio of green pigment to yellow pigment of about 6:4.
- 24. The color filter of claim 21, wherein the filter includes a blue layer formed with a blue pigment and a red violet pigment in a ratio of blue pigment to red violet pigment of about 7:3.
Priority Claims (15)
Number |
Date |
Country |
Kind |
53-108726 |
Apr 1988 |
JPX |
|
53-174102 |
Jul 1988 |
JPX |
|
53-175610 |
Jul 1988 |
JPX |
|
53-189201 |
Jul 1988 |
JPX |
|
53-189202 |
Jul 1988 |
JPX |
|
53-252524 |
Oct 1988 |
JPX |
|
253043 |
Oct 1988 |
JPX |
|
53-257819 |
Oct 1988 |
JPX |
|
53-268507 |
Oct 1988 |
JPX |
|
53-283418 |
Nov 1988 |
JPX |
|
53-291497 |
Nov 1988 |
JPX |
|
53-299039 |
Nov 1988 |
JPX |
|
53-004038 |
Jan 1989 |
JPX |
|
54-021505 |
Jan 1989 |
JPX |
|
54-021509 |
Jan 1989 |
JPX |
|
Parent Case Info
This is a division of application Ser. No. 07/344,636, filed Apr. 28, 1989, now abandoned.
US Referenced Citations (5)
Foreign Referenced Citations (5)
Number |
Date |
Country |
0246334 |
Nov 1987 |
EPX |
0340968 |
Nov 1989 |
EPX |
57-89499 |
Jun 1982 |
JPX |
60-208280 |
Oct 1985 |
JPX |
243298 |
Oct 1988 |
JPX |
Non-Patent Literature Citations (3)
Entry |
Saji, et al., "Electro. Form. of a Phthalocyanine Thin Film" Chem. Letters 1988. |
Saji, et al., "Electro. Form of Organic Thin Film", J. Am. Chem. Soc. 1987 109:5881-83. |
Saji, et al., "Reversible Form. and Disruption of Micelles", J. Chem. Soc., Chem. Comm. 1985, pp. 865-866. |
Divisions (1)
|
Number |
Date |
Country |
Parent |
344636 |
Apr 1989 |
|