1. Field of the Invention
The present invention relates to a thin film semiconductor device having a polycrystalline semiconductor film, and a process and apparatus for producing a polycrystalline semiconductor film. The thin film semiconductor device of the present invention is useful for image display devices.
2. Related Art
The prior art process for crystallizing an amorphous silicon thin film by scanning with a pulse laser will be described with reference to
Further, an international patent publication W09745827 discloses the following process. That is, when the width L of the laser beam 105 shown in
In the above process of the prior art, as the time required for crystal growth is 100 ns or less, the obtained crystals have a grain size of 1 μm or less and are greatly nonuniform in grain size. The orientation of grains is out of order, the density of defects is large, and the roughness of the film surface is large. Therefore, it is impossible to grow polycrystalline silicon having a large grain size or to control the grain size or the position of the grain boundary accurately. Therefore, the grain boundary is included in the channel at random. Consequently, it is difficult to improve the characteristic properties, reliability and uniformity of TFT devices.
Since the beam must be converged to a size of 1 μm or less in the technology disclosed by the above international patent publication W09745827, the energy of the laser is lost and the optical system of an irradiation laser become complicated. As the moving distance between laser pulses is 1 μm or less, it takes a long time to crystallize the whole substrate and it is difficult to improve throughput and reduce costs. Particularly, this process cannot be applied to a large-area substrate. Further, very small distance movement is easily influenced by vibration and involves a yield problem.
It is a first object of the present invention to provide a production process and apparatus for forming on an insulating substrate made from glass or the like a high-quality polycrystalline semiconductor film whose grain boundary, grain size and crystal orientation can be controlled and whose film roughness and crystal defects formed in crystallization process have been reduced, and to provide a thin semiconductor device comprising the above polycrystalline semiconductor film.
It is a second object of the present invention to provide a production process and apparatus for forming a low-cost and high-quality polycrystalline semiconductor film, which can reduce the number of production steps, can be applied to a large-area substrate and have a high throughput, and to provide a thin film semiconductor device comprising the above polycrystalline semiconductor film.
It is a third object of the present invention to provide a production process and apparatus for forming on an inexpensive insulating substrate made from glass or the like a high-quality polycrystalline semiconductor film which operates with high performance and high reliability and is excellent in uniformity among devices, and to provide a thin film semiconductor device comprising the above polycrystalline semiconductor film.
The major aspects of the present invention will be described below.
According to a first aspect of the present invention, there is provided a thin film semiconductor device which has an insulating substrate, a first semiconductor film which is a polycrystalline semiconductor film, a gate electrode formed on the first semiconductor film through a gate insulating film, first charge transmitting and receiving means and second charge transmitting and receiving means formed on the first semiconductor film at a predetermined interval therebetween, and a channel region formed between the first and second charge transmitting and receiving means, wherein
the main orientation of the first semiconductor film constituting the channel region is {110} with respect to the main surface of the insulating substrate or the gate insulating film.
It is possible to provide a thin film semiconductor device having high reliability by selecting the main orientation of the semiconductor film of the channel region with respect to the main surface of the insulating substrate or the gate insulating film even when a polycrystalline semiconductor film is used. The method of controlling the main orientation of the polycrystalline film will be described hereinafter.
An MIS type thin film semiconductor device according to the present invention may vary in structure as follows.
According to a second aspect of the present invention, there is provided a thin film semiconductor device which has an insulating substrate, a first semiconductor film which is a polycrystalline semiconductor film, a gate electrode formed on the first semiconductor film through a gate insulating film, first charge transmitting and receiving mean and second charge transmitting and receiving means formed on the first semiconductor film at a predetermined interval therebetween, and a channel region formed between the first and second charge transmitting and receiving means, wherein
In the thin film semiconductor device of the present invention, the first semiconductor film comprises a small inclination grain boundary having an angle of 75° or less with respect to a direction for connecting the first and second charge transmitting and receiving means.
According to a third aspect of the present invention, there is provided a thin film semiconductor device which has an insulating substrate, a first semiconductor film which is a polycrystalline semiconductor film, a gate electrode formed on the first semiconductor film through a gate insulating film, first charge transmitting and receiving mean and second charge transmitting and receiving means formed on the first semiconductor film at a predetermined interval therebetween, and a channel region formed between the first and second charge transmitting and receiving means, wherein
the main orientation of the first semiconductor film constituting the channel region is {110} with respect to the main surface of the insulating substrate or the gate insulating film; and the channel region of the first semiconductor film has crystal grains for connecting the first charge transmitting and receiving means and the second charge transmitting and receiving means.
The third aspect of the present invention is more preferred. That is, the channel region of the first semiconductor film is composed of crystal grains having such a length in a longitudinal direction as to connect the first charge transmitting and receiving means and the second charge transmitting and receiving means. Therefore, a thin film semiconductor device having higher reliability can be provided.
According to a fourth aspect of the present invention, there is provided a thin film semiconductor device which has an insulating substrate, a first semiconductor film which is a polycrystalline semiconductor film, a gate electrode formed on the first semiconductor film through a gate insulating film, first charge transmitting and receiving mean and second charge transmitting and receiving means formed on the first semiconductor film at a predetermined interval therebetween, and a channel region formed between the first and second charge transmitting and receiving means, wherein
the main orientation of the first semiconductor film constituting the channel region is {110} with respect to the main surface of the insulating substrate or the gate insulating film; and the main orientation of the surface of the first semiconductor film substantially perpendicular to a direction for connecting the first and second charge transmitting and receiving means is {100}. The channel region of the first semiconductor film is composed of crystal grains having a length in a longitudinal direction for connecting the first charge transmitting and receiving means and the second charge transmitting and receiving means, and the main orientation of the polycrystalline film is {100}, thereby making it possible to provide a thin film semiconductor device having extremely high reliability. Briefly speaking the conclusion, this is because each crystal grain has the same properties as a monocrystal though the first semiconductor film is polycrystal.
According to a fifth aspect of the present invention, there is provided a thin film semiconductor device which has at least two semiconductor device portions on an insulating substrate, a second semiconductor layer and an insulating film layer selectively formed on a partial region of the insulating substrate, the laminate consisting of the second semiconductor layer and the insulating film layer being in contact with a first semiconductor layer, the second semiconductor layer being not existent between a first semiconductor device and a second semiconductor device, a gate electrode formed on the first semiconductor layer through a gate insulating film, first charge transmitting and receiving means and second charge transmitting and receiving means formed on the first semiconductor film at a predetermined interval therebetween, and a channel region formed between the first and second charge transmitting and receiving means. Also in this thin film semiconductor device, the main orientation of the first semiconductor film constituting the channel region is more preferably {110} with respect to the main surface of the insulating non-crystalline substrate or the gate insulating film.
This thin film semiconductor device has the second semiconductor layer below a desired semiconductor device portion and the semiconductor device portion has the first aspect of the present invention. Further, in the present invention, the second semiconductor layer may be existent below the desired semiconductor device portion and the semiconductor device portion may have anyone of the second to fourth aspects of the present invention. It is needless to say that the present invention can be carried out using any one of the semiconductor device portions disclosed in this specification.
According to a sixth aspect of the present invention, there is provided a thin film semiconductor device which has at least two semiconductor device portions on an insulating substrate, a second thin film which is selectively formed on a first thin film having a first heat conductivity and which has a second heat conductivity higher than the first heat conductivity, the second thin film being not in contact with a semiconductor layer and arranged between a first semiconductor device portion and a second semiconductor device portion, and the semiconductor device portions being the thin film semiconductor device of any one of the first to fourth aspects of the present invention.
According to a seventh aspect of the present invention, there is provided a thin film semiconductor device which has at least two semiconductor device portions on an insulating substrate, a second thin film which is selectively formed on a first thin film having a first heat conductivity and which has a second heat conductivity lower than the first heat conductivity, the second thin film being in contact with a semiconductor layer and not arranged between a first semiconductor device portion and a second semiconductor device portion, and the semiconductor device portions being the thin film semiconductor device of any one of the first to fourth aspects.
Practical variations of the thin film semiconductor device of the present invention will be described hereinafter.
A semiconductor film production process according to the major aspects of the present invention will be described hereinbelow. A polycrystalline semiconductor film of interest can be obtained by using the following process.
According to an eighth aspect of the present invention, there is provided a process for producing a polycrystalline semiconductor film by carrying out separately the step of growing crystal nuclei in a semiconductor layer formed on an insulating substrate and the step of melt recrystallizing a semiconductor thin film by irradiating a laser beam to grow crystal grains.
According to a ninth aspect of the present invention, there is provided a process for producing a polycrystalline semiconductor film, wherein a non-crystalline semiconductor film formed on the insulating substrate is melt recrystallized by irradiating a laser beam to grow crystal grains.
According to a tenth aspect of the present invention, there is provided a process for producing a polycrystalline semiconductor film, wherein the wavelength of the laser beam is selected from a range of 240 nm to 600 nm and the absorption coefficient for the wavelength of the non-crystalline semiconductor film is larger than the absorption coefficient of the polycrystalline semiconductor film.
According to an eleventh aspect of the present invention, there is provided a process for producing a polycrystalline semiconductor film, wherein the crystal nuclei of the polycrystalline silicon film formed on the insulating film are formed by melt recrystallization by the irradiation of a laser beam.
The crystal nuclei of the polycrystalline silicon film on the insulating substrate are preferably grown by catalytic chemical vapor deposition.
The production apparatus of the present invention comprises means for modulating the pulse width of a laser beam, the time-dependent shape of laser beam intensity and the interval of laser beam pulses, means for shaping the irradiation range of the profile of the laser beam irradiated from an oscillation source to a predetermined form and focusing it on an object to be irradiated, and means of moving the insulating substrate at a predetermined speed and pitch in synchronism with the irradiation of the laser beam.
In the present invention, the charge transmitting and receiving means generally means a source or drain region.
a) to 1(c) are diagrams of a semiconductor device according to Embodiment 1 of the preset invention;
a) and 2(b) are diagrams for explaining the semiconductor device according to Embodiment 1 of the present invention;
a) to 3(e) are sectional views for explaining a semiconductor device production process according to the present invention in the order of production steps;
a) and 5(b) are diagrams showing time changes of laser beam intensity;
a) and 6(b) are diagrams showing examples of spatial distribution of laser beam intensity;
a) to 7(c) are diagrams for explaining a semiconductor device according to Embodiment 2 of the present invention;
a) to 8(f) are sectional views for explaining a semiconductor device production process according to the present invention in the order of production steps;
a) to 9(c) are diagrams for explaining a semiconductor device according to Embodiment 3 of the present invention;
a) to 10(e) are sectional views for explaining a semiconductor device production process according to the present invention in the order of production steps;
a) to 11(c) are diagrams for explaining a semiconductor device according to Embodiment 4 of the present invention; and
Prior to the explanation of preferred embodiments of the present invention, a complementary explanation related to a typical embodiment of the present invention will be given.
To attain the first and second objects of the present invention, the following means is useful.
A region thicker than the channel region is formed in part of a drain or source region constituting a semiconductor layer. Thereby, an extremely useful polycrystalline semiconductor film can be obtained.
Further, the above objects can be easily attained by the following means.
The pulse width of the above laser beam is 100 ns to 1 ms and the energy density is 200 mJ/cm2 to 10 J/cm2. The intensity distribution of the laser beam has such a distribution pattern that intensity is uniform in the width of the beam, or monotonously increases or decreases from one direction to the other.
Further, the above third object can be attained by an MIS type field effect transistor having a gate electrode formed on a first semiconductor layer which is a polycrystalline semiconductor film formed on an insulating substrate through a gate insulating film, a channel region formed on the semiconductor layer and a source region and a drain region formed on both sides of the channel region, wherein a semiconductor layer which is a polycrystalline semiconductor film used in the channel of a semiconductor in which the main orientation of crystal grains constituting the channel region with respect to the surface of the substrate or the gate insulating film is {110} and the main orientation of the surface perpendicular to a direction for connecting the source and drain regions is {100}.
Further, the above objects can be easily attained by applying the following features to a polycrystalline semiconductor film.
The first feature is that a small inclination angle grain boundary having an angle of 75° or less is located between the source and drain regions of the channel region.
The second feature is that the surface roughness of the channel region is smaller than 20 nm and the internal tensile stress of the channel region is 109 dyn/cm2 or more.
The third feature is that the density of metal elements contained in the semiconductor layer is 1019 cm−3 or less and the density of crystal defects contained in the channel region is 1017 cm−3 or less.
A preferred example of the thin film semiconductor device of the present invention is a thin film semiconductor device which has a low-melting point glass substrate as the above insulating substrate. The insulating substrate is typified by a non-crystalline substrate such as a glass substrate, particularly a low-melting point glass substrate.
The present invention provides the following thin film semiconductor devices:
In the thin film semiconductor device of the present invention, the grain size of the semiconductor crystals of the channel region may be larger than the grain size of the crystal grains of the charge transmitting and receiving means, that is, source and drain regions.
The present invention also provides the following polycrystalline semiconductor thin film production processes:
A thin film semiconductor device, production process and production apparatus according to preferred embodiments of the present invention will be described hereinafter with reference to the accompanying drawings.
a) to 1(c) are diagrams for explaining a thin film semiconductor device according to Embodiment 1 of the present invention.
Each silicon semiconductor layer comprises a channel region 12, a source region 20, a drain region 19 and a projecting crystal nucleus region 30. The channel region 12 is composed of a polycrystalline silicon film having a large grain size and the crystal nucleus region 30 is generally composed of a polycrystalline silicon film having a small grain size.
In this embodiment, as seen in the plan view of
The channel region 12 having a large grain size is obtained by a crystallization method as shown in
a) to 3(e) are sectional views showing the production process of the thin film semiconductor device of this embodiment. A base layer which is a silicon dioxide film 101 and an amorphous or polycrystalline silicon film 110 are formed on a non-crystalline substrate 100 made from glass or the like (
In this embodiment, after the polycrystalline silicon film including the crystal nucleus region 30 is formed on the insulating substrate, the step of melt recrystallizing the semiconductor thin film by the irradiation of a laser beam to grow grains from the above crystal nuclei can be carried out separately. The wavelength of a laser beam suitable to selectively grow crystal grains efficiently is desirably selected from a range of 240 to 600 nm. The reason for this is that the absorption coefficient of the amorphous silicon film at a wavelength of 500 nm is about 5 times larger than the absorption coefficient of the polycrystalline silicon film. Therefore, it is easy to selectively melt recrystallize other semiconductor layer regions with crystal nuclei composed of a polycrystalline silicon film as a seed. Meanwhile, the crystal nucleus region composed of a polycrystalline silicon film having a small grain size on the insulating substrate can be formed by melt recrystallization with the irradiation of a general excimer pulse laser beam.
a) and 2(b) schematically show the crystalline state of the semiconductor layer, particularly the channel region.
The main orientation of a polycrystalline substance at least in the channel region 12 is {110} with respect to the surface of the gate insulating film and the substrate. The polycrystalline substance is a polycrystalline silicon film having a main orientation of the surface almost perpendicular to a direction for connecting the source region 20 and the drain region 19 such as of {100}. A small inclination angle grain boundary having a rotation angle of 70° or less is located between a plurality of crystal grains constituting the channel region 12.
Further, the surface roughness of the channel region 12 is smaller than 20 nm, the internal tensile stress is 109 dyn/cm2 or more, and the density of the contained crystal defects is 1017 cm−3 or less. The density of metal elements contained in the whole semiconductor layer including the channel region 12 is 1019 cm−3 or less.
The pulse width, time-dependent shape and pulse interval of the laser beam are shown in
a) and
By moving the insulating substrate 206 or the mirror 208 at a predetermined speed and interval in synchronism with the irradiation of the laser beam, a desired region can be crystallized.
In the present invention, the alignment pattern on the insulating substrate can be detected by a level difference of the semiconductor layer film or a level difference in the crystal nucleus region 30 in
According to this embodiment, a high-quality polycrystalline semiconductor film whose grain boundary, grain size and crystallization direction can be controlled and whose film roughness and crystal defects formed by crystallization have been reduced can be formed on the insulating substrate made from glass or the like. According to this embodiment, a production process and apparatus for forming a low-cost and high-quality polycrystalline semiconductor film, which can reduce the number of production steps, can be applied to a large-area substrate, and have a high throughput are realized.
Further, when the polycrystalline semiconductor film shown in this embodiment is used in a MIS type field effect transistor, the field effect mobility can be controlled to about 300 cm2/V·s or more and variations in threshold voltage can be suppressed to ±0.2 V or less. Thus, according to the present invention, a thin film semiconductor device which operates with high performance and high reliability and has excellent uniformity among devices can be obtained.
In this embodiment, a polycrystalline silicon film is used as a semiconductor film before the irradiation of a laser beam. When an amorphous silicon film is used, the same effect is obtained. In this embodiment, an inclined laser beam is used. When a uniform beam is used, the same effect is obtained. Further, in this embodiment, crystals are grown with the crystal nucleus region 30 as a starting point. By optimizing the shape of a laser beam, the same effect is obtained in a structure containing no crystal nuclei 30 on the projection. In this case, the initial semiconductor film is a polycrystalline silicon film containing crystal nuclei and can be obtained by melt recrystallization by the irradiation of an excimer laser beam. The same effect is obtained when the above polycrystalline silicon film is formed at a low temperature by CAT-CVD (Catalytic-Chemical Vapor Deposition).
a) to 7(c) are diagrams for explaining a semiconductor device according to Embodiment 2 of the present invention. In this embodiment, a second semiconductor layer is formed below the semiconductor layer constituting a channel from the viewpoint of crystal growth.
In
The first semiconductor layer has a channel region 12, source region 20 and drain region 19. The channel region 12 is composed of a polycrystalline silicon film having a large grain size. A second semiconductor layer 41 is selectively inserted between the silicon semiconductor layer and the underlying layer film 101 with an insulating film 40. The second semiconductor layer 41 is not formed in a region between a plurality of semiconductor devices.
a) to 8(f) are sectional views showing a process for producing the thin film semiconductor device of this embodiment. A base layer which is the silicon dioxide film 101, an amorphous silicon layer which is the second semiconductor layer 41 and a silicon dioxide layer 40 are formed on a non-crystalline substrate 100 made from glass or the like (
The channel region 12 having a large grain size is obtained by a crystallization method shown in
When the laser beam is irradiated under the above conditions, crystallization starts from a region devoid of the second silicon semiconductor layer below the silicon semiconductor layer. The reason for this is that the laser beam passing through the first silicon semiconductor film reaches the second silicon semiconductor film when the laser beam is irradiated. The laser beam is absorbed in the second silicon semiconductor film and the temperature of the semiconductor layer rises. This temperature rise functions as a heat sink to suppress quenching. In a region where this heat sink is not formed in the layer underlying the first silicon semiconductor layer, the temperature is low and the crystallization start time is early. Therefore, crystallization starts from the region devoid of the second semiconductor layer below the first silicon semiconductor layer and the region becomes the crystal nucleus region 42. The wavelength of a laser beam suitable for selectively growing crystal grains at a high efficiency is desirably selected from a range of 240 to 600 nm. In this embodiment, after a polycrystalline silicon film including the crystal nucleus region 30 is formed on the insulating substrate, the step of melt recrystallizing the semiconductor thin film by the irradiation of a laser beam to grow grains from the crystal nuclei can be carried out separately. The crystal nucleus region composed of a polycrystalline silicon film having a small grain size on the insulating substrate can be formed by melt recrystallization with the irradiation of a laser beam from an excimer pulse laser of the prior art.
a) and 2(b) show the crystal state of the semiconductor layer, particularly the channel region. The semiconductor layer is composed of a polycrystalline silicon film in which at least the main orientation of the channel region is {110} with respect to the surface of the gate insulating film and the main orientation of the surface almost perpendicular to a direction for connecting the above source region 20 and the drain region 19 is {100}. A small inclination angle grain boundary having a rotation angle of 75° or less is formed between a plurality of crystal grains constituting the channel region 12. Further, the surface roughness of the channel region, 12 is smaller than 20 nm, the internal tensile stress thereof is 109 dyn/cm2 or more, and the density of crystal defects contained therein is 1017 cm−3 or less. The density of metal elements contained in the whole semiconductor layer including the channel region 12 is 1019 cm−3 or less.
When the production process and apparatus for forming a polycrystalline semiconductor film by melt recrystallizing a semiconductor thin film shown in
According to this embodiment, a high-quality polycrystalline semiconductor film whose grain boundary, grain size and crystal orientation can be controlled and whose film roughness and crystal defects formed by crystallization have been reduced can be formed on the insulating substrate made from glass or the like. According to this embodiment, a production process and apparatus for forming a low-cost and high-quality polycrystalline semiconductor film, which can reduce the number of production steps, can be applied to a large-area substrate, and have a high throughput are realized. Further, when the polycrystalline semiconductor film shown in this embodiment is used in an MIS type field effect transistor, the field effect mobility can be controlled to be about 300 cm2/V·s or more and variations in threshold voltage can be suppressed to ±0.2 V or less. According to this embodiment, a semiconductor device which operates with high performance and high reliability and is excellent in uniformity among devices can be obtained.
a) to 9(c) are diagrams for explaining a semiconductor device according to Embodiment 3 of the present invention. In this embodiment, a member which facilitates the partial radiation of heat during crystal growth is used.
a) to 9(c) show a semiconductor device having three polycrystalline silicon thin film transistors formed thereon.
In
a) to 10(e) are sectional views showing the production process of the thin film semiconductor device of this embodiment. A base layer which is a silicon dioxide film 101 and a Si3N4 layer as the insulating film 50 having a higher heat conductivity than the underlying layer film 101 are formed on the non-crystalline substrate 100 made from glass or the like (
The channel region 12 having a large grain size is obtained by a crystallization method shown in
a) and 2(b) show the crystal state of the semiconductor layer, particularly the channel region. The semiconductor layer is composed of a polycrystalline silicon film in which at least the main orientation of the channel region is {110} with respect to the surface of the gate insulating film and the main orientation of the surface almost perpendicular to a direction for connecting the above source region 20 and the drain region 19 is {100}. A small inclination angle grain boundary having a rotation angle of 70° or less is formed between a plurality of crystal grains constituting the channel region 12. Further, the surface roughness of the channel region 12 is smaller than 20 nm, the internal tensile stress thereof is 109 dyn/cm2 or more, the density of crystal defects contained therein is 1017 m−3 or less, and the density of metal elements contained in the whole semiconductor layer including the channel region 12 is 1019 cm−3 or less.
When the production process and apparatus for forming a polycrystalline semiconductor film by melt recrystallizing a semiconductor thin film shown in
According to this embodiment, a high-quality polycrystalline semiconductor film whose grain boundary, grain size and crystal orientation can be controlled and whose film roughness and crystal defects formed by crystallization have been reduced can be formed on the insulating substrate made from glass or the like. According to this embodiment, a production process and apparatus for forming a low-cost and high-quality polycrystalline semiconductor film, which can reduce the number of production steps, can be applied to a large-area substrate, and have a high throughput are realized. Further, when the polycrystalline semiconductor film of this embodiment is used in an MIS type field effect transistor, the field effect mobility can be controlled to be about 300 cm2/V·s or more, variations in threshold voltage can be suppressed to ±0.2 V or less, and a semiconductor device which operates with high performance and high reliability and is excellent in uniformity among devices can be obtained.
a) to 11(c) are diagrams for explaining a semiconductor device according to Embodiment 4 of the present invention.
The channel region 12 having a large grain size is obtained by a crystallization method shown in
a) and 2(b) show the crystal state of the semiconductor layer, particularly the channel region. The semiconductor layer is composed of a polycrystalline silicon film in which at least the main orientation of the channel region is {110} with respect to the surface of the gate insulating film and the main orientation of the surface almost perpendicular to a direction for connecting the above source region 20 and the drain region 19 is {100}. A small inclination angle grain boundary having a rotation angle of 70° or less is formed between a plurality of crystal grains constituting the channel region 12. Further, the surface roughness of the channel region 12 is smaller than 20 nm, the internal tensile stress thereof is 109 dyn/cm−2 or more, the density of crystal defects contained therein is 1017 m−3 or less, and the density of metal elements contained in the whole semiconductor layer including the channel region 12 is 1019 cm−3 or less.
When the production process and apparatus for forming a polycrystalline semiconductor film by melt recrystallizing a semiconductor thin film shown in
According to this embodiment, a high-quality polycrystalline semiconductor film whose grain boundary, grain size and crystal orientation can be controlled and whose film roughness and crystal defects formed by crystallization have been reduced can be formed on the insulating substrate made from glass or the like. According to this embodiment, a production process and apparatus for forming a low-cost and high-quality polycrystalline semiconductor film, which can reduce the number of production steps, can be applied to a large-area substrate, and have a high throughput are realized. Further, when the polycrystalline semiconductor film of this embodiment is used in an MIS type field effect transistor, the field effect mobility can be controlled to be about 300 cm2/V·s or more, variations in threshold voltage can be suppressed to ±0.2 V or less, and a semiconductor device which operates with high performance and high reliability and is excellent in uniformity among devices can be obtained.
According to the present invention, there is obtained a semiconductor device having on an insulating substrate made from glass or the like a high-quality polycrystalline semiconductor film whose grain boundary, grain size and crystal orientation can be controlled and whose film roughness and crystal defects formed by crystallization have been reduced. There are also provided a production process and apparatus for forming a low-cost and high-quality polycrystalline semiconductor film, which can reduce the number of production steps, can be applied to a large-area substrate, and have a high throughput. Moreover, there are obtained a production process and apparatus for forming on an inexpensive insulating substrate made from glass or the like a high-quality polycrystalline semiconductor film which operates with high performance and high reliability and is excellent in uniformity among devices, as well as a semiconductor device comprising the above polycrystalline semiconductor film.
According to the present invention, a thin film semiconductor device can be formed on a non-crystalline substrate. Further, there is provided a process for producing a polycrystalline semiconductor thin film, which can be used for the above device. Still further, there is provided a production apparatus useful for the above production process.
| Number | Date | Country | Kind |
|---|---|---|---|
| 2001-19570 | Jan 2001 | JP | national |
This application is a Divisional application of application Ser. No. 09/791,853, filed Feb. 26, 2001, the entire disclosure of which is hereby incorporated by reference. Now U.S. Pat. No. 6,756,614.
| Number | Name | Date | Kind |
|---|---|---|---|
| 5543351 | Hirai et al. | Aug 1996 | A |
| 5624860 | Plumton et al. | Apr 1997 | A |
| 5815494 | Yamazaki et al. | Sep 1998 | A |
| 6303963 | Ohtani et al. | Oct 2001 | B1 |
| 6440824 | Hayashi et al. | Aug 2002 | B1 |
| 6451631 | Grigoropoulos et al. | Sep 2002 | B1 |
| 6635554 | Im et al. | Oct 2003 | B1 |
| 20010026835 | Tanaka | Oct 2001 | A1 |
| 20020031876 | Hara et al. | Mar 2002 | A1 |
| 20020040981 | Yamazaki et al. | Apr 2002 | A1 |
| Number | Date | Country |
|---|---|---|
| 0043691 | Mar 1991 | EP |
| 03068167 | Jul 1997 | JP |
| 09181325 | Jul 1997 | JP |
| WO 9745827 | Jan 1982 | WO |
| Number | Date | Country | |
|---|---|---|---|
| 20040063337 A1 | Apr 2004 | US |
| Number | Date | Country | |
|---|---|---|---|
| Parent | 09791853 | Feb 2001 | US |
| Child | 10670356 | US |