Tight oil reservoir CO2 flooding multi-scale channeling control system and preparation method

Abstract

A tight oil reservoir CO2 flooding multi-scale channeling control system and a preparation method, including nanoscale CO2 responsive worm-like micellar systems and micron-scale CO2 responsive dispersion gel, are provided. The nanoscale CO2 responsive worm-like micelle system is prepared by CO2 reactive monomers and organic anti-ion monomers stirred in water. The micron-scale CO2 responsive dispersion gel is made of acrylamide, a responsive monomer, a silane coupling agent modified hydroxylated multi-walled carbon nanotubes as raw materials, cross-linked in water. The tight oil reservoir CO2 multi-scale channel control system, has strong flow control ability during CO2 displacement, and high-strength carbon nanotubes are introduced into the micro-scale CO2 responsive dispersion gel, which effectively improves the strength and long-term stability of the dispersion gel, significantly enhances the sealing effect on cracks, and after displacement of the CO2 of the system, the worm-like micelles revert to spherical micelles with good responsive reversibility.

Description

FIELD OF THE INVENTION

The invention relates to the technical field of oilfield development, in particular to a tight oil reservoir CO₂ flooding multi-scale channeling control system and preparation method.

BACKGROUND OF THE INVENTION

The country is rich in tight oil resources, with geological resources of about 200×108 t. Under the background that the country has great crude oil consumption, and conventional crude oil resources are far from meeting the national demand, the efficient development of tight oil is very urgent. However, tight oil reservoirs have low permeability, poor pore-throat connectivity, and strong microscopic heterogeneity, resulting in almost no productivity before fracturing. Although the productivity is significantly improved after fracturing, but the water rises rapidly and the recovery efficiency is low (generally between 5% and 10%), therefore, it is necessary to improve the production of tight oil reservoirs through enhanced oil recovery technology.

Under the realistic background of intensified global climate change and the goal of “carbon peaking and carbon neutralization”, CO₂ flooding is the important pathways for CO₂ sequestration and recycling, CO₂ flooding is also an important emission reduction technology for zero carbon and negative carbon. However, after volume fracturing of tight oil reservoirs, the artificial fracture network is complex, and the CO₂ injected into will be premature breakthrough along the fracture, resulting in low sweep efficiency and recovery efficiency. Therefore, how to realize equilibrium CO₂ flooding under cross-scale conditions of tight reservoir fracture and matrix permeability has become a research hotspot.

Foam and gel are commonly used in oilfields to control fractures to achieve cross-scale equilibrium CO₂ flooding in reservoirs, but they have fatal shortcomings in channeling control in tight oil reservoirs. The higher viscosity of the foam and the Jamin effect endow it with better plugging performance in heterogeneous reservoirs, but its strength and stability are not enough to control fractures; the base fluid of the gel system has fluid loss, chromatographic separation and macromolecular degradation, resulting in unstable gel strength and matrix damage. Therefore, it is urgent to develop low-damage matrix and selective channeling control system for fractured high-strength tight oil reservoirs with CO₂ injection.

Currently more and more CO₂ responsive materials have been developed that are inexpensive, plentiful and environmentally friendly. Current reported CO₂ responsive materials include responsive block polymers, microspheres, and worm-like micelles, which size will increase after in contact with CO₂, and the size will be recovered after other gases are used to replace CO₂, showing CO₂ switch function, providing the possibility for the construction of tight oil reservoirs CO₂ flooding selective channeling control system. At present, it has been reported that some scholars have used nano-scale CO₂ switch-type worm-like micelles for preventing CO₂ channeling in fractured low-permeability reservoirs, and the blocking ability of CO₂ switch-type worm-like micelles was clarified through artificial fracture displacement experiments, but the applicable temperature is low (<60° C.). Some scholars have also developed micron-scale CO₂ switch-type dispersion, and revealed the switching property through the change of particle size under CO₂/N₂ atmosphere, and its channeling potential was clarified by the fracture core displacement experiment, but CO₂ switch-type dispersion is used in large concentrations, so there is an urgent need to develop low-cost CO₂ switch-type temperature-resistant channeling control system to realize cross-scale CO₂ equilibrium displacement in tight oil reservoirs, and CO₂ resource utilization in the process of channeling control.

SUMMARY OF THE INVENTION

For existing shortcomings of the CO₂ responsive anti-channeling system, the present invention proposes a CO₂ flooding multi-scale channeling control systems, which have good deep migration ability, CO₂ responsiveness and high viscosity, suitable for CO₂ anti-channeling during displacement after fracturing in tight oil reservoirs.

The present invention discloses a tight oil reservoir CO₂ flooding multi-scale channeling control system, including nanoscale CO₂ responsive worm-like micelle system and micron-scale CO₂ responsive dispersion gel, wherein, in mass percent, the micron-scale CO₂ responsive dispersion gel are prepared by cross-linking the following components:

acrylamide 15%-25%;

responsive monomer 3%-8%;

silane coupling agent modified hydroxylated multi-walled carbon nanotubes 0.05%-0.1%;

initiator 0.01%-0.1% of total monomer mass;

cross-linking agent 0.5%-2% of the total monomer mass;

the other is water, and the total mass percent of the components is 100%;

the preparation method of the micron-scale CO₂ responsive dispersion gel, mainly includes:

after the silane coupling agent-modified hydroxylated multi-walled carbon nanotubes are dispersed uniformly in water by ultrasonic waves, under the condition of stirring speed of 300-500 r/min, acrylamide, responsive monomer, initiator and cross-linking agent are respectively added to the solution; inject N₂ into the solution until the solution becomes viscous, and use a thermometer to monitor the temperature change of the solution at this time, until the temperature of the solution rises to the highest temperature, the solution is in thermal insulation for 2-4 hours under the condition of the highest temperature of the solution to obtain a black gel; after granulation, drying and pulverization, obtain micron CO₂ responsive dispersion gel;

In one embodiment, in terms of concentration, the nanoscale CO₂ responsive worm-like micelle system is prepared by cross-linking the following components:

CO₂ responsive monomer 30-90 mmol/L;

organic counter ion monomer 30-90 mmol/L;

the solvent is water;

the preparation method of the nanoscale CO₂ responsive worm-like micelle system is:

CO₂ responsive monomer is completely dissolved in water to formulate CO₂ responsive monomer solution, under the condition of stirring speed of 300-500 r/min, add organic counter ion monomer with the same amount of the CO₂ responsive monomer to the CO₂ responsive monomer solution, and stir at room temperature until it is uniform to obtain nano-scale CO₂ responsive worm-like micelle system.

Furthermore, the CO₂ responsive monomer is one of N,N-dimethylcyclohexylamine; N,N-dimethylbenzylamine; N,N-dimethylbutylamine; tetramethylethylenediamine; trimethylamine; N,N-Dimethyloleic acid amidopropyl tertiary amine; diethylenetriamine; cocoyl dimethyl tertiary amine; erucic acid amidopropyl dimethyl tertiary amine; or a combination thereof.

Furthermore, the organic counter ion monomer is one or a combination of sodium p-styrenesulfonate, sodium dodecylbenzenesulfonate, sodium p-toluenesulfonate and sodium oleate.

In another embodiment, the silane coupling agent used for the modification of the hydroxylated multi-walled carbon nanotubes is one or a combination of γ-methacryloyloxypropyltrimethoxysilane, vinyl tri(β-methoxyethoxy) silane, and vinyl triethoxy silane.

In one embodiment, the responsive monomer is one of N-methyl-N-vinylformamide, N,N-diethylaminoethyl methacrylate and dimethylaminoethyl methacrylate, or a combination thereof.

In one embodiment, the initiator is composed of ammonium persulfate, ammonium hydrogen sulfite and azobisisobutyramidine hydrochloride in a weight ratio of 1:1:2.

In one embodiment, the cross-linking agent is selected from one of N,N-methylenebisacrylamide, phenolic crosslinking agent and polyethyleneimine, or a combination thereof.

Another object of present invention is to provide a preparation method of the tight oil reservoir CO₂ flooding multi-scale channeling control system, mainly includes the following steps: micron-scale CO₂ responsive dispersion gel is added to nano-scale CO₂ responsive worm-like micelles to form an initial mixing system to allow the concentration range of the micron-scale CO₂ responsive dispersion gel in the initial mixing system is 0.3%-0.5%, and then the initial mixing system is stirred to allow the micron-scale CO₂ responsive dispersion gel in nano-scale CO₂ responsive worm-like micelle system uniform suspension to obtain the tight oil reservoirs CO₂ multi-scale channeling control system.

Compared with the prior art, the beneficial effects of the present invention are:

1. After nano-scale CO₂ responsive worm-like micelle system contacts CO₂, the spherical micelles were transformed into worm-like micelles, the solution viscosity increased significantly, and the flood control capability is enhanced during CO₂ displacement;

2. High-strength carbon nanotubes is introduced into the micron CO₂ responsive dispersion gel, improves the strength and long-term stability of the dispersion gel. After the dispersion gel contacts CO₂, the hydrophilicity is enhanced, the size of the dispersion gel becomes larger, and the plugging effect on cracks is enhanced;

3. Nanoscale CO₂ responsive worm-like micelles coupled with micron-scale CO₂ responsive dispersion gel system, forms a whole through supramolecular interactions after contact CO₂, thus enhancing the plugging strength of the system during the CO₂ displacement process; After displacement the CO₂ in the system, the size of the dispersion gel becomes smaller, and the worm-like micelles recovers to spherical micelles, showing good response reversibility.

BRIEF DESCRIPTION OF THE DRAWINGS

In order to more clearly illustrate the technical solution of the present invention, the drawings described in the embodiment will be briefly described below, and it should be understood that the following drawings are only shown in some embodiments of the present invention, so it should be seen as a defined scope, and will be obtained in accordance with these figures, without paying creative labor, in terms of ordinary skill in the art.

FIG. 1 shows CO₂ responsive performance evaluation result graph of the tight oil reservoirs CO₂ responsive multi-scale channeling control system;

FIG. 2 shows a microscopic topography of the tight oil reservoirs CO₂ responsive multi-scale channeling control system;

FIG. 3 shows a test chart of anti-channeling performance of the tight oil reservoirs CO₂ responsive multi-scale channeling control system during CO₂ displacement.

DETAILED DESCRIPTION OF PREFERRED EMBODIMENTS

The present invention will be further described in detail below with reference to the embodiments and the accompanying drawings, but the embodiments of the present invention are not limited thereto.

Example 1

1) Preparation of Nanoscale CO₂ Responsive Worm-Like Micellar Systems

Dissolve N,N-dimethyl oleoaminde-propylamine in deionized water, prepare 200 mL of N,N-dimethyloleic acid amidopropyl tertiary amine solution with a concentration of 90 mmol/L. Add 18 mmol sodium p-styrene sulfonate to the above solution under the condition of stirring at a stirring speed of 300 r/min, and stop stirring after the solution is uniform to obtain nano-scale CO₂ responsive worm-like micelle system.

2) Micron CO₂ Preparation of Responsive Dispersion Gel

0.1 g of γ-methacryloyloxypropyl trimethoxysilane modified hydroxylated multi-walled carbon nanotubes were uniformly dispersed in 75 mL of deionized water under ultrasonic conditions, and then under the condition of stirring at a stirring speed of 300 r/min, 20 g of acrylamide, 5 g N,N-diethylaminoethyl methacrylate, 0.5 mL ammonium persulfate (concentration 1 wt %), 0.5 mL sodium bisulfite (concentration 1 wt %) and 1 mL azobisisobutyramidine hydrochloride (concentration 1 wt %) %) and 1 mL of phenolic cross-linking agent were added to the solution. The solution is then introduced with N₂ until the solution becomes viscous and use a thermometer to monitor the temperature of the solution. When the temperature of the solution rises to the highest point and starts to cool down, keep the temperature for 2 hours to obtain a black monomer gel; the monomer gel is granulated, dried, pulverized to get micron CO₂ responsive dispersion gel.

It is worth noting that the method for modifying carbon nanotubes by using a silane coupling agent to prepare the above-mentioned silane-modified carbon nanotubes is a prior art in the art, and will not be repeated here.

3) Preparation of CO₂ Responsive Multiscale Channeling Control Systems.

0.8 g micron-scale CO₂ responsive dispersion gel obtained above was added to the aforementioned 200 mL of 90 mmol/L nano-scale CO₂ responsive worm-like micelle system, fully stirred until the dispersion gel is uniformly suspended and dispersed in the micelle system, that is, the tight oil reservoir CO₂ responsive multi-scale channeling control system.

Example 2

1) Preparation of Nanoscale CO₂ Responsive Worm-Like Micellar Systems

Dissolve N,N-dimethyl oleoaminde-propylamine in deionized water, prepare 200 mL of N,N-dimethyloleic acid amidopropyl tertiary amine solution with a concentration of 70 mmol/L, and under a condition of stirring at a stirring speed of 500 r/min, add 14 mmol sodium oleate is added to the above solution, and stop stirring after the solution is uniform to obtain nano-scale CO₂ responsive worm-like micelle system.

2) Preparation of Micron CO₂ Responsive Dispersion Gel

0.07 g of γ-methacryloyloxypropyl trimethoxysilane modified hydroxylated multi-walled carbon nanotubes are uniformly dispersed in 70 mL of deionized water under ultrasonic conditions, and then under a condition of stirring at a stirring speed of 500 r/min, 20 g of acrylamide, 8 g N,N-diethylaminoethyl methacrylate, 0.6 mL ammonium persulfate (concentration 1 wt %), 0.6 mL sodium bisulfite (concentration 1 wt %) and 1.2 mL azobisisobutyramidine hydrochloride (concentration 1 wt %) and 0.2 g N,N-methylenebisacrylamide are added to the solution. The solution is then introduced with N₂ until the solution becomes viscous and use a thermometer to monitor the temperature of the solution. When the temperature of the solution rises to the highest point and starts to cool down, keep the temperature for 2 hours to obtain a black monomer gel; the monomer gel is granulated, dried, pulverized to get micron CO₂ responsive dispersion gel.

3) Preparation of CO₂ Responsive Multiscale Channeling Control System

1.0 g micron-scale CO₂ responsive dispersion gel obtained above is added to the aforementioned 200 mL of 70 mmol/L nanoscale CO₂ responsive worm-like micelle system, fully stirred until the dispersion gel is uniformly suspended and dispersed in the micelle system, that is, obtaining the tight oil reservoir CO₂ responsive multi-scale channeling control system.

1. CO₂ Responsive Evaluation of the Tight Oil Reservoirs CO₂ Responsive Multi-Scale Channeling Control System

Under stirring condition at a rate of 100 mL/min, CO₂ is injected into the tight oil reservoir CO₂ responsive multi-scale channeling control system prepared in Example 1. After 60 min, the viscosity of the system at 30° C. was measured by Brookfield DV-III viscometer (shear rate 7.34s^-1); then inject N₂ into the system under the same conditions, repeat the above steps three times, observe the CO₂ of the system responsiveness and reversibility, the experimental results are as follows FIG. 1 shown.

It can be seen that after the system contacts CO₂, the viscosity increased from 10.4 mPa·s to 2339 mPa·s. When the CO₂ in the system is replaced by N₂, the viscosity of the system was reduced to 10.4 mPa·s. After 3 cycles, the highest viscosity of the system remained at 2339 mPa·s, and the lowest viscosity remained at 10 mPa·s, showing good CO₂ responsiveness and reversibility.

2. Micromorphology of Tight Oil Reservoirs CO₂ Responsive Multiscale Channeling Control System

Under stirring conditions at a rate of 100 mL/min, CO₂ is injected into the tight oil reservoir CO₂ responsive multi-scale channeling control system prepared in Example 2, after 60 min, stop the introduction of CO₂, the micro-morphology of the system was observed by environmental scanning electron microscope, and the results are as FIG. 2 shown. The three-dimensional network structure can be clearly observed in the system, which is the basic structure of worm-like micelles. In addition, supramolecular aggregates formed by worm-like micelles and particle side chains can be observed on the surface of the disperse gel. The dispersion gel and worm-like micelles are formed as a whole through supramolecular aggregates, which can effectively increase the anti-channeling properties of the system, ensuring that the channeling control effect of the entire channeling control system.

3. Evaluation of Anti-Channeling Performance

To verify the effect of the present invention proposed CO₂ responsive multi-scale channeling control system in tight oil reservoir CO₂ flooding, the development of CO₂ oil displacement experiment, using the CO₂ responsive multi-scale channeling control system prepared in Example 2. Fractured rock slabs were used to carry out the displacement experiments. The rock slab parameters are 10 cm in length and width, 1 cm in height, and 0.2 mm in crack width. With “CO₂ flooding-injection system-CO₂ flooding-injection system-CO₂ flooding-injection system-CO₂ flooding” step, keeping the injection volume of each system at 0.25 PV, the final measurement results are as follows FIG. 3 shown. See FIG. 3, It can be seen that when CO₂ is first injected, the injected CO₂ channeling occurs along the fracture, and no crude oil is recovery at this time; when the system is injected in an alternate way, the system and CO₂ full contact, the viscosity of the system increases, a higher pressure gradient is established, and the injected CO₂ turning to enter the matrix, expanding the swept volume, when the pressure difference reaches about 0.2 MPa, the final recovery factor is increased by about 23%, and it has good channeling control potential.

The above description is only a preferred embodiment of the present invention, but the protection scope of the present invention is not limited to this. Changes or substitutions should be included within the protection scope of the present invention. Therefore, the protection scope of the present invention should be subject to the protection scope of the claims.

Claims

1. A tight oil reservoir CO2 flooding multi-scale channeling control system, comprising nanoscale CO2 responsive worm-like micelle system and micron-scale CO2 responsive dispersion gel; wherein, in mass percent, the micron-scale CO2 responsive dispersion gel are prepared by cross-linking the following components:acrylamide 15%-25%; responsive monomer 3%-8%;silane coupling agent modified hydroxylated multi-walled carbon nanotubes 0.05%-0.1%;initiator 0.01%-0.1% of total monomer mass;cross-linking agent 0.5%-2% of the total monomer mass; andwater, wherein the total mass percent of the components is 100%;the preparation method of the micron-scale CO2 responsive dispersion gel is:after the silane coupling agent modified hydroxylated multi-walled carbon nanotubes are dispersed uniformly in water by ultrasonic waves, under the condition of stirring speed of 300-500 r/min, the acrylamide, responsive monomer, initiator and cross-linking agent are respectively added to the solution; N2 is injected into the solution until the solution becomes viscous, and a thermometer is used to monitor the temperature change of the solution, until the temperature of the solution rises to a highest temperature when cooling down starts, the solution is kept in thermal insulation for 2-4 hours under the condition of the highest temperature of the solution to obtain a black gel; micron-scale CO2 responsive dispersion gel is obtained after granulation, drying and pulverization of the black gel;wherein, the responsive monomer is N-methyl-N-vinylformamide, N,N-diethylaminoethyl methacrylate, dimethylaminoethyl methacrylate, or a combination thereof;wherein, the nanoscale CO2 responsive worm-like micelle system is prepared by cross-linking the following components:CO2 responsive monomer 30-90 mmol/L;organic counter ion monomer 30-90 mmol/L; anda solvent comprising water;the preparation method of the nanoscale CO2 responsive worm-like micelle system is:CO2 responsive monomer is completely dissolved in water to formulate CO2 responsive monomer solution, under the condition of stirring speed of 300-500 r/min, the organic counter ion monomer is added with the same amount of the CO2 responsive monomer to the CO2 responsive monomer solution, and the solution is stirred at room temperature to obtain uniform nano-scale CO2 responsive worm-like micelle system;wherein the CO2 responsive monomer is N,N-dimethylcyclohexylamine, N,N-dimethylbenzylamine, N,N-dimethylbutylamine, tetramethylethylenediamine, trimethylamine, N,N-dimethyloleoaminde-propylamine, diethylenetriamine, cocoyl dimethyl tertiary amine, erucic acid amidopropyl dimethyl tertiary amine, or a combination thereofthe organic counter ion monomer is sodium p-styrenesulfonate, sodium dodecylbenzenesulfonate, sodium p-toluenesulfonate, sodium oleate, or a combination thereof.

2. The tight oil reservoir CO2 flooding multi-scale channeling control system as claimed in claim 1, wherein the silane coupling agent modified hydroxylated multi-walled carbon nanotubes is γ-methacryloyloxypropyltrimethoxy silane, vinyl tri(β-methoxyethoxy) silane, vinyl triethoxy silane, or a combination thereof.

3. The tight oil reservoir CO2 flooding multi-scale channeling control system as claimed in claim 1, wherein the initiator is composed of ammonium persulfate, ammonium hydrogen sulfite and azobisisobutyramidine hydrochloride in a weight ratio of 1:1:2.

4. The tight oil reservoir CO2 flooding multi-scale channeling control system as claimed in claim 1, wherein the cross-linking agent is N,N-methylenebisacrylamide, phenolic crosslinking agent, polyethyleneimine, or a combination thereof.