The present disclosure relates to the field of touch display, and in particular to a method for manufacturing a touch panel, a touch panel, a touch screen and a display device.
New-generation one glass solution (OGS, where an indium tin oxide (ITO) conductive film and a sensor are directly formed on a protective glass substrate) product is a new trend of capacitive touch screens. Compared with a product with a sensor glass/tempered glass (G/G) cover plate, one glass substrate is saved in the OGS product, thereby reducing the production cost and improving the yield.
A process of manufacturing a traditional OGS product includes: arranging an ink layer surrounding a transparent substrate to form an ink border; forming, on the transparent substrate with the ink border, a vanishing layer made of silicon dioxide (SiO2) and niobium pentoxide (Nb2O5); sputtering an ITO layer onto the vanishing layer at a high temperature (about 280° C.); and coating a planarization layer onto the ITO layer. Although the ITO layer formed by sputtering at a high temperature has a high degree of crystallization and a good vanishing effect, the planarization layer may be prone to falling off and the high-temperature resistance of the ink is highly demanded. In recent years, a process of sputtering the ITO layer at a low temperature (200° C. to 250° C.) has been introduced to optimize process conditions. In addition, the vanishing effect of the traditional vanishing layer made of SiO2 and Nb2O5 is not good due to the degree of crystallization of ITO. Furthermore, when a new-type ITO pattern is applied, the process is highly demanded, the production cost is increased, and the yield cannot be guaranteed.
A main object of the present disclosure is to provide a touch panel manufacturing method, a touch panel, a touch screen and a display device, so as to simplify a process and improve a vanishing effect during the vanishing of a touch panel electrode.
In one aspect, the present disclosure provides in some embodiments a method for manufacturing a touch panel, including steps of: forming, on a transparent substrate, a non-opaque film layer with a micro-pattern; and forming a touch panel electrode on the non-opaque film layer; where the non-opaque film layer is configured to vanish a shadow of the touch panel electrode.
Alternatively, the micro-pattern is of a regular shape.
Alternatively, the step of forming on the transparent substrate the non-opaque film layer with the micro-pattern includes forming the non-opaque film layer on the transparent substrate, and etching the non-opaque film layer to form the micro-pattern.
Alternatively, the non-opaque film layer is an optical anti-reflection film layer.
Alternatively, prior to the step of forming the touch panel electrode on the non-opaque film layer, the method further includes forming an ink border on the non-opaque film layer with the micro-pattern, and subsequent to the step of forming the touch panel electrode on the non-opaque film layer, the method further includes forming a planarization layer on the transparent substrate with the touch panel electrode.
Alternatively, the touch panel electrode is an indium tin oxide (ITO) electrode, and the step of forming the touch panel electrode on the non-opaque film layer further includes forming the touch panel electrode within a predetermined temperature range, where the predetermined temperature range is from 200° C. to 250° C. inclusively.
In another aspect, the present disclosure provides in some embodiments a touch panel, including: a transparent substrate; a non-opaque film layer with a micro-pattern and formed on the transparent substrate; and a touch panel electrode formed on the non-opaque film layer, where the non-opaque film layer is configured to vanish a shadow of the touch panel electrode.
Alternatively, the micro-pattern is of a regular shape.
Alternatively, the non-opaque film layer is an optical anti-reflection film layer.
Alternatively, the touch panel further includes: an ink border formed on the non-opaque film layer with the micro-pattern; and a planarization layer formed on the transparent substrate with the touch panel electrode.
Alternatively, the touch panel electrode is an ITO electrode formed on the non-opaque film layer within a predetermined temperature range, and the predetermined temperature range is from 200° C. to 250° C. inclusively.
Alternatively, the touch panel is a one glass solution (OGS) capacitive touch panel.
In yet another aspect, the present disclosure provides in some embodiments a touch screen including the above-mentioned touch panel.
In still yet another aspect, the present disclosure provides in some embodiments a display device including the above-mentioned touch screen.
According to the method for manufacturing the touch panel, the touch panel, the touch screen and the display device in the embodiments of the present disclosure, different from the related art where a vanishing layer is provided, the non-opaque film layer with the micro-pattern is formed on the transparent substrate. As a result, it is able to control the haze, diffusion, viewing angle and concealment of the micro-pattern to vanish a shadow of the ITO electrode in a better manner, and to simplify the process.
The present disclosure will be described hereinafter in a clear and complete manner in conjunction with the drawings and embodiments. Obviously, the following embodiments are merely a part of, rather than all of, the embodiments of the present disclosure, and based on these embodiments, a person skilled in the art may, without any creative effort, obtain the other embodiments, which also fall within the scope of the present disclosure.
Unless otherwise defined, any technical or scientific term used herein shall have the common meaning understood by a person of ordinary skills. Such words as “one” or “one of” are merely used to represent the existence of at least one member, rather than to limit the number thereof. Such words as “on”, “under”, “left” and “right” are merely used to represent relative position relationship, and when an absolute position of the object is changed, the relative position relationship will be changed too.
As shown in
According to the method for manufacturing the touch panel in the embodiments of the present disclosure, different from the related art where a vanishing layer is provided, the non-opaque film layer with the micro-pattern is formed on the transparent substrate. As a result, it is able to control the haze, diffusion, viewing angle and concealment of the micro-pattern to vanish a shadow of the ITO electrode in a better manner, and to simplify the process.
In some embodiments of the present disclosure, the non-opaque film layer may be made of an organic resin material, SiO2 or silicon oxynitride (SiNO), as long as light may transmit through the non-opaque film layer and the micro-pattern may be formed on the non-opaque film layer to change a light path and vanish a shadow of a pattern of the touch panel electrode on the non-opaque film layer. The non-opaque film layer may be formed on the transparent substrate by coating, plating, depositing, etc., which will not be particularly defined herein.
The micro-pattern may be of a regular shape, so as to improve the vanishing effect.
In some embodiments of the present disclosure, the step of forming on the transparent substrate the non-opaque film layer with the micro-pattern includes forming the non-opaque film layer on the transparent substrate and etching the non-opaque film layer to form the micro-pattern. It should be noted that, the required pattern may be formed by exposing, developing and etching the non-opaque film layer, or formed by softening through heating and then impressing the non-opaque film layer. An appropriate process may be selected in accordance with the material of the non-opaque film layer.
Alternatively, the non-opaque film layer may be an optical anti-reflection film layer. Some existing touch panels may each have an optical anti-reflection film layer, and when the optical anti-reflection film layer is selected as the non-opaque film layer and the micro-pattern is formed on the optical anti-reflection film layer, it is able to simplify the process and reduce the production cost.
In the embodiments of the present disclosure, prior to the step of forming the touch panel electrode on the non-opaque film layer, the method further includes forming an ink border on the non-opaque film layer with the micro-pattern.
In the embodiments of the present disclosure, subsequent to the step of forming the touch panel electrode on the non-opaque film layer, the method further includes forming a planarization layer on the transparent substrate with the touch panel electrode.
In the embodiments of the present disclosure, the touch panel electrode may be an ITO electrode or any other touch panel electrode.
Alternatively, the touch panel electrode may be an ITO electrode, and the step of forming the touch panel electrode on the non-opaque film layer further includes forming the touch panel electrode within a predetermined temperature range, where the predetermined temperature range is from 200° C. to 250° C. inclusively.
According to the method in the embodiments of the present disclosure, through forming the ITO electrode by sputtering at a low temperature and forming the optical anti-reflection film layer, it is able to vanish the shadow, reduce the requirement on the high temperature resistance of the ink border, improve the vanishing effect as compared with the related art where a traditional vanishing layer is used in combination with the ITO electrode formed by sputtering at a low temperature, and prevent the planarization layer from being easily fallen off from the transparent substrate at a high temperature. In addition, the existing vanishing layer made of SiO2 and Nb2O5 is not required, so it is able to simple the process.
The present disclosure further provides in some embodiments a touch panel, which includes: a transparent substrate; a non-opaque film layer with a micro-pattern and formed on a transparent substrate; and a touch panel electrode formed on the non-opaque film layer, where the non-opaque film layer is configured to vanish the shadow of the touch panel electrode.
According to the touch panel in the embodiments of the present disclosure, different from the related art where a vanishing layer is provided, the non-opaque film layer with the micro-pattern is formed on the transparent substrate. As a result, it is able to control the haze, diffusion, viewing angle and concealment of the micro-pattern to vanish a shadow of the ITO electrode in a better manner, and to simplify the process.
Alternatively, the micro-pattern is of a regular shape, so as to improve the vanishing effect. It should be noted that, the micro-pattern may further correspond to a pattern of the touch panel electrode, so as to vanish the shadow of the pattern of the touch panel electrode in a better manner.
Alternatively, the non-opaque film layer may be an optical anti-reflection film layer, and the non-opaque film layer may be an optical anti-reflection film layer. Some existing touch panels may each have an optical anti-reflection film layer, and when the optical anti-reflection film layer is selected as the non-opaque film layer and the micro-pattern is formed on the optical anti-reflection film layer, it is able to simplify the process and reduce the production cost.
In the embodiments of the present disclosure, the touch panel may further include: an ink border formed on the non-opaque film layer with the micro-pattern, where the ink border may be plated onto the non-opaque film layer with the micro-pattern.
In the embodiments of the present disclosure, the touch panel may further include: a planarization layer formed on the transparent substrate with the touch panel electrode, where the planarization layer may be formed by coating.
In the embodiments of the present disclosure, the touch panel electrode may be an ITO electrode or any other touch panel electrode.
Alternatively, the touch panel electrode may be an ITO electrode formed on the non-opaque film layer within a predetermined temperature range, and the predetermined temperature range is from 200° C. to 250° C. inclusively.
According to the method in the embodiments of the present disclosure, through forming the ITO electrode by sputtering at a low temperature and forming the optical anti-reflection film layer, it is able to vanish the shadow, reduce the requirement on the high temperature resistance of the ink border, improve the vanishing effect as compared with the related art where a traditional vanishing layer is used in combination with the ITO electrode formed by sputtering at a low temperature, and prevent the planarization layer from being easily fallen off from the transparent substrate at a high temperature.
Alternatively, the touch panel may be an OGS capacitive touch panel. For an existing OGS capacitive touch panel including a vanishing layer, a vanishing effect of the ITO pattern is not significant when the ITO pattern is formed by sputtering at a low temperature (200° C. to 250° C.). In the embodiments of the present disclosure, a better vanishing effect may be obtained when the ITO electrode is formed by sputtering at a low temperature. In some other embodiments of the present disclosure, any other touch panel may also be used.
The method for manufacturing the touch panel and the touch panel will be described hereinafter.
At first, Step 21 is performed, i.e., an optical anti-reflection film is plated onto the transparent substrate 31 by vacuum magnetron sputtering.
Step 22 is then performed, i.e., the optical anti-reflection film is etched so as to form the optical anti-reflection film layer 32 with the micro-pattern.
Next, Step 23 is performed, i.e., the ink border 33 is plated onto the optical anti-reflection film layer 32 with the micro-pattern.
Then, Step 24 is performed, i.e., the ITO electrode 34 is formed on the optical anti-reflection film layer 32 by vacuum sputtering, exposing, developing and etching at a low temperature (200° C. to 250° C.), where the optical anti-reflection film layer 32 is configured to vanish the shadow of the ITO electrode.
Finally, the planarization layer 35 (e.g., a resin protective layer) is coated onto the optical anti-reflection film layer 32, so as to obtain the touch panel.
The micro-pattern 4 in
The present disclosure further provides in some embodiment a touch screen including the above-mentioned touch panel.
The present disclosure further provides in some embodiments a display device including the above-mentioned touch screen. The display device may be a liquid crystal display, a liquid crystal television, an organic light emitting diode (OLED) panel, an OLED display, an OLED television or an electronic paper.
The above are merely the preferred embodiments of the present disclosure. It should be noted that, a person skilled in the art may make further modifications and improvements without departing from the principle of the present disclosure, and these modifications and improvements shall also fall within the scope of the present disclosure.
| Number | Date | Country | Kind |
|---|---|---|---|
| 201410827968.1 | Dec 2014 | CN | national |
| Filing Document | Filing Date | Country | Kind |
|---|---|---|---|
| PCT/CN2015/078743 | 5/12/2015 | WO | 00 |