Claims
- 1. A transmissively read, optical recording medium comprising,
- a colloid matrix layer having a surface layer with a uniform thickness, the surface layer formed by irregular spheroidal silver grains having an average diameter less than 0.1 micron and being capable of modification with a light beam into smooth spherical silver grains having substantially the same average diameter as the irregular spheroidal silver grains but with a substantially reduced covering power than the irregular spheroidal silver grains before light beam modification.
- 2. The medium of claim 1 further comprising a thin, flexible, transparent overcoat disposed over said surface layer.
- 3. The medium of claim 2 wherein said overcoat is cured by one of ultraviolet radiation and electron beam radiation.
- 4. The medium of claim 3 wherein said overcoat is 10 to 75 microns thick.
- 5. The medium of claim 1 wherein said irregular spheroidal and said smooth spherical silver grains have average diameters within the range of 0.03 and 0.07 micron.
- 6. The medium of claim 1 wherein portions of said surface layer containing substantially said irregular spheroidal silver grains have a transmissivity contrast ratio of at least 1:1.2 with portions of said surface layer containing substantially said light beam modified smooth spherical silver grains.
- 7. The medium of claim 1 wherein portions of said surface layer containing substantially said irregular spheroidal silver grains have a white light optical density of at least 1.2 and portions of said surface layer containing substantially said light beam smooth spherical silver grains have a white light optical density of 0.9 and less.
- 8. The medium of claim 1 wherein portions of said surface layer containing substantially said smooth spherical silver grains show an increased transmissivity for red and near infrared light compared to the transmissivity of said irregular spheroidal grains.
- 9. The medium of claim 1 wherein said uniform thickness of said surface layer is not more than 1.0 micron thick.
- 10. The medium layer of claim 1 wherein said uniform thickness of said surface layer is within the range of 0.50 and 0.75 micron.
- 11. The medium of claim 1 wherein said colloid matrix comprises a clear gelatin.
- 12. A transmissively read, optical recording medium comprising,
- a colloid matrix layer having a surface layer with a thickness of not more than 1.0 micron, the surface layer formed by first and second type spheroidal silver grains having average diameters of not greater than 0.1 micron, the first type of spheroidal silver grains having a rough surface and the second type of spheroidal silver grains having a smooth surface, the first type of silver grains being capable of being modified by a light beam into the second type of silver grains, portions of the surface layer containing substantially the first type of silver grains being substantially less transmissive to a read beam than portions of the surface layer light beam modified to contain substantially the second type of silver grains.
- 13. The medium of claim 12 further comprising a flexible transparent overcoat having a thickness of between 10 and 75 microns.
- 14. The medium of claim 12 wherein said first and second types of spheroidal silver grains have average diameters within the range of 0.03 and 0.07 micron.
- 15. The medium of claim 12 wherein said portions of said surface layer containing substantially said first type of silver grains has a read beam transmissivity contrast ratio of at least 1:2 with said portions of said surface layer containing substantially said second type of silver grains.
- 16. The medium of claim 12 wherein said portions of said surface layer containing substantially the first type of spheroidal silver grains have a red light optical density of at least 1.0, and said portions of said surface layer containing substantially the second type of spheroidal silver grains have a red light optical density of 0.85 and less.
- 17. The medium of claim 12 wherein said uniform thickness of said surface layer is within the range of 0.50 and 0.75 micron.
- 18. The medium of claim 12 wherein said colloid matrix comprises clear gelatin.
- 19. A light beam sensitive photographic element containing the medium of claim 1.
- 20. The light beam sensitive photographic element of claim 19 wherein said element includes one of a microfiche and a wallet-size data card.
- 21. A light beam sensitive photographic element containing the medium of claim 12.
- 22. The light beam sensitive photographic element of claim 21 wherein said element includes one of a microfiche and a wallet-size data card.
- 23. A spheroidal silver grain of a first type that has an irregular shape with a non-smooth surface, the first type of spheroidal silver grain having a light beam induced capability for modification into a spheroidal silver grain of a second type having a smooth spherical shape with a generally smooth surface, the first and second types of silver grain having a diameter of not greater than 0.1 micron.
- 24. The silver grain of claim 23 wherein said silver grain of the first and second types has a diameter within the range of 0.03 to 0.07 micron.
- 25. The silver grain of claim 23 wherein said first type of silver grain is prepared by treating a silver halide grain having a diameter of not greater than 0.05 micron.
- 26. The silver grain of claim 25 wherein said silver halide grain is selected from the group consisting of silver chloride and silver bromide.
- 27. A method of making a transmissively read, optical recording medium comprising the steps of,
- forming a layer of silver precipitating nuclei in a monodispersed, photosensitive silver-halide emulsion layer having very fine grains having an average size of approximately 0.05 micron, the emulsion layer having a uniform thickness, and
- contacting the nucleated emulsion layer with a monobath solution containing a high level of sulfite whereby irregular shaped spherical silver grains are formed having an average diameter less than 0.1 m.
- 28. The method of claim 27 further comprising the step of providing a radiation cured overcoat over said monobath contacted emulsion layer.
- 29. The method of claim 27 whereby said silver-halide emulsion layer contains silver chloride.
- 30. The method of claim 27 whereby said nuclei layer is formed by exposure to light.
- 31. The method of claim 27 wherein said step of contacting said nucleated emulsion layer lasts between 2 seconds and 2 minutes.
- 32. The method of claim 27 wherein said monobath solution is maintained between the temperatures of 15.degree. and 40.degree. C.
- 33. The method of claim 27 wherein said level of sulfite in said monobath solution is within the range of 75 and 200 gr. per liter.
- 34. The method of claim 27 further comprising the step of fixing said monobath treated emulsion in a thiosulfite solution.
CROSS-REFERENCE TO RELATED APPLICATION
This application is a continuation-in-part of application Ser. No. 07/210,527, filed June 22, 1988, now U.S. Pat. No. 4,884,260, which is a divisional of application Ser. No. 7/039,507, filed Apr. 16, 1987, now U.S. Pat. No. 4,753,864.
US Referenced Citations (10)
Foreign Referenced Citations (1)
Number |
Date |
Country |
76068 |
Jan 1980 |
JPX |
Divisions (1)
|
Number |
Date |
Country |
Parent |
39507 |
Apr 1987 |
|
Continuation in Parts (1)
|
Number |
Date |
Country |
Parent |
210527 |
Jun 1988 |
|