Patent Application
20050152987
1. Field of the Invention
The present invention relates to a process and a method for producing osteoinductive particulate bone compositions or preparations, where the bone particles have improved osteoinduction activity and to methods for making and using same.
More particularly, the present invention relates to a process and a method for producing osteoinductive particulate bone compositions or preparations including a distribution of bone particles sizes, where the particles sizes are less that 355 μm or simply 355 μ and where the bone particles have improved osteoinductive activity.
2. Description of the Related Art
It is well known that implantation of bone decalcified with hydrochloric acid or of demineralized bone matrix into musculature of rodents leads to heterotopic bone formation (Urist, et al. 1983 and others). In fact, this is a standard laboratory test devised by Urist for the detection of bone morphogenetic protein (BMP) activity in various bone preparations. However, rodent animal models have a limitation, as these animals are peculiar in their ability to produce heterotopic cancellous bone in response to implantation of several tissues including bone and various bone preparations. Whether this parallels response in higher animals or in humans is unknown. However, the rodent animal model is a convenient one and it is easy to use.
It has been shown as early as the 1950's (LaCroix) that exposure of bone (autologous or allogeneic) to alcohol or to heat markedly diminishes its osteoinductive capacity. It has been also established, but is not necessarily acknowledged that intraosseous lipids serve as vehicle for BMP. Extraction of the same from bone allografts would likely interfere with the delivery of BMP or other growth factors at the site of osteoinductivity.
Thus, there is a need in the art for a particulate bone preparation that has superior initial osteoinductive capacity than traditional demineralized or chemically extracted bone.
Compositions
The present invention provides a particulate bone composition with improved osteogenic capacity or osteoinductive activity.
The present invention also provides a particulate bone composition including a particle size distribution of nascent bone particles with improved osteogenic capacity or osteoinductive activity.
The present invention also provides a particulate bone composition including a particle size distribution of nascent bone particles, allograft bone particles or mixtures or combinations thereof with improved osteogenic capacity or osteoinductive activity.
The present invention also provides a particulate bone composition including a particle size distribution of nascent bone particles, allograft bone particles or mixtures or combinations thereof with improved osteogenic capacity or osteoinductive activity, where the particles have a particle size less than or equal to about 355 μ, where μ means microns (1×10−6 m).
The present invention also provides an undemineralized, freeze dried particulate bone composition including a particle size distribution of nascent bone particles, allograft bone particles or mixtures or combinations thereof with improved osteogenic capacity or osteoinductive activity, where the particles having particle sizes between about 25 μ and about 355 μ.
The present invention also provides a particulate bone composition including a particle size distribution of nascent bone particles, allograft bone particles or mixtures or combinations thereof with improved osteogenic capacity or osteoinductive activity, where the particles have a particle size less than or equal to about 355 μ and having a distribution of particles having particles sizes between 355 μ and 250 μ, between 250 μ, and 150 μ and below 150 μ.
The present invention also provides a preferred particulate bone composition including a particle size distribution of nascent bone particles, allograft bone particles or mixtures or combinations thereof with improved osteogenic capacity or osteoinductive activity, where the distribution includes: (1) from about 1 wt. % to about 10 wt. % of 2355p particles, (2) from about 5 wt. % to about 15 wt. % of <355 μ and ≧300 μ particles, (3) from about 10 wt. % to about 25 wt. % of <300 μ and 225 μ particles, (4) from about 5 wt. % to about 15 wt. % of <250 μ and >180 μ particles, (5) from about 20 wt. % to about 40 wt. % of <180p and 2 106p particles, (6) from about 5 wt. % to about 15 wt. % of <106 μ and >75 μ particles, (7) from about 5 wt. % to about 15 wt. % of <75 μ and ≧53 μ particles, and (8) from about 1 wt. % to about 10 wt. % of ≦53 μ and ≦25 μ particles.
Methods
The present invention provides a method including the step of commutating or grinding of bone to form the particulate bone preparations of this invention, where the commutating or grinding is performed under conditions to ensure that a temperature of the bone being ground does not rise above a critical temperature that would reduce, diminish or eliminate its osteoinductive capacity or activity.
The present invention also provides a method for preparing non-demineralized cortical bone, cancellous bone or mixtures or combinations thereof having a desired particle size distribution including the step of commutating frozen or freeze-dried bone for a time and at a temperature sufficient to produce the desired particle size distribution, where the temperature is below a critical temperature known to be detrimental to an osteogenic capacity or osteoinductive activity of bone. The critical temperature is between about 45° C. to about 50° C., which significantly reduces or completely eliminates osteoinductive properties of bone. The commutating step of this invention includes a defined interruption of grinding so that the temperature to which the bone is exposed is carefully controlled so that the temperature of the bone is kept below the critical temperature which would result in a loss of osteoinductive activity. The mill grinder is preferably operated in cycles of about 8 seconds to about 18 seconds. The bone is then sieved for about 14 seconds to about 15 seconds or longer. This allows for sufficient cooling and for the removal of particles having the desired particle sizes according to the compositions of this invention. This method of defined interrupted commutating does not allow the temperature of bone or grinder to rise above about 33° C. from the initial temperature of the bone which is between about 18° C. and about 20° C. The defined interruption process cycle operates for no longer than 3 minutes with an average operating time of about 2.5 minutes being preferred. However, shorter or longer cycles can be employed provided of course that a temperature of the bone and grinder does not rise to or above the critical temperature, which is preferably set at less than or equal to 40° C., particularly, less than or equal to 35° C. and especially less than or equal to 33° C.
The present invention also provides a method repairing bone defects including the step of administering a composition of this invention to a bone defect site of an animal including a human to induce healing of bone defect.
The present invention also provides in vivo and in vitro methods for studying and assessing osteoinductive and toxicity properties of the particulate bone preparations of this invention. The in vivo assays include studies in fully immunocompetent non-human primates. In these animals, a 12×14 mm defect is created in a long bone. The defect is then filled with a bone graft material. The animals are examined at 3 and 6 weeks post-transplantation. The limbs are X-rayed and studied morphologically. The animals were then killed and the bone bearing the transplant was rapidly frozen in liquid nitrogen and then cut with a saw with a diamond blade and photographed. The specimens were then fixed in 10% formalin in Earle's balanced salt solution and decalcified in Pereney's fluid. Paraffin sections were cut and stained with hematoxylin eosin, Masson's trichrome stain and Romanowski-Giemsa stain. The in vitro assay was performed on primary or low-passage cultures of human periosteum or chondrocytes. The latter was employed to detect cytotoxicity (if any) of the preparations.
The invention can be better understood with reference to the following detailed description together with the appended illustrative drawings in which like elements are numbered the same:
FIGS. 5A-D depict non-human primate bone site preparation and implantation of allografts;
FIGS. 6A&B depict photographs of a control group distal femur having a defect 6 weeks postoperative;
FIGS. 7A&B depict photographs of distal femur defect filled with an autograft, 6 weeks post-transplantation;
FIGS. 8A-C depict photographs of distal femur having a defect filled with an allograft of this invention 2 weeks post-transplantation;
FIGS. 9A-C depict photographs of distal femur having a defect filled with a cortical microparticulate bone composition of this invention, 6 weeks post-transplantation;
FIGS. 10A-C depict photographs of distal femur having a defect filled with a cortical ground bone material, 6 weeks post-transplantation;
FIGS. 11A-C depict photographs of distal femur having a defect filled with a cancellous microparticulate bone composition of this invention, 6 weeks post-transplantation;
FIGS. 12A-C depict photographs of distal femur having a defect filled with powdered demineralized cortical bone 3 weeks post-transplantation;
FIGS. 13A-C depict photographs of distal femur having a defect filled with a powdered demineralized cortical bone allograft 6 weeks post-transplantation; and
FIGS. 14A-C depict photographs of proximal tibia having a defect filled with demineralized cortical crushed bone allograft 6 weeks post-transplantation.
The inventors have found that a composition that accelerates release of BMP and/or other growth factors can be constructed based on a unique particle size distribution of natural bone because the particles have multiple surfaces and are inherently three dimensional. The preferred the compositions of this invention have a distribution of particles all below about 355 μ with at least 30 wt. % of particles having a particle size of less than 180 μ. This particle size distribution provides a unique particulate bone composition of either cancellous bone or cortical bone or mixtures thereof with improved osteoinductive activity. This particulate bone can be effectively used as a single preparation or in mixture with various vehicles such as collagen matrices, viscous chemicals such as hydroxyethyl starch, polyvinyl pyrrolidone etc. The method of bone allograft/xenograft preparation described in the present invention avoids extraction of lipids or inactivation of growth factors and preserves bone composition in its native state. Bearing in mind the uncertainties of rodent animal models the inventors used non-human primates in testing various bone graft preparations. These were implanted intraosseously. In this model bone preparation of certain particle sizes gave unexpectedly superior results compared to other conventional bone grafts.
The present invention is based on the inventors unexpected discovery that Non-demineralized (undecalcified) cortical bone or cancellous bone or mixtures thereof in particle sizes less than about 355 μ repeatedly and reliably induces bone formation in defects in bones of non-human primates. Moreover, new bone formation is induced at a rapid rate with direct formation of new osteoid.
The inventors discovered using non-human primate model that this particulate bone preparation generally referred to as particulate bone has a high degree of osteoinductivity of a specific variety, i.e., it induces direct bone formation rather than bone formation through endochondral ossification. The use of non-human primate model with bone being the site of implantation provides information which is applicable to human response, unlike information derived from rodents which can produce heterotopic ossification in response to intramuscular introduction of various bone preparations, matrices or extracts.
The present invention broadly relates to a bone implant composition including a distribution of particles of bone having particle sizes less than or equal to about 355 μ and preferably a mixtures of particles having particles sizes between about 355 μ and about 250 μ, particles having particles sizes between about 250 μ and about 150 μ, and particles having particles sizes below about 150 μ, where the compositions have improved osteoinductive activity or osteogenic capacity.
The present invention broadly relates to a method for making a bone implant composition including a distribution of particles of bone having particle sizes of about 355 μ and preferably a mixtures of particles having particles sizes between about 355 μ and about 250μ, particles having particles sizes between about 250 μ and about 150μ, and particles having particles sizes below about 150 μ, where the compositions have improved osteoinductive activity or capacity, where the method includes the step of periodically grinding a bone sample into a composition of this invention, where the periods between each grinding are sufficient to maintain a temperature of the bone below about 33° C.
The present invention broadly relates to a method for treating bone defects including the step of administering one or more therapeutically effective amount of a bone implant composition including a distribution of particles of bone having particle sizes of about 355 μ to a bone defect, where composition preferably is a mixtures of particles having particles sizes between about 355 μ and about 250 μ, particles having particles sizes between about 250 μ and about 150 μ, and particles having particles sizes below about 150 μ, where the compositions have improved osteoinductive activity or capacity.
The present invention also broadly relates to particulate bone composition including a particle size distribution of nascent bone particles, autograft bone particles, xenograft bone particles, allograft bone particles or mixtures or combinations thereofwith improved osteoinductive capacity. Preferred distribution are shown in Table I.
From Table I, it is obvious that the preferred composition include a particle size distribution including at least 31 wt. % of particles have a diameter less than 180 μ, preferably at least 40 wt. % of particles have a diameter less than 1801i, and preferably at least 46 wt % of particles have a diameter less than 180w. Alternatively, the compositions have a particle size distribution including between about 30 wt. % and about 75 wt % of particles have a diameter less than 180 μ, preferably, between about 35 wt. % and about 60 wt. % of particles have a diameter less than 180 μ and particularly, between about 40 wt. % and about 50 wt. % of particles have a diameter less than 180 μ. One preferred embodiment of the composition of this invention includes a distribution of particles comprising about 50 wt % of particles having a particle size between about 250 μ and about 150 μ, about 25 wt % of particles having a particles size between about 150, and about 100 μ, and about 25 wt % of particles having a particle size less than about 100 μ. A typical composition prepared by according to the method of this invention has a particle size distribution of including:
The inventors have shown that micro-particulate bone has superior osteogenic capacity and osteoinductive activity, and in fact, that the smaller the p articles the better the osteoinductive activity. Thus, preferred embodiments of this invention include bone compositions having particle sizes: (a) less than or equal to about 355 μ, (b) less than or equal to 300 μ, (c) less than or equal to 250 μ, (d) less than or equal to 180 μ, (e) less than or equal 106 μ, (f) less than or equal to 75 μ, (g) less than or equal to 53 μ and (h) less than or equal to 25 μ. The inventors believe that compositions having smaller particles sizes or particle size distributions including smaller sized particles have superior osteogenic capacity and superior osteoinductive activity.
The osteogenic capacity or osteoinductive activity of the preparations of this invention are thought by the inventors to depend primarily on particle size and retention of unaltered growth factors and other substances. The osteogenic capacity or osteoinductive activity of either cortical bone or cancellous bone or mixtures thereof decreases if particles exceed the range of 355 μ. Likewise exposure of the same preparations to hydrogen peroxide, ethyl alcohol or isopropyl alcohol markedly decreases its osteoinductive capacity. The invention is directed to the method of preparation of non-demineralized osteoinductive bone particles as well as to the clinical application of these preparations.
It has been demonstrated that the preparations of this invention that comprise a defined particle size distribution of particulate cortical bone or cancellous bone or mixtures thereof exert osteoinduction in the skeletal structures of higher animals namely non-human primates. This animal model, unlike rodent models, which produce heterotopic bone formation in the muscles, is closest to humans. Thus, it can be anticipated that response to the particulate bone preparations of this invention in humans will be similar to that in non-human primates.
The present invention is directed to implants for stimulating osteoinduction, bone regrowth, and/or bone repair by the implantation of a particulate bone preparation of this invention in a bone defect in an animal including a human. Moreover, the present invention can include particulate bone that has been treated with additional bone growth factors to further enhance and improve bone regeneration after implantation.
The process of particulate bone preparation is equally applicable to allogeneic and xenogeneic bone. The particulate bone preparations of this invention are unique because they avoid entirely the need for harsh chemical treatments and extractions, which alter inherent native properties of bone. The particulate bone preparations of this invention can be produced either from freeze-dried bone not subjected to any chemical treatment or from frozen bone. The invention permits reproducible production of a particulate bone preparation with optimal osteoinductivity clearly demonstrable in higher animal models.
Histologic examination of bone sections filled with particulate bone showed significant healing and complete replacement of bone allograft particles with newly formed bone six weeks post implantation without cartilage components as shown in
Preparation of Particulate Bone Particles Measuring Less Than 355 μ
The present invention prepares particulate cortical bone or cancellous bone or mixtures thereof without “undesirable constituents.” For the purposes of the present invention the term “undesirable constituents” means any constituent other than osteoid tissue normally present in bone or bone marrow. This includes blood, bone marrow, free fat and soft connective tissue elements.
Detailed Description of the Preparation of the Particulate Bone
Particulate bone of a powdery consistency can be prepared from previously freeze-dried cortical bone or cancellous bone or mixtures thereof. After freeze-drying and associated processing which includes repeated washing in warm saline or other balanced salt solutions to remove “undesirable constituents”, the bone is immersed directly into liquid nitrogen vapor and is then freeze-dried in accordance with previously published procedures (Malinin 1, 2, 3) to a residual moisture of 5 to 6% or less. Residual moisture content was determined gravimetrically.
J Freeze-dried bone is cut into cubes with a band saw, an oscillating or a rotary saw without heating the bone preparation, by avoiding pressure on the bone being cut and by limiting the time of grinding to no more than 15 second for each surface being cut.
Cut bone cubes, rectangles or other small configurations are further cut in a turbo mill, micro hammer cutter mill, disc mill, toothed disc mill, jet mill or other similar mills capable of grinding bone or reducing bone to particles having a particle size less than about 355 μ. Although usually dry bone is ground, cutting of wet bone preparation can be also accomplished.
Any grinding process is associated with heat production. Heating bone above about 45° C. to about 50° C. is undesirable as the heat significantly reduces to completely abolishes osteoinductive properties of bone. Continuous grinding for 3 to 5 minutes in any of the conventional grinding mills will raise the temperature to 70° C. or above. The inventors have devised a method for defined interrupted grinding so that the temperature exposure to the bone can be carefully controlled and kept below a temperature which would not result in a loss of osteoinductive activity. The mill is operated in cycles of about 8 seconds to about 18 seconds, then the bone is sieved a duration of about 14 seconds to about 15 seconds. This does not allow the temperature of bone or grinder to rise above about 33° C. from the initial temperature of the product of between about 18° C. and about 20° C. The cycle operates for no longer than 3 minutes with an average operating time of about 2.5 minutes. The results of typical temperature profiles of bone being ground and that of the grinder and its components are shown graphically in
The above described procedures of repeated grinding and sieving allows for the preparation of specific formulation of non-decalcified particulate bone preparations with high osteoinductive properties. One preferred embodiment of this invention includes compositions having a particle size distributions as follows: (1) from about 24.6 wt % to about 36.3 wt % of particles having a particle size between about 350 μ and about 250 μ; (2) 22 wt % to about 25 wt % of particles having a particle size between 25 μ and about 150 μ; and (3) from about 36.7 wt % to about 46.7 wt % of particles having a particle size less than 150 μ. Particularly, the particles having a particle size below about 25 μ should have the following distribution: 35-65 wt % of particles having a particle size between about 250 μ and about 150 μ, about 10 wt % to about 40 wt % of particles having a particles size between about 150 μ and about 100 μ, and about 10 wt % to about 40 wt % of particles having a particle size less than about 100 μ. More particularly, the particles having a particle size below about 250 μ should have the following distribution: 40 wt % to about 60 wt % of particles having a particle size between about 250 μ and about 150 μ, about 15 wt % to about 35 wt % of particles having a particles size between about 150 μ and about 100g, and about 15 wt % to about 35 wt % of particles having a particle size less than about 100 μ. Especially, the particles having a particle size below about 250 μ should have the following distribution: 50 wt % of particles having a particle size between about 250 μ and about 150 μ, about 25 wt % of particles having a particles size between about 150 μ and about 100 μ, and about 25 wt % of particles having a particle size less than about 100 μ. Particles less than 150 μ are shown in the photograph of
Referring now to
Referring now to
Referring to FIGS. 2B&C, cut sections of the femur and the tibia with bone defects filled with preparations under study. Numbers 1 and 4 designate defects filled with a particulate preparation that is not demineralized. The defects are completely healed and replaced with newly formed trabecular bone. Number 2 is a defect filled with an autograft. The defect is partially filled with sclerotic bone. Number 3 is defect filled with granular bone. Graft particles are still visible and the defect is only partially filled.
Referring to
Referring now to
New Experimental Data
These examples illustrate a study of bone allograft particles size in relation to healing of bone defects in non-human primates.
Ideal size of particulate bone used to fill osseous defects has not been determined. Likewise, the osteoinductive properties of deminerialized and non-demineralized particulate bone have not been compared in a non-human primate model. Information obtained from rodent model studies might not be directly applicable to humans because osteoinductive capacity of bone allografts in rodents is measured by the formation of heterotopic bone. Humans and higher animals do not respond to extraosseous particulate allograft implantation by forming heterotopic bone. Thus, the inventors have studied the healing of experimentally induced bone defects in non-human primates packed with various particulate bone allograft preparations. These bone preparations were freeze-dried, non-demineralized and demineralized. Frozen particulate bone was also tested.
Studies were performed on 24 adult, young male baboon (Papio hymadryas). Bone allografts were excised and processed under aseptic conditions. Particulate alllografts were prepared in three different particles size distributions: 1) all particles less than 250 μ, referred to as “bone powder” in these examples; 2) particles between 500 μ and 800 μ, referred to as “ground bone” in these examples; and 3) particles between lmm and 2 mm, referred to as “crushed bone” in theses examples. Both non-demineralized and demineralized allografts were freeze-dried after freezing in liquid nitrogen vapor. Frozen preparations were ground in the frozen state to minimize heating as set forth above.
Bone allografts were placed in 10 mm diameter defects made with a burr in the distal femurs and proximal tibias of the right leg in AP or medial-lateral planes as shown in FIGS. 5A-D. Three or four defects were created in each animal. Control detects were left unfilled. Positive controls were filled with autografts. The soft tissue and skin were closed in layers with Vicryl sutures and after recuperation, the animals were returned to their enclosures without limitations of physical activity.
Animals were sacrificed at 2 to 3 weeks or at 6 weeks or at six weeks postopertion.
Referring now to FIGS. 5A-D, the surgical procedure for forming the filling the defects in the femur or tibia of a baboon is shown. Look at
Referring to
Referring to
Referring to
Referring to
Referring to
Referring to
Referring to FIGS. 12A-B, a section of distal femur with a defect filled with demineralized cortical bone powder three weeks post transplantation is shown, where the defect remains unhealed. Allograft material is plainly visible in the gross specimen as shown in FIGS. 12A&B and in the radiograph as shown in
Referring to
Referring to
Results
The control defects were filled with fibrous connective tissue, but remained unhealed six weeks postoperative. However, rims of newly formed bone were evident at the edges of the defects. Defects packed with particulate autografts were filled with newly formed cancellous bone. At two weeks, defects filled with microparticulate cortical bone allograft showed unaltered bone allograft particles in the center of the defect, and bone particles surrounded by osteoclasts and osteoblasts in the periphery. By six weeks, the defects were filled entirely with newly formed bone. Bone defects packed with cortical ground bone had clearly recognizable (macroscopic and microscopic) bone particles in the defect with early osteogenesis in the periphery. Defects packed with cortical crushed bone were similar in appearance to those packed with ground bone allografts.
Microparticulate cancellous bone allograft behaved in the same manner as did microparticulate cortical bone allograft. At six weeks, cancellous bone particles formed a new network bone with particles themselves surrounded by newly formed bone and repopulated with osteocytes. Active osteogenesis as evidenced by rims of osteoblasts surrounding the allograft particles was present. At three weeks, demineralized cortical bone particles placed in a defect were intact. There was only a thin rim of newly formed bone in the periphery, but this was separated from the allograft by a sleeve of mesenchymal tissue. At six weeks, there was clear evidence of endochondral bone formation in the periphery of the allograft mass. Demineralized crushed bone at six weeks had distinct particles with virtually no new bone formation except in the periphery as did cortical crushed bone allografts.
Discussion
The data showed a clear difference in the healing pattern of bone allografts in relationship to the size of the graft particles. The most complete and rapid healing was achieved with freeze-dried microparticulate cortical and cancellous bone allografts, i.e., allografts comprising micron sized particles. This type of graft was easy to pack into the defect cavity and to obliterate the defect. The bone powder grafts were hemostatic and highly osteogenic. The allografts incorporated by direct ossification. Allografts with larger particles (ground or crushed cortical bone) were difficult to impact and thus would not completely obliterate the defect. Although these two forms were osteogenic, the healing associated with these grafts was much slower than observed with the microparticulate bone grafts. No difference was noted between microparticulate cancellous and cortical bone preparations.
Results with demineralized bone allografts having comparable particles sizes to the non-demineralized allografts were disappointing. With these latter allografts, new bone formation was induced primarily only in the periphery. When demineralized allograft particles were replaced, endochondral ossification was noted.
Conclusion
Incorporation of particulate bone allografts is dependent on the size of the particles in the grafts and the method of its preparation. Freeze-dried, microparticulate cortical bone allografts first provide biomechanical support and most rapid healing of the defect into which they are placed. They incorporate by direct ossification, thus producing rapid new bone formation. Demineralized cortical bone powder allografts stimulate the surrounding bone, but by themselves do not undergo accretion. Healing from the periphery is accomplished via as lower process of endochondral ossification.
Closing
All references cited herein are incorporated by reference. While this invention has been described fully and completely, it should be understood that, within the scope of the appended claims, the invention may be practiced otherwise than as specifically described. Although the invention has been disclosed with reference to its preferred embodiments, from reading this description those of skill in the art may appreciate changes and modification that may be made which do not depart from the scope and spirit of the invention as described above and claimed hereafter.
This application claims provisional priority to U.S. Provisional Patent Application Ser. No. 60/508,191 filed 2 Oct. 2003.
| Number | Date | Country | |
|---|---|---|---|
| 60508191 | Oct 2003 | US |