Tungsten comprising nanomaterials and related nanotechnology

Information

  • Patent Grant
  • 7708974
  • Patent Number
    7,708,974
  • Date Filed
    Tuesday, May 10, 2005
    19 years ago
  • Date Issued
    Tuesday, May 4, 2010
    14 years ago
Abstract
Nanoparticles comprising tungsten, methods of manufacturing nanoparticles comprising tungsten, and applications of nanoparticles comprising tungsten, such as electronics, optical devices, photonics, reagents for fine chemical synthesis, pigments, and catalysts are provided.
Description
FIELD OF THE INVENTION

The present invention generally relates to methods of manufacturing submicron and nanoscale powders comprising tungsten and applications of such powders.


RELEVANT BACKGROUND

Nanopowders in particular and sub-micron powders in general are a novel family of materials whose distinguishing feature is that their domain size is so small that size confinement effects become a significant determinant of the materials' performance. Such confinement effects can, therefore, lead to a wide range of commercially important properties. Nanopowders, therefore, are an extraordinary opportunity for design, development, and commercialization of a wide range of devices and products for various applications. Furthermore, since they represent a whole new family of material precursors where conventional coarse-grain physiochemical mechanisms are not applicable, these materials offer unique combinations of properties that can enable novel and multifunctional components of unmatched performance. Yadav et al. in U.S. Pat. No. 6,344,271 and in co-pending and commonly assigned U.S. patent application Ser. Nos. 09/638,977, 10/004,387, 10/071,027, 10/113,315, and 10/292,263, all of which along with the references contained therein are hereby incorporated by reference in their entirety, teach some applications of sub-micron and nanoscale powders.


SUMMARY OF THE INVENTION

Briefly stated, the present invention involves methods for manufacturing nanoscale powders comprising tungsten and applications thereof.


In some embodiments, the present invention provides nanoparticles of doped or undoped tungsten oxides.


In some embodiments, the present invention provides methods for manufacturing doped or undoped metal oxides comprising tungsten.


In some embodiments, the present invention provides oxide composites and coatings that comprise doped or undoped tungsten.


In some embodiments, the present invention provides applications of powders comprising doped or undoped tungsten oxides.


In some embodiments, the present invention provides catalysts for use in a variety of applications.


In some embodiments, the present invention provides additives for use in a variety of applications.


In some embodiments, the present invention provides materials and devices for optical, sensing, thermal, biomedical, structural, superconductive, energy, and security application, as well as other applications.


In some embodiments, the present invention provides methods for producing novel nanoscale powders comprising tungsten in high volume, low-cost, and reproducible quality.





BRIEF DESCRIPTION OF THE DRAWINGS


FIG. 1 shows an exemplary overall approach for producing submicron and nanoscale powders in accordance with the present invention.





DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

This invention is generally directed to very fine powders comprising tungsten (W). The scope of the teachings includes high purity powders. Powders discussed herein are of mean crystallite size less than 1 micron, and in certain embodiments less than 100 nanometers. Methods for producing and utilizing such powders in high volume, low-cost, and reproducible quality are also outlined.


Definitions


For purposes of clarity, the following definitions are provided to aid the understanding of the description and specific examples provided herein. Whenever a range of values are provided for a specific variable, both the upper and lower limit of the range are included within the definition.


“Fine powders” as used herein, refers to powders that simultaneously satisfy the following criteria:

    • (1) particles with mean size less than 10 microns; and
    • (2) particles with aspect ratio between 1 and 1,000,000.
      • For example, in some embodiments, the fine powders are powders that have particles with a mean domain size less than 5 microns and with an aspect ratio ranging from 1 to 1,000,000.


“Submicron powders” as used herein, refers to fine powders with a mean size less than 1 micron. For example, in some embodiments, the submicron powders are powders that have particles with a mean domain size less than 500 nanometers and with an aspect ratio ranging from 1 to 1,000,000.


The terms “nanopowders,” “nanosize powders,” “nanoparticles,” and “nanoscale powders” are used interchangeably and refer to fine powders that have a mean size less than 250 nanometers. For example, in some embodiments, the nanopowders are powders that have particles with a mean domain size less than 100 nanometers and with an aspect ratio ranging from 1 to 1,000,000.


“Pure powders,” as the term is used herein, are powders that have composition purity of at least 99.9% by metal basis. For example, in some embodiments the purity is 99.99%.


“Nanomaterials,” as the term is used herein, are materials in any dimensional form that have a domain size less than 100 nanometers.


“Domain size,” as that term is used herein, refers to the minimum dimension of a particular material morphology. In the case of powders, the domain size is the grain size. In the case of whiskers and fibers, the domain size is the diameter. In the case of plates and films, the domain size is the thickness.


The terms “powder,” “particle,” and “grain” are used interchangeably and encompass oxides, carbides, nitrides, borides, chalcogenides, halides, metals, intermetallics, ceramics, polymers, alloys, and combinations thereof. These terms include single metal, multi-metal, and complex compositions. These terms further include hollow, dense, porous, semi-porous, coated, uncoated, layered, laminated, simple, complex, dendritic, inorganic, organic, elemental, non-elemental, composite, doped, undoped, spherical, non-spherical, surface functionalized, surface non-functionalized, stoichiometric, and non-stoichiometric forms or substances. Further, the term powder in its generic sense includes one-dimensional materials (fibers, tubes, etc.), two-dimensional materials (platelets, films, laminates, planar, etc.), and three-dimensional materials (spheres, cones, ovals, cylindrical, cubes, monoclinic, parallelolipids, dumbbells, hexagonal, truncated dodecahedron, irregular shaped structures, etc.).


“Aspect ratio,” as the term is used herein, refers to the ratio of the maximum to the minimum dimension of a particle.


“Precursor,” as the term is used herein, encompasses any raw substance that can be transformed into a powder of same or different composition. In certain embodiments, the precursor is a liquid. The term precursor includes, but is not limited to, organometallics, organics, inorganics, solutions, dispersions, melts, sols, gels, emulsions, or mixtures.


“Powder,” as the term is used herein, encompasses oxides, carbides, nitrides, chalcogenides, metals, alloys, and combinations thereof. The term includes hollow, dense, porous, semi-porous, coated, uncoated, layered, laminated, simple, complex, dendritic, inorganic, organic, elemental, non-elemental, dispersed, composite, doped, undoped, spherical, non-spherical, surface functionalized, surface non-functionalized, stoichiometric, and non-stoichiometric forms or substances.


“Coating” (or “film” or “laminate” or “layer”), as the term is used herein, encompasses any deposition comprising submicron and nanoscale powders. The term includes in its scope a substrate, surface, deposition, or a combination thereof that is hollow, dense, porous, semi-porous, coated, uncoated, simple, complex, dendritic, inorganic, organic, composite, doped, undoped, uniform, non-uniform, surface functionalized, surface non-functionalized, thin, thick, pretreated, post-treated, stoichiometric, or non-stoichiometric form or morphology.


“Dispersion,” as the term is used herein, encompasses inks, pastes, creams, lotions, Newtonian, non-Newtonian, uniform, non-uniform, transparent, translucent, opaque, white, black, colored, emulsified, with additives, without additives, water-based, polar solvent-based, or non-polar solvent-based mixtures of powder in any fluid or fluid-like state.


In some embodiments, the present invention is directed to submicron and nanoscale powders comprising doped or undoped tungsten oxides. Given the relative abundance of tungsten in the earth's crust and current limitations on purification technologies, it is expected that many commercially produced materials would have naturally occurring tungsten impurities. These impurities are expected to be below 100 parts per million and in most cases in concentration similar to other elemental impurities. Removal of such impurities does not materially affect the properties of interest for an application. For the purposes herein, powders comprising tungsten impurities wherein tungsten is present in a concentration similar to other elemental impurities are excluded from the scope of this invention. However, it is emphasized that in one or more doped or undoped compositions of matter, tungsten may be intentionally engineered as a dopant into a powder at concentrations of 100 ppm or less, and these are included in the scope of this invention.


In a generic sense, the invention teaches nanoscale powders, and in more generic sense, submicron powders comprising at least 100 ppm by weight, in some embodiments greater than 1 weight % by metal basis, and in other embodiments greater than 10 weight % by metal basis, of tungsten (W).


While several embodiments for manufacturing nanoscale and submicron powders comprising tungsten are disclosed, for the purposes herein, the nanoscale or submicron powders may be produced by any method or may result as a byproduct from any process.



FIG. 1 shows an exemplary overall approach for the production of submicron powders in general and nanopowders in particular. The process shown in FIG. 1 begins with a tungsten containing raw material (for example, but not limited to, coarse oxide powders, metal powders, salts, slurries, waste products, organic compounds, or inorganic compounds). FIG. 1 shows one embodiment of a system for producing nanoscale and submicron powders in accordance with the present invention.


The process shown in FIG. 1 begins at 100 with a tungsten metal-containing precursor such as an emulsion, fluid, particle-containing fluid suspension, or water-soluble salt. The precursor may be evaporated tungsten metal vapor, evaporated alloy vapor, a gas, a single-phase liquid, a multi-phase liquid, a melt, a sol, a solution, fluid mixtures, solid suspension, or combinations thereof. The metal-containing precursor comprises a stoichiometric or a non-stoichiometric metal composition with at least some part in a fluid phase. Fluid precursors are utilized in certain embodiments of this invention. Typically, fluids are easier to convey, evaporate, and thermally process resulting in a more uniform product.


In one embodiment of this invention, the precursors are environmentally benign, safe, readily available, high-metal loading, lower-cost, fluid materials. Examples of tungsten metal-containing precursors include, but are not limited to, metal acetates, metal carboxylates, metal ethanoates, metal alkoxides, metal octoates, metal chelates, metallo-organic compounds, metal halides, metal azides, metal nitrates, metal sulfates, metal hydroxides, metal salts soluble in organics or water, compounds of the metal, comprising ammonium compounds of the metal comprising sodium/potassium/lithium, and metal-containing emulsions.


In another embodiment, multiple metal precursors may be mixed if complex nano-nanoscale and submicron powders are desired. For example, a tungsten precursor and alkali (or alkaline earth) precursor may be mixed to prepare sodium tungsten oxide powders for color and for electroceramic applications. As another example, a tungsten precursor, a vanadium precursor and titanium precursor may be mixed in correct proportions to yield a high purity, high surface area, mixed oxide powder for catalyst applications. In yet another example, a barium precursor (and/or zinc precursor) and a tungsten precursor may be mixed to yield powders for pigment applications. Such complex nanoscale and submicron powders can help create materials with surprising and unusual properties not available through the respective single metal oxides or a simple nanocomposite formed by physically blending powders of different compositions.


It is desirable to use precursors of a higher purity to produce a nanoscale or submicron powder of a desired purity. For example, if a purity greater than x% (by metal weight basis) is desired, one or more precursors that are mixed and used may have purities greater than or equal to x% (by metal weight basis).


With continued reference to FIG. 1, the metal-containing precursor 100 (containing one or a mixture of metal-containing precursors) is fed into a high temperature process 106, which may be implemented using a high temperature reactor, for example. In some embodiments, a synthetic aid such as a reactive fluid 108 may be added along with the precursor 100 as it is being fed into the reactor 106. Examples of such reactive fluids include, but are not limited to, hydrogen, ammonia, halides, carbon oxides, methane, oxygen gas, and air.


While the discussion herein teaches methods of preparing nanoscale and submicron powders of oxides, the teachings may be readily extended in an analogous manner to other compositions such as carbides, nitrides, borides, carbonitrides, and chalcogenides. These compositions can be prepared from micron-sized powder precursors of these compositions or by utilizing reactive fluids that provide the elements desired in these tungsten comprising compositions. In some embodiments, high temperature processing may be used. However, a moderate temperature processing or a low/cryogenic temperature processing may also be employed to produce nanoscale and submicron powders using the methods of the present invention.


The precursor 100 may be pre-processed in a number of other ways before any thermal treatment. For example, the pH may be adjusted to ensure precursor stability. Alternatively, selective solution chemistry, such as precipitation with or without the presence of surfactants or other synthesis aids, may be employed to form a sol or other state of matter. The precursor 100 may be pre-heated or partially combusted before the thermal treatment.


The precursor 100 may be injected axially, radially, tangentially, or at any other angle into the high temperature region 106. As stated above, the precursor 100 may be pre-mixed or diffusionally mixed with other reactants. The precursor 100 may be fed into the thermal processing reactor by a laminar, parabolic, turbulent, pulsating, sheared, or cyclonic flow pattern, or by any other flow pattern. In addition, one or more metal-containing precursors 100 can be injected from one or more ports in the reactor 106. The feed spray system may yield a feed pattern that envelops the heat source or, alternatively, the heat sources may envelop the feed, or alternatively, various combinations of this may be employed. In some embodiments, the spray is atomized and sprayed in a manner that enhances heat transfer efficiency, mass transfer efficiency, momentum transfer efficiency, and reaction efficiency. The reactor shape may be cylindrical, spherical, conical, or any other shape. Methods and equipment such as those taught in U.S. Pat. Nos. 5,788,738, 5,851,507, and 5,984,997 (each of which is hereby specifically incorporated by reference in its entirety) can be employed.


With continued reference to FIG. 1, after the precursor 100 has been fed into reactor 106, it may be processed at high temperatures to form the product powder. In other embodiments, the thermal processing may be performed at lower temperatures to form the powder product. The thermal treatment may be done in a gas environment with the aim to produce products, such as powders, that have the desired porosity, density, morphology, dispersion, surface area, and composition. This step produces by-products, such as gases. To reduce costs, these gases may be recycled, mass/heat integrated, or used to prepare the pure gas stream desired by the process.


In embodiments using high temperature thermal processing, the high temperature processing may be conducted at step 106 (FIG. 1) at temperatures greater than 1500 K, in some embodiments greater than 2500 K, in some embodiments greater than 3000 K, and in some embodiments greater than 4000 K. Such temperatures may be achieved by various methods including, but not limited to, plasma processes, combustion in air, combustion in purified oxygen or oxygen rich gases, combustion with oxidants, pyrolysis, electrical arcing in an appropriate reactor, and combinations thereof. The plasma may provide reaction gases or may provide a clean source of heat.


A high temperature thermal process at 106 results in a vapor comprising the metal(s) in one or more phases. After the thermal processing, this vapor is cooled at step 110 to nucleate submicron powders, in certain embodiments nanopowders. In certain embodiments, the cooling temperature at step 110 is maintained high enough to prevent moisture condensation. The dispersed particles form because of the thermokinetic conditions in the process. By engineering the process conditions, such as pressure, residence time, supersaturation and nucleation rates, gas velocity, flow rates, species concentrations, diluent addition, degree of mixing, momentum transfer, mass transfer, and heat transfer, the morphology of the nanoscale and submicron powders can be tailored. It is important to note that the focus of the process should be on producing a powder product that excels in satisfying the end application requirements and customer needs.


In certain embodiments, the nanopowder is quenched after cooling to lower temperatures at step 116 to minimize and prevent agglomeration or grain growth. Suitable quenching methods include, but are not limited to, methods taught in U.S. Pat. No. 5,788,738. In certain embodiments, sonic to supersonic quenching may be used. In other embodiments, coolant gases, water, solvents, cold surfaces, or cryogenic fluids might be employed. In certain embodiments, quenching methods are employed which can prevent deposition of the powders on the conveying walls. Suitable methods include, but are not limited to, electrostatic means, blanketing with gases, the use of higher flow rates, mechanical means, chemical means, electrochemical means, or sonication/vibration of the walls.


In some embodiments, the high temperature processing system includes instrumentation and software that can assist in the quality control of the process. Furthermore, in certain embodiments, the high temperature processing zone 106 is operated to produce fine powders 120, in certain embodiments submicron powders, and in certain embodiments nanopowders. The gaseous products from the process may be monitored for composition, temperature, and other variables to ensure quality at step 112 (FIG. 1). The gaseous products may be recycled to be used in process 108 or used as a valuable raw material when nanoscale and submicron powders 120 have been formed, or they may be treated to remove environmental pollutants if any. Following quenching step 116, the nanoscale and submicron powders may be cooled further at step 118 and then harvested at step 120.


The product nanoscale and submicron powders 120 may be collected by any method. Suitable collection means include, but are not limited to, bag filtration, electrostatic separation, membrane filtration, cyclones, impact filtration, centrifugation, hydrocyclones, thermophoresis, magnetic separation, and combinations thereof.


The quenching at step 116 may be modified to enable preparation of coatings. In such embodiments, a substrate may be provided (in batch or continuous mode) in the path of the quenching powder containing gas flow. By engineering the substrate temperature and the powder temperature, a coating comprising the submicron powders and nanoscale powders can be formed.


In some embodiments, a coating, film, or component may also be prepared by dispersing the fine nanopowder and then applying various known methods, such as, but not limited to, electrophoretic deposition, magnetophorectic deposition, spin coating, dip coating, spraying, brushing, screen printing, ink-jet printing, toner printing, and sintering. The nanopowders may be thermally treated or reacted to enhance their electrical, optical, photonic, catalytic, thermal, magnetic, structural, electronic, emission, processing, or forming properties before such a step.


It should be noted that the intermediate or product at any stage of the process described herein, or similar process based on modifications by those skilled in the art, may be used directly as a feed precursor to produce nanoscale or fine powders by methods taught herein and other methods. Other suitable methods include, but not limited to, those taught in commonly owned U.S. Pat. Nos. 5,788,738, 5,851,507, and 5,984,997, and co-pending U.S. patent application Ser. Nos. 09/638,977 and 60/310,967 which are all incorporated herein by reference in their entirety. For example, a sol may be blended with a fuel and then utilized as the feed precursor mixture for thermal processing above 2500 K to produce nanoscale simple or complex powders.


In summary, one embodiment for manufacturing powders comprises (a) preparing a precursor comprising at least 100 ppm by weight of tungsten element; (b) feeding the precursor into a high temperature reactor operating at temperatures greater than 1500 K, in certain embodiments greater than 2500 K, in certain embodiments greater than 3000 K, and in certain embodiments greater than 4000 K; (c) wherein, in the high temperature reactor, the precursor converts into vapor comprising the rare earth metal in a process stream with a velocity above 0.25 mach in an inert or reactive atmosphere; (d) cooling the vapor to nucleate submicron or nanoscale powders; (e) quenching the powders at high gas velocities to prevent agglomeration and growth; and (f) filtering the quenched powders from the gases.


Another embodiment for manufacturing nanoscale powders comprising tungsten comprises (a) preparing a fluid precursor comprising two or more metals, at least one of which is tungsten in a concentration greater than 100 ppm by weight; (b) feeding the said precursor into a high temperature reactor operating at temperatures greater than 1500 K, in some embodiments greater than 2500 K, in some embodiments greater than 3000 K, and in some embodiments greater than 4000 K in an inert or reactive atmosphere; (c) wherein, in the said high temperature reactor, the said precursor converts into vapor comprising tungsten; (d) cooling the vapor to nucleate submicron or nanoscale powders; (e) quenching the powders at gas velocities exceeding 0.1 Mach to prevent agglomeration and growth; and (f) separating the quenched powders from the gases. In certain embodiments, the fluid precursor may include synthesis aids, such as surfactants (also known as dispersants, capping agents, emulsifying agents, etc.), to control the morphology or to optimize the process economics and/or product performance.


One embodiment for manufacturing coatings comprises (a) preparing a fluid precursor comprising one or more metals, one of which is tungsten; (b) feeding the precursor into a high temperature reactor operating at temperatures greater than 1500 K, in some embodiments greater than 2500 K, in some embodiments greater than 3000 K, and in some embodiments greater than 4000 K in an inert or reactive atmosphere; (c) wherein, in the high temperature reactor, the precursor converts into vapor comprising tungsten; (d) cooling the vapor to nucleate submicron or nanoscale powders; (e) quenching the powders onto a substrate to form a coating on the substrate comprising tungsten.


The powders produced by teachings herein may be modified by post-processing as taught by commonly owned U.S. patent application Ser. No. 10/113,315, which is hereby incorporated by reference in its entirety.


Methods for Incorporating Nanoparticles into Products

Submicron and nanoscale powders can be incorporated into a composite structure by any method. Some non-limiting exemplary methods are taught in commonly owned U.S. Pat. No. 6,228,904 which is hereby incorporated by reference in its entirety.


The submicron and nanoscale powders taught herein may be incorporated into plastics by any method. In one embodiment, the method comprises (a) preparing nanoscale or submicron powders comprising tungsten by any method, such as a method that employs fluid precursors and a peak processing temperature exceeding 1500 K; (b) providing powders of one or more plastics; (c) mixing the nanoscale or submicron powders with the powders of plastics; and (d) co-extruding the mixed powders into a desired shape at temperatures greater than the softening temperature of the powders of plastics but less than the degradation temperature of the powders of plastics. In another embodiment, a masterbatch of the plastic powder comprising nanoscale or submicron powders comprising tungsten is prepared. These masterbatches can later be processed into useful products by techniques well known to those skilled in the art. In yet another embodiment, the tungsten metal containing nanoscale or submicron powders are pretreated to coat the powder surface for ease in dispersability and to ensure homogeneity. In a further embodiment, injection molding of the mixed powders comprising nanoscale powders and plastic powders is employed to prepare useful products.


One embodiment for incorporating nanoscale or submicron powders into plastics comprises (a) preparing nanoscale or submicron powders comprising tungsten by any method, such as a method that employs fluid precursors and peak processing temperature exceeding 1500 K; (b) providing a film of one or more plastics, wherein the film may be laminated, extruded, blown, cast, or molded; and (c) coating the nanoscale or submicron powders on the film of plastic by techniques such as spin coating, dip coating, spray coating, ion beam coating, sputtering. In another embodiment, a nanostructured coating is formed directly on the film by techniques such as those taught in herein. In some embodiments, the grain size of the coating is less than 200 nm, in some embodiments less than 75 nm, and in some embodiments less than 25 nm.


Submicron and nanoscale powders can be incorporated into glass by any method. In one embodiment, nanoparticles of tungsten are incorporated into glass by (a) preparing nanoscale or submicron powders comprising tungsten by any method, such as a method that employs fluid precursors and temperature exceeding 1500 K in an inert or reactive atmosphere; (b) providing glass powder or melt; (c) mixing the nanoscale or submicron powders with the glass powder or melt; and (d) processing the glass comprising nanoparticles into articles of desired shape and size.


Submicron and nanoscale powders can be incorporated into paper by any method. In one embodiment, the method comprises (a) preparing nanoscale or submicron powders comprising tungsten; (b) providing paper pulp; (c) mixing the nanoscale or submicron powders with the paper pulp; and (d) processing the mixed powders into paper, such as by molding, couching and calendering. In another embodiment, the tungsten metal containing nanoscale or submicron powders are pretreated to coat the powder surface for ease in dispersability and to ensure homogeneity. In a further embodiment, nanoparticles are applied directly on the manufactured paper or paper-based product; the small size of nanoparticles enables them to permeate through the paper fabric or reside on the surface of the paper and thereby functionalize the paper.


The submicron and nanoscale powders taught herein may be incorporated into leather, fibers, or fabric by any method. In one embodiment, the method comprises (a) preparing nanoscale or submicron powders comprising tungsten by any method, such as a process that includes a step that operates above 1000 K; (b) providing leather, fibers, or fabric; (c) bonding the nanoscale or submicron powders with the leather, fibers, or fabric; and (d) processing the bonded leather, fibers, or fabric into a product. In yet another embodiment, the tungsten metal containing nanoscale or submicron powders are pretreated to coat or functionalize the powder surface for ease in bonding or dispersability or to ensure homogeneity. In a further embodiment, nanoparticles are applied directly on a manufactured product based on leather, fibers, or fabric; the small size of nanoparticles enables them to adhere to or permeate through the leather, fibers (polymer, wool, cotton, flax, animal-derived, agri-derived), or fabric and thereby functionalize the leather, fibers, or fabric.


Submicron and nanoscale powders can be incorporated into creams or inks by any method. In one embodiment, the method comprises (a) preparing nanoscale or submicron powders comprising tungsten by any method, such as a method that employs fluid precursors and peak processing temperatures exceeding 1500 K; (b) providing a formulation of cream or ink; and (c) mixing the nanoscale or submicron powders with the cream or ink. In yet another embodiment, the tungsten comprising nanoscale or submicron powders are pretreated to coat or functionalize the powder surface for ease in dispersability and to ensure homogeneity. In a further embodiment, pre-existing formulation of a cream or ink is mixed with nanoscale or submicron powders to functionalize the cream or ink.


Nanoparticles comprising tungsten can be difficult to disperse in water, solvents, plastics, rubber, glass, paper, etc. The dispersability of the nanoparticles can be enhanced in certain embodiments by treating the surface of the tungsten oxide powders or other tungsten comprising nanoparticles. The treatment step may lead to physical bonding in certain embodiments. In other embodiments, the treatment step may lead to chemical bonding of desirable functional groups to the surface of the nanoparticles. For example, fatty acids (e.g. propionic acid, stearic acid and oils) or organometallics comprising silicon or organometallics comprising titanium can be applied to or with the nanoparticles to enhance the surface compatibility. If the powder has an acidic surface, ammonia, quaternary salts, or ammonium salts can be applied to the surface to achieve desired surface pH. In other cases, acetic acid wash can be used to achieve the desired surface state. Trialkyl phosphates and phosphoric acid can be applied to reduce dusting and chemical activity. In yet other cases, the powder may be thermally treated to improve the dispersability of the powder.


Applications of Nanoparticles and Submicron Powders Comprising Tungsten

Pigments


Nanoparticles comprising tungsten containing multi-metal oxides offer some surprising and unusual benefits as pigments. Nanoparticles are smaller than the visible wavelengths of light which leads to visible wavelengths interacting in unusual ways with nanoparticles compared to particles with grain sizes much bigger than the visible wavelengths (400-700 nm). The small size of nanoparticles can also lead to more uniform dispersion. In certain embodiments, it is important that the nanoparticles be non-agglomerated (i.e. do not have sintered neck formation or hard agglomeration). In some embodiments, the nanoparticles have non-functionalized, i.e. clean surface; in other embodiments, the surface is modified or functionalized to enable bonding with the matrix in which they need to be dispersed.


One of the outstanding process challenges for manufacturing inorganic pigments is the ability to ensure homogeneous lattice level mixing of elements in a complex multi-metal formulation. One of the features of the process described herein is its ability to prepare complex compositions with the necessary homogeneity. Therefore, the teachings herein are ideally suited for creating color and making superior performing pigments with nanoparticles comprising tungsten.


Some non-limiting illustrations of pigments containing tungsten are barium tungsten oxide, zinc tungsten oxide, calcium tungsten oxide, tin doped tungsten oxide, tungsten bronzes, phosphotungstomolybdic acid, and non-stoichiometric substances comprising tungsten.


In one embodiment, a method for manufacturing a pigmented product comprises (a) preparing nanoscale or submicron powders comprising tungsten; (b) providing powders of one or more plastics; (c) mixing the nanoscale or submicron powders with the powders of plastics; and (d) processing the mixed powders into the product. In yet another embodiment, the tungsten containing nanoscale or submicron powders are pretreated to coat the powder surface for ease in dispersability and to ensure homogeneity. In a further embodiment, extrusion or injection molding of the mixed powders comprising nanoscale powders and plastic powders can be employed to prepare useful products.


Additives


Nanoscale tungsten comprising substances are useful lubricating additives. A non-limiting illustration is tungsten disulfide nanoparticles. The small size of tungsten disulfide nanoparticles enables thinner films in certain embodiments offering reduced costs at higher performance. Such lubricating nanoparticles, in certain better embodiments, offer ability to distribute forces more uniformly. In certain embodiments such as high precision, tight gap moving surfaces, lubricating additives may be added to the lubricating fluid or oils to improve the life or motor or engine. The unusual characteristic that makes lubricating nanoparticle additives useful is that the particle size enables by nanotechnology can be less than the naturally occurring characteristic roughness sizes. The nanoparticles can enter and buffer (or reside) in crevices, troughs thereby reducing the damaging internal pressures, forces and inefficient thermal effects. These additives can be dispersed in existing or novel lubricating formulations and thereby provide an easy way to incorporate the benefits of nanotechnology. Tungsten disulfide, molybdenum disulfide, molybdenum tungsten sulfide and such inorganic or organic nanoparticle composition are useful lubricating additives elsewhere as well, e.g. shaving blades and any surface that requires minimization of the adverse effects of friction.


Biochemical Analytical Agent


Sodium tungsten oxide nanoparticles, in high purity form in certain embodiments, are useful in biochemical analysis. The high surface area of nanoparticles comprising tungsten, particularly when the mean particle size is less than 100 nanometers, make them useful in these applications.


Sulfur and Carbon Accelerating Analytical Agent


Tungsten nanoparticles, in metallic form in certain embodiments, are useful in the analysis of carbon and sulfur by combustion in an induction furnace. The high surface area and surface activity of nanoparticles comprising tungsten, particularly when the mean particle size is less than 100 nanometers, make them useful in these applications.


Electrical & Lighting Applications


Nanomaterials comprising tungsten offer several unusual benefits as electron emitters. These benefits are a consequence of (a) the small size of nanoparticles which can enable very thin film devices, (b) high surface area, which can lower the sintering temperatures and sintering times, (c) inherently low vapor pressure of tungsten metal even at high temperatures and (d) unusual quantum confinement and grain boundary effects. These properties can be used to prepare improved electron emitting devices and electrical contacts. Photocopiers, facsimile machines, laser printers and air cleaners can benefit from charger wires prepared from tungsten comprising nanomaterials. Other nanodevices that can be prepared from nanoscale powders comprising tungsten include electrodes, chemical sensors, biomedical sensors, phosphors, and anti-static coatings. Tungsten comprising nanomaterials also offer novel compositions for chemical mechanical polishing applications.


For reasons described above, nanomaterials comprising tungsten are in certain embodiments particularly useful at direct heated cathode or heater coils for indirectly heated cathodes in cathode ray tubes, displays, x-ray tubes, klystrons, magnetrons for microwave ovens and electron tubes. Multimetal nanomaterial compositions comprising tungsten include those based on rare earths and thoria for high intensity discharge lamps and welding electrodes. X-ray device anodes can also benefit from the low vapor pressure and thermal conductivity of tungsten comprising nanomaterials.


The unusual combination of vapor pressure, electrical conductivity and electronic properties make nanomaterial compositions comprising tungsten useful as substrate for high power semiconductor rectifying devices, high voltage breakers (e.g. W—Cu, W—Ag contacts). In other embodiments, various forms of infiltrated tungsten comprising nanocomposites are useful for these applications. High temperature furnace parts such as heating coils, reflectors, thermocouples can also benefit from the quantum confined and low vapor pressure characteristics of nanomaterials comprising tungsten.


Nanomaterials comprising tungsten are useful for lighting applications (incandescent lamps) because of the same unusual combination of properties discussed above. Illustrative applications include household lamps, automotive lamps, and reflector lamps for floodlight or projector applications. Specialty lamps can also benefit from the nanotechnology taught herein in applications such as, but not limited to, audio-visual projectors, fiber-optical systems, video camera lights, airport runway markers, photoprinters, medical and scientific instruments, and stage or studio systems. In certain embodiments of lighting product and applications, alloys and dispersion strengthened forms of tungsten comprising materials are useful.


Electronics Applications


Nanomaterials comprising tungsten are useful in certain embodiments as phosphors and electronic materials. These benefits are a consequence of (a) the small size of nanoparticles which can enable very thin film devices, (b) high surface area which can lower the sintering temperatures and sintering times, (c) inherently low vapor pressure of tungsten metal even at high temperatures, (d) significant thermal and electrical conductivity, and (e) unusual quantum confinement and grain boundary effects. These properties can be used to prepare improved phosphors for x-rays (e.g. calcium tungsten oxide, magnesium tungsten oxide). Improved and more cost effective heat removal components comprising of tungsten and copper based heat sinks can be prepared from nanomaterials. Tungsten comprising nanomaterials inks (water, solvent or UV curable), adhesives and pastes can be useful in developing electrodes and conductors for ceramic circuit board and other applications.


For silicon based semiconductor devices, tungsten nanomaterials offer a close thermal coefficient of expansion. In combination with other useful properties mentioned above, tungsten and complex compositions comprising tungsten offer materials that can help achieve a thermal coefficient of expansion similar to compositions comprising silicon and metals used in microelectronics. These properties can be used to prepare improved microelectronic components. Tungsten comprising nanomaterials inks and pastes can be useful in preparing improved DRAM chips, other silicon devices, and liquid crystal display products.


Any method can be employed to utilize nanoparticles comprising tungsten in electronic devices taught herein. In one embodiment, a method for employing nanoparticles comprising tungsten in miniature batteries comprises (a) preparing nanoscale or submicron powders comprising tungsten; (b) preparing an ink (water based, solvent based or UV curable monomer based ink) or adhesive or paste from the powders; and (c) utilizing the ink or adhesive or paste to prepare an electronic device.


Catalysts


Tungsten containing nanoparticles such as oxides, sulfides and heteropoly complexes are useful catalysts for a number of chemical reactions. For example, they can be used in hydration, dehydration, hydroxylation, and epoxidation reactions as catalysts or promoters. In one embodiment, a method for producing catalysts or promoters comprises (a) preparing nanoscale powders comprising tungsten such that the surface area of the said powder is greater than 25 square meters per gram, in some embodiments greater than 75 square meters per gram, and in some embodiments greater than 150 square meters per gram; and (b) reducing the powder in a reducing environment (or activating the powder in any other way) and then conducting a chemical reaction in the presence of the nanoscale powders comprising doped or undoped tungsten compound. In some embodiments, a further step of dispersing the nanoscale powders in a solvent and then depositing these powders onto a substrate from the dispersion may be employed before chemical reaction is conducted.


The catalyst powders described above can be combined with zeolites and other well-defined porous materials to enhance the selectivity and yields of useful chemical reactions.


Optics and Phosphors


Non-stoichiometric nanoparticles comprising tungsten offer several unusual benefits as phosphors and for detector applications. These benefits are a consequence of one or more of the following characteristics (a) small size, (b) high surface area, (c) dispersability in various media, inks, and solid matrices, (e) unusual and complex combinations of density, vapor pressures, work functions, and band gaps. The advantages of phosphors and detectors comprising tungsten-containing nanoparticles are (a) high dots per inch density, (b) ability to form homogeneous products, and (c) the ability to prepare very thin films thereby reducing the raw material required for same or superior performance. Nanoparticles can also be post-processed (calcination, sintering) to grow the grain to the optimal size in order to provide the brightness level, decay time and other characteristics desired.


Multi-metal compositions (two, three, four, or more metals) comprising tungsten are used in certain embodiments. A specific illustration of fluorescent composition is calcium tungstate. These phosphor nanopowders can be used for scintillation counters, display applications, lamps, fluorescent bulbs, light emitting devices, markers, security pigments, fabric pigments, luminous paints, toys, special effects, etc.


Tungsten comprising nanoparticles are useful in forming thin films comprising tungsten that lose oxygen in bright light thereby becoming bluish and filtering light; these films reoxidize in darkness thereby becoming clear. One of the many useful properties of nanomaterials comprising tungsten is the ability of tungsten to lose oxygen easily (e.g. WO3—W20O58 transition).


Interstitial Compounds


Interstitial compounds comprising tungsten (e.g. carbide, nitrides, borides, silicides) offer several unusual benefits in hard, refractory applications. These benefits are a consequence of one or more of the following characteristics (a) size, (b) hardness, (c) size confinement, (e) unusual and complex combinations of density, vapor pressures, and physical properties. Nanoparticles can also be post-processed (calcination, sintering) to grow the grain to the optimal size in order to provide other characteristics as desired. Interstitial nanomaterial compositions comprising tungsten (and other metal(s)) are useful in cutting tools, structural elements of kilns, turbines, engines, sandblast nozzles, protective coatings and the like.


Reagent and Raw Material for Synthesis


Nanoparticles comprising tungsten such as tungsten oxide and tungsten containing multi-metal oxide nanoparticles are useful reagents and precursors to prepare other compositions of nanoparticles comprising tungsten. In a generic sense, nanoparticles comprising tungsten are reacted with another substance, i.e., reagent, such as, but not limited to, an acid, alkali, organic, monomer, ammonia, reducing fluids, oxidizing fluids, halogens, phosphorus compounds, chalcogenides, biological materials, gas, vapor or solvent; the high surface area of nanoparticles facilitates the reaction and the product resulting from this reaction is also nanoparticles. The reagent can take any suitable form and can comprise nitrogen, a halogen, hydrogen, carbon, or oxygen.


These product nanoparticles can then be suitably applied or utilized to catalyze or as reagents to prepare other fine chemicals for a wide range of applications. A few non-limiting illustrations utilizing tungsten comprising nanoparticles follow. These teachings can be extended to multi-metal oxides and to other compositions such as tungsten interstitial compounds and organometallics based on tungsten. In certain embodiments, the nanoparticles may be treated or functionalized or activated under various temperatures, pressure, charge or environment composition before use.


Tungsten: Tungsten oxide nanoparticles are reacted with carbon or reacted with hydrogen comprising reducing gases at temperatures above 450° C. to produce nanoparticles of tungsten. In certain embodiments, lower temperatures may be used. If other embodiments, heating the nanocrystals in a vacuum or ambient pressures or higher pressures at temperatures such as 800 K, 1200 K, etc. may be used. Tungsten metal nanoparticles are useful in many applications (such as forming tungsten metal wire for filaments, etc.) and as a precursor for forming other compositions of matter comprising tungsten.


An embodiment for producing nanoparticles comprising tungsten comprises (a) preparing nanoscale powders comprising tungsten oxide (b) reacting the nanoscale powders with a reducing compound or environment; and (c) collecting resultant nanoparticles comprising tungsten. The higher surface area of tungsten comprising nanomaterials enables surprisingly lower temperatures and times for the conversion. In certain embodiments, the processing temperatures and times are lowered by at least 10%. In certain embodiments, the processing temperatures and times are lowered by at least 30%. In certain embodiments, the processing temperatures and times are lowered by at least 50%. In certain embodiments, the processing temperatures and times are lowered by at least 70%.


Tungsten Halides: Tungsten comprising nanoparticles are reacted with a halogen comprising compound to form tungsten halide comprising compounds. To illustrate, but not limit, tungsten nanoparticles are chlorinated to prepare WCl6 bluish black crystalline solid nanoparticles. The chlorination is performed above 400° C. and 100-1000 Torr in one embodiment (other combinations of T and P may be used in other embodiments). In certain embodiments, volume expansion with phase transformation is taken care by providing excess volume. By addition of oxygen or moisture during chlorination, oxychlorides of tungsten may be formed. Tungsten fluoride is prepared in one embodiment by reacting fluorine with tungsten nanoparticles. Tungsten bromide, WBr6, is formed in certain embodiments by exchange reactions such as those between BBr3 with WCl6 nanoparticles. In another embodiment, WBr5 is formed by reacting bromine vapor with tungsten nanoparticles above 350° C. Oxyfluorides (e.g. WOF4), which are extremely hygroscopic, can be formed by reacting oxygen-fluorine mixtures with tungsten metal nanoparticles. In other embodiments, mixing tungsten, tungsten oxide and excess iodine followed by reaction above 300° C. yields tungsten oxydiiodide (WO2I2).


Tungsten suboxides: Tungsten oxide (WO3 yellow) nanoparticles can be reacted with reducing compounds such as hydrogen to produce nanoparticles of tungsten suboxides (e.g. WO1.63-2.99). The suboxides possess different colors than the stoichiometric trioxide form (e.g. green yellow, blue, brown). Further reductions yield W3O, which is grayish and offers properties of both an oxide and those of a metallic compound.


Tungsten bronzes: Tungsten bronze nanoparticles can be represented by the generic formula M1-xWO3. The M in this generic formula can be an alkali metal (Na, K, Cs) or any other metal. The x in the generic formula can be zero or any number greater than zero and less than one. Tungsten bronze nanoparticles can be prepared by reacting tungsten oxide nanoparticles with any compound of M. In some embodiments, this is an oxide of metal M, a hydroxide of M, or metal M. In other embodiments, other compositions can be employed. The reaction may be assisted by high temperatures, vacuum, high pressures, gas environment, such as hydrogen or carbon comprising species or oxygen or inert. Other methods for preparing tungsten bronze nanoparticles include electrolytic reduction, fusion, solid state reactions, co-condensation, vapor phase deposition, sputtering and the like. In some embodiments, nanoparticles of various constituents are used to enable cost effective manufacturing with uniform properties.


Tungsten bronze nanoparticles offer unusual properties. To illustrate, but not limit, sodium tungsten bronzes offer positive temperature coefficient of resistance when x>xc, and negative temperature coefficient of resistance when x<xc. The xc depends on the particle size, oxygen deficiency and other nanoparticle characteristics. For example, xc is 0.3 in certain embodiments and 0.6 in other embodiments and may be another number in other embodiments. Nanoparticles comprising sodium tungsten bronzes offer intense color with metallic sheen depending on the value of x in Na1-xWO3. These and other nanoparticles comprising tungsten can be combined with mica or other platelets to provide special effect pigments. Nanoparticles of tungsten bronzes are also useful as catalysts for oxidation reactions and fuel cell applications.


Mixed metal tungsten compounds: Tungsten metal nanoparticles or tungsten oxide nanoparticles can be reacted with other nanoparticles comprising metal to produce nanoparticles of mixed metal compounds comprising tungsten. Examples of such compounds include but are not limited to, BaWO4, CdWO4, CaWO4, SrWO4, PbWO4, Na2WO4, Ce2(WO4)3, etc. Alternatively, as discussed previously, mixed metal compositions such as these tungstates can also be directly prepared from precursors. Tungstate nanoparticles are useful materials for optical, electronic, catalyst, pigment, and other applications. Ceramics, corrosion resistance, and fire inhibition formulations can also benefit from the unusual surface activity, small size, and other properties of tungstate nanomaterials.


Polytungstate compounds: Tungstates, as discussed above, show unusual polytungstate nanocluster forming characteristics when certain formulation conditions, such as pH, are varied. Metatungstate, paratungstate, heteropolyanions, isopolyanions, etc. can be prepared by adjusting pH, mixing in organic acids, monomers and the like. Heteropolytungstate nanoparticles such as those comprising K, Co, P, Ce, rare earths and large cations are useful as catalysts, passivation of metals and alloys, and as precipitants for colored lakes, toners and dye manufacturing.


EXAMPLES 1-2
Tungsten Oxide Powders

Ammonium tungstate precursor was dissolved in a 50:50 water and isopropyl alcohol mix. This mix was sprayed into a DC thermal plasma reactor described herein at a rate of about 100 ml/min using about 150 standard liters per minute oxygen. The peak temperature in the thermal plasma reactor was above 3000 K. The vapor was cooled to nucleate nanoparticles and then quenched by Joule-Thompson expansion. The powders collected were analyzed using X-ray diffraction (Warren-Averbach analysis) and BET. It was discovered that the powders had a crystallite size of less than 100 nm and a specific surface area greater than 10 m2/gm. It was also found that the nanopowders were readily dispersible in water, polar solvents, non-polar solvents and UV curable monomers confirming that inks can be readily prepared with these nanoscale powders.


Next, in a separate run with the same process, the mix was sprayed at a rate of about 75 ml/min using about 150 standard liters per minute oxygen. The peak temperature in the thermal plasma reactor was above 3000 K. The vapor was cooled and then quenched by Joule-Thompson expansion. The powders collected were analyzed using X-ray diffraction (Warren-Averbach analysis) and BET. It was discovered that the powders had a crystallite size less than 75 nm and a specific surface area of greater than 15 m2/gm.


These examples show that nanoparticles comprising tungsten can be prepared and that the characteristics of tungsten oxide powder can be varied with process variations.


EXAMPLE 3
Tungsten Tin Oxide Powders

A mixture comprising ammonium metatungsate and tin organometallic compound were processed in a thermal quench reactor with a peak temperature above 2000 K. The vapor was cooled and then quenched by Joule-Thompson expansion. It was discovered that the powders had an average crystallite size of less than 40 nm. The color of the powder was observed to be a beautiful blue. This example shows that the thermal plasma process can be used to create blue color nanopigments.


Other embodiments of the invention will be apparent to those skilled in the art from a consideration of the specification or practice of the invention disclosed herein. It is intended that the specification and examples be considered as exemplary only, with the true scope and spirit of the invention being indicated by the following claims.

Claims
  • 1. A nanomaterial composition of matter comprising (a) non-stoichiometric nanoparticles of tungsten oxide, and(b) at least one metal other than tungsten, wherein the composition comprises a tungsten bronze.
  • 2. The nanomaterial composition of matter of claim 1, wherein the at least one metal other than tungsten is sodium.
  • 3. The nanomaterial composition of matter of claim 1, wherein the at least one metal other than tungsten is selected from barium, zinc, calcium, tin, and combinations thereof.
  • 4. The nanomaterial composition of matter of claim 1, further comprising oxygen.
  • 5. The nanomaterial composition of matter of claim 1, wherein the nanomaterial composition comprises non-agglomerated nanoparticles.
  • 6. The nanomaterial composition of matter of claim 1, wherein the nanomaterial composition comprises nanoparticles having non-functionalized surfaces.
  • 7. The nanomaterial composition of matter of claim 1, wherein the nanomaterial composition comprises nanoparticles having functionalized or modified surfaces.
  • 8. The nanomaterial composition of matter of claim 7, wherein the functionalized surfaces comprise fatty acids, propionic acid, stearic acid, oils and combinations thereof.
  • 9. The nanomaterial composition of matter of claim 7, wherein the functionalized surfaces comprise organometallics comprising silicon or titanium.
  • 10. The nanomaterial composition of matter of claim 1, wherein the nanomaterial composition comprises particles having a mean particle size of less than 100 nanometers.
  • 11. A nanomaterial composition of matter comprising (a) non-stoichiometric nanoparticles of tungsten oxide, and(b) at least one metal other than tungsten, wherein the at least one metal other than tungsten is sodium.
CROSS-REFERENCE TO RELATED PATENT APPLICATIONS

This application is a continuation-in-part of U.S. patent application Ser. No. 10/679,611, filed Oct. 6, 2003, which is hereby incorporated by reference in its entirety. This application is also a continuation-in-part of U.S. patent application Ser. No. 10/315,272, filed Dec. 10, 2002, now U.S. Pat. No. 7,547,431, which is hereby incorporated by reference in its entirety. The present application claims the benefit of provisional application under 60/569,689, filed May 10, 2004, which application is hereby incorporated by reference in its entirety.

US Referenced Citations (286)
Number Name Date Kind
2952575 Baltzer Sep 1960 A
3531413 Rosensweig Sep 1970 A
3565676 Holzl Feb 1971 A
3635819 Kaiser Jan 1972 A
3700575 Paine Oct 1972 A
3734790 Kirshenbaum May 1973 A
3764540 Khalafalla et al. Oct 1973 A
3806449 Kaiser Apr 1974 A
3905109 Cohen et al. Sep 1975 A
3917538 Rosensweig Nov 1975 A
3981844 Romankiw Sep 1976 A
4017820 Ross Apr 1977 A
4019994 Kelley Apr 1977 A
4094804 Shimoiizaka Jun 1978 A
4208294 Khalafalla et al. Jun 1980 A
4234437 Friberg et al. Nov 1980 A
4252678 Smith Feb 1981 A
4280918 Homola et al. Jul 1981 A
4292029 Craig et al. Sep 1981 A
4315827 Bottenberg et al. Feb 1982 A
4329241 Massart May 1982 A
4356098 Chagnon Oct 1982 A
4381244 Berkowitz et al. Apr 1983 A
4381922 Frey et al. May 1983 A
4416721 Deregibus Nov 1983 A
4426356 Nair Jan 1984 A
4430239 Wyman Feb 1984 A
4453199 Ritchic et al. Jun 1984 A
4484943 Miura et al. Nov 1984 A
4485085 David et al. Nov 1984 A
4534917 Walz Aug 1985 A
4584244 Fenton Apr 1986 A
4588575 David May 1986 A
4609608 Solc Sep 1986 A
4610857 Ogawa et al. Sep 1986 A
4619845 Ayers et al. Oct 1986 A
4631952 Donaghey Dec 1986 A
4642207 Uda et al. Feb 1987 A
4701218 Barker et al. Oct 1987 A
4721610 Yoshida et al. Jan 1988 A
4760296 Johnson et al. Jul 1988 A
4842832 Inoue et al. Jun 1989 A
4851262 McFeaters Jul 1989 A
4857492 Bradley et al. Aug 1989 A
4944985 Alexander et al. Jul 1990 A
4984446 Yagawara et al. Jan 1991 A
4988539 Breuil et al. Jan 1991 A
5011627 Lutz et al. Apr 1991 A
5030669 Hendrickson et al. Jul 1991 A
5093286 Nogami et al. Mar 1992 A
5106796 Drozdyk et al. Apr 1992 A
5127951 Imasato et al. Jul 1992 A
5128081 Siegel et al. Jul 1992 A
5130210 Iwasaki et al. Jul 1992 A
5130277 Ueda et al. Jul 1992 A
5134039 Alexander et al. Jul 1992 A
5147448 Roberts et al. Sep 1992 A
5149381 Grewe et al. Sep 1992 A
5149596 Smith et al. Sep 1992 A
5165992 Yajima Nov 1992 A
5180394 Davidson Jan 1993 A
5180650 Sacripante et al. Jan 1993 A
5187209 Hirai et al. Feb 1993 A
5190583 Menzel et al. Mar 1993 A
5194128 Beaty et al. Mar 1993 A
5215580 Elfenthal et al. Jun 1993 A
5252949 Kirby et al. Oct 1993 A
5258338 Maher Nov 1993 A
5264157 Bidan et al. Nov 1993 A
5308804 Lee May 1994 A
5334292 Rajeshwar et al. Aug 1994 A
5338430 Parsonage et al. Aug 1994 A
5350641 Mogensen et al. Sep 1994 A
5355764 Marinos et al. Oct 1994 A
5356120 König et al. Oct 1994 A
5356842 Yamakawa et al. Oct 1994 A
5368951 Shiratori et al. Nov 1994 A
5381664 Bennett et al. Jan 1995 A
5385776 Maxfield et al. Jan 1995 A
5387462 Debe Feb 1995 A
5403375 König et al. Apr 1995 A
5407458 König et al. Apr 1995 A
5414588 Barbee, Jr. et al. May 1995 A
5417956 Moser May 1995 A
5420083 Brandt May 1995 A
5420227 Pfeil et al. May 1995 A
5427672 Böcker et al. Jun 1995 A
5433906 Dasch et al. Jul 1995 A
5447708 Helble et al. Sep 1995 A
5460830 Kossovsky et al. Oct 1995 A
5462751 Kossovsky et al. Oct 1995 A
5462903 Rousset et al. Oct 1995 A
5466575 Cozzette et al. Nov 1995 A
5466587 Fitzpatrick-McElligott et al. Nov 1995 A
5466652 Paparizos et al. Nov 1995 A
5468358 Ohkawa et al. Nov 1995 A
5472477 König Dec 1995 A
5476003 Neumann Dec 1995 A
5482656 Hiraoka et al. Jan 1996 A
5486277 Barbee, Jr. et al. Jan 1996 A
5486435 Brochu et al. Jan 1996 A
5486675 Taylor et al. Jan 1996 A
5489449 Umeya et al. Feb 1996 A
5503081 Lindblom et al. Apr 1996 A
5507965 Padoy et al. Apr 1996 A
5514734 Maxfield et al. May 1996 A
5518810 Nishihara et al. May 1996 A
5527849 Roman et al. Jun 1996 A
5539965 Safari et al. Jul 1996 A
5548000 Nagel et al. Aug 1996 A
5548474 Chen et al. Aug 1996 A
5549700 Graham et al. Aug 1996 A
5554670 Giannelis et al. Sep 1996 A
5560960 Singh et al. Oct 1996 A
5569561 Exnar et al. Oct 1996 A
5571401 Lewis et al. Nov 1996 A
5571612 Motohiro et al. Nov 1996 A
5590387 Schmidt et al. Dec 1996 A
5593939 Saito et al. Jan 1997 A
5614011 Binder et al. Mar 1997 A
5618475 Johnson et al. Apr 1997 A
5624718 Dearney Apr 1997 A
5629075 Ishikawa et al. May 1997 A
5629474 Williams May 1997 A
5635654 Hebsur et al. Jun 1997 A
5650156 Grinstaff et al. Jul 1997 A
5665277 Johnson et al. Sep 1997 A
5665807 Roman et al. Sep 1997 A
5679471 Cheng et al. Oct 1997 A
5681575 Burrell et al. Oct 1997 A
5688417 Cadre et al. Nov 1997 A
5690706 Sigalas et al. Nov 1997 A
5709786 Friese et al. Jan 1998 A
5714536 Ziolo et al. Feb 1998 A
5718047 Nakayama et al. Feb 1998 A
5720805 Wellinghoff et al. Feb 1998 A
5726247 Michalczyk et al. Mar 1998 A
5739193 Walpita et al. Apr 1998 A
5764004 Rabinowitz Jun 1998 A
5770022 Chang et al. Jun 1998 A
5770126 Singh et al. Jun 1998 A
5788738 Pirzada Aug 1998 A
5800866 Myers et al. Sep 1998 A
5840387 Berlowitz-Tarrant et al. Nov 1998 A
5851507 Pirzada Dec 1998 A
5858080 Bugnon Jan 1999 A
5874134 Rao et al. Feb 1999 A
5876683 Glumac et al. Mar 1999 A
5880197 Beall et al. Mar 1999 A
5891986 Yamaguchi et al. Apr 1999 A
5897945 Lieber et al. Apr 1999 A
5905000 Yadav et al. May 1999 A
5922537 Ewart et al. Jul 1999 A
5935461 Witherspoon et al. Aug 1999 A
5939146 Lavernia Aug 1999 A
5952040 Yadav et al. Sep 1999 A
5981415 Waku et al. Nov 1999 A
5984997 Bickmore Nov 1999 A
5989648 Phillips Nov 1999 A
6020419 Bock et al. Feb 2000 A
6027742 Lee et al. Feb 2000 A
6036774 Lieber et al. Mar 2000 A
6042900 Rakhimov et al. Mar 2000 A
6045925 Klabunde et al. Apr 2000 A
6057637 Zettl et al. May 2000 A
6065476 Agrawal et al. May 2000 A
6080232 Sperlich et al. Jun 2000 A
6109095 Addiego Aug 2000 A
6110266 Gonzales-Blanco et al. Aug 2000 A
6110399 McArdle et al. Aug 2000 A
6110557 Weir et al. Aug 2000 A
6114038 Castro et al. Sep 2000 A
6117541 Frisk Sep 2000 A
6127450 Angeletakis Oct 2000 A
6132563 Frach et al. Oct 2000 A
6132905 Kumar et al. Oct 2000 A
6139618 Hayashi et al. Oct 2000 A
6143356 Jablonski Nov 2000 A
6162532 Black et al. Dec 2000 A
6165247 Kodas et al. Dec 2000 A
6170292 Boulos et al. Jan 2001 B1
6180389 Douglas et al. Jan 2001 B1
6194481 Furman et al. Feb 2001 B1
6214368 Lee et al. Apr 2001 B1
6228904 Yadav May 2001 B1
6258417 Goswami et al. Jul 2001 B1
6258974 Wellinghoff et al. Jul 2001 B1
6261484 Phillips et al. Jul 2001 B1
6268054 Costantino et al. Jul 2001 B1
6268222 Chandler et al. Jul 2001 B1
6270347 Webster et al. Aug 2001 B1
6291070 Arpac et al. Sep 2001 B1
6294009 Letschert et al. Sep 2001 B1
6299937 Richart Oct 2001 B1
6300640 Bhargava et al. Oct 2001 B1
6306610 Bawendi et al. Oct 2001 B1
6312831 Crawley et al. Nov 2001 B1
6326144 Bawendi et al. Dec 2001 B1
6328798 Bostrom et al. Dec 2001 B1
6331312 Lee et al. Dec 2001 B1
6344271 Yadav Feb 2002 B1
6361161 Anstadt et al. Mar 2002 B1
6375864 Phillips et al. Apr 2002 B1
6387519 Anderson et al. May 2002 B1
6387981 Zhang et al. May 2002 B1
6399037 Pflug et al. Jun 2002 B1
6410765 Wellinghoff et al. Jun 2002 B1
6413638 Mager et al. Jul 2002 B1
6416818 Aikens et al. Jul 2002 B1
6416868 Sullivan et al. Jul 2002 B1
6417127 Yamamoto et al. Jul 2002 B1
6419989 Betz et al. Jul 2002 B1
6432526 Arney et al. Aug 2002 B1
6432866 Tennent et al. Aug 2002 B1
6436317 Malozemoff et al. Aug 2002 B1
6440243 Tan et al. Aug 2002 B1
6440561 Hayashi et al. Aug 2002 B2
6447806 Gassmann et al. Sep 2002 B1
6447848 Chow et al. Sep 2002 B1
6467897 Wu et al. Oct 2002 B1
6468497 Khan et al. Oct 2002 B1
6468808 Nie et al. Oct 2002 B1
6479156 Schmidt et al. Nov 2002 B1
6485557 Swiler Nov 2002 B1
6497729 Moussy et al. Dec 2002 B1
6498208 Border et al. Dec 2002 B2
6503316 Sakoske et al. Jan 2003 B1
6503475 McCormick et al. Jan 2003 B1
6528029 Dettling et al. Mar 2003 B1
6541112 Swiler Apr 2003 B1
6548171 Barbera-Guillem et al. Apr 2003 B1
6569397 Yadav May 2003 B1
6572672 Yadav et al. Jun 2003 B2
6572693 Wu et al. Jun 2003 B1
6589312 Snow et al. Jul 2003 B1
6600127 Peterson et al. Jul 2003 B1
6602595 Yadav et al. Aug 2003 B2
6616968 Bostrom et al. Sep 2003 B2
6623557 Hayashi et al. Sep 2003 B2
6652967 Yadav Nov 2003 B2
6653356 Sherman Nov 2003 B2
6663948 Takiyama et al. Dec 2003 B1
6667360 Ng et al. Dec 2003 B1
6680279 Cai et al. Jan 2004 B2
6682872 Sachdev et al. Jan 2004 B2
6689192 Phillips et al. Feb 2004 B1
6689823 Bellare et al. Feb 2004 B1
6693143 Pflug Feb 2004 B2
6716525 Yadav et al. Apr 2004 B1
6719821 Yadav Apr 2004 B2
6726992 Yadav et al. Apr 2004 B1
6746791 Yadav et al. Jun 2004 B2
6800127 Babler Oct 2004 B2
6830710 Bennett et al. Dec 2004 B2
6830822 Yadav Dec 2004 B2
6832735 Yadav Dec 2004 B2
6849109 Yadav et al. Feb 2005 B2
6855426 Yadav Feb 2005 B2
6855749 Yadav et al. Feb 2005 B1
6916872 Yadav et al. Jul 2005 B2
6933331 Yadav et al. Aug 2005 B2
20010038803 Morales et al. Nov 2001 A1
20020018854 McCarthy et al. Feb 2002 A1
20020033131 Bostrom et al. Mar 2002 A1
20020100164 Tanaka et al. Aug 2002 A1
20020149656 Nohr et al. Oct 2002 A1
20030017336 Gedanken et al. Jan 2003 A1
20030035955 Yadav Feb 2003 A1
20030102099 Yadav et al. Jun 2003 A1
20030122114 Dobler et al. Jul 2003 A1
20030124043 Yadav Jul 2003 A1
20030124050 Yadav et al. Jul 2003 A1
20030132420 Yadav Jul 2003 A1
20030199624 Yadav et al. Oct 2003 A1
20030207112 Yadav Nov 2003 A1
20030207977 Yadav et al. Nov 2003 A1
20030207978 Yadav et al. Nov 2003 A1
20030209057 Yadav et al. Nov 2003 A1
20030224214 Garito et al. Dec 2003 A1
20040021133 Nagpal et al. Feb 2004 A1
20040127987 Evans et al. Jul 2004 A1
20040139820 Kodas et al. Jul 2004 A1
20040139888 Yadav Jul 2004 A1
20040178530 Yadav et al. Sep 2004 A1
20040180203 Yadav et al. Sep 2004 A1
20040233526 Kaminsky et al. Nov 2004 A1
Foreign Referenced Citations (22)
Number Date Country
4238688 May 1994 DE
0 004 859 Oct 1979 EP
0 084 769 Aug 1983 EP
0 550 874 Jul 1993 EP
0 736 885 Oct 1996 EP
0 810 259 Dec 1997 EP
1215041 Dec 2001 EP
2 722 492 Jan 1996 FR
60-196659 May 1985 JP
102110 Apr 1990 JP
08261979 Nov 1996 JP
102110 Jun 1998 JP
1654258 Jun 1991 RU
WO 9106036 May 1991 WO
WO 9401143 Jan 1994 WO
WO 9500609 Jan 1995 WO
WO 9501643 Jan 1995 WO
WO 9629711 Sep 1996 WO
WO 9715935 May 1997 WO
WO 9716479 May 1997 WO
WO 9724297 Jul 1997 WO
WO 0066485 Sep 2000 WO
Related Publications (1)
Number Date Country
20050271566 A1 Dec 2005 US
Provisional Applications (1)
Number Date Country
60569689 May 2004 US
Continuation in Parts (2)
Number Date Country
Parent 10679611 Oct 2003 US
Child 11125316 US
Parent 10315272 Dec 2002 US
Child 10679611 US