Patent Application
20150270037
1. Field of the Invention
The present invention relates to a voltage nonlinear resistive element and a method for manufacturing the voltage nonlinear resistive element.
2. Description of the Related Art
Voltage nonlinear resistive elements (varistors) are elements having a structure in which a voltage nonlinear resistor is disposed between a pair of electrodes, and are widely used as elements for protecting electronic circuits from abnormal voltage in various sensors, such as humidity sensors and temperature sensors. Patent Literature 1 discloses a voltage nonlinear resistive element of this type in which a resistor is disposed between a pair of electrodes, wherein the resistor has a structure in which a zinc oxide ceramic layer is joined to a metal oxide layer represented by M1-xAxBO3 (M: rare-earth element, A: at least one of Sr and Ba, B: at least one of Mn and Co, x≦0.4). The resistor is produced by joining a green zinc oxide ceramic and a green metal oxide and sintering them as one body at a temperature in the range of 1200° C. to 1350° C. The zinc oxide ceramic layer has a specific resistance in the range of 0.001 to several ohms mm (10−4 to 10−1 of ohms cm). The specific resistance is identical to volume resistivity.
PTL 1: Japanese Patent No. 4123957
Patent Literature 1 states that when an electric current of 1 mA flows through the voltage nonlinear resistive element, the voltage VlmA between both ends is approximately 4 V. However, voltage in a high electric current region (for example, in the case that an electric current of 20 A/cm2 flows) is not studied.
The present invention solves such problems and principally aims to lower clamping voltage in a high electric current region of a zinc oxide voltage nonlinear resistive element.
A voltage nonlinear resistive element according to the present invention includes
a voltage nonlinear resistor containing at least one joined body in which a zinc oxide ceramic layer composed mainly of zinc oxide and having a volume resistivity of less than 1.0×10−2 Ωcm is joined to a rare-earth metal oxide layer composed mainly of a rare-earth metal oxide, and
a pair of electrodes disposed on the voltage nonlinear resistor such that an electrically conductive path passes through a junction between the zinc oxide ceramic layer and the rare-earth metal oxide layer.
In this voltage nonlinear resistive element, the zinc oxide ceramic layer of the voltage nonlinear resistor is a zinc oxide ceramic layer having a lower volume resistivity than before. Thus, the clamping voltage in a high electric current region (for example, in the case that an electric current of 20 A/cm2 flows) can be lower than before. As a result, for example, even when a large current flows through a voltage nonlinear resistive element according to the present invention due to static electricity, a rise in voltage can be decreased, and the dielectric breakdown of the element can be prevented.
In a voltage nonlinear resistive element according to the present invention, the zinc oxide ceramic layer may contain one or more selected from the group consisting of Al2O3, In2O3, and Ga2O3. The addition of such a trivalent metal ion can relatively easily decrease the volume resistivity of the zinc oxide ceramic layer.
In a voltage nonlinear resistive element according to the present invention, the rare-earth metal oxide layer may be formed on the zinc oxide ceramic layer by sputtering. The rare-earth metal oxide layer can be formed by sputtering without exposing the zinc oxide ceramic layer to a high temperature. Thus, the volume resistivity of the zinc oxide ceramic layer is not increased by heat.
In a voltage nonlinear resistive element according to the present invention, the voltage nonlinear resistor may include two or more of the stacked joined bodies, and a rare-earth metal oxide layer, or a rare-earth metal oxide layer and a conductor layer, or a rare-earth metal oxide layer, a conductor layer, a rare-earth metal oxide layer are disposed between adjacent zinc oxide ceramic layers. Thus, the number of stacked joined bodies in the voltage nonlinear resistor can be adjusted for various varistor voltages.
A method for manufacturing a voltage nonlinear resistive element according to the present invention includes the steps of
(a) producing a joined body by forming a rare-earth metal oxide layer composed mainly of a rare-earth metal oxide on a zinc oxide ceramic layer composed mainly of zinc oxide and having a volume resistivity of less than 1.0×10−2 Ωcm by sputtering,
(b) producing a layered voltage nonlinear resistor by preparing at least two of the joined bodies, stacking the joined bodies with a conductor foil interposed between the rare-earth metal oxide layer of one of the joined bodies and the zinc oxide ceramic layer of the other of the joined bodies, or directly stacking the joined bodies without anything interposed therebetween, and joining the joined bodies in this state by heat treatment in an inert atmosphere at a temperature in the range of 300° C. to 700° C., and
(c) forming a pair of electrodes such that an electrically conductive path passes through a junction between the zinc oxide ceramic layer and the rare-earth metal oxide layer, or alternatively
(a) producing a joined body by forming a rare-earth metal oxide layer composed mainly of a rare-earth metal oxide on a zinc oxide ceramic layer composed mainly of zinc oxide and having a volume resistivity of less than 1.0×10−2 Ωcm by sputtering,
(b) producing a layered voltage nonlinear resistor by preparing at least two of the joined bodies, stacking the joined bodies with a conductor foil interposed between the rare-earth metal oxide layer of one of the joined bodies and the rare-earth metal oxide layer of the other of the joined bodies, or directly stacking the joined bodies without anything interposed therebetween, and joining the joined bodies in this state by heat treatment in an inert atmosphere at a temperature in the range of 300° C. to 700° C., and
(c) forming a pair of electrodes such that an electrically conductive path passes through a junction between the zinc oxide ceramic layer and the rare-earth metal oxide layer.
This method can be used to relatively easily manufacture a voltage nonlinear resistive element that includes a plurality of stacked joined bodies in a voltage nonlinear resistor. Furthermore, because the heat treatment temperature in the step (b) ranges from 300° C. to 700° C. and is relatively low, this can prevent the volume resistivity of the zinc oxide ceramic layers from being increased by heat. In particular, this effect is significant when the heat treatment temperature in the step (b) ranges from 300° C. to 500° C.
Preferred embodiments of the present invention will be described below with reference to the accompanying drawings.
The voltage nonlinear resistive element 10 includes a voltage nonlinear resistor (hereinafter abbreviated to a resistor) 14 and a pair of electrodes 16 and 18 disposed on opposite sides of the resistor 14.
The resistor 14 includes a joined body 12 in which a zinc oxide ceramic layer 12a is joined to a rare-earth metal oxide layer 12b composed mainly of a rare-earth metal oxide. The zinc oxide ceramic layer 12a is a layer composed mainly of zinc oxide and having a volume resistivity of less than 1.0×10−2 Ωcm. The volume resistivity is preferably 1.0×10−3 Ωcm or less. This can result in a still lower clamping voltage in a high electric current region than before. The rare-earth metal oxide layer 12b preferably has a thickness in the range of 0.01 to 1 μm, more preferably 0.05 to 0.5 μm. The rare-earth metal oxide is not particularly limited and is preferably Pr2O3, La2O3, or Yb2O3, for example.
The pair of electrodes 16 and 18 are formed on the resistor 14 such that an electrically conductive path passes through a junction between the zinc oxide ceramic layer 12a and the rare-earth metal oxide layer 12b. The electrodes 16 and 18 may be formed of any electrically conductive material that can form a satisfactory ohmic contact with the zinc oxide ceramic, for example, gold, silver, platinum, or aluminum. When a voltage is applied to the element such that the electrode 18 is an anode, an electric current can flow easily. On the other hand, when a voltage is applied to the element such that the electrode 16 is an anode, the element exhibits voltage nonlinearity.
An example of the manufacture of the voltage nonlinear resistive element 10 will be described below.
Formation of Zinc Oxide Ceramic Layer 12a
The zinc oxide ceramic layer 12a can be formed by cutting a plate material having a predetermined size from a zinc oxide ceramic block having a volume resistivity of less than 1.0×10−2 Ωcm, preferably 1.0×10−3 Ωcm or less. The zinc oxide ceramic block can be produced by dissolving a trivalent ion of Al, Ga, In, or the like in a zinc oxide ceramic as a dopant or by introducing an oxygen defect by firing a zinc oxide powder in a nonoxidizing atmosphere. A zinc oxide ceramic block in which a dopant is dissolved can be produced by first mixing a zinc oxide powder with an Al2O3, Ga2O3, In2O3, or another trivalent metal oxide powder such that the trivalent metal oxide constitutes 0.05% to 2.0% by mass and forming the mixed powder into a compact having a predetermined shape. The compact is then held in a nonoxidizing atmosphere (for example, a nitrogen or argon atmosphere) at a temperature in the range of 900° C. to 1200° C. for several hours and is then fired at a temperature in the range of 1300° C. to 1500° C. for several hours. In this manner, a zinc oxide ceramic block having low volume resistivity can be relatively easily produced. In order to achieve the target volume resistivity, the mass percentage of the trivalent metal oxide powder to be mixed with the zinc oxide powder or the firing temperature may be adjusted. The zinc oxide powder used as a raw material preferably has an average particle size in the range of 0.02 to 5 μm. The trivalent metal oxide powder preferably has an average particle size in the range of 0.01 to 0.5 μm. The trivalent metal oxide powder is preferably an Al2O3 powder. The Al2O3 powder may be formed of θ-alumina, γ-alumina, or boehmite. In order to produce the zinc oxide ceramic block having low volume resistivity by firing the zinc oxide powder in a nonoxidizing atmosphere, for example, the zinc oxide powder is fired in a nonoxidizing atmosphere (for example, a nitrogen or argon atmosphere) at a temperature in the range of 1300° C. to 1500° C. for several hours.
Formation of Rare-Earth Metal Oxide Layer 12b
The rare-earth metal oxide layer 12b may be formed of a rare-earth metal oxide alone or a mixture of two or more rare-earth oxides or may contain a rare-earth metal oxide as a main component and another oxide (for example, Cr2O3, MnO, Cod, ZnO, or SiO2) as an accessory component. When the rare-earth metal oxide layer 12b is formed of a rare-earth metal oxide alone, for example, the rare-earth metal oxide layer 12b may be formed on the zinc oxide ceramic layer 12a by sputtering a target of the rare-earth metal oxide. Instead of sputtering, vacuum evaporation or ion plating may also be used. The rare-earth metal oxide layer 12b may also be formed by applying a paste containing a rare-earth metal oxide powder to the zinc oxide ceramic layer 12a, drying the paste, and heat-treating the dried product at a relatively low temperature (for example, in the range of 200° C. to 700° C., preferably 200° C. to 500° C.). When the rare-earth metal oxide layer 12b contains an accessory component, the rare-earth metal oxide layer 12b may be formed on the zinc oxide ceramic layer 12a by simultaneously sputtering targets of the rare-earth metal oxide and the accessory component. The rare-earth metal oxide layer 12b may also be formed by applying a paste containing a rare-earth metal oxide powder and an accessory component powder to the zinc oxide ceramic layer 12a, drying the paste, and heat-treating the dried product at a relatively low temperature. In the case of heat treatment, the volume resistivity of the zinc oxide ceramic layer 12a is less likely to be increased by heating because the temperature is relatively low. However, because sputtering can be performed at a lower temperature, sputtering can eliminate the possibility of such an increase in volume resistivity.
Formation of Electrodes 16 and 18
In the present embodiment, the resistor 14 includes one joined body 12 in which the zinc oxide ceramic layer 12a is joined to the rare-earth metal oxide layer 12b. The electrodes 16 and 18 can be formed on both sides of the resistor 14 by vapor deposition or sputtering of an electrode material. The electrode material may be gold, silver, platinum, or aluminum. Plate-shaped electrodes 16 and 18 may be joined to each surface of the resistor 14 with an electrically conductive joint member.
When a voltage is applied to the voltage nonlinear resistive element 10 described above in detail such that the electrode 16 is an anode, the voltage nonlinear resistive element 10 exhibits voltage nonlinearity. Thus, the clamping voltage in a high electric current region (for example, in the case that an electric current of 20 A/cm2 flows) can be lower than before. As a result, for example, even when a large current flows through the voltage nonlinear resistive element 10 due to static electricity, a rise in voltage can be decreased, and the dielectric breakdown of the element can be prevented.
The present invention should not be limited to the embodiments described above and can be implemented in various aspects within the scope of the present invention.
For example, although the voltage nonlinear resistive element 10 includes the electrodes 16 and 18 on both sides of the resistor 14 containing one joined body 12, the resistor 14 may be replaced with a layered resistor composed of a plurality of joined bodies 12. Such a layered resistor can be used to control the varistor voltage. Thus, it is possible to manufacture a voltage nonlinear resistive element that has a varistor voltage suitable for the intended application. Examples that include a layered resistor are illustrated in
A voltage nonlinear resistive element 30 illustrated in
A voltage nonlinear resistive element 130 illustrated in
A voltage nonlinear resistive element 40 illustrated in
A voltage nonlinear resistive element 140 illustrated in
Although a plurality of joined bodies 12 in the embodiments illustrated in
Zinc oxide (average particle size 1.5 μm) was added to 0.1% by mass of θ-alumina (average particle size 0.02 μm), the mixture was wet-blended, was dried, was passed through a sifter having a sieve opening of 75 μm, and was shaped to form a compact. The compact was degreased and held in a N2 atmosphere at 1100° C. for 5 hours and was then fired at 1400° C. for 5 hours, thereby producing a zinc oxide ceramic block. The zinc oxide ceramic block had a volume resistivity of 9.0×10−3 am. A 10 mm×10 mm×1 mm zinc oxide ceramic sheet was cut from the zinc oxide ceramic block. After the sheet was polished and washed, a sputtered praseodymium oxide film (thickness 0.3 μm) was formed on the zinc oxide ceramic sheet by high-frequency plasma sputtering a target of praseodymium oxide (Pr2O3), thereby producing a joined body. RFS-200 manufactured by ULVAC KIKO, Inc. was used for sputtering. The deposition conditions were as follows: target size: 80 mm in diameter, RF output: 20 W, gas pressure (Ar): 2.0 Pa, deposition time: 15 minutes.
The joined body was directly used as a resistor. An Al vapor deposition electrode was formed on both sides of the resistor. Thus, a voltage nonlinear resistive element was manufactured (see
*1 clamping voltage at an electric current corresponding to 1 mA/cm2
*2 clamping voltage at an electric current corresponding to 20 A/cm2
A zinc oxide ceramic block was produced in the same manner as in Example 1 except that zinc oxide was mixed with 1% by mass θ-alumina. The zinc oxide ceramic block had a volume resistivity of 9.3×10−4 Ωcm. A 10 mm×10 mm×1 mm zinc oxide ceramic sheet was cut from the zinc oxide ceramic block. The sheet is used to produce a joined body in the same manner as in Example 1. The joined body was directly used as a resistor. An Al vapor deposition electrode was formed on both sides of the resistor. Thus, a voltage nonlinear resistive element was manufactured. Electric current-voltage characteristics were measured by applying a voltage between the electrodes of the voltage nonlinear resistive element in the same manner as in Example 1. Table 1 and
A zinc oxide ceramic block was produced in the same manner as in Example 1 except that zinc oxide was mixed with 2% by mass θ-alumina. The zinc oxide ceramic block had a volume resistivity of 1.1×10−4 am. A 10 mm×10 mm×1 mm zinc oxide ceramic sheet was cut from the zinc oxide ceramic block. The sheet is used to produce a joined body in the same manner as in Example 1. The joined body was directly used as a resistor. An Al vapor deposition electrode was formed on both sides of the resistor. Thus, a voltage nonlinear resistive element was manufactured. Electric current-voltage characteristics were measured by applying a voltage between the electrodes of the voltage nonlinear resistive element in the same manner as in Example 1. Table 1 and
Aqueous aluminum nitrate was added to zinc oxide. The amount of aluminum nitrate was 0.01% by mass on an Al2O3 basis. The water content of the product was adjusted to be 50% by mass by the addition of water. Minute amounts of binder and antifoaming agent were added to the product. The product was agitated by ultrasonic waves for 30 minutes and with an impeller blade for 30 minutes. After agitation, the product was granulated using a spray dryer to produce a granulated powder. The granulated powder was passed through a sifter having a sieve opening of 200 μm, was shaped, was degreased, and was fired in the air at 1400° C. for 5 hours, thereby producing a zinc oxide ceramic block. The zinc oxide ceramic block had a volume resistivity of 2.0×10−2 Ωcm. A 10 mm×10 mm×1 mm zinc oxide ceramic sheet was cut from the zinc oxide ceramic block. A sputtered rare-earth metal oxide film was formed on the zinc oxide ceramic sheet in the same manner as in Example 1, thereby producing a joined body. The joined body was directly used as a resistor. An Al vapor deposition electrode was formed on both sides of the resistor. Thus, a voltage nonlinear resistive element was manufactured. Electric current-voltage characteristics were measured by applying a voltage between the electrodes of the voltage nonlinear resistive element in the same manner as in Example 1. Table 1 and
Comparative Example 2 is an example in which a zinc oxide compact was fired in an air (in Example 1 and 2, the compact was fired in a N2 atmosphere). Zinc oxide was added to 0.1% by mass of θ-alumina, the mixture was wet-blended and dried. After heat-treating at a temperature of 1000° C., the calcined mixture was ground in a ball mill until the particle size of it becomes 1 μm or less. Zinc oxide and θ-alumina are the same one as used in Example 1. The ground product was dried, was passed through a sifter having a sieve opening of 75 μm, and was shaped to form a compact. The compact was degreased and fired in an air at 1300° C. for 5 hours, thereby producing a zinc oxide ceramic block. The zinc oxide ceramic block had a volume resistivity of 7.3×10−1 Ωcm. A 10 mm×10 mm×1 mm zinc oxide ceramic sheet was cut from the zinc oxide ceramic block. A sputtered rare-earth metal oxide film (praseodymium oxide) was formed on the zinc oxide ceramic sheet in the same manner as in Example 1, thereby producing a joined body. The joined body was directly used as a resistor. An Al vapor deposition electrode was formed on both sides of the resistor. Thus, a voltage nonlinear resistive element was manufactured. Electric current-voltage characteristics were measured by applying a voltage between the electrodes of the voltage nonlinear resistive element in the same manner as in Example 1. Table 1 and
A zinc oxide ceramic block was produced in the same manner as in Comparative Example 2 except that zinc oxide was mixed with 1% by mass θ-alumina. The zinc oxide ceramic block had a volume resistivity of 3.5×10−2 Ωcm. A 10 mm×10 mm×1 mm zinc oxide ceramic sheet was cut from the zinc oxide ceramic block. A sputtered rare-earth metal oxide film (praseodymium oxide) was formed on the zinc oxide ceramic sheet in the same manner as in Example 1, thereby producing a joined body. The joined body was directly used as a resistor. An Al vapor deposition electrode was formed on both sides of the resistor. Thus, a voltage nonlinear resistive element was manufactured. Electric current-voltage Characteristics were measured by applying a voltage between the electrodes of the voltage nonlinear resistive element in the same manner as in Example 1. Table 1 and
Voltage generated in a high electric current region (for example, a region of 20 A/cm2 or more) was lower in the voltage nonlinear resistive elements according to Examples 1 to 3, which included the zinc oxide ceramic sheet having a volume resistivity of less than 1.0×10−2 Ωcm (particularly 1.0×10−3 Ωcm or less), than in the voltage nonlinear resistive element according to Comparative Example 1 to 3, which included the zinc oxide ceramic sheet having a volume resistivity of 2.0×10−2 Ωcm or more and being fired in an air. Thus, the voltage nonlinear resistive elements according to Examples 1 to 3 had an improved electronic circuit protective function.
Two joined bodies were prepared in the same manner as in Example 3. A zinc oxide ceramic sheet of one of the joined bodies was brought into contact with a sputtered praseodymium oxide film of the other of the joined bodies with a Au—Ge alloy (the mass ratio of Au/Ge=88/12) foil (thickness 50 μm) interposed therebetween. The joined bodies in this state were joined by heat treatment in an inert atmosphere at 420° C. for 10 minutes, thereby producing a layered resistor. An Al vapor deposition electrode was formed on both sides of the resistor. Thus, a voltage nonlinear resistive element was manufactured (see
These examples are only examples of the present invention and do not limit the present invention.
The present application claims priority from Japanese Patent Application No. 2014-056498 filed on Mar. 19, 2014, the entire contents of which are incorporated herein by reference.
The voltage nonlinear resistive element of the present invention is applicable to elements for protecting electronic circuits from abnormal voltage, specifically used for various sensors, such as humidity sensors and temperature sensors.
| Number | Date | Country | Kind |
|---|---|---|---|
| 2014-056498 | Mar 2014 | JP | national |