Water-based vacuum forming laminating adhesive

Abstract

A water-based vacuum forming laminating adhesive includes an ionic water-dispersed polyurethane, a carbodiimide and/or an aziridine, and optionally a vinyl acetate polymer. The polyurethane is characterized by a high polydispersity index, which provides a combination of adhesion and thermal stability. The polyurethane is made by chain extending an isocyanate functional urethane prepolymer with polyamine and ketimine.

Description

Claims

1. A water-based adhesive composition, comprising:

(a) an ionic water-dispersed polyurethane having a polydispersity index of at least 20; and

(b) a carbodiimide.

2. The composition of claim 1 further including an aziridine curing agent.

3. The composition of claim 1 further including a vinyl acetate polymer or copolymer.

4. The composition of claim 1 wherein the polyurethane (a) includes cationic groups derived from amine groups.

5. The composition of claim 4 wherein the polyurethane (a) is the reaction product of a urethane prepolymer containing isocyanate groups reacted in solvent with isocyanate-reactive ketimine and polyamine, followed by hydrolysis of the ketimine and neutralization to form cationic amine groups.

6. The composition of claim 5 wherein the ketimine is a diketimine.

7. The composition of claim 5 wherein the polyamine is a triamine.

8. The composition of claim 1 wherein said composition is stable for at least 30 days at 23.degree. C.

9. The composition of claim 1 further including a plasticizing agent.

10. The composition of claim 8, comprising:

24-64 weight percent of an ionic water dispersed polyurethane (a) based on weight of resin solids;

0-48 weight percent of vinyl acetate based on weight of resin solids;

0-10 weight percent of aziridine based on weight of resin solids;

0.5-10 weight percent of carbodiimide; and

0-33 weight percent of plasticizer based on weight of resin solids.

11. The composition of claim 2 wherein said aziridine is trimethylolpropane-tris-(.beta.-(N-aziridinyl)propionate).

12. The composition of claim 1 wherein the polydispersity index of the polyurethane is at least 25.

13. A waterborne polyurethane which is the reaction product of a urethane prepolymer containing isocyanate groups reacted in solvent with isocyanate-reactive ketimine and polyamine, followed by hydrolysis of the ketimine and neutralization to form cationic amine groups.

14. The composition of claim 13 wherein the ketimine is a diketimine.

15. The composition of claim 13 wherein the polyamine is a triamine.

16. The composition of claim 13 wherein the polydispersity index of the polyurethane is at least 20.

17. The composition of claim 13 wherein the polydispersity index of the polyurethane is at least 25.