Weatherability and adherence of polypropylene

Polypropylene resins have excellent mechanical properties, thermal properties and processability, in addition to being light in weight and relatively inexpensive, so that they find applications in a variety of molding shapes and sizes.
However, since polypropylene resins have inferior adherence to other materials, such as are used in coating compositions, their use in applications requiring that they be coated, printed or adhered to another material has inevitably been limited.
To improve the adherence of other materials to polypropylene resins, a specific primer coating has been applied to the polypropylene. However, primer coatings are expensive, and not always successful. Accordingly, a plasma surface treatment of the polypropylene using oxidizing gases has recently been suggested, to improve the adherability of the surface. By this method, the adherability of the surface of polypropylene resins has been improved to a practically sufficient level.
Polypropylene resins also have the disadvantage of poor weather resistance. Moldings which are used outdoors, such as automobile bumpers, must have good weatherability, and to do so, various kinds of stabilizers have been used.
Of these stabilizers, compounds containing 2,2,6,6-tetramethyl piperidyl groups in the molecule give the best stabilizing effects, and thus are usually added to moldings which are to be coated so as to prevent such degradation.
However, when a low temperature plasma treatment is applied to the surface of a polypropylene resin molding which contains a 2,2,6,6-tetramethyl piperidyl compound, to improve the adherability, the adherability is often degraded significantly, and after coating, the coating film can be peeled off or swelled out, raising serious problems.
In accordance with the present invention, these problems are overcome by subjecting a surface of polypropylene to the action of activated oxygen gas at a temperature below about 100.degree. C. in the presence of a 2,2,6,6-tetramethyl piperidyl compound for a time sufficient to improve such weather resistance and adherence.
The 2,2,6,6-tetramethyl piperidyl compound contains at least one group having the formula: ##STR1## wherein R is selected from the group consisting of alkyl, hydroxyalkyl and alkoxy, having from about one to eighteen carbon atoms, alkylaryl having from seven to about eighteen carbon atoms, and acyl having from one to about eighteen carbon atoms.
The invention accordingly also provides polypropylene resin moldings having excellent weather resistance and adherence to other materials, comprising polypropylene and a compound having an N-alkyl or N-acyl 2,2,6,6-tetramethyl piperidyl group represented by the formula: ##STR2## wherein R is selected from the group consisting of alkyl having from one to about eighteen carbon atoms and acyl having from one to about eighteen carbon atoms, after having been subjected to such a low temperature plasma treatment.
The low temperature plasma treatment is effected at a temperature below about 100.degree. C., and preferably at below about 50.degree. C., by causing a low pressure oxidizing gas, oxygen or a mixture of oxygen with ozone, nitrogen, air, argon, carbon dioxide, chlorine, fluorine or bromine, to excite by high frequency electric discharge or microwave discharge, so as to generate an activated gas, and contacting the surface of the polypropylene moldings with the activated gas. Treatment time and gas pressure are not critical. An effective treatment is obtained at a gas pressure within the range from about 0.1 to about 10 torr for from about 5 seconds to about 15 minutes.
In the foregoing Formula (I), the R alkyl includes methyl, ethyl, propyl, isopropyl, butyl, isobutyl, pentyl, hexyl, octyl, 2-ethylhexyl, decyl, dodecyl, tetradecyl and octadecyl; alkylaryl include benzyl, phenylethyl, phenpropyl, phenbutyl, phenhexyl, phenoctyl, phendodecyl, hydroxyalkyl include hydroxyethyl, hydroxypropyl, hydroxybutyl, hydroxyhexyl, hydroxyoctadecyl; and alkoxy including ethoxyethyl and 2,3-epoxypropyl.
Exemplary R acyl include acetyl, propionyl, acryloyl, methacryloyl, butyroyl, octanoyl, decanoyl, dodecanoyl, octadecanoyl, benzoyl, 4-tertbutylbenzoyl, salicyloyl and phthaloyl.
The N-alkyl and N-acyl (or 1-alkyl and 1-acyl) 2,2,6,6-tetramethyl piperidine compounds of this invention are known compounds that as indicated have in the molecule the group: ##STR3##
Such 2,2,6,6-tetramethyl piperidine compounds, inter alia, are disclosed in the following illustrative patents:
Japanese patents Nos. 46-31733, 46-31734, 46-31735, 47-1628, 47-7380, 47-8539 and 48-12410; Japan kokai Nos. 46-5082, 47-590, 48-95986, 49-53570, 49-58085, 49-60337, 49-61236, 49-61238, 49-63738, 49-64634, 49-72332, 49-120492, 50-5435, 50-26779, 52-78876, 52-89677, 52-91875, 52-125175, 52-139071, 53-67749, 53-71082, 54-71185, 54-103877, 56-30985, 56-75488, 56-138189, 56-161387, 57-24393, 57-58681, 57-63359, 57-80453, 57-121034, 57-137358, 57-146755, 57-167316, 57-177022, 58-5319, 58-10568, 58-32642, 58-32864, 58-37025, 58-38720, 58-4703058-53931, 58-57444, 58-57445, 58-69879, 58-77862, 58-92660, 58-108238, 58-120646, 58-152053, 58-152881, 58-154739, 58-159460, 58 -168634, 58-194862, 58-194931, 58-201777, 58-206594, 58-210094, 58-217554;
U.S. Pat. Nos. 3,542,729, 3,640,928, 3,684,765, 3,705,126, 3,893,972, 3,925,376, 3,929,804, 3,940,401, 3,992,390, 3,899,464, 3,984,371, 3,971,795, 3,959,291, 3,993,655, 4,007,158, 4,038,280, 4,061,616, 4,086,204, 4,089,841, 4,096,114, 4,101,508, 4,102,858, 4,104,248, 4,104,251, 4,105,625, 4,107,139, 4,108,829, 4,110,334, 4,115,476, 4,116,927, 4,118,369, 4,128,608, 4,136,081, 4,140,673, 4,144,224, 4,148,784, 4,151,356, 4,154,722, 4,161,592, 4,162,246, 4,166,813, 4,173,599, 4,177,186, 4,185,007, 4,197,236, 4,198,334, 4,210,612, 4,219,465, 4,223,147, 4,234,728, 4,237,297, 4,238,388, 4,238,613, 4,276,401, 4,279,804, 4,288,593, 4,289,686, 4,293,466, 4,293,467, 4,293,468, 4,308,362, 4,309,546, 4,311,820, 4,312,804, 4,315,859, 4,316,025, 4,316,837, 4,317,911, 4,321,374, 4,322,531, 4,326,063, 4,331,586, 4,335,242, 4,336,183, 4,340,534, 4,348,524, 4,351,915, 4,356,279, 4,356,287, 4,356,307, 4,369,274, 4,369,321, 4,376,836, 4,378,443, 4,395,508, 4,400,513, 4,404,301, 4,405,735, 4,408,051, 4,412,021, 4,413,075, 4,413,076, 4,413,093 and 4,413,096.
Particularly preferred classes of 2,2,6,6-tetramethyl piperidyl compounds have the formulae II and III: ##STR4## wherein; R is selected from the group consisting of alkyl having from one to about eighteen carbon atoms; and acyl having from one to about eighteen carbon atoms;
X is ##STR5## Y is --O-- or --N(R.sub.8)--; R.sub.7 is alkyl having from one to about five carbon atoms;
R.sub.8 is hydrogen or alkyl having from one to about eighteen carbon atoms;
R.sub.1 is a residue of mono- or poly-carboxylic acid;
n is a number from 1 to about 6;
m is a number from 0 to about 5; and
n+m is from 1 to about 6;
R.sub.2 is --O--R.sub.8 or --N(R.sub.8)R.sub.9 ;
R.sub.9 is alkyl having from one to about eighteen carbon atoms; and
R.sub.8 and R.sub.9 may be taken together to form alkylene or oxadialkylene;
R.sub.3 is alkylene or ##STR6## R.sub.4 is alkylene; and p is a number from one to about twenty; p represents the number of units in the polymer molecule of III,
Exemplary N-alkyl and N-acyl 2,2,6,6-tetramethyl piperidyl compounds include 1,2,2,6,6-pentamethyl-4-piperidylbenzoate, bis(1,2,2,6,6-pentamethyl-4-piperidyl) sebacate, bis(1-benzyl-2,2,6,6-tetramethyl-4-piperidyl) sebacate, bis(1-acetyl-2,2,6,6-tetramethyl-4-piperidyl) sebacate, tetrakis(1,2,2,6,6-pentamethyl-4-piperidyl) butanetetracarboxylate, tetrakis(1-octyl-2,2,6,6-pentamethyl-4-piperidyl) butanetetracarboxylate, tetrakis(1-acetyl-2,2,6,6-pentamethyl-4-piperidyl) butanetetracarboxylate, bis(1,2,2,6,6-pentamethyl-4-piperidyl)-2-butyl-2-(3,5-ditert-butyl-4-hydroxybenzyl) malonate, bis(1-acryloyl-2,2,6,6-tetramethyl-4-piperidyl)-2-butyl-2-(3,5-di-tert-butyl-4-hydroxybenzyl) malonate, bis(1,2,2,6,6-pentamethyl-4-piperidyl)di(tridecyl)butanetetracarboxylate, bis[1-(2,3-epoxypropyl)-2,2,6,6-tetramethyl-4-piperidyl]-di(tridecyl) butanetetracarboxylate, N-(1,2,2,6,6-pentamethyl-4-piperidyl) dodecyl succinic acid imide, 3,9-bis[1,1-dimethyl-2-tris (1,2,2,6,6-pentamethyl-4-piperidyloxycarbonyl) butylcarbonyloxyethyl]-2,4,8,10-tetraoxaspiro [5.5]undecane, 1,3,8-triaza-7,7,9,9-tetramethyl-3-dodecyl-8-acetylspiro [4.5] decane-2,4-di-one, bis(3-ethyl-8,8,9,10,10-pentamethyl-1,5-dioxaspiro [5.5]-3-undecylmethylether.
Small amounts of these compounds is effective. An amount within the range from about 0.001 to about 5 parts by weight, preferably from about 0.01 to about 3 parts by weight, per 100 parts by weight of the resin, is satisfactory.
Any polypropylene resin can be improved by the process of the present invention, including propylene homopolymers and random or block copolymers of propylene and an .alpha.-olefin which contain ethylene or other .alpha.-olefin in an amount from 1 to 30 wt. %, as well as blends of polypropylene with other olefin polymers and copolymers, such as low and high density polyethylene, ethylene/vinyl acetate copolymer, ethylene/propylene copolymer rubbers and styrene/butadiene blockcopolymer rubbers.
In addition, phenolic antioxidants, thioether antioxidants, organic phosphorus-containing compounds such as organic phosphites, and other ultraviolet light absorbers can be added to the polypropylene resin, as needed to improve resistance to oxidation and light.
Phenolic antioxidants which can be employed together with the stabilizer of the invention include 2,6-di-t-butyl-p-cresol, 2,6-di-phenyl-4-octadecyloxyphenol, stearyl(3,5-di-t-butyl-4-hydroxyphenyl)-propionate, distearyl-3,5-di-t-butyl-4-hydroxybenzylphosphonate, thio-diethylenebis(3,5-di-t-butyl-4-hydroxyphenylpropionate, hexamethylene-bis(3,5-di-t-butyl-4-hydroxyphenylpropionate, 4,4'-thiobis(6-t-butyl-m-cresol), 2-octylthio-4,6-bis(3,5-di-t-butyl-4-hydroxyphenoxy)-s-triazine, 2,2'-methylenebis(4-methyl-6-t-butylphenol), 2,2'-methylene-bis(4-ethyl-6-t-butylphenol), bis(3,3-bis(4-hydroxy-3-t-butylphenyl) butylic acid) glycol ester, 4,4'-butylidenebis (6-t-butyl-m-cresol), 2,2'-ethylidenebis(4,6-di-t-butylphenol), 2,2'-ethylidenebis(4-sec-butyl-6-t-butylphenol), 3,6-dioxaoctylenebis(3-methyl-5-t-butyl-4-hydroxyphenylpropionate), 1,1,3-tris(2-methyl-4-hydroxy-5-t-butylphenyl) butane, bis(2-t-butyl-4-methyl-6-(2-hydroxy-3-t-butyl-5-methyl benzyl)phenyl) terephthalate, 1,3,5-tris(2,6-dimethyl-3-hydroxy-4-t-butylbenzyl) isocyanurate, 1,3,5-tris(3,5-di-t-butyl-4-hydroxybenzyl) isocyanurate, 1,3,5-tris(3,5-di-t-butyl-4-hydroxybenzyl)-2,4,6-trimethylbenzene, 1,3,5-tris((3,5-di-t-butyl-4-hydroxyphenyl) propionyloxyethyl) isocyanurate, tetrakis(methylene-3-(3,5-di-t-butyl-4-hydroxyphenyl)-propionate) methane.
The amount of phenolic antioxidant to be added is within the range from about 0.001 to about 5 parts by weight, and preferably from about 0.01 to about 3 parts by weight, per 100 parts by weight of the resin.
Thioether antioxidants which can be employed together with the stabilizer of the invention, include dialkylthiodipropionates, such as dilauryl-, dimyristyl- and di-stearylthiodipropionate, and esters of .beta.-alkylthiopropionic acid with polyhydric alcohols, such as pentaerythritol tetrakis(.beta.-dodecylthiopropionate).
Phosphite antioxidants which can be employed together with the stabilizer of the invention include trioctylphosphite, trilaurylphosphite, tridecylphosphite, octyl diphenylphosphite, tris(2,4-di-t-butylphenyl) phosphite, tris(nonylphenyl) phosphite, hexa(tridecyl) 1,1,3-tris(2-methyl-4-hydroxy-5-t-butylphenyl) butane triphosphite, tetra(C.sub.12-15 alkyl) 4,4'-isopropylidenediphenol diphosphite, tetra(tridecyl)4,4'-butylidenebis(3-methyl-6-t-butylphenol) diphosphite, hydrogenated-4,4'-isopropylidenediphenol polyphosphite, distearyl pentaerythritol diphosphite, phenyl 4,4'-isopropylidenediphenol pentaerythritol diphosphite, bis(2,4-di-t-butylphenyl) pentaerythritol diphosphite, bis (2,6-di-t-butyl-4-methylphenyl) pentaerythritol diphosphite, di(nonylphenyl) pentaerythritol diphosphite and 4,4'-isopropylidenebis (2-t-butylphenol) di(nonylphenyl) phosphite.
Ultraviolet light absorbers which can be employed together with the stabilizer of the invention include hydroxybenzophenones such as 2-hydroxy-4-methoxybenzophenone, 2-hydroxy-4-n-octoxybenzophenone, 2,2'-dihydroxy-4-methoxybenzophenone and 2,4-dihydroxybenzophenone; benzotriazoles such as 2-(2'-hydroxy-3'-t-butyl-5'-methylphenyl)-5-chlorobenzotriazole, 2-(2'-hydroxy-3',5'-di-t-butylphenyl)-5-chloro-benzotriazole, 2-(2'-hydroxy-5'-methylphenyl) benzotriazole and 2-(2'-hydroxy-3',5'-di-t-amylphenyl) benzotriazole; benzoates such as phenyl salicylate, p-t-butylphenyl salicylate, 2,4-di-t-butylphenyl-3,5-di-t-butyl-4-hydroxybenzoate and hexadecyl-3,5-di-t-butyl-4-hydroxybenzoate; Ni compounds such as 2,2'-thiobis(4-t-octylphenol) Ni salt, (2,2'-thiobis(4-t-octylphenolate))-n-butylamine Ni and (3,5-di-t-butyl-4-hydroxybenzyl) phosphonic acid monoethyl ester Ni salt; substituted acrylonitriles such as .alpha.-cyano-.beta.-methyl-.beta.-(p-methoxyphenyl) acrylic acid methyl ester; and oxanilides such as N-2-ethylphenyl-N'-2-ethoxy-5-t-butylphenyloxanilide and N-2-ethylphenyl-N'-2-ethoxyphenyloxanilide.
In addition, inorganic fillers such as talc, calcium carbonate and glass fiber, metal soaps such as calcium stearate and calcium stearoyl-lactate, nucleating agents, etc. may be added to the polypropylene resin of the present invention, as occasion demands.
The invention is applicable to polypropylene resin moldings formed in any desired shape by any melting method conventionally known per se in the art, such as injection molding, extrusion molding, blow molding, etc. The molding method constitutes no part of the present invention.
The following Examples represent preferred embodiments of the process and molded products of the invention.

EXAMPLES 1 TO 9
Molding compositions containing stabilizers of the invention and of the prior art were prepared by blending the following components uniformly in a high speed mixer:
______________________________________Ingredients Parts by Weight______________________________________Propylene homopolymer 100Calcium stearate 0.1Tetrakis[methylene-3-(3,5-di-tert-butyl- 0.14-hydroxyphenyl)propionate] methane2-(2'-Hydroxy-3'-tert-butyl-5'-methyl- 0.2phenyl)-5-chlorobenzotriazoleStabilizer as shown in Table I 0.2______________________________________
The mixtures were extruded at 230.degree. C. in a 50.phi.-uniaxial extruder, thereby preparing pellets. Test pieces of 100.times.100.times.3 mm were prepared by injection molding of the pellets.
The test pieces were treated in a microwave plasma treatment apparatus (TMZ-9602Z, product of Toshiba Corporation) at room temperature (25.degree. C.) for 10 seconds at a flow rate of 400 cc/minute and a pressure of 0.5 torr, with activated oxygen gas and a power output of 400 W.
The test pieces after having undergone the plasma treatment were sprayed with twin pack polyurethane coating (R-263, product of Nippon Beechemical Co., Ltd.) to attain a film thickness of about 100 to 120.mu.. Thereafter, the coated test pieces were baked at 90.degree. C. for 40 minutes.
Then, a strip of the coating film was cut out at a width of 10 mm, and the belt-shaped coating film strip then was peeled off from one end of the cut and folded in the opposite direction, thereby conducting a 180 degree peeling test at a pulling rate of 20 mm/minute. Further, after immersing a coated test piece in hot water of 40.degree. C. for 10 days, it was observed whether or not the coating film was swelled.
Further, using a test piece uncoated and untreated and a test piece uncoated but treated, light stability was measured in a sunshine Weatherometer at 83.degree. C. The results are shown in Table I:
TABLE I__________________________________________________________________________ Hours to Failure Peel Uncoated/ Uncoated/ strengthExample No. Stabilizer Untreated Treated (g/cm) Swelling__________________________________________________________________________Control 1 None 400 300 760 noneControl 2 Bis(2,2,6,6-tetramethyl-4- 2300 1500 370 severe piperidyl) sebacateControl 3 Tetrakis(2,2,6,6-tetramethyl-4- 2500 1800 480 slight piperidyl)butanetetracarboxylateExample 1 Bis(1,2,2,6,6-pentamethyl-4- 2300 2000 640 none piperidyl) sebacateExample 2 Bis(1-acetyl-2,2,6,6-tetramethyl- 2200 2000 690 none 4-piperidyl) sebacateExample 3 Tetrakis(1,2,2,6,6-pentamethyl-4- 2600 2300 730 none piperidyl) butanetetracarboxylateExample 4 Bis(1,2,2,6,6-pentamethyl-4-piperidyl)- 2500 2300 720 none di(tridecyl)butanetetracarboxylateExample 5 1,3,8-Triaza-7,7,9,9-tetramethyl-8- 2200 1900 680 none acetylspiro [4.5] decane-2,4-dioneExample 6 3,9-Bis(1,1-dimethyl-2-(tris- 2500 2300 700 none (1,2,2,6,6-pentamethyl-4- piperidyloxycarbonyl)butylcarbonyl- oxy)ethyl)-2,4,8,10-tetraoxaspiro- [5.5] undecaneExample 7 Bis(1,2,2,6,6-pentamethyl-4- 2200 2000 620 none piperidyl)-2-butyl-2-(3,5-di-t- butyl-4-hydroxybenzyl) malonateExample 8 Bis(3-ethyl-8,8,9,10,10-pentamethyl- 2400 2100 690 none 1,5-dixoaspiro [5.5]-3-undecylmethyl) etherExample 9 N-(1,2,2,6,6-Pentamethyl-4- 2300 1900 700 none piperidyl) dodecylsuccinimide__________________________________________________________________________
From the results shown in Table I for Examples 1 to 9, it is apparent that the polypropylene resin moldings which contain a compound having an N-alkyl or N-acyl 2,2,6,6-tetramethyl piperidyl group are superior in light stability after plasma treatment, and also their adherence to coating film is not reduced, as compared with polypropylene resin moldings which contain a compound having the corresponding N-unsubstituted-2,2,6,6-tetramethyl piperidyl group.
EXAMPLES 10 TO 13
Molding compositions containing stabilizers of the invention and of the prior art were prepared by blending the following components uniformly in a high speed mixer:
______________________________________Ingredients Parts by Weight______________________________________Ethylene/propylene random copolymer 100(ethylene content: 12 wt. %)Calcium stearate 0.05Tetrakis[methylene-3-(3,5-d-di- 0.05tertbutyl-4-hydroxyphenyl) propionate]methane2,6-di-tert-butyl-p-cresol 0.05Tris(2,4-di-tert-butylphenyl) phosphite 0.12-(2'-Hydroxy-3'-tert-butyl-5'- 0.2methylphenyl)-5-chlorobenzotriazoleStabilizer shown in Table II 0.2______________________________________
The mixtures were extruded at 230.degree. C. in a 50.phi.-uniaxial extruder, thereby preparing pellets. Test pieces of 100.times.100.times.3 mm were prepared by injection molding of the pellets.
The test pieces were treated in a microwave plasma treatment apparatus (TMZ-9602Z, product of Toshiba Corporation) at room temperature (25.degree. C.) for 10 seconds at a flow rate of 400 cc/minute and a pressure of 0.5 torr, with activated oxygen gas and a power output of 400 W.
The test pieces after having undergone the plasma treatment were sprayed with twin pack polyurethane coating (R-263, product of Nippon Beechemical Co., Ltd.) to attain a film thickness of about 100 to 120.mu.. Thereafter, the coated test pieces were baked at 90.degree. C. for 40 minutes.
Then, a strip of the coating film was cut out at a width of 10 mm, and the belt-shaped coating film strip then was peeled off from one end of the cut and folded in the opposite direction, thereby conducting a 180 degree peeling test at a pulling rate of 20 mm/minute. Further, after immersing a coated test piece in hot water of 40.degree. C. for 10 days, it was observed whether or not the coating film was swelled.
Further, using a test piece uncoated and untreated and a test piece uncoated but treated, light stability was measured in a sunshine Weatherometer at 83.degree. C. The results are shown in Table II:
TABLE II__________________________________________________________________________ Hours to Failure Peel Uncoated/ Uncoated/ strengthExample No. Stabilizer Untreated Treated (g/cm) Swelling__________________________________________________________________________Control 1 None 400 300 620 noneControl 2 Bis(2,2,6,6-tetramethyl-4- 2500 1800 340 severe piperidyl) sebacateControl 3 Tetrakis(2,2,6,6-tetramethyl-4- 2700 2000 410 slight piperidyl) butanetetracarboxylateExample 10 Bis(1,2,2,6,6-pentamethyl-4- 2500 2200 510 none piperidyl) sebacateExample 11 1,3,8-Triaza-7,7,9,9-tetramethyl- 2300 2000 540 none 8-acetylspiro [4.5] decane-2,4-dioneExample 12 Tetrakis(1,2,2,6,6-pentamethyl-4- 2800 2500 570 none piperidyl) butanetetracarboxylateExample 13 Bis(1,2,2,6,6-pentamethyl-4- 2700 2300 560 none piperidyl)-di(tridecyl) butane- tetracarboxylate__________________________________________________________________________
The results for Examples 10 to 13 demonstrate that the polypropylene resin moldings which contain a compound having an N-alkyl or acyl 2,2,6,6-tetramethyl piperidyl group are superior in light stability after plasma treatment and also their adherence to coating film is not reduced, as compared with polypropylene resin moldings which contain a compound having the corresponding N-unsubstituted-2,2,6,6-tetramethyl piperidyl group.
EXAMPLES 14 TO 17
Molding compositions containing stabilizers of the invention and of the prior art were prepared by blending the following components uniformly in a high speed mixer:
______________________________________Ingredients Parts by Weight______________________________________Propylene homopolymer 90Ethylene-propylene rubber (EP02P, 10product of Japanese EP Rubber Co.)Calcium stearate 0.05Tetrakis(methylene-3-(3,5-3-di-tert- 0.2butyl-4-hydroxyphenyl) propionate)methane2-(2'-Hydroxy-3'-tert-butyl-5'-methyl- 0.2phenyl)-5-chloribenzotriazoleStabilizer shown in Table III 0.2______________________________________
The mixtures were extruded at 230.degree. C. in a 50.phi.-uniaxial extruder, thereby preparing pellets. Test pieces of 100.times.100.times.3 mm were prepared by injection molding of the pellets.
The test pieces were treated in a microwave plasma treatment apparatus (TMZ-9602Z, product of Toshiba Corporation) at room temperature (25.degree. C.) for 10 seconds at a flow rate of 400 cc/minute and a pressure of 0.5 torr, with activated oxygen gas and a power output of 400 W.
The test pieces after having undergone the plasma treatment were sprayed with twin pack polyurethane coating (R-263, product of Nippon Beechemical Co., Ltd.) to attain a film thickness of about 100 to 120.mu.. Thereafter, the coated test pieces were baked at 90.degree. C. for 40 minutes.
Then, a strip of the coating film was cut out at a width of 10 mm, and the belt-shaped coating film strip then was peeled off from one end of the cut and folded in the opposite direction, thereby conducting a 180 degree peeling test at a pulling rate of 20 mm/minute. Further, after immersing a coated test piece in hot water of 40.degree. C. for 10 days, it was observed whether or not the coating film was swelled.
Further, using a test piece uncoated and untreated and a test piece uncoated but treated, light stability was measured in a sunshine Weatherometer at 83.degree. C. The results are shown in Table III:
TABLE III__________________________________________________________________________ Hours to Failure Peel Uncoated/ Uncoated/ strengthExample No. Stabilizer Untreated Treated (g/cm) Swelling__________________________________________________________________________Control 1 None 400 300 630 noneControl 2 Tetrakis(2,2,6,6-tetramethyl-4- 2300 1600 430 slight piperidyl) butanetetracarboxylateExample 14 Bis(1,2,2,6,6-pentamethyl-4- 2100 1700 520 none piperidyl) sebacateExample 15 Tetrakis(1,2,2,6,6-pentamethyl-4- 2400 2200 580 none piperidyl) butanetetracarboxylateExample 16 Bis(1,2,2,6,6-pentamethyl-4- 2300 2100 560 none piperidyl)-di(tridecyl) butane- tetracarboxylateExample 17 3,9-Bis(1,1-dimethyl-2-(tris- 2300 2000 580 none (1,2,2,6,6-pentamethyl-4- piperidyloxycarbonyl) butylcarbonyl- oxy) ethyl)-2,4,8,10-tetraoxaspiro- [5.5] undecane__________________________________________________________________________
The results shown in Table III for Examples 14 to 17 demonstrate that the polypropylene resin moldings which contain a compound having an N-alkyl or acyl 2,2,6,6-tetramethyl piperidyl group are superior in light stability after plasma treatment and also do not have their adherence to coating film reduced, as compared with polypropylene resin moldings which contain a compound having the corresponding N-unsubstituted-2,2,6,6-tetramethyl piperidyl group.

Number	Name	Date
4404301	Kuboto et al.	Sep 1983
4429077	Karrer et al.	Jan 1984
4499220	Minagawa et al.	Feb 1985

Weatherability and adherence of polypropylene

Information

Patent Number

Date Filed

Date Issued

Inventors

Original Assignees

Examiners

CPC

US Classifications

Field of Search

US

International Classifications

Abstract

Description

Claims

Priority Claims (1)

Parent Case Info

US Referenced Citations (3)

Foreign Referenced Citations (1)

Continuations (1)