WET-CHEMICAL SYSTEMS AND METHODS FOR PRODUCING BLACK SILICON SUBSTRATES

Abstract

A wet-chemical method of producing a black silicon substrate. The method comprising soaking single crystalline silicon wafers in a predetermined volume of a diluted inorganic compound solution. The substrate is combined with an etchant solution that forms a uniform noble metal nanoparticle induced Black Etch of the silicon wafer, resulting in a nanoparticle that is kinetically stabilized. The method comprising combining with an etchant solution having equal volumes acetonitrile/acetic acid:hydrofluoric acid:hydrogen peroxide.

Description

CROSS REFERENCE TO RELATED PATENT APPLICATION

This application claims priority to U.S. Provisional Patent Application No. 61/260,179, filed on Nov. 11, 2009 and entitled “Wet-Chemical Systems and Methods for Producing Black Silicon Substrates” by Yost et. al., hereby incorporated by reference as if fully set forth herein.

TECHNICAL FIELD

The described subject matter relates to wet-chemical systems and methods for producing black silicon substrates, and to black silicon substrates with reduced reflective losses.

BACKGROUND

Reflection of incident light reduces the efficiency (photocurrent) of silicon solar cells. Without antireflection, about 40% of sunlight is lost. This anti-reflection must be effective across the entire solar spectrum and at a wide variety of incident sunlight angles. Acceptance of light from a broad range of angles aids in capturing morning, afternoon, and diffuse scattered light. These same antireflection properties are also useful in silicon-based optical detectors.

Presently, antireflection on crystal silicon photovoltaics is achieved through several different techniques, but none is completely satisfactory. Anisotropic (pyramidal) texture etching of single crystal silicon reduces reflectivity to about 5-15% on 100-oriented single-crystal silicon, but mainly for light incident at angles near 90° and not for low incident angles. This technique also consumes a lot of silicon material, making it impractical for film silicon photovoltaics. On other forms of silicon and silicon solar cells, deposited, quarter-wavelength films of ITO, SiO_x, SiN_x or other materials are used to reduce reflectivity, but the effect is based on interference and therefore tuned to a specific wavelength and is not necessarily effective across the entire solar spectrum. Averaged across the solar spectrum, reflection can be reduced to about 5-15%. Lower-reflection approaches that work effectively at all incident angles are still needed.

Previous black silicon etching approaches result in low reflectivity across the entire solar spectrum and a wide range of angles of incidence, but the gold evaporation step is expensive to implement and difficult to control.

The foregoing examples of the related art and limitations related therewith are intended to be illustrative and not exclusive. Other limitations of the related art will become apparent to those of skill in the art upon a reading of the specification and a study of the drawings.

SUMMARY

The following embodiments and aspects thereof are described and illustrated in conjunction with systems, tools and methods that are meant to be exemplary and illustrative, not limiting in scope. In various embodiments, one or more of the above-described problems have been reduced or eliminated, while other embodiments are directed to other improvements.

Exemplary embodiments are disclosed for the use of chlorauric acid (HAuCl₄) to replace the evaporated gold layer of current art. Exemplary embodiments are also disclosed for the use of organic modifiers to alter the activity of ions in solution. Mixing these ions into the solution instead of predepositing a gold layer aids the production of black silicon surfaces via an in-situ reduction of HAuCl₄ to gold nanoparticles of about 5-10 nm in size.

Performing the etch procedure after the phosphorus diffusion of the silicon surface to preserve minority carrier lifetime is also advantageous. The black silicon etching approach results in low reflectivity across the entire solar spectrum and a wide range of angles of incidence with the ability to texture heavily phosphorus-doped silicon wafers, which offers process flexibility and avoids costly minority carrier lifetime damage. Exemplary embodiments are disclosed herein for several wet-chemical methods for the production of Si surfaces that exhibit nearly complete suppression of reflectivity in the range of about 350-1000 nm wavelength.

In addition to the exemplary aspects and embodiments described above, further aspects and embodiments will become apparent by reference to the drawings and by study of the following descriptions.

BRIEF DESCRIPTION OF THE DRAWINGS

Exemplary embodiments are illustrated in referenced figures of the drawings. It is intended that the embodiments and figures disclosed herein are to be considered illustrative rather than limiting.

FIG. 1 illustrates an etching system for use in texturing silicon surfaces using catalytic solutions, with catalytic metal molecules or ionic species of catalytic material, and an oxidant-etchant solution.

FIG. 2 is a plot of results for an example of Black Etches on a heavily n-diffused silicon wafer with and without additional light sources. Step Height (“SH”) data for the amount of silicon removed is also included in the graph.

FIG. 3 is a plot of results for an exemplary technique for utilizing the organic modified Black Etch process.

FIG. 4 is a 100,000×SEM (scanning electron microscope) picture of an actual solar cell produced from a deep phosphorous-diffused silicon wafer after organic modified Black Etch process.

FIG. 5 is a 150,000× cross-sectional SEM picture of an actual solar cell produced from a deep phosphorous-diffused silicon wafer after organic modified Black Etch process.

FIG. 6 is a plot of results of a reflectivity comparison between the exemplary Black-Etch techniques on deep phosphorous-diffused silicon wafers.

DETAILED DESCRIPTION

Briefly, wet-chemical methods for producing black silicon substrates are disclosed. Exemplary embodiments are disclosed herein for several wet-chemical methods for the production of Si surfaces that exhibit nearly complete suppression of reflectivity in the range of about 350-1000 nm wavelength. Exemplary embodiments provide a simple way to get the benefits of “black silicon” and reduce reflective losses to below 3% across the “useful” solar spectrum and over a wide range of incident angles with the ability to texture a heavily phosphorus-doped wafer, which offers process flexibility during solar cell fabrication. Exemplary embodiments are disclosed for the use of chlorauric acid to replace the evaporated gold layer of current art and the use of organic modifiers to alter the activity of ions in solution. Mixing these ions into the solution instead of predepositing a gold layer is advantageous for the production of black silicon surfaces via an in-situ reduction of HAuCl₄ to gold nanoparticles of about 5-10 nm in size.

The soaking of single crystalline silicon wafers, which have been heavily doped with n-type dopant phosphorus, from phosphorous oxychloride (POCl₃) gaseous diffusion at about 950° C. for one hour, in a given volume of dilute (0.4 mM) solution of chlorauric acid when combined with an etchant solution comprised of equal volumes (1:1:1) of 50/50 vol % acetonitile/acetic acid:50 wt./vol. % hydrofluoric acid:30 wt./vol/% hydrogen peroxide provides a kinetically stabilized and uniform gold-nanoparticle induced Black Etch of the n-doped silicon surface within approximately four minutes. The function of the acetic acid is to provide a hydrophyllic hydrogen-bonded environment which accelerates the oxidation of the silicon surface, while the acetonitrile acts as a dissociaton limiter for the hydrofluoric acid and prevents the loss of too much of the diffused silicon layer which may compromise the n-p junction. It is noted that the soaking can be performed in the same time after the addition of the 0.4 mM chlorauric acid solution.

Exemplary embodiments include controlling the hydrophyllicity on silicon surfaces and the activity of hydrofluoric acid/hydrogen peroxide etching solutions by the addition of acetic acid and acetonitrile. Embodiments are disclosed which describe a process-specific repair for unsuccessful attempts to produce nanoporous Black-Silicon on wafers which have already been given a heavily and deep phosphorous diffused p/n junction (e.g., by POCL₃). The use of organic HF activity modifier (e.g., acetonitrile) and a silicon-surface hydrophyllicity modifier (e.g., acetic acid) in conjunction with the chlorauric acid (HAuCl₄) or like solution, together with a 1:1 mixture of hydrofluoric acid and hydrogen peroxide, enables the successful production of an anti reflective nanoporous layer on an already processed silicon wafer in one step.

The substrates manufactured into devices may be lightly-Boron-doped p-type, dual-side polished, single-crystal Float Zone silicon (100) wafers of approximately 1 to 3 ohm-cm resistivity.

An example of the etching procedure uses very dilute (e.g., less than about 1 mM) solutions of gold ions in the form of HAuCl₄ or the like. The time scale for the optimized process was reduced to about 4 minutes in order to obtain both minimum reflectance (e.g., up to about 5%) and the best surface uniformity. Piezoelectric profilometry showed samples of the Black Etch to consume approximately 1000 nm Si in that time.

Exemplary wet-chemical methods for producing black silicon substrates and methods of production thereof may be better understood with reference to the Figures and following discussion.

FIG. 1 illustrates an etching system for use in texturing silicon surfaces using catalytic solutions, with catalytic metal molecules or ionic species of catalytic material, and an oxidant-etchant solution.

The system 100 includes one or more wafers, substrates, or devices 110 with silicon surfaces. These may be Si wafers for solar cells, optoelectronics, or other products. The silicon surface 116 on silicon sample 112 may be mono-crystalline, multi-crystalline, amorphous, or the like, and the type of doping may be varied such as to be n and/or p-type doping of varying levels (such as from about 0.25 ohm-cm to about 50 ohm-cm or the like). The wafer, substrate, or device 110 may have one silicon surface or two or more such surfaces that are etched during operation of system 100.

The system 100 does not require a metal deposition station, but, instead, the system 100 may include an etching assembly 120 with a wet etching vessel or container 122 made of Teflon or high density polyethylene. During operation, one or more of the Si wafers 110 or Si layers on substrate 112 are placed into the vessel 122 before adding a volume of a catalytic solution containing the chosen metal ion along with the organic modifiers, acetic acid and acetonitrile, solution 140. In FIG. 1, a single substrate 112 is shown in the vessel with an exposed silicon surface 116 but a plurality of such surfaces 116 may be etched concurrently.

The assembly 120 includes a mechanism 126 for agitating or stirring the final reaction solution 124 initially and/or during etching. In one example, the mechanism 126 may be a mechanical or magnetic-based stirring device, while in some cases enhanced or more repeatable results are achieved with an ultrasonic agitator or the like for stirring/agitating the final reaction solution 124 by sonication. The assembly 120 may include a heater 128 to maintain or raise the temperature of the final reaction solution 124 within one or more desired temperature ranges to facilitate etching of surface 116. A temperature gauge or thermometer 130 may be provided to monitor the temperature of the solution (and, optionally, provide control feedback signals to heater 128), and a timer 134 may be provided as a visual and/or audio indicator to an operator of the assembly 120 regarding an etching or stripping step.

The system 100 further may utilize a catalytic solution 140 that provides a supply or source of a catalytic metal such as a metal containing molecular or ionic species of a catalytic metal and the organic modifiers, acetic acid and acetonitrile. This source provides a quantity of catalyst for the final reaction solution 124 such as a quantity of a transition or noble metal such as gold, silver, platinum, palladium, copper, nickel, cobalt, and the like. Good results are typically achieved with solutions containing HAuCl₄, AgF, and the similar acids or materials that release metal-containing molecules or ionic species of such metals when mixed with the oxidant-etchant solutions 142 and 144, which comprise the Black Etch solution 146 added to vessel 122. Generally, this catalytic solution with a metal catalyst is added to the vessel 122 to make up a portion of the final reaction solution 124. The etching and oxidizing solutions which constitute the balance of the final reaction solution 124 and their makeup are discussed in further detail below.

To achieve etching of the silicon surface 116, the system 100 includes a source for an etching agent 142 and of an oxidizing agent 144. These may be chosen specifically for texturing/etching of silicon, and the etching agent 142 may be HF, NH₄F, or other etchant. The oxidizing agent may be H₂O₂ or other agent, such as an agent that has its decomposition catalyzed by the metal provided by catalytic solution 140. For example, the oxidizing agent 144 may include H₂O₂, O₃, CO₂, K₂Cr₂O₇, CrO₃, KIO₃, KBrO₃, NaNO₃, HNO₃, KMnO₄, or the like or a mixture thereof. These agents (or solutions thereof) 142, 144 may be added separately to the vessel 122 to form the final reaction solution 124 along with the catalytic solution 140 or, as shown, an oxidant-etchant (black-etch) solution 146 may be formed first by combining the etching agent 142 and the oxidizing agent 144 and then putting this solution in the vessel 122. The assembly 120 is then operated such as by agitation via mechanism 126 and heating by heater 128 for a time (“etch time”) to texture the surface 116. After the etch time elapses, the solution 124 is removed (or substrate 112 is moved to another container or vessel for de-ionized water rinsing and metal stripping), and remaining metal catalyst is removed, as it may be present as an undesirable impurity in silicon. To this end, the system 100 includes a source of a metal stripping solution 150 that is added to the vessel 122, and the stripping solution may be stirred or agitated (and, optionally, heated with heater 128) by mechanism 126 until all or substantially all of the metal from material 140 is removed from surface 116. The substrate or wafer 112 may then be used as-is or as a component or layer of a larger device such as a solar cell or photovoltaic device, an optoelectronic device, a biomedical device, or other similar devices.

In FIG. 2, the graph 200 indicates examples of heavily n-diffused silicon wafers induced with Black Etch solutions with and without additional light sources. For example, adding a W-filament flashlight source 210 to the solution resulted in a SH of about 300 nm. Another embodiment utilized a 3 W 12V LED light source 220 resulting in a SH of about 575 nm. The SH without any additional light source 230 was about 300 nm.

In FIG. 3, the graph 300 shows the results for an exemplary technique for utilizing the organic modified Black Etch process resulting in s SH of about 750 nm.

FIG. 4 is a 100,000×SEM (scanning electron microscope) picture 400 of an actual solar cell produced from a deep phosphorous-diffused silicon wafer after organic modified Black Etch process.

FIG. 5 is a 150,000× cross-sectional SEM picture 500 of an actual solar cell produced from a deep phosphorous-diffused silicon wafer after organic modified Black Etch process.

FIG. 6 is a plot 600 of results of a reflectivity comparison between the exemplary Black-Etch techniques on deep phosphorous-diffused silicon wafers. In one example, the finished black Si solar cells 610 utilized a solution of HAuCl₄/Acetonitrile/Acetic acid/HF/H₂O₂ that mixed for approximately 4 minutes. In another embodiment, the finished black Si solar cells 620 utilized a solution of HAuCl₄/RF/H₂O₂ mixed for approximately 9 minutes.

EXAMPLES

In this example, polytetrafluoroethylene (PTFE) or Teflon® lab ware was utilized. The chemicals utilized were clean-room/reagent grade. Gentle swirling of the solution was used for mixing during the reaction, which includes the organic modifiers (acetonitrile and acetic acid). Ultrasonication was utilized for the initial trial of aqueous 26.25% H₂O₂, 6.25% HF (7:1 volume ratio) solution, which required additional light sources placed at about 50 mm above the wafer and for about 8-9 minutes to achieve minimum reflectance. It is noted that the use of ultrasonication for the organic-modified reaction results in an excess (>1500 nm) of silicon being etched away. The light source used a 6V tungsten filament lamp and a 3 W, 12-V blue LED.

A 26.25% H₂O₂, 6.25% HF (7:1 volume ratio) solution was found to aggressively black-etch (ultrasonicated) HF oxide-stripped silicon and wafers which have been deeply n-doped (i.e. 60 min. at about 950° C. with POCL₃). In this case, however, an 8-9 minute Black Etch time performed under high-intensity light with ultrasonic mixing has been found to produce wafers with less than about 5% reflectivity.

The wafers tested were about 0.5 inch square p(boron-doped)-type-Float Zone (FZ), polished on both sides, and approximately 1 to 3 ohm-cm resistivity and a (100) surface orientation. Both sides were subject to about one hour phosphorus diffusion at about 950° C. with POCl₃. The phosphorous-silicate glass formed on both sides was removed by 5% aqueous HF for about 10 minutes.

Another example used 2% HF to remove the phosphorous silicate residue following the POCL₃ diffusion before the Black-etch with 0.4 mM HAuCl₄. Reactive-ion etching/removal by SF₆ of the nip junction on one side was performed and a back contact was formed on it by about a five minute annealing of a silicon/aluminum paste at about 800° C. One side was protected by paraffin and the other side was subjected to the Black Etch process. The gold was removed by about a four minute ultrasomca_tion of the wafer in a solution comprising about 25 g I₂ and about 100 g KI per liter of DI H₂O. The paraffin was then removed with trichloroethylene (TCE) and a standard palladium/silver front grid was evaporated on the front side. The volume of Black Etch reagent and metal ion solution used for each reaction was about 4 ml of each for a total volume of about 8 ml. The stability of a pre-mixed solution (with respect to time) was demonstrated to be about 2 minutes at room temperature.

An exemplary procedure entailed placing the Si wafer in about a 0.8 mM solution of HAuCl₄ solution with an equal volume of a 1:1 mixture of the organic modifiers, acetic acid and acetonitrile (an effective [HAuCl₄] of 0.4 mM) for approximately 2-minutes prior to the addition of a Black Etch solution consisting of a 1:1:1 volume ratio solution of DI H₂O, HF, and H₂O₂, and gently swirling for approximately four minutes. The size of the resultant “Purple of Cassius” nanogold particles was determined by TEM (transmission electron microscopy) to be less than about 10 nm.

Another example was followed by the addition of an equal volume of a 1:0.5:0.5 ratio of 0.8 mM HAuCl₄:CAN:HOAc solution with gentle swirling agitation for about minutes, 15 seconds. XPS (X-ray photoelectron spectroscopy) revealed that the particles do not contain Au(I)ions, (i.e., from AuF), but only AuO or Au. It is noted that the initial reaction solutions tested comprised of equal volumes (1:1:1) of 50/50 vol % acetonitrile/acetic acid:50 wt./vol. % HF:30 wt./vol/% H₂O₂, work equally well with an aqueous 0.4 mM HAuCl₄ solution, but needed to be used within about two hours or the HF and H₂O₂ in the etchant solution decomposes the acetonitrile into cyanic acid (HOCN) and methanol and renders the black-etch inactive.

The catalytic nature of the Black-Etch process was confirmed by the observation of about a four-fold rate increase with about a 20° C. increase in reaction temperature. In one embodiment, only 30-60 seconds were used to reach the same degree of Black-Etch at about 45° C. compared with about 180-240 seconds for room temperature (25° C.) reactions. Perpendicular and cross-sectional SEM studies of mono-crystalline Si (100) wafers tested showed a uniform surface morphology containing an average of about 10 nm diameter cylindrical etch tunnels approximately 343 nm deep for the “standard” four minute Black-Etch.

With the heavily phosphorous diffused n-junctions implanted in p-(B) type silicon prior, the following representative results have been achieved with a fresh 1:1:1 volume ratio solution of about 50% acetonitrile/50% acetic Acid:50 wt./vol/% HF:30 wt./vol. % H₂O₂ in conjunction with an equal volume of a 0.4 mM HAuCl₄ solution for of about four minutes without ultrasonication (Black Si Etch I). These wafers exhibited a much lower reflectivity across the 350-1000 nm wavelength range (R_ave) than other methods which utilized the maximal H₂O₂ (7:1 HF:H₂O₂) 3 W 12V blue LED light assisted inorganic etch (Black Si Etch II) as shown in Table 1.

TABLE 1
	Jsc	Voc
Cell Type	(mA/cm2)	(V)	Fill Factor	Efficiency	Rave (%)
Black Si Etch I	33.30	0.570	0.570	10.84	1.0
Black Si Etch II	25.23	0.591	0.690	10.3	3.3

The low fill factor, open circuit voltage (V_oc) and efficiency is believed to result from thin metal contact on the porous surface, increasing the series resistance. However, the embodiments disclosed herein are not necessarily limited as such.

The acetic acid provides a hydrophilic hydrogen-bonded environment, which accelerates the oxidation of the silicon surface, while the acetonitrile serves as a dissociation limiter for the hydrofluoric acid and reduces or altogether eliminates the loss of too much of the diffused silicon layer, which may compromise the n-p junction.

Other methods utilized about a 3:2:1 volume ratio solution of acetic acid:50 wt./vol/% HF:30 wt./vol. % H₂O₂ in conjunction with an equal volume of a 0.4 mM HAuCl₄ solution for about two minutes (Black Si Etch III) without ultrasonication. Approximately one micron of the diffused layer junction was removed and the following cell parameters in Table 2 were achieved.

TABLE 2
	Jsc	Voc	Fill
Cell Type	(mA/cm2)	(V)	Factor	Efficiency	Rave (%)
Black Si	30.71	0.575	0.7366	13.0	5.3
Etch III

In the examples, the metal stripping solution comprised about 25 g I₂/100 g KI per Liter DI H₂O and was used for the same time (in the ultrasonic bath) and volume as for the Black Etch procedure. The effective concentration of KI₃ in this solution is about 0.8M. Aqua Regia 3:1 (HCL:HNO₃) has also been used for Au stripping, giving approximately the same residue gold according to SIMS (Secondary Ion Mass Spectrometry) profile{[Au] versus depth} for Black-etches utilizing HAuCl₄ as KI₃. A Cary-5G UV-Vis and or a Varian 6000i spectrometer equipped with a calibrated spherical reflectance chambers was used for all final reflectance measurements.

It is noted that the example discussed above is provided for purposes of illustration and is not intended to be limiting. Still other embodiments and modifications are also contemplated. While a number of exemplary aspects and embodiments have been discussed above, those of skill in the art will recognize certain modifications, permutations, additions and sub combinations thereof. It is therefore intended that the following appended claims and claims hereafter introduced are interpreted to include all such modifications, permutations, additions and sub-combinations as are within their true spirit and scope.

Claims

1. A wet-chemical method of producing black silicon substrates, comprising: soaking crystalline silicon wafers in a predetermined volume of a diluted inorganic compound solution;combining the wafers with an etchant solution wherein the solution comprises having equal volumes of an acetonitrile solution from acetic acid combined with a hydrofluoric acid and hydrogen peroxide etching solution; andproviding a kinetically stabilized and uniform noble metal nanoparticle induced Black Etch of the silicon wafer.

2. The method of claim 1, wherein the inorganic compound solution comprises chlorauric acid.

3. The method of claim 1, wherein the wafers are doped with n-type dopant phosphorus from phosphorous oxychloride gaseous diffusion.

4. The method of claim 1, wherein the wafers are doped with p-type dopant.

5. The method of claim 1, wherein the noble metal nanoparticle comprises gold, silver, platinum, palladium, copper, nickel or cobalt.

6. The method of claim 1, further comprising reducing reflective losses to less than about 3% across the useful solar spectrum and over a wide range of incident angles.

7. The method of claim 1, further comprising texturing a heavily phosphorus-doped wafer.

8. The method of claim 1, wherein use of an organic HF activity modifier and a silicon-surface hydrophyllicity modifier in conjunction with the chlorauric acid solution and a 1:1 mixture of hydrofluoric acid and hydrogen peroxide produces an anti-reflective nano-porous layer on an already processed silicon wafer.

9. The method of claim 1, further comprising producing Si surfaces that exhibit nearly complete suppression of reflectivity in the wavelength range of about 350-1000 nm.

10. A method comprising: combining gold-containing ionic or molecular species with a hydrogen peroxide/hydrogen fluoride and organic activity modifier etch; producing a broad-spectrum anti-reflective silicon surface.

11. A black silicon substrate comprising: a crystalline silicon wafer soaked in a predetermined diluted volume of an inorganic compound solution; wherein the wafer is combined with an etchant solution that forms a uniform noble metal nanoparticle induced Black Etch of the silicon wafer, wherein the nanoparticle is kinetically stabilized.

12. The black silicon substrate of claim 1, wherein the inorganic compound solution comprises chlorauric acid.

13. The black silicon substrate of claim 1, wherein the etchant solution comprises having equal volumes of an acetonitrile solution from acetic acid combined with a hydrofluoric acid and hydrogen peroxide etching solution; after which the substrate provides a kinetically stabilized and uniform noble metal nanoparticle induced Black Etch of the silicon wafer.

14. The black silicon substrate of claim 11 wherein the substrate exhibits reflective losses of less than about 3% across the useful solar spectrum and over a wide range of incident angles.

15. The black silicon substrate of claim 11 wherein the substrate is comprised of a texturized and heavily phosphorus-doped wafer, the wafer providing process flexibility during solar cell fabrication.

16. The black silicon substrate of claim 11 wherein the substrate is subjected to an organic HF activity modifier and a silicon-surface hydrophyllicity modifier in conjunction with the chlorauric acid solution and a 1:1 mixture of hydrofluoric acid and hydrogen peroxide to produce an anti-reflective nano-porous layer on an already processed silicon wafer in one step.

17. The black silicon substrate of claim 11 wherein the substrate comprises a surface that exhibits nearly complete suppression of reflectivity in the wavelength range of about 350-1000 nm.