Patent Application
20160129548
This application is based upon and claims the benefit of priority from the prior Japanese Patent Application No. 2014-229052 filed on Nov. 11, 2014, the entire contents of which are incorporated herein by reference.
Embodiments described herein relate generally to an abrasive cloth and a polishing method.
In a manufacturing process of a semiconductor device, chemical mechanical polishing (hereinafter referred to as “CMP”) is used to flatten, for example, a metallic film or a polycrystalline silicon film on a substrate, or an insulating film buried in a trench.
Next-generation devices of a three-dimensional layer stack type of the 19 nm generation or later are particularly required to ensure high flatness in a CMP process in order to reduce focus errors in an exposure process, which result from miniaturization and the increase in the number of stacked layers.
In the accompanying drawings:
In accordance with an embodiment, a polishing method includes supplying slurry to a surface of a polishing layer including a polymer, and bringing a polishing object into contact with the polishing layer to polish the polishing object. The polishing layer has a fibrous first substance mixed therein or contains a second substance. The second substance is higher in specific heat and higher in thermal conductivity than the polymer in such a manner that the second substance is surrounded by the polymer.
Embodiments will now be explained with reference to the accompanying drawings. Like components are provided with like reference reference numerals throughout the drawings and repeated descriptions thereof are appropriately omitted. It is to be noted that the accompanying drawings illustrate the invention and assist in the understanding of the illustration and that the shapes, dimensions, and ratios in each of the drawings are different in some parts from those in an actual apparatus.
In the specification of the present application, “stacking” not only includes stacking layers in contact with each other but also includes staking layers with another layer interposed in between. “Being mounted on” not only includes being mounted in direct contact but also includes being mounted with another layer interposed in between. Moreover, terms indicating directions such as the top and the bottom in the description represent relative directions when the surface of a polishing table on which an abrasive cloth is mounted is the top in the description of a CMP apparatus and when the surface of a substrate on which a polishing object is formed is the top in the description of the polishing object. Therefore, the directions may be different from actual directions based on gravitational acceleration directions.
The seat portion 11 has a polishing table shaft 11a, and a polishing table 11b coupled to the polishing table shaft 11a. The polishing table shaft 11a is connected to an unshown motor, and is rotated and driven by this motor so that the polishing table 11b rotates in the direction of, for example, the arrow AR1 via the polishing table shaft 11a.
The abrasive cloth 12 is mounted on the polishing table 11b. The abrasive cloth 12 is not particularly limited in its structure as long as a polishing layer is formed on the surface thereof with which the polishing object 14 comes into contact. For example, the abrasive cloth 12 may have a layer stack structure having two or more layers. The abrasive cloth 12 according to the present embodiment has a thermal diffusivity of 0.05 mm2/s or less, preferably 0.04 mm2/s or less, and has a storage modulus of 200 MPa or more at 20° C. to 60° C. The detailed configuration of the abrasive cloth 12 will be described later in detail.
The holding portion 13 is movable in any of X-, Y-, and Z-directions that constitute three dimensions. For example, when a surface 20 of the abrasive cloth 12 is disposed parallel to an X-Y plane as shown in
The seat portion 11 and the holding portion 13 are preferably rotated and driven together from the perspective of eliminating the unevenness of the polishing amount of the polishing object 14. When these portions are rotated and driven, the rotation direction of the holding portion 13 and the rotation direction of the seat portion 11 are preferably the same as shown in
The supply part 15 is located above the seat portion 11, for example, above the center of a circle when the seat portion 11 is circular cylindrical, and the supply part 15 supplies a slurry SL to the surface 20 of the abrasive cloth 12. The slurry SL includes, for example, a chemical such as an abrasive, and water.
The surface adjusting part 16 has a function to return the surface part of the abrasive cloth 12 which is worn or clogged with abrasive grains in the abrasive due to the polishing of the polishing object 14, to an initial state before the polishing of the polishing object 14.
The abrasive cloth cooling part 17 is located in the vicinity of the surface 20 of the abrasive cloth 12, and cools the surface part of the abrasive cloth 12. The abrasive cloth cooling part 17 includes, for example, a heat exchanger (not shown) which contacts the surface part of the abrasive cloth 12, or a non-contact mechanism (not shown) which supplies an inactive gas (heat-exchange gas) to the surface part of the abrasive cloth 12.
An abrasive cloth 122 shown in
Specific materials of the polymer 200 include polyurethane, polyurea, polyethylene, polypropylene, polyester, polyamide, polyvinyl chloride, an epoxy resin, an ABS resin, an AS resin, butadiene rubber, styrene butadiene rubber, ethylene propylene rubber, silicon rubber, fluoro rubber, and mixtures of the above substances. In the present embodiment, it is preferable to use polyurethane.
According to the abrasive cloth 122 in the present example, the low-thermal-conductivity substance WF is mixed in the polymer 200, so that frictional heat generated between the abrasive cloth 12 and the polishing object 14 during polishing does not easily diffuse into the abrasive cloth 12, and most of the generated frictional heat can be eliminated by the abrasive cloth cooling part 17 before reaching the inside of the abrasive cloth 12. As a result, it is possible to inhibit a temperature rise inside the abrasive cloth 12.
An abrasive cloth 124 shown in
Since the thermal conductivity of the high-specific-heat high-thermal-conductivity substance 300 is higher than that of the polymer 200, the frictional heat generated between the abrasive cloth 12 and the polishing object 14 preferentially flows into the material 300. As a result, it is possible to prevent the decrease of the storage modulus of the whole abrasive cloth 12 attributed to a temperature rise. When, for example, polyurethane is selected as the polymer, it is preferable that the specific heat of the high-specific-heat high-thermal-conductivity substance 300 is 1900 J/(kg·K) or more and the thermal conductivity thereof is 0.15 J/(m·s·K) or more. A specific example of the high-specific-heat high-thermal-conductivity substance 300 having such characteristics includes water (H2O).
The low-thermal-conductivity substance WF and the high-specific-heat high-thermal-conductivity substance 300 need to be contained at a position that is deep to some degree from the surface of the abrasive cloth 12, and need to be contained in a place which is shallow but into which the frictional heat comes.
Each of the distribution amounts of the low-thermal-conductivity substance WF (Example 1) and the high-specific-heat high-thermal-conductivity substance 300 (Example 2) is determined in consideration of the balance between the distribution amount and the hardness of the abrasive cloth 12 to be required.
A polishing method using the CMP apparatus 10 shown in
When the polishing layer is formed by the polymer 200 alone, the lower limit value of its thermal diffusivity is about 0.06 mm2/s. However, if the low-thermal-conductivity substance WF is mixed in the polymer 200 (Example 1), or if the high-specific-heat high-thermal-conductivity substance 300 higher in specific heat and thermal conductivity than the polymer 200 is previously contained so as to be surrounded by the polymer 200 (Example 2), the thermal diffusivity of the polishing layer can be reduced to 0.04 mm2/s or less, and the storage modulus at 20° C. to 60° C. can be 200 MPa or more.
At a thermal diffusivity of 0.05 mm2/s or less, the temperature rise inside the abrasive cloth 12 during polishing can be inhibited. At a storage modulus of 200 MPa or more, sufficient flatness of the surface of the polishing object can be ensured by the effect of the inhibited temperature rise.
At the time of CMP, the polishing object 14 is turned upside down from the state shown in
According to the present embodiment, the abrasive cloth 12 has a low thermal diffusivity of 0.05 mm2/s or less, so that the frictional heat between the abrasive cloth 12 and the polishing object 14 does not diffuse into the abrasive cloth 12 too much, and is mostly consumed to raise the temperature of the uppermost surface. The abrasive cloth cooling part 17 cools from the surface side of the abrasive cloth 12, and can therefore more effectively cool the abrasive cloth 12 than when the thermal diffusivity of the abrasive cloth 12 is high. As a result, it is possible to maintain a higher storage modulus of the whole abrasive cloth. Consequently, high flatness of the surface of the polishing object 14 can be ensured.
According to the present embodiment, the thermal diffusivity can be measured by, for example, a laser flash method.
The storage modulus can be measured by, for example, a nonresonant forced vibration method.
If the thermal diffusivity of the abrasive cloth 12 is 0.05 mm2/s or less, a temperature rise inside the abrasive cloth 12 during polishing can be inhibited. If the storage modulus is 200 MPa or more, sufficient flatness of the surface of the polishing object can be ensured by the effect of the inhibited temperature rise.
The abrasive cloth according to at least one embodiment described above has a thermal diffusivity of 0.05 mm2/s or less, so that it is possible to inhibit a temperature rise inside the abrasive cloth during polishing. Thus, it is possible to prevent the decrease of the storage modulus of the whole abrasive cloth attributed to a temperature rise. Therefore, it is possible to ensure high flatness in the surface of the polishing object.
According to polishing method in at least one embodiment described above, the slurry is supplied to the surface of the polishing layer of the abrasive cloth having a thermal diffusivity of 0.05 mm2/s or less, the polishing object is brought into contact with the polishing layer, and the polishing object is polished. Therefore, a temperature rise inside the abrasive cloth during polishing is inhibited, so that the decrease of the storage modulus can be prevented, and high flatness of the surface of the polishing object can be ensured.
While certain embodiments have been described, these embodiments have been presented by way of example only, and are not intended to limit the scope of the inventions. Indeed, the novel embodiments described herein may be embodied in a variety of other forms; furthermore, various omissions, substitutions and changes in the form of the embodiments described herein may be made without departing from the spirit of the inventions. The accompanying claims and their equivalents are intended to cover such forms or modifications as would fall within the scope and spirit of the inventions.