20130118666
Aircraft tires are subject to extreme operating conditions due to the heavy load per tire coupled with the high speed of the aircraft. Because of the heavy loading, the tires are subject to much greater deflection than passenger or truck tires.
Aircraft tires have two common constructions: bias and radial. Over 70% of aircraft tires are bias, which means they have a casing made of layers of alternate layers of ply that are at alternate angles substantially less than 90 degrees relative to the center line of the tread. However, radial tires are becoming more common as airframe manufacturers seek lighter weight. Radial tires are like passenger tires in that they have the ply oriented at substantially 90 degrees relative to the tread centerline. Aircraft tires come in a range of sizes, however the H-type size range has historically been a bias tire. Due to the modern trend, it is desired that radial aircraft tires are available in the H-type size. This has not been possible in the past because they have more deflection in the sidewall due to bending under loading. As a result, radial tires may have an increased heat generation and mechanical fatigue in the bead area of the tire. There may also be problems of bead cracking and scuffing in the bead region, as well as rubber deformation under the bead core.
Thus an improved radial tire with increased durability and bending resistance is desired.
A first aspect of the invention is a pneumatic aircraft tire having a radial carcass, tread, a crown reinforcement including one or more belt layers or strips reinforced by cords oriented relative to the circumferential direction at an angle of between 0° and 45° with respect to the equatorial plane of the tire. The B/W of the tire ranges between 60-70%, wherein B is the width of the tire between the wheel flange, and W is the inflated tire width under rated pressure.
A second aspect of the invention includes a pneumatic aircraft tire having a radial carcass, tread, a crown reinforcement having one or more belt layers or strips reinforced by cords oriented relative to the circumferential direction at an angle of between 0° and 45° with respect to the equatorial plane of the tire. The tire includes a B/W ratio which ranges from about 0.6 to about 0.7 (60-70%), wherein B is the width of the tire between the wheel flange, and W is the inflated tire width under rated pressure. The tire may further optionally include a tire bead portion having a Ra/Fr1 relationship which ranges from about 0.6 to about 2.1, wherein: Ra is the tire radius of the bead sidewall at uninflated and in a new and unused condition, and Fr1 is the wheel flange maximum radius. The tire may further optionally include a SW/TS ratio which ranges from about 0.1 to about 0.5, wherein SW is the chafer gauge at area A, TS is the total sidewall rubber gauge at area AH, wherein A is defined as the region in the sidewall that has a lower radial endpoint defined by the point of contact between the flange and the tire at inflated, unloaded condition, and an upper radial endpoint AH defined by the tire wheel flange point of contact when the tire is at inflated, and at 200% rated load.
“Apex” means a non-reinforced elastomer positioned radially above a bead core.
“Aspect ratio” of the tire means the ratio of its section height to its section width multiplied by 100% for expression as percentage.
“Axial” and “axially” means lines or directions that are parallel to the axis of rotation of the tire.
“Bead” means that part of the tire comprising an annular tensile member wrapped by, or otherwise attached to ply cords and shaped, with or without other reinforcement elements such as flippers, chippers, apexes, toe guards and chafers, to fit the design rim.
“Belt or breaker reinforcing structure” means at least two layers of plies of parallel cords, woven or unwoven, underlying the tread, unanchored to the bead, and having both left and right cord angles in the range from 5° to 45° with respect to the equatorial plane of the tire.
“Bias ply tire” means a tire having a carcass with reinforcing cords in the carcass ply extending diagonally across the tire from bead core to bead core at about a 25°-65° angle with respect to the equatorial plane of the tire. Cords run at opposite angles in alternate layers.
“Carcass” means the tire structure apart from the belt structure tread, under tread, and sidewall rubber over the plies, but including the beads.
“Circumferential” means lines or direction extending along the perimeter of the surface of the annular tread perpendicular to the axial direction.
“Chafers” refers to narrow strips of material placed around the outside of the bead to protect cord plies from the rim, distribute flexing above the rim, and to seal the tire.
“Cord” means one of the reinforcement strands of which the plies in the tire are comprised.
“Equatorial plane (EP)” means the plane perpendicular to the tire's axis of rotation and passing through the center of its tread.
“Flipper” means a reinforced fabric wrapped about the bead core.
“Footprint” means the contact patch are area of the tire tread with a flat surface at zero speed and under normal load and pressure.
“H type tire” means a B/W range of between 60-70%, wherein B is the width between the wheel flange, and W is the inflated tire width under rated pressure.
“Innerliner” means the layer or layers of elastomer or other material that form the inside surface of a tubeless tire and that contain the inflating fluid within the tire.
“Net-to-gross ratio” means the ratio of the tire tread rubber that makes contact with the road surface while in the footprint, divided by the area of the tread in the footprint including non-contacting portions such as grooves.
“Normal inflation pressure” refers to the specific design inflation pressure and load assigned by the appropriate standards organization for the service condition for the tire.
“Section width” is the distance between a tire's sidewalls measured at the widest part of the tire when inflated to rated pressure and not under load.
“Zigzag belt reinforcing structure” means at least two layers of cords or a ribbon of parallel cords having 1 to 20 cords in each ribbon and laid up in an alternating pattern extending at an angle between 5° and 30° between lateral edges of the belt layers.
The invention will be described by way of example and with reference to the accompanying drawings in which:
With reference to
The tire 100 is a radial ply tire of the tubeless type construction. The tire 100 has an air impervious inner liner 22 which contains fluid or air under pressure. Radially outward of the inner liner 22 are one or more radial plies 20. Each ply 20 extends from an annular tensile member commonly referred to as a bead core 30. As shown the plies 20 may wrap about the bead core 30 either turning axially out and up forming a ply turnup or alternately turning axially in and under the bead core 30. The plies may be anchored to the bead utilizing other configurations known to those skilled in the art.
Each of these carcass plies 20 may comprise any suitable cord, typically nylon cords such as nylon-6,6 cords extending substantially perpendicular to an equatorial plane EP of the tire (i.e. extending in the radial direction of the tire). Preferably the nylon cords have an 1890 denier/2/2 or 1890 denier/3 construction. One or more of the carcass plies may also comprise an aramid and nylon cord structure, for example, a hybrid cord, a high energy cord or a merged cord. Examples of suitable cords are described in US Pat. No. 4,893,665, U.S. Pat. No. 4,155,394 or U.S. Pat. No. 6,799,618. Preferably, the ply cords have a percent elongation at break greater than 8% and less than 30%, and more preferably greater than 9% and less than 28%.
The tire is shown mounted on a rim flange having a rim flange width extending from one bead to the other bead and indicated as B in
Radially above the bead core 30 is a first rubber apex 40. The first rubber apex is preferably triangular in shape, and preferably does not extend past the point AH, which is explained in more detail, below. A flipper 31 is wrapped around the first apex and bead core, and has ends radially inward of the apex 40. Preferably radially below the plies 20 is a chafer 11, which extends from a position radially inward of the bead to the bead toe, and then to the bead heel, to a position radially outward of the bead, terminating in a point CH 13. It is preferred that the chafer 11 extend radially outward so that the end CH 13 is radially outward of AH. A is the contact area of the tire with the wheel flange under loaded condition, and has a lower point AI defined by the contact edge at inflated, but unloaded condition and an upper limit AH at inflated conditions under 200% rated load.
Axially outward of the plies 20 is a second, optional apex 43 which is an elongated strip of elastomeric material extending radially outward of the bead adjacent the chafer. This apex 43 is interposed between the sidewall 9, the chafer 11 and the ply 20.
Radially outward of the carcass plies 20 is a belt package 50. A fabric layer 53 is shown radially outward of the belt package 50. Above the fabric layer 53 is a tread 18 as shown, the tread 18 has a plurality of circumferentially continuous grooves 17.
The belt package 50 as shown in
As shown in
The belt package 50 further comprises at least one zigzag belt reinforcing structure 70. The zigzag belt reinforcing structure 70 is comprised of two layers of cord interwoven together, wherein each layer of cord is inclined generally in the circumferential direction while being inclined to extend between alternating lateral belt edges. The strip is wound along such zigzag path many times while the strip is shifted a desired amount in the circumferential direction so as not to form a gap between the adjoining strips 43. As a result, the cords extend in the circumferential direction while changing the bending direction at a turnaround point at both ends 44, 45. The cords of the zigzag belt structure cross with each other, typically at a cord angle of 5 degrees to 30 degrees with respect to the equatorial plane EP of the tire when the strip 43 is reciprocated at least once between both side ends 44 and 45 of the ply within every 360 degrees of the circumference as mentioned above. The two layers of cords formed in each zigzag belt structure are embedded and inseparable in the belt layer and wherein there are no cut ends at the outer lateral ends of the belt.
It is preferred that the zigzag belt structure 70 is the most radially outward belt structure of the belt package 50. It is additionally preferred that there is only one zigzag belt structure. The zigzag belt structure 70 is preferably wider than the first belt structure 51, and more preferably is wider than both the first belt structure 51 but has a width less than the second belt structure 60. The ratio of the zigzag belt width Wz to the second belt structure width Ws is preferably as follows:
0.6<BWz/BWs<1.0 (1)
The cords of any of the above described spiral or zigzag belt layers may be nylon, nylon 6,6, aramid, or combinations thereof, including merged, hybrid, high energy constructions known to those skilled in the art. One example of a suitable cord construction for the belt cords, carcass cords (or both), may comprise a composite of aramid and nylon, containing two cords of a polyamide (aramid) with construction of 3300 dtex with a 6.7 twist, and one nylon or nylon 6/6 cord having a construction of 1880 dtex, with a 4.5 twist. The overall merged cable twist is 6.7. Preferably, the belt cords have an elongation at break greater than about 8% and less than about 26% and a break strength greater than about 400 N. More preferably, the belt cords have an elongation at break in the range of about 9% to about 25%. It is additionally preferred that the ply cords have a greater elongation at break than the belt cords elongation at break. The cord properties such as percent elongation at break, linear density and tensile strength are determined from cord samples taken after being dipped but prior to vulcanization of the tire.
The tire structure 100 as mentioned is an example of one type of tire structures that can utilize the bead core 30, of the present invention. Although the tire 100 as shown is an aircraft tire structure, the invention is also usable in other tires such as for example, truck tires, off the road tires, or highly loaded heavy-duty tires. With reference to
Aluminum is an ideal alloy in that it provides excellent corrosion resistance when used with steel and it is very strong at the welded joint. Aluminum can be tempered, further increasing the tensile strength of the central core 36. The tensile strength of 6061 aluminum alloys can vary in the range of 125 MPa for 6061 T0 to 310 MPa for 6061 T6. Aluminum alloys in 6061 T4 range have superb strength ratios while maintaining excellent ductility.
As further illustrated the central core 36 is wrapped by a sheath of two or more sheath layers 35, preferably at least two sheath layers 35. The wires 35 of the sheath layers are steel helically or spirally wound about the central core 33. The invention is not limited to the bead core illustrated, and other bead designs may be utilized.
The bead area design of the present invention reduces the problem of bead cracking and deformation by reducing the tire wheel contact pressure and reducing the heat generation. As best shown in
The bead of the present invention is designed to have a bead compression ratio of less than about 24%, and more preferably less than about 18%. The bead compression ratio can be defined by t1/T, wherein: t1 is the interference gauge of chafer rubber between the rim and the tire, as measured under the center of the bead core perpendicular to tire bead seat surface 14. t1 can be calculated by subtracting the bead seat radius from the rim flange radius. T is the total material gauge under the bead core as measured in a radial direction along the bead core centerline, from the radially innermost edge 15 of the bead core 30 to the radially innermost edge of the bead area 14.
Therefore,
and more preferably,
In order to improve the bead durability, another important parameter is defined by the following relationship:
Wherein: SW is the gauge thickness of the sidewall at point AH; A is the contact area of the tire with the wheel flange, and has a lower point A1 defined by the contact edge at inflated, but unloaded condition and an upper limit AH at inflated conditions, and loaded under 200% rated load; TS is the total rubber gauge of the sidewall and other rubber components such as the apex, which is axially outward of the ply, as measured at the point AH.
Table I, below, lists tabulated values and results for example tires 1 through 6. All of the tires were the following size: H37.5×12.0R19 20PR mounted on wheel size: H37.5×12.0R19 with an elliptical flange shape and width between the wheel flange is 7.75″. The parameters Ra, Fr1, T, t1, TS, Sw were determined. All of the tires in Table I were subjected to a taxing distance index, which was measured on each tire tested on a dynamic tire tester, at a rated load of 25,600 lbs at a rated pressure of 212 psi, at a test speed at 40 mph under a test load at 41000 lbs. The tire was run continuously at the test conditions until the tire blew out.
Each tire construction of Table 1 was subjected to a FAA TSO test. After the test, the chafing index was determined for each tire by visual inspection and measurement of the width, depth and length of cracking in the bead area. The bead deformation under the bead core at the bead seat was also measured by measuring the depth gauge of the deformation. For all three indexes, the higher the numerical value, the better the performance. Thus the best performing tire for all three indexes were examples 5 and 6 of the present invention.
Variations in the present invention are possible in light of the description of it provided herein. While certain representative embodiments and details have been shown for the purpose of illustrating the subject invention, it will be apparent to those skilled in this art that various changes and modifications can be made therein without departing from the scope of the subject invention. It is, therefore, to be understood that changes can be made in the particular embodiments described which would be within the full-intended scope of the invention as defined by the following appended claims.
This Application claims the benefit of and incorporates by reference U.S. Provisional Application No. 61/496,338 filed Jun. 13, 2011. This invention relates in general to radial ply tires, and more particularly to tires subjected to very heavy loads, high pressures and high speed.
| Number | Date | Country | |
|---|---|---|---|
| 61496338 | Jun 2011 | US |