The invention generally relates to a semiconductor device and method of manufacture and, more particularly, to a semiconductor device that includes FinFETs with different oxide thicknesses on front and back gates and a method of manufacture of such a device.
Conventional metal oxide semiconductor field effect transistors (MOSFETs) have a single control gate on a planar substrate. Single control of the channel often leads to undesired leakage current between the source and drain when the transistor is intended to be non-conductive. This becomes especially problematic as the critical dimensions of integrated circuits continue to decrease.
An improved planar structure employs two gates, one on each side of the channel. As this arrangement increases the electrostatic coupling between the gates and the channel, the drive current of the transistor is increased and the leakage current is decreased. Unfortunately, however, such planar double gate devices are difficult to manufacture.
One mode of operation of a double-gate FET is to switch the two gates simultaneously. Another use of the two gates is to switch only one gate and apply a bias to the second gate to dynamically alter the threshold voltage of the FET. This mode of operation is commonly called back-gate. Advantageously, the performance of a backgated chip can be fine tuned either dynamically or after manufacturing.
Backgated devices offer interesting improvements to device technology as the devices are scaled down. For metal gate devices, threshold voltage adjustment by doping results in buried layer devices. Backgated devices can be used to adjust the threshold voltage without creating buried layer devices.
Threshold voltage adjustment can also be achieved for fully depleted thin silicon devices by conventional doping. However, increased impurity scattering by additional dopants may cause a significant degradation in mobility and drive current.
FinFETs are an attractive alternative to planar double gated devices because FinFETs are much easier to manufacture. The body of a FinFET is formed from a vertical semiconductor structure, generally referred to as a “fin”, that acts as a channel. A poly-Si layer may be deposited over the fin and patterned to form perfectly aligned gates straddling the fin. The fin terminates on both sides at the source and drain. Among the many advantages offered by FinFETs is better gate control at short gate lengths. FinFETs thus facilitate scaling of CMOS dimensions while maintaining an acceptable performance.
When gates are formed on both sides of the fin as described above, the device is generally referred to as a double gate FinFET. Use of a double gate suppresses short channel effects (SCE), provides for lower leakage, and provides for improved switching behavior.
The FinFET fabrication process can be modified to convert double gate FinFETs into backgated devices. One modification involves oxide thickness. In backgated devices, it is typically preferable to have a thicker oxide in the back-gate (i.e., the biased nonswitching gate) than in the front-gate to minimize front-gate to back-gate capacitance and source/drain to back-gate capacitance.
Oxides having different thicknesses may be grown on two sides of the fin of a FinFET when the fin is formed with a sidewall image transfer (SIT) process. However, growing two different thicknesses in the SIT process has shortcomings. For example, the oxide may be damaged during etching of a dummy gate or during reactive ion etching (RIE) of the opposite side of a fin, which are integral steps of the SIT process. Also, if the fin is produced using a process other than SIT, a different method for obtaining multiple oxide thicknesses is needed.
The invention is directed to overcoming one or more of the problems as set forth above.
In a first aspect of the invention, a method of fabricating a semiconductor structure is provided. The method entails forming a fin for a FinFET on a substrate. The fin has first and second sides. A first impurity is introduced on the first side of the fin. A dielectric layer is formed on the first and second sides. Due to the presence of the impurity, the dielectric layer is thicker on one of the first and second sides than the other of the first and second sides.
In a second aspect of the invention, a method of fabricating a semiconductor structure includes forming a fin for a FinFET on a substrate. The fin has first and second sides. A first impurity is directionally implanted on the first side of the fin. A dielectric layer is formed on the first and second sides of the fin. Due to the presence of the introduced impurity, the dielectric layer is thicker on one of the first and second sides than the other of the first and second sides. A FinFET gate having front and backgate sides and a top surface is also formed. The FinFET gate straddles the fin.
In a third aspect of the invention, a semiconductor structure is provided. The semiconductor structure includes a substrate and a fin for a FinFET on the substrate. The fin has first and second sides. The structure also includes a first impurity introduced on the first side of the fin. Additionally, a dielectric layer formed on the first and second sides of the fin is thicker on one of the first and second sides than the other of the first and second sides due to the presence of the introduced impurity.
An exemplary process according to the invention involves steps of introducing impurities into at least one side of a fin of a FinFET to enable formation of dielectric layers with different thicknesses. The impurity, which may be introduced by implantation, either enhances or retards dielectric formation having a thicker dielectric layer in the back-gate (i.e., the biased non-switching gate) than in the front-gate thereby reducing front-gate to back-gate capacitance as well as source and drain to back-gate capacitance.
Referring now to
A hard mask 130 is formed in a conventional manner on the exposed surface of silicon layer 120. The hard mask may be comprised of an insulating layer such as silicon oxide, silicon nitride, a low dielectric constant material, or other suitable etchant insulator which allows the use of aggressive etch chemistries such as plasma etching. By way of example, a protective hard mask stack composed of SiO2 and Si3N4 may be deposited by chemical vapor deposition over the silicon layer 120. The order of formation of the nitride layer and oxide layer may be reversed, or only one of the layers may be used instead of using both.
After hard mask deposition, a photoresist may be applied to the hard mask to define a pattern through use of optical lithography, electron beam lithography, x-ray lithography, or other conventional means, to define a lithographic mask 210 as shown in
Those skilled in the art will appreciate that the fin structure 310 may be formed using various techniques, such as by blanket deposition of each layer followed by selective etching as described above, or by selective deposition of each layer. The particular method of fin formation is not important to the invention.
Now referring to
Next, an impurity is directionally implanted into a side of the fin 310, as shown in
Implantation of the impurity enables forming a backgated FinFET with a front-gate having a different dielectric thickness than the control backgate. The backgate dielectric is usually the thicker layer. By way of example and not limitation, nitrogen or some other retarding impurity may be implanted in the front gate side to retard oxide dielectric growth on that side. Alternatively, silicon or argon or some other enhancing implant may be introduced to the backgate side to enhance oxide dielectric growth on that side. Other suitable implant species include heavy ions that will increase oxidation, such as cesium, oxygen and germanium. The impurities mention above may be implanted between 0.1 to 10 KeV at doses from 1e14 to 1e16 with title angles from approximately 10 to 45 degrees, as an example.
Illustratively, to implant nitrogen in the front gate side to retard oxide dielectric growth, a plasma nitridation process may be used. Remote plasma nitridation (RPN) using microwave or decoupled plasma nitridation (DPN) using radio frequency may interact with a nitrogen-containing gas to generate plasma containing nitrogen radicals.
The front gate side may be directionally targeted by the plasma that contains nitrogen. For example, directing the plasma at the front gate side at an angle from the vertical (e.g., 0-30°) should avoid material implantation on the backgate side. The directional aspect of implantation is important to ensure that the implant does not uniformly affect the gate structure with the same impurity. If both sides of the gate are equally affected by the implant, the implant will not result in a difference in dielectric layer thickness.
An exemplary gas composition of the plasma is 75% helium and 25% nitrogen at a pressure of 20 to 80 mTorr. The plasma nitrogen concentration may vary, for example, from 10% to 25%, with helium, neon or argon providing the balance. A source of nitrogen is introduced into the plasma to form the nitrogen-containing plasma. The source of nitrogen may, for example, be N.sub.2, NH3, NO, N2O, and/or mixtures thereof. The plasma may be applied at 10 to 50 W for 10 to 60 seconds.
During plasma nitridation, the fin 310 can be unbiased in which case the ionized substances are accelerated by the plasma potential and then implanted into the insulating surface. Alternatively, a bias voltage can be applied to the fin 310 to further accelerate the ions” movement from the plasma. Either a direct current or a radio frequency bias voltage can be used to bias the substrate. This step of the process thus introduces an impurity (e.g., nitrogen) solely or predominantly into one side of the fin (e.g., the front gate side) to affect (e.g., retard) dielectric growth.
A similar directional implantation process may be used to introduce some other retarding or enhancing impurity, e.g., argon or silicon, into a side of the fin, without departing from the scope of the invention. The particular directional implantation technique is not particularly important. Other techniques, now known or later developed, may be used to directionally implant a retarding or enhancing impurity into a side of the fin, without departing from the scope of the invention.
With the impurity implanted, the backgated FinFET can then be completed using conventional FinFET manufacturing processes. For illustrative purposes, a description of exemplary process steps will now be provided.
Referring now to
Next, a gate is formed straddling the fin as shown in
After forming the gate 720, the gate mask 710 can be stripped. This may be accomplished using any suitable mask removal technique, such as selective wet or dry etching.
At this point, appropriate dopants may be implanted to form doped source and drain regions, gate regions and extension regions, as shown in
Optionally, extension and halo implants may also be formed. For nFETs, typically B, In, or Ga are used for halo implants with energies in the range of 5 to 15 keV and a dose of 1×1013 to 8×1013 cm−3 Similarly, for pFETs, P, As, or Sb are used for the halos, with energies from 20 to 45 keV and dose of 1×1013 to 8×1013 cm−3.
Next, a spacer may be formed along the sidewalls of the gate and the channel by deposition and selective etching of a dielectric such as silicon nitride or silicon dioxide. Spacer formations on the sidewalls of the channel may be removed, if desired, by additional etching, leaving gate spacers 910 and 920 on either side of gate as shown in
After spacer formation, the hard mask over the source and drain can be removed to enable direct access to the underlying source and drain material. This can be achieved by anisotropically etching (e.g., reactive ion etching) the hard mask such that it is removed over the source and drain islands.
Subsequently, the surface may be chemically mechanically polished (CMP) to substantially level the gate height, as shown in
To complete the device, contacts to sources, drains, and gates may then be formed. Accordingly, a dielectric may be deposited and planarized, for example, using a chemical mechanical polishing process. Contact holes may then be structured and etched using an anisotropic process (e.g., reactive ion etching) or the like. The contact holes may then be filled in a conventional manner using a conducting material, such as doped polysilicon, silicide (e.g., WSi), metals (e.g., Au, Al, Mo, W, Ta, Ti, Cu, or ITO (indium-tin oxide)), or the like, being deposited by evaporation, sputering, or other known techniques, thereby forming source and drain contacts. Then a first metal layer may be deposited and structured using a reactive ion etching process or the like. Alternatively, the structuring of a first metal layer may be done following a damascene process flow.
The resulting structure includes a FinFET having different dielectric layer thickness on the front and back gate sides. Impurities introduced into at least one side of a fin of the FinFET enable formation of dielectric layers with different thicknesses. The impurity, which may be introduced by implantation, either enhances or retards dielectric formation.
While the invention has been described in terms of exemplary embodiments, those skilled in the art will recognize that the invention can be practiced with modifications and in the spirit and scope of the appended claims.
The present application is a continuation application of U.S. Application Ser. No. 11/365,504, filed on Mar. 2, 2006 which, in turn, is divisional application of copending U.S. Application Ser. No. 10/709,323, filed on Apr. 28, 2004, both of which are incorporated herein by reference in its entirety.
Number | Name | Date | Kind |
---|---|---|---|
6433609 | Voldman | Aug 2002 | B1 |
6448615 | Forbes et al. | Sep 2002 | B1 |
6593192 | Zahurak et al. | Jul 2003 | B2 |
6611023 | En et al. | Aug 2003 | B1 |
6885055 | Lee | Apr 2005 | B2 |
20020105039 | Hanafi et al. | Aug 2002 | A1 |
20030193070 | Chan et al. | Oct 2003 | A1 |
20030209761 | Yagishita et al. | Nov 2003 | A1 |
20040075122 | Lin et al. | Apr 2004 | A1 |
Number | Date | Country |
---|---|---|
2003-110109 | Apr 2003 | JP |
Number | Date | Country | |
---|---|---|---|
20060237774 A1 | Oct 2006 | US |
Number | Date | Country | |
---|---|---|---|
Parent | 10709323 | Apr 2004 | US |
Child | 11365504 | US |
Number | Date | Country | |
---|---|---|---|
Parent | 11365504 | Mar 2006 | US |
Child | 11427222 | US |