This invention relates to conductive interconnects for integrated circuits and more particularly to deposited silver (Ag) interconnects clad in a deposited silver-aluminum (Ag(Al)) alloy.
Continuous shrinkage in device dimensions in ultra-large-scale-integration (ULSI) technologies has resulted in interconnects being subjected to high current densities and thermal stresses leading to their premature failure. Electromigration is one of the governing phenomenon which contributes to early failure of interconnects. Choices of metallization is an important parameter that affects the performance of chip interconnects. Until recently, Al was considered as the ideal interconnect metallization, but its relatively high resistivity (˜2.7 μΩ-cm) and poor electromigration resistance have led to an ongoing search for a better replacement. Ag is one of the potential interconnect materials and has excellent electromigration resistance. However, Ag tends to agglomerate at higher temperatures, and does not adhere too well to dielectrics due to its inert nature when in contact with most materials.
The closest art is believed to be PCT application Serial No. PCT/US04/028705 entitled “Thermal Stability for Silver Metallization,” of Kim and Alford, filed Sep. 2, 2004, claiming priority from U.S. provisional patent application Ser. No. 60/499,645. Both applications are incorporated herein by reference. Like the provisional application, the PCT application mainly deals with the thermal stability of Ag(Al) alloy thin films on SiO2 in terms of prevention of agglomeration and improvement of adhesion between the metallization and the substrate. The present invention, however, deals with a cladded Ag metallization structure.
In accordance with the present invention interconnects for integrated circuits, components and devices of substantially pure Ag are clad in an Ag(Al) alloy. Preferably, in an exemplary embodiment, an Ag(Al) alloy is deposited on a semiconductor oxide layer to a thickness of from about 6 nm to 12 nm, and preferably from about 8 nm to about 10 nm. A layer of substantially pure Ag is then deposited on the thin alloy film. A further thin film of the Ag(Al) is then deposited over the Ag to a thickness of preferably from about 3 nm to about 10 nm and more preferably from about 4 nm to about 6 mm. The alloy in accordance with the preferred exemplary embodiment has Al content in a range from about 0.5 atomic % to about 5 atomic % and more preferably in a range from greater than about 0.5 atomic % to about 2 atomic %, the remainder of the alloy content being substantially pure Ag.
Put another way, in the preferred embodiment, the layer of alloy deposited on the oxide layer is of a thickness sufficient to create a continuous film separating the Ag from the underlying oxide. This prevents agglomeration and the alloy film on the oxide is also of a thickness so as to prevent diffusion of the silver into the oxide. The further alloy film deposited over the Ag is of a thickness so as to be a continuous film capable of passivating the Ag upper surface. In the preferred exemplary embodiment the oxide is SiO2 grown on a Si wafer.
The clad structure is intended to alleviate problems of adhesion and agglomeration observed in pure Ag films and is put forth as a replacement for Al and Cu interconnect metallization in the microelectronics industry because of the reasons listed below:
This invention solves the problems of electromigration and Joule heating-induced early failure of interconnect metallization. It also alleviates problems, viz. agglomeration and poor adhesion to SiO2 associated with pure Ag metallization.
This invention can be used as:
For conventional electronics, microelectronics fabrication industries can use this invention. Also fabrication companies which are still using Al as interconnect metallization can switch to the Ag and Ag alloy clad structure proposed here and forgo the difficulties of Cu processing (etching, step coverage, CMP). For high temperature electronics, automotive companies are interested in electronics for under the hood applications. The invention is useful for flexible OLED displays and flexible electronics also.
This invention will be useful for interconnect metallization used for conventional microelectronics as well as high temperature applications. The Alford group at Arizona State University previously developed a reactive ion etch process for Ag metallization. See “Novel technique to pattern silver using CF4 and CF4/O2 glow discharges,” P. Nguyen, Y. Zeng, and T. L. Alford, J. Vac. Sci. Technol. B 19, 158 (2001), incorporated herein by reference. The conjunction with these two technologies will also enable smaller fabrication facilities to use current Al etch processes and extend their usefulness by not encumbering the cost of chemical mechanical polishing toolsets associated with copper metallization and the accompanying diffusion barrier technology. Moreover, the low resistivity and good adhesion properties makes this metallization compatible with the Ag contacts used in organic light emitting diodes.
The silver-silver alloy clad structure proposed here consists of layers of Ag(Al-5 atomic %)/Ag/(Ag(Al-5 atomic %)/SiO2. A cross-section of such a structure is shown in
The Ag(Al) alloy layer in contact with the oxide layer on a wafer acts as an adhesion layer between SiO2 and the subsequent layers of metals/dielectrics. The alloy thin film on the top of the oxide acts as a cladding layer for the pure Ag and thus reduces surface diffusion and enhances the electromigration resistance of the stack structure. The electromigration behavior of the entire structure is further improved because the Ag alloy encapsulation, being harder due to solution hardening effect, produces compression stress between the Ag alloy-Ag interface thus leading to reduced hillock formation and also since most of the current flows through the Ag layer due to its comparatively lower resistivity. Thus the Joule heating effect in the clad structure is lower. The present structure, then, is based on the proposition that the use of the Ag(Al) alloy layers in such a clad structure offsets the need for extra diffusion barrier layers and also improves the overall electromigration behavior of the structure.
The Ag(Al) alloy should contain Al from about 0.5 atomic % to about 5 atomic %, the remainder of the alloy being substantially pure Ag. Preferably the percentage of aluminum in the alloy is between greater than about 0.5 atomic % to about 2 atomic %. The thickness of the thin alloy film in contact with the SiO2 can range between about 6 nm to about 12 mm, more preferably from about 8 nm to about 10 nm. A benefit of this construction is that the Ag layer thickness has no criticality and may be of any of a wide range of thicknesses. The final Ag(Al) alloy layer can have a thickness in the range from about 3 nm to about 10 nm, and more preferably is from about 4 nm to 6 nm thick.
Experimental Fabrication
The Ag(Al) alloy of a specific exemplary experimental embodiment was 5 atomic % Al. The source of the Ag(Al) alloy was prepared by forming a solid solution of 95 atomic % pure Ag slugs and 5 atomic % pure Al slugs in the electron-beam (e-beam) evaporator. Single-line test structures of 3.75 μm line widths of pure Ag, Ag(Al) alloy and Ag(Al)/Ag/Ag(Al) on SiO2 were fabricated on (100)-oriented p-type silicon wafers with nominal resistivity between 0.2 and 0.8 Ω-cm by standard lift-off technique. The Si wafers were dipped in HF for 30 s to remove native oxide as indicated at 10 in the process flow chart of
Experimentally, as indicated at 18, 20 and 22, without breaking vacuum, clad structures were obtained by sequential deposition of the Ag(Al) alloy (˜10 nm), the pure Ag (˜130 nm) and the Ag(Al) alloy (˜10 nm) on the patterned oxide of the wafer using an e-beam evaporator at a base pressure of 3×10−6 torr and deposition pressure of 4×10−6 torr. The pure Ag and Ag(Al) alloy metal depositions were also done by known e-beam evaporation technique. The deposition environment pressure should be as near to null as possible.
Test Results
The failure time of the fabricated single line test structures was determined using a Tektronics 372 Semiconductor Workbench. In order to accelerate the failure of the structures the testing was done at elevated temperatures by placing the samples on a resistance heated hot stage. The test structures were all subjected to a constant current (0.15 A) and temperature conditions (190° C.) and their corresponding failure times were obtained. The failure criterion for the test lines was set to be complete open circuit. Table I below gives the resistivity in μΩ-cms and failure times in seconds obtained for the three different structures (Ag/SiO2, Ag(Al)/SiO2 and Ag(Al)/Ag/Ag/(Al)/SiO2) under the set temperature and current conditions.
As observed in the Table I above, the failure time of Ag(Al)/SiO2 structures was about six times better than that of pure Ag because the alloy does not agglomerate on the SiO2 thus there is reduced surface diffusion and hence enhanced electromigration lifetime. In case of the clad structure the failure time is nearly 38 times better than pure Ag and almost 7 times better than that of the alloy structure because of the reasons cited in the previous section. Thus it has been experimentally proven that the cladded Ag and Ag alloy structure shows better adhesion and electromigration resistance compared to pure Ag and can be thus proposed to be used as high temperature interconnect metallization.
While one or more specific preferred embodiments have been described application, those skilled in the art will readily recognize modifications, variations and equivalents that do not depart from the spirit and scope of the subject invention, as herein claimed.
This application is a continuation of, and claims priority to, U.S. patent application Ser. No. 11/208,251 filed on Aug. 18, 2005, entitled “CLADDED SILVER AND SILVER ALLOY METALLIZATION FOR IMPROVED ADHESION ELECTROMIGRATION RESISTANCE,” now issued as U.S. Pat. No. 7,446,037, which claims priority to U.S. Provisional Patent Application No. 60/602,762 filed on Aug. 18, 2004, the entire content and disclosures of which are hereby incorporated by reference in their entirety except for those sections, if any, that are inconsistent with this specification.
Number | Name | Date | Kind |
---|---|---|---|
6023100 | Tao et al. | Feb 2000 | A |
6100194 | Chan et al. | Aug 2000 | A |
6218219 | Yamazaki et al. | Apr 2001 | B1 |
6486514 | Jeong et al. | Nov 2002 | B2 |
6946791 | Choi et al. | Sep 2005 | B2 |
7446037 | Alford et al. | Nov 2008 | B2 |
20040072444 | Park et al. | Apr 2004 | A1 |
Number | Date | Country | |
---|---|---|---|
20090085212 A1 | Apr 2009 | US |
Number | Date | Country | |
---|---|---|---|
60602762 | Aug 2004 | US |
Number | Date | Country | |
---|---|---|---|
Parent | 11208251 | Aug 2005 | US |
Child | 12237905 | US |