Composition for oxide CMP

Information

  • Patent Grant
  • 5759917
  • Patent Number
    5,759,917
  • Date Filed
    Monday, December 30, 1996
    27 years ago
  • Date Issued
    Tuesday, June 2, 1998
    26 years ago
Abstract
A chemical mechanical polishing composition comprising carboxylic acid, a salt and a soluble cerium compound at a pH above 3 and a method to selectively polish a silicon oxide overfill in preference to a silicon nitride film layer in a single step during the manufacture of integrated circuits and semiconductors.
Description

BACKGROUND OF THE INVENTION
1. Field of the Invention
The present invention relates to chemical mechanical polishing slurries for semiconductor integrated circuit substrates. Specifically, this invention is a CMP slurry having a unique chemistry that is especially suitable for chemical mechanical planarization where a high silicon dioxide removal rate, and a low silicon nitride removal rate are required on the same substrate.
2. Description of the Related Art
Integrated circuits (IC) are made up of millions of active devices formed in or on a silicon substrate. The active devices form functional circuits and components. These devices are then connected by the use of multilevel metallized interconnects and vias. Interconnection structures normally have a first layer metallization, an interconnect plug, a second layer of metallization, and sometimes a third or more layers of metallization with their respective interconnects. Inter level dielectrics (ILDs), such as doped and undoped SiO2 are used to electrically isolate the different levels of interconnections.
Shallow trench isolation (STI) is a technology for device isolation in a give layer in the IC manufacturing process. In the STI process, silicon nitride is deposited on thermally grown oxide. After deposition of the nitride, a shallow trench is etched into the substrate using a mask. A layer of oxide is then deposited into the trench so that the trench forms an area of insulated dielectric which acts to isolate the devices in a chip, and thus reduces the cross-talk between active devices. The excess deposited oxide must be polished of and the trench planarized to prepare for the next level of metallization. The silicon nitride is applied to the silicon to prevent polishing of the masked silicon oxide of the device.
In a typical mechanical polishing process, the substrate is placed in direct contact with a rotating polishing pad. A carrier applies pressure against the backside of the substrate. During the polishing process, the pad and table are rotated while a downward force is maintained against the substrate back. An abrasive and chemically reactive solution, commonly referred to as "a CMP slurry", is flowed onto the pad during polishing. The chemicals and abrasive particles in the slurry initiate the polishing process by interacting with the wafer being polished. The polishing process is facilitated by the rotational movement of the pad relative to the substrate as slurry is provided to the wafer/pad interface. Polishing is continued in this manner until the final desired film thickness is achieved by removal of the required amount of thin-film material.
When polishing oxides, it is desirable of the slurry used to have a high removal rate towards the oxide layer and a low removal rate towards other layers which may be exposed during CMP, such as silicon nitride. The polishing slurry should be tailored to provide effective polishing at the desired polishing ranges selective to specific thin layer materials, while minimizing, at the same time, surface imperfections, defect, corrosion, erosion and the removal of silicon nitride and other stop layers.
CMP slurries useful for polishing oxides typically contain an abrasive at an alkaline or high pH. These slurries either rely on potassium hydroxide or ammonium hydroxide to effectively buffer the high pH. While these slurries polish silica at high rates they also polish silicon nitride at high rates. Typically, the ratio of these removal rates, i.e., the selectivity is, at most, about 5 to 1 silicon oxide to silicon nitride. It is believed that the mechanism of silicon nitride polishing is oxidative hydrolysis of the nitride to the oxide in an aqueous environment. At alkaline pH this oxide and nitride are similarly etched at a high rate. Thus, present CMP slurries undesirably polish silicon nitride at an unacceptably high rate.
There remains a need in the semiconductor industry for CMP slurries that have greater than a 5 to 1 oxide to nitride selectivity. Accordingly, new CMP slurries that selectively remove the oxide at high rates while leaving the stop layer of silicon nitride relatively intact are needed to overcome the present manufacturing problems, increase throughput and reduce costs of the CMP process. This is because a low selectivity process, when used in a manufacturing environment, will necessarily suffer overpolishing--in thinner film parts of the wafer--and the nitride stop layer will not prevent breakthrough to the underlying thin film(s).
SUMMARY OF THE INVENTION
This invention is a chemical mechanical polishing composition that is capable of polishing a silicon dioxide layer at a high rate.
This invention is also a chemical mechanical polishing composition that inhibits the polishing of a silicon nitride film.
In addition, this invention is a method of using a chemical mechanical polishing composition that selectively removes silicon dioxide from a substrate while leaving a silicon nitride layer associated with the substrate essentially intact.
In one embodiment, this invention is a chemical mechanical polishing composition comprising carboxylic acid, a salt and a soluble cerium compound. The composition has a pH from about 3.0 to about 11, and preferably from about 3.8 to about 5.5 and is useful for selectively removing silicon dioxide from layered substrates.
In another embodiment, this invention is a chemical mechanical polishing slurry comprising the chemical mechanical polishing composition described above and an abrasive. The slurry is especially useful for silicon dioxide film polishing.
In still another embodiment, the present invention is a method for using a chemical mechanical polishing composition comprising a carboxylic acid, a salt and a soluble cerium compound in an aqueous solution having a pH from about 3.0 to about 11 to selectively remove oxide overfill in preference to a silicon nitride film layer during the manufacture of integrated circuits and semiconductors.





BRIEF DESCRIPTION OF THE DRAWING
FIG. 1--Plot of pH versus PETEOS removal rate and nitrate removal rate.





DESCRIPTION OF THE CURRENT EMBODIMENTS
The present invention is directed to a chemical mechanical polishing composition that comprises, a carboxylic acid, a salt, and a soluble cerium compound, having a pH of from about 3.0 to about 11.0. The chemical mechanical composition may be used alone or it may be combined with a metal oxide abrasive to form a slurry. The compositions and slurries of this invention polish oxide layers such as silicon dioxide layers associated with substrates at high rates. In addition, the compositions of this invention have been found to inhibit silicon nitride polishing. The present invention is also directed to novel methods for using the compositions and slurries of this invention to polish oxide layers.
Before describing the details of the various preferred embodiments of this invention a term that is used herein will be defined. The "chemical mechanical composition" refers to the combination of at least one carboxylic acid, at least one salt, and at least one soluble cerium compound that may be used in conjunction with an abrasive pad to remove one or more layers of a substrate. The term "slurry" or "chemical mechanical polishing slurry" refers to the combination of the chemical mechanical polishing composition and at least one abrasive.
Carboxylic acids useful in a CMP slurry of the present invention include monofunctional and di-functional carboxylic acids and their salts. Preferably, the carboxylic acid is selected from the group including acetic acid, adipic acid, butyric acid, capric acid, caproic acid, caprylic acid, citric acid, glutaric acid, glycolic acid, formic acid, fumaric acid, lactic acid, lauric acid, malic acid, maleic acid, malonic acid, myristic acid, oxalic acid, palmitic acid, phthalic acid, propionic acid, pyruvic acid, stearic acid, succinic acid, tartaric acid, valeric acid, 2-(2-methyoxyethoxy) acetic acid, 2-�2-(2-methyoxyethoxy)ethyoxy! acetic acid, poly(ethylene glycol)bis(carboxymethyl)ether, and derivatives, including salts thereof. A most preferred carboxylic acid is acetic acid.
In the composition of the present invention, the carboxylic acid can comprise greater than 10% of the slurry. In a preferred embodiment, the carboxylic acid is present in the composition of this invention in an amount ranging from about 0.05 to about 10% by weight. In a more preferred embodiment, however, the carboxylic acid is present in the composition of this invention in an amount ranging from about 0.1 to about 3%.
The chemical mechanical composition of the present invention includes a salt. The term "salt" refers to any water soluble salts including organic salts and inorganic salts such as nitrate, phosphate, and sulfate salts. Soluble salts also refers to salts that are only partially or marginally soluble in water. Preferred salts are nitrate salts.
The term "nitrate salt" includes nitric acid. Useful nitrate salts include compositions of the formula (M).sub.n (NO.sub.3).sub.m where n and m are both integers. When n=m, M is monovalent and can be alkali earth metals such as Li, Na, K, as well as H, NH.sub.4, NR.sub.4 where R is an alkyl group having from 1 to 10 or more carbon atoms or is a mixture thereof, including NMe.sub.4, NBu.sub.4 and so forth. When n.noteq.m, then M is a multivalent cation or metal or a combination of a multivalent cations and monovalent cations. One known preferred nitrate salt is ammonium cerium nitrate, (NH.sub.4).sub.2 Ce(NO.sub.3).sub.6.
The salt may be present in the composition in the amount of from about 0.05 to about 6% by weight of the composition. It is most preferred that the salt is present in the composition in the amount ranging from about 0.1 to about 4% by weight.
The chemical mechanical composition of the present invention includes at least one soluble cerium compound. Non-limiting examples of soluble cerium compounds useful in a composition of the present invention include water soluble hydrated and non-hydrated salts of cerium hydroxide (Ce(OH).sub.4), ammonium cerium sulfate, (NH.sub.4).sub.2 SO.sub.4 Ce.sub.2 (SO.sub.4).sub.3 ; cerium acetate, Ce(O.sub.2 CH.sub.3).sub.3 ; cerium sulfate, Ce(SO.sub.4).sub.2 ; cerium bromate, Ce(BrO.sub.3).sub.3 .multidot.9H.sub.2 O; cerium bromide, CeBr.sub.3 ; cerium carbonate, Ce(CO.sub.3).sub.2, cerium chloride, CeCl.sub.3 ; cerium oxalate, Ce(C.sub.2 O.sub.4).sub.3 ; cerium nitrate, Ce(NO.sub.3).sub.3 (OH).multidot.6H.sub.2 O and any other known soluble cerium compounds. A preferred soluble cerium compound is ammonium cerium nitrate, (NH.sub.4).sub.2 Ce(NO.sub.3).sub.6. The soluble cerium compound will be present in the composition of this invention in an amount ranging from about 0.05 weight percent to about 10.0 weight percent and preferably from about 0.1 to about 4.0 weight percent.
A preferred embodiment of the chemical mechanical composition of the present invention includes ammonium cerium nitrate as both the salt and as the soluble cerium compound. Other soluble cerium nitrate salts may be incorporated into the composition of this invention as both the soluble cerium compound and as the salt. Ammonium cerium nitrate may be present in composition of the present invention in an amount ranging from about 0.05 to about 6% weight percent of the overall composition weight. A more preferred range of ammonium cerium nitrate is from about 0.1 to about 4.0 weight percent.
The chemical mechanical composition of this invention may be used alone or in conjunction with an abrasive to give a chemical mechanical polishing "slurry."Abrasives useful in conjunction with the compositions of the present invention include metal oxide abrasives. The metal oxide abrasive may be selected from the group including alumina, titania, zirconia, germania, silica, ceria and mixtures thereof. In addition, useful abrasives may be the result of mixing precursers of two or more metal oxides to give a chemical admixture of a mixed metal oxide abrasive. For example, alumina can be co-formed with silica, or combined alumina/silica.
Useful metal oxide abrasives may be produced by any techniques known to those skilled in the art, including high temperature processes such as sol-gel, hydrothermal or, plasma process, or by processes for manufacturing fumed or precipitated metal oxides. Pulverized or crushed metal oxide abrasives are also useful in the CMP slurry of this invention and may be manufactured by milling or grinding using conventional manufacturing techniques such as jet-milling, ball milling, bead milling, and other milling and pulvizeration techniques and process know to one skilled in the art.
Preferred abrasives suitable for the CMP slurries of this invention are silica and cerium oxide (ceria) with fumed silica being most preferred. Other suitable silica abrasives can be made by methods such as sol-gel, hydrothermal, plasma process, flame pyrolysis or by other processes for manufacturing metal oxides.
Pulverized abrasives are also suitable for this invention. Any pulverized metal oxide abrasive may be used in a CMP slurry of this invention. However, pulverized cerium oxide is preferred. The cerium oxide abrasive is ground in a media mill to give pulverized ceria. The original cerium oxide particle may be either mined cerium oxide or precipitated and calcined cerium oxide or a combination thereof. The grinding may be accomplished in an aqueous medium using any type of a grinding or milling apparatus such as by jet milling or ball milling. A preferred grinding mechanism is a medial mill with either yttria tetragonal zirconia (YTZ) or zirconium silicate media. The grinding process may use a dispersant or steric stabilizer.
The preferred pulverized metal oxide abrasive will have a narrow particle size distribution with a median particle size (i.e., aggregate particle or single particle) of less than about 0.5 microns. The particles may be diluted and filtered after the grinding. Preferably, after filtration, the particle sizes of the pulverized metal oxide abrasive range from about 40 to about 1000 nm, and preferably from about 100 to about 300 nm. The preferred pulverized abrasive should contain less than about 10 weight percent of particles having a median particle size greater than 0.6 .mu.m.
Precipitated cerium oxide is a suitable abrasive for oxide CMP. Precipitated cerium oxide particles are made from a variety of precursors including acetates, carbonates and hydroxide and nitrate salts of cerium. The median particle size of precipitated cerium oxide particles may range of from about 10 nm to about 500 nm, with the preferred size of precipitated cerium oxide particles being in the range of from about 30 to about 300 nm.
Another preferred abrasive is fumed silica. The production of fumed metal oxides is a well-known process which involves the hydrolysis of suitable feed stock vapor (such as silicon tetrachloride for a silica abrasive) in a flame of hydrogen and oxygen. Molten particles of roughly spherical shape are formed in the combustion process. The diameters of the particles are varied through process parameters, and these molten spheres of silica or similar oxide, typically referred to as primary particles, fuse with one another by colliding at their contact points to form branched, three dimensional chain-like aggregates. The force necessary to break aggregates is considerable and often irreversible. During cooling and collecting, the aggregates undergo further collisions that may result in some mechanical entanglement causing the formation of aggregates.
A preferred metal oxide will have a surface area, as calculated from the method of S. Brunauer, P. H. Emmet, and I. Teller, J. Am. Chemical Society, Volume 60, Page 309 (1938) and commonly referred to a BET, ranging from about 5 m.sup.2 /g to about 430 m.sup.2 /g and preferably from about 30 m.sup.2 /g to about 170 m.sup.2 /g. Due to stringent purity requirements in the IC industry the preferred metal oxide should be of a high purity. High purity means that the total impurity content, from sources such as raw material impurities and trace processing contaminants, is typically less than 1% and preferably less than 0.01% (i.e., 100 ppm).
In a preferred embodiment, the metal oxide abrasive consists of metal oxide aggregates having about 99 weight percent of the particles less than about 1.0 micron in diameter, a mean aggregate diameter less than about 0.4 micron and a force sufficient to repel and overcome the van der Waals forces between abrasive aggregates themselves. Such metal oxide abrasives have been effective in minimizing or avoiding scratching, pit marks, divots and other surface imperfections during polishing. The aggregate size distribution in the present invention may be determined using known techniques such as transmission electron microscopy (TEM). The mean aggregate diameter refers to the average equivalent spherical diameter when using TEM image analysis, i.e., based on the cross-sectional area of the aggregate. The surface potential or the hydration force of the metal oxide particles must be sufficient to repel and overcome the van der Waals attractive forces between the particles.
In another preferred embodiment, the metal oxide abrasive may consist of discrete metal oxide particles having a particle diameter less than 0.5 micron (500 nm) and a surface area ranging from about 10 m.sup.2 /g to about 250 m.sup.2 /g.
A CMP slurry of this invention will include from about 2 weight percent to about 25 weight percent metal oxide abrasive and preferably from about 2 weight percent to about 15 weight percent metal oxide abrasive.
Metal oxide abrasives useful in CMP slurries of the present invention are incorporated into the aqueous medium of the polishing slurry as a concentrated aqueous dispersion of metal oxides comprising from about about 3% to about 55% solids, and preferably between 30% and 50% solids. The aqueous dispersion of metal oxides may be produced using conventional techniques, such as slowly adding the metal oxide abrasive to an appropriate media, for example, de-ionized water, to form a colloidal dispersion. The dispersions are typically completed by subjecting them to high shear mixing conditions known to those skilled in the art.
The abrasives useful in a CMP slurry of the present invention can be a mixture of the abrasives described above. For example, precipitated cerium oxide, pulverized cerium oxide (also referred to a ceria) and fumed silica could be incorporated into a CMP slurry of the present invention. Other combinations of abrasives are also useful in the CMP slurry. In addition, the mixture of abrasives could include any relative proportion of one abrasive to another. For example, a combination of from about 5 to 100 weight percent of the pulverized oxide abrasive described above with from about 0 to about 95 weight percent precipitated abrasive has been found to be effective as a CMP slurry abrasive in STI applications.
Commercially available precipitated cerium oxides sold at a pH of about 1.5, are ineffective as CMP slurries. We have, however, discovered that significantly increasing the pH of the commercially available slurry to about 3.5 results in a CMP slurry that is useful for STI polishing. Furthermore, we have surprisingly discovered that a CMP slurry with the composition and pH disclosed above exhibits a high oxide layer removal rate and low nitride layer removal rate.
The CMP slurry of this invention must have a pH from about 3.0 to about 11.0 to be effective. More preferably, the slurry pH will range from about 3.5 to about 6.0, and most preferably the pH is from about 3.8 to about 5.5. Slurry pH is adjusted by adding any base to the composition and preferably by adding a non-metal base such as ammonium hydroxide to the slurry.
In order to further stabilize a polishing slurry of this invention against settling, flocculation and decomposition of the oxidizing agent, a variety of additional optional additives, such as surfactants, polymeric stabilizers or other surface active dispersing agents, can be used. The surfactant can be anionic, cationic, nonionic, amphoteric and combinations of two or more surfactants can be employed. Furthermore, it has been found that the addition of a surfactant may be useful to improve the within-wafer-non-uniformity (WIWNU) of the wafers, thereby improving the surface of the wafer and reducing wafer defects.
In general, the amount of an additive used, such as a surfactant, in the present invention should be sufficient to achieve effective steric stabilization of the slurry and will typically vary depending on the particular surfactant selected and the nature of the surface of the metal oxide abrasive. For example, if not enough of a selected surfactant is used, it will have little or no effect on stabilization. On the other hand, too much of the surfactant may result in undesirable foaming and/or flocculation in the slurry. As a result, additives like surfactants should generally be present in a range between about 0.001% and 10% by weight. Furthermore, the additive may be added directly to the slurry or treated onto the surface of the metal oxide abrasive utilizing known techniques. In either case, the amount of additive is adjusted to achieve the desired concentration in the polishing slurry.
The chemical mechanical polishing compositions and slurries of this invention are capable of selectively removing the silicon dioxide layer from layered substrates at very high rates. Furthermore, the compositions and slurries of this invention inhibit the polishing of silicon nitride from layered substrates. One important application for the chemical mechanical polishing compositions and slurries of this invention is in the manufacture of integrated circuits and semiconductors. In such a polishing application, the compositions and slurries of this invention effectively remove silicon dioxide for shallow trench device isolation.
The compositions and slurries of this invention preferably exhibit oxide removal rate of from about 1200 .ANG./min to about 6000 .ANG./min or more with an oxide to nitride removal selectivity of from about 5 to about 100 or more and preferably from about 15 to about 50 or more.
The compositions and slurries of the present invention may be incorporated in a single package which includes an aqueous composition of at least one carboxylic acid, a soluble cerium compound, a salt, an optional abrasive, and optional additives at the requisite pH. To avoid changes in activity of slurry over time it may be preferable to use at least a two package system where the first package comprises at least one carboxylic acid, a salt and a soluble cerium compound at any pH and the second package comprises the optional abrasive at any pH. These two packages will be engineered so that when they are mixed, the useful composition is in the required pH range. Alternatively, the components in one container may be in dry form while the component in the other container are in the form of an aqueous dispersion. Other two-container combinations of the ingredients of the CMP slurry of this invention are within the knowledge of one having ordinary skill in the area.
At the requisite pH, the compositions and slurries of the present invention do not significantly increase the silicon nitride removal rate. However, the composition and slurry of this invention significantly increases the removal rate of silicon dioxide in comparison to known slurries. The polishing slurry of the present invention may be used during the various stages of semiconductor integrated circuit manufacture to provide effective removal of silicon oxide layers at desired removal rates while minimizing surface imperfections and defects.
EXAMPLE 1
The following examples illustrate preferred embodiments of this invention as well as preferred methods for using compositions of this invention. All compositions and slurries were used in an STI polishing protocol as outlined below.
The CMP slurries were used to chemically-mechanically polish blanket PETEOS and silicon nitride using a IC1000/SUBA IV pad stack manufactured by Rodel, Inc. The polishing was performed using an IPEC/WESTECH 472 CMP tool at a down force of 9 psi, a slurry flow rate of 140 ml/min., a platen speed of 35 rpm and a carrier speed of 24 rpm.
EXAMPLE 2
Pulverized Ceria Formulations
A pulverized ceria slurry was prepared in order to evaluate its ability to polish blanket silicon dioxide and nitride wafers. Rhodite grade 400HS ceria, having particle sizes approximately 2-4 .mu.m was purchased from Universal Photonics, Hicksville, N.Y. and pulverized using an agitator bead mill to a primary median particle size of 150 nm. Pulverizing was accomplish under wet conditions so that the resulting slurry, pH approximately 7.5-8.5, contained 20-30% solids after the pulverizing process.
The slurry was then diluted and the pH adjusted to produce the slurries listed in Table 1. The slurries were used to polish a substrate according to the methods described in Example 1.
TABLE 1______________________________________ PETEOS RR Nitride RRSlurry No. pH % solids (.ANG./min) (.ANG./min) Selectivity______________________________________1 8 4.0 925 1050 0.892 8 5.0 4337 1137 3.813 8 7.5 4800 1130 4.254 8 10.0 5145 1153 4.465 10 4.0 4342 1101 3.956 10 10.0 4344 1015 4.28______________________________________
The pulverized ceria slurries were used for polishing The data indicates that the pulverized ceria slurries yield very high PETEOS (silicon oxide layer) removal rates.
EXAMPLE 3
Precipitated Ceria Nitrate Formulations
A nitrate stabilized ceria slurry containing precipitated ceria particles, nitric acid, acetic acid, pH=1.8 and 20% solids, was purchased from Nyacol Products (Ashland, Mass.). The pH of the slurry was adjusted to from about 4.2-6.8 by adding ammonium hydroxide. The slurries were used to polish substrates according to the method described in Example 1. The polishing results are reported in Table 2.
TABLE 2______________________________________Slurry % PETEOS NitrideNo. pH solids Additives RR RR Selectivity______________________________________7 4.2 20 406 14.5 288 5.8 20 281 208 1.359 6.1 20 241 281 0.8610 6.2 20 163 354 0.46______________________________________
The polishing data indicates that at the lowest pH (4.2) selectivity is high, but overall oxide removal rates are low.
EXAMPLE 4
Precipitated Ceria Acetate Formulations
A ceria acetate slurry, containing ceria particles and acetic acid, pH=1.8 and 20% solids, was purchased from Nyacol Products (Ashland, Mass.). The pH of the slurry was adjusted to 4.5 and the solids content to 15%. The slurry was applied to substrate according to the methods described in Example 1 and the result showed an oxide layer removal rate of 117 .ANG./min and a nitride layer removal rate of 10.5 .ANG./min for an oxide to nitride selectivity of 11.1.
EXAMPLE 5
Crushed/Precipitated Ceria Formulations
A ceria slurry, composed of varying weight percent amounts of the pulverized ceria manufactured as set forth in Example 2 and precipitated ceria purchased from Nyacol Products (Ashland, Mass.) was formulated as shown in Table 3. The slurries were used to polish substrates according to the methods described in Example 1 and the polishing results are set forth in Table 3, below.
TABLE 3______________________________________ PETEOS NitrideSlurry % total % pulverized RR RRNo. pH solids ceria in slurry (.ANG./min) (.ANG./min) Selectivity______________________________________11 4 8 20 1595 108.4 14.7112 4 8 40 2168 183.4 11.8213 4 8 60 3356 826.5 4.0614 4 8 80 4785 209.1 22.88______________________________________
The results indicate that a CMP slurry including 80% pulverized ceria and 20% precipitated ceria produced the most desired properties of high PETEOS rates, low nitride rates and high selectivity.
EXAMPLE 6
Chemical Formulation Using Pulverized Ceria
A slurry, composed of L-90, a fumed silica particles manufactured by Cabot Corporation and sold under the trademark CAB-O-SIL.RTM., ammonium cerium nitrate, acetic acid, of varying percentages, and deionized water was formulated as shown in Table 4. All slurries were adjusted to pH=4 after the inclusion of additives. The slurries were applied to substrate according to the methods described in Example 1.
TABLE 4______________________________________ weight weight % Amm. % Nitride PETEOS weight % Cerium Acetic RR RR Selec-Slurry silica Nitrate Acid (.ANG./min) (.ANG./min) tivity______________________________________20 4 0.1 0.1 58 280 4.8321 4 0.1 1 52 253 4.8722 4 0.65 0.5 59 619 10.4923 4 1 0.1 44 1535 34.8924 4 1 1 312 1524 4.8825 4 1 0 104.62 1337.9 12.7926 4 2 0.05 57.51 1103 19.1827 4 3 0.1 89.99 835.8 9.2928 4 1 0.5 71.5 803.1 11.2329 4 2 0.1 24.1 346.6 14.3830 4 2 0.5 71.1 768.0 10.8______________________________________
High PETEOS removal rates and low nitride removal rates were obtained with high nitrate (1% nitrate) content and low (0.1%) acetic acid content.
EXAMPLE 7
Chemical Formulation Using Silica--pH Test
A slurry, composed of 4 weight percent CAB-O-SIL.RTM. L-90 fumed silica, 1.8 weight percent ammonium cerium nitrate, and 0.6 weight percent acetic acid of varying percentages was formulated as shown in Table 5. The pH of the slurries varied from between 4.0 to 5.0. The slurries were applied to substrate according to the methods described in Example 1.
TABLE 5______________________________________ weight weight % Acetic PETEOSSlurry % silica pH Acid Nitride RR RR Selectivity______________________________________31 4 4.0 0.6 114 1713.7 15.0332 4 4.3 0.6 141 1988.9 14.1133 4 4.7 0.6 199 2810.5 14.1234 4 5.0 0.6 219 2355 10.75______________________________________
High PETEOS removal rates are obtained and selectivity was very good for each slurry. The results indicate that slurry pH has a strong effect on PETEOS removal rate and the optimum removal rate of oxide is achieved at about pH 4.7 (FIG. 1).
While the present invention has been described by means of specific embodiments, it will be understood that modifications may be made without departing from the spirit of the invention. The scope of the invention is not considered to be limited by the description of the invention set forth in the specification and examples, but rather defined by the following claims.
EXAMPLE 8
A composition composed of 1.8 wt % ammonium cerium nitrate, 0.8 wt % acetic acid, and deionized water was used to polish PETEOS and silicon nitride wafers according to the method of Example 1. The pH of the slurry was adjusted to 4.5. The composition polished PETEOS at 690 .ANG./min and silicon nitride at 23 .ANG./min, giving a PETEOS selectivity of 30.
Claims
  • 1. An aqueous chemical mechanical polishing composition comprising:
  • a salt;
  • soluble cerium; and
  • a carboxylic acid, wherein the composition has a pH of from about 3 to about 11.
  • 2. The aqueous chemical mechanical polishing composition of claim 1, wherein the pH is from about 3.8 to about 5.5.
  • 3. The aqueous chemical mechanical polishing composition of claim 1, wherein the salt is a nitrate salt.
  • 4. The aqueous chemical mechanical polishing composition of claim 3, wherein the nitrate salt is a compound having the formula:
  • (M).sub.n (NO.sub.3).sub.m
  • wherein n and m are both integers and wherein when n=m, M is an alkali earth metal, H, NH.sub.4 or NR.sub.4 where R is an alkyl group having from 1 to 10 carbon atoms and wherein when n.noteq.m, M is a multivalent cation or metal or a combination of multivalent cations and monovalent cations.
  • 5. The aqueous chemical mechanical polishing composition of claim 3, including from about 0.05 to about 6.0 weight percent nitrate salt.
  • 6. The aqueous chemical mechanical polishing composition of claim 3, wherein the nitrate salt is ammonium cerium nitrate.
  • 7. The aqueous chemical mechanical polishing composition of claim 1, wherein the carboxylic acid is selected from the group consisting of monofunctional acids, di-functional acids and salts thereof.
  • 8. The aqueous chemical mechanical polishing composition of claim 1, wherein the carboxylic acid is at least one compound selected from the group consisting of acetic acid, adipic acid, butyric acid, capric acid, caproic acid, caprylic acid, citric acid, glucaric acid, glycolic acid, formic acid, fumaric acid, lactic acid, lauric acid, malic acid, maleic acid, malonic acid, myristic acid, oxalic acid, palmitic acid, phthalic acid, propionic acid, pyruvic acid, stearic acid, succinc acid, tartaric acid, valeric acid, 2-(2-methoxyethoxy) acetic acid, 2-�2-(2-methoxyethoxy)ethoxy! acetic acid and poly(ethylene glycol)bis (carboxymethyl)ether and mixtures thereof.
  • 9. The aqueous chemical mechanical polishing composition of claim 1, wherein the carboxylic acid is acetic acid.
  • 10. The aqueous chemical mechanical polishing composition of claim 1 including from about 0.05 to about 10.0 weight percent carboxylic acid.
  • 11. The aqueous chemical mechanical polishing composition of claim 10, including from about 0.1 to about 3.0 weight percent carboxylic acid.
  • 12. The aqueous chemical mechanical polishing composition of claim 1, including from about 0.05 to about 10 weight percent soluble cerium.
  • 13. The aqueous chemical mechanical polishing composition of claim 1, wherein the soluble cerium is at least one compound selected from the group consisting of ammonium cerium sulfate, cerium acetate, cerium sulfate hydrate, cerium hydroxide, cerium bromate, cerium bromide, cerium chloride, cerium oxalate, cerium nitrate, cerium carbonate and mixtures thereof.
  • 14. The aqueous chemical mechanical polishing composition of claim 1, wherein the salt and the soluble cerium are ammonium cerium nitrate.
  • 15. The aqueous chemical mechanical polishing composition of claim 14, including from about 0.1 to about 4.0 weight percent ammonium cerium nitrate.
  • 16. A chemical mechanical polishing slurry comprising:
  • a salt;
  • soluble cerium;
  • a carboxylic acid; and
  • an abrasive, wherein the composition has a pH of from about 3 to about 11.
  • 17. The chemical mechanical polishing slurry of claim 16, including from about 1 to about 25 weight percent abrasive.
  • 18. The chemical mechanical polishing slurry of claim 16, wherein the abrasive is a metal oxide.
  • 19. The chemical mechanical polishing slurry of claim 18, wherein the metal oxide abrasive is at least one compound selected from the group consisting of including alumina, titania, zirconia, germania, silica, ceria or mixture and chemical admixtures thereof.
  • 20. The chemical mechanical polishing slurry of claim 19, wherein the abrasive is a physical mixture of at least two elemental oxides selected from the group consisting of alumina, titania, zirconia, germania, silica, ceria.
  • 21. The chemical mechanical polishing slurry of claim 16, wherein the abrasive is milled or ground.
  • 22. The chemical mechanical polishing slurry of claim 17, including from about 2 to about 15 weight percent metal oxide abrasive.
  • 23. The aqueous chemical mechanical polishing slurry of claim 17, comprising from about 0.5 to about 10 weight percent nitrate salt, from about 0.5 to about 10 weight percent carboxylic acid and from about 0.5 to about 10 percent soluble cerium.
  • 24. The aqueous chemical mechanical polishing slurry of claim 17 comprising from about 0.1 to about 3.0 weight percent acetic acid, and from about 0.1 to about 4.0 weight percent ammonium cerium nitrate wherein the slurry has a pH of from about 3.8 to about 5.5.
  • 25. A chemical mechanical polishing slurry comprising from about 2 to about 15 weight percent metal oxide abrasive, from about 0.5 to about 10 weight percent nitrate salt, from about 0.5 to about 10 weight percent carboxylic acid and from about 0.5 to about 10 percent soluble cerium, wherein the slurry has a pH of from about 3 to about 11.
  • 26. The chemical mechanical polishing slurry of claim 25 comprising from about 0.1 to about 3.0 weight percent acetic acid, from about 0.1 to about 4.0 weight percent ammonium cerium nitrate, and from about 1.0 to about 15 percent fumed silica, wherein the slurry has a pH from about 3.8 to about 5.5.
  • 27. The chemical mechanical polishing slurry of claim 25 comprising from about 0.1 to about 3.0 weight percent acetic acid, from about 0.1 to about 4.0 weight percent ammonium cerium nitrate, and from about 1.0 to about 15 percent milled or ground ceria, wherein the slurry has a pH from about 3.8 to about 5.5.
  • 28. A method for removing at least a portion of a silicon dioxide layer from a substrate comprising:
  • mixing a salt, a soluble cerium compound, a carboxylic acid, and de-ionized water to form a chemical mechanical polishing composition having a pH of from about 3.0 to about 11.0;
  • applying the chemical mechanical polishing composition to the substrate; and
  • removing at least a portion of the silicon dioxide layer from the substrate by bringing a pad into contact with the substrate and moving the pad in relation to the substrate.
  • 29. The method of claim 28, wherein the substrate is a layered substrate comprising at least one layer of silicon dioxide and at least one layer of silicon nitride.
  • 30. The method of claim 29, wherein the silicon dioxide is removed at a rate at least five-fold greater than the removal rate of silicon nitride.
  • 31. The method of claim 28, wherein the carboxylic acid is acetic acid.
  • 32. The method of claim 28, wherein the salt and soluble cerium compound are ammonium cerium nitrate.
  • 33. The method of claim 28, further including at least one metal oxide abrasive selected from the group consisting of including alumina, titania, zirconia, germania, silica, ceria and mixtures thereof.
  • 34. The method of claim 33, wherein the metal oxide abrasive is silica.
  • 35. A method for removing at least a portion of a silicon dioxide layer from a silicon wafer, said silicon wafer including a silicon nitride layer, said method comprising:
  • mixing from about 2 to about 15 weight percent silica, from about 0.1 to about 4.0 weight percent ammonium cerium nitrate, from about 0.1 to about 3.0 weight percent of acetic acid and de-ionized water to form a chemical mechanical polishing slurry having a pH of between about 3.8 to about 5.5;
  • applying the chemical mechanical polishing slurry to a pad;
  • rotating the pad; and
  • removing at least a portion of the silicon dioxide layer by bringing the rotating pad into contact with the wafer and rotating the wafer in relation to the rotating pad.
US Referenced Citations (11)
Number Name Date Kind
4752628 Payne Jun 1988
4867757 Payne Sep 1989
4944836 Beyer et al. Jul 1990
5244534 Yu et al. Sep 1993
5264010 Brancaleoni et al. Nov 1993
5340370 Cadien et al. Aug 1994
5354490 Yu et al. Oct 1994
5382272 Cook et al. Jan 1995
5389352 Wang Feb 1995
5391258 Brancaleoni et al. Feb 1995
5480476 Cook et al. Jan 1996
Non-Patent Literature Citations (1)
Entry
NYACOI Colloidal Ceria Nitrate MSDS (Oct. 17, 1994).