The present disclosure relates generally to the field of semiconductor technology. More particularly, the present disclosure relates to a connection structure between the semiconductor structure and the carrier and a method for forming the same.
As known in the art, semiconductor structures such as surface acoustic wave (SAW) devices are frequently used in commercial applications as radio frequency (RF) and intermediate frequency (IF) filters to provide frequency selectivity and other electronic functions. It is also known that during assembly process, bumps of the semiconductor structure are typically attached to pads on a carrier using a solder. However, the flux splashing that occurs in a solder reflow process often leads to undesired contamination of the bottom surface of the semiconductor structure.
Therefore, there is a need in this industry to provide an improved method for forming a connection structure between the semiconductor structure and the carrier, which is capable of solving the above-mentioned prior art problems and shortcomings.
It is one object of the present disclosure to provide an improved method for forming a connection structure, which can avoid the above-mentioned prior art shortcomings.
According to one aspect of the invention, a method for forming a connection structure is disclosed. A semiconductor structure having a first pad and a bump respectively on a bottom surface thereof is provided. A carrier having a second pad on a top surface thereof is provided. The second pad corresponds to the bump. An epoxy portion is disposed onto the second pad of the carrier. A diameter of the epoxy portion is less than or equal to a diameter of the bump. After depositing the epoxy portion, the bump is attached to the second pad via the epoxy portion.
According to another aspect of the present invention, a connection structure is disclosed. The connection structure comprises a semiconductor structure having a first pad and a bump respectively on a bottom surface thereof, a carrier having a second pad on a top surface thereof, and an epoxy portion connected between the bump and the second pad. The second pad corresponds to the bump. According to one embodiment of the invention, a diameter of the epoxy portion is less than a diameter of the bump.
These and other objectives of the present invention will no doubt become obvious to those of ordinary skill in the art after reading the following detailed description of the preferred embodiment that is illustrated in the various figures and drawings.
The accompanying drawings are included to provide a further understanding of the embodiments, and are incorporated in and constitute a part of this specification. The drawings illustrate some of the embodiments and, together with the description, serve to explain their principles. In the drawings:
Below, exemplary embodiments will be described in detail with reference to accompanying drawings so as to be easily realized by a person having ordinary knowledge in the art. The inventive concept may be embodied in various forms without being limited to the exemplary embodiments set forth herein. Descriptions of well-known parts are omitted for clarity, and like reference numerals refer to like elements throughout.
The following detailed description is, therefore, not to be taken in a limiting sense, and the scope of the present invention is defined only by the appended claims, along with the full scope of equivalents to which such claims are entitled.
It is noted that references in the specification to “one embodiment,” “an embodiment,” “an exemplary embodiment,” “some embodiments,” etc., indicate that the embodiment described may include a particular feature, structure, or characteristic, but every embodiment may not necessarily include the particular feature, structure, or characteristic. Moreover, such phrases do not necessarily refer to the same embodiment.
Further, when a particular feature, structure or characteristic is described in contact with an embodiment, it would be within the knowledge of a person skilled in the pertinent art to affect such feature, structure or characteristic in contact with other embodiments whether or not explicitly described.
The terms wafer and substrate used herein include any structure having an exposed surface onto which a material layer is deposited, for example, to form a circuit structure including, but not limited to, an interconnection metal line or a redistribution layer (RDL). The term substrate is understood to include wafers, but not limited thereto. The term substrate is also used to refer to semiconductor structures during processing, and may include other layers that have been fabricated thereupon.
The present disclosure pertains to a connection structure and a method for forming the same. By applying an electrically conductive epoxy portion on the pads of the carrier during assembly process of the semiconductor structure, the problem of contamination of the bottom surface of the semiconductor structure could be avoided.
Although not shown in the figures, it is known that an IDT may be a series of thin metal strips or “fingers” fabricated on a suitable piezoelectric substrate. One set of fingers is connected to an input/output terminal, while the opposite set of fingers is connected to a second terminal. In single-ended IDTs, the second terminal is grounded. For differential input signals however, the second terminal is a pulse input/output terminal.
Still referring to
According to one embodiment, an epoxy portion 204 is disposed onto the second pad 202 of the carrier 20. According to one embodiment, the epoxy portion 204 may be deposited onto the second pad 202 by stencil printing or any suitable methods known in the art.
According to one embodiment, a diameter d2 of the epoxy portion 204 is less than or equal to the diameter d1 of the bump 104. According to one embodiment, the epoxy portion 204 is electrically conductive. For example, the epoxy portion 204 comprises silver and epoxy resin, but is not limited thereto.
As shown in
According to one embodiment, the epoxy portion 204 may have a viscosity of less than 12000 cps at room temperature before attaching the bump 104 to the second pad 202. According to one embodiment, the epoxy portion 204 may have a viscosity of greater than 8000 cps at room temperature before attaching the bump 104 to the second pad 202. Preferably, the viscosity of the epoxy portion 204 is chosen to be less than 12000 cps (for example, at 25° C.) before the bump 104 is attached to the second pad 202, thus the undesirable adhesion is reduced in the assembly process. In addition, when the curing processing is performed by heating the epoxy portion 204, the epoxy portion 204 is hardly to be deformed because of the chosen viscosity range, therefore, the epoxy portion 204 is hardly contacting the bottom surface 10b of the semiconductor structure 10, and the risk of the semiconductor structure-surface contamination is reduced.
According to one embodiment, the epoxy portion 204 may have a resistivity of less than 5×10−5ohm-cm3 for providing the better electric conductivity and reducing the influence on the performance of the semiconductor structure 10. According to one embodiment, the epoxy portion 204 may have a thickness ranging between 0.03 mm and 0.07 mm before attaching the bump 104 to the second pad 202. According to one embodiment, the diameter d3 of the epoxy portion 204 is less than or equal to the diameter d1 of the bump 104 after attaching the bump 104 to the second pad 202.
According to one embodiment, a height h between the bottom surface 10b of the semiconductor structure 10 and the top surface 20a of the carrier 20 is more than 10 μm after attaching the bump 104 to the second pad 202. By providing such configuration, the influence on the performance of the semiconductor structure 10 is reduced. According to one embodiment, the bump 104 is not in physical contact with the second pad 202.
As shown in
It is advantageous to use the present disclosure because by applying the epoxy portion 204, a conventional solder reflow process can be omitted. Therefore, the risk of contaminating the bottom surface 10b of the semiconductor structure 10 is reduced. By controlling the diameter and the thickness of the epoxy portion 204, the contacting area between the epoxy portion 204 and the side edge of the bump 104 can be reduced, which may reduce the risk that the epoxy portion 204 contacts the bottom surface 10b of the semiconductor structure 10 via the side edge of the bump 104. By selecting suitable viscosity of the epoxy portion 204, the undesirable adhesion is reduced in the assembly process and the risk of the semiconductor structure-surface contamination is reduced. By selecting suitable resistance of the epoxy portion 204, the influence on the performance of the semiconductor structure 10 is reduced. Further, because an adequate height h between the bottom surface 10b of the semiconductor structure 10 and the top surface 20a of the carrier 20 can be maintained, the influence on the performance of the semiconductor structure 10 is reduced. Therefore, the method as disclosed can significantly improve the reliability of the assembly of the SAW chip on the carrier.
According to one embodiment, the semiconductor structure 10 may comprise a wafer or a SAW chip. According to one embodiment, the carrier 20 may comprise a HTCC substrate, a LTCC substrate, a silicon substrate, or a PCB. According to one embodiment, the bump is a gold bump. According to one embodiment, the second pad 202 is a metal pad comprising gold, copper, aluminum, titanium, titanium nitride, silver or any combinations thereof.
According to one embodiment, the epoxy portion is electrically conductive. According to one embodiment, the epoxy portion 204 may comprise silver and epoxy resin. According to one embodiment, the epoxy portion 204 may have a resistivity of less than 5×10−5 ohm-cm3. According to one embodiment, a height h between the bottom surface 10b of the semiconductor structure 10 and the top surface 20a of the carrier 20 is more than 10 μm.
According to one embodiment, the connection structure 1 may further comprise a dry film 30 laminated on the semiconductor structure 10 and the top surface 20a of the carrier 20. According to one embodiment, the dry film 30 may comprise an epoxy resin film. The circuit element 101 of the semiconductor structure 10 is located within a cavity 50 sealed between the dry film 30, the bottom surface 10b of the semiconductor structure 10 and the top surface 20a of the carrier 20.
Please refer to
Those skilled in the art will readily observe that numerous modifications and alterations of the device and method may be made while retaining the teachings of the invention. Accordingly, the above disclosure should be construed as limited only by the metes and bounds of the appended claims.
This application claims priority from U.S. provisional application No. 62/751,690 filed Oct. 28, 2018, which is included in its entirety herein by reference.