Copolymers for optical fibers

Abstract

A copolymer for optical fibers of fluoroalkylmethacrylate and methacrylic acid, the fluoroalkylmethacrylate having such properties that a homopolymer made of only the fluoroalkylmethacrylate has a glass transition temperature and a refractive index each in the range given by the following formulae (I) and (II), respectively:(1/Tg).ltoreq.9.47.times.10.sup.-3 -4.556.times.10.sup.-3 n.sup.20 (I)n.sup.20 .ltoreq.1.42 (II)wherein Tg represents the glass transition temperature (.degree.K.) of the homopolymer and n.sup.20 represents the refractive index thereof.

Description

This invention relates to fluoroalkylmethacrylate copolymers which are useful as cladding materials in manufacturing fibers for light transmission thereinafter referred to as optical fibers).

Heretofore used as core materials for optical fibers are glass, polystyrene, polymethylmethacrylate and the like which have excellent light-transmitting property. Cladding materials for optical fibers must be low in refractive index and outstanding in transparency, elasticity, adhesiveness to core materials and heat resistibility.

It has been proposed to use as cladding materials a variety of fluorine-containing resins because of their low refractive index. For example, Japanese Examined Patent Publication No. 8978/1968 discloses optical fibers comprising an alkylmethacrylate polymer as a core material and a fluoroalkymethyacrylate or fluoroalkylacrylate homopolymer or fluoroalkylmethacrylate-fluoroalkylacrylate copolymer as a cladding material, the homopolymer or copolymer being obtained by polymerization of a monomer represented by the formula ##STR1## wherein X represents hydrogen, fluorine or chlorine, n is an integer of 2 to 10, m is an integer of 1 to 6, and Y represents hydrogen or methyl. However, it has been found that the foregoing homopolymer or copolymer is not sufficient in any of heat resistibility and adhesiveness to core materials. In shaping fibers, such polymer decomposes and foams at a temperature of about 220.degree. to 240.degree. C., thereby forming bubbles in the cladding. Further, the polymer renders it difficult to obtain optical fibers involving a small loss of light energy because its poor adhesiveness to core materials causes light scattering at the interface between the core and cladding. In recent years, attention has been focussed on the use of optical fibers of plastics materials in the manufacture of terminal equipment for optical communication, since the optical fibers of plastics materials are inexpensive to manufacture and can be mass produced. But the optical fibers of plastics materials heretofore known involve a great loss of light energy and thus are not suited to production of the terminal equipment. In the present situation, there is a demand for optical fibers of plastics materials entailing a small loss of light.

It is an object of the present invention to provide copolymers for optical fibers.

It is another object of the invention to provide copolymers suitable as cladding materials for optical fibers.

It is a further object of the invention to provide cladding materials of plastics for optical fibers which involve an extremely small loss of light energy.

It is a still further object of the invention to provide cladding materials for optical fibers which materials have excellent adhesiveness to the core materials and high heat resistibility.

Other objects and features of the present invention will become apparent from the following description.

We conducted extensive research to develop cladding materials which retain the low refractive index and good transparency of polyfluoroalkylmethacrylate and which have high heat resistibility and excellent adhesiveness to the core material, and found that a copolymer comprising fluoroalkylmethacrylate having specific polymeric characteristics and methacrylic acid is excellent in heat resistibility and in adhesiveness to the core and possesses remarkable properties required for optical fibers such as a low refractive index and a high glass transition temperature, hence suitable as cladding materials for optical fibers. This novel finding has matured to the present invention.

This invention provides a copolymer of fluoroalkylmethacrylate and methacrylic acid, the fluoroalkylmethacrylate having such properties that a homopolymer of the fluoroalkylmethacrylate has a glass transition temperature and a refractive index each in the range given by the following formulae (I) and (II), respectively:

(1/Tg).ltoreq.9.47.times.10.sup.-3 -4.556.times.10.sup.-3 n.sup.20 (I) n.sup.20 .ltoreq.1.42 (II) wherein Tg represents the glass transition temperature (.degree. K.) of the homopolymer and n.sup.20 represents the refractive index of the homopolymer.

Typical examples of fluoroalkylmethacrylate the homopolymer of which have the glass transition temperature of the formula (I) and the refractive index of the formula (II) are trifluoroethylmethacrylate (Tg=73.degree. C., n.sup.20 =1.4107, the two values being shown hereinafter in this order), 2,2,3,3-tetrafluoropropylmethacrylate (75.degree. C., 1.4200), 2,2,3,3,3-pentafluoropropylmethacrylate (72.degree. C., 1.395), 2-trifluoromethyl-3,3,3-trifluoropropylmethacrylate (75.degree. C., 1.3922), 2-trifluoromethyl-2,3,3,3-tetrafluoropropylmethacrylate (79.degree. C., 1.3800), 2,2,3,4,4,4-hexafluorobutylmethacrylate (50.degree. C., 1.4010), 1-methyl-2,2,3,4,4,4-hexafluorobutylmethacrylate (65.degree. C., 1.4005), 1,1,2,2-tetrahydroperfluorodecylmethacrylate (89.5.degree. C., 1.3672), 1,1,2,2-tetrahydro-9-trifluoromethylperfluorodecylmethacrylate (81.5.degree. C., 1.3650), 1,1-dihydroperfluorobutylmethacrylate (56.degree. C., 1.3900), 1,1-dimethyl-2,2,3,3-tetrafluoropropylmethacrylate (93.degree. C., 1.4200), 1,1-dimethyl-2,2,3,3,4,4,5,5-octafluoropentylmethacrylate (65.degree. C., 1.3988), 1,1-dimethyl-2,2,3,4,4,4-hexafluorobutylmethacrylate (83.degree. C., 1.4008), etc.

With this invention, other monomers can be incorporated as components in the present copolymer to adjust the numerical aperture required for a specific use, because the numerical aperture depends on the both values of refractive indexes of the core and cladding. Usable as such additional monomers are any suitable compounds which do not impair the properties required of cladding materials for optical fibers such as a refractive index and glass transition temperature. Preferable of these monomers is methacrylic acid ester, particularly methyl methacrylate. The amount of such monomers to be used is not particularly limited, unless the required properties for the cladding materials are deteriorated. Usually the amount thereof is less than 30% by weight relative to the weight of the fluoroalkylmethacrylate.

According to the present invention, the methacrylic acid to be copolymerized with the fluoroalkylmethacrylate is used to improve the adhesiveness to the core and the heat resistibility. The amount of the methacrylic acid to be used is 0.5 to 10% by weight, preferably 1 to 77% by weight, based on the weight of the fluoroalkylmethacrylate. The acrylic acid content of less than 0.5% by weight fails to enhance the adhesiveness and heat resistibility. With its amount in excess of 10% by weiht, cross linking is likely to occur at a temperature of 220.degree. to 240.degree. C. during the shaping operation.

The copolymer of the present invention for use as cladding materials is prepared by the conventional polymerization methods among which solution polymerization and bulk polymerization are preferably conducted to reduce the amount of impurities to be contained in the copolymer.

Suitable polymerization initiators useful in preparing copolymers for cladding materials by solution, suspension or bulk polymerization method are organic peroxides among which it is preferred to use isobutyrylperoxide, octanoylperoxide, di-i-propylperoxydicarbonate, [Cl(CF.sub.2 CFCl).sub.2 CF.sub.2 COO], [H(CF.sub.2 CF.sub.2).sub.3 COO].sub.2 and (ClCF.sub.2 CF.sub.2 COO).sub.2. The emulsion polymerization method employs persulfate as an oxidizing agent such as ammonium persulfate, potassium persulfate, etc.; sodium sulfite or the like as a reducing agent; salts of iron (II) sulfate or like transition metals as a redox initiator.

Solvents which can be used in preparing the present copolymer by solution or suspension method include fluorine-containing solvents such as CCl.sub.2 F.sub.2, CCl.sub.2 FCClF.sub.2, CClF.sub.2 CClF, ##STR2##

The polymerization temperature is usually 0.degree. to 100.degree. C. and preferably 10.degree. to 80.degree. C., although it can be determined according to the decomposition temperature of the polymerization initiator. The reaction pressure is usually between 1 and 50 kg/cm.sup.2 G.

The cladding materials of the present invention can be used conjointly with any of suitable known core materials for optical fibers. The process for assembling optical fibers from the cladding material of the present invention and the conventional core material is not particularly limitative but can be appropriately adopted from known methods.

Since the present cladding materials for optical fibers are excellent in adhesiveness to the core, the materials do not cause the reduction in the amount of light transferred which is attributable to light scattering at the interface between the core and cladding due to a poor adhesiveness to the core. Moreover, the present cladding materials have an outstanding transparency, elasticity and heat resistibility in addition to the foregoing properties.

The present invention will be described below in greater detail with reference to the following examples and comparison examples in which all parts and percentages are by weight unless otherwise specified.

EXAMPLE 1

Into an autoclave were placed 95 parts of 2,2,3,3,3-pentafluoropropylmethacrylate and 5 parts of methacrylic acid, and 0.025 part of azobisisobutyronitrile and 0.05 part of n-dodecylmercaptan were added after which bulk polymerization was conducted at 70.degree. C. and completed in about 7 hours. The copolymer thus otained was dried at 130.degree. C. for 13 hours by a vacuum drying apparatus. The dried copolymer amounted to 93 parts and was found to have a refractive index of 1.400, a softening point of 81.degree. C. and a melt viscosity of 8.times.10.sup.-3 poise at 220.degree. C.

A composite filament having a diameter of 400.mu. and a cladding thickness of 20.mu. was formed by extrusion at 230.degree. C. through a spinning head by using polymethylmethacrylate as a core material and the copolymer obtained above as a cladding material.

The filament was 81%/50 cm in light transmission ratio. A 60 cm length of the filament was subjected to a bending test in which one end of the filament was attached to a fixed terminal of a bending tester and the other end to a movable terminal thereof disposed at a spacing of 5 cm from the fixed terminal. The movable terminal was reciprocated between the distance of 5-55 cm from the fixed terminal. The light transmission ratio of the filament was measured after 1000 times repetition of the bending test and was found to be 80%/50 cm which was a similar value of the ratio before the test.

EXAMPLES 2 TO 10

Nine kinds of copolymers made of monomers listed in Table 1 below were prepared by the same polymerization method as in Example 1. Polymethylmethacrylate was used as a core material and each copolymer as a cladding material. Composite filaments were produced in the same manner as in Example 1 and subjected to the bending test.

Table 1 shows monomer ratios used in preparation of copolymers, the glass transition temperatures and the refractive indexes of copolymers, the light transmission ratios (%/50 cm) of the filaments before and after the bending test, and the glass transition temperatures and the refractive indexes of fluoroalkylmethacrylate homopolymers.

TABLE 1__________________________________________________________________________ Properties of homopolymer of Properties Light transmission fluoroalkyl-Monomer of ratio of filament methacrylateFluoroalkyl- Methyl Methacrylic copolymer % alone methacrylate methacrylate acid Tg Before** After** TgExample monomer % % % n.sup.20 (.degree.C.) test test (.degree.C.) n.sup.20__________________________________________________________________________2 4F.sub.1 M 99 0 1 1.420 76 76 75 75 1.42003 3FE 95 0 5 1.415 76 73 72 73 1.41074 6FM 75 21 4 1.420 70 75 74 50 1.40105 6FE 80 16 4 1.418 70 72 73 65 1.40056 i6FC 72 25 3 1.420 83 77 75 75 1.39227 i7FC 70 26 4 1.416 87 74 73 79 1.38008 17F 65 29 6 1.415 76 75 75 89.5 1.36729 7F 73 23 4 1.420 74 74 74 56 1.390010 4F.sub.2 iP 80 19 1 1.419 72 75 72 65 1.3988__________________________________________________________________________ *Details of monomers are shown later. **Bending test

COMPARISON EXAMPLES 1 TO 5

Five kinds of copolymers were prepared by the same polymerization method as in Example 1 using monomers listed in Table 2 given below. Composite filaments were formed in the same manner as in Example 1 by using polymethylmethacrylate as a core material and each copolymer obtained above as a cladding material. The filaments were subjected to the bending test.

Table 3 below shows the properties of fluoroalkylmethacrylate homopolymer and copolymers and the light transmission ratio of the filaments before and after the bending test.

In Table 1 and 3, Tg was obtained by measuring heat absorption with use of DSC II Model, while increasing the temperature at a rate of 10.degree. C./mini; the refractive index was measured by using D line of sodium at 20.degree. C. with use of Abbe refractometer; and the light transmission ratio of the filaments was measured according to ASTM D 1003 (1961).

TABLE 2______________________________________MonomerCom- Fluoroalkyl- Methyl Methacrylicparison Mono- methacrylate methacrylate acidExample mer % % %______________________________________1 17F 65 35 02 17F 65 20 153 17F 65 29 6 (Butyl acrylate)4 i7FN.sub.2 42 52 65 i7FN.sub.2 61 36 3______________________________________ TABLE 3__________________________________________________________________________ Properties of homopolymer of Light transmission fluoroalkyl- ratio of filament methacrylateMonomer (%) aloneComp. Tg Before* After* TgExample n.sup.20 (.degree.C.) test test n.sup.20 (.degree.C.) Remarks__________________________________________________________________________1 1.413 76 38 >30 1.3672 89.5 The copolymer foamed in extrusion. -2 1.420 76 -- -- 1.3672 89.5 T he copolymer had light color and cross linking occurred, hindering fiberization. -3 1.415 62 73 36 1.3 672 89.5 The copolymer foamed in extrusion.4 1.445 70 53 51 1.3700 305 1.420 56 71 45 1.3700 30 The cladding material had a low Tg value and a poor bending resistance.__________________________________________________________________________ *Bending test Note: The monomers of fluoroalkylmethacrylate shown in Tables 1 and 2 refer to compounds represented by the formula ##STR3##- - wherein R is as indicated below Monomer R4F.sub.1 M CH.sub.2 CF.sub.2 CF.sub.2 H3FE CH.sub.2 CF.sub.36FM CH.sub.2 CF.sub.2 CFHCF.sub.36FE ##STR4##i6FC ##STR5##i7FC ##STR6##17F CH.sub.2 CH.sub.2 C.sub.8 F.sub.177F CH.sub.2 CF.sub.2 CF.sub.2 CF.sub.34F.sub.2 iP ##STR7##i7FN.sub.2 ##STR8##

Claims

1. In an optical fiber comprising a cladding and a core, the improvement wherein said cladding comprises a copolymer comprising

(a) 100 parts by weight of fluoroalkylmethacrylate, said fluoroalkylmethacrylate giving, when singly polymerized, a homopolymer having the properties of a glass transition temperature and a refractive index satisfying the following formulae (I) and (II), respectively:

(1/Tg.ltoreq.9.47.times.10.sup.-3 -4.556.times.10.sup.-3 .times.n.sup.20 (I)

n.sup.20 .ltoreq.1.42 (II)

wherein Tg represents the glass transition temperature and n.sup.20 represents the refractive index of said homopolymer and

(b) 0.5 to 10 parts by weight of methacrylic acid.