1. Field of the Invention
The present invention relates to a magnetoresistive (MR) element utilizing a magnetoresistive (MR) film such as a spin valve film, a tunnel-junction film, and the like. In particular, the invention relates to a current-perpendicular-to-the-plane (CPP) structure magnetoresistive element allowing a sensing current to have a component perpendicular to the surface of a substratum receiving a magnetoresistive film.
2. Description of the Prior Art
A conventional CPP structure magnetoresistive element often includes a magnetoresistive film such as a spin valve film overlaid on the surface of a substratum. The spin valve film is interposed between a pair of magnetic domain controlling films along the surface of the substratum, for example. A biasing magnetic field is established between the magnetic domain controlling films in a predetermined direction. The biasing magnetic field serves to unify the magnetization of the free ferromagnetic layer within the spin valve film. A so-called Barkhausen noise can thus be suppressed. The magnetic domain controlling films are made of a hard magnetic material. Specifically, the magnetic domain controlling film forms a hard magnetic film. The intensity of the biasing magnetic field depends on the thickness of the magnetic domain controlling films and the strength of the residual magnetization.
The CPP structure MR element enables reduction in size of the magnetoresistive film as compared with a conventional current-in-the-plane, CIP, structure magnetoresistive element. The reduced size of the magnetoresistive film causes a reduced distance between the magnetic domain controlling films. This allows the free ferromagnetic layer in the magnetoresistive film to receive the biasing magnetic field of an excessive intensity. The biasing magnetic field in this case tends to hinder the rotation of magnetization in the free ferromagnetic layer.
It is accordingly an object of the present invention to provide a current-perpendicular-to-the-plane structure magnetoresistive element capable of controlling the direction of magnetization in a free magnetic layer of a magnetoresistive film in facilitated manner in accordance with the size of the magnetoresistive film.
According to a first aspect of the present invention, there is provided a current-perpendicular-to-the-plane (CPP) structure magnetoresistive element comprising: a lower electrode defining a datum plane intersecting with a medium-opposed surface; an upper electrode opposed to the datum plane by a predetermined distance; a magnetoresistive film located in a space between the upper and lower electrodes, said magnetoresistive film extending along the datum plane in contact with the lower electrode; and a non-magnetic body extending along the datum plane at a position adjacent the magnetoresistive film.
The CPP structure magnetoresistive element allows electric current to flow between the upper and lower electrodes in the direction perpendicular to the datum plane. The inventors have confirmed that the current magnetic field is established along a horizontal cross-section perpendicular to the flow of the electric current in the direction rotating around the center of the flow. Moreover, the inventors have discovered that the intensity of the current magnetic field increases as the distance gets larger from the center of the flow. In general, when the current magnetic field is induced around a single flow of electric current, the intensity of the current magnetic field decreases depending upon an increased distance from the center of the flow. However, the inventors have found that the intensity of the current magnetic field increases as the distance gets larger from the center of the flow if the electric current having a uniform distribution over the horizontal cross-section flows in the vertical direction. The inventors have found that the magnetization of a sufficient intensity can be established in a predetermined direction along the medium-opposed surface in the CPP structure magnetoresistive element based on the current magnetic field. The inventors have found that the current magnetic field can be utilized to control the direction of the magnetization in the free magnetic layer.
In general, the value of electric current is set based on the heat generation of the magnetoresistive film in the CPP structure magnetoresistive element. Accordingly, as long as the quantity of the heat generated, namely of the electric power is maintained constant, the current magnetic field serves to establish the magnetic field of a sufficient intensity within the free magnetic layer. The magnetization can easily be controlled in the free magnetic layer irrespective of reduction in the size of the magnetoresistive film.
The CPP structure magnetoresistive element may further comprise: upper and lower shielding layers sandwiching the upper and lower electrodes, the magnetoresistive film and the non-magnetic body along the medium-opposed surface; and a soft magnetic body extending along the medium-opposed surface from the upper shielding layer to the lower shielding layer in parallel with the magnetoresistive film.
The soft magnetic body serves as a shielding layer, so that the magnetic field acts on the magnetoresistive film over a reduced extent. In particular, a higher resolution can be achieved for magnetic information data in the lateral direction of recording tracks. The CPP structure magnetoresistive element thus contributes to a further improvement of recording density. In this case, the soft magnetic body may be connected to either one of the upper and lower shielding layers. The upper shielding layer may serve as the upper electrode in the CPP structure magnetoresistive element. The lower shielding layer may serve as the lower electrode in the CPP structure magnetoresistive element.
According to a second aspect of the present invention, there is provided a magnetoresistive element comprising: a magnetoresistive film extending along a datum plane intersecting with a medium-opposed surface; upper and lower shielding layers sandwiching the magnetoresistive film along the medium-opposed surface; and a soft magnetic body extending along the medium-opposed surface from the upper shielding layer to the lower shielding layer in parallel with the magnetoresistive film.
The soft magnetic body serves as a shielding layer in the magnetoresistive film, so that the magnetic field acts on the magnetoresistive film over a reduced extent. In particular, a higher resolution can be achieved for magnetic information data in the lateral direction of recording tracks. The CPP structure magnetoresistive element thus contributes to a further improvement of recording density. In this case, the soft magnetic body may be connected to either one of the upper and lower shielding layers. The upper shielding layer may serve as the upper electrode in the magnetoresistive element. The lower shielding layer may serve as the lower electrode in the magnetoresistive element.
The aforementioned CPP structure magnetoresistive element as well as the aforementioned magnetoresistive element may be utilized in a head slider, for example. The head slider is usually employed in a magnetic recording medium drive such as a hard disk drive, for example.
The above and other objects, features and advantages of the present invention will become apparent from the following description of the preferred embodiments in conjunction with the accompanying drawings, wherein:
A head actuator 15 is also incorporated within the inner space of the main enclosure 12. The head actuator 15 is coupled to a vertical support shaft 16 for relative rotation. The head actuator 15 includes rigid actuator arms 17 extending from the vertical support shaft 16 in the horizontal direction. A head suspension assembly 18 is attached to the tip or front end of the individual actuator arm 17 so as to extend forward from the actuator arm 17. The actuator arms 17 are related to the front and back surfaces of the magnetic recording disk 13.
The head suspension assembly 18 includes a load beam 19. The load beam 19 is connected to the front end of the actuator arm 17 through a so-called elastic deformable section. The elastic deformable section serves to generate a predetermined urging force directed toward the surface of the magnetic recording disk 13. A flying head slider 21 is supported at the front end of the load beam 19. The flying head slider 21 is received on a gimbal spring, not shown, fixed to the load beam 19 for relative change of attitude.
When the magnetic recording disk 13 rotates, the flying head slider 21 is allowed to receive airflow generated along the surface of the rotating magnetic recording disk 13. The airflow serves to generate a positive pressure or lift as well as a negative pressure on the flying head slider 21. The flying head slider 21 is thus allowed to keep flying above the surface of the magnetic recording disk 13 during the rotation of the magnetic recording disk 13 at a higher stability established by the balance between the urging force of the load beam 19 and a combination of the lift and the negative pressure.
A power source 22 such as a voice coil motor (VCM) is connected to the actuator arm 17, for example. The power source 22 serves to realize the swinging movement of the actuator arm 17 around the support shaft 16. The rotation of the actuator arm 17 enables the movement of the head suspension assembly 18 in the radial direction of the magnetic recording disk 13. When the actuator arm 17 is driven to swing about the support shaft 16 during the flight of the flying head slider 21, the flying head slider 21 is allowed to cross the recording tracks defined on the magnetic recording disk 13 in the radial direction of the magnetic recording disk 13. This radial movement serves to position the flying head slider 21 right above a target recording track on the magnetic recording disk 13.
A front rail 26 and a rear rail 27 are formed on the bottom surface 24 of the slider body 23. The front rail 26 is designed to extend along the inflow or leading end of the slider body 23. The rear rail 27 is located near the outflow or trailing end of the slider body 23. Air bearing surfaces (ABSs) 28, 29 are respectively defined on the top surfaces of the front and rear rails 26, 27. The inflow ends of the air bearing surfaces 28, 29 are connected to the top surfaces of the front and rear rails 26, 27 through steps 31, 32, respectively.
The bottom surface 24 of the flying head slider 21 is designed to receive airflow 25 generated along the rotating magnetic recording disk 13. The steps 31, 32 serve to generate a relatively larger positive pressure or lift at the air bearing surfaces 28, 29. Moreover, a larger negative pressure is induced behind the front rail 26. The negative pressure is balanced with the lift so as to stably establish a flying attitude of the flying head slider 21.
A read/write electromagnetic transducer 33 is mounted on the slider body 23. The read/write electromagnetic transducer 33 is embedded within the alumina film 23b of the slider body 23. A read gap and a write gap of the read/write electromagnetic transducer 33 are exposed at the air bearing surface 29 of the rear rail 27. It should be noted that a diamond-like-carbon (DLC) protection film may extend over the surface of the air bearing surface 29 so as to cover over the front end of the read/write electromagnetic transducer 33. The read/write electromagnetic transducer 33 will be described later in detail. The flying head slider 21 may take any shape or form other than the aforementioned one.
The thin film magnetic head 34 includes an upper magnetic pole layer 39 exposing the front end at the air bearing surface 29, and a lower magnetic pole layer 38 likewise exposing the front end at the air bearing surface 29. The upper and lower magnetic pole layers 39, 38 may be made of FeN, NiFe, or the like, for example. The combination of the upper and lower magnetic pole layers 39, 38 establishes the magnetic core of the thin film magnetic head 34.
A non-magnetic gap layer 41 is interposed between the upper and lower magnetic pole layers 39, 38. The non-magnetic gap layer 41 may be made of Al2O3 (alumina), for example. When a magnetic field is induced at the conductive swirly coil pattern, a magnetic flux is exchanged between the upper and lower magnetic pole layers 39, 38. The non-magnetic gap layer 41 allows the exchanged magnetic flux to leak out of the air bearing surface 29. The thus leaked magnetic flux forms a magnetic field for recordation, namely, a write gap magnetic field.
The CPP structure MR read element 35 includes a lower electrode 42 spreading over the upper surface of the alumina layer 37 as a basement insulation layer. The lower electrode 42 may have not only a property of electric conductors but also a soft magnetic property. If the lower electrode 42 is made of a soft magnetic electric conductor, such as NiFe, for example, the lower electrode 42 is also allowed to serve as a lower shielding layer for the CPP structure MR read element 35.
A flattened surface or datum plane 43 is defined on the upper surface of the lower electrode 42. The flattened surface 43 is designed to intersect with the bottom surface 24 at right angles. A magnetoresistive (MR) film 44 is overlaid on the flattened surface 43. The magnetoresistive film 44 is patterned into a predetermined contour. The magnetoresistive film 44 extends rearward from the tip or front end exposed at the air bearing surface 29 along the flattened surface 43. Contact and electric connection is thus established between the magnetoresistive film 44 and the lower electrode 42. The structure of the magnetoresistive film 44 will be described later in detail.
An upper electrode 45 is located on the magnetoresistive film 44. The magnetoresistive film 44 is thus interposed between the upper and lower electrodes 45, 42. An upper shielding layer 46 is located on the upper electrode 45. The upper shielding layer 46 may have not only a soft magnetic property but also a property of electric conductors. Likewise, the upper electrode 45 may have not only a property of electric conductors but also a soft magnetic property. If the upper electrode 45 is made of a soft magnetic electric conductor, such as NiFe, for example, the upper electrode 45 is also allowed to serve as an upper shielding layer for the CPP structure MR read element 35. The distance between the aforementioned lower electrode 42 and the upper electrode 45 determines a linear resolution of recordation along a recording track on the magnetic recording disk 13.
A non-magnetic layer 47 extends on the flattened surface 43 at a position adjacent the magnetoresistive film 44. The non-magnetic layer 47 is interposed between the lower electrode 42 and the upper shielding layer 46. The non-magnetic layer 47 may be made of an insulating material such as Al2O3, SiO2, or the like. Since the non-magnetic layer 47 has an insulating property, short circuit is prevented between the upper shielding layer 46 and the lower electrode 42 even if the upper shielding layer 46 has a property of electric conductivity.
When the CPP structure MR read element 35 is opposed to the surface of the magnetic recording disk 13 for reading magnetic information data, the magnetoresistive film 44 allows the magnetization of the free ferromagnetic layer 53 to rotate in response to the inversion of the magnetic polarity applied from the magnetic recording disk 13. The rotation of the magnetization in the free ferromagnetic layer 53 induces variation in the electric resistance of the magnetoresistive film 44. When a sensing current is supplied to the magnetoresistive film 44 through the upper electrode 45 and the lower electrode 42, a variation in the voltage appears, in response to the variation in the magnetoresistance, in the sensing current output from the upper electrode layer 45 and the lower electrode 42. The variation in the level can be utilized to detect a magnetic bit data recorded on the magnetic recording disk 13.
Here, the inventors have observed the current magnetic field within the free ferromagnetic layer 53 in response to supply of electric current. The inventors executed software programs for analyzing the magnetic field on a computer. The electric current was set to flow through the magnetoresistive film 44 in the vertical direction perpendicular to the flattened surface 43. As shown in
The inventors have further observed the magnetic field generated in the free ferromagnetic layer 53. The aforementioned software programs were again employed for observation. Here, the magnetic field of the pinned ferromagnetic layer 51, the magnetostatic influence and the exchange interaction were taken into consideration in addition to the influence of the current magnetic field. The contour of the magnetoresistive film 44 was set at a square having sides of 0.16 μm long each. As is apparent from
Simultaneously, the inventors have observed the magnetic field generated in the free ferromagnetic layer in a CPP structure MR read element according to a comparative example. The aforementioned magnetoresistive film 44 was structured in the CPP structure MR read element of the comparative example. In this case, the magnetoresistive film 44 was located between a pair of magnetic domain controlling film along the air bearing surface. A biasing magnetic field was established in a predetermined direction between the magnetic domain controlling films across the free ferromagnetic layer. As is apparent from
The inventors have thereafter observed the distribution of intensity for the current magnetic field generated in the magnetoresistive film 44 and the distribution of intensity for the biasing magnetic field in the magnetoresistive film 44 in the CPP structure MR read element of the comparative example. The aforementioned software programs were again employed for observation. Here, the magnitude of the electric current was set in accordance with the following expression:
I2R═P(=const.) (1)
Here, the value of the electric current was set based on the heat generation in the magnetoresistive film 44, namely P=550 μW. The position of the magnetic field was determined in accordance with the distance from the end of the free ferromagnetic layer 53 along the air bearing surface 29. As shown in
As shown in
Etching process is effected based on the resist film 61. Ion milling may be employed in the etching process, for example. As shown in
The non-magnetic film 47 having an insulating property is formed on the lower electrode 42. Sputtering may be employed to form the lower electrode 42. As shown in
As shown in
The CPP structure MR read element 35a enables control on the direction of the magnetization in the free ferromagnetic layer 53 based on the current magnetic field in the same manner as described above. Moreover, since the soft magnetic pieces 63 serve as shielding layers, the magnetic field from the magnetic recording disk 13 acts on the magnetoresistive film 44 over a reduced extent. In particular, a higher resolution can be achieved for magnetic information data in the lateral direction of recording tracks. The CPP structure MR read element 35a thus contributes to a further improvement of recording density.
The first and second material films 58, 59 may be employed to form the CPP structure MR read element 35a in the same manner as described above. The magnetoresistive film 44 and the upper electrode 45 are formed out of the first and second material films 58, 59 as shown in
The resist film 61 is removed after the formation of the basement non-magnetic film 64 and the soft magnetic material film 65. The removal of the resist film 61 causes lift-off of the basement non-magnetic film 64 and the soft magnetic material film 65 on the resist film 61. The upper surface of the upper electrode 45 thus gets exposed. A resist film 66 is thereafter formed on the soft magnetic material film 65 and the upper electrode 45 in a predetermined pattern. Etching process is then effected based on the resist film 66. Ion milling may be employed in the etching process, for example. The soft magnetic material film 65 is removed around the resist film 66. The soft magnetic pieces 63 are in this manner formed out of the soft magnetic material film 65. Here, the upper surface of the basement non-magnetic film 64 may partially be scraped of f around the soft magnetic pieces 63.
The insulating non-magnetic layer 47 is then formed on the lower electrode 42. Sputtering may be employed to form the non-magnetic layer 47. As shown in
As shown in
Number | Date | Country | Kind |
---|---|---|---|
2002-296080 | Oct 2002 | JP | national |
Number | Date | Country | |
---|---|---|---|
Parent | PCT/JP03/12834 | Oct 2003 | US |
Child | 11022733 | Dec 2004 | US |