The invention is directed to a method for coating substrates with a decorative hard-material layer which is performed in a vacuum coating chamber, whereby the decorative hard-material layer is deposited by means of a reactive HIPIMS-process (High Power Pulse Magnetron Sputtering), and the energy content in power pulses is regulated so that the deposited hard-material layer has a homogeneous color, a high smoothness and a high hardness.
The U.S. Pat. No. 4,415,421A describes a method for manufacturing decorative, gold-colored layers which comprise deposition of a stainable protective layer of TiN by means of electron beam evaporation and deposition of a gold layer on the surface of the TiN-layer by means evaporation of gold.
The patent EP0201508B1 describes gold-colored TiN-layers doped with gold and the manufacturing methods thereof.
In the Patent DE3134587C2 there is nevertheless addressed that for the practical appliance, gold is not well suited as a material for manufacturing gold-colored films because it is, on one hand, very expensive and it provides on the other hand, no good abrasion resistance and is consequently easily deteriorated. Therefore, one proposes in the DE3134587C2 to make use of a coating, which comprises instead of a gold-colored layer of gold, a gold-colored layer of a Cu—Sn—Al-alloy. The gold-colored Cr—Sn—Al-layer shall be applied between a primary coating and a final coating. The primary and the final coatings may be realized according to the DE3134587C2 in that a paint color of a material as of Polyester, Acrylic resin or Polyurethane is applied by means of spraying or brushing and is thereafter heated and then dried thereby realizing a predetermined thickness. For the final coating a transparent paint color shall be used.
A further possibility to manufacture a gold-colored coating without having to use gold as coating material is described in the German Laid Open DE3150039A1. According to the DE3150039A1 a gold-colored layer, free of gold, is manufactured from TiN and ZrN which exhibits a good abrasion resistance.
Similarly the DE3731127C2 proposes a method for decorative coating of substrates by which a gold-colored layer is deposited by means of cathodic arc evaporation from a target of a Ti, Zr or TiZr-alloy, whereby the coating is performed in a reactive atmosphere containing nitrogen and whereby the target has a negative polarity with respect to the anode. The DE3731127C2 teaches that by making use of a target of TiZr-alloy and of nitrogen gas, gold-colored layers may be manufactured which have a composition TixZr1-xN with 0<x<1 the color appearance thereof varying with x. Further, the DE3731127C2 teaches that by a use of a Ti-target and of nitrogen as reactive gas and additionally of O2- and/or of C-containing gas as a doping gas, gold-colored TiN-layers may be manufactured which are doped with O2 and/or C, the color-appearance thereof varying as a function of the relative doping content.
Additionally, the DE3731127C2 teaches that by the use of a Zr-target and of nitrogen as reactive gas and additionally also of O2- and/or C-containing gas as a doping gas, white gold-colored TiN-layers may be manufactured which are doped with O2 and/or C, the color appearance of which varying as a function of the relative doping content
The patent EP1614764B1 describes a decorative object with a cold colored coating the color thereof being realized by depositing a multitude of superimposed pairs of alternate TiN- and ZrN-layers whereby the ratio of the weight of Zr and of the sum of the weights of Zr and Ti within the coating is between 50% and 80%. On one hand this multi-layer structure results in a color according of gold 2N18 or 1N14 or 3N18 and on the other hand the multi-layer structure allows that, whenever the outermost layers are worn, the color appearance is still maintained. In the EP1614764B1 it is also mentioned that the method for depositing the decorative layer on an object should be preferably a sputtering method in which Ti- and Zr-containing sputtering sources are used.
R. Hallmann reports in his master theses “A Study of TiN Coatings on Medical Implants Deposited by HiPIMS”, which was made at the Technical University of Luleain in Sweden that he succeeded to manufacture TiN-layers with different color appearances from golden-yellow up to brownish by means of HIPIMS. Hallmann mentions that a significant influence of some coating characteristics as e.g. of porosity and density upon the color appearance could be ascertained and also a slight correlation was found between color appearance and oxygen content.
In the journal Surface and Coatings Technology 116-119 (1999) 278-283 Roquiny reports about the influence of nitrogen flow on the color of TiN-layers which were deposited using reactive sputtering processes. The color of the deposited TiN-layers varied according to Roquiny from metallic grey via gold up to brownish red as the nitrogen flow was increased.
Nevertheless, manufacturing of homogeneous layer colors when coating by means of a reactive sputter- or HIPIMS-processes is still a big challenge.
When coating by means of reactive sputter- or HIPIMS-processes often a metallic target is used as a sputtering material source whereby at least one reactive gas is used which reacts at least partially with material from the target surface in such a manner that areas of the target surface become covered by the material, which results from the reaction and which is commonly a ceramic material. The degree of covering depends from the process parameters e.g. significantly from the reactive gas flow. This phenomenon is normally called target poisoning. One says, that the target is completely poisoned when the target surface is completely covered.
Principally target poisoning is a severe problem when manufacturing decorative layers by means of reactive sputter- or HIPIMS-processes because at such processes target poisoning normally leads to the appearance of hysteresis behavior with respect to the process parameters and leads generically to process instability.
Consequently, the industrial manufacturing of decorative layers exhibiting a homogeneous layer color by means of reactive sputter- or HIPIMS-processes is not economical, especially not, if a coating chamber having of large dimensions is used, because in this case the inhomogeneity of the resulting coating color at the coated substrates, which are distributed along the coating chamber, is even larger.
Beside of this, there exists a further problem, when using HIPIMS-processes, namely that, due to the pulsating variation of the sputter power as used, there occur variations of partial pressure of the reactive gas in the coating chamber during the coating process, which as well lead to inhomogeneity of the resulting layer color.
It is the object of the present invention to provide a method for coating surfaces of substrates with decorative hard-material layers which, on one hand imparts to the coated surface, a durable colored appearance and, on the other hand, allows an easy realization of a homogeneous color appearance.
The object of the present invention is resolved by providing a method according to claim 1.
The inventor has found that it is surprisingly possible to produce hard-material layers with a highly homogeneous color appearance, with a very high hardness and with a very smooth layer surface by means of reactive HIPIMS-processes, which layers, due to these layer characteristics are especially highly suited for decorative applications, if at the HIPIMS-process, power pulses and/or power pulse-sequences are applied with an energy content, with respect to the target surface, of at least, preferably larger than 0.2 Joule/cm2 per power pulse or respectively per power pulse-sequence. We understand by the term “power pulse-sequence” a burst of multiple power pulses.
The
Under the term “power pulse or power pulse-sequence with an energy content with respect to the target surface” one understands within the frame of the present invention the complete energy content which is input to the target surface during the pulse duration, tPuls, of a power pulse 1 or during the sequence duration, tPulssequenz, of a power pulse-sequence 3, whereby, as surface of the target, that target surface is considered upon which the plasma is effectively projected during the pulse duration, tPuls, of the power pulse 1 or, respectively, during the sequence duration (pulse burst duration), tPulssequenz, of the power pulse-sequence 3. This target surface is often named “Racetrack” and may be recognized at the target as area of target material consumption.
The energy content to be applied according to the invention to a power pulse 1 at the HIPIMS-process may, as an example, be realized by setting a respectively very high pulse power, P, and/or setting of a respectively very extended pulse length or pulse duration, tPlus. The respective pulse power, P, and pulse duration, tPuls, may obviously be set only so large, that the target material in the respective coating chamber arrangement does become thermally overloaded. In a similar manner the entire energy content, according to the invention may be realized in a power pulse-sequence 3 at the HIPIMS-process by setting the pulse powers, P, of the pulses which make up the sequence or the burst of pulses within a power pulse-sequence 3 and/or by setting the sequence duration, tPulssequenz, of the power pulse-sequence 3.
The HIPIMS-processes which are operated according to the invention are highly stable and astonishingly neither the process stability nor the homogeneity of the layer characteristics, which are important for decorative applications, or the hard-material layers, which are manufactured in this manner, are impaired by possible target poisoning appearances and/or reactive partial pressure variations.
More concretely, the present invention is directed to a method for coating of at least partial areas of the surface of a substrate or, respectively, to a method for manufacturing of substrates with a surface area having a decorative hard-material layer in a coating chamber, whereby for manufacturing the hard-material layer, a reactive HIPIMS-process is used at which at least one reactive gas is used and at least one target of a material which may react during operation of the HIPIMS-process with the reactive gas in such a manner, that thereby a predetermined layer color is produced and whereby the HIPIMS-process is operated making use of power pulses and/or power pulse-sequences with an energy content, with respect to the target surface, of at least, preferably of more than 0.2 Joule/cm2 per power pulse or respectively per power pulse-sequence and thereby a homogeneous color appearance of the hard-material layer is realized.
It may not be excluded that beside of power pulses and/or power pulse-sequences (power pulse bursts), which fulfils these requirements also power pulses and/or power pulse-sequences (power pulse bursts) may be used which do not fulfil the addressed requirement namely with respect to energy content. Thereby, one can assume that at least 50% of the power pulses and/or power pulse-sequences which are applied, should fulfil the addressed requirement. As practiced today, practically all power pulses and respectively power pulse-sequences fulfil the addressed requirement or, respectively, the even sharper requirements still to be addressed.
Further, mixed operation may be applied with power pulses and with power pulse-sequences.
Further, it may be pointed out that the thermal loading of the target is also governed by the selected Duty-Cycle beside of by the pulse power and the pulse duration or respectively by single pulse powers and sequence duration (pulse burst duration), i.e. by:
Preferably the energy content of at least, preferably of more than 0.2 Joule/cm2 per power pulse or respectively per power pulse-sequence is set including setting of a power density of at least, preferably of more than 100 W/cm2, preferably with a current density of at least, preferably of more than 0.2 A/cm2.
According to a preferred form of realization of the present invention the HIPIMS-process is operated by making use of power pulses and/or power pulse-sequences with an energy content, with respect to the target surface, of at least, preferably of more than one 1 Joule/cm2 per power pulse or respectively per power pulse-sequence.
This energy content per power pulse or respectively per power pulse-sequence is preferably input under setting of a power density of at least, preferably of more than 500 W/cm2, preferably with a current density of at least, preferably of more than 1 A/cm2.
According to an especially preferred realization form of the present invention, the HIPIMS-process is operated making use of power pulses and/or power pulse-sequences with an energy content, with respect to the target surface, of at least, preferably of more than 10 joules/cm2 per power pulse or respectively per power pulse-sequence.
This energy content is preferably input under setting of a power density of at least, preferably of more than 1000 W/cm2, preferably at a current density of at least, preferably of more than 2 A/cm2.
Preferably, the concentration of the reactive gas within the coating chamber is controlled by a regulating—open-loop control or negative feedback control—of a reactive gas flow.
In the following the present invention is further described by means of some examples and with the help of the
An outstanding homogeneity of the color appearance along the entire coating height could be confirmed for the TiCN- and TiN-layers deposited according to the invention, as may be seen in the
Gold-colored layers with a multilayer layer-structure of a multitude of alternatingly deposited thin TiN- and ZrN-layers may also be perfectly manufactured by making use of a method according to the present invention. This, as an example in that one, using at the same HIPIMS-coating process uses, nitrogen as reactive gas and at least one HIPIMS-target of Ti as well as a HIPIMS-target of Zr positioned in the coating chamber so and operated so that TiN- and ZrN-layers are alternatingly deposited on the substrates to be coated.
According to the present invention different colors of the gold standard may be easily produced at hard-material layers deposited according to the present invention by setting different nitrogen flows, this especially when using Ti-containing targets or preferably targets which consist of titanium.
According to the invention the nitrogen flow may be exactly regulated so that the color appearance accords preferably a color according to that of gold 2N18 or 1N14 or 3N18.
The inventor has recognized that especially hard-material layers with nice colors for decorative applications may be manufactured by using targets which comprise titanium or titanium and aluminum or zirconium.
According to a preferred form of realization of a method according to the invention at least one target is used which consists of titanium or of titanium and aluminum or of zirconium.
For manufacturing nitrides, oxides, carbides, oxynitrides or carbonitrides which may provide different layer characteristics and color appearances to the layers manufactured according to the present invention, nitrogen gas or oxygen gas or a carbon-containing gas, e.g. C2H2 or CH4 or a mixture of such gases, e.g. N2 and C2H2, may be fed to the coating chamber for operating the HIPIMS-process. Preferably a coating according to the present invention is applied to substrates at which the hard-material layer shall have a decorative function.
Methods according to the invention and as described here are especially and very highly suited for coating different decorative objects as substrates which may be of different materials. A highly significant advantage of using a method according to the present invention for manufacturing decorative hard-material layers is that one may also coat temperature sensitive substrates which, as an example, may not be exposed to temperatures above 200° C. This becomes possible because the HIPIMS-processes according to the invention may be operated so that the duration of a power pulse, tPuls, or the duration of the single pulses within a power pulse-sequence or the duration of a power pulse-sequence, tPussequenz, as well as the respective pulse pauses (Duty-Cycle) and the relevant target surface may be selected so that very low coating temperatures, i.e. very low substrate temperatures may be met during the coating process without occurrence of process instabilities.
According to the invention one may produce hard-material layers with different colors of the gold standard by setting of a respective nitrogen flow but also other hard-material layers may be produced, the color appearance thereof being adjustable within a large coating range by setting of the respectively applied reactive gas flow or of the concentration of different reactive gases.
In the frame of the present invention and as an example, decorative hard-material layers with predetermined color and with an excellent homogeneous appearance, with very high hard hardness and super-smooth surface were manufactured according to the invention. The reactive gas flows used as well as the measured mechanical characteristic of the manufactured hard-material layers are shown in table 1. All the processes were realized at substrate temperatures between 150° C. and 500° C.
The very high mechanical stability of those hard-material layers and respectively the very good combination of hardness and E-Module allow that these layers provide at the objects coated therewith a durable color appearance.
These layers have a very good adherence to the substrate and have a very high wear resistance. Consequently, these decorative hard-material layers may be used over years.
The methods according to the present invention allow to reach highly homogeneous color appearances even if the substrates have very extended surfaces to be coated.
Methods according to the present invention are especially suited whenever a multitude of substrates are to be distributed along the height extend of a large coating chamber and a homogeneous color appearance over all substrates shall be reached.
| Filing Document | Filing Date | Country | Kind |
|---|---|---|---|
| PCT/EP2014/063611 | 6/26/2014 | WO | 00 |
| Number | Date | Country | |
|---|---|---|---|
| 61839454 | Jun 2013 | US |