The present invention generally relates to an electrode for use in a plasma processing chamber, and more particularly to an upper electrode that can be easily fabricated, and has a longer service life.
Silicon wafer is a substrate material used in the fabrication of integrated circuit and other microdevices. Many of the integrated circuit fabrication process involve plasma, such as dry etch, chemical vapor deposition, physical vapor deposition, and etc. The standard wafer size has increased over the years from 100 mm to 150 mm, 200 mm, up to 300 mm as a standard diameter used in today's facilities. At present, manufacturers are planning for 450 mm and larger diameter silicon wafer. For properly performing a plasma related fabrication process, such as dry etch process, the upper electrode of the plasma process chamber has also been correspondingly improved in size to provide a larger gas spurting area. The major challenge in fabricating a large upper electrode lies in the fabrication of a large electrical (e.g. cathode) plate, a key component of the upper electrode, which requires large silicon ingots of semiconductor grade. Although any dimension of semiconductor grade monocrystalline silicon ingot can be fabricated using the Czochralski method, fabrication efficiency and cost of silicon ingot are still great barricades to overcome in fabricating large electrical plates.
As mentioned earlier, the standard wafer size for semiconductor fabrication increased from 100 mm to 300 mm, the silicon electrical plate within an upper electrode of a plasma processing chamber must also be correspondingly increased. Under the current trend toward a 450 mm diameter silicon wafers, the technical bottleneck for efficient fabrication of suitable upper electrode for the plasma process is expected. Therefore, it is highly desirable to provide improved configuration/fabrication process of a plasma upper electrode to overcome this issue.
The present invention is directed to a structure of an upper electrode for use in a plasma process reaction chamber. The disclosed upper electrode allows adjustment of the electrode size and thickness according to the requirements. It should be noted that even though the present invention is illustrated by an embodiment of fabricating a structure of an upper electrode for a plasma processing chamber, however it would be recognized by those skilled in the art that the present invention has a much broader range of applicability.
One embodiment of the present invention is to provide a structure of an upper electrode for use in a plasma processing chamber. The electrode comprises a center segment and a plurality of extension segments. The extension segments may be attached to the center segment to adjust the spurting area covered by the electrode. Gas distribution holes may be selectively formed on the center segment and or extension segments. By adding or removing the extension segments, the dimension of the upper electrode and the area of gas spurting region of the upper electrode may be adjusted.
During the fabrication process, the electrode may be configured to dispense very large silicon ingots, therefore large size upper electrodes may be fabricated relatively more easily compared to the conventional process. One embodiment of the present invention suggests that by patching plurality of smaller dimension silicon slabs to configure the electrode with desired dimension and gas spurting area.
Another embodiment of the present invention use plasma etch system as an example to illustrate an example plasma process system with flexibility of handling and varying sample size. The plasma etch system comprises a process reaction chamber, a vacuum device, a chuck electrode, an upper electrode, a power source and a gas supply device. The upper electrode comprises an electrical plate including a center plate and a plurality of extension segment plates. The extension segment plates comprise a plurality of gas distribution holes. Therefore, by adding or removing extension segment plates, the dimension of the upper electrode and the gas spurting area of the upper electrode may be correspondingly increased or decreased.
According to yet another embodiment of the present invention, the upper electrode may be comprised of a plurality of laminated segments stacked on each other, and the thickness of the upper electrode may be adjusted by adjusting the number of laminated segments.
According to yet another embodiment of the present invention, the surface of the center plate and at least one of the extension segment plates may be coated with a protective coating layer comprised of plasma erosion preventing material, such as silicon nitride (Si3N4) or silicon carbide (SiC). The protection coating may extend through the gas distributing hole. The center plate and/or extension segment plates may further comprise at least one coating free region for facilitating electrical connection of the center plate and extension segment plates to the plasma process reaction chamber.
Reference will now be made in detail to specific embodiments of the present invention. Examples of these embodiments are illustrated in the accompanying drawings. While the invention will be described in conjunction with these specific embodiments, it will be understood that it is not intended to limit the invention to these embodiments. In fact, it is intended to cover alternatives, modifications, and equivalents as may be included within the spirit and scope of the invention as defined by the appended claims. In the following description, numerous specific details are set forth in order to provide a through understanding of the present invention. The present invention may be practiced without some or all of these specific details. In other instances, well-known process operations are not described in detail in order not to obscure the present invention.
To resolve this problem, in one embodiment of the present invention, a structure of an upper electrode 200 is provided, as illustrated in
As illustrated in
In one example, the first and second gas distribution holes 203, 204 are identical. In another example, they are different in at least one structural characteristic. For example, the first and second gas distribution holes 203, 204 can be different in diameter, opening shape, interior configuration, etc.
The area of gas spurting region is composed of areas of gas distribution holes 203 and 204. As illustrated in
In one embodiment, the center plate 201 is surrounded by and attached to the extension segment plates 202. The extension segment plates 202 can be attached to each other and to the center plate 201 as well. The center segment plates 2011 and the extension segment plates 202 may have an arbitrary shape including a polygon or curved edge. For example, they may be circular and sectorial as illustrated in
The extension segment plates 202 can be bonded to each other and to the center plate by brazing, soldering, adhering or mechanical fitting method, or any combination thereof. In one embodiment, the adhesives or bonding materials, or materials used to build the mechanical fitting structure could be thermally and electrically conductive materials, such as metals, conductive epoxies, or the like. The bonding material may be preferably formed from low vapor pressure materials which have lower tendencies to contaminate low pressure reactor environments.
In another embodiment of the present invention, the surface of center plate and at least one extension segment plates are coated with a protective coating layer of plasma erosion preventing material, such as silicon nitride (Si3N4) or silicon carbide (SiC). Referring now to FIGS. 3A and 3A-1, which illustrates an electrical plate 300 coated with protection coating on the exposed surface, according to an embodiment of the present invention. The thickness of the protection coating may be in a range of 1 to 50 micron. The protection coating may extend through the gas distribution hole as illustrated in
Reference will now be made in detail to use the plasma etch process as an example to express plasma process.
The center plate 405A may be surrounded by and attached to the extension segment plates 405B. The extension segment plates 405B may be attach to each other and to the center plate 405A as well. The center segment plates (not shown) and the extension segment plates 405B may have an arbitrary shape including a polygonal or curved edge as described above.
The extension segment plates 405B may be bonded to each other and to the center plate 405A by brazing, soldering, adhering or mechanical fitting method, or combination thereof In one embodiment, the adhesives or other bonding materials, or materials used to build the mechanical structure could be thermally and electrically conductive materials, such as metals, conductive epoxies, or the like. The bonding material may be preferably formed from low vapor pressure materials which have lower tendencies to contaminate low pressure reactor environments.
Although specific embodiments of the present invention have been described, it will be understood by those of skill in the art that there are other embodiments that are equivalent to the described embodiments. Accordingly, it is to be understood that the invention is not to be limited by the specific illustrated embodiments, but only by the scope of the appended claims.