Patent Application
20230411143
The present invention relates to an epitaxial wafer cleaning method.
With ongoing miniaturization of semiconductor devices, ever higher levels of cleanliness and quality are required for their underlying wafers. A cause of quality degradation is the presence of particles. Particles adhere to a front surface, a back surface, and an end surface (also referred to as an edge portion) of a wafer, and there are various types of, and various causes of adhesion of, such particles.
In particular, an epitaxial wafer for use in logic semiconductors has a higher quality epitaxial film formed on its front surface, on which a semiconductor device is to be formed. The epitaxial film can be formed by decomposing gases, such as trichlorosilane, at a high temperature and epitaxially growing a silicon single crystal film on the front surface of the wafer.
There has been a problem of particle adhesion to the back surface or end surface of the wafer due to the back surface or edge portion of the wafer being in contact with, or in proximity to, a jig inside an epitaxial apparatus.
Previously, cleanliness of the front surface of a wafer, which is the surface on which a semiconductor device is to be formed, has been of importance. For example, as disclosed in Patent Document 1, cleaning techniques such as employing SC-1, SC-2, HF, and brushes have been used to clean the front surface of a wafer before forming an epitaxial film. For wafers after having an epitaxial film formed thereon, attempts to reduce particles have also been focused on reducing particles adhered to the front surface of the wafer, including performing batch cleaning and, as disclosed in Patent Document 2, using cleaning techniques such as employing ozonated water and brushes.
Ongoing miniaturization of semiconductor devices has resulted in the particle size, which is a concern during semiconductor device manufacturing processes, becoming smaller. As such, particles not only on the front surface of the wafer but also on the back surface or edge portion thereof now greatly affect yields of semiconductor devices. This has made the effect of particles adhered to the back surface or edge portion of the wafer during epitaxial film formation non-negligible.
The present invention has been made to solve the above problems. An object of the present invention is to provide an epitaxial wafer cleaning method that is performed after epitaxial film formation for manufacturing an epitaxial wafer with minimized generation of particles from the back surface or edge portion of the wafer during semiconductor device manufacturing processes.
The present invention has been made to achieve the above object, and provides an epitaxial wafer cleaning method for cleaning a wafer having an epitaxial film formed on a front surface thereof, comprising:
a first cleaning step of supplying a cleaning solution containing O3 to all surfaces, including front, back, and end surfaces, of the wafer to perform spin cleaning;
a second cleaning step of supplying a cleaning solution to the back and end surfaces of the wafer to perform cleaning with a roll brush after the first cleaning step;
a third cleaning step of supplying a cleaning solution containing O3 to the front surface of the wafer to perform spin cleaning after the second cleaning step; and
a fourth cleaning step of supplying a cleaning solution containing HF to the front surface of the wafer to perform spin cleaning after the third cleaning step.
Such an epitaxial wafer cleaning method can provide an epitaxial wafer with minimized generation of particles from the back surface or edge portion of the wafer during semiconductor device manufacturing processes.
Preferably, the third cleaning step and the fourth cleaning step are performed in this order a plurality of times after the second cleaning step.
This can provide a cleaner front surface condition for the wafer.
Preferably, after the fourth cleaning step, a step of supplying a cleaning solution containing O3 to the front surface of the wafer to perform spin cleaning is performed as a final cleaning step.
This can form an oxide film on the front surface of the wafer and allow it to serve as a protective film.
Preferably, a PVA brush is used as the roll brush.
This can prevent metal contamination on the wafer.
As described above, the inventive epitaxial wafer cleaning method can provide an epitaxial wafer cleaning method that is performed after epitaxial film formation for manufacturing an epitaxial wafer with minimized generation of particles from the back surface or edge portion of the wafer during semiconductor device manufacturing processes. During single-wafer cleaning of the wafer after having an epitaxial film formed thereon, brush cleaning is performed on the back surface and the edge portion of the wafer, followed by spin cleaning of the front surface. This can reduce particles on the front surface, back surface, and edge portion and achieve the best cleanliness through the cleaning.
Hereinafter, the present invention will be described in detail, but the present invention is not limited to the following description.
As described above, a need has existed for an epitaxial wafer cleaning method that is performed after epitaxial film formation for manufacturing an epitaxial wafer with minimized generation of particles from the back surface or edge portion of the wafer during semiconductor device manufacturing processes.
Hence, the present inventors investigated cleaning capabilities to remove particles on the back surface and the edge portion of the wafer after having an epitaxial film formed thereon, and found that the particle removal rate is greatly affected by which cleaning method is used.
Batch SC-1 (an NH4OH/H2O2/H2O cleaning solution mixture) cleaning was capable of removing particles at both low and high temperatures of the cleaning solution, but not at a satisfactory level.
Also, cleaning with an O3/HF cleaning solution mixture, ultrasonic-assisted cleaning with an O3/HF solution mixture, oxide film delaminating cleaning with an HF aqueous solution, and two-fluid cleaning with pure water and air, all conducted using a single-wafer spin cleaning machine, did not provide a satisfactory level of particle removal capabilities.
Then, the present inventors tried cleaning with brushes and found it to be cleaning with a satisfactory level of particle removal capabilities. Additionally, while brushes used for cleaning can be broadly classified into roll brushes and disk brushes, roll brushes were found to have higher particle removal capabilities.
Cleaning with roll brushes includes a method of rotating two roll brushes and placing a wafer therebetween to simultaneously clean both front and back surfaces of the wafer with the brushes, and a method of pressing one roll brush against either the front or back surface of the wafer to clean only one surface of the wafer. The method of simultaneously cleaning both front and back surfaces of the wafer by rotating two roll brushes was found to degrade the cleanliness of the front surface of the wafer with an epitaxial film formed thereon, which is inherently sufficiently clean (without cleaning) with few particles, because the brush cleaning causes adhesion of microparticles as the brush contacts the epitaxial film on the front surface of the wafer.
From the above, it was found that the batch cleaning and the single-wafer spin cleaning without brush cleaning cannot sufficiently remove particles on the back surface or edge portion of the wafer after having an epitaxial film formed thereon. Thus, the present inventors have found that it is possible to achieve the best cleanliness with the fewest particles on the front surface, back surface, and edge portion of the wafer by cleaning the back surface and the edge portion with roll brushes and cleaning the front surface only by spin cleaning.
The present inventors have earnestly studied to solve the above problems and consequently found that it is possible to provide an epitaxial wafer cleaning method that is performed after epitaxial film formation for manufacturing an epitaxial wafer with minimized generation of particles from the back surface or edge portion of the wafer during semiconductor device manufacturing processes by employing an epitaxial wafer cleaning method for cleaning a wafer having an epitaxial film formed on a front surface thereof, comprising: a first cleaning step of supplying a cleaning solution containing O3 to all surfaces, including front, back, and end surfaces, of the wafer to perform spin cleaning; a second cleaning step of supplying a cleaning solution to the back and end surfaces of the wafer to perform cleaning with a roll brush after the first cleaning step; a third cleaning step of supplying a cleaning solution containing O3 to the front surface of the wafer to perform spin cleaning after the second cleaning step; and a fourth cleaning step of supplying a cleaning solution containing HF to the front surface of the wafer to perform spin cleaning after the third cleaning step. This finding has led to the completion of the present invention.
A description will be given below with reference to the drawings.
First, a cleaning apparatus used in the cleaning method according to the present invention will be described. An ordinary spin cleaning apparatus may be used for spin cleaning performed in the first, third, and fourth cleaning steps. In such cases, a parallel arrangement of a spin cleaning unit that can rotate a wafer W while holding it in a chamber section and supply a chemical solution to the front and back surfaces of the rotating wafer from a chemical solution supply nozzle and a brush cleaning unit (described below) is possible. The wafer can be transferred to the respective units for cleaning as appropriate according to each cleaning step.
A brush cleaning unit used in the second cleaning step will now be described. The second cleaning step in the cleaning method according to the present invention can employ a brush cleaning unit that performs single-wafer spin brush cleaning.
Preferably, the brush cleaning unit includes an edge brush holding jig 5 that holds the wafer W and connects to a driving section for rotating the wafer W, and a backside brush cleaning section that connects to a driving section for rotating the backside brush 2, which is the roll brush longer than the diameter of the wafer W, and cleans the back surface of the wafer W by rotating and pressing this backside brush 2, which is the roll brush against the back surface. The brush cleaning unit may include a plurality of edge brush holding jigs 5 and a plurality of edge brushes 1, which is the roll brush.
The edge brush 1 and the backside brush 2, both are the roll brush, are preferably made of resin, and more preferably made of polyvinyl alcohol (PVA), from the viewpoint of metal impurity contamination on the wafer W.
The cleaning method according to the present invention will now be described.
First, a wafer with an epitaxial film formed on a front surface thereof is provided, for which the cleaning method according to the present invention is to be performed. The type of the wafer to be provided is not particularly limited as long as it is an epitaxial wafer. For example, a silicon epitaxial wafer with a silicon epitaxial film formed on a silicon wafer can be used, though the material of the wafer can be selected as appropriate. In the case of forming a silicon epitaxial film on a silicon wafer, for example, the epitaxial film can be formed by introducing gases, such as trichlorosilane, into a chamber section in an epitaxial apparatus under a high temperature and decomposing these gases to epitaxially grow a silicon single crystal film on the front surface of the wafer.
Then, as the first cleaning step, the epitaxial wafer is set in the spin cleaning unit, and an O3-containing cleaning solution is supplied to all surfaces of the wafer W, including the front, back and end surfaces, to perform spin cleaning. In this first cleaning step, the front surface of the wafer W after having the epitaxial film formed thereon is in a very active state. Thus, spin cleaning is performed with the O3-containing cleaning solution in order to decompose and remove organic matter so that contamination by particles, organic matter, metallic impurities, etc., will not occur, as well as to form an oxide film on all surfaces of the front, back, and end surfaces. Preferably, the O3-containing cleaning solution is supplied from the chemical solution supply nozzle located at the center of the rotating wafer W for a period of time to sufficiently cover the wafer W and to decompose and remove organic matter and form a sufficient oxide film on all surfaces. At this time, as the O3-containing cleaning solution having been supplied to the front and back surfaces of the wafer W reaches, and is thus supplied to, the end surface, organic matter on the end surface of the wafer W can also be decomposed and removed. The O3-containing cleaning solution may be supplied separately toward the end surface of the wafer W. Alternatively, after spin cleaning of the front surface, the wafer may be inverted to perform spin cleaning of the back surface.
As the second cleaning step after the first cleaning step, the wafer is transferred to the brush cleaning unit shown in
As the third cleaning step after the second cleaning step, the wafer is transferred to, and set in, the spin cleaning unit, where the O3-containing cleaning solution is supplied to the front surface of the wafer W to perform spin cleaning. Further, as the fourth cleaning step after the third cleaning step, an HF-containing cleaning solution is supplied to the front surface of the wafer W to perform spin cleaning. While the front surface of the wafer W is cleaned after performing the brush cleaning of the back surface and the edge portion of the wafer W in the second cleaning step, the front surface of the wafer W after having the epitaxial film formed thereon is inherently very clean with few particles adhered. Since the oxide film has already been formed as a protective film by the O3-containing cleaning solution in the first cleaning step, particles adhered during the brush cleaning are removed along with the oxide film as the protective film when it is removed. Performing the cleaning of the third cleaning step using the O3-containing cleaning solution and the fourth cleaning step using the HF-containing cleaning solution in this order can achieve a very clean front surface condition, with few particles adhered, that is comparable to the cleanliness after the epitaxial film formation.
Additionally preferably, the third cleaning step and the fourth cleaning step are repeated a plurality of times in this order after the second cleaning step. Also preferably, after the fourth cleaning step, a step of supplying an O3-containing cleaning solution to the front surface of the wafer to perform spin cleaning is performed as a final cleaning step in order to form an oxide film on the front surface of the wafer W and allow it to serve as a protective film.
After the cleaning, the method can move to a step of evaluating particles on the back surface and the edge portion of the wafer W. For the evaluation step for the back surface of the wafer W, a sensitive evaluation is possible by evaluating the wafer W that is inverted such that its front surface comes to the side that is originally on the back. For evaluating particles on the back surface, the number of particles (defects) can be measured using, for example, an SP5 particle counter manufactured by KLA Corporation. For evaluating particles on the edge portion, the number of particles (defects) on the edge portion can be measured using an edge inspection apparatus EZ-300 manufactured by Lasertec Corporation.
The present invention is described below in detail using Example, although this Example does not limit the present invention.
First, as the first cleaning step, spin cleaning was performed by supplying O3 water to the front and back surfaces of the wafer sufficiently enough to cover its end surface. The wafer rotation speed was set to 1000 rpm, the O3 concentration to 20 ppm, the temperature to 24° C., the O3 water flow rate to 1 L/min, and the cleaning time to 20 sec.
Then, as the second cleaning step, brush cleaning was performed on the back surface and the edge portion of the wafer. The wafer rotation speed was set to 50 rpm, the edge brush rotation speed to 20 rpm, and the backside brush rotation speed to 150 rpm. Pure wafer was flowed as the cleaning solution, with the pure water flow rate set to 1 L/min and the cleaning time to 40 sec.
Then, as the third cleaning step, spin cleaning was performed by flowing O3 water to the front surface of the wafer. The wafer rotation speed was set to 1000 rpm, the O3 concentration to 20 ppm, the temperature to 24° C., the O3 water flow rate to 1 L/min, and the cleaning time to 20 sec. Subsequently, as the fourth cleaning step, spin cleaning of the front surface was performed by flowing HF. The wafer rotation speed was set to 1000 rpm, the HF concentration to 0.3 wt. % (mass percent concentration), the temperature to 24° C., the HF flow rate to 1 L/min, and the cleaning time to 7 sec. The third cleaning step and the fourth cleaning step were repeated twice in this order.
Then, as the final cleaning step, spin cleaning of the front surface of the wafer was performed by flowing O3 water. The wafer rotation speed was set to 300 rpm, the O3 concentration to 20 ppm, the temperature to 24° C., the O3 water flow rate to 1 L/min, and the cleaning time to 40 sec.
The wafer was then dried with the wafer rotation speed set to 1000 rpm and the drying time to 30 sec.
Cleaning and drying of an epitaxial wafer was performed in the same manner as in Example, except that brush cleaning was not performed.
SC-1 cleaning of an epitaxial wafer was performed using a batch cleaning machine. Using chemical solutions of 28 wt. % NH4OH and 30 wt. % H2O2, the wafer was cleaned by immersion in an NH4OH/H2O2/H2O (1:1:10) cleaning solution mixture for 5 minutes at a liquid temperature of 70° C.
For the epitaxial wafers used in Example and Comparative Example, particle removal rates were evaluated for the back surface and the edge portion of the same wafer after formation thereon of an epitaxial film (before the cleaning steps) and after the cleaning steps. For the back surface, the number of particles (defects) of 28 nm or greater was measured using an SP5 particle measuring instrument manufactured by KLA Corporation; for the edge portion, the number of particles (defects) on the edge portion was measured using an edge inspection apparatus EZ-300 manufactured by Lasertec Corporation. The number of particles adhered to the back surface after the epitaxial film formation was taken as 1 and compared to the number of particles after the cleaning steps, and a ratio with respect to the number of particles removed was calculated for comparison of the cleaning effect as expressed in terms of removal rates.
Comparison between Example and Comparative Examples 1, 2 demonstrates that, during single-wafer spin cleaning of the wafer after having an epitaxial film formed thereon, performing cleaning with an O3-containing cleaning solution to decompose and remove organic matter on the front, back, and end surfaces of the wafer and to form an oxide film, then performing brush cleaning of the back and end surfaces, followed by cleaning the front surface of the wafer by sequentially performing spin cleaning with an O3-containing cleaning solution and spin cleaning with HF made it possible to remove particles on the back and end surfaces while maintaining the particle level on the front surface as it had been after the epitaxial film formation, thereby improving the cleanliness of the wafer to a favorable level.
It should be noted that the present invention is not limited to the above-described embodiments. The embodiments are just examples, and any examples that substantially have the same feature and demonstrate the same functions and effects as those in the technical concept disclosed in claims of the present invention are included in the technical scope of the present invention.
| Number | Date | Country | Kind |
|---|---|---|---|
| 2020-180466 | Oct 2020 | JP | national |
| Filing Document | Filing Date | Country | Kind |
|---|---|---|---|
| PCT/JP2021/033609 | 9/13/2021 | WO |