Patent Application
20220344586
The present invention relates generally to electrode devices and, in particular, to an etch-resistant doped scavenging carbide electrode.
Resistive random access memory (a.k.a. RRAM or ReRAM) is considered as a promising technology for electronic synapse devices or memristor for neuromorphic computing as well as high-density and high-speed non-volatile memory application. In neuromorphic computing applications, a resistive memory device can be used as a connection (synapse) between a pre-neuron and post-neuron, representing the connection weight in the form of device resistance. Multiple pre-neurons and post-neurons can be connected through a crossbar array of RRAMs, which naturally expresses a fully-connected neural network. The density of ReRAM can be increased by vertically stacking ReRAM stacks as practiced in Flash NAND technology, however, ReRAM stacks are typically deposited by Physical Vapor Deposition (PVD) to control the oxygen vacancy concentration in the metal oxide layer and this prevents application to three-dimensional (3D) structures. Thus, there is a need for RRAM for 3D structures.
Additional aspects and/or advantages will be set forth in part in the description which follows and, in part, will be apparent from the description, or may be learned by practice of the invention.
A multilayered electrode comprising a first layer, an intermediate layer located directly on the first layer, and a top layer located on top of the intermediate layer. Wherein the intermediate layer is comprised of a doped carbide active layer.
A resistive switching memory stack, comprised of a bottom electrode, an oxide layer located on the bottom electrode; and a top electrode located on the oxide layer. The top electrode is comprised of a first layer, an intermediate layer located directly on the first layer, and a top layer located on top of the intermediate layer. Wherein the intermediate layer is comprised of a doped carbide active layer.
The above and other aspects, features, and advantages of certain exemplary embodiments of the present invention will be more apparent from the following description taken in conjunction with the accompanying drawings, in which:
The following description with reference to the accompanying drawings is provided to assist in a comprehensive understanding of exemplary embodiments of the invention as defined by the claims and their equivalents. It includes various specific details to assist in that understanding but these are to be regarded as merely exemplary. Accordingly, those of ordinary skill in the art will recognize that various changes and modifications of the embodiments described herein can be made without departing from the scope and spirit of the invention. In addition, descriptions of well-known functions and constructions may be omitted for clarity and conciseness.
The terms and words used in the following description and claims are not limited to the bibliographical meanings but are merely used to enable a clear and consistent understanding of the invention. Accordingly, it should be apparent to those skilled in the art that the following description of exemplary embodiments of the present invention is provided for illustration purpose only and not for the purpose of limiting the invention as defined by the appended claims and their equivalents.
The present invention is directed to a resistive switching memory stack for a three-dimensional structure. The resistive switching memory stack can be used for, but is not limited to, Resistive Random Access Memories (RRAMs), neuromorphic computing applications, and so forth.
In an embodiment, a metal-insulator-metal stack is formed. The bottom electrode is formed from TiN, deposited by Atomic layer Deposition (ALD), Chemical Vapor Deposition (CVD), or Physical Vapor Deposition (PVD). ALD HfO2 or Ta2O5 or ZrO2 are used as base oxides. The top electrode is formed as an ALD TiN/Si or N-doped(M)AlC/TiN stack, where M is a transition metal such as, but not limited to, Ti, Ta, and Nb. Regarding the top electrode, oxygen vacancy concentration is controlled by the TiN/doped(M)AlC thicknesses and Al % in the doped (M)AlC layer of the top electrode. Wherein the doped scavenging carbide electrode (doped (M)AlC) comprises a conductive doped carbide active layer between a conductive bottom metal-nitride barrier, and a conductive top metal-nitride cap. Wherein the conductive doped carbide active layer is deposited by alternating carbide and dopant-containing layers. Wherein the dopant-containing layers are Si or N. Wherein the Si layers are deposited using thermal CVD (e.g. silane, disilane, trisilane, exachlorodisilane, etc.) forming Al4SiC4 doped active layer. Wherein the SiN layers are deposited by thermal ALD (e.g. SiCl4/NH3 precursors). Wherein the dopent-containing layers are AlN and the AlN layers are deposited by thermal ALD (e.g. TMA/NH3).
The metal-insulator-metal stack can be all deposited by ALD and applicable to a 3D structure including, but not limited to any of the following: a Vertical Restive Random Access Memory (VRRAM); a deep Trench in Front End of Line (FEOL); a cylinder trench in Back End of Line (BEOL); and a fin structure. It is to be appreciated that the preceding 3D structures are merely illustrative and, thus, the present invention can be readily applied to other 3D structures are readily contemplated by one of ordinary skill in the art given the teachings of the present invention provided herein, while maintaining the spirit of the present invention.
As used herein, a “fin structure” refers to a semiconductor material, which is employed as the body of a semiconductor device, in which the gate structure is positioned around the fin structure such that charge flows down the channel on the two sidewalls of the fin structure and optionally along the top surface of the fin structure.
As used herein, a “metal” is an electrically conductive material, wherein metals atoms are held together by the force of metallic bonds, and the energy band structure of the metal's conduction and valence bands overlap, and hence, there is no energy gap.
As used herein, the term “memory device” means a structure in which the electrical state can be altered and then retained in the altered state, in this way a bit of information can be stored.
Atomic Layer Deposition (ALD) is a thin film deposition method in which a film is grown on a substrate by exposing its surface to alternate gaseous species (typically referred to as precursors). In contrast to chemical vapor deposition, the precursors in ALD are never present simultaneously in the reactor, but instead are inserted as a series of sequential, non-overlapping pulses. In each pulse, the precursor molecules react with the surface in a self-limiting way, so that the reaction terminates once all the reactive sites on the surface are consumed. Consequently, the maximum amount of material deposited on the surface after a single exposure to all of the precursors (a.k.a. an ALD cycle) is determined by the nature of the precursor-surface interaction. By varying the number of ALD cycles, it is possible to grow materials uniformly and with high precision on arbitrarily complex and large substrates such as three-dimensional structures.
The resistive switching memory stack 100 includes a bottom electrode 110, a metal oxide layer 120, and a top electrode 130. The metal oxide layer 120 is disposed over the bottom electrode 110, and the top electrode 130 is disposed over the metal oxide layer 120.
The bottom electrode 110 is formed from TiN. In an embodiment, the bottom electrode 110 is 10-50 nm thick.
The metal oxide layer 120 is formed from HfO2 or Ta2O5 or ZrO2. In an embodiment, the metal oxide layer 120 is 3-10 nm thick.
The top electrode 130 includes a bottom layer 131, an intermediate layer 132, and a top layer 133.
The bottom layer 131 is formed from TiN or TaN. In an embodiment, the bottom layer 131 is 0.3-3.0 nm thick.
The intermediate layer 132 is formed from a doped carbide (M)AlC, where M is a transition metal and can be, but is not limited to, e.g., Ti, Ta, Nb, and so forth. Wherein the carbide can be selected from a group consisting of AlxCy, Al4C3, or TixAlyCz. The doping material can be, for example, Si, N, or an equivalent. The doping material in the intermediate layer 132 prevents the scavenging of O from the dielectric layer (e.g. the metal oxide layer 120). The doping material in the intermediate layer 232 does decrease hydration potential and wet etchability, to chemistry such as H2O, NH4OH, H2O2, of the intermediate layer 232, without compromising the ability of the intermediate layer 232 to scavenge oxygen from the dielectric layer of the memory cell. The scavenging effect is needed to control the forming, set, and reset voltages of the cell, i.e. its fundamental operating principle. The etch resistance effect is needed to prevent undercut/delamination in the intermediate layer 232 post RIE pillar definition of the memory cell when exposed to wet chemistry, including etchants. The intermediate layer 132 can be comprised of a doped carbide, for example, Al4SiC4. Wherein the pillar cell contained in crossbar architecture do not exhibit an undercut of the intermediate layer 132 containing the conductive doped carbide active layer. In an embodiment, the intermediate layer 132 is 1-5 nm thick.
The top layer 133 is formed from TiN or TaN. In an embodiment, the top layer 133 is 10-50 nm thick.
It is to be appreciated that various changes can be made to the structure shown in
The resistive switching memory stack 200 includes a first low resistivity metal layer 205, a bottom electrode 210, a metal oxide layer 220, a top electrode 230, and a second low resistivity metal layer 240.
The bottom electrode 210 is disposed over the first low resistivity metal layer 205, the metal oxide layer 220 is disposed over the bottom electrode 210, the top electrode 230 is disposed over the metal oxide layer 220, and the second low resistivity metal layer 240 is disposed over the top electrode 230.
The first low resistivity metal layer 205 is formed from one or more of W, Al, and/or Cu.
The bottom electrode 210 is formed from TiN. In an embodiment, the bottom electrode 210 is 5-10 nm thick.
The metal oxide layer 220 is formed from HfO2 or Ta2O5 or ZrO2. In an embodiment, the metal oxide layer 220 is 3-10 nm thick.
The top electrode 230 includes a bottom layer 231, an intermediate layer 232, and a top layer 233.
The bottom layer 231 is formed from TiN or TaN. In an embodiment, the bottom layer 231 is 0.3-3.0 nm thick.
The intermediate layer 232 is formed from a doped carbide (M)AlC, where M is a transition metal. Wherein the carbide can be selected from a group consisting of AlxCy, Al4C3, or TixAlyCz. The doping material can be, for example, Si, N, or an equivalent. The doping material in the intermediate layer 232 does not prevent the scavenging of O from the dielectric layer (e.g. the metal oxide layer 120). The doping material in the intermediate layer 232 does decrease hydration potential and wet etchability, to chemistry such as H2O, NH4OH, H2O2, of the intermediate layer 232, without compromising the ability of the intermediate layer 232 to scavenge oxygen from the dielectric layer of the memory cell. The scavenging effect is needed to control the forming, set, and reset voltages of the cell, i.e. its fundamental operating principle. The etch resistance effect is needed to prevent undercut/delamination in the intermediate layer 232 post RIE pillar definition of the memory cell when exposed to wet chemistry, including etchants. The intermediate layer 232 can be comprised of a doped carbide, for example, Al4SiC4. Wherein the pillar cell contained in crossbar architecture do not exhibit an undercut of the intermediate layer 232 containing the conductive doped carbide active layer. In an embodiment, the intermediate layer 232 is 1-5 nm thick.
The top layer 233 is formed from TiN or TaN. In an embodiment, the top layer 233 is 1-3 nm thick.
The second low resistivity metal layer 240 is formed from one or more of W, Al, and/or Cu. It is to be appreciated that the metals can be the same or different between the first low resistivity metal layer 205 and the second low resistivity metal layer 240.
It is to be appreciated that the stacks shown in
At step 310, form a bottom electrode from TiN. In an embodiment, the bottom electrode 110 is 10-50 nm thick. Of course, other metals and/or thicknesses can be used for the bottom electrode, while maintaining the spirit of the present invention.
At step 320, form, over the bottom electrode, a metal oxide layer from HfO2 or Ta2O5 or ZrO2. In an embodiment, the metal oxide layer is 3-10 nm thick. Of course, other metals and/or thicknesses can be used for the metal oxide layer, while maintaining the spirit of the present invention.
At step 330, form, over the metal oxide layer, a top electrode having a bottom layer, an intermediate layer, and a top layer. The bottom layer 131 is formed from TiN or TaN. In an embodiment, the bottom layer 131 is 0.3-3.0 nm thick. The intermediate layer 132 is formed from a doped (M)AlC, where M is a transition metal and the doping material is Si, N or another suitable material. Wherein the intermediate layer 132, e.g., the doped scavenging carbide electrode (doped (M)AlC), is formed by alternating deposition of carbide and dopant-containing layers. Wherein the carbide can be selected from a group consisting of AlxCy, Al4C3, or TixAlyCz. The doping material in the intermediate layer 232 does decrease hydration potential and wet etchability, to chemistry such as H2O, NH4OH, H2O2, of the intermediate layer 232, without compromising the ability of the intermediate layer 232 to scavenge oxygen from the dielectric layer of the memory cell. The scavenging effect is needed to control the forming, set, and reset voltages of the cell, i.e. its fundamental operating principle. The etch resistance effect is needed to prevent undercut/delamination in the intermediate layer 232 post RIE pillar definition of the memory cell when exposed to wet chemistry, including etchants. Wherein the dopant-containing layers are Si or N. Wherein the Si layers are deposited using thermal CVD (e.g. silane, disilane, trisilane, exachlorodisilane, etc.) forming Al4SiC4 doped active layer. Wherein the SiN layers are deposited by thermal ALD (e.g. SiCl4/NH3 precursors). Wherein the dopent-containing layers are AlN and the AlN layers are deposited by thermal ALD (e.g. TMA/NH3). In an embodiment, the intermediate layer 132 is 1-5 nm thick. The top layer 133 is formed from TiN or TaN. In an embodiment, the top layer 133 is 10-50 nm thick. Of course, other metals and/or thicknesses can be used for each of the layers of the top electrode, while maintaining the spirit of the present invention.
At step 410, form a first low resistivity metal layer 205 from one or more of W, Al, and/or Cu. Of course, other metals can be used for the first low resistivity metal layer, while maintaining the spirit of the present invention.
At step 420, form, over the first low resistivity metal layer 205, a bottom electrode 210 from TiN. In an embodiment, the bottom electrode 210 is 5-10 nm thick. Of course, other metals and/or thicknesses can be used for the bottom electrode 210, while maintaining the spirit of the present invention.
At step 430, form, over the bottom electrode 210, a metal oxide layer 220 from HfO2 or Ta2O5 or ZrO2. In an embodiment, the metal oxide layer 220 is 3-10 nm thick. Of course, other metals and/or thicknesses can be used for the metal oxide layer 220, while maintaining the spirit of the present invention.
At step 440, form, over the metal oxide layer 220, a top electrode 230 having a bottom layer 231, an intermediate layer 232, and a top layer 233. The bottom layer 231 is formed from TiN or TaN. In an embodiment, the bottom layer 231 is 0.3-3.0 nm thick. The intermediate layer 232 is formed from a doped (M)AlC, where M is a transition metal, and the doping material is Si or N. Wherein the intermediate layer 232, e.g., the doped scavenging carbide electrode (doped (M)AlC), is formed by alternating deposition of carbide and dopant-containing layers. Wherein the carbide can be selected from a group consisting of AlxCy, Al4C3, or TixAlyCz. The doping material in the intermediate layer 232 does decrease hydration potential and wet etchability, to chemistry such as H2O, NH4OH, H2O2, of the intermediate layer 232, without compromising the ability of the intermediate layer 232 to scavenge oxygen from the dielectric layer of the memory cell. The scavenging effect is needed to control the forming, set, and reset voltages of the cell, i.e. its fundamental operating principle. The etch resistance effect is needed to prevent undercut/delamination in the intermediate layer 232 post RIE pillar definition of the memory cell when exposed to wet chemistry, including etchants. Wherein the dopant-containing layers are Si or N. Wherein the Si layers are deposited using thermal CVD (e.g. silane, disilane, trisilane, exachlorodisilane, etc.) forming Al4SiC4 doped active layer. Wherein the SiN layers are deposited by thermal ALD (e.g. SiCl4/NH3 precursors). Wherein the dopent-containing layers are AlN and the AlN layers are deposited by thermal ALD (e.g. TMA/NH3). In an embodiment, the intermediate layer 232 is 1-5 nm thick. The top layer 233 is formed from TiN or TaN. In an embodiment, the top layer 233 is 1-3 nm thick. Of course, other metals and/or thicknesses can be used for each of the layers of the top electrode 230, while maintaining the spirit of the present invention.
At step 450, form, over the top electrode 230, a second low resistivity metal layer 240 from one or more of W, Al, and/or Cu. Of course, other metals can be used for the second low resistivity metal layer 240, while maintaining the spirit of the present invention.
It is to be appreciated that for the sake of illustration, various metals and metal oxides and various thickness for the metals and metal oxides have been described herein. However, as readily appreciated by one of ordinary skill in the art given the teachings of the present invention provided herein, these and other metals and metal oxides can also be used, as well as other thicknesses, while maintaining the spirit of the present invention. For example, regarding the electrodes described herein, such electrodes may include any suitable conductive material, such as polycrystalline or amorphous silicon, germanium, silicon germanium, a metal (e.g., tungsten, titanium, tantalum, ruthenium, zirconium, cobalt, copper, aluminum, lead, platinum, tin, silver, gold), a conducting metallic compound material (e.g., tantalum nitride, titanium nitride, tungsten silicide, tungsten nitride, ruthenium oxide, cobalt silicide, nickel silicide), carbon nanotube, conductive carbon, graphene, or any suitable combination of these materials. The conductive material may further comprise dopants that are incorporated during or after deposition.
It is to be understood that aspects of the present invention will be described in terms of a given illustrative architecture; however, other architectures, structures, substrate materials and process features and steps can be varied within the scope of aspects of the present invention.
It will also be understood that when an element such as a layer, region or substrate is referred to as being “on” or “over” another element, it can be directly on the other element or intervening elements can also be present. In contrast, when an element is referred to as being “directly on” or “directly over” another element, there are no intervening elements present. It will also be understood that when an element is referred to as being “connected” or “coupled” to another element, it can be directly connected or coupled to the other element or intervening elements can be present. In contrast, when an element is referred to as being “directly connected” or “directly coupled” to another element, there are no intervening elements present.
The present embodiments can include a design for an integrated circuit chip, which can be created in a graphical computer programming language, and stored in a computer storage medium (such as a disk, tape, physical hard drive, or virtual hard drive such as in a storage access network). If the designer does not fabricate chips or the photolithographic masks used to fabricate chips, the designer can transmit the resulting design by physical means (e.g., by providing a copy of the storage medium storing the design) or electronically (e.g., through the Internet) to such entities, directly or indirectly. The stored design is then converted into the appropriate format (e.g., GDSII) for the fabrication of photolithographic masks, which typically include multiple copies of the chip design in question that are to be formed on a wafer. The photolithographic masks are utilized to define areas of the wafer (and/or the layers thereon) to be etched or otherwise processed.
Methods as described herein can be used in the fabrication of integrated circuit chips. The resulting integrated circuit chips can be distributed by the fabricator in raw wafer form (that is, as a single wafer that has multiple unpackaged chips), as a bare die, or in a packaged form. In the latter case, the chip is mounted in a single chip package (such as a plastic carrier, with leads that are affixed to a motherboard or other higher level carrier) or in a multichip package (such as a ceramic carrier that has either or both surface interconnections or buried interconnections). In any case, the chip is then integrated with other chips, discrete circuit elements, and/or other signal processing devices as part of either (a) an intermediate product, such as a motherboard, or (b) an end product. The end product can be any product that includes integrated circuit chips, ranging from toys and other low-end applications to advanced computer products having a display, a keyboard or other input device, and a central processor.
It should also be understood that material compounds will be described in terms of listed elements, e.g., SiGe. These compounds include different proportions of the elements within the compound, e.g., SiGe includes SixGe1-x where x is less than or equal to 1, etc. In addition, other elements can be included in the compound and still function in accordance with the present principles. The compounds with additional elements will be referred to herein as alloys.
Reference in the specification to “one embodiment” or “an embodiment”, as well as other variations thereof, means that a particular feature, structure, characteristic, and so forth described in connection with the embodiment is included in at least one embodiment. Thus, the appearances of the phrase “in one embodiment” or “in an embodiment”, as well any other variations, appearing in various places throughout the specification are not necessarily all referring to the same embodiment.
It is to be appreciated that the use of any of the following “/”, “and/or”, and “at least one of”, for example, in the cases of “A/B”, “A and/or B” and “at least one of A and B”, is intended to encompass the selection of the first listed option (A) only, or the selection of the second listed option (B) only, or the selection of both options (A and B). As a further example, in the cases of “A, B, and/or C” and “at least one of A, B, and C”, such phrasing is intended to encompass the selection of the first listed option (A) only, or the selection of the second listed option (B) only, or the selection of the third listed option (C) only, or the selection of the first and the second listed options (A and B) only, or the selection of the first and third listed options (A and C) only, or the selection of the second and third listed options (B and C) only, or the selection of all three options (A and B and C). This can be extended, as readily apparent by one of ordinary skill in this and related arts, for as many items listed.
The terminology used herein is for the purpose of describing particular embodiments only and is not intended to be limiting of example embodiments. As used herein, the singular forms “a,” “an” and “the” are intended to include the plural forms as well, unless the context clearly indicates otherwise. It will be further understood that the terms “comprises,” “comprising,” “includes” and/or “including,” when used herein, specify the presence of stated features, integers, steps, operations, elements and/or components, but do not preclude the presence or addition of one or more other features, integers, steps, operations, elements, components and/or groups thereof.
Spatially relative terms, such as “beneath,” “below,” “lower,” “above,” “upper,” and the like, can be used herein for ease of description to describe one element's or feature's relationship to another element(s) or feature(s) as illustrated in the FIGS. It will be understood that the spatially relative terms are intended to encompass different orientations of the device in use or operation in addition to the orientation depicted in the FIGS. For example, if the device in the FIGS. is turned over, elements described as “below” or “beneath” other elements or features would then be oriented “above” the other elements or features. Thus, the term “below” can encompass both an orientation of above and below. The device can be otherwise oriented (rotated 90 degrees or at other orientations), and the spatially relative descriptors used herein can be interpreted accordingly. In addition, it will also be understood that when a layer is referred to as being “between” two layers, it can be the only layer between the two layers, or one or more intervening layers can also be present.
It will be understood that, although the terms first, second, etc. can be used herein to describe various elements, these elements should not be limited by these terms. These terms are only used to distinguish one element from another element. Thus, a first element discussed below could be termed a second element without departing from the scope of the present concept.
Having described preferred embodiments of an apparatus and method (which are intended to be illustrative and not limiting), it is noted that modifications and variations can be made by persons skilled in the art in light of the above teachings. It is therefore to be understood that changes may be made in the particular embodiments disclosed which are within the scope of the invention as outlined by the appended claims. Having thus described aspects of the invention, with the details and particularity required by the patent laws, what is claimed and desired protected by Letters Patent is set forth in the appended claims.