Patent Grant
11992981
The present invention relates to a method for producing expanded polymer pellets, the polymer pellets obtained therewith as well as their use, such as for producing cushioning elements, for example for sports apparel or sports shoes. The present invention further relates to a method for the manufacture of molded components using expanded polymer pellets, articles obtained therewith and the use of the articles, such as for sound insulation.
Expanded polymers or polymer foams are well known from the prior art. From WO 2006/077395 A1, closed-cell polyamide foams are known, which are produced in the form of sheets and can be further processed to form e.g. seals.
WO 2006/045513 A1 and EP 1 650 255 A1 describe the production of a cross-linked foam of a copolymer having polyamide blocks and polyether blocks and the use of the foam. WO 2007/082838 A1 relates to expandable, blowing agent-containing thermoplastic polyurethane having a specific hardness. In a similar manner, WO 2010/010010 A1 relates to an expandable, blowing agent-containing thermoplastic polymer blend comprising thermoplastic polyurethane and styrene polymer. DE 10 2011 108 744 A1 is directed towards a method for the production of shoe soles, wherein plastic bodies made from foamed thermoplastic elastomer on the basis of urethane (TPU) or on the basis of polyetherblockamide (PEBA) are used.
Compared to this, the objective of the present invention is to provide expanded polymer pellets that can be produced in as wide a processing window as possible and that can be further processed to form stable parts which can be used in a broad area of application, e.g. for the production of parts having damping properties and a low weight. A further objective is to provide an improved method for the manufacture of molded components or articles from expanded polymer pellets.
According to a first aspect, this objective is solved by a method for producing expanded polymer pellets, which comprises the following steps:
The invention further concerns polymer pellets produced with the method as well as their use, e.g. for the production of cushioning elements for sports apparel, in particular for producing soles or parts of soles of sports shoes. In addition, the invention concerns a shoe, in particular a sports shoe, with such a sole.
The polyamide may, for example, comprise as a basis a polyamide, a copolyamide and/or a polyetherblockamide. Furthermore, the polyetherblockamide may comprise at least one of the following features:
The blowing agent may be selected from nitrogen, carbon dioxide, ethanol, isopropanol, or mixtures thereof. Furthermore, a nucleating agent, a chain extender, or both may be added in step b.
It is possible that the die is a round die. The pressure at the die may lie in the range of 70 to 250 bar. The mass temperature at the die may lie in the range from 150° C. to 170° C.
It is possible that the expanded polymer is pelletized in an underwater pelletizing device.
A further aspect of the invention concerns expanded polymer pellets, which are obtainable by a method described above. The pellets may comprise a size in the range from 2 to 10 mm when measured according to ISO 9276. Moreover, the pellets may comprise a particle density in the range from 20 to 400 kg/m3. Furthermore, the pellets may comprise a mean cell diameter in the range from 10 to 350 □m.
A further aspect of the invention concerns the use of the expanded polymer pellets for producing cushioning elements for sports apparel, in particular for producing soles for shoes.
A further aspect of the invention concerns a cushioning element for sports apparel, in particular a sole for a shoe or a part thereof, produced using the expanded polymer pellets described above.
A further aspect of the invention concerns a shoe, in particular a sports shoe, with a sole as described above.
A further aspect of the invention concerns expanded polymer pellets which are based on polyamide, and exhibit a variation of less than 50% in their storage modulus in the temperature range of −40° C. to +40° C.
A second aspect of the invention relates to a method for the manufacture of molded components, comprising
In an exemplary embodiment the chain extender has been provided after a polymerization of the polymer material.
In another exemplary embodiment, the expanded polymer material comprises a semi-crystalline polymer.
In step b, the heat energy can be provided by means of at least one of the following: pressurized steam, electromagnetic radiation, radio frequency radiation, microwave radiation, infrared radiation, ultraviolet radiation, electromagnetic induction.
In one embodiment, during step b. the pellets are heated to a temperature between a glass transition temperature and below the onset of melting of the expanded polymer material. In exemplary embodiments, the pellets are heated up to a range of from 100° C. to 5° C. below the melting point of the expanded polymer material. They may be heated up to a range of from 60° C. to 5° C. below the melting point of the expanded polymer material, such as 40° C. to 5° C. below the melting point of the expanded polymer material.
The chain extender can comprise at least one selected from a polymeric material containing epoxy groups, pyromellitic dianhydride, and styrene maleic anhydride, or combinations of one or more thereof. In one embodiment, the chain extender is a styrene-acrylate copolymer containing reactive epoxy groups, such as a compound of the following formula:
wherein R1 to R5 are H, CH3, a higher alkyl group, or combinations of them; R6 is an alkyl group, and x, y, and z are each between 1 and 20.
In another embodiment, the chain extender is selected from one or more of a tri-epoxide or tetra-epoxide. The chain extender may be, for example, triglycidyl isocyanurate and/or tetraglycidyl diamino diphenyl methane. In another embodiment, the chain extender is selected from one or more of styrene maleic anhydride. In a further embodiment, the chain extender is pyromellitic dianhydride.
In one embodiment, the polymer is selected from at least one of polyamides, polyester, polyetherketones, and polyolefins. The polyamide can be at least one of homopolyamide, copolyamide, polyetherblockamide, and polyphthalamide. The polyester can be at least one of polybutylene terephthalate (PBT), thermoplastic polyester ether elastomer (TPEE), and polyethylene terephthalate (PET). The polyetherketone can be at least one of polyether ketone (PEK), polyether ether ketone (PEEK), and polyetherketoneketone (PEKK). The polyolefin can be at least one of polypropylene (PP), polyethylene (PE), olefin co-block polymer (OBC), polyolefine elastomer (POE), polyethylene co-vinyl acetate (EVA), polybutene (PB), and polyisobutylene (PIB).
In another embodiment, the polymer is selected from at least one of polyoxymethylene (POM), polyvinylidene chloride (PVCD), polyvinylalcohol (PVAL), polylactide (PLA), polytetrafluoroethylene (PTFE), polyvinylidene fluoride (PVDF), tetrafluoroethylene (FEP), ethylene-tetrafluoroethylene (ETFE), polyvinylfluoride (PVF), perfluoroalkoxy (PFA), and thermoplastic polyurethanes (TPU).
In an exemplary embodiment, the polymer comprises polybutylene terephthalate (PBT) and the chain extender comprises at least one selected from a polymeric material containing epoxy groups, pyromellitic dianhydride, styrene maleic anhydride, or combinations of one or more thereof, in particular a styrene-acrylate copolymer containing reactive epoxy groups. In another exemplary embodiment, the polymer comprises polyamide (PA) or polyetherblockamide (PEBA) and the chain extender comprises at least one selected from a polymeric material containing epoxy groups, pyromellitic dianhydride, styrene maleic anhydride, or combinations of one or more thereof, in particular a styrene-acrylate copolymer containing reactive epoxy groups. In a further exemplary embodiment, the polymer comprises thermoplastic polyester ether elastomer (TPEE) and the chain extender comprises at least one selected from a polymeric material containing epoxy groups, pyromellitic dianhydride, styrene maleic anhydride, or combinations of one or more thereof, in particular a styrene-acrylate copolymer containing reactive epoxy groups.
A further aspect of the invention relates to a method for the manufacture of molded components, comprising
In one embodiment of the manufacture method of the second or further aspect, the pellets are produced by a method comprising the steps of:
In some embodiments, the pellets are produced by the method according to the first aspect of the invention.
The chain extender may be added in an amount to provide amorphous regions in the expanded polymer material allowing interdiffusion of polymer chains across the interfaces of the pellet boundaries, in particular in an amount of 0.1 to 20% by weight, more particular 1% to 10% by weight, such as 1% to 5% by weight, based on 100% by weight of the base polymer material.
The base polymer material may be a polyamide, for instance at least one of homopolyamide, copolyamide, polyetherblockamide, and polyphthalamide, as an example, polyamide 12.
The chain extender may be a polymeric material containing epoxy groups, such as a styrene-acrylate copolymer containing reactive epoxy groups.
It is possible that the pellets of the expanded material have internally an at least partially ruptured foam structure.
A further aspect of the invention concerns an article, which is obtainable by the method described above with respect to the second or further aspect of the invention.
In an exemplary embodiment, the article is produced using pellets of the expanded material that may have internally an at least partially ruptured foam structure. Such an article may be used for e.g. sound insulation.
Another aspect concerns an article as described above, wherein the article is provided as at least one of the following: a packaging material, a reusable packaging material, a pallet, an article for medical transportation, an article for chemical transportation, an article for breakable goods transportation, an article for interior insulation, an article for exterior insulation, an article for pipe insulation, a geofoam, a temporary housing, a road crash protection, an article for appliance insulation, an article for industrial appliance insulation, a sun visor, a dash board, a car seat, a center console, a car door, a child/baby seat, an article for battery cover/insulation, an article for engine insulation, a bumper, a crash structure, a protective helmet, an article of protective clothing, a boat fender, a medical stretcher, a surf/rescue board, a buoy, a boat hull, a snowmobile seat, a core for skis/snowboards/water skis/wakeboards, a jet ski seat, an artificial turf, a venue or playground flooring, a sports hall protective flooring/wall, a conditioning roller, a resistance weight for aerobics, a swimming aid, an article of furniture, a bean bag, a cow mat, a drone, an article of luggage, a plane seat, a plane/glider wing, an article for aeroplane cabin insulation, a plane food tray, an article for airline food trolley insulation, an under floor, an article for heating protection, an article of advanced protective equipment, a medical cast, a turbine/rotor blade core, a run-flat tyre, hand grips, beverage insulation, lamp covers, mattresses.
Another aspect concerns the use of an article produced with the method according to the second or further aspect of the invention, in the production of cushioning elements for sports apparel, in particular for the production of soles for shoes, preferably midsoles.
Another aspect concerns the use of an article produced with the method according to the second or further aspect of the invention, for packaging applications, reusable packaging, pallets, medical transportation, chemical transportation, breakable goods transportation, interior insulation, exterior insulation, pipe insulation, geofoam, temporary housing, road crash protection, appliance insulation, industrial appliance insulation, sun visor, dash board, car seat, center console, car door, child/baby seat, battery cover/insulation, engine insulation, bumper, crash structures, protective helmet, protective clothing, boat fenders, medical stretchers, surf/rescue boards, buoys, boat hulls, snowmobile seats, core for skis/snowboards/water skis/wakeboards, jet ski seat, artificial turf, venue or playground flooring, sports hall protective flooring/walls, conditioning roller, resistance weights for aerobics, swimming aids, furniture, bean bags, cow mats, drones, luggage, plane seats, plane/glider wings, aeroplane cabin insulation, plane food tray, airline food trolley insulations, under floor, heating protection, advanced protective equipment, medical cast, turbine/rotor blade core, a run-flat tyre, hand grips, beverage insulation, lamp covers, mattresses.
A further aspect of the invention concerns a shoe, comprising an element, in particular a sole, obtainable by a method described above with respect to the second or further aspect of the invention. Another aspect of the invention concerns a shoe comprising a foam element molded by using a method described above with respect to the second or further aspect of the invention.
Preferred embodiments of the invention are described in the following description, the figures and the claims.
The figures show:
In the following detailed description, preferred examples and embodiments of the invention are described.
First Aspect of the Invention
The polymer used for the production of the expanded polymer pellets comprises at least one polyamide. The polymer can be on the basis of a polyamide. In particular, the polymer can comprise at least 10% by weight, in particular at least 30% by weight, preferably at least 50% by weight, of a polyamide, in each case based on 100% by weight of the polymer. Preferred ranges are 10 to 99% by weight, preferably 25 to 99% by weight, more preferably 50 to 99% by weight, of polyamide, in each case based on 100% by weight of the polymer. It is also possible that the polymer comprises or consists of 100% by weight of polyamide.
The polymer can be on the basis of a polyamide. In particular, the polymer can comprise at least 10% by weight, in particular at least 30% by weight, preferably at least 50% by weight, of a polyamide, in each case based on 100% by weight of the polymer. Preferred ranges are 10 to 99% by weight, preferably 25 to 99% by weight, more preferably 50 to 99% by weight, of polyamide, in each case based on 100% by weight of the polymer. It is also possible that the polymer comprises or consists of 100% by weight of polyamide.
Suitable polymers are polyamides or polyamide-containing polymers that are expandable. Particularly suitable are those having a tensile modulus above 10 MPa and/or having a low temperature dependency. Suitable are, for example, polyamide-6 (PA 6), polyamide-6.6 (PA 6.6), polyamide-6.10 (PA 6.10), polyamide-11 (PA 11), polyamide-12 (PA 12), polyamide-10.12, or polyamide-10.10. Also combinations thereof can be used. Particularly well suited is PA 11 or PA 12, or a mixture thereof. Preferably, PA 12 is used. Suitable polyamides or polyamide-containing polymers are commercially available.
Particularly well suited is polyetherblockamide (PEBA). Polyetherblockamide is a blockcopolymer with polyamide-segments and polyether-segments. For example, suitable polyetherblockamides comprise a content of polyether-blocks from 1 to 90% by weight, in particular from 1 to 50% by weight, and a content of polyamide-blocks from 10 to 99% by weight, in particular from 50 to 99% by weight, in each case based on 100% by weight of the polyetherblockamide. It is also possible to use blends or mixtures of two or more, in particular two, different polyetherblockamides. It is further possible that the polymer comprises or consists of 100% by weight of polyetherblockamides. It is further possible that the polymer comprises or consists of 100% by weight of polyamide and polyetherblockamides.
Particularly well suited are furthermore polyetherblockamides which comprise at least one of the following properties:
Herein, the Shore D hardness is measured according to ISO 868. The tensile modulus is measured according to ISO 527-1. The density is measured according to ISO 1183. In the present invention, the melting point or melting range, respectively, relates to a measurement according to ISO 11357. Herein, the melting point or melting range, respectively, of the polymer designates the point or range at or within which the crystalline regions of a semi crystalline polymer melt.
Suitable polyetherblockamides are commercially available. They may be produced by known methods, e.g. by means of copolycondensation of polyamide-blocks containing reactive ends with polyether-blocks containing reactive ends such as described in WO 2006/045513 A1.
From among the mentioned polyamides and polyetherblockamides, mixtures or blends thereof might be used as well. The polymer for producing the expanded polymer pellets may contain or be blended with another polymer in addition to the polyamide, for example, thermoplastic polyurethane (TPU), polyphenylene ether (PPE), styrene-acrylonitrile (SAN), and/or rubber, in particular TPU. The content of the other polymer may be below 50% by weight, in particular below 10% by weight, preferably below 5% by weight, based on 100% by weight of the polymer. In one embodiment, the polymer used for producing the expanded pellets comprises no (i.e. 0%) thermoplastic polyurethane. In one embodiment the polymer used for producing the expanded pellets comprises no (i.e. 0%) other polymer than the polyamide.
The polymer used for producing the expanded pellets may be used in any form, for example as granulate or powder, in particular as granulate. Suitable forms of the polymers are commercially available. In case that the base or starting polymer contains adherent humidity or water, the polymer is preferably dried before melting and drying is completed prior to foaming, in accordance with procedures known to the skilled person.
In the first step of the method according to the invention, the polymer is melted. Suitable methods for melting or fusing are known to the person skilled in the art. The melting may, for example, be done in an extruder. Suitable extrusion devices or extruders are not subject to any restrictions. Common extruders or commercially available extruders can be used, for example single screw or twin screw extruders. The extruder also serves to homogeneously disperse the polymer.
The dimensioning of the extruders (e.g. design, length and number of revolutions of the extruder screws, temperature profile, pressure) may be chosen by the skilled person, such that added materials are homogeneously dispersed and intermixed into the melted polymer. The extruder is usually operated at a temperature at which the polymer material is completely melted. Suitable temperatures depend on the polymer used and can be routinely determined by the skilled person, for example, for polyamide 12 suitable temperatures are in the range from 180 to 320° C., in particular from 220 to 290° C.
It is also possible to use two extruders arranged in series. Good results are, for example, obtained, if the first extruder is a twin screw extruder and the second extruder is a single screw extruder. The first extruder is used to plasticize the material and homogeneously disperse additional materials, e.g. a blowing agent. Due to the inclusion of the blowing agent, the viscosity of the material is significantly reduced, and the second extruder could be used to cool down the material in order to improve the melt properties and increase the pressure needed for foaming expansion. This can also be achieved by employing a single extruder being sufficiently long to allow the material to be heated and then cooled in a controlled way. Additionally, it is possible to insert a static mixer between the first and second extruder. Suitable temperatures for the first extruder lie in the range from 170 to 320° C., in particular in the range from 170 to 220° C. or from 220 to 290° C. Suitable temperatures for the second extruder depend stronger on the used polymer, e.g. for polyamide 12 a mass temperature in the range from 150 to 190° C., in particular from 165 to 180° C., is suitable, and for polyetherblockamide a mass temperature in the range from 130 to 180° C., in particular from 155 to 165° C., is suitable.
An exemplary arrangement 1 is shown in
In one embodiment, at least one blowing agent is added to the melted polymer. In general, volatile liquids, gases, and decomposable compounds that are inert with respect to the polymer melt under the conditions present in the extruder and which form a gas, are suitable as a blowing agent. Suitable blowing agents are nitrogen, carbon dioxide, ethanol, isopropanol, or mixtures thereof. Particularly well suited is supercritical carbon dioxide, or a mixture of supercritical carbon dioxide with ethanol. The blowing agent may be fed to the extruder with the base polymer with or without being previously mixed. Alternatively, the blowing agent may be added to the polymer melt at a suitable location of the extruder and be intermixed within the extruder. Suitably, the blowing agent is homogeneously dispersed in the polymer or melted polymer. The amount of added blowing agent lies in the range from 1 to 20% by weight, in particular from 1 to 10% by weight, in each case based on 100% by weight of the polymer melt. Particular amounts of blowing agent are 1, 2, 3, 4, 5, 7.5, 10 or 15% by weight, based on 100% by weight of the polymer melt. Particularly suitable is e.g. a carbon dioxide-ethanol mixture with 2 to 6% by weight of carbon dioxide and 2 to 4% by weight of ethanol, based on 100% by weight of the polymer melt.
In addition to the blowing agent, further conventional additives or materials that facilitate the processing may be added to the polymer melt in the extruder, for example, a nucleating agent, a chain extender, flame inhibitors, plasticizers, reinforcing agents, pigments, dyes, heat- or light-stabilizers, antistatic agents, fillers, or mixtures thereof. Suitable nucleating agents are additives which can be both soluble and not soluble in the polymer melt to promote foam cell nucleation. Examples of non-soluble nucleating agents include talc, or silica. It is also possible to add a crosslinking agent to the polymer melt. Crosslinking agents are described e.g. in WO 2006/045513 A1 and EP 1 650 255 A1. In one embodiment, no crosslinking agent is used, or the polymer pellets are not crosslinked.
In one embodiment, at least one chain extender is added to the polymer melt. It is also possible to feed at least one chain extender together with the polymer to the extrusion device. Suitable chain extenders are compounds which increase the melt strength of the polymer melt. Particularly suitable chain extenders are oligomeric or polymeric compounds with reactive groups, e.g. epoxy groups, which react with the melted polymer to increase the molecular weight and degree of branching, thus improving the rheological properties, such as the melt viscosity and the melt strength of the polymer used. Suitable chain extenders can be based on styrene-acrylate copolymers and are commercially available, e.g. Joncryl® ADR-4368C of BASF. Suitable amounts of chain extender are 0.05 to 10% by weight, in particular 0.1 to 5% by weight or 0.1 to 3% by weight, based on 100% by weight of the polymer. The use of chain extenders is particularly beneficial when using polyetherblockamides as polymers for the production of the expanded pellets. In another exemplary embodiment, a peroxide is used as chain extender for initiating chain extension, such as an organic peroxide, e.g. dicumyl peroxide. The use of a peroxide is described in the article “Structure Modification of Isotactic Polypropylene through Chemical Crosslinking: Toughening Mechanism” of S. Bouhelal et al., Journal of Applied Polymer Science DOI 10.1002/app (Vol. 103, 2968-2976 (2007)).
In one embodiment, the polymer for producing the expanded pellets comprises polyetherblockamide or consists of polyetherblockamide, and a chain extender is added as additional material to the polymer melt.
In addition, it is also possible to melt the polymer together with granulate made of used tires (rubber) and caoutchouc powder. The thermal decomposition of the compounds in the extruder leads to the formation of cracked gas (nitrogen and carbon monoxide), which can act as blowing agent, and carbon, which can act as reinforcing and nucleating agent.
After extrusion the melt is expanded through a die. The die may, for example, be a round die or a slit die, in particular a round die. The diameter of the die depends on the size of the extruder, the desired particle size and density, and may be e.g. in the range from 1 to 5 mm. Expediently, the die is attached to the extruder. The pressure at the die depends on the polymer material used and density specification, and may lie in the range from 40 to 400 bar, in particular in the range from 60 to 250 bar. Preferably, for polyamide the pressure may lie in the range from 80 bar to 220 bar, and for polyetherblockamide the pressure may lie in the range from 45 bar to 200 bar. The mass temperature at the die depends on the polymer melt and may lie in the range from 140 to 180° C., in particular from 150 to 170° C.
Inside the die and particularly after leaving the die, the melt is subjected to a sudden pressure drop and the polymer expands or foams. Depending on the shape of the die, the expanded or foamed polymer is obtained as a strand or a foil. Preferably, a round die is used to obtain a strand. The expanded polymer or foam is stabilized by cooling. Cooling can be done in an under-water pelletizing device, a water bath, a conveyor belt, or a calibration unit where the geometry of the foam strand also can be adjusted.
Subsequently, the expanded polymer is pelletized. Suitable pelletizing devices are known to the skilled person, e.g. an under-water pelletizing device or an under-water granulator. The pelletizing may, for example, be performed in an under-water pelletizing device which enables both controlled cooling of the expanded polymer and pelletizing. Such devices are commercially available. Their operation is based on the principle that the polymer strand leaving the die is cut into discrete particles in a cutting chamber that is completely filled with water. The dimensions of the cut particles depend upon the cutting speed and throughput of the extruder/die and also the dimensions of the die. Suitable temperatures for the water in the cutting chamber are in the range of from 20 to 100° C., in particular from 50 to 100° C., preferably from 70 to 90° C. Due to the temperature difference between the extrudate having been expanded through the die and the water in the cutting chamber, the polymer immediately solidifies in form of particles, preferably sphere-like particles. The pelletizing device is expediently positioned directly after the die. A suitable under-water pelletizing device is for example shown in
Herein, as a further example, the pelletizing of the expanded polymer can be performed in a pelletizing chamber or granulating chamber using a liquid. A suitable liquid is a liquid that can be temperature-controlled and allows to adjust temperature and pressure. A suitable liquid is e.g. water.
The shape and size of the expanded polymer pellets can be adjusted by e.g. the throughput in the extruder, the shape of the die, the temperature and pressure at the die, the water temperature and water pressure in an under-water pelletizer, the cutting speed of the blades of the pelletizer. The selection of suitable conditions lies within the routine skill and knowledge of the skilled person.
The expanded polymer pellets may have a spherical shape, an ellipsoid shape, or triangular shape. Preferably, the pellets have substantially spherical shape. If the pellets are essentially spherical in shape, they may, for example, comprise a size from 2 to 10 mm when measured according to ISO 9276, and a particle density in the range from 20 to 400 kg/m3, e.g. from 50 to 300 kg/m3. Suitable mean cell diameters are within the range from 10 to 350 □m. In one embodiment, the smallest diameter (dimension) of the expanded polymer pellets is 10 mm.
The invention also concerns expanded polymer pellets which are based on polyamide, and exhibit a variation of less than 40%, preferably a variation in the range of 30 to 40%, in their storage modulus in the temperature range of −40° C. to +40° C. Preferably, they have a density in the range of from 70 to 100 kg/m3.
The invention further concerns expanded polymer pellets which are based on polyetherblockamide, and when formed into a test plate exhibit a relative energy loss during a full hysteresis cycle (after 10 or more cycles) in the range from 10 to 90%, preferably from 10 to 35%. Preferably, they have a density in the range of from 50 to 90 kg/m3. Herein, the relative energy loss during a full hysteresis cycle designates the quotient of the area (integral) within the hysteresis loop divided by the total energy exerted during compression, i.e. the area (integral) under the compression branch of the hysteresis loop in a force versus compressive strain (displacement) diagram. This is illustrated in
The expanded polymer pellets can be used in a wide range of applications. The expanded polymer pellets may be processed to form components that are very light-weight and show good temperature performance and temperature independence. They can be processed to produce components exhibiting light-weight, good elasticity and good energy resilience in a wide temperature range.
The expanded polymer pellets are therefore very well suited for producing cushioning elements or components with cushioning properties, such as for sport apparel, for example for producing soles for shoes, in particular sports shoes. To this end, the expanded polymer pellets are expediently loaded into a mold comprising a cavity having a shape that corresponds to the component being produced. Therein, the expanded polymer pellets are connected to each other, in particular by letting heat act on them, for example by feeding pressurized steam to the mold.
The invention also concerns sports apparel and shoes, in particular sports shoes, produced using of the expanded polymer pellets.
Other applications of use for the expanded polymer pellets are areas where cushioning or damping properties and high stability within a large temperature range are desirable, e.g. in the automotive sector or aviation industry. They also can be used to form components having good energy absorbing properties. They are, for example, suitable in components for automotive crash protection.
Second Aspect of the Invention
In a second aspect, the invention concerns a method for the manufacture of molded components, comprising loading pellets or beads of an expanded polymer material into a mold, and connecting the pellets or beads by providing heat energy, wherein the expanded polymer material of the pellets or beads comprise a chain extender. The terms “pellets” and “beads” are used interchangeably herein.
As an example, the chain extender can be provided after a polymerization of the polymer material. For example, the chain extender can be added in a separate compounding step and/or immediately before expanding the polymer material. The chain extender may be incorporated into the base polymer material that is used for the production of the pellets of the expanded polymer material. The chain extender may be added to the base polymer in a compounding stage. Alternatively, the base polymer may be first supplied to the polymer processing apparatus, e.g. an extruder, via a supply, e.g. a hopper, and then the chain extender may be added.
For connecting the pellets, heat energy may be provided in a variety of different ways. The heat energy may for example be provided in the form of pressurized steam that is supplied to the molding tool. Alternatively or in addition, the heat energy may also be provided by means of an electromagnetic field. The heat energy may for example be provided by irradiating the molding tool and/or the pellets with electromagnetic radiation. The electromagnetic radiation may for example be selected from one or more of the following frequency ranges: radio frequency radiation (30 kHz-300 MHz), microwave radiation (300 MHz-300 GHz), infrared radiation (300 GHz-400 THz), ultraviolet radiation (789 THz-3 PHz), or from another frequency range.
The heat energy may also be provided by means of electromagnetic induction. An energy absorbing material may be added to the pellets, to increase the amount of heat energy absorbed by the pellets, for example when irradiated with electromagnetic radiation or being heated by electromagnetic induction. All of the above mentioned possibilities may be combined with one another.
During step b. the pellets can be heated to a temperature between a glass transition temperature and below the onset of melting of the expanded polymer material. This heating leads to an increase of the amorphous chain mobility and to bead to bead fusion of the expanded polymer pellets. As an example, the heating is preferably conducted above a glass transition temperature of the expanded polymer material. In exemplary embodiments, the pellets are heated up to a range of from 100° C. to 5° C. below the melting point of the expanded polymer material. They may be heated up to a range of from 60° C. to 5° C. below the melting point of the expanded polymer material, such as 50° C. to 5° C. below or 40° C. to 5° C. below the melting point of the expanded polymer material.
The term “onset of melting” as used herein means the temperature at which the polymer material starts to melt. This may be determined e.g. according to DSC (differential scanning calorimetry), such that, in a diagram of heat flow versus temperature, the temperature at which the heat flow increases indicates the onset of melting. The term “melting point” as used herein, means e.g. the melting peak obtained by DSC. Suitable conditions for DSC are e.g. a heating rate of 10K/min for a temperature range of 25° C. to 250° C. The glass transition temperature of the expanded polymer material also can be determined by, for example, DSC.
The chain extender can comprise at least one compound selected from a polymeric material containing epoxy groups, pyromellitic dianhydride, and styrene maleic anhydride, or combinations of two or more thereof. Suitable chain extenders are styrene-acrylate copolymers containing reactive epoxy groups, for example, a compound of the following formula:
wherein R1 to R5 are H, CH3, a higher alkyl group, or combinations of them; R6 is an alkyl group, and x, y, and z are each between 1 and 20. Such a chain extender is commercially available as Joncryl® ADR-4368C (of BASF)
The chain extender also may be a tri-epoxide, tetra-epoxide, or a combination thereof. Suitable chain extenders are, for example, triglycidyl isocyanurate and/or tetraglycidyl diamino diphenyl methane. Another suitable chain extender is a styrene maleic anhydride. A further suitable chain extender is pyromellitic dianhydride.
The chain extender also may be a peroxide, for example an organic peroxide, e.g. dicumyl peroxide. The use of a peroxide is described in the article “Structure Modification of Isotactic Polypropylene through Chemical Crosslinking: Toughening Mechanism” of S. Bouhelal et al., Journal of Applied Polymer Science DOI 10.1002/app (Vol. 103, 2968-2976 (2007)).
The expanded polymer material may comprise a semi-crystalline polymer, or a polymer blend containing at least one semi-crystalline polymer.
The polymer of the expanded polymer material may be polyamide, polyester, polyetherketone, polyolefin, or a combination thereof. The polyamide can be homopolyamide, copolyamide, polyetherblockamide, polyphthalamide, or a combination thereof. A very suitable material is polyetherblockamide (PEBA). Generally the polyamides can be the same polyamides as defined above in the context of the first aspect of the invention. The polyester can be polybutylene terephthalate (PBT), thermoplastic polyester ether elastomer, (TPEE), polyethylene terephthalate (PET), or a combination thereof. The polyetherketone can be polyether ketone (PEK), polyether ether ketone (PEEK), polyetherketoneketone (PEKK), or a combination thereof. The polyolefin can be polypropylene (PP), polyethylene (PE), olefin co-block polymer (OBC), polyolefine elastomer (POE), polyethylene co-vinyl acetate (EVA), polybutene (PB), polyisobutylene (PIB), or a combination thereof.
Other suitable polymers are polyoxymethylene (POM), polyvinylidene chloride (PVCD), polyvinylalcohol (PVAL), polylactide (PLA), polytetrafluoroethylene (PTFE), polyvinylidene fluoride (PVDF), tetrafluoroethylene (FEP), ethylene-tetrafluoroethylene (ETFE), polyvinylfluoride (PVF), perfluoroalkoxy (PFA), thermoplastic polyurethane (TPU), or a combination thereof.
As an example, the polymer comprises polybutylene terephthalate (PBT) and the chain extender comprises a polymeric material containing epoxy groups. As a further example, the polymer comprises PBT and the chain extender comprises pyromellitic dianhydride. As a further example, the polymer comprises PBT and the chain extender comprises styrene maleic anhydride. As a further example, the polymer comprises PBT and the chain extender comprises a styrene-acrylate copolymer containing reactive epoxy groups, or e.g. Joncryl® ADR-4368C.
As another example, the polymer comprises polyamide, such as polyamide 12, or polyetherblockamide (PEBA), and the chain extender comprises a polymeric material containing epoxy groups. As a further example, the polymer comprises polyamide, such as polyamide 12, or polyetherblockamide (PEBA), and the chain extender comprises pyromellitic dianhydride. As a further example, the polymer comprises polyamide, such as polyamide 12, or polyetherblockamide (PEBA), and the chain extender comprises styrene maleic anhydride. As a further example, the polymer comprises polyamide, such as polyamide 12, or polyetherblockamide (PEBA), and the chain extender comprises a styrene-acrylate copolymer containing reactive epoxy groups or e.g. Joncryl® ADR-4368C.
In a further exemplary embodiment, the polymer comprises thermoplastic polyester ether elastomer (TPEE) and the chain extender comprises a polymeric material containing epoxy groups. As a further example, the polymer comprises TPEE and the chain extender comprises pyromellitic dianhydride. As a further example, the polymer comprises TPEE and the chain extender comprises styrene maleic anhydride. As a further example, the polymer comprises TPEE and the chain extender comprises a styrene-acrylate copolymer containing reactive epoxy groups or e.g. Joncryl® ADR-4368C.
In a further exemplary embodiment, the polymer comprises polylactide (PLA) and the chain extender comprises a polymeric material containing epoxy groups. As a further example, the polymer comprises PLA and the chain extender comprises pyromellitic dianhydride. As a further example, the polymer comprises PLA and the chain extender comprises styrene maleic anhydride. As a further example, the polymer comprises PLA and the chain extender comprises a styrene-acrylate copolymer containing reactive epoxy groups or e.g. Joncryl® ADR-4368C.
In a further exemplary embodiment, the polymer comprises polyethylene terephthalate (PET) and the chain extender comprises a polymeric material containing epoxy groups. As a further example, the polymer comprises PET and the chain extender comprises pyromellitic dianhydride. As a further example, the polymer comprises PET and the chain extender comprises styrene maleic anhydride. As a further example, the polymer comprises PET and the chain extender comprises a styrene-acrylate copolymer containing reactive epoxy groups or e.g. Joncryl® ADR-4368C.
In a further exemplary embodiment, the polymer comprises polyoxymethylene (POM) and the chain extender comprises a polymeric material containing epoxy groups. As a further example, the polymer comprises POM and the chain extender comprises pyromellitic dianhydride. As a further example, the polymer comprises POM and the chain extender comprises styrene maleic anhydride. As a further example, the polymer comprises POM and the chain extender comprises a styrene-acrylate copolymer containing reactive epoxy groups or e.g. Joncryl® ADR-4368C.
In a further aspect, the invention concerns a method for the manufacture of molded components, comprising loading pellets of an expanded polymer material into a mold, wherein the expanded polymer material of the pellets comprises an additive increasing the amorphous content of the polymer material; and connecting the pellets by heating the pellets to a temperature between a glass transition temperature and below the onset of melting of the expanded polymer material. The heating can be carried out as described above. An additive increasing the amorphous content of the polymer material modifies the polymer such that better connecting of the pellets in the mold is achieved. Such an additive can be a chain extender, without being restricted thereto. A further suitable additive is a peroxide, such as an organic peroxide, e.g. dicumyl peroxide. The use of a peroxide is described in the article “Structure Modification of Isotactic Polypropylene through Chemical Crosslinking: Toughening Mechanism” of S. Bouhelal et al., Journal of Applied Polymer Science DOI 10.1002/app (Vol. 103, 2968-2976 (2007)).
The pellets used for manufacturing the molded components may be produced by using the above described methods using either a chain extender or an additive increasing the amorphous content of the polymer material, or a combination thereof. It is also possible to provide for two or more melting stages before expansion. It is also possible to add the blowing agent and chain extender or additive in two or more melting stages before expanding, e.g. melting the polymer, adding the chain extender or additive, then cooling, melting the polymer, and adding the blowing agent. Further possible is melting the polymer, adding a chain extender, then cooling, and repeating the process but with adding the blowing agent.
The chain extender may be added in an amount of 0.1 to 20% by weight, in particular 0.1 to 15% by weight, preferably 0.1 to 10% by weight, such as 0.1 to 5% by weight or 1 to 5% by weight, based on 100% by weight of the base polymer material. The same amounts may be used for an additive increasing the amorphous content of the polymer material.
Particularly suitable base polymer material are selected from polyamides and are, for instance, homopolyamide, copolyamide, polyetherblockamide, and polyphthalamide. Very suitable is, as an example, polyamide 12.
The chain extender may be a polymeric material containing epoxy groups, such as a styrene-acrylate copolymer containing reactive epoxy groups.
Molded components can be manufactured in a molding from the pellets of the expanded polymer material using steam-chest molding. This technology as well as steam-chest molding machines are known in the art. Such steam-chest molding machines are commercially available, e.g. from the company Kurtz GmbH (Germany). In this process, first the pellets are fed into the mold. After closing the mold, the pellets are subjected to steam pressure. The conditions used for steam pressure and temperature are dependent on the material of the pellets used (polymer material, chain extender, additive). These conditions can be determined by the person skilled in the art using routine experiments. The temperature can be chosen such as to be, on the one hand, above the glass transition temperature of the polymer material to allow additional mobility of the amorphous regions in the polymer and, on the other hand, below the onset of melting of the polymer material so that the foamed pellets do not begin to melt and ultimately collapse. As an example, the molding can be conducted using a steaming profile with a ramping the pressure/temperature up and down for a predetermined time of duration. The skilled person can determine suitable pressure, temperature, and time/cycle conditions by balancing e.g. pressure and time. If the pressure is too high, the pellets can collapse and melt. If the time is too short, the pellets will not receive enough energy and may not fuse correctly. It is also possible to use the melting material of the polymer material to create fusion, for example, for expanded polypropylene having double melting peak with fusion occurring between melting peaks.
It is possible that the pellets of the expanded material have internally an at least partially ruptured foam structure.
If the article is produced using pellets of the expanded material that may have internally an at least partially ruptured foam structure, the molded component produced is suitable for e.g. sound insulation.
The molded components produced may be used as or be suitable as at least one of the following: a packaging material, a reusable packaging material, a pallet, an article for medical transportation, an article for chemical transportation, an article for breakable goods transportation, an article for interior insulation, an article for exterior insulation, an article for pipe insulation, a geofoam, a temporary housing, a road crash protection, an article for appliance insulation, an article for industrial appliance insulation, a sun visor, a dash board, a car seat, a center console, a car door, a child/baby seat, an article for battery cover/insulation, an article for engine insulation, a bumper, a crash structure, a protective helmet, an article of protective clothing, a boat fender, a medical stretcher, a surf/rescue board, a buoy, a boat hull, a snowmobile seat, a core for skis/snowboards/water skis/wakeboards, a jet ski seat, an artificial turf, a venue or playground flooring, a sports hall protective flooring/wall, a conditioning roller, a resistance weight for aerobics, a swimming aid, an article of furniture, a bean bag, a cow mat, a drone, an article of luggage, a plane seat, a plane/glider wing, an article for aeroplane cabin insulation, a plane food tray, an article for airline food trolley insulation, an under floor, an article for heating protection, an article of advanced protective equipment, a medical cast, a turbine/rotor blade core, a run-flat tyre, hand grips, beverage insulation, lamp covers, mattresses.
The molded components produced may be used as or be suitable as an article, in the production of cushioning elements for sports apparel, in particular for the production of soles for shoes, preferably midsoles.
An aspect of the invention concerns a shoe, in particular a shoe comprising a cushioning element. The cushioning element may be a sole, in particular a midsole. Suitable midsoles may be produced e.g. by fusing expanded polyetherblockamide pellets containing chain extender. Such midsoles are shown in
Another aspect of the invention concerns an article comprising a foam. The foam can be produced by fusing or connecting expanded polymer pellets using the methods described above. The article may be sport apparel, for example a shoe, such as a sports shoe. The shoe may comprise the foam in form of a cushioning element, e.g. as sole or midsole.
The molded components also may be used for sound insulation. Suitable molded components are in particular foams with open cell configuration. As an example, the expanded pellets, and thus the fused foam may have an at least partially ruptured structure. Pellets or fused foams suitable for producing sound insulation articles may be produced e.g. from polyamide, such as polyamide 12. The polyamide may contain a chain extender. Such expanded pellets are shown in
The invention is illustrated by means of the following examples that show embodiments but do not limit the invention.
As base polymer, a polyamide 12 material was used. The polyamide 12 used was Vestamid LX 9012 obtainable from Evonik Industries AG, Marl. As blowing agent, a combination of 4% by weight of (supercritical) carbon dioxide and 3% by weight of ethanol, based on 100% by weight of the base polymer, was used.
The base polymer and blowing agent were fed to the twin screw extruder 2 according to the setup shown in
The pellets were investigated by means of DMA (dynamic mechanical analysis) to evaluate the storage modulus at different temperatures, and further by scanning electron microscopy (SEM).
For DMA, a known test apparatus was used and a storage modulus analysis was carried out with a −40° C. to +40° C. temperature sweep under the following test conditions: 5° C. increments; 5 min soak time at each temperature; 25% initial compression strain; 5% sinusoidal oscillation around initial strain; and 1 Hz oscillation. The pellets tested had substantially spherical shape with approximately 5 mm diameter. The results obtained are shown in
As is evident from that figure, the polyamide pellets EPA12 show a variation of approx. 35%, more precisely a decrease by approx. 35% in storage modulus when changing the temperature from −40° C. to +40° C., compared to the expanded polypropylene particles EPP with approx. 288% decrease in storage modulus.
In
As base polymer, a PEBA material was used. The used PEBA material was Vestamid E62-S3 obtainable from Evonik Industries AG, Marl. According to supplier's information the number following the letter E indicates the Shore D hardness according to ISO 868, meaning that Vestamid E62-S3 comprises a Shore D hardness of 62. As blowing agent, a combination of 4% by weight of (supercritical) carbon dioxide and 2% by weight of ethanol, based on 100% by weight of the base polymer, was used. Further, a chain extender based on styrene-acrylate copolymer was used. The chain extender was Joncryl® ADR-4368C of BASF which was used in an amount of 2% by weight, based on 100% by weight of the base polymer.
The base polymer, blowing agent and chain extender were fed to the twin screw extruder 2 according to the setup shown in
Further, for evaluating mechanical properties, the pellets were bonded together via steam to produce a test plate. The test plate had a density of approx. 84 kg/m3 and was tested with regard to its compression behavior.
The compression testing was carried out using a known testing apparatus at 23° C. under the following test conditions: 20 mm thick sample; 50% compression; heel stamp (diameter of 50 mm); speed of 50 mm/min; and 5N pre-load. The results obtained are shown in
The diagram in
The diagram of
In
As base polymer, a PEBA material was used. The used PEBA material was Vestamid E62-S3 obtainable from Evonik Industries AG, Marl. Further, a chain extender based on styrene-acrylate copolymer, namely Joncryl® ADR-4368C (BASF) was used in amounts of 1% by weight, 2% by weight, and 2.5% by weight, based on 100% by weight of the base polymer. For comparison, the base polymer was also tested without chain extender. The polymer together with the same blowing agents as described in Example 2 and the indicated amount of chain extender were melted in an extruder, similar to Example 2. Subsequently, similar to Example 2, the melt was expanded through a round die and fed to an underwater pelletizing device to obtain expanded pellets.
The pellets (before molding) were tested on their heat flow-temperature behavior via DSC measurement using a heating rate of 10K/min for a temperature range of from 25° C. to 250° C. The test results obtained are shown
The pellets containing 2.5% by weight of chain extender were loaded into a mold and fused by providing steam into the mold. The mold was a tool for molding midsoles for shoes.
As base polymer, a PEBA material was used. The used PEBA material was Vestamid E55 obtainable from Evonik Industries AG, Marl. A chain extender based on styrene-acrylate copolymer, namely Joncryl® ADR-4368C (BASF), was used in amounts of 3% by weight, 4.5% by weight, and 5% by weight, based on 100% by weight of the base polymer. For comparison, the base polymer was also tested without chain extender. The polymer together with the same blowing agents as described in Example 2 and the indicated amount of chain extender were melted in an extruder, similar to Example 2. Subsequently, similar to Example 2, the melt was expanded through a round die and fed to an underwater pelletizing device to obtain expanded pellets.
The pellets (before molding) were tested on their heat flow-temperature behavior via DSC measurement using a heating rate of 10K/min for a temperature range of from 25° C. to 250° C. The test results obtained are shown
The pellets containing 5% by weight of chain extender were loaded into a mold and fused by providing steam into the mold. The mold was a tool for molding midsoles for shoes.
As base polymer, a polybutylene terephthalate (PBT) material was used. The used PBT material was Ultradur B4520 obtainable from BASF. A chain extender based on styrene-acrylate copolymer, namely Joncryl® ADR-4368C (BASF), was used in amounts of 1% by weight and 1.5% by weight, based on 100% by weight of the base polymer. For comparison, the base polymer was also tested without chain extender. A compact material was formed, wherein the process included melting of the polymer, adding the chain extender and extrusion of the resulting material. Subsequently, the compact material was cooled and the material's heat flow-temperature behavior was measured using DSC using a heating rate of 10K/min for a temperature range of from 25° C. to 250° C. The test results obtained are shown
As base polymer, a TPEE material was used. The used TPEE material was Arnitel EM400 obtainable from DSM. A chain extender based on styrene-acrylate copolymer, namely Joncryl® ADR-4368C (BASF), was used in an amount of 2% by weight, based on 100% by weight of the base polymer. For comparison, the base polymer was also tested without chain extender. A compact material was formed, wherein the process included melting of the polymer, adding the chain extender and extrusion of the resulting material. Subsequently, the compact material was cooled and the material's heat flow-temperature behavior was measured using DSC using a heating rate of 10K/min for a temperature range of from 25° C. to 250° C. The test results obtained are shown in
As base polymer, a polyamide 12 (PA12) material was used. The polyamide 12 used was Vestamid LX 9012 (obtainable from Evonik Industries AG, Marl). As blowing agent, a combination of 4% by weight of (supercritical) carbon dioxide and 3% by weight of ethanol, based on 100% by weight of the base polymer, was used. A chain extender based on styrene-acrylate copolymer, namely Joncryl® ADR-4368C (BASF), was used in the amount of 1.5% by weight, based on 100% by weight of the base polymer, and without chain extender.
The polymer together with the same blowing agent and the indicated amount of chain extender were melted in an extruder, similar to Example 1. Subsequently, similar to Example 1 the melt was expanded through a round die and fed to an underwater pelletizing device to obtain expanded pellets.
In
As base polymer, a PLA material was used. The used PLA material was Ingeo 3251D obtained from NatureWorks. A chain extender based on styrene-acrylate copolymer, namely Joncryl® ADR-4368C (BASF), was used in amounts of 1% by weight and 2% by weight, based on 100% by weight of the base polymer. For comparison, the base polymer was also tested without chain extender. A compact material was formed using a twin-screw micro-compounder, wherein the process included melting of the polymer, adding the chain extender and extrusion of the resulting material. Subsequently, the compact material was cooled and the material's heat flow-temperature behavior was measured using DSC using a heating rate of 10K/min for a temperature range of from 25° C. to 250° C. The test results obtained are shown in
As base polymer, a PET material was used. The used PET material was PET-Type 40 (injection-molding grade) obtained from Hoechst Celanese. A chain extender based on styrene-acrylate copolymer, namely Joncryl® ADR-4368C (BASF), was used in amounts of 1% by weight, 2% by weight and 3% by weight, based on 100% by weight of the base polymer. For comparison, the base polymer was also tested without chain extender. A compact material was formed using a twin-screw micro-compounder, wherein the process included melting of the polymer, adding the chain extender and extrusion of the resulting material. Subsequently, the compact material was cooled and the material's heat flow-temperature behavior was measured using DSC using a heating rate of 10K/min for a temperature range of from 25° C. to 250° C. The test results obtained are shown in
As base polymer, a POM material was used. The used POM material was Delrin® 100P NC010 obtained from DuPont. A chain extender based on styrene-acrylate copolymer, namely Joncryl® ADR-4368C (BASF), was used in amounts of 1% by weight and 2% by weight, based on 100% by weight of the base polymer. For comparison, the base polymer was also tested without chain extender. A compact material was formed using a twin-screw micro-compounder, wherein the process included melting of the polymer, adding the chain extender and extrusion of the resulting material. Subsequently, the compact material was cooled and the material's heat flow-temperature behavior was measured using DSC using a heating rate of 10K/min for a temperature range of from 25° C. to 250° C. The test results obtained are shown in
In the following, further embodiments are described to facilitate the understanding of the invention:
| Number | Date | Country | Kind |
|---|---|---|---|
| 10 2014 216 992.5 | Aug 2014 | DE | national |
| PCT/EP2015/057909 | Apr 2015 | WO | international |
This patent application is a continuation patent application of U.S. patent application Ser. No. 15/506,951, filed on Feb. 27, 2017 (“the '951 application”), which is the U.S. national stage application under 35 U.S.C. § 371 of PCT/EP2015/069368, filed on Aug. 24, 2015, which application is related to and claims priority benefit from German Patent Application No. DE 10 2014 216 992.5, filed on Aug. 26, 2014 (“the '992 application”) and International Patent Application No. PCT/EP2015/057909, filed on Apr. 10, 2015 (“the '909 application”). The '951, '992 and '909 applications are hereby incorporated herein in their entireties by this reference.
| Number | Name | Date | Kind |
|---|---|---|---|
| 4026834 | Cordes et al. | May 1977 | A |
| 4028287 | Sato et al. | Jun 1977 | A |
| 4988740 | Walter et al. | Jan 1991 | A |
| 5502106 | LaFleur et al. | Mar 1996 | A |
| 6039085 | Hsich | Mar 2000 | A |
| 6110983 | Tokoro et al. | Aug 2000 | A |
| 6339109 | Day et al. | Jan 2002 | B1 |
| 6984694 | Blasius, Jr. et al. | Jan 2006 | B2 |
| 7897077 | Seibring et al. | Mar 2011 | B2 |
| 7994231 | Jacobs et al. | Aug 2011 | B2 |
| 8268901 | Britton et al. | Sep 2012 | B2 |
| 8372512 | Hirai et al. | Feb 2013 | B2 |
| 8535585 | Casalini et al. | Sep 2013 | B2 |
| D709680 | Herath | Jul 2014 | S |
| D740003 | Herath | Oct 2015 | S |
| D740004 | Hoellmueller et al. | Oct 2015 | S |
| 9249270 | Sampath et al. | Feb 2016 | B2 |
| D758056 | Galway et al. | Jun 2016 | S |
| D776410 | Galway et al. | Jan 2017 | S |
| D783264 | Hoellmueller et al. | Apr 2017 | S |
| 9610746 | Wardlaw et al. | Apr 2017 | B2 |
| 9781970 | Wardlaw et al. | Oct 2017 | B2 |
| 9781974 | Reinhardt | Oct 2017 | B2 |
| 9788598 | Reinhardt | Oct 2017 | B2 |
| 9788606 | Reinhardt | Oct 2017 | B2 |
| 9795186 | Reinhardt et al. | Oct 2017 | B2 |
| 9820528 | Reinhardt et al. | Nov 2017 | B2 |
| 9849645 | Wardlaw et al. | Dec 2017 | B2 |
| 9930928 | Whiteman et al. | Apr 2018 | B2 |
| 9968157 | Wardlaw et al. | May 2018 | B2 |
| 10005218 | Rudolph et al. | Jun 2018 | B2 |
| 10039342 | Reinhardt et al. | Aug 2018 | B2 |
| D828686 | Hoellmueller et al. | Sep 2018 | S |
| D828991 | Herath | Sep 2018 | S |
| 10259183 | Wardlaw et al. | Apr 2019 | B2 |
| 10279516 | Daeschlein et al. | May 2019 | B2 |
| D851889 | Dobson et al. | Jun 2019 | S |
| D852475 | Hoellmueller et al. | Jul 2019 | S |
| D853691 | Coonrod et al. | Jul 2019 | S |
| D853699 | Coonrod et al. | Jul 2019 | S |
| 10759096 | Smith et al. | Sep 2020 | B2 |
| 11117294 | Holmes et al. | Sep 2021 | B2 |
| 20050156344 | Dietzen et al. | Jul 2005 | A1 |
| 20070112082 | Hahn et al. | May 2007 | A1 |
| 20090051061 | Seibring et al. | Feb 2009 | A1 |
| 20090108480 | Schmaus et al. | Apr 2009 | A1 |
| 20100190877 | Schips et al. | Jul 2010 | A1 |
| 20100239834 | Dietrich et al. | Sep 2010 | A1 |
| 20110008608 | Bellin et al. | Jan 2011 | A1 |
| 20110294910 | Kriha et al. | Dec 2011 | A1 |
| 20120007267 | Pawlosk et al. | Jan 2012 | A1 |
| 20120010307 | Pawloski et al. | Jan 2012 | A1 |
| 20120041086 | Sampath et al. | Feb 2012 | A1 |
| 20120280419 | Martin et al. | Nov 2012 | A1 |
| 20130059938 | Paetz-lauter et al. | Mar 2013 | A1 |
| 20140151918 | Hartmann | Jun 2014 | A1 |
| 20140227506 | Kuwabara et al. | Aug 2014 | A1 |
| 20150174808 | Rudolph | Jun 2015 | A1 |
| 20150353701 | Urbanczyk et al. | Dec 2015 | A1 |
| 20160037859 | Smith et al. | Feb 2016 | A1 |
| 20160227876 | Le et al. | Aug 2016 | A1 |
| 20160278481 | Le et al. | Sep 2016 | A1 |
| 20160295955 | Wardlaw et al. | Oct 2016 | A1 |
| 20160302508 | Kormann et al. | Oct 2016 | A1 |
| 20160346627 | Le et al. | Dec 2016 | A1 |
| 20170253710 | Smith et al. | Sep 2017 | A1 |
| 20170340067 | Dyckmans et al. | Nov 2017 | A1 |
| 20170341325 | Le et al. | Nov 2017 | A1 |
| 20170341326 | Holmes et al. | Nov 2017 | A1 |
| 20170341327 | Le et al. | Nov 2017 | A1 |
| 20180000197 | Wardlaw et al. | Jan 2018 | A1 |
| 20180035755 | Reinhardt et al. | Feb 2018 | A1 |
| 20180154598 | Kurtz et al. | Jun 2018 | A1 |
| 20180206591 | Whiteman et al. | Jul 2018 | A1 |
| 20180235310 | Wardlaw et al. | Aug 2018 | A1 |
| 20180290349 | Kirupanantham et al. | Oct 2018 | A1 |
| 20180303198 | Reinhardt et al. | Oct 2018 | A1 |
| 20190021435 | Kormann et al. | Jan 2019 | A1 |
| 20190291371 | Wardlaw et al. | Sep 2019 | A1 |
| Number | Date | Country |
|---|---|---|
| 1314433 | Sep 2001 | CN |
| 1440435 | Sep 2003 | CN |
| 1890307 | Jan 2007 | CN |
| 1318466 | May 2007 | CN |
| 101044196 | Sep 2007 | CN |
| 101611095 | Dec 2009 | CN |
| 101959942 | Jan 2011 | CN |
| 103517648 | Jan 2014 | CN |
| 103890066 | Jun 2014 | CN |
| 102004015093 | Oct 2005 | DE |
| 256489 | Feb 1988 | EP |
| 0256489 | Jun 1990 | EP |
| 60042432 | Mar 1985 | JP |
| H01-132642 | May 1989 | JP |
| 04356541 | Dec 1992 | JP |
| 07179645 | Jul 1995 | JP |
| 2000086800 | Mar 2000 | JP |
| 2001253965 | Sep 2001 | JP |
| 2001329103 | Nov 2001 | JP |
| 2007514027 | May 2007 | JP |
| 2007516307 | Jun 2007 | JP |
| 2010111740 | May 2010 | JP |
| 2010525099 | Jul 2010 | JP |
| 2010184956 | Aug 2010 | JP |
| 2011105879 | Jun 2011 | JP |
| 2011213968 | Oct 2011 | JP |
| 2011225819 | Nov 2011 | JP |
| 2011256290 | Dec 2011 | JP |
| 2013517340 | May 2013 | JP |
| 2014151201 | Aug 2014 | JP |
| 2014158708 | Sep 2014 | JP |
| 2017525819 | Sep 2017 | JP |
| 2006045513 | May 2006 | WO |
| 2007082838 | Jul 2007 | WO |
| 2010010010 | Jan 2010 | WO |
| 2011134996 | Nov 2011 | WO |
| 2013148841 | Oct 2013 | WO |
| 2013153190 | Oct 2013 | WO |
| 2014198779 | Dec 2014 | WO |
| 2016030026 | Mar 2016 | WO |
| Entry |
|---|
| Office Action, Korean Patent Application No. 10-2017-7008202, dated Mar. 23, 2022, 20 pages. |
| Office Action, European Patent Application No. 15756143.2, dated May 17, 2022, 4 pages. |
| U.S. Appl. No. 17/004,430, Advisory Action, dated Apr. 6, 2022, 8 pages. |
| Office Action, Korean Patent Application No. 10-2017-7008195, dated Apr. 26, 2021, 19 pages. |
| Office Action, European Patent Application No. 15756143.2, dated Jul. 30, 2021, 3 pages. |
| U.S. Appl. No. 15/507,054, Notice of Allowance, dated Apr. 2, 2020, 8 pages. |
| U.S. Appl. No. 17/004,430, Non-Final Office Action, dated Sep. 22, 2021, 7 pages. |
| Al-Itry et al., “Improvement of Thermal Stability, Rheological and Mechanical Properties of PLA, PBAT and Their Blends by Reactive Extrusion with Functionalized Epoxy”, Polymer Degradation and Stability, vol. 97, 2012, pp. 1898-1947. |
| Extended European Search Report, European Patent Application No. 22191468.2, dated Sep. 13, 2022, 9 pages. |
| Office Action, Chinese Patent Application No. 202110418171.6, dated Aug. 22, 2022, 22 pages. |
| Office Action, Korean Patent Application No. 10-2017-7008202, dated Aug. 3, 2022, 6 pages. |
| U.S. Appl. No. 17/004,430, Non-Final Office Action, dated Sep. 27, 2022, 9 pages. |
| U.S. Appl. No. 17/004,430 , Final Office Action, dated Feb. 11, 2022, 11 pages. |
| Arkema, “Pebax Product Range Overview Sheet—General Characteristics,” retrieved from the Internet at http://www.pebax.com/export/sites/pebax/.content/medias/downloads/literature/pebax_product_range_and_properties.pdf, Oct. 2, 2007, pp. 1-2. |
| Arkema Brochure, “Pebax—Polyether Block Amides,” retrieved from the Internet at http://www.pebax.com/export/sites/pebax/.content/medias/downloads/literature/pebax-product-range-brochure.pdf, Aug. 26, 2009, pp. 1-14. |
| International Patent Application No. PCT/EP2015/057909, International Search Report and Written Opinion dated Nov. 9, 2015, 18 pages. |
| International Patent Application No. PCT/EP2015/069368, International Search Report and Written Opinion dated Dec. 23, 2015, 18 pages. |
| Japanese Application No. 2017-511251, Office Action dated Dec. 19, 2017, 9 pages (5 pages for the original document and 4 pages for the English translation). |
| Japanese Application No. 2017-511248, Office Action dated Feb. 20, 2018, 10 pages (6 pages for the original document and 4 pages for the English translation). |
| Japanese Patent Application No. 2017-511248, Office Action dated Sep. 4, 2018, 7 pages (3 pages of translation and 4 pages or original document). |
| U.S. Appl. No. 15/507,054, Non-Final Office Action dated Dec. 19, 2018, 12 pages. |
| Chinese Patent Application No. CN 201580045630.3, dated Nov. 2, 2018, 21 pages (11 pages of English translation and 10 pages of Original document). |
| European Patent Application No. EP 15713960.1, dated Oct. 15, 2018, 5 pages. |
| Japanese Patent Application No. 2018-088909, Office Action dated Mar. 26, 2019, 6 pages (machine English translation provided). |
| Xu et al., “Chain Extension of Polyamide 6 using Multifunctional Chain Extenders and Reactive Extrusion for Melt Foaming”, European Polymer Journal, available at www.http://dx.doi.org/10.1016/j.eurpolymj.2017.09.012, 2017, 38 pages. |
| Yeh et al., “Carbon Dioxide-Blown Expanded Polyamide Bead Foams With Bimodal Cell Structure”, Ind. Eng. Chem. Res. 2019, 58, 2019, pp. 2958-2969. |
| “Joncryl ADR-4368”, BASF Corporation, Jan. 25, 2018, 8 pages. |
| Office Action, Japanese Patent Application No. 2018-237707, dated Feb. 12, 2020, 14 pages. |
| Office Action, German Patent Application No. 1020142169925, dated Feb. 5, 2020, 10 pages. |
| Office Action, European Patent Application No. 15756143.2, dated Jan. 22, 2020, 5 pages. |
| U.S. Appl. No. 15/507,054 , Non-Final Office Action, dated Dec. 2, 2019, 15 pages. |
| Sun et al., “Novel Biodegradable Cast Film from Caron Dioxide Based Copolymer and Poly (Lactic Acid)”, In: J Polym Environ, 2016, pp. 23-36. |
| European Patent Application No. 15713960.1, Office Action, dated Jul. 7, 2020, 5 pages. |
| U.S. Appl. No. 15/507,054, Corrected Notice of Allowability, dated Jul. 29, 2020, 3 pages. |
| Office Action, European Patent Application No. 15756143.2, dated Sep. 4, 2020, 5 pages. |
| Office Action, European Patent Application No. 15713960.1, dated Feb. 26, 2021, 5 pages. |
| Office Action, Japanese Patent Application No. 2019-228251, dated Mar. 2, 2021, 9 pages. |
| U.S. Appl. No. 29/592,935, filed Feb. 3, 2017, Unpublished. |
| U.S. Appl. No. 29/592,946, filed Feb. 3, 2017, Unpublished. |
| U.S. Appl. No. 29/595,857, filed Mar. 2, 2017, Unpublished. |
| U.S. Appl. No. 62/137,139, filed Mar. 23, 2015, Unpublished. |
| U.S. Appl. No. 29/663,342, filed Sep. 13, 2018, Unpublished. |
| U.S. Appl. No. 29/643,233, filed Apr. 5, 2018 , Unpublished. |
| U.S. Appl. No. 29/641,371, filed Mar. 21, 2018, Unpublished. |
| U.S. Appl. No. 29/663,029, filed Sep. 11, 2018, Unpublished. |
| U.S. Appl. No. 29/641,256, filed Mar. 20, 2018, Unpublished. |
| U.S. Appl. No. 29/641,223, filed Mar. 20, 2018, Unpublished. |
| U.S. Appl. No. 29/614,532, filed Aug. 21, 2017, Unpublished. |
| U.S. Appl. No. 29/664,097, filed Sep. 21, 2018, Unpublished. |
| U.S. Appl. No. 29/679,962, filed Feb. 12, 2019, Unpublished. |
| U.S. Appl. No. 29/691,166, filed May 14, 2019, Unpublished. |
| U.S. Appl. No. 29/691,854, filed May 20, 2019, Unpublished. |
| U.S. Appl. No. 16/465,485, filed May 30, 2019, Unpublished. |
| U.S. Appl. No. 29/693,455, filed Jun. 3, 2019, Unpublished. |
| U.S. Appl. No. 29/694,634, filed Jun. 12, 2019, Unpublished. |
| Office Action, European Patent Application No. 15756143.2, dated Mar. 13, 2019, 6 pages. |
| Office Action, Japanese Patent Application No. 2017-511248, dated Mar. 5, 2019, 4 pages. |
| Decision to Grant, Japanese Patent Application No. 2017-511248, dated Jul. 16, 2019, 5 pages. |
| Office Action, Chinese Patent Application No. 201580045630.3, dated Aug. 27, 2019, 31 pages. |
| Office Action, European Patent Application No. 15713960.1, dated Aug. 22, 2019, 6 pages. |
| Office Action, Chinese Patent Application No. 201580045604.0, dated Sep. 25, 2019, 7 pages. |
| U.S. Appl. No. 15/507,054 , Advisory Action, dated Sep. 5, 2019, 6 pages. |
| U.S. Appl. No. 15/507,054 , Final Office Action, dated May 29, 2019, 13 pages. |
| U.S. Appl. No. 15/507,054 , Restriction Requirement, dated Sep. 10, 2018, 6 pages. |
| Office Action, Chinese Patent Application No. 201580045630.3, dated Nov. 2, 2018, 18 pages. |
| Xintuo et al., “Effect of Crosslinkers and Chain Extenders on Crystalline Properties of Copolyamides”, Journal of Beijing Institute of Clothing, Dec. 31, 2005, 7 pages. |
| U.S. Appl. No. 15/506,951, Advisory Action, dated Mar. 25, 2021. |
| U.S. Appl. No. 15/506,951, Final Office Action, dated Nov. 13, 2020, 9 pages. |
| U.S. Appl. No. 15/506,951, Final Office Action, dated Dec. 30, 2019, 10 pages. |
| U.S. Appl. No. 15/506,951 , Non-Final Office Action, dated Apr. 2, 2020, 8 pages. |
| U.S. Appl. No. 15/506,951 , Non-Final Office Action, dated Jun. 14, 2019, 10 pages. |
| U.S. Appl. No. 15/506,951 , Notice of Allowance, dated May 19, 2021, 8 pages. |
| Office Action, Chinese Patent Application No. 202011292644.4, dated Jul. 1, 2022, 19 pages. |
| Office Action, Chinese Patent Application No. 202110419668.X, dated Jul. 20, 2022, 21 pages. |
| Office Action, Chinese Patent Application No. 202011296168.3, dated Jul. 11, 2022, 25 pages. |
| Office Action, Chinese Patent Application No. 202110418457.4, dated Jul. 27, 2022, 24 pages. |
| Office Action, Japanese Patent Application No. 2021-142602, dated Aug. 9, 2022, 4 pages. |
| “Pebax Product Range and Properties”, Arkema, Jun. 30, 2007, 2 pages. |
| Chen et al., “The Effect Influence of Cross-Linking Agent and Chain Extender on the Crystalline Properties of Copolyamide”, Journal of Beijing Institute of Clothing Technology, Dec. 31, 2005, 17 pages. |
| European Extended Search Report, European Patent Application No. 23190094.5, dated Aug. 28, 2023, 12 pages. |
| Office Action, Chinese Patent Application No. 202110419668.X, dated Feb. 17, 2023, 17 pages. |
| Office Action, Chinese Patent Application No. 202110418171.6, dated Feb. 22, 2023, 17 pages. |
| Office Action, Chinese Patent Application No. 202110418457.4, dated Jan. 12, 2023, 8 pages. |
| Office Action, Chinese Patent Application No. 202011296168.3, dated Jan. 31, 2023, 22 pages. |
| U.S. Appl. No. 17/004,430, Final Office Action, dated Apr. 13, 2023, 11 pages. |
| Number | Date | Country | |
|---|---|---|---|
| 20210370561 A1 | Dec 2021 | US |
| Number | Date | Country | |
|---|---|---|---|
| Parent | 15506951 | US | |
| Child | 17399842 | US |