Patent Application
20070105396
An aspect of the present invention relates to a method for fabricating electronic devices, including but not limited to thin film transistors, by applying fluid to a substrate. The present invention also relates to a thin film transistor and a brush painting apparatus.
Electronics based on organic and inorganic solution-processable materials has attracted enormous research interest over the past few decades. These materials have proven their potential for use in a wide range of applications, such as light-emitting diodes (LEDs), photovoltaic cells and thin film transistors (TFTs). Recent developments in patterning technologies have further proven their potential for the manufacture of large area integrated devices on both rigid and flexible substrates. There exist several techniques to fabricate structures based on a solution process, such as screen printing, ink-jet printing and dip-coating on patterned substrates. The printing resolution of screen printing is very limited, and the frequent damage of masks used in the process leads to a high cost for this technique. Ink-jet printing is a very promising technique, but recently achieved free-format printing resolutions (˜50 μm) are still not sufficient to meet the requirements of the electronics industry. Dip-coating on a pre-patterned substrate is difficult to use in practical applications, because the flow of liquid over the substrate is hard to control. Any insufficiency or pile up of solvent can lead to failure of the patterning defined by dip-coating. Thus, to enable mass production of high resolution structures by a solution process, it is desirable to develop other patterning techniques.
Although there are many lithography techniques that can be used to fabricate high resolution structures, their multi-step nature and the associated alignment processes dramatically increase the cost of the fabrication process. An object of the invention is to provide a fast and cheap high resolution patterning method for the fabrication of electronic devices.
According to a first aspect of the present invention, there is provided a method for fabricating an electronic device, the method comprising: creating a surface energy pattern on a substrate; and brush painting a first fluid onto the substrate to form a pattern of fluid corresponding to the surface energy pattern on the substrate.
The technique of the invention offers a cheap, fast, high resolution patterning method which allows different types of ink to be used to paint electronic devices on the same substrate. The brushing technique of the invention enables a pattern to be formed faster than is possible using ink-jet printing. Patterns involving multi-layered materials and chemical patterns in a continuous film can also be fabricated by this technique. In combination with ink-jet printing or other deposition techniques, the invention enables the fabrication of high resolution patterns of electronically functional materials for the production of electronic devices.
Preferably, the method further comprises depositing another structured layer on the substrate using ink-jet printing.
Preferably, the surface energy pattern comprises a material philic to the first fluid and a material phobic to the first fluid. Suitably, the philic material is hydrophilic, oleophilic or lyophilic and the phobic material is hydrophobic, oleophobic or lyophobic.
Preferably, the step of creating a surface energy pattern comprises depositing a first self-assembled monolayer (SAM) onto the substrate. Suitably, the first SAM is deposited using soft contact printing. Preferably, the first SAM comprises H1,H1,H2,H2-perfluorodecyltrichlorosilane.
In one embodiment, the first fluid comprises a conductive polymer. Suitably, the first fluid comprises poly(3,4-ethylene-dioxythiophene) (PEDOT) and poly(styrene sulphonic acid) (PSS).
In another embodiment, the first fluid comprises a metal. Suitably, the first fluid comprises one of Au, Ag, Cu, Al, Ni and Pt. Preferably, the first fluid comprises one of Ag and Au. Suitably, the method further comprises: annealing the substrate to form a pattern of the one of Ag and Au on the substrate; and depositing a second SAM on the pattern of the one of Ag and Au. Preferably, the second SAM comprises 1H,1H,2H,2H-perfluorodecanethiol.
In one embodiment, the method further comprises depositing a semiconductor layer over the substrate. Preferably, this method further comprises depositing a dielectric layer on the semiconductor layer. Suitably, this method further comprises depositing a pattern of conductive material on the dielectric layer.
In one embodiment, the substrate comprises a conductive layer and an insulating layer, and the step of forming a surface energy pattern comprises forming a surface energy pattern on the insulating layer.
Conveniently, the method further comprises: brush painting a second fluid onto the substrate to form a multi-layered pattern corresponding to the surface energy pattern on the substrate. Preferably, this method further comprises a step of curing the pattern of fluid either thermally or optically before the step of brush painting a second fluid onto the substrate.
Suitably, the first and second fluids are identical. Alternatively, the first and second fluids comprise different materials.
Preferably, the method further comprises: performing a surface treatment to change the polarity of the wetting contrast of the surface of the substrate after the step of brush painting; and brush painting a further fluid onto the substrate.
Suitably, the first fluid is brush painted onto the substrate in a first area of the substrate and another fluid is brush painted onto the substrate in a second area of the substrate, and the two fluids comprise different materials.
Preferably, features of the surface energy pattern are less than 1 mm in size. Suitably, material deposited by brush painting has a thickness between 10 nm and 10 μm. Preferably, brush painting is performed by moving the substrate at a speed from 0.001 m/s to 1 m/s relative to a brush head.
In one embodiment, there is provided a roll-to-roll or sheet-to-sheet process for fabricating electronic devices comprising a method as described above. In another embodiment, there is provided an electronic device fabricated by a method as described above.
According to a second aspect of the present invention, there is provided a thin film transistor comprising: a conductive layer; a layer of insulator formed on the conductive layer; a pattern of conductive material and a first self-assembled monolayer (SAM) formed on the layer of insulator; a second SAM formed on the conductive material; and a semiconductor layer formed on the first SAM and the second SAM.
The thin film transistor according to the present invention can be manufactured quickly and cheaply on a large scale using brush painting, and provides high performance.
Preferably, the semiconductor layer comprises a polymer material and the first SAM directs polymer chains in the semiconductor layer to be locally aligned. By directing the polymer chains to be locally aligned, the first SAM improves charge transfer in the polymer semiconductor layer.
Suitably, the semiconductor layer comprises P3HT and the first SAM comprises H1,H1,H2,H2-perfluorodecyltrichlorosilane.
Preferably, the second SAM increases the work function of the conductive material.
By acting to increase the work function of the conductive material, the second SAM improves charge transfer from the conductive material to the semiconductor layer, thus improving the performance of the TFT.
Suitably, the conductive material comprises silver and the second SAM comprises 1H,1H,2H,2H-perfluorodecanethiol.
According to a third aspect of the present invention, there is provided a brush painting apparatus comprising: an ink-absorbent brush head; an ink container connected to the brush head by an ink flow path; and a conveyor belt; wherein a surface of the conveyor belt faces the brush head.
Preferably, the surface of the conveyor belt is in contact with the brush head.
Embodiments of the present invention will now be described by way of further example only and with reference to the accompanying drawings, in which:
In the structure fabrication method of an embodiment of the invention a substrate is first pre-patterned by soft-contact printing. Following the pre-patterning, a solution of functional materials is painted onto the substrate using brushing to define the first layer of a device with a high resolution (such as a TFT channel between source and drain electrodes). Subsequent structured layers, in which a relatively low fabrication resolution is tolerable (such as a gate electrode for a TFT), are defined by ink-jet printing.
The soft-contact printed pattern formed on the substrate has a large wetting contrast defining ink-receptive areas and ink repellent areas. When a liquid film is deposited by brushing, a de-wetting process on the ink-repellent areas causes a sharp division between ink-receptive areas on which ink is deposited and ink-repellent areas on which substantially no ink is deposited. As a result, a well-defined pattern is produced. The pattern can be used directly as a pattern of device components, or used as a template to transfer a pattern onto other materials.
In the following, a preferred embodiment of the invention is described. The preferred embodiment uses inks based on silver colloids and inks based on polymer colloids containing poly(3,4-ethyfene-dioxythiophene) (PEDOT) doped with poly(styrene sulphonic acid) (PSS).
A structured polydimethylsiloxane (PDMS) stamp 20 is wetted for one minute using a solution of 0.005 mol H1,H1,H2,H2-perfluorodecyltrichlorosilane in hexane. After drying by nitrogen flow the stamp is brought into firm contact with the substrate for 30 s to form a self-assembled molecular monolayer (SAM) pattern 30 of H1,H1,H2,H2-perfluorodecyltrichlorosilane. However, any technique suitable for creating a surface energy pattern can be used to pre-pattern the substrate, including soft-contact printing, Photo-SAM lithography, micro-embossing, nanoimprinting, photolithography, optical interference and off-set printing.
Suitable SAM materials include molecules having a silane or thiol head group. The tail group of the molecules can be fluorine, alkyl, amino, hydroxyl or another group which is hydrophobic, lyophobic, hydrophilic or lyophilic depending on the substrate and ink solution. If it is intended for ink to be deposited on the regions of the substrate uncoated by the SAM, then the tail group of the SAM molecules must have a lower affinity for the ink than the substrate material. Conversely, if it is intended for ink to be deposited on the SAM, then the tail group of the SAM molecules must have a higher affinity for the ink than the substrate material. The surface energy pattern may comprise a plurality of SAM layers having different properties to allow a plurality of materials to be deposited onto the substrate by brush painting.
A brush 40, which is made from a natural fibre material such as paper or cotton, is dipped in PEDOT-PSS polymer or silver ink and is used to paint the ink onto the SAM pre-patterned substrate to define an ink pattern 50. The material used for the brush head must be capable of absorbing the ink and must also be soft enough not to damage the SAM layer. Micro-porous paper has been found to be a particularly suitable material for the brush head. It has been discovered that although a dry paper brush abrades and damages the SAM layer, a paper brush wetted with ink can be used without damaging the SAM layer.
In this context, the term brush is not limited to a head having bristles, but includes any flexible and absorbent member that can be used to deposit a fluid onto a surface. Similarly, the term brush painting includes brushing or wiping a surface using any such flexible and absorbent member in which fluid is absorbed.
In one embodiment, the brushing apparatus comprises an ink container and a brush head. The container is connected to the brush head by an ink flow path so that ink from the container is absorbed into the material of the brush head. The ink container may be positioned above the brush head so that ink flows from the container to the brush head under gravity. In other embodiments ink may be supplied to the brush head under pressure, by capillary action or by a siphon arrangement, in which case it is not necessary for the ink container to be above the brush head. The brush head is held stationary and a roll-to-roll conveyor belt is disposed beneath the brush head, the surface of the conveyor belt being pressed against or very close to the brush head. To perform brush painting, pre-patterned substrates are moved past the brush head on the conveyor belt so that the brush head moves over the substrate in contact with the upper surface of the substrate. However, in other embodiments a brush head can be moved over a stationary substrate or both head and substrate can move.
Suitable ink materials include soluble organic materials, soluble inorganic materials and colloidal suspensions based on water or other organic and inorganic solutions. The invention is generally applicable to a large range of inks for creating patterns of electrically functional material. Electrically functional materials include organic, inorganic or hybrid materials serving as conductors, semiconductors, or insulators.
During the brush painting process, the ink is held on the brush by capillary force, which depends on the wetting ability and the microstructure of the brush material. In principle, if the force of affinity between the substrate and the ink is larger than the capillary force holding the ink on the brush then the ink is transferred onto the substrate. Conversely, if the force of affinity between the substrate and ink is less than the capillary force then the ink remains on the brush. Accordingly, the force of affinity between the ink and either the coated or the uncoated areas of the substrate must be larger than the capillary force holding the ink on the brush in order for ink to be deposited. It is possible to create a pattern having a high wetting contrast by soft-contact printing. When the inked brush is drawn over such a pattern on the substrate, the areas with high wet-ability will accept the ink while the areas with low wet-ability will repel the ink.
The pressure of the brush on the substrate in the brush painting process of this embodiment is about 100 N/m2, and the speed of the brush across the substrate is about 10 cm/s. However, brush pressures between 10 N/M2 and 1000 N/M2 and brushing speeds between 0.001 m/s and 1 m/s can be used.
By combining the above patterning method with ink-jet printing it is possible to fabricate a polymer TFT such as that shown in
The soft-contact printed SAM layer can have a dual function when a polymer layer is deposited over the SAM layer. The SAM layer acts as a de-wetting layer to separate the painted materials, as described above, and also directs the chains of the polymer layer to align, which improves charge transfer in the polymer layer.
After another step of baking at 60° C. for 30 min, PEDOT-PSS is printed on the dielectric layer 70 to form the gate electrode 80, completing the TFT structure fabrication. Alternative techniques for depositing materials used as substrate coating layers and device components over the layer or layers deposited by brushing include doctor blading, printing (e.g. screen printing, offset printing, flexo printing, pad printing or inkjet printing), evaporation, sputtering, chemical vapour deposition, dip- and spray-coating, spin-coating and electroless plating. However, the combination of ink-jet printing technology with the brushing technique described above is particularly advantageous because the combined method allows electronic devices and integrated circuits to be produced quickly and cheaply over large areas. By using a brushing technique for portions of a device which benefit from a high resolution fabrication technique and using ink-jet printing for other portions of the device which are less sensitive to the resolution of the fabrication method, high performance devices can be produced on a large scale.
For silver source-drain electrodes a surface treatment is preferred to tune the work function of the electrodes. In the material combination above, the polymer semiconductors used are p-type and hence the source-drain electrodes must have a high work function to achieve good carrier injection from the electrodes 50 into the semiconductor layer 60. The treatment process used is:
An alternative method for treating the silver electrodes is to expose the electrodes to a CF4 plasma.
The brush painting patterning technique can also be used to pattern a multilayered structure, as shown in
The brush painting technique can also be used to fabricate patterns having a chemical contrast in a continuous film, as illustrated in
For example, if a glass substrate 200 is used and the first material 220 is silver or gold, a CF4 plasma treatment can be used to make the surface of the substrate 200 hydrophilic and the surface of the first material 220 hydrophobic. Finally, a patterned layer of the second material 240 is deposited by brush painting. The exposed areas of the substrate 200 accept the second material 240.
By scaling the brush used in the above brush painting technique to a small size, such as a few microns in width, it is possible to deposit different materials at different desired locations on the same substrate. A patterned substrate fabricated by such a micro-brushing technique is illustrated in
Another embodiment of the invention is a method for fabricating a bottom gate TFT, as shown in
The sample is submerged into a 0.005 mol solution of 1H,1H,2H,2H-perfluorodecanethiol in ethanol for 15 hours to form a 1H,1H,2H,2H-perfluorodecanethiol second SAM layer 340 on the silver 330, and is rinsed in ethanol, toluene and IPA. Rinsing is performed to remove crystals formed on the silver 330. After baking the sample at 60° C. for 10 min, a 40 nm thick layer of P3HT semiconductor polymer 350 is spin-coated on the top of the sample to complete the TFT.
The first SAM layer 320 has a dual function in the formation of the TFT: it acts as a de-wetting layer to separate the brush painted silver suspension 330 into the desired pattern, and it also directs the P3HT polymer chains to be locally aligned, which improves charge transfer in the polymer layer. The second SAM layer 340 acts to increase the work function of the silver 330, thereby improving charge transfer from the silver electrodes 330 to the semiconductor polymer 350 and improving the performance of the TFT.
The TFT exhibits very high performance: the hole mobility is 2×10−2 cm2V−1S−1 and the current on/off ratio is approximately 105.
All of the processing steps described above can be implemented in either a batch or a continuous roll-to-roll production environment.
The aforegoing description has been given by way of example only and it will be appreciated by a person skilled in the art that modifications can be made without departing from the scope of the present invention.
| Number | Date | Country | Kind |
|---|---|---|---|
| 0522584.2 | Nov 2005 | GB | national |