Patent Application
20110243835
The invention relates to an indium oxide-based sintered body, particularly a sintered body that includes indium oxide and scandium oxide or aluminum oxide, and a sputtering target using the same.
In recent years, development of displays has rapidly progressed, and various displays such as a liquid crystal display and an EL display have been extensively used for office automation equipment such as a personal computer and a word processor. These displays have a sandwich structure in which a display element is disposed between transparent conductive films.
A silicon-based semiconductor film is mainly used for a switching device (e.g., thin film transistor (TFT)) that drives a display. A silicon-based thin film exhibits excellent stability, excellent workability, a high TFT switching speed, and the like. A silicon-based thin film is generally formed by chemical vapor deposition (CVD).
An amorphous silicon-based thin film has a problem that a high-speed animation or the like cannot be displayed at a high frame rate due to a relatively low switching speed. A crystalline silicon-based thin film achieves a relatively high switching speed, but requires a high temperature of 800° C. or more, laser heating, or the like for crystallization. Specifically, a large amount of energy and a large number of steps are required for producing a crystalline silicon-based thin film. A silicon-based thin film exhibits excellent performance as a voltage device, but shows a change in characteristics with time when causing a current to flow therethrough.
In view of the above situation, an oxide semiconductor film has been studied as a film as an alternative to a silicon-based thin film. For example, Patent Document 1 discloses an oxide semiconductor pn-junction device, and discloses a transparent semiconductor thin film formed of zinc oxide and magnesium oxide as a semiconductor film that forms the device.
A transparent semiconductor thin film formed of zinc oxide and magnesium oxide is etched by a weak acid at a very high etching rate. However, since such a transparent semiconductor thin film is also etched by an etchant used for a metal thin film, the transparent semiconductor thin film may be etched together with a metal thin film formed on the transparent semiconductor thin film when etching the metal thin film. Therefore, the above transparent semiconductor thin film cannot be suitably used when selectively etching only a metal thin film formed on the transparent semiconductor film.
Patent Document 2 discloses an ITO sintered body that contains indium oxide (In2O3), tin oxide (SnO2), and scandium oxide (Sc2O3) as the main components so that the weight ratio satisfies the relationships “(In2O3+Sc2O3):SnO2=99 to 94:1 to 7” and “In2O3:Sc2O3=99.8 to 60:0.2 to 40”. The sintered body disclosed in Patent Document 2 contains 1 to 7 wt % of tin oxide, and functions as a conductive film instead of a semiconductor film since carriers are produced from tin oxide.
Patent Document 3 discloses a thin film that contains indium oxide, tin oxide, and yttrium oxide as the main components. Patent Document 3 relates to a transparent conductive film, and is silent about an oxide semiconductor.
An object of the invention is to provide a sintered body (sputtering target) that enables stable film formation of an indium oxide-based oxide semiconductor film.
Another object of the invention is to provide a sputtering target for producing an excellent crystalline oxide semiconductor film.
The invention provides the following sintered body, sputtering target, and the like.
1. A sintered body comprising an indium oxide crystal, and an oxide solid-dissolved in the indium oxide crystal, the oxide being oxide of one or more metals selected from the group consisting of aluminum and scandium, the sintered body having an atomic ratio “(total of the one or more metals)/(total of the one or more metals and indium)×100)” of 0.001% or more and less than 45%.
2. The sintered body according to 1, wherein the atomic ratio is 0.01 to 30 atom %.
3. The sintered body according to 1, wherein the atomic ratio is 0.5 to 15 atom %.
4. The sintered body according to any one of 1 to 3, wherein the indium oxide crystal has a bixbyite structure.
5. The sintered body according to any one of 1 to 4, wherein the indium oxide crystal has a grain size of less than 10 μm.
6. The sintered body according to any one of 1 to 5, comprising indium oxide and scandium oxide, the indium oxide having a lattice constant within a range between the lattice constant of InScO3 and the lattice constant of In2O3.
7. The sintered body according to any one of 1 to 5, comprising indium oxide and aluminum oxide, the indium oxide having a lattice constant within a range between the lattice constant of InAlO3 and the lattice constant of In2O3.
8. The sintered body according to any one of 1 to 7, further comprising a metal ion having a positive valence of 4 or more in an amount of 10 to 5000 atomic ppm.
9. The sintered body according to 8, comprising the metal ion having a positive valence of 4 or more in an amount of 100 to 2000 atomic ppm.
10. The sintered body according to 8 or 9, wherein the metal ion having a positive valence of 4 or more is one or both of a tin ion and a cerium ion.
11. A method of producing the sintered body according to any one of 1 to 7, the method comprising mixing a powder of oxide of one or more metals selected from the group consisting of aluminum and scandium with a powder of indium oxide, and firing the mixture at 1200 to 1600° C. for 2 to 200 hours.
12. A method of producing the sintered body according to any one of 8 to 10, the method comprising mixing a powder of oxide of one or more metals selected from the group consisting of aluminum and scandium, a powder of indium oxide, and a powder of a metal having a positive valence of 4 or more, and firing the mixture at 1200 to 1600° C. for 2 to 200 hours.
13. The method according to 11 or 12, wherein the mixture is fired in an oxidizing atmosphere.
14. A sputtering target produced using the sintered body according to any one of 1 to 10.
15. A metal oxide thin film formed using the sputtering target according to 14.
16. A semiconductor film comprising the metal oxide thin film according to 15.
17, A thin film transistor comprising the semiconductor film according to 16.
18. The thin film transistor according to 17, the thin film transistor being a channel-etch thin film transistor.
19. The thin film transistor according to 17, the thin film transistor being an etch-stopper thin film transistor.
20. A semiconductor device comprising the thin film transistor according to any one of 17 to 19.
The above sintered body ensures excellent film-forming stability when used as a sputtering target. An excellent semiconductor film is obtained using the sputtering target.
A sintered body according to the invention includes an indium oxide crystal, and an oxide solid-dissolved in the indium oxide crystal, the oxide being oxide of one or more metals selected from the group consisting of aluminum and scandium (hereinafter may be referred to as “specific positive trivalent metal”), the sintered body having an atomic ratio “(total of the one or more metals)/(total of the one or more metals and indium)×100)” of 0.001% or more and less than 45%. The atomic ratio is preferably 0.001 to 40 atom %, and more preferably 0.5 to 15 atom %. If the atomic ratio is within the above range, an oxide semiconductor film produced using the sintered body as a sputtering target exhibits high mobility, and a stable thin film transistor can be produced using the oxide semiconductor film.
The content (atomic ratio) of each metal element (ion) in the sintered body may be determined by inductively coupled plasma (ICP) measurement.
The expression “a metal oxide is solid-dissolved in indium oxide” used herein means that a peak attributed to a metal oxide (oxides of aluminum oxide and scandium) (i.e., raw material) added to indium oxide is not observed by X-ray diffraction measurement of the sintered body.
The lattice constant of an indium oxide crystal normally changes linearly toward the lattice constant of indium oxide or the specific positive trivalent metal oxide due to the addition of the specific positive trivalent metal oxide.
The expression “the lattice constant of the sintered body is within a range between the lattice constant of indium oxide and the lattice constant of the specific positive trivalent metal oxide” used herein means that the specific positive trivalent metal oxide is sufficiently solid-dissolved in indium oxide, and no specific positive trivalent metal oxide that causes an abnormal discharge is present in the sintered body. Therefore, a sputtering target produced using the sintered body ensures stable sputtering, and can produce an oxide semiconductor having excellent surface smoothness (flatness). Note that the specific positive trivalent metal oxide may be included in the sintered body in such an amount that an abnormal discharge does not occur.
In the sintered body according to the invention, it is preferable that the specific positive trivalent metal oxide be completely solid-dissolved in indium oxide. This makes it possible to achieve more stable film formation when using the sintered body as a sputtering target.
The specific positive trivalent metal oxide exhibits high reduction resistance, and suppresses reduction of indium oxide. Therefore, occurrence of nodules is suppressed when using a sputtering target that includes the sintered body according to the invention.
The specific positive trivalent metal oxide has a high ability to bond to oxygen. This makes it possible to suppress oxygen deficiency in a crystalline thin film produced using a sputtering target that includes the sintered body according to the invention, so that a semiconductor thin film is easily obtained.
Moreover, since the specific positive trivalent metal oxide exhibits acid resistance and alkali resistance, the resulting thin film exhibits improved acid resistance and alkali resistance.
Since the lattice constant of a crystalline thin film formed of indium oxide decreases due to the addition of the specific positive trivalent metal oxide, the interatomic distance between the cations decreases. Therefore, a transistor produced using the resulting thin film exhibits improved mobility, so that the S value and the durability of the transistor are improved.
The indium oxide crystal included in the sintered body according to the invention preferably has a bixbyite structure. The bixbyite structure can be confirmed by observing a peak by X-ray diffraction measurement.
The indium oxide crystal preferably has a grain size of less than 10 μm. If the grain size of the indium oxide crystal is too large, an abnormal discharge may occur during sputtering, or nodules may be formed on the sputtering target. The grain size of the indium oxide crystal may be reduced by causing oxide of one or more metals selected from the group consisting of aluminum and scandium to be solid-dissolved in the indium oxide crystal.
The grain size (major axis) of the indium oxide crystal refers to the average grain size of the indium oxide crystals included in the entire field of view (30×30 μm) when observing the sintered body using a scanning electron microscope. If a crystal having a grain size of 10 μm or more is not observed within the field of view, the indium oxide crystals have an average grain size of less than 10 μm.
The sintered body according to the invention preferably has a bulk resistance of 1 Ωcm or less, and particularly preferably 0.5 Ωcm or less. The bulk resistance of the sintered body can be adjusted to 1 Ωcm or less by causing one or more metal oxides to be sufficiently dispersed and solid-dissolved therein. If one or more metal oxides are not sufficiently dispersed and solid-dissolved, an abnormal discharge may occur during sputtering. Note that the sintered body need not have a bulk resistance of less than 0.001 Ωcm.
The sintered body according to the invention preferably has a density of 5.5 g/cm3 or more, more preferably 5.8 g/cm3 or more, and particularly preferably 6.0 g/cm3 or more. Note that the upper limit of the density of the sintered body is the density of indium oxide. The density of the sintered body can be adjusted to 5.5 g/cm3 or more by causing one or more metal oxides to be sufficiently dispersed and solid-dissolved therein. If the sintered body has a low density, the surface of the target may blacken during sputtering, so that an abnormal discharge may occur. Moreover, the sputtering rate may decrease.
The relative density of the sintered body can be adjusted to 90% or more by causing one or more metal oxides to be sufficiently dispersed and solid-dissolved therein. If the oxide sintered body has a low relative density, an abnormal discharge may occur due to blackening of the surface of the target, or the sputtering rate may decrease. The relative density of the sintered body is preferably 95% or more, and more preferably 97% or more. The upper limit of the relative density is 100% or less.
A sintered body according to a preferred embodiment of the invention includes indium oxide and scandium oxide, the indium oxide having a lattice constant within a range between the lattice constant of InScO3 and the lattice constant of In2O3.
A sintered body according to another preferred embodiment of the invention includes indium oxide and aluminum oxide, the indium oxide having a lattice constant within a range between the lattice constant of InAlO3 and the lattice constant of In2O3.
The above sintered body preferably includes a metal ion having a positive valence of 4 or more in an amount of 10 to 5000 atomic ppm, and particularly preferably 100 to 2000 atomic ppm. The bulk resistance of the sintered body can be further reduced due to a metal element having a positive valence of 4 or more. If the content of a metal ion having a positive valence of 4 or more exceeds 5000 ppm, the resulting oxide semiconductor film may not exhibit normally-off semiconductor properties. It is preferable that a metal oxide having a positive valence of 4 or more be also solid-dissolved in indium oxide (i.e., a peak attributed to a metal oxide having a positive valence of 4 or more is not observed). The bulk resistance of the resulting sintered body decreases due to the addition of a positive tetravalent metal oxide. A sputtering target produced using such a sintered body ensures more stable sputtering, and can stably produce an oxide semiconductor film having excellent surface smoothness.
Examples of the metal ion having a positive valence of 4 or more include Ti, Zr, Hf, Nb, Ta, W, Ge, Sn, and Ce. The metal ion having a positive valence of 4 or more is preferably one or both of a tin ion and a cerium ion. SnO2 is abundantly available (i.e., SnO2 supply is stable), and has no toxicity. A small amount (5000 atomic ppm or less) of cerium is incorporated in the indium oxide crystal at the sintering temperature (1200° C. or more) of the sintered body, so that the bulk resistance of the sintered body decreases. The amount of cerium incorporated in indium oxide decreases at the crystallization temperature (e.g., about 250° C. to about 450° C.) of the thin film, so that the effect of reducing the bulk resistance (i.e., the effect of producing carriers) decreases. An oxide semiconductor that exhibits normally-off semiconductor properties can be easily obtained by thus controlling carriers in the resulting crystalline indium oxide film.
The sintered body according to the invention has low bulk resistance, and may suitably be used as a sputtering target. A sputtering target produced using the sintered body ensures stable sputtering, and can stably produce a crystalline indium oxide film. It is also possible to produce a thin film having excellent semiconductor properties.
The sintered body according to the invention may be produced by sintering (firing) a powder mixture prepared by mixing indium oxide with scandium oxide or aluminum oxide at 1200 to 1600° C. for 2 to 200 hours, for example.
Each oxide used as the raw material is preferably a powder having a purity of 99.99% or more. When adding a metal element having a positive valence of 4 or more, a compound (e.g., oxide) of the metal element is used. The compound of the metal element preferably has a purity of 99.99% or more. If each raw material has a purity of 99.99% or more, the impurity content is reduced to less than 100 atomic ppm.
The amount of each raw material is determined depending on the amount of each metal element included in the desired sintered body.
The raw material mixture is mixed and ground using a mill (e.g., bead mill, ball mill, or planetary mill). The mixture is then granulated, and shaped into a shape suitable for a sputtering target or the like.
The mixture may be shaped by pressing, cold isostatic pressing, uniaxial pressing, die forming, casting, injection molding, or the like. A molding aid such as polyvinyl alcohol, methyl cellulose, polywax, or oleic acid may be used when shaping the mixture.
The shaped product is sintered at 1200 to 1600° C. for 2 to 200 hours to obtain a sintered body.
If the sintering temperature is less than 1200° C., a highly dense sintered body may not be obtained. If the sintering temperature exceeds 1600° C., indium oxide and scandium oxide may be pyrolyzed. The sintering temperature is preferably 1300 to 1600° C., and more preferably 1300 to 1550° C.
The sintering time is 2 to 200 hours. If the sintering time is less than 2 hours, the shaped product may not be completely sintered, so that a highly dense sintered body may not be obtained. If the sintering time exceeds 200 hours, it may be disadvantageous from the economical point of view. The sintering time is preferably 5 to 150 hours, and more preferably 10 to 100 hours.
The shaped product is preferably sintered in an oxidizing atmosphere. The oxidizing atmosphere may be air, an oxygen stream, or a pressurized oxygen atmosphere.
The sintered body is cut or ground to a desired shape, and bonded to a backing plate to obtain a sputtering target.
A metal oxide thin film according to the invention is formed in a film using the above sputtering target. The metal oxide thin film is optionally annealed after film formation. The metal oxide thin film is a semiconductor thin film, and may be used for a thin film transistor (e.g., channel-etch thin film transistor or etch-stopper thin film transistor).
The invention is further described below by way of examples and comparative examples. Note that the invention is not limited to the following examples that illustrate preferred examples. The invention also includes various modifications and other examples that are based on the technical concept of the invention.
The following oxide powders were used as raw material powders. The specific surface area of each powder was measured by the BET method.
(a) Indium oxide powder (specific surface area: 6 m2/g)
(b) Scandium oxide powder (specific surface area: 3 m2/g)
The powder mixture had a specific surface area of 6.0 m2/g.
A powder mixture of 990 g of indium oxide and 10 g of scandium oxide was mixed and ground using an agitator bead mill with a wet medium. Zirconia beads having a diameter of 1 mm were used as the media. The specific surface area of the raw material powder mixture was increased by 2 m2/g by grinding while checking the specific surface area of the raw material powder mixture.
The ground powder mixture was dried using a spray dryer, put in a die (diameter: 100 mm, thickness: 20 mm), and pressed using a cold press machine.
The shaped product was sintered at 1500° C. for 20 hours in an oxygen atmosphere (in which oxygen was circulated) to obtain a sintered body.
The measured lattice constant almost coincided with the theoretical lattice constant (see
The density of the sintered body calculated from the weight and the external dimensions of the sintered body cut to a given size was 6.7 g/cm3. The sintered body had a high density, and may suitably be used as a sputtering target sintered body.
The bulk resistance of the sintered body measured by a four-probe method using a resistance meter (“Loresta” manufactured by Mitsubishi Chemical Corporation) was 0.9 Ωcm.
The atomic ratio “Sc/(In+Sc)” in the sintered body determined by ICP measurement was 0.02.
The crystal grain size of the sintered body was 4.8 μm. Note that the average grain size of the indium oxide crystals included in the entire field of view (30×30 μm) when observing the sintered body using a scanning electron microscope was taken as the crystal grain size.
Table 1 shows the sintering conditions, the properties of the sintered body, and the like.
The presence or absence of nodules generated during sputtering was evaluated under the following conditions.
Specifically, a 4-inch target was installed in a sputtering apparatus (manufactured by Shimadzu Corporation). DC magnetron sputtering (power: 10 kWhr, output: 400 W) was performed in an argon gas (100%) atmosphere, and the presence or absence of nodules formed on the surface of the target was observed with the naked eye. A case where nodules were continuously formed in the inner circumferential area and the outer circumferential area of erosion was evaluated as “occurred”.
The presence or absence of an abnormal discharge was evaluated under the following conditions.
Specifically, a 4-inch target was installed in a sputtering apparatus (manufactured by Shimadzu Corporation). DC magnetron sputtering (power: 9 kWhr, output: 400 W) was performed in an argon gas atmosphere, and the voltage during sputtering was monitored for 5 minutes. It was determined that an abnormal discharge occurred when the voltage decreased by 10% or more. A case where an abnormal discharge occurred 10 times or more was evaluated as “Occurred”, and a case where an abnormal discharge occurred less than 10 times was evaluated as “Did not occur”. An abnormal discharge is normally observed 100 times or more when an abnormal discharge has occurred.
A sintered body was produced and evaluated in the same manner as in Example 1, except for changing the atomic ratio “Sc/(In +Sc)”, the sintering temperature, and the sintering time as shown in Table 1. The evaluation results are shown in Table 1.
Note that the measured lattice constant almost coincided with the theoretical lattice constant (see
A sintered body was produced in the same manner as in Example 2, except for using cerium oxide (CeO2) in addition to indium oxide and scandium oxide so that the Ce content was 800 atomic ppm or 1200 atomic ppm based on the total metal elements. The resulting sintered bodies had a density of 6.5 g/cm3, and a bulk resistance of 0.015 Ωcm or 0.011 Ωcm, respectively. It was thus confirmed that the bulk resistance of the sintered body can be reduced by adding a metal element having a positive valence of 4 or more. A peak of a bixbyite structure attributed to indium oxide was observed by X-ray diffraction. The sintered bodies had a lattice constant of 10.1015 Å or 10.1019 Å, respectively. A peak attributed to Sc2O3 or CeO2 (raw material) was not observed.
A sintered body was produced and evaluated in the same manner as in Example 1, except for using only 1000 g of indium oxide without using scandium oxide, and changing the sintering temperature and the sintering time as shown in Table 1. The evaluation results are shown in Table 1.
It was confirmed that the sintered body produced in Comparative Example 1 had a large crystal grain size as compared with the sintered bodies produced in the examples.
A sintered body was produced and evaluated in the same manner as in Example 3, except for changing the sintering temperature and the sintering time as shown in Table 1. The evaluation results are shown in Table 1.
It was confirmed that the sintered body produced in Comparative Example 2 had a large crystal grain size as compared with the sintered bodies produced in the examples. A peak attributed to scandium oxide was observed in addition to a peak attributed to the solid solution of indium oxide and scandium oxide when magnifying the X-ray diffraction chart. It was thus confirmed that scandium oxide was not solid-dissolved in the indium oxide crystal.
A sintered body was produced and evaluated in the same manner as in Example 1, except for using indium oxide and scandium oxide in the atomic ratio shown in Table 1, and changing the sintering temperature and the sintering time as shown in Table 1. The evaluation results are shown in Table 1.
It was confirmed that the sintered body produced in Comparative Example 3 had a low density as compared with the sintered bodies produced in the examples. The lattice constant determined from the X-ray diffraction results almost coincided with the theoretical line when scandium oxide is solid-dissolved in indium oxide. However, a peak attributed to scandium oxide was observed in addition to a peak attributed to the solid solution of indium oxide and scandium oxide when magnifying the X-ray diffraction chart. It was thus confirmed that scandium oxide was not solid-dissolved in the indium oxide crystal. Since the sintered body produced in this comparative example had low strength due to low density and a large crystal grain size, the sintered body was not processed into a target.
A channel-etch thin film transistor shown in
A conductive silicon substrate 10 provided with a thermally oxidized film (SiO2 film) (thickness: 200 nm) was used. The thermally oxidized film functions as a gate insulating film 30, and the conductive silicon part functions as a gate electrode 20.
An oxide film (thickness: 40 nm) (i.e., a precursor of a semiconductor film 40) was formed in a film on the gate insulating film 30 by a sputtering method using a sputtering target (Sc/(In+Sc)=0.06) formed of the sintered body produced in Example 2. Specifically, the atmosphere was evacuated until the back pressure became 5×10−4 Pa, and the sputtering process was performed at room temperature at a pressure of 0.2 Pa and a sputtering power of 100 W while introducing argon (9.5 sccm) and oxygen (0.5 sccm).
A resist was applied to the substrate on which the oxide film was formed, and pre-baked at 80° C. for 15 minutes to form a resist film. The resist film was then irradiated with UV light (intensity: 300 mJ/cm2) through a mask, and developed using 3 wt % tetramethylammonium hydroxide (TMAH). The resist film was then washed with purified water, and post-baked at 130° C. for 15 minutes to form a resist pattern having the desired shape.
The oxide film formed on the substrate provided with the resist pattern was etched using a mixed acid of phosphoric acid, acetic acid, and nitric acid. After removing the resist, the substrate was washed with purified water, and dried by blowing air.
The substrate was then heated at 300° C. for 30 minutes in air inside a hot-blast heating furnace so that the oxide film became a semiconductor to obtain a semiconductor film 40.
A molybdenum metal film was then formed on the semiconductor film 40 and the gate insulating film 30 to a thickness of 300 nm.
A resist was applied to the molybdenum metal film, and pre-baked at 80° C. for 15 minutes to form a resist film. The resist film was then irradiated with UV light (intensity: 300 ml/cm2) through a mask, and developed using 3 wt % tetramethylammonium hydroxide (TMAH). The resist film was then washed with purified water, and post-baked at 130° C. for 15 minutes to form a source/drain electrode resist pattern.
The molybdenum metal film formed on the substrate provided with the resist pattern was etched using a mixed acid of phosphoric acid, acetic acid, and nitric acid to form a channel region 60, a source electrode 50, and a drain electrode 52. The substrate was then washed with purified water, and dried by blowing air to obtain a thin film transistor in which the distance (L) between the source electrode and the drain electrode was 200 μm, and the width (W) of the channel region 60 was 500 μm. The semiconductor film 40 under the channel region was not etched. A crystallized indium oxide film has resistance against (is not dissolved in) a mixed acid of phosphoric acid, acetic acid, and nitric acid. Therefore, a channel-etch thin film transistor can be easily produced.
A normally-off thin film transistor having a field-effect mobility of 17.3 cm2/V·sec, an on-off ratio of 107, and an S value of 0.9 was thus obtained. The thin film transistor had clear pinch-off output characteristics. The threshold voltage (Vth) after applying a voltage of 20 V to the gate electrode for 100 minutes was 0.2 V.
An indium oxide film including scandium oxide was formed on a quartz glass substrate under the same conditions as the sputtering conditions employed in (A). The indium oxide film was then heated at 300° C. for 30 minutes in air inside a hot-blast heating furnace. As a result of X-ray diffraction (XRD) measurement of the resulting semiconductor film, an X-ray diffraction pattern indicating only a peak derived from an indium oxide structure was obtained. It was thus confirmed that the semiconductor film was crystalline. Since the lattice constant of the crystalline semiconductor film was smaller than that of an indium oxide thin film, it was considered that high mobility was achieved.
The carrier concentration determined by hole measurement was 5.7×10+16/cm3.
The following oxide powders were weighed and used as raw material powders. The specific surface area of each powder was measured by the BET method.
(a) Indium oxide powder (specific surface area: 6 m2/g)
(b) Aluminum oxide powder (specific surface area: 6 m2/g)
A powder mixture of the powders (a) and (b) had a specific surface area of 6.0 m2/g.
A powder mixture of 995 g of indium oxide and 5 g of aluminum oxide was mixed and ground using an agitator bead mill with a wet medium. Zirconia beads having a diameter of 1 mm were used as the media. The specific surface area of the raw material powder mixture was increased by 2 m2/g by grinding while checking the specific surface area of the raw material powder mixture.
The ground raw material powder mixture was dried using a spray dryer, put in a die (diameter: 100 mm, thickness: 20 mm), and pressed using a cold press machine. The shaped product was sintered at 1550° C. for 20 hours in an oxygen atmosphere (in which oxygen was circulated) to obtain a sintered body.
As a result of analyzing the X-ray diffraction chart, an In2O3 bixbyite structure was included in the sintered body. A peak attributed to aluminum oxide (raw material) was not observed. The lattice constant was 10.11587.
The density, the bulk resistance, the crystal grain size, the presence or absence of nodules, and the presence or absence of an abnormal discharge were measured and evaluated in the same manner as in Example 1. The results are shown in Table 2.
A sintered body was produced and evaluated in the same manner as in Example 6, except for mixing indium oxide and aluminum oxide in the ratio shown in Table 2, and changing the sintering temperature and the sintering time as shown in Table 2. The results are shown in Table 2.
A sintered body was produced in the same manner as in Example 8, except for using cerium oxide (CeO2) in addition to indium oxide and aluminum oxide so that the Ce content was 800 atomic ppm or 1200 atomic ppm based on the total metal elements. The resulting sintered bodies had a density of 6.56 g/cm3, and a bulk resistance of 0.017 Ωcm or 0.009 Ωcm, respectively. It was thus confirmed that the bulk resistance of the sintered body can be reduced by adding a metal element having a positive valence of 4 or more. A peak of a bixbyite structure attributed to indium oxide was observed by X-ray diffraction. The sintered bodies had a lattice constant of 10.1015 Å or 10.1019 Å, respectively. A peak attributed to Al2O3 or CeO2 (raw material) was not observed.
A channel-etch thin film transistor shown in
A normally-off thin film transistor having a field-effect mobility of 49.3 cm2/V·sec, an on-off ratio of 107, and a S value of 0.89 was thus obtained. The thin film transistor had clear pinch-off output characteristics. The threshold voltage (Vth) after applying a voltage of 20 V to the gate electrode for 100 minutes was 0.2 V.
A semiconductor film was formed and heated in the same manner as in Evaluation Example 1(B), except for using the sputtering target produced in Example 8. As a result of X-ray diffraction (XRD) measurement of the resulting semiconductor film, an X-ray diffraction pattern indicating only a peak of an indium oxide structure was obtained. It was thus confirmed that the semiconductor film was crystalline. The carrier concentration determined by hole measurement was 5.7×10+16/cm3.
The sintered body according to the invention may be used as a sputtering target for forming an indium oxide-based semiconductor film. A film produced using the sputtering target according to the invention may be used for a transistor.
| Number | Date | Country | Kind |
|---|---|---|---|
| 2008-318293 | Dec 2008 | JP | national |
| Filing Document | Filing Date | Country | Kind | 371c Date |
|---|---|---|---|---|
| PCT/JP2009/059954 | 6/1/2009 | WO | 00 | 6/14/2011 |