Patent Grant
11932590
The present invention relates to a novel inhibitor for ruthenium-containing gas (RuO4 gas) generation and method for inhibiting RuO4 gas generation to inhibit a RuO4 gas to be generated when a semiconductor wafer containing ruthenium is brought into contact with a treatment liquid in a manufacturing process of a semiconductor element.
In recent years, microfabrication design has been promoted for the design rule for semiconductor elements, and thus the wiring resistance tends to increase. As a result of the increase in wiring resistance, the high-speed operation of a semiconductor element is markedly impaired, thus making it necessary to take countermeasures. In view of this, a desired wiring material is a wiring material having more solid electromigration resistance and a lower electric resistance value than conventional wiring materials.
Ruthenium has higher electromigration resistance than aluminum and copper which are conventional wiring materials, and ruthenium can decrease the electric resistance value of the wiring, thus attracting attention particularly as a wiring material for which the design rule for semiconductor elements is 10 nm or less. Not only in cases where ruthenium is used as a wiring material but also in cases where copper is used as a wiring material, ruthenium can prevent electromigration, and thus, using ruthenium as a barrier metal for copper wiring is under study.
In cases where ruthenium is selected as a wiring material in a wiring formation step of a semiconductor element, the wiring is formed by dry or wet etching in the same manner as in cases where a conventional wiring material is used. However, since it is difficult to etch ruthenium by dry etching with an etching gas, or to etch/remove ruthenium by CMP polishing, more precise etching is desired, and specifically, wet etching is attracting attention.
In cases where ruthenium is subjected to wet etching under alkaline conditions, ruthenium is dissolved, for example, in the form of RuO4− or RuO42− in a treatment liquid. RuO4− or RuO42− is changed to RuO4 in a treatment liquid, and part of the RuO4 is gasified and released into a gas phase. RuO4 is strongly oxidative, and thus, not only is harmful to the human body but also is easily reduced to generate RuO2 particles. In general, particles cause a decrease in the yield rate, which constitutes a serious problem in semiconductor formation steps. Against such a background, it is very important to inhibit the generation of a RuO4 gas.
Patent Document 1 describes a chemical liquid with a pH of 12 or higher and an oxidation-reduction potential of 300 mV vs. SHE or higher as an etching liquid for a ruthenium film. In addition, a method for etching a ruthenium film using a solution of a halogen oxoate, such as hypochlorite, chlorite, and bromate, is presented.
Patent Document 2 proposes a method of oxidizing, dissolving, and removing ruthenium with an aqueous solution containing orthoperiodic acid having a pH of 11 or higher.
Patent Document 3 describes a CMP slurry containing a ruthenium-coordinated nitric oxide ligand (N—O ligand) that does not generate a RuO4 gas in chemical mechanical polishing (CMP) of ruthenium.
Patent Document 1: Japanese Patent Laid-Open No. 2002-161381
Patent Document 2: International Publication No. WO2016/068183
Patent Document 3: Japanese Patent Laid-Open No. H5-314019
However, based on the study by the present inventors, it has been found that there is room for improvement with respect to the conventional etching liquids described in the cited Document 1 to 3 because of the following.
For example, the method for etching ruthenium described in Patent Document 1 is intended to remove a ruthenium residue adhered to the back surface or bevels of a semiconductor substrate, and is capable of dissolving and removing ruthenium. However, Patent Document 1 does not mention anything about the inhibition of a RuO4 gas, and in fact the method described in Patent Document 1 could not inhibit RuO4 gas generation.
In addition, Patent Document 2 discloses a ruthenium removal composition containing orthoperiodic acid, which can etch an etching residue containing ruthenium. However, Patent Document 2 does not mention anything about the inhibition of a RuO4 gas, and a RuO4 gas generated during the etching treatment could not be inhibited.
Further, Patent Document 3 shows that it is possible to inhibit a toxic RuO4 gas by using a CMP slurry containing a ruthenium-coordinated nitric oxide ligand (N—O ligand) in performing CMP. However, since the CMP slurry shown in Patent Document 3 is acidic, it is difficult to inhibit a RuO4 gas by the CMP slurry composition shown in Patent Document 3 under alkaline conditions where the dissolution mechanism of ruthenium is different. In fact, when the ruthenium N—O ligand described in Patent Document 3 was added to an alkaline ruthenium etching liquid containing hypochlorous acid, then a RuO4 gas was generated, therefore it was confirmed that there was no RuO4 gas inhibitory effect.
Therefore, an object of the present invention is to provide an inhibitor for RuO4 gas generation capable of inhibiting a RuO4 gas, which may be generated when a semiconductor wafer containing ruthenium is brought into contact with a treatment liquid under alkaline conditions.
The present inventors diligently made a study to achieve the above object, in which addition of a variety of onium salts to a treatment liquid for semiconductor wafers containing ruthenium was investigated. Since it was not possible to inhibit a RuO4 gas merely by using a treatment liquid for semiconductor wafers containing ruthenium, various additive ingredients were combined. As a result, it was found that the RuO4 gas generation could be inhibited by adding a specific onium salt, thereby completing the present invention.
In other words, the composition of the present invention is as follows.
Aspect 1: An inhibitor for RuO4 gas generation comprising an onium salt consisting of an onium ion and a bromine-containing ion.
Aspect 2: The inhibitor for RuO4 gas generation according to Aspect 1, wherein the onium salt is a quaternary onium salt expressed by Formula (1), a tertiary onium salt expressed by Formula (2), an onium salt expressed by Formula (3), or an onium salt expressed by Formula (4).
(In Formula (1), A+ is an ammonium ion or a phosphonium ion; and R1, R2, R3, and R4 are independently an alkyl group with a carbon number from 1 to 25, an allyl group, an aralkyl group having an alkyl group with a carbon number from 1 to 25, or an aryl group. When R1, R2, R3, and R4 are alkyl groups, at least one of the alkyl groups in R1, R2, R3, and R4 has a carbon number of 2 or more. At least one hydrogen atom in a ring of an aryl group in the aralkyl group, or the aryl group may be replaced with a fluorine atom, a chlorine atom, an alkyl group with a carbon number from 1 to 10, an alkenyl group with a carbon number from 2 to 10, an alkoxy group with a carbon number from 1 to 9, or an alkenyloxy group with a carbon number from 2 to 9; and in these groups, at least one hydrogen atom may be replaced with a fluorine atom or a chlorine atom.
In Formula (2), A+ is a sulfonium ion; and R1, R2, and R3 are independently an alkyl group with a carbon number from 1 to 25, an allyl group, an aralkyl group having an alkyl group with a carbon number from 1 to 25, or an aryl group. When R1, R2, and R3 are alkyl groups, at least one of the alkyl groups in R1, R2, and R3 has a carbon number of 2 or more. At least one hydrogen atom in a ring of an aryl group in the aralkyl group, or the aryl group may be replaced with a fluorine atom, a chlorine atom, an alkyl group with a carbon number from 1 to 10, an alkenyl group with a carbon number from 2 to 10, an alkoxy group with a carbon number from 1 to 9, or an alkenyloxy group with a carbon number from 2 to 9; and in these groups, at least one hydrogen atom may be replaced with a fluorine atom or a chlorine atom.
In Formula (3), Z is an aromatic group or alicyclic group that may comprise a nitrogen atom, a sulfur atom, or an oxygen atom, and in the aromatic group or the alicyclic group, a hydrogen atom bonded to a carbon atom or a nitrogen atom may have a chlorine atom, a bromine atom, a fluorine atom, an iodine atom, at least one alkyl group with a carbon number from 1 to 15, at least one alkenyloxy group with a carbon number from 2 to 9, an aromatic group that may be substituted with at least one alkyl group with a carbon number from 1 to 15, or an alicyclic group that may be substituted with at least one alkyl group with a carbon number from 1 to 15. A+ is an ammonium ion or a sulfonium ion. R is a chlorine atom, a bromine atom, a fluorine atom, an iodine atom, an alkyl group with a carbon number from 1 to 15, an allyl group, an aromatic group that may be substituted with at least one alkyl group with a carbon number from 1 to 15, or an alicyclic group that may be substituted with at least one alkyl group with a carbon number from 1 to 15. The n is an integer of 1 or 2 and indicates the number of R. When n is 2, R may be the same or different and may form a ring.
In Formula (4), A+ is independently an ammonium ion, or a phosphonium ion; and R1, R2, R3, R4, R5, and R6 are independently an alkyl group with a carbon number from 1 to 25, an allyl group, an aralkyl group having an alkyl group with a carbon number from 1 to 25, or an aryl group. At least one hydrogen atom in a ring of an aryl group in the aralkyl group, or the aryl group may be replaced with a fluorine atom, a chlorine atom, an alkyl group with a carbon number from 1 to 10, an alkenyl group with a carbon number from 2 to 10, an alkoxy group with a carbon number from 1 to 9, or an alkenyloxy group with a carbon number from 2 to 9; and in these groups, at least one hydrogen atom may be replaced with a fluorine atom or a chlorine atom. The a is an integer from 1 to 10.
In Formulas (1) to (4), X− is a bromine-containing ion.)
Aspect 3: The inhibitor for RuO4 gas generation according to Aspect 2, wherein the quaternary onium salt is a salt comprising at least one ammonium ion selected from the group consisting of tetraethylammonium ion, tetrapropylammonium ion, tetrabutylammonium ion, tetrapentylammonium ion, and tetrahexylammonium ion.
Aspect 4: The inhibitor for RuO4 gas generation according to any one of Aspects 1 to 3, wherein the concentration of the onium salt in the inhibitor for RuO4 gas generation is from 0.0001 to 50 mass %.
Aspect 5: The inhibitor for RuO4 gas generation according to any one of Aspects 1 to 4, wherein the bromine-containing ion is a bromite ion, a bromate ion, a perbromate ion, a hypobromite ion, or a bromide ion.
Aspect 6: The inhibitor for RuO4 gas generation according to any one of Aspects 1 to 5, wherein the concentration of hypobromite ion in the inhibitor for RuO4 gas generation is 0.001 mol/L or more and 0.20 mol/L or less.
Aspect 7: The inhibitor for RuO4 gas generation according to any one of Aspects 1 to 6, wherein the concentration of hypobromite ion in the inhibitor for RuO4 gas generation is 0.01 mol/L or more and 0.10 mol/L or less.
Aspect 8: The inhibitor for RuO4 gas generation according to any one of Aspects 1 to 7, wherein the pH of the inhibitor for RuO4 gas generation at 25° C. is 8 or more and 14 or less.
Aspect 9: The inhibitor for RuO4 gas generation according to any one of Aspects 1 to 8, wherein the pH of the inhibitor for RuO4 gas generation at 25° C. is 12 or more and 13 or less.
Aspect 10: The inhibitor for RuO4 gas generation according to any one of Aspects 1 to 9, wherein the inhibitor for RuO4 gas generation comprises an oxidizing agent different from the bromine-containing ion.
Aspect 11: The inhibitor for RuO4 gas generation according to Aspect 10, wherein the oxidizing agent is an oxidizing agent comprising a hypochlorite ion, or ozone.
Aspect 12 A method for inhibiting RuO4 gas generation comprising a step of using the inhibitor for RuO4 gas generation according to any one of Aspects 1 to 11.
With the inhibitor for RuO4 gas generation of the present invention, RuO4 gas generation, which may cause particle formation or decrease in the yield rate in a semiconductor manufacturing process, can be inhibited owing to the onium salt effect. In addition, since the selectable pH range and types of oxidizing agents are expanded, it becomes possible to materialize a stable treatment liquid by selecting an appropriate oxidizing agent.
An inhibitor for RuO4 gas generation means a composition that inhibits RuO4 gas generation when the same is added to a liquid for treating ruthenium (hereinafter referred to as “ruthenium treatment liquid”), and refers to a liquid containing an onium salt consisting of an onium ion and a bromine-containing ion.
The ruthenium treatment liquid refers to a liquid containing a component that comes into contact with ruthenium to cause physical or chemical changes to the ruthenium. Examples thereof include liquids used in steps of treating ruthenium, such as an etching step, a residue removal step, a washing step, and a CMP step, in semiconductor manufacturing processes. A liquid for cleaning ruthenium adhered to chamber inner walls, piping, etc. of each device used in the semiconductor manufacturing processes is also included.
The ruthenium treated with a ruthenium treatment liquid is wholly or partially dissolved, dispersed, or precipitated in the ruthenium treatment liquid, which becomes responsible for generation of RuO4 (gas) and/or RuO2 (particles). When an inhibitor for RuO4 gas generation of the present invention is added to a ruthenium treatment liquid, an anion, such as RuO4− and RuO42− (hereinafter occasionally referred to as RuO4−, etc.), present in the ruthenium treatment liquid and an onium ion form an ion pair soluble in the ruthenium solution, so as to inhibit generation of a RuO4 gas and/or RuO2.
The inhibitor for RuO4 gas generation of the present invention contains an onium salt to inhibit RuO4 gas generation. The onium salt consists of an onium ion and a bromine-containing ion. In this regard, the bromine-containing ion is an ion that contains bromine, and examples thereof include a bromite ion, a bromate ion, a perbromate ion, a hypobromite ion, and a bromide ion.
In order for an onium salt contained in the inhibitor for RuO4 gas generation of the present invention to exhibit its power of inhibiting RuO4 gas generation, dissociation of the onium salt to an onium ion and a bromine-containing ion is required. This is because the onium ion generated by the dissociation of the onium salt interacts with RuO4−, etc. to inhibit RuO4 gas generation. Since an onium salt comprising a halogen-containing ion easily dissociates, excellently dissolves, and can stably supply onium ions, the same can be used as an onium salt to be contained in the inhibitor for RuO4 gas generation of the present invention. Among others, an onium salt comprising a bromine-containing ion is more stable and more easily synthesizable than an onium salt comprising a chlorine-containing ion, or a fluorine-containing ion, and therefore a high-purity product can be obtained industrially at a low cost. In addition, an onium salt comprising a bromine-containing ion has an advantage of containing more onium ions per unit weight than that comprising an iodine-containing ion. Therefore, an onium salt contained in the inhibitor for RuO4 gas generation comprises a bromine-containing ion.
When the onium salt is contained, RuO4 gas generation from the ruthenium treatment liquid can be inhibited. That is, RuO4−, etc. generated by dissolution of ruthenium are trapped in the ruthenium treatment liquid by electrostatic interaction with onium ions. Since the trapped RuO4−, etc. exist relatively stable in the treatment liquid as an ion-pair, they hardly change into RuO4. As a result, the RuO4 gas generation is inhibited and generation of RuO2 particles is also inhibited.
As an onium salt that is effective in inhibiting a RuO4 gas, those expressed by the following Formulas (1) to (4) are preferred.
(In Formula (1 ), A+ is an ammonium ion, or a phosphonium ion; and R1, R2, R3, and R4 are independently an alkyl group with a carbon number from 1 to 25, an allyl group, an aralkyl group having an alkyl group with a carbon number from 1 to 25, or an aryl group. When R1, R2, R3, and R4 are alkyl groups, at least one of the alkyl groups in R1, R2, R3, and R4 has a carbon number of 2 or more. At least one hydrogen atom in a ring of an aryl group in the aralkyl group, or the aryl group may be replaced with a fluorine atom, a chlorine atom, an alkyl group with a carbon number from 1 to 10, an alkenyl group with a carbon number from 2 to 10, an alkoxy group with a carbon number from 1 to 9, or an alkenyloxy group with a carbon number from 2 to 9; and in these groups, at least one hydrogen atom may be replaced with fluorine or chlorine. X− is a bromine-containing ion.)
(In Formula (2), A+ is a sulfonium ion; and R1, R2, and R3 are independently an alkyl group with a carbon number from 1 to 25, an allyl group, an aralkyl group having an alkyl group with a carbon number from 1 to 25, or an aryl group. When R1, R2, and R3 are alkyl groups, at least one of the alkyl groups in R1, R2, and R3 has a carbon number of 2 or more. At least one hydrogen atom in a ring of an aryl group in the aralkyl group, or the aryl group may be replaced with a fluorine atom, a chlorine atom, an alkyl group with a carbon number from 1 to 10, an alkenyl group with a carbon number from 2 to 10, an alkoxy group with a carbon number from 1 to 9, or an alkenyloxy group with a carbon number from 2 to 9; and in these groups, at least one hydrogen atom may be replaced with a fluorine atom or a chlorine atom. X− is a bromine-containing ion.)
The alkyl groups of R1, R2, R3, and R4 in Formula (1) or (2) can be used without any particular restriction insofar as their carbon numbers are independently from 1 to 25. When the carbon number is higher, specifically when the carbon number is, for example, 3 or higher, an onium ion more strongly interacts with RuO4−, etc., so that a RuO4 gas is better inhibited. On the other hand, the larger the carbon number is, the bulkier the onium ion becomes, so the ion pair to be generated at the time of the electrostatic interaction with RuO4−, etc. become less soluble in a ruthenium treatment liquid to generate precipitates. The precipitates become particles and cause decrease in the yield rate of a semiconductor element. In this regard, when the carbon number is larger, the solubility in a ruthenium treatment liquid becomes lower, and air bubbles are apt to be formed in the treatment liquid. When the solubility is higher, a larger amount of an onium salt can be dissolved in the treatment liquid, and therefore the inhibitory effect on the RuO4 gas becomes higher. Conversely, when the carbon number is smaller, the interaction between the onium ions and RuO4−, etc. becomes weaker, and therefore the inhibitory effect on the RuO4 gas becomes weaker. Consequently, the carbon numbers of alkyl groups in Formula (1) or (2) are independently preferably from 1 to 25, more preferably from 2 to 10, and most preferably from 3 to 6. However, when R1, R2, R3, and R4 in Formula (1) are alkyl groups, the carbon number of at least one alkyl group among R1, R2, R3, and R4 may be 2 or more: and when R1, R2, and R3 in Formula (2) are alkyl groups, the carbon number of at least one alkyl group among R1, R2, and R3 may be 2 or more. When an onium salt includes alkyl groups having such carbon numbers, the RuO4 gas generation can be inhibited, and precipitates are less likely to be formed through interactions with RuO4−, etc. Therefore, the same can be used favorably as an inhibitor for RuO4 gas generation.
The aryl groups of R1, R2, R3, and R4 in Formula (1) or (2) independently include not only an aromatic hydrocarbon, but also a heteroaryl with a heteroatom, and, although there is no particular restriction, a phenyl group and a naphthyl group are preferred. Examples of the heteroatom include nitrogen, oxygen, sulfur, phosphorus, chlorine, bromine, and iodine.
The quaternary and tertiary onium salts expressed by Formulas (1) and (2) are salts composed of an ammonium ion, a phosphonium ion, or a sulfonium ion that can exist stably in an inhibitor for RuO4 gas generation, or a ruthenium treatment liquid. In general, the alkyl chain length of these ions can be easily controlled, and it is also easy to introduce an allyl group or an aryl group. This makes it possible to control the size, symmetry, hydrophilicity, hydrophobicity, stability, solubility, charge density, surface active performance, etc. of the ions, and such properties of salts composed of these ions can be similarly controlled. Such salts can be used as an onium salt represented by Formula (1) or (2) according to the present invention.
(In Formula (3), Z is an aromatic group or alicyclic group that may comprise a nitrogen atom, a sulfur atom, or an oxygen atom, and in the aromatic group or the alicyclic group, a hydrogen atom bonded to a carbon atom or a nitrogen atom may have a chlorine atom, a bromine atom, a fluorine atom, an iodine atom, at least one alkyl group with a carbon number from 1 to 15, at least one alkenyloxy group with a carbon number from 2 to 9, an aromatic group that may be substituted with at least one alkyl group with a carbon number from 1 to 15, or an alicyclic group that may be substituted with at least one alkyl group with a carbon number from 1 to 15. A+ is an ammonium ion or a sulfonium ion. R is a chlorine atom, a bromine atom, a fluorine atom, an iodine atom, an alkyl group with a carbon number from 1 to 15, an allyl group, an aromatic group that may be substituted with at least one alkyl group with a carbon number from 1 to 15, or an alicyclic group that may be substituted with at least one alkyl group with a carbon number from 1 to 15. The n is an integer of 1 or 2 and indicates the number of R. When n is 2, R may be the same or different and may form a ring. X− is a bromine-containing ion.)
An onium salt having the above structure can exist stably in an alkaline inhibitor for RuO4 gas generation or ruthenium treatment liquid. In this regard, the solubility of the onium salt in the inhibitor for RuO4 gas generation or ruthenium treatment liquid, and the stability of ion pairs of the onium ion and RuO4, etc. may be regulated by replacing a hydrogen atom bonded to a carbon or a nitrogen atom in the aromatic group or alicyclic group of Z in Formula (3) with an alkyl group, an aromatic group substituted with an alkenyloxy group, or an alicyclic group substituted with an alkyl group each having a suitable carbon number, or by appropriately selecting for R from an alkyl group, an allyl group, an aromatic group which may be substituted with an alkyl group, or an alicyclic group which may be substituted with an alkyl group.
Examples of the onium ions include cations such as imidazolium ion, pyrrolidinium ion, pyridinium ion, piperidinium ion, ammonium ion, phosphonium ion, fluoronium ion, chloronium ion, bromonium ion, iodonium ion, oxonium ion, sulfonium ion, selenonium ion, telluronium ion, arsonium ion, stibonium ion, and bismuthonium ion; and imidazolium ion, pyrrolidinium ion, pyridinium ion, piperidinium ion, and oxazolium ion are preferable.
Specific examples of onium salts comprising these onium ions include 1-butyl-2,3-dimethylimidazolium bromide, 1-hexyl-3-methylimidazolium bromide, 1-methyl-3-n-octylimidazolium bromide, 1-butyl-1-methylpyrrolidinium bromide, 1-ethyl-1-methylpyrrolidinium bromide, 1-butyl-1-methylpiperidinium bromide, 5-azoniaspiro[4,4]nonane bromide, 1-methylpyridinium bromide, 1-ethylpyridinium bromide, and 1-propylpyridinium bromide.
(In Formula (4), A+ is independently an ammonium ion, or a phosphonium ion; and R1, R2, R3, R4, R5, and R6 are independently an alkyl group with a carbon number from 1 to 25, an allyl group, an aralkyl group having an alkyl group with a carbon number from 1 to 25, or an aryl group. At least one hydrogen atom in a ring of an aryl group in the aralkyl group, or the aryl group may be replaced with a fluorine atom, a chlorine atom, an alkyl group with a carbon number from 1 to 10, an alkenyl group with a carbon number from 2 to 10, an alkoxy group with a carbon number from 1 to 9, or an alkenyloxy group with a carbon number from 2 to 9; and in these groups, at least one hydrogen atom may be replaced with a fluorine atom or a chlorine atom. The a is an integer from 1 to 10. X− is a bromine-containing ion.)
The alkyl groups of R1, R2, R3, R4, R5, and R6 in Formula (4) can be used without any particular restriction insofar as their carbon numbers are independently from 1 to 25. The valence of an onium salt represented by Formula (1) above is 1, but the one represented by Formula (4) is a dication with a valence of 2, so it is apt to be bound to RuO4−, etc. by a stronger electrostatic interaction. For this reason, even when the carbon number of an alkyl group in Formula (4) is smaller than that in Formula (1), it exerts an inhibitory effect on a RuO4 gas. For these reasons, the carbon numbers of the alkyl groups in Formula (4) are independently preferably from 1 to 25, more preferably from 1 to 10, and most preferably from 1 to 6. When the onium salt includes alkyl groups having such carbon numbers, the RuO4 gas generation can be inhibited through interactions with RuO4−, etc., and precipitates are less likely to be formed. Therefore, the same can be used favorably as an inhibitor for RuO4 gas generation.
The aryl groups of R1, R2, R3, R4, R5, and R6 in Formula (4) independently include not only an aromatic hydrocarbon but also a heteroaryl containing a heteroatom, and, although there are no particular restrictions, a phenyl group and a naphthyl group are preferable. Examples of the heteroatom include nitrogen, oxygen, sulfur, phosphorus, chlorine, bromine, and iodine.
The onium salt expressed by Formula (4) is composed of an ammonium ion or a phosphonium ion that can exist stably in an inhibitor for RuO4 gas generation or a ruthenium treatment liquid. In general, it is easy to regulate the alkyl chain length of an ammonium ion or a phosphonium ion, and it is also easy to introduce an allyl group or an aryl group. This makes it possible to control the size, symmetry, hydrophilicity, hydrophobicity, stability, solubility, charge density, surface active performance, etc. of the ammonium ion or the phosphonium ion.
Examples of the onium salt expressed by Formula (4) which can be suitably applied may include hexamethonium bromide, and decamethonium bromide. An inhibitor for RuO4 gas generation containing such an onium salt can inhibit generation of a RuO4 gas and RuO2 particles especially in a treatment of ruthenium.
As the quaternary onium salt expressed by Formula (1) contained in the inhibitor for RuO4 gas generation of the present invention, an ammonium salt is preferable, because the stability is excellent and a high-purity industrial product thereof is easily available at a low price. Among others a tetraalkylammonium salt is preferable as the onium salt, because it is extremely stable and easily synthesizable. Specific examples thereof include salts comprising a tetraethyl ammonium ion, a tetrapropylammonium ion, a tetrabutylammonium ion, a tetrapentylammonium ion, and a tetrahexylammonium ion. An inhibitor containing the onium salt can inhibit especially generation of a RuO4 gas and RuO2 particles in a treatment of ruthenium.
The concentration of the onium salt in the inhibitor for RuO4 gas generation is preferably from 0.0001 to 50 mass %. When the concentration of the onium salt is too small, not only the interaction with RuO4−, etc. is weakened to reduce the inhibitory effect on a RuO2 gas is reduced, but also the amount of RuO4−, etc. soluble in a ruthenium treatment liquid is decreased to reduce the number of times of reuse of the ruthenium treatment liquid. On the other hand, when its addition amount is too large, the amount of onium ions adsorbed on the ruthenium surface increases to cause reduction in the dissolution rate of ruthenium or non-uniform etching of the ruthenium surface. Therefore, it is preferable that the inhibitor for RuO4 gas generation of the present invention contains an onium salt at from 0.0001 to 50 mass %, more preferably at from 0.01 to 35 mass %, and further preferably at from 0.1 to 20 mass %. The concentration ranges of the onium salt in a liquid mixture of an inhibitor for RuO4 gas generation and a ruthenium treatment liquid can be adjusted to the aforedescribed concentration ranges. When the onium salt is added, one kind can be added, or a combination of two or more kinds can be added. When two or more kinds of onium salts are added, it is possible to inhibit effectively RuO4 gas generation insofar as the total concentration of onium salts is in the above concentration range. The above concentration ranges of the onium salt can be applied to any of the onium salts expressed by Formulas (1) to (4).
The inhibitor for RuO4 gas generation of the present invention can contain an oxidizing agent. The oxidizing agent refers to one that has the ability to substantially dissolve ruthenium contained in a semiconductor wafer. As the oxidizing agent any of publicly known oxidizing agents that can dissolve ruthenium can be used without any particular restriction. Examples of the oxidizing agent include, but are not limited to, halogen oxyacid and permanganic acid and their salts, hydrogen peroxide, ozone, and a cerium(IV) salt. In this regard, the halogen oxyacid means hypochlorous acid, chlorous acid, chloric acid, perchloric acid, hypobromous acid, bromous acid, bromic acid, perbromic acid, hypoiodous acid, iodous acid, iodic acid, metaperiodic acid, orthoperiodic acid, periodic acid, and ions thereof. Since the oxidizing agent can dissolve ruthenium contained in a wafer, dissolution of ruthenium and inhibition of RuO4 gas generation can be carried out at the same time by using the inhibitor for RuO4 gas generation containing the oxidizing agent and onium salt. Further, addition of an oxidizing agent promotes dissolution of ruthenium, as well as redissolution of precipitated RuO2 particles. Therefore, a ruthenium-containing wafer can be treated efficiently while inhibiting generation of a RuO4 gas and RuO2 particles by using the inhibitor for RuO4 gas generation containing the onium salt and oxidizing agent.
Among the oxidizing agents, from the viewpoints that they can be used stably under alkaline conditions, and in a broad concentration range, halogen oxyacid, an ion of halogen oxyacid, hydrogen peroxide, or ozone is suitable as the oxidizing agent; hypochlorous acid, hypobromous acid, metaperiodic acid, orthoperiodic acid, ions thereof, or ozone is more suitable; hypochlorous acid, hypobromous acid, a hypochlorite ion, a hypobromite ion, or ozone is further suitable; a hypobromite ion, a hypochlorite ion, or ozone is still further suitable; and a hypobromite ion, or a hypochlorite ion is most preferable. These oxidizing agents can also be present in a treatment liquid as salts, which are preferably, for example, a tetraalkylammonium hypochlorite, or a tetraalkylammonium hypobromite; and more preferably tetramethylammonium hypochlorite, or tetramethylammonium hypobromite. An oxidizing agent to be contained in a treatment liquid can be composed of one kind, or two or more kinds. For example, when bromine-containing ions are contained as an oxidizing agent in the inhibitor for RuO4 gas generation, the inhibitor for RuO4 gas generation can further include an oxidizing agent different from the bromine-containing ions. As such an oxidizing agent different from the bromine-containing ions, an oxidizing agent containing hypochlorite ions or ozone is preferable, and an oxidizing agent containing hypochlorite ions is more preferable. The reasons therefor will be described below taking a case where the bromine-containing ion is a hypobromite ion as an example. A hypobromite ion is reduced to Br− by oxidation of ruthenium, etc., natural decomposition, decomposition by ultraviolet light, thermal decomposition, or contact with a reducing agent or an acid. Since Br− does not dissolve ruthenium, has a low inhibitory effect on a RuO4 gas, and does not re-dissolve RuO2 particles, the inhibitory power on RuO4 gas generation tends to decline due to decrease in hypobromite ions. When the inhibitor for RuO4 gas generation of the present invention contains an appropriate oxidizing agent different from hypobromite ions, such as hypochlorite ions or ozone, Br− produced by reduction or decomposition can be re-oxidized to hypobromite ions, so that the decline of the inhibitory power on RuO4 gas generation due to decrease in hypobromite ions can be mitigated. In other words, when hypobromite ions and an appropriate oxidizing agent are contained in a treatment liquid, the stability of an inhibitor for RuO4 gas generation is improved. As such an oxidizing agent, it is required that the oxidation-reduction potential between the oxidizing agent and a chemical species formed by reduction of the oxidizing agent exceeds the oxidation-reduction potential of the hypobromite ion/Br− system, and among others hypochlorite ions or ozone is preferable, because Br− can be efficiently oxidized to a hypobromite ion.
There is no particular restriction on a method for producing the above tetramethylammonium hypochlorite or tetramethylammonium hypobromite, and those produced by various publicly known methods can be used. For example, tetramethylammonium hypochlorite, or tetramethylammonium hypobromite produced by a method, in which chlorine or bromine is blown into tetramethylammonium hydroxide, a method, in which hypochlorous acid or hypobromous acid is mixed with tetramethylammonium hydroxide, a method, in which cations in a solution of hypochlorite or hypobromite are replaced with tetramethyl ions using an ion exchange resin, a method, in which a distillate of a solution containing hypochlorite or hypobromous acid is mixed with tetramethylammonium hydroxide, can be used favorably.
Although there is no particular restriction on the concentration of the hypobromite ions in the inhibitor for RuO4 gas generation of the present invention insofar as it does not depart from the spirit and scope of the present invention, it is preferably 0.001 mol/L or more and 0.20 mol/L or less in terms of the bromine element content included in hypobromite ions, more preferably 0.005 mol/L or more and 0.20 mol/L or less, and most preferably 0.01 mol/L or more and 0.10 mol/L or less. When the concentration of hypobromite ions is too low, the RuO2 particles generated by dissolution of ruthenium cannot be dissolved, and there arises a risk that the yield rate of elements may be lowered due to adhesion of RuO2 to a semiconductor wafer. Meanwhile, when the concentration of hypobromite ions is too high, decomposition is accelerated by oxidation of onium ions, and there arises a risk that the gas inhibition effect is decreased. The inhibitor for RuO4 gas generation, in which the concentration is controlled in the above range, is capable of treating efficiently ruthenium-containing wafers, while inhibiting generation of a RuO4 gas and RuO2 particles.
The pH of the inhibitor for RuO4 gas generation of the present invention at 25° C. is preferably 8 or more and 14 or less. When the pH is less than 8, dissolution of ruthenium is more likely to occur via RuO2 or Ru(OH)3 rather than via anions such as RuO4−, etc., the gas inhibition effect of onium salts is prone to be lowered. This RuO2 constitutes a source of particles, and when the pH is less than 8, there arises a problem that the generated amount of RuO4 gas increases. Meanwhile, when the pH is higher than 14, the re-dissolution of RuO2 is likely to be suppressed, and generation of RuO2 particles becomes problematic. Therefore, in order to fully develop the inhibitory power on RuO4 gas generation, the pH of the inhibitor is preferably 8 or more and 14 or less, and more preferably 12 or more and 13 or less. In this pH range, dissolved ruthenium exists as anions, such as RuO4− or RuO42−, and therefore it can easily form ion pairs together with onium ions contained in the inhibitor, to inhibit effectively RuO4 gas generation.
Other additives conventionally used in a treatment liquid for semiconductors can be optionally added in the inhibitor for RuO4 gas generation of the present invention to the extent that the purpose of the invention is not impaired. For example, an acid, a metal corrosion inhibitor, a water-soluble organic solvent, a fluorine compound, an oxidizing agent, a reducing agent, a complexing agent, a chelating agent, a surfactant, a defoaming agent, a pH adjuster, and a stabilizer can be added as other additives. These additives can be added singly, or in combination of two or more kinds thereof.
The inhibitor for RuO4 gas generation of the present invention may contain alkali metal ions, alkaline earth metal ions, or the like derived from the aforedescribed additives, or due to circumstances during a manufacturing process of the inhibitor for RuO4 gas generation. For example, sodium ions, potassium ions, or calcium ions may be contained. However, since these alkali metal ions, alkaline earth metal ions, etc. are harmful to a semiconductor element (adverse effects such as reduction of the yield rate of a semiconductor wafer, etc.), if they remain on a semiconductor wafer, their amount should preferably be small, and practically they should substantially not be contained. Therefore, for example, as the pH adjuster, an organic alkali such as ammonia, amine, choline, or tetraalkylammonium hydroxide, is preferable, rather than an alkali metal hydroxide such as sodium hydroxide, or an alkaline earth metal hydroxide.
Specifically, the total amount of alkali metal ions and alkaline earth metal ions is preferably 1 mass % or less, more preferably 0.7 mass % or less, further preferably 0.3 mass % or less, especially preferably 10 ppm or less, and most preferably 500 ppb or less.
In the inhibitor for RuO4 gas generation of the present invention, the remaining component except the onium salt and other additives is water. The water contained in the inhibitor is preferably water which is made free from metal ions, organic impurities, and particles by any one of distillation, ion exchange, filtration, and various kinds of adsorption treatments, and the water is particularly preferably pure water or ultrapure water. Such water can be obtained by a known method widely utilized for semiconductor production.
The method for inhibiting RuO4 gas generation is a method comprising a step of adding an inhibitor for RuO4 gas generation of the present invention to a ruthenium treatment liquid. Specifically, the RuO4 gas generation can be inhibited by adding an inhibitor for RuO4 gas generation of the present invention to a ruthenium treatment liquid used in the etching step, residue removal step, washing step, CMP step, etc. in a semiconductor manufacturing process. In addition, the RuO4 gas generation can be inhibited by using the inhibitor for RuO4 gas generation of the present invention, when ruthenium adhered to chamber inner walls, piping, etc. of each device used in the semiconductor manufacturing process is cleaned off. For example, on the occasion of a maintenance of equipment that forms Ru using physical vapor deposition (PVD), chemical vapor deposition (CVD), atomic layer deposition (ALD), or the like, it becomes possible to inhibit RuO4 gas generation during cleaning by adding the inhibitor for RuO4 gas generation to a cleaning liquid used at the time of removing Ru adhered to chambers, pipes, or the like. According to this method, the RuO4 gas generation can be inhibited by the mechanism described above.
For example, when the inhibitor for RuO4 gas generation of the present invention is used in a ruthenium wiring formation step, the procedure is as follows. First, a substrate made of a semiconductor (e.g. Si) is prepared. The prepared substrate is subjected to an oxidation treatment to form a silicon oxide film on the substrate. Then, an interlayer insulating film constituted with a low-dielectric-constant (low-k) film is formed and via holes are formed at predetermined intervals. After the formation of the via holes, they are filled with ruthenium by thermal CVD, and a ruthenium film is further deposited thereon. The ruthenium film is etched by a ruthenium treatment liquid to which the inhibitor for RuO4 gas generation has been added, and is thereby planarized while RuO4 gas generation is inhibited. This makes it possible to form highly reliable ruthenium wiring in which generation of RuO2 particles is inhibited. Additionally, the ruthenium treatment liquid to which the inhibitor for RuO4 gas generation has been added can be used also to remove ruthenium adhered to the bevels of a semiconductor wafer.
The inhibitor for RuO4 gas generation can inhibit RuO4 gas generation not only in a ruthenium treatment liquid but also in a liquid after treating ruthenium (hereinafter referred to as ruthenium-containing liquid). In this regard, the ruthenium-containing liquid means a liquid that contains even a small amount of ruthenium. There is no particular restriction on the ruthenium contained in the ruthenium-containing liquid, insofar as it includes a ruthenium element without limitation to a ruthenium metal. Examples thereof include Ru, RuO4−, RuO42−, RuO4, RuO2, and a ruthenium complex. Examples of a ruthenium-containing liquid include a waste liquid effluent from a semiconductor manufacturing process, or chamber cleaning as described above, and a treatment liquid having captured a RuO4 gas in an exhaust gas treatment equipment (scrubber). When even a small amount of ruthenium is contained in a ruthenium-containing liquid, RuO2 particles are formed via a RuO4 gas, and they pollute a tank or piping, or accelerate deterioration of equipment due to the oxidizing effect of the particles. Further, a RuO4 gas generated from ruthenium-containing liquid is strongly toxic to the human body even at a low concentration. Since a ruthenium-containing liquid has various adverse effects on the equipment and the human body as described above, it is necessary to treat it safely and rapidly while inhibiting the RuO4 gas generation. When the inhibitor for RuO4 gas generation of the present invention is added to a ruthenium-containing liquid, not only the RuO4 gas generation can be inhibited, and the ruthenium-containing liquid is treated safely, but also the contamination or deterioration of a tank or piping of the equipment can be reduced.
When the inhibitor for RuO4 gas generation of the present invention is mixed with a ruthenium treatment liquid or a ruthenium-containing liquid, the concentration of onium salts contained in the inhibitor for RuO4 gas generation of the present invention is preferably so adjusted that the concentration of at least one onium salt in the liquid after mixing falls with a range from 0.0001 to 50 mass %.
The addition amount of an inhibitor for RuO4 gas generation of the present invention to a ruthenium treatment liquid or a ruthenium-containing liquid can be determined considering the amount of ruthenium present in the liquid. Although there is no particular restriction on the addition amount of the inhibitor for RuO4 gas generation of the present invention, it is preferably from 10 to 500,000 in terms of weight ratio with respect to the amount of the ruthenium present in a ruthenium treatment liquid or a ruthenium-containing liquid set at 1, more preferably from 100 to 100,000, and further preferably from 1000 to 50,000.
The pH at 25° C. of the liquid mixture of an inhibitor for RuO4 gas generation and a ruthenium treatment liquid or a ruthenium-containing liquid is preferably for example, 7 or more and 14 or less. In order to adjust the pH of the liquid mixture, the pH adjuster illustrated above can be added.
The present invention will be described below more specifically with reference to Examples, but the present invention is not limited to these Examples.
First, sodium hypochlorite (NaClO; produced by Wako Pure Chemical Industries, Ltd.) and ultrapure water were added in a 100 mL fluorine resin-made container, and then the pH was adjusted to the pH described in Table 1 using a 15 mass % aqueous solution of HCl, or a 1.0 mol/L aqueous solution of NaOH to yield 30 mL of a ruthenium treatment liquid. Next, an onium salt and ultrapure water were charged in a 100 mL fluorine resin-made container, and the pH was adjusted to the pH described in Table 1 similarly as described above to yield 30 mL of an inhibitor for RuO4 gas generation. The onium salt in Example 21 was prepared by mixing sodium bromate and an aqueous solution of tetrapropylammonium hydroxide. The obtained ruthenium treatment liquid and inhibitor for RuO4 gas generation were mixed together to yield 60 mL of a liquid mixture. Meanwhile, in Comparative Examples 1 to 4, 30 mL of ultrapure water adjusted to the same pH as the ruthenium treatment liquid was mixed in place of the inhibitor for RuO4 gas generation. With respect to the ruthenium treatment liquid, to which sodium hypochlorite was added, it was confirmed that the oxidizing agent concentration was 0.56 mol/L (4.0 mass % as the effective chlorine concentration).
The pH of 10 mL of the liquid mixture prepared in each of Examples and Comparative Examples was measured using a tabletop pH meter (LAQUA F-73; manufactured by Horiba, Ltd.). The pH was measured after each liquid mixture was prepared and stabilized at 25° C.
The generation amount of RuO4 gas was measured by ICP-OES. Into an airtight container, 5 mL of the liquid mixture was placed, and one piece of Si wafer with a size of 10 mm×20 mm, on which a ruthenium film having a thickness of 1200 Å was formed, was immersed in the liquid at 25° C. or 50° C. until all ruthenium was dissolved. The temperatures of the liquid mixture (treatment temperature) during the immersion is shown in Table 1 or Table 2. Then, an air flow was passed through the airtight container, and the gas phase in the airtight container was bubbled into the absorbing liquid (1 mol/L NaOH) in a container to cause the RuO4 gas generated during the immersion of the wafer to be trapped in the absorbing liquid. The amount of ruthenium in this absorbing liquid was measured by ICP-OES to determine the amount of Ru in the generated RuO4 gas. The amount of Ru in the RuO4 gas in Table 1 is a value obtained by dividing the weight of ruthenium contained in the absorbing liquid by the area of the immersed wafer. Whether all ruthenium on the Si wafer immersed in the liquid mixture was dissolved was verified by using a four-probe resistivity meter (Loresta-GP; manufactured by Mitsubishi Chemical Analytech Co., Ltd.) to measure the sheet resistances before and after immersion, which were converted to film thicknesses.
A liquid mixture was prepared in the same manner as in Example 1 or Comparative Example 1, except that a 0.07 mol/L orthoperiodic acid (H5IO6; (produced by Fujifilm Wako Pure Chemical Corporation) was used as the oxidizing agent. Using this liquid mixture, the pH measurement and quantitative evaluation of a RuO4 gas were carried out similarly as in Example 1.
A liquid mixture was prepared in the same manner as in Example 4, except that a 0.002, 0.02, 0.2, 0.4, or 0.6 mol/L sodium hypobromite (NaBrO; produced by Kanto Chemical Co., Ltd.) was used as the oxidizing agent. The concentration of sodium hypobromite in the liquid mixture was checked using an ultraviolet and visible spectrophotometer (UV-2600, manufactured by Shimadzu Corporation). Using this liquid mixture, the pH measurement and quantitative evaluation of a RuO4 gas were carried out similarly as in Example 1.
A liquid mixture was prepared in the same manner as in Example 4, except that an inhibitor for RuO4 gas generation further comprising a 0.56 mol/L sodium hypochlorite was used. Using this liquid mixture, the pH measurement and quantitative evaluation of a RuO4 gas were carried out similarly as in Example 1.
Sodium hypochlorite (produced by Wako Pure Chemical Industries, Ltd.) and ultrapure water were added in a 100 mL fluorine resin-made container to yield 30 mL of a ruthenium treatment liquid. The pH of the ruthenium treatment liquid was adjusted to the same value as the pH of the ruthenium-containing liquid set forth in Table 2 using a 15 mass % aqueous solution of HCl or a 1.0 mol/Laqueous solution of NaOH. Six pieces of Si wafers with a size of 10 mm×20 mm, on which a 2400 Å thick ruthenium film was deposited were immersed in 30 mL of the obtained treatment liquid at 25° C. until the entire ruthenium was dissolved to obtain the ruthenium-containing liquid described in Table 2. The concentration of ruthenium in the ruthenium-containing liquid measured by ICP-OES is shown in Table 2.
Next, an onium salt and ultrapure water were added in a 100 mL fluorine resin-made container, and the pH was adjusted to the pH as described in Table 2 to yield 30 mL of an inhibitor for RuO4 gas generation. The onium salt in Example 50 was prepared by mixing sodium bromate and an aqueous solution of tetrapropylammonium hydroxide.
With respect to the obtained liquid (liquid mixture) in which a ruthenium-containing liquid and an inhibitor for RuO4 gas generation were mixed together, the pH of the liquid mixture was measured by the method described in Example 1, and then the quantitative evaluation of a RuO4 gas generated from the liquid mixture was performed. The temperature of the liquid mixture during wafer immersion (processing temperature) is shown in Table 2. However, since the liquid mixture already contained ruthenium, dissolution of ruthenium was not performed in the quantitative evaluation of the RuO4 gas.
A liquid mixture was prepared in the same manner as in Example 30, except that a 0.035 mol/L orthoperiodic acid (produced by Fujifilm Wako Pure Chemical Corporation) was used as the oxidizing agent. Using this liquid mixture, the quantitative evaluation of RuO4 gas was carried out similarly as in Example 30.
A liquid mixture was prepared in the same manner as in Example 33, except that a 0.001, 0.01, 0.1, 0.2, or 0.3 mol/L sodium hypobromite was used as the oxidizing agent. The concentration of sodium hypobromite in the liquid mixture was checked using an ultraviolet and visible spectrophotometer (UV-2600, manufactured by Shimadzu Corporation). Using this liquid mixture, the quantitative evaluation of a RuO4 gas was carried out similarly as in Example 30.
Into a 1.5 L fluorine resin-made container, 0.42 g of tetrapropylammonium perruthenate and ultrapure water were added, and the pH was adjusted to the pH described in Table 2 using a 15 mass % aqueous solution of HCl, or a 1.0 mol/L aqueous solution of NaOH to yield 1 L of a ruthenium-containing liquid.
Next, an onium salt and ultrapure water were added in a 100-mL fluorine resin-made container, and the pH was adjusted to the value described in Table 2 to yield 30 mL of an inhibitor for RuO4 gas generation.
With respect to a liquid prepared by mixing 30 mL of the obtained ruthenium-containing liquid, and 30 mL of the obtained inhibitor for RuO4 gas generation, the quantitative evaluation of a RuO4 gas was carried out at 25° C. similarly as in Example 30.
A liquid in which 4.8 mg of RuO2 powder was dispersed in 30 mL of ultrapure water was used as the ruthenium-containing liquid. The pH of the ruthenium-containing liquid was adjusted to pH 12.0 using a 15 mass % aqueous solution of HCl, or a 1.0 mol/L aqueous solution of NaOH. Next, the onium salt described in Table 2 and ultrapure water were added into a 100-mL fluorine resin-made container, and thereafter the pH was adjusted to the pH described in Table 2 to yield 30 mL of an inhibitor for RuO4 gas generation. The quantitative evaluation of a RuO4 gas was performed similarly as in Example 30 using a liquid mixture obtained by mixing the obtained ruthenium-containing liquid and inhibitor for RuO4 gas generation.
To ultrapure water 1.9 mg of a Ru powder and 2.4 mg of a RuO2 powder were added, and the pH was adjusted to the value set forth in Table 2 using a 15 mass % aqueous solution of HCl, or a 1.0 mol/L aqueous solution of NaOH to yield 30 mL of a ruthenium-containing liquid containing 6.0×10−4 mol/L of Ru and 6.0×10−4 mol/L of RuO2.
Next, an onium salt and ultrapure water were added in a 100-mL fluorine resin-made container, and the pH was adjusted to the value described in Table 2 to yield 30 mL of an inhibitor for RuO4 gas generation.
With respect to a liquid (liquid mixture) prepared by mixing at 25° C. 30 mL of the obtained ruthenium-containing liquid, and 30 mL of the obtained inhibitor for RuO4 gas generation, the quantitative evaluation of a RuO4 gas was carried out similarly as in Example 30.
Sodium hypochlorite (produced by Wako Pure Chemical Industries, Ltd.) and ultrapure water were added in a 100 mL fluorine resin-made container, and the pH was adjusted to the value set forth in Table 2 using a 15 mass % aqueous solution of HCl, or a 1.0 mol/L aqueous solution of NaOH. By adding 1.9 mg of a Ru pow der and 2.4 mg of a RuO2 powder to the obtained ruthenium treatment liquid, 30 mL of a ruthenium-containing liquid containing 6.0×10−4 mol/L of Ru and 6.0×10−4 mol/L of RuO2 was obtained.
Next, an onium salt and ultrapure water were added in a 100 mL fluorine resin-made container, and the pH was adjusted to the pH described in Table 2 to yield 30 mL of an inhibitor for RuO4 gas generation.
With respect to the liquid in which 30 mL of the obtained ruthenium-containing liquid and 30 mL of the obtained inhibitor for RuO4 gas generation were mixed, the quantitative evaluation of a RuO4 gas was carried out at 25° C. similarly as in Example 30.
Sodium hypochlorite (produced by Wako Pure Chemical Industries, Ltd.) or orthoperiodic acid (produced by Fujifilm Corporation Wako Pure Chemical Industries, Ltd.), and ultrapure water were added in a 100 mL fluorine resin-made container, and the pH was adjusted to the pH described in Table 2 using a 15 mass % aqueous solution of HCl or a 1.0 mol/L aqueous solution of NaOH to yield 30 mL of a ruthenium treatment liquid. Six pieces of Si wafers with a size of 10 mm×20 mm, on which a 2400 Å thick ruthenium film was deposited were immersed in 30 mL of the obtained ruthenium treatment liquid at 25° C. until the entire ruthenium was dissolved to obtain the ruthenium-containing liquid described in Table 2. In the case of the ruthenium-containing liquid to which sodium hypochlorite was added, it was confirmed that the concentration thereof was 0.28 mol/L (2.0 mass % as the effective chlorine concentration). To the obtained ruthenium-containing liquid, 30 mL of ultrapure water adjusted to the same pH was mixed, and the quantitative evaluation of a RuO4 gas was carried out similarly as in Example 30.
Comparing Example 1 with Comparative Example 1 (pH 8.0), Example 4 with Comparative Example 2 (pH 12.0), and Example 5 with Comparative Example 3 (pH 12.5) respectively, it can be known that the addition of an onium salt can inhibit RuO4 gas generation at all pH levels. In Examples 1 to 3, the addition amount of the onium salt was varied, and it was confirmed that the higher addition amount of the onium salt enhances the inhibitory effect on a RuO4 gas.
In Examples 8 to 21, onium salts as expressed in the above Formulas (1) to (4) and different from the kinds used in Examples 1 to 7 were used, and in all cases, an inhibitory effect on RuO4 gas generation was obtained. The concentration of the onium salt in Example 4 was 10 mass %, while in Example 9 it was 0.2 mass %, indicating that in Example 9 in which the carbon number of the onium salt is larger, a comparable inhibitory effect on RuO4 gas generation can be obtained with a smaller addition amount.
Comparing Comparative Example 4 with Example 22, it can be seen that the addition of an onium salt inhibits RuO4 gas generation also at 50° C.
Comparing Comparative Example 2 with Examples 24 to 28, it can be seen that the addition of an onium salt inhibits RuO4 gas generation, even when NaBrO is used as the oxidizing agent at from 0.002 to 0.6 mol/L.
Comparing Comparative Example 5 with Example 23, it can be seen that the addition of an onium salt inhibits RuO4 gas generation, even when orthoperiodic acid is used as the oxidizing agent at 0.07 mol/L.
From the results shown in Table 2, it can be seen that generation of a ruthenium-containing gas is inhibited, when an inhibitor for RuO4 gas generation containing any of the onium salts expressed by Formulas (1) to (4) is added to a ruthenium-containing liquid. This demonstrates that the inhibitor for RuO4 gas generation of the present invention can be used suitably for the treatment of a ruthenium-containing liquid.
| Number | Date | Country | Kind |
|---|---|---|---|
| 2019-176727 | Sep 2019 | JP | national |
| 2019-193081 | Oct 2019 | JP | national |
| 2019-211875 | Nov 2019 | JP | national |
| 2020-045869 | Mar 2020 | JP | national |
| 2020-117652 | Jul 2020 | JP | national |
| Filing Document | Filing Date | Country | Kind |
|---|---|---|---|
| PCT/JP2020/035677 | 9/23/2020 | WO |
| Publishing Document | Publishing Date | Country | Kind |
|---|---|---|---|
| WO2021/060234 | 4/1/2021 | WO | A |
| Number | Name | Date | Kind |
|---|---|---|---|
| 6161195 | Konishi et al. | Dec 2000 | A |
| 10361092 | Roberts et al. | Jul 2019 | B1 |
| 20020060202 | Fukunaga et al. | May 2002 | A1 |
| 20030017419 | Futase et al. | Jan 2003 | A1 |
| 20050092351 | Saito et al. | May 2005 | A1 |
| 20090120458 | Hao | May 2009 | A1 |
| 20120256122 | Sato et al. | Oct 2012 | A1 |
| 20140076355 | Hirabayashi et al. | Mar 2014 | A1 |
| 20160130500 | Chen et al. | May 2016 | A1 |
| 20170222138 | Park et al. | Aug 2017 | A1 |
| 20200354632 | Sugimura et al. | Nov 2020 | A1 |
| Number | Date | Country |
|---|---|---|
| 3 726 565 | Oct 2020 | EP |
| 5-314019 | Nov 1993 | JP |
| 2002-161381 | Jun 2002 | JP |
| 2008-42014 | Feb 2008 | JP |
| 2011-503326 | Jan 2011 | JP |
| 2014-62297 | Apr 2014 | JP |
| 201504397 | Feb 2015 | TW |
| 2011074601 | Jun 2011 | WO |
| 2016068183 | May 2016 | WO |
| 2019142788 | Jul 2019 | WO |
| 2019150990 | Aug 2019 | WO |
| 2019151144 | Aug 2019 | WO |
| 2019151145 | Aug 2019 | WO |
| Entry |
|---|
| Barak et al. (J. Org. Chem., 1989, 54(14), 3484). (Year: 1989). |
| International Search Report (ISR) dated Nov. 17, 2000 in International (PCT) Application PCT/JP2020/035677. |
| International Search Report (ISR) dated Nov. 17, 2020 in International (PCT) Application PCT/JP2020/035677. |
| International Search Report dated Oct. 13, 2020 in International (PCT) Patent Application No. PCT/JP2020/026635, with category indication (“Y”) of cited references. |
| Office Action dated Aug. 17, 2022, in U.S. Appl. No. 17/261,387. |
| Office Action dated Aug. 1, 2023 in Singapore Patent Application No. 11202203094Y. |
| Number | Date | Country | |
|---|---|---|---|
| 20210340095 A1 | Nov 2021 | US |