Patent Application
20130161312
This invention relates to methods and systems for processing thin films, and more particularly to forming crystalline semiconductor thin films from amorphous or polycrystalline thin films using laser irradiation. In particular the present invention relates to a method and system for the production of integrated thin film transistors.
In recent years, various techniques for crystallizing or improving the crystallinity of an amorphous or polycrystalline semiconductor film have been investigated. This technology is used in the manufacture of a variety of devices, such as image sensors and active-matrix liquid-crystal display (AMLCD) devices. In the latter, a regular array of thin-film transistors (TFT) is fabricated on an appropriate transparent substrate, and each transistor serves as a pixel controller.
Semiconductor films are processed using excimer laser annealing (ELA), in which a region of the film is irradiated by an excimer laser to partially melt the film and then is crystallized. The process typically uses a long, narrow beam shape that is continuously advanced over the substrate surface, so that the beam can potentially irradiate the entire semiconductor thin film in a single scan across the surface ELA produces homogeneous small grained polycrystalline films; however, the method often suffers from microstructural non-uniformities which can be caused by pulse to pulse energy density fluctuations and/or non-uniform beam intensity profiles.
Sequential lateral solidification (SLS) using an excimer laser is one method that has been used to form high quality polycrystalline films having large and uniform grains. SLS produces large grains and controls the location of grain boundaries. A large-grained polycrystalline film can exhibit enhanced switching characteristics because the number of grain boundaries in the direction of electron flow is reduced. SLS systems and processes are described in U.S. Pat. Nos. 6,322,625, 6,368,945, and 6,555,449 issued to Dr. James Im, and U.S. patent application Ser. No. 09/390,537, the entire disclosures of which are incorporated herein by reference, and which are assigned to the common assignee of the present application.
In an SLS process, an initially amorphous (or small grain polycrystalline) film is irradiated by a very narrow laser beamlet. The beamlet is formed by passing a laser beam through a patterned mask, which is projected onto the surface of the film. The beamlet melts the amorphous film, which then recrystallizes to form one or more crystals. The crystals grow primarily inward from edges of the irradiated area. After an initial beamlet has crystallized a portion of the amorphous film, a second beamlet irradiates the film at a location less than the lateral growth length from the previous beamlet. In the newly irradiated film location, crystal grains grow laterally from the crystal seeds of the polycrystalline material formed in the previous step. As a result of this lateral growth, the crystals attain high quality along the direction of the advancing beamlet. The elongated crystal grains are separated by grain boundaries that run approximately parallel to the long grain axes, which are generally perpendicular to the length of the narrow beamlet. See
When polycrystalline material is used to fabricate electronic devices, the total resistance to carrier transport is affected by the combination of barriers that a carrier has to cross as it travels under the influence of a given potential. Due to the additional number of grain boundaries that are crossed when the carrier travels in a direction perpendicular to the long grain axes of the polycrystalline material or when a carrier travels across a large number of small grains, the carrier will experience higher resistance as compared to the carrier traveling parallel to long grain axes. Therefore, the performance of devices such as TFTs fabricated on polycrystalline films will depend upon both the crystalline quality and crystalline orientation of the TFT channel relative to the long grain axes.
Devices that use a polycrystalline thin film often do not require that the entire thin film have the same system performance and/or mobility orientation. For example, the mobility requirements for the TFT column and row drivers (the integration regions) are considerably greater than for the pixel controllers or pixel regions. Processing the entire film surface, e.g., the integration regions and the pixel regions, under the conditions necessary to meet the high mobility requirements of the integration regions can be inefficient and uneconomical since excess irradiation and processing time of the lower performance regions of the thin film may have been expended with no gain in system performance.
The present invention recognizes that films of different thicknesses have different film properties. In particular, it is observed that for similarly processed films a thicker film exhibits a higher carrier mobility than a thinner film. This is observed for all directional solidification processes, such as CW-laser scanning, sequential laser solidification and zone melt refinement, and is true for films that have been processed, for example, using an excimer laser, a solid-state laser or a continuous wave laser as the laser source.
The present invention provides a crystalline film containing a first crystalline region having a first film thickness that is processed in a crystallization process to provide a first crystalline grain structure. The film further contains a second crystalline region having a second film thickness that is processed in a crystallization process to provide a second crystalline grain structure. The first and second film thicknesses are different and are selected to provide crystalline regions having selected degrees and orientations of crystallization. Typically, the region of greater thickness can contain the longer grains in the direction of crystal growth. Thicker films also often possess wider grains. The film is suitable for use, for example, in an integrated circuit device or as an active channel in a thin film transistor (TFT). The film may be a semiconductor material or a metal.
In one aspect of the invention, a method for processing a film includes (a) generating a first laser beam pattern from a pulsed laser beam, the laser beam pattern having an intensity that is sufficient to at least partially melt at least a portion of a first region of a film to be crystallized; (b) generating a second laser beam pattern from a pulsed laser beam, the second laser beam pattern having an intensity that is sufficient to at least partially melt at least a portion of a second region of the film to be crystallized, wherein the first region of the film comprises a first thickness and the second region of the film comprises a second thickness, and the first and second thicknesses are different; (c) irradiating the first region of the film with the first set of patterned beamlets to form a first crystalline region having a first grain structure; and (d) irradiating the second region of the film with the second set of patterned beamlets to form a second crystalline region having a second grain structure. The laser beam pattern includes a “set” of patterned beamlets, and the set of patterned beamlets includes one or more laser beamlets.
In one or more embodiments, the method further includes after step (c), repositioning the first laser beam pattern on the film to illuminate a second portion of the first region of the film, and irradiating the first region of the film as in step (c), the steps of repositioning and irradiating occurring at least once; and after step (d), repositioning the second laser beam pattern on the film to illuminate a second portion of the second region of the film, and irradiating the second region of the film as in step (d), the steps of repositioning and irradiating occurring at least once.
In one or more embodiments, the irradiation conditions are selected from those suitable for sequential laser solidification (SLS), excimer laser annealing (ELA) and uniform grain structure (UGS) crystallization. A plurality of laser beam sources can be used to generate a plurality of laser beam patterns. The plurality of laser beam sources can be used to irradiate the same or different regions of the film.
Various objects, features, and advantages of the present invention can be more fully appreciated with reference to the following detailed description of the invention when considered in connection with the following drawing, in which like reference numerals identify like elements. The following drawings are for the purpose of illustration only and are not intended to be limiting of the invention, the scope of which is set forth in the claims that follow.
The quality of a film that has been crystallized using a laser-induced crystallization growth technique depends, in part, on the thickness of the processed film. This observation is used to crystallize different regions of the film in an energy- and time-efficient manner and to provide a desired film characteristic. Laser-induced crystallization is typically accomplished by laser irradiation using a wavelength of energy that can be absorbed by the film. The laser source may be any conventional laser source, including but not limited to, excimer laser, continuous wave laser and solid-state laser. The irradiation beam pulse can be generated by other known sources for short energy pulses suitable for melting a semiconductor or metallic material. Such known sources can be a pulsed solid state laser, a chopped continuous wave laser, a pulsed electron beam and a pulsed ion beam, and the like.
Films of different thicknesses, although similarly processed, have different film properties. Thick films generally exhibit a higher electron mobility than similarly processed thin films. “Thick” and “thin” are used here in the relative sense, in that any film that is thicker relative to a second comparative film will exhibit improved film properties. A film can be situated on a substrate and can have one or more intermediate layers there between. The film can have a thickness between 100 Å and 10,000 Å so long as at least certain areas thereof can be completely or partially melted throughout their entire thickness. While the invention pertains to all films of all thicknesses susceptible to laser-induced crystallization, “thick” films typically can range from about 500 Å (50 nm) to about 10,000 Å (1 μm), and more typically from about 500 Å (50 nm) to about 5000 Å (500 nm); and “thin” films typically can range from about 100 Å (10 nm) to about 2000 Å (200 nm) and more typically about 200-500 Å (20-50 nm).
In one or more embodiments, the thin film may be a metal or semiconductor film. Exemplary metals include aluminum, copper, nickel, and molybdenum. Exemplary semiconductor films include conventional semiconductor materials, such as silicon, germanium, and silicon-germanium. It is also possible to use other elements or semiconductor materials for the semiconductor thin film. An intermediate layer situated beneath the semiconductor film can be made of silicon oxide, silicon nitride and/or mixtures of oxide, nitride or other materials that are suitable for use as a thermal insulator to protect the substrate from heat or as a diffusion barrier to prevent diffusion of impurities from the substrate to the film.
Although thick films demonstrate higher mobilities, it is more costly and time intensive to process them. For example, higher energy densities may be required in order to entirely melt through the thickness of the film. Since higher energy density is typically achieved by concentrating the laser beam into a smaller beam shape (cross-sectional area), smaller sections of the film surface can be processed at a time, so that sample throughput is reduced.
Thus according to one or more embodiments of the present invention, a semiconductor film to be crystallized having regions of different heights (film thicknesses) is provided. In those regions of the films where high electron mobility is required for optimal device function, the semiconductor film layer is “thick.” In those regions of the film where lower electron mobility is adequate for device performance, a “thin” film is deposited. Thus, thick films are located only in those regions of the substrate requiring high speed or mobility, and the thick film regions are processed using a slower, more energy intensive crystallization process. The remaining surface (which is typically the bulk of the surface) is a thin film that is processed more rapidly using a low cost, low energy crystallization process.
Improvements in crystal properties typically are observed regardless of the specific crystallization process employed. The films can be laterally or transversely crystallized, or the films can crystallize using spontaneous nucleation. By “lateral crystal growth” or “lateral crystallization,” as those terms are used herein, it is meant a growth technique in which a region of a film is melted to the film/surface interface and in which recrystallization occurs in a crystallization front moving laterally across the substrate surface. By “transverse crystal growth” or “transverse crystallization,” as those terms are used herein, it is meant a growth technique in which a region of film is partially melted, e.g., not through its entire thickness, and in which recrystallization occurs in a crystallization front moving through the film thickness, e.g., from the film surface towards the center of the film in a direction transverse to that of the above-described lateral crystallization. In spontaneous nucleation, crystal growth is statistically distributed over the melted regions and each nucleus grows until it meets other growing crystals. Exemplary crystallization techniques include excimer laser anneal (ELA), sequential lateral solidification (SLS), and uniform grain structure (UGS) crystallization.
Referring to
Referring to
The stage 270 is a precision x-y stage that can accurately position the substrate 260 under the beam 240. The stage 270 can also be capable of motion along the z-axis, enabling it to move up and down to assist in focusing or defocusing the image of the mask 280 produced by the laser beam 240 at the location 265. In another embodiment of the method of the present invention, it is preferable for the stage 270 to also be able to rotate.
In uniform grain structure (UGS) crystallization, a film of uniform crystalline structure is obtained by masking a laser beam so that non-uniform edge regions of the laser beam do not irradiate the film. The mask can be relatively large, for example, it can be 1 cm×0.5 cm; however, it should be smaller than the laser beam size, so that edge irregularities in the laser beam are blocked. The laser beam provides sufficient energy to partially or completely melt the irradiated regions of the thin film. UGS crystallization provides a film having an edge region and a central region of uniform fine-grained polycrystals of different sizes. In the case where the laser irradiation energy is above the threshold for complete melting, the edge regions exhibit large, laterally grown crystals. In the case where the laser irradiation energy is below the threshold for complete melting, grain size will rapidly decrease from the edges of the irradiated region. For further detail, see U.S. application Ser. No. 60/405,084, filed Aug. 19, 2002 and entitled “Process and System for Laser Crystallization Processing of Semiconductor Film Regions on a Substrate to Minimize Edge Areas, and Structure of Such Semiconductor Film Regions,” which is hereby incorporated by reference.
Sequential lateral solidification is a particularly useful lateral crystallization technique because it is capable of grain boundary location-controlled crystallization and provides crystal grain of exceptionally large size. Sequential lateral solidification produces large grained semiconductor, e.g., silicon, structures through small-scale translations between sequential pulses emitted by an excimer laser. The invention is described with specific reference to sequential lateral solidification of an amorphous silicon film; however, it is understood that the benefits of present invention can be readily obtained using other lateral crystallization techniques or other film materials.
An amorphous silicon thin film sample is processed into a single or polycrystalline silicon thin film by generating a plurality of excimer laser pulses of a predetermined fluence, controllably modulating the fluence of the excimer laser pulses, homogenizing the modulated laser pulses, masking portions of the homogenized modulated laser pulses to obtain a laser beam pattern, irradiating an amorphous silicon thin film sample with the laser beam pattern to effect melting of portions thereof irradiated by the beamlets, and controllably translating the sample with respect to the laser beam pattern (or vice versa) to thereby process the amorphous silicon thin film sample into a single crystal or grain boundary-controlled polycrystalline silicon thin film. In one or more embodiments of the sequential lateral solidification process, highly elongated crystal grains that are separated by grain boundaries that run approximately parallel to the long grain axes are produced. The method is illustrated with reference to
The many microtranslations called for by the sequential lateral solidification process increase processing time; however, they produce a film having highly elongated, low defect grains. In one or more embodiments, this process is used to process the thick regions of the semiconductor film. The polycrystalline grains obtained using this process are typically of high mobility, e.g., 300-400 cm2/V-s. This is the value typically found for devices with having parallel grain boundaries but few perpendicular grain boundaries. These highly elongated grains are well suited for the active channel regions in integration TFTs.
According to the above-described method of sequential lateral solidification, the entire film is crystallized using multiple pulses. This method is hereinafter referred to as an “n-shot” process, alluding to the fact that a variable, or “n”, number of laser pulses (“shots”) is required for complete crystallization. Further detail of the n-shot process is found in U.S. Pat. No. 6,322,625, entitled “Crystallization Processing of Semiconductor Film Regions on a Substrate and Devices Made Therewith,” and in U.S. Pat. No. 6,368,945, entitled “System for Providing a Continuous Motion Sequential Lateral Solidification,” both of which are incorporated in their entireties by reference.
In one or more embodiments, regions of the semiconductor film are processed using a sequential lateral solidification process that produces smaller crystal grains than those of the preceding “n-shot” method. The film regions are therefore of lower electron mobility; however the film is processed rapidly and with a minimum number of passes over the film substrate, thereby making it a cost-efficient processing technique. These crystallized regions are well suited for the thin film regions of the semiconductor thin film used as the active channel in pixel control TFTs.
The process uses a mask such as that shown in
The sample is then translated a distance approaching, but more than, half the width of the mask feature, and the film is irradiated with a second excimer laser pulse. For example, in one embodiment, the sample (or mask) is translated a distance equal to ½ (mask feature width 360+mask spacing 340). The second irradiation melts the remaining amorphous regions 742 spanning the recently crystallized regions 740 to form melt regions 751, 752 and 753. The initial crystal seed region 743 melts and serves as a site for lateral crystal growth. As shown in
According to the above-described method of sequential lateral solidification, the entire mask area is crystallized using only two laser pulses. This method is hereinafter referred to as a “two-shot” process, alluding to the fact that only two laser pulses (“shots”) are required for complete crystallization. Further detail of the two-shot process is found in Published International Application No. WO 01/18854, entitled “Methods for Producing Uniform Large-Grained and Grain Boundary Location Manipulated Polycrystalline Thin Film Semiconductors Using Sequential Lateral Solidification,” which is incorporated in its entirety by reference.
According to one or more embodiments of the present invention, a method for producing an article having thick film regions of high mobility and thin film regions of low mobility is provided. An exemplary process set forth in the flow diagram 800 of
In step 810 a thin film having at least two thicknesses is deposited on a substrate, with each film thickness intended to provide crystalline regions having different film properties. In one or more embodiments, the film property of interest is mobility; however other film properties such as crystal orientation, crystal size, and grain defects can also be considered. Of course, the film can have more than two film thickness regions to thereby provide more than two different film properties. The size and placement of devices on the film is selected to correspond to the different film thickness regions. For example, pixel control devices are located in regions of thinner film thickness and integration devices are located in regions of thicker film thickness.
The fabrication of films of different thicknesses is known in the art. For example, a film can be deposited evenly across the substrate, and thereafter sections thereof are removed, e.g., etched or polished, to form regions of thicker and thinner film thicknesses. In some exemplary embodiments, the film is etched back to expose the underlying substrate, and a second layer of semiconductor material is deposited over the exposed substrate and existing semiconductor layer to form a film of different thicknesses. Alternatively, the film is etched so as to remove some, but not all, of the semiconductor material in the thin film regions. In other exemplary embodiments, photolithography can be used to pattern the film surface, followed by selective deposition or material removal in the exposed regions of the patterned substrate.
In step 820 the laser beam conditions (beam shape, beam energy density, beam homogeneity, etc.) and mask design (where present) are selected for processing the thick regions of the semiconductor film. The order of irradiation is not critical to the invention and either thick or thin film regions can be processed first, or they can be processed simultaneously. As is discussed in greater detail below, one or more laser beam sources may be used to generate the laser beam pattern that irradiates the film surface. A laser beam generated from a laser beam source may be split or steered to generate secondary laser beams, each of which can be shaped using masks and/or laser optics to provide patterned beamlets with desired characteristics.
In step 830 the “thick” film region of the semiconductor film is irradiated to obtain a first crystalline region. According to one or more embodiments of the present invention, the region is irradiated in a sequential lateral solidification “n”-shot process. The first crystalline region may include the entire “thick” film region, such that the film is crystallized up to the edge of the thick film region. Edge melting may result in material flow at the interface between the thick and thin films; however, rapid recrystallization and surface tension are expected to limit material flow. Alternatively, the entire thick film region may not be irradiated, forming for example an amorphous border between the “thick” and “thin” film regions.
In step 835, it is determined whether thick film processing is complete. If not, the process returns to step 830 to process a new portion of the thick film region. If thick film region is crystallized, the step is complete, and the process advances to the next step.
In step 840 the laser beam conditions (beam shape, beam energy density, beam homogeneity, demagnification, etc.) and mask design are selected for processing the thin regions of the semiconductor film. The order of irradiation is not critical to the invention, and this step is carried out before, during or after processing of the thick film. As is the case for the thick film region, one or more laser sources can be used to generate the laser beamlets used to irradiate the thin film regions of the film. In addition, the laser beam generated from a laser beam source may be split or steered to generate secondary laser beams, each of which can be shaped using masks and/or laser optics to provide patterned beamlets with desired characteristics.
In step 850 the “thin” film region of the semiconductor film is irradiated to obtain a second crystalline region. According to one or more embodiments of the present invention, the region is irradiated in a sequential lateral solidification two-shot process. ELA and UGS crystallization can also be used to provide a crystalline region of uniform grain structure.
In step 855, it is determined whether the thin film processing is complete. If not, then the process returns to step 850 and a new portion of the thin film is irradiated. If complete, the process advances to step 860 and is done.
Variations of the process are contemplated within the scope of the present invention. For example, the crystallization method used for the first and second regions of the film can be the same or different. In one or more embodiments, the thick film regions requiring higher mobility can be processed using a technique such as SLS that produces elongated, grain boundary location-controlled grain structure, and the thin film regions can be processed using a less expensive technique, such as UGS crystallization. In one or more embodiments of the present invention, a portion of the “thick” and/or “thin” regions are processed. The remaining unprocessed portions remain in the as-deposited crystalline state, e.g., amorphous or small-grained polycrystalline. The size and location of the processed and unprocessed regions of the “thick” and/or “thin” regions may be selected, for example, to correspond to devices to be located on the film.
By way of further example, even when using the same crystallization technique, the masks for the first and second irradiations can be the same or different. When the masks are the same, then the conditions of irradiation typically may vary, as for example described above where an “n”-step and a two-step process are used for the two film thickness regions. In some embodiments, different masks are used for the first and second irradiations. For example, the orientation of the mask features can vary so that crystal growth proceeds in different directions on the film. Mask orientation can be varied by rotating the mask or the substrate stage on which the sample rests or by using different masks.
In some embodiments, the laser features, e.g., the laser beam shape and energy density, can be modified so that each region of the amorphous film is irradiated with a laser beam (i.e., a laser beam pattern) having different beam characteristics, e.g., beam energy profile (density), beam shape, beam pulse duration, etc. The beam characteristics of the laser beams being delivered to the amorphous film can be controlled and modulated via the optical elements, e.g., lenses, homogenizers, attenuators, and demagnification optics, etc., and the configuration and orientation of a mask(s), if present. By modulating the beam characteristics of the laser beams in accordance with the processing requirements (to facilitate crystallization) of the film portion to be irradiated, the laser source's output energy can be more efficiently utilized in the crystallization fabrication process, which in turn can lead to improved (i.e., shorter) film processing times and/or lower energy processing requirements. Accordingly, the laser beams can be controlled and modulated so that different regions of the film that have different processing requirements are irradiated by laser beams having different beam characteristics. For example, the “thin” portions of the amorphous film layer can be subjected to laser beams that have certain energy beam characteristics while the “thick” portions of the film layer can be subjected to laser beams that have different energy beam characteristics.
Laser beams having differing energy beam characteristics can be generated and delivered to the amorphous film using systems that have a single optical path or, alternatively, have a plurality of optical paths. An optical path, as that term is used herein, refers to the trajectory of a laser beam pulse as the laser beam pulse travels from a laser beam source to a thin film sample. Optical paths thus extend through both the illumination and projection portions of the exemplary systems. Each optical path has at least one optical element that is capable of manipulating the energy beam characteristics of a laser beam pulse that is directed along that optical path.
In systems having a single optical path, one or more of the optical elements and the mask (if present) can be adjusted, inserted or substituted, etc., within the optical path so as provide laser beamlets having different energy beam characteristics. Additionally, the orientation of the substrate, relative to the orientation of the incoming laser beams, can also be adjusted to effectively produce a laser beam that has different energy beam characteristics. In one or more embodiments, for example, the laser system can include a mask that is rotatable via a mask holder. The mask is held in a first position to facilitate the irradiation processing of a first portion of the film and then is rotated to a second position, e.g., rotate 90°, to facilitate the irradiation processing of a second portion of the film. In one or more embodiments, the laser system can include two masks having different masking shapes being located on a mask holder. To irradiate a first portion of the silicon film, the first mask is aligned with the laser beam optical path via the mask holder. To irradiate a second portion, the second mask is then aligned with the laser beam optical path via the mask holder, e.g., the mask holder can be a rotatable disk cartridge. In yet another embodiment, for example, the system can include an adjustable demagnification optical element. To generate laser beams having differing energy beam characteristics, the adjustable demagnification optical element is set to a first magnification during the irradiation of a portion of the amorphous film and then set to a different magnification during the irradiation of another portion of the amorphous film. Thus, laser beams having different energy beam characteristics can be generated and delivered to the amorphous film on the same optical path. Other modification to modify beam characteristics of a laser beam in a single optical path will be apparent to those of skill in the art.
Generating laser beam with different beam characteristics along a single optical path may cause the crystallization processing times to otherwise increase in some circumstances since the delivery of the irradiation energy to the amorphous film may need to be interrupted to facilitate the modulation of the energy beam characteristics. In this instance, a system having a single laser beam path may not be advantageous since the changing of the optical elements, the mask configuration or orientation, or the substrate orientation, etc., to facilitate an adjustment of the laser beam characteristics could dramatically lower the duty cycle of the delivered laser energy. In one or more embodiments and to generate laser beams having differing energy beam characteristics while maintaining an acceptable delivered irradiation duty cycle, the systems for irradiating the amorphous film can include a plurality of optical paths. As shown schematically in
An exemplary apparatus having dual optical paths that can generate and deliver laser beams having different energy beam characteristics to a film is shown in
At the beam steering element 950, the incoming laser beams 240 are directed along one of two different out-going optical paths, each of which leads to the substrate 260 that is mounted on the wafer-handling stage 270. The first optical path includes a mirror 960, a variable-focus field lens 970a, a mask 280a and a projection lens 295a, while the second optical path includes a variable-focus field lens 970b, a mask 280b and a projection lens 295b. The masks 280a and 280b are typically mounted to mask stages (not shown) that are capable of accurately positioning the masks (e.g., in three dimensions) in relationship to the incoming laser beams 240. Laser beams 240 traveling along the two different optical paths pass through optical elements that have different optical properties. For example, in one embodiment, the mask 280a of the first optical path has a different masking configuration than the mask 280b of the second optical path. Thus, laser beam 240a, which is directed to region 265a of substrate 260 via the first optical path, will have energy beam characteristics that are different from the energy beam characteristics of the laser beam 240b that is directed to region 265b of substrate 260 via the second optical path. Regions 265a, 265b are shown as having different film thicknesses.
In certain embodiments, the beam steering element 950 can have two modes: a transmissive or pass-through mode and a reflective or redirect mode. While operating in a pass-through mode, the laser beams 240 entering the beam steering element 950 essentially pass completely through the beam steering element 950 onto a first optical path. While operating in a redirect mode, the laser beams 240 entering the beam steering element 950 are essentially completely redirected by a reflective surface(s) onto a second optical path.
The wafer-handling stage 270 is capable of accurately positioning the substrate 260 masks (e.g., in three dimensions) in relationship to the incoming laser beams 240a and 240b. As previously discussed, the dual-thickness amorphous film is deposited in a controlled manner upon a surface of the substrate 260. Laser beam(s) 240 can then be directed to the second optical path via the beam steering element 950 so that laser beam(s) 240b having second beam characteristics are generated and directed to different portions of the film. Therefore, by coordinating (i.e., via a computer) the generation of the laser beam 240, the operations of the beam steering element 950 and the positioning of the substrate 260 via the wafer-handling stage 270, the delivery of laser beams 240a and 240b (having different beam characteristics) to different portions of the amorphous film can be facilitated.
In other exemplary embodiments, the beam steering element 950 is a beam splitter that allows a portion of the laser beam to pass through the beam splitter to pathway 240a and a portion of the laser beam to be redirected along pathway 240b so that different portions of the thin film can be irradiated at the same time.
In other exemplary embodiments, a plurality of laser sources and a plurality of optical paths, such as those described in detail above, can be employed. Each laser source generates a laser beam(s) that can be directed along a corresponding optical path so as to produce a laser beam(s) having specific beam characteristics. The laser beam(s) can then be directed via the optical path to a region of the thin film. For example, a laser beam(s) from the laser source can be directed along the first optical path so that a laser beam(s) having first beam characteristics is produced and delivered to certain portions of the film while a laser beam(s) from a second laser source can be directed along a second optical path so that a laser beam(s) having different beam characteristics is produced and delivered to certain other portions of the film. This is illustrated schematically in
In some embodiments, a plurality of laser systems, which each use a plurality of optical pathways, can be employed. In such embodiments, each laser system can be made up of one or more laser sources. In such embodiments, different laser systems can be used to process different regions of the thin film. For example, laser beams generated by the laser source(s) of a first laser system and by the laser source(s) of a second laser system can be directed along two other different optical paths so as to process a “thick” region of the thin film. The laser beam(s) generated by the laser source(s) of the first laser system can be directed to the corresponding optical paths via a beam steerer or a beam splitter depending upon whether the generated laser beam(s) are to be split or not. The laser beams(s) of the second laser system can be processed and handled similarly. The laser beams that are directed to the “thin” region may have similar or different energy beam characteristics. Similarly, the laser beams that are directed to the “thick” region may have similar or different energy beam characteristics. An exemplary embodiment having two independent laser systems 1210a and 1210b with corresponding beam splitters 1230a and 1230b is depicted in
In still other embodiments as described above, beam splitters can operate as a beam steering elements that can operate in a transmissive or pass-through mode and a reflective or redirect mode. While operating in a pass-through mode, the laser beams entering the beam steering element essentially pass completely through the beam steering element onto a first optical path. While operating in a redirect mode, the laser beams entering the beam steering element are essentially completely redirected by a reflective surface(s) onto a second optical path.
Further detail is provided in co-pending patent application entitled “Systems And Methods For Inducing Crystallization of Thin Films Using Multiple Optical Paths” filed on even date herewith, and in co-pending patent application entitled “Systems And Methods For Processing Thin Films” filed on even date, the contents of which are incorporated by reference.
The devices fabricated by the present invention include not only an element such as a TFT or a MOS transistor, but also a liquid crystal display device (TFT-LCDs), an EL (Electro Luminescence) display device, an EC (Electro Chromic) display device, active-matrix organic light emitting diodes (OLEDs), static random access memory (SRAM), three-dimensional integrated circuits (3-D ICs), sensors, printers, and light valves, or the like, each including a semiconductor circuit (microprocessor, signal processing circuit, high frequency circuit, etc.) constituted by insulated gate transistors.
Although various embodiments that incorporate the teachings of the present invention have been shown and described in detail herein, those skilled in the art can readily devise many other varied embodiments that incorporate these teachings.
This patent application is a divisional application of and claims priority under 35 U.S.C. §120 to U.S. patent application Ser. No. 12/754,159, filed Apr. 5, 2012 and entitled “Laser-Irradiated Thin Films Having Variable Thickness,” the entire contents of which are incorporated herein by reference, which is a continuation application of and claims priority to U.S. patent application Ser. No. 11/651,305, filed Jan. 9, 2007 and entitled “Laser-Irradiated Thin Films Having Variable Thickness,” the entire contents of which are incorporated herein by reference, which is a divisional application of and claims priority to U.S. patent application Ser. No. 10/754,157, filed Jan. 9, 2004 and entitled, “Laser-Irradiated Thin Films Having Variable Thickness,” the entire contents of which are incorporated herein by reference and which claims priority under 35 U.S.C. §119(e) to U.S. Provisional Patent Application Ser. No. 60/503,424 filed Sep. 16, 2003, which is hereby incorporated by reference.
| Number | Date | Country | |
|---|---|---|---|
| 60503424 | Sep 2003 | US |
| Number | Date | Country | |
|---|---|---|---|
| Parent | 12754159 | Apr 2010 | US |
| Child | 13740664 | US | |
| Parent | 10754157 | Jan 2004 | US |
| Child | 11651305 | US |
| Number | Date | Country | |
|---|---|---|---|
| Parent | 11651305 | Jan 2007 | US |
| Child | 12754159 | US |