11/578,975 is a national stage entry of PCT/FR05/50260 filed Apr. 20, 2005.
The invention relates to a method enabling realignment between levels after a stage of epitaxy on a substrate. The invention also relates to a substrate having at least one guide mark enabling this realignment.
In particular, it concerns the production of epitaxies of semiconducting material.
Epitaxy is a crystalline growth of a material, generally produced on the same material, respecting the crystalline lattice and orientations. Realignment of levels after a stage of thick epitaxy on silicon is very important for applications in microelectronics and in micro-systems. One often needs to carry out certain technological operations (also called photo-lithographic levels) on the silicon substrate base (solid substrate or SOI), before a thick epitaxy. These levels are very precisely aligned (within less than a micrometer) relative to each other because of the very small dimensions of the patterns. After a stage of thick epitaxy (several tens of micrometers), it is necessary to continue the technological process with supplementary layers which must be perfectly aligned on the pre-epitaxial layers. The thicker the epitaxy, the more difficult the realignment.
On of the realignment techniques known to those skilled in the art is to use guide marks on the rear face of the substrate, these guide marks being aligned with the levels of the front face (active) using specific equipment (double face aligner). Because the epitaxy deposited on the front face does not damage this guide mark, it can be re-used as reference for the post-epitaxy levels.
The main disadvantages of this technique are:
A second technique consists of using the mechanical pre-alignment function of standard equipment (called “steppers”) which make it possible to position the substrate in a relatively precise manner without any reference on the substrate.
This second technique is illustrated in
Another technique consists of producing, on the front face of the substrate, a mark or reference in the substrate material (or in a material deposited on this substrate) which, after the production of epitaxy, will be transferred onto the surface of the epitaxied layer.
Intrinsically, the technique of transferring a guide mark is the most interesting (standard equipment and substrate) and potentially the most precise (work on the same face and optical recognition).
The present invention therefore proposes a technique for realignment between levels, using a guide mark on the front face of the substrate, this mark being reproduced after epitaxy with very good quality and without any shift.
The aim of the invention is thus a method enabling realignment between levels after a stage of epitaxy on a face of a substrate, comprising the production of at least one initial guide mark on said substrate face, this initial guide mark being designed so as to be transferred, during epitaxy, onto the surface of the epitaxied layer, the method being characterised in that the initial guide mark is produced in such a way that, during epitaxy, its edges create growth defects that propagate as far as the surface of the epitaxied layer to provide, on the surface of the epitaxied layer, a transferred guide mark reproducing the shape of the initial guide mark and in alignment with the initial guide mark.
Advantageously, the production of the initial guide mark can include the formation of a plate comprising a stack of at least one layer of material that does not allow development of epitaxy, formed on the face of the substrate, and of a layer of material allowing development of epitaxy. This plate can be formed by stages of deposit and engraving of layers. The layer of material not allowing development of epitaxy can be a layer of a dielectric material.
Said substrate face can be a face allowing epitaxy of a semiconductor material. It can also be a semiconductor material.
According to a special application, said substrate face is in monocrystalline silicon, the layer of material of the initial guide mark allowing development of epitaxy being in polycrystalline silicon, the edges of the guide mark being aligned with the crystalline axes of the monocrystalline silicon of the substrate. In order to obtain the material not allowing development of epitaxy, the formation of the plate can thus comprise the formation of a silicon oxide layer and/or the formation of a layer of silicon nitride.
A further aim of the invention is a substrate intended for producing epitaxy on one of its faces, comprising at least one initial guide mark designed to obtain, after the epitaxy stage, a guide mark transferred onto the surface of the epitaxied layer, characterised in that the initial guide mark has edges able to create, during epitaxy, growth defects that propagate as far as the surface of the epitaxied layer to provide, on the epitaxied layer surface, the transferred guide mark which reproduces the shape of the initial guide mark and is in alignment with the initial guide mark.
Advantageously, the initial guide mark can comprise a stack including at least one layer of material preventing development of epitaxy, formed on the substrate face, and a layer of a material allowing development of epitaxy.
The invention will be better understood and other advantages and particularities will become clear by reading the following description, given as a non-limiting example, accompanied by the attached drawings among which:
The following part of the description refers, as a non-limiting example, to the case of a substrate with a silicon face intended to support a silicon epitaxy.
On face 31, at least one initial guide mark 32 is produced. This initial guide mark is obtained by deposit and engraving of a stack of several layers. This guide mark makes it possible to cause certain defects during epitaxy, these defects being intended to be transferred and to be visible on the surface. The stack comprises successively, on the face 31 and after engraving, a layer of silicon oxide 33, a layer of silicon nitride 34 and a layer of polycrystalline silicon 35. The stack may only consist of a single. layer of dielectric material (in oxide or nitride form). The different layers can have the following thicknesses: about 100 nm for silicon oxide, around 500 nm for silicon nitride, and about 100 nm for polycrystalline silicon.
Since the epitaxied silicon 36 is monocrystalline, the geometry of the guide mark 32 is aligned with the crystallographic axes of the silicon of face 31. As an example, the guide mark 32 is aligned in the <110> direction for silicon shown by the orientation face 31 (100).
During epitaxy, the edges of the guide mark will create growth defects that propagate along the <111> plane as far as the surface of the epitaxied material. These planes are inclined at an angle α of 54.7° for silicon (100) and will therefore provoke the enlargement of the initial guide mark 32 while still remaining perfectly aligned with the latter. The final design will thus be widened on each side of the initial guide mark by a distance W such that:
e being the thickness of the epitaxied layer.
A transferred guide mark 37 is obtained, whose surface is an enlarged reproduction of the surface of the initial guide mark 32.
The inventors of the present invention have noted that the layer of polycrystalline silicon 35 of the initial guide mark 32 made it possible to obtain good quality epitaxy above the guide mark with low roughness. After the epitaxy stage, the transferred guide mark 37 is of very high quality and is very well aligned and perfectly readable by standard photolithographic equipment (steppers).
| Number | Date | Country | Kind |
|---|---|---|---|
| 04 50752 | Apr 2004 | FR | national |
| Filing Document | Filing Date | Country | Kind | 371c Date |
|---|---|---|---|---|
| PCT/FR2005/050260 | 4/20/2005 | WO | 00 | 10/18/2006 |
| Publishing Document | Publishing Date | Country | Kind |
|---|---|---|---|
| WO2005/106943 | 11/10/2005 | WO | A |
| Number | Name | Date | Kind |
|---|---|---|---|
| 4936930 | Gruber et al. | Jun 1990 | A |
| 5128280 | Matsumoto et al. | Jul 1992 | A |
| 5270255 | Wong | Dec 1993 | A |
| 5283205 | Sakamoto | Feb 1994 | A |
| 5314837 | Barber et al. | May 1994 | A |
| 5405810 | Mizuno et al. | Apr 1995 | A |
| 5500392 | Reynolds et al. | Mar 1996 | A |
| 5700732 | Jost et al. | Dec 1997 | A |
| 5792122 | Brimhall et al. | Aug 1998 | A |
| 5798292 | Jost et al. | Aug 1998 | A |
| 5801090 | Wu et al. | Sep 1998 | A |
| 5925937 | Jost et al. | Jul 1999 | A |
| 6046094 | Jost et al. | Apr 2000 | A |
| 6137186 | Jost et al. | Oct 2000 | A |
| 6207529 | Jost et al. | Mar 2001 | B1 |
| 6358814 | Harada | Mar 2002 | B1 |
| 6596604 | Lojek et al. | Jul 2003 | B1 |
| 6605516 | Jost et al. | Aug 2003 | B2 |
| 7396407 | Saenger et al. | Jul 2008 | B2 |
| 20060099781 | Beaumont et al. | May 2006 | A1 |
| 20060208257 | Branz et al. | Sep 2006 | A1 |
| 20060255331 | Chen et al. | Nov 2006 | A1 |
| 20070221120 | Diem et al. | Sep 2007 | A1 |
| Number | Date | Country |
|---|---|---|
| 0 961 320 | Dec 1999 | EP |
| 63108717 | May 1988 | JP |
| 07-153669 | Jun 1995 | JP |
| 10312964 | Nov 1998 | JP |
| Number | Date | Country | |
|---|---|---|---|
| 20070221120 A1 | Sep 2007 | US |