The present invention relates to radiation-sensitive elements having a coating comprising at least one silsesquioxane. The invention furthermore relates to radiation-sensitive compositions used for the production of said elements, a process for imaging such elements and imaged elements obtained therefrom.
The technical field of lithographic printing is based on the immiscibility of oil and water, wherein the oily material or the printing ink is preferably accepted by the image area, and the water or fountain solution is preferably accepted by the non-image area. When an appropriately produced surface is moistened with water and a printing ink is applied, the background or non-image area accepts the water and repels the printing ink, while the image area accepts the printing ink and repels the water. The printing ink in the image area is then transferred to the surface of a material such as paper, fabric and the like, on which the image is to be formed. Generally, however, the printing ink is first transferred to an intermediate material, referred to as blanket, which then in turn transfers the printing ink onto the surface of the material on which the image is to be formed; this technique is referred to as offset lithography.
A frequently used type of lithographic printing plate precursor comprises a photosensitive coating applied onto a substrate on aluminum basis. The coating can react to electromagnetic radiation such that the exposed portion becomes so soluble that it is removed during the developing process. Such a plate is referred to as positive working. On the other hand, a plate is referred to as negative working if the exposed portion of the coating is hardened by the radiation. In both cases, the remaining image area accepts printing ink, or is oleophilic, and the non-image area (background) accepts water, or is hydrophilic. The differentiation between image and non-image areas takes place during exposure, for which a film is attached to the printing plate precursor under vacuum in order to guarantee good contact. The plate is then exposed by means of a radiation source. Alternatively, the plate can also be exposed digitally without a film, e.g. with a UV laser. When a positive plate is used, the area on the film corresponding to the image on the plate is so opaque that the light does not reach the plate, while the area on the film corresponding to the non-image area is clear and allows light to permeate the coating, whose solubility increases. In the case of a negative plate, the opposite takes place: The area on the film corresponding to the image on the plate is clear, while the non-image area is opaque. The coating beneath the clear film area is hardened due to the incident light, while the area not affected by the light is removed during developing. The light-hardened surface of a negative working plate is therefore oleophilic and accepts printing ink, while the non-image area that used to be coated with the coating removed by the developer is desensitized and therefore hydrophilic.
It is known for example from DE 10 113 926 A1, DE 19 739 953 A1 and EP-B-0 900 653 that the use of inorganic particles or polymer particles, such as e.g. SiO2 or polyethylene particles, in free-radical polymerizable radiation-sensitive coatings of printing plate precursors can improve the print run stability of a plate.
However, processing radiation-sensitive compositions comprising such particles is not very easy since the particles should be distributed as evenly as possible in the coating produced from the composition. Usually, this requires special dispersion processes as well as the use of dispersing agents. Still, an aggregation of the particles in the coating solution frequently occurs which is due to an insufficient storage stability of these solutions. Furthermore, the use of particles causes problems during the filtration of the coating solutions since the pore size of the filter has to be larger than the size of the particles used in the solution. However, insufficiently filtered coating solutions lead to coating imperfections.
Another possibility is the production of coatings containing inorganic particles or polymer particles using the so-called dual feed process (see e.g. U.S. Pat. No. 6,548,215). However, this requires special coating techniques which increases the costs of the coating process.
However, in all cases, the particles present in the coating can easily break out of the coating during printing which then leads to a printed image of unacceptable low quality.
It is therefore the object of the present invention to provide a radiation-sensitive elements which, when used in the production of lithographic printing plates, allows a higher print run of the printing plates with—at the same time—a high degree of radiation sensitivity; furthermore, special dispersion processes should be avoided and break-outs in the image elements during printing should be largely excluded.
This object is achieved by a radiation-sensitive element comprising
The first essential component of the radiation-sensitive composition of the present invention is a monomer, oligomer and/or polymer with at least one ethylenically unsaturated group accessible to free-radical polymerization.
All monomers, oligomers and polymers which are free-radical polymerizable and comprise at least one C—C double bond can be used as ethylenically unsaturated monomers, oligomers and polymers. Monomers, oligomers and polymers with C—C triple bonds can also be used, but they are not preferred. Suitable compounds are well known to the person skilled in the art and can be used in the present invention without any particular limitations. Esters of acrylic and methacrylic acids, itaconic acid, crotonic acid, isocrotonic acid, maleic acid and fumaric acid with one or more unsaturated groups in the form of monomers, oligomers or prepolymers are preferred. They may be present in solid or liquid form, with solid and highly viscous forms being preferred. Compounds suitable as monomers include for instance trimethylol propane triacrylate and -methacrylate, pentaerythritol triacrylate and -methacrylate, dipentaerythritolmonohydroxy pentaacrylate and -methacrylate, dipentaerythritol hexaacrylate and -methacrylate, pentaerythritol tetraacrylate and -methacrylate, ditrimethylol propane tetraacrylate and -methacrylate, diethyleneglycol diacrylate and -methacrylate, triethyleneglycol diacrylate and -methacrylate or tetraethyleneglycol diacrylate and -methacrylate. Suitable oligomers and/or prepolymers are for example urethane acrylates and -methacrylates, epoxide acrylates and methacrylates, polyester acrylates and methacrylates, polyether acrylates and methacrylates or unsaturated polyester resins.
In addition to monomers and/or oligomers, use can also be made of polymers comprising free-radical polymerizable C—C double bonds in the main or side chains. Examples thereof include reaction products of maleic acid anhydride/olefin copolymers and hydroxyalkyl(meth)acrylates (cf. e.g. DE-A-4311738); (meth)acrylic acid polymers, partially or fully esterified with allyl alcohol (cf. e.g. DE-A-3332640); reaction products of polymeric polyalcohols and isocyanato(meth)acrylates; unsaturated polyesters; (meth)acrylate-terminated polystyrenes, poly(meth)acrylic acid ester, poly(meth)acrylic acids, poly(meth)acrylamides; (meth)acrylic acid polymers, partially or fully esterified with epoxides comprising free-radical polymerizable groups; and polyethers. In this connection, the prefix “(meth)” indicates that both derivatives of acrylic acid and of methacrylic acid can be used.
Additional suitable C—C-unsaturated free-radical polymerizable compounds are described e.g. in EP-A-1 176 007.
It is of course possible to use different kinds of monomers, oligomers or polymers in admixture; furthermore, mixtures of monomers and oligomers and/or polymers can be used in the present invention, as well as mixtures of oligomers and polymers. The free-radical polymerizable monomers/oligomers/polymers are preferably present in an amount of 5 to 95 wt.-%; if monomers/oligomers are used, especially preferred 20 to 85 wt.-%, based on the dry layer weight of a radiation-sensitive coating prepared from the radiation-sensitive composition of the present invention. As used in the present invention, the term “dry layer weight of the radiation-sensitive coating” is therefore synonymous with the term “solids of the radiation-sensitive composition”.
Another essential component of the radiation-sensitive composition of the present invention is at least one radiation-sensitive initiator or an initiator system for free-radical polymerization of the monomers, oligomers or polymers present. It depends on the type of initiator or initiator system. whether the radiation-sensitive element of the present invention is imaged with UV radiation, visible (VIS) radiation or IR radiation.
Initiators which directly form free radicals upon absorption of UV radiation are known to the person skilled in the art and are for example described in K.K. Dietliker: “Chemistry & Technology of UV&EB formulation for coatings, inks & prints”, Vol. 3 (SITA Technology, London (1991)). They, include for example oxime ethers and oxime esters, benzoins and benzoin ethers, (α-hydroxy or (α-aminoacetophenones, acyl phosphine oxides and diacyl phosphine oxides.
Within the framework of the present invention, an initiator system comprising
For the purpose of the present invention, these initiator systems are divided into two groups, namely those wherein the sensitizer absorbs radiation from the range of more than 750 to 1,200 nm (also briefly referred to as IR absorbers) and those wherein the sensitizer absorbs radiation from the range of 300 to 750 nm. When an initiator system of the first group is used, an IR-sensitive element is obtained whereas the use of an initiator system of the second group leads to a UV or VIS-sensitive element.
Based on its absorption properties, the sensitizer used in the initiator systems determines whether the radiation-sensitive composition is sensitive in the UV, VIS or IR range.
In the present invention, the IR absorbers are preferably selected from the class of triarylamine dyes, thiazolium dyes, indolium dyes, oxazolium dyes, cyanine dyes, polyaniline dyes, polypyrrol dyes, polythiophene dyes and phthalocyanine dyes and pigments. However, other IR absorbers, for example those described in EP 1 160 095 A1, can be used as well.
The following compounds are e.g. suitable IR absorbers:
According to one embodiment of the present invention, an IR absorber of formula (I) is used.
wherein
These IR absorbers absorb in the range of 800 to 1,200 nm; those of formula (I) absorbing in the range of 810 to 860 nm are preferred.
In UV- or VIS-sensitive compositions, compounds of the formula (II) can be used as sensitizers of the oxazole type.
wherein each R4, R5 and R6 is independently selected from a halogen atom, an optionally substituted alkyl group, an optionally substituted aryl group, which may also be fused, an optionally substituted aralkyl group, a group —NR′R″ and a group —OR″′,
Preferably, R4, R5 and R6 are independently selected from a halogen atom, C1-C8 alkyl and a group —NR′R″, wherein R′ and R″ are independently preferably selected from hydrogen atoms and C1-C6 alkyl.
Oxazole derivatives of formula (II) wherein at least one of the groups R4, R5 and R6 represents a group —NR′R″, wherein R′ and R″ are preferably independently selected from hydrogen atoms and C1-C6 alkyl, are especially preferred, and it is particularly preferred that R′=R″=C1-C6 alkyl.
The oxazole derivatives of formula (II) mentioned above can be prepared according to processes well known to the person skilled in the art. In this connection, reference is made to DE-A-1120875 and EP-A-129 059; the processes described in these documents can also be used for the synthesis of oxazoles not explicitly described therein by varying the starting compounds accordingly.
Compounds of formula (III) can also be used as sensitizers for UV or VIS-sensitive compositions:
wherein X1 is a spacer group comprising at least one C—C double bond conjugated to the heterocycles,
The spacer group X1 can be a chain-shaped or cyclic unit or a combination thereof. It is preferably selected from:
In the six-membered rings shown above, it is preferred that the binding sites be in the 1,4-position, in the five-membered rings, the 2,5-position is preferred. The five- and six-membered rings shown above can optionally comprise one or more substituents such as e.g. C1-C10 alkyl and halogen atoms, even if they are not shown in the above formulas.
Preferred sensitizers are represented by formulas (IIIa), (IIIb) and (IIIc):
wherein s and t are independently 0 or an integer from 1 to 4 (preferably 0 or 1), each group R10 and R11 is independently selected from a halogen atom, an alkyl, aryl, aralkyl, alkoxy, aryloxy, aralkyloxy group, a saturated or non-aromatic unsaturated carbocyclic ring, a fused aryl group, —SO3H, —NR102, —COOR11 and —COR11,
The sensitizers of formula (III) can be prepared according to processes well known to the person skilled in the art. In this connection, reference is made to A. Dorlars et al., Angew. Chemie [Applied Chemistry], Vol. 87 (1975), 693-707; the processes described therein can also be used for the synthesis of compounds not explicitly disclosed therein by varying the starting compounds accordingly.
Other possible sensitizers for UV- or VIS-sensitive compositions include 1,4-dihydropyridine compounds of formula (IV)
wherein
According to a preferred embodiment, R12 is a hydrogen atom.
If R13 and R14 do not form rings with adjacent substituents, they are preferably independently selected from C1-C5 alkyl groups or aryl groups.
If R15 and R16 do not form rings with adjacent substituents, they are preferably independently selected from —C(O)OR18.
R17 is preferably selected from C1-C5 alkyl groups or aryl groups.
R18 is preferably, selected from C1-C5 alkyl groups and it is especially preferred that it represent a methyl group.
According to one embodiment, the substitution of the 1,4-dihydropyridine ring with R13/R15 and R14/R16 is symmetrical, i.e. R13=R14 and R15=R16.
According to a preferred embodiment, R13 and R14 are independently selected from optionally substituted alkyl groups, optionally substituted aryl groups, CN and a hydrogen atom, and R15 and R16 are independently selected from —C(O)OR18, —C(O)R18, —C(O)NR19R20 and CN.
Further suitable sensitizers are 1,4-dihydropyridine derivatives of formula (IVa)
wherein R12 and R17 are as defined above,
It goes without saying that the number of groups R8 and/or R9 in formulas (IVa), (IVc), (IVe) and (IVf) is reduced if two groups R8 and/or R9 of adjacent ring carbon atoms together form a fused aromatic ring.
In the 1,4-dihydropyridine derivatives of formula (IVa), R12 is preferably a hydrogen atom, R17 is a methyl or phenyl group and Z1 is preferably O or CH2; the substituents R8a to R8d and R9a to R9d are independently preferably selected from. hydrogen atoms and methyl groups. Of the derivatives of formula (IVa) those with symmetrical substitution at the dihydropyridine ring are especially preferred.
In the derivatives of formula (IVb), R12 is preferably a hydrogen atom and R17 is preferably a methyl or phenyl group. The substituents R10a to R10d and R11a to R11d are independently preferably selected from C1-C5 alkyl groups, OR′ and halogen atoms; a symmetrical substitution of the two aromatic rings is especially preferred.
In the 1,4-dihydropyridine derivatives of formula (IVc), R12 is preferably a hydrogen atom, R17 is preferably a methyl or phenyl group, R14 is preferably a methyl group and R16 is preferably C(O)OR18 (wherein R18 is as defined above). The substituents R9a to R9f are independently preferably selected from C1-C5 alkyl groups. A methyl group is especially preferred.
In the derivatives of formula (IVd), Y1 is preferably a 1,4-phenylene or 1,2-ethylene group. Furthermore, it is preferred that both groups R12 be the same, both groups R13 be the same, both groups R14 be the same, both groups R15 be the same and both groups R16 be the same; the preferred definitions given with respect to formula (IV) apply to all groups R12 to R16.
In the derivatives of formula (IVe), R13 is preferably C1-C5 alkyl, R15 is preferably —C(O)OR18, R16 is preferably C(O)OR18 and R17 is preferably C1-C5 alkyl or phenyl groups (R18 is as defined above). The substituents R9a to R9f are preferably independently selected from C1-C5 alkyl groups.
In the derivatives of formula (IVf), R13 is preferably C1-C5 alkyl, R15 is preferably C(O)OR18, R16 is preferably C(O)OR18 and R17 is preferably a C1-C5 alkyl or a phenyl group (wherein R18 is as defined above). The substituents R9a to R9h are preferably independently selected from C1-C5 alkyl groups.
In the derivatives of formula (IVg), R13 is preferably C1-C5 alkyl, R15 is preferably C(O)OR18, R16 is preferably C(O)OR18 and R17 is preferably a C1-C5 alkyl or a phenyl group. The substituents R11 are preferably independently selected from C1-C5 alkyl groups.
Of the 1,4-dihydropyridine derivatives of formulas (IVa) to (IVg) those of formulas (IVa) and (IVd) are especially preferred.
The 1,4-dihydropyridine derivatives of formula (IV) can be prepared according to processes well known to the person skilled in the art, such as the Hantzsch synthesis. As an example, reference is made to J. Org. Chem. 30 (1965), p. 1914 et seqq., and Angew. Chem. [Applied Chemistry] (Intern.) 20 (1981), p. 762 et seqq.; the processes described therein can also be used for the synthesis of 1,4-dihydropyridines not explicitly disclosed therein by varying the starting compounds accordingly.
Compounds of formula (V) can also be used as sensitizers for UV- or VIS-sensitive compositions:
wherein
For the person skilled in the art, it goes without saying that due to the number of binding sites available at the π-units
the maximum number of substituents R21, R22 and R23 (i.e. o, p and q) is limited; the same of course applies to the maximum number (2+r) of the heterocyclic units bonded to
If X2=O, 2,4,5-substituted oxazoles are obtained, accordingly, if X2=S, 2,4,5-substituted thiazoles are obtained and accordingly, if X2=Se, 2,4,5-substituted selenazoles are obtained; of those compounds, oxazoles and thiazoles are preferred, and oxazoles are especially preferred.
The substituted heterocyclic unit
is bonded at least twice (r=0) to
it is not necessary that these substituents of
all be the same, i.e. for every substituent of
each X2,
R22, R23, p and q is selected independently.
The unsaturated unit
is preferably selected from:
It is especially preferred that
represents:
It is particularly preferred that
represents:
The units
preferably also represent structures SUS-1 to SUS-6; the optional substituents R22 and R23 are not shown. It is especially preferred that
each represent optionally substituted aryl groups, in particular phenyl groups, which are optionally mono- or polysubstituted with a halogen atom or a group NR272 (each R27 is preferably independently selected from alkyl and aryl).
Compounds with a covalent bond between
as depicted below
are not sensitizers according to the present invention; the interaction between
results in chromophores which do not lead to a highly sensitive photosystem.
The optional substituents R21, R22 and R23 are independently selected from a hydrogen atom, a halogen atom, an alkyl group (preferably C1-C8), an aralkyl group, a group —NR24R25 (wherein R24 and R25 are independently selected from alkyl (preferably C1-C8), aryl and aralkyl) and a group —OR26 (wherein R26 is selected from alkyl (preferably C1-C8), aryl and aralkyl).
The following compounds of formula (V) are especially preferred:
Sensitizer 1:
The sensitizers of formula (V) used in the present invention exhibit a strong yellow to greenish fluorescence.
The compounds of formula (V) used in the present invention can be prepared according to processes well known to the person skilled in the art, for example analogously to the process described in EP 0 129 059 and U.S. Pat. No. 3,257,203; the processes described in these documents can also be used for the synthesis of compounds not explicitly described therein by varying the starting compounds accordingly.
The optimum amount of sensitizer depends on various factors such as its extinction coefficient at the emitted wavelength, or the emitted wavelengths of the radiation source used, the thickness of the radiation-sensitive layer of the radiation-sensitive element and its molecular weight. Typically, they are used in amounts of 0.5 to 15 wt.-%, based on the dry layer weight of the radiation-sensitive coating. These values apply to initiator systems of both groups. Each initiator system has an optimum value for the molar ratio (nM=Mol Sens:Mol Coinit) of sensitizer (Sens) and coinitiator (Coinit) which has to be determined by way of appropriate tests. It is usually between 0.1 and 2.
In the present invention, the coinitiators for UV/VIS-sensitive compositions can for example be selected from amines, such as alkanol amines; N,N-dialkylamino benzoic acid esters; N-arylglycines and derivatives thereof (e.g. N-phenylglycine); aromatic sulfonyl halides; trihalomethylsulfones; imides such as N-benzoyloxyphthalimide; diazosulfonates; 9,10-dihydroanthracene derivatives; N-aryl, S-aryl or O-aryl polycarboxylic acids with at least two carboxy groups of which at least one is bonded to the nitrogen, oxygen or sulfur atom of the aryl unit (e.g. aniline diacetic acid and derivatives thereof and other coinitiators described in U.S. Pat. No. 5,629,354); hexaarylbiimidazoles such as e.g. 2,2-bis-(2-chlorophenyl)4,5,4′,5′-tetraphenyl-2′H-[1,2′]biimidazole and 2,2′,5-tris(2-chlorophenyl)-4-(3,4-dimethoxyphenyl)-4,5′-diphenylbi-imidazole; thiol compounds (e.g. 2-mercaptobenzthiazole, 2-mercaptobenzimidazole and 3-mercapto-1,2,4-triazole); phosphines; stannanes; arsines; silanes; 1,3,5-triazine derivatives with 1 to 3 CX3 groups (wherein every X is independently selected from a chlorine or bromine atom, and is preferably a chlorine atom), such as e.g. 2-phenyl-4,6-bis(trichloromethyl)-s-triazine, 2-(4-methoxyphenyl)-4,6-bis(trichloromethyl)-s-triazine, 2,4,6-tris(trichloromethyl)-s-triazine, 2-methyl-4,6-bis(trichloromethyl)-s-triazine, 2-(styryl-4,6-bis(trichloromethyl)-s-triazine, 2-(p-methoxystyryl)-4,6-bis(trichloromethyl)-s-triazine, 2-(4-methoxy-naphtho-1-yl)-4,6-bis-trichloromethyl-s-triazine, 2-(4-ethoxy-naphtho-1-yl)-4,6-bis(trichloromethyl)-s-triazine and 2-[4-(2-ethoxyethyl)-naphtho-1-yl]-4,6-bis(trichloromethyl)-s-triazine; oxime ethers and oxime esters, such as for example those derived from benzoin; α-hydroxy- or α-amino-acetophenones; alkyltriaryl borates; benzoin ethers and benzoin esters; metallocenes (preferably titanocenes, and especially preferred those with two five-membered cyclodienyl groups, such as e.g. cyclopentadienyl groups and one or two six-membered aromatic groups with at least one ortho fluorine atom and optionally also a pyrryl group, such as bis(cyclo-pentadienyl)-bis-[2,6-difluoro-3-(pyrr-1-yl)-phenyl]titanium and dicyclopentadiene-bis-2,4,6-trifluorophenyl-titanium or zirconium); onium salts, such as ammonium salts, diaryliodonium salts, triarylsulfonium salts, aryldiazonium salts, phosphonium salts and N-alkoxypyidinium salts; peroxides (e.g. those listed in EP-A1-1 035 435 as activators of the type of an organic peroxide), acylphosphine oxides; azo compounds, diacylphosphine oxides and triacylphosphine oxides.
IR-sensitive elements according to the present invention preferably comprise one or more polyhalogenalkyl-substituted compounds, onium salts and other compounds described in U.S. Pat. No. 6,309,792 B 1 as coinitiator.
Polyhalogenalkyl-substituted compounds are compounds comprising either one polyhalogenated or several monohalogenated alkyl substituents. The halogenated alkyl group preferably comprises 1 to 3 carbon atoms; a halogenated methyl group is especially preferred. Fluorine, chlorine and bromine atoms are preferably used as halogen atoms, with chlorine and bromine atoms being especially preferred.
Especially suitable polyhalogenalkyl-substituted compounds and onium salts have already been listed in connection with the coinitiators of the UV- or VIS-sensitive initiator systems.
The absorption properties of the polyhalogenalkyl-substituted compound have a decisive impact on the daylight stability of the IR-sensitive elements. Compounds having a UV/VIS absorption maximum in the range of about 300 to 750 nm lead to elements which can no longer be developed after having been stored in daylight for 6 to 8 minutes and subsequently postheated. In principle, such elements cannot only be imaged with IR light but also with UV light. Thus, if daylight stability of the element is a desired characteristic, polyhalogenalkyl-substituted compounds are preferred that do not show an essential UV/VIS absorption at >330 nm.
The gist of the present invention is the use of at least one silsesquioxane having at least one substituent with at least one ethylenically unsaturated group each.
“Silsesquioxanes” (also referred to as “silasesquioxanes”) are silicon-oxygen compounds of the general formula Si2nH2nO3n, which formally comprise 1.5 oxygen atoms per silicon atom.
The substituted silsesquioxanes used in the present invention can be described by the general formula (VI)
Si2uRIV2uO3u (VI)
wherein each RIV is independently selected from H and organic groups, with the proviso that at least one group RIV is an organic group having at least one ethylenically unsaturated group and u assumes values between 8 and 1,000. Products wherein u is 8, 10 or 12 are preferred.
The silsesquioxanes that can be used in the present invention can have a cage structure, a partial cage structure, a ladder structure or a random structure.
The ethylenically unsaturated group can be bonded directly to a Si atom or via a spacer.
Preferably, the at least one organic group RIV with at least one ethylenically unsaturated group is selected from a straight-chain, branched or cyclic alkenyl group preferably comprising 2 to 18 carbon atoms (2 to 10 carbon atoms are especially preferred and 2 to 6 carbon atoms are particularly preferred), a styryl group, an acrylic acid group, a methacrylic acid group, an acrylamide or methacrylamide group, a crotonyl or isocrotonyl group, an itaconic acid group and a maleic acid or fumaric acid group. The groups mentioned above can comprise one or more substituents (preferably 0 or 1 substituent), for example selected from halogen atoms (fluorine, chlorine, bromine, iodine), CN, ORV, SRV or COORV (RV independently represents a hydrogen atom or an alkyl group).
Suitable spacers are preferably alkylene groups preferably comprising 2 to 6 carbon atoms, alkyleneoxy groups preferably comprising 2 to 6 carbon atoms, alkyl(dialkylsilyloxy) groups (wherein the alkyl groups preferably comprise 1 to 3 carbon atoms) or phenylene groups which can optionally be substituted (preferably 0 or 1 substituent, for example selected from halogen atoms (fluorine, chlorine, bromine, iodine) CN, ORV, SRV or COORV (RV independently represents a hydrogen atom or an alkyl group)).
Preferably, the silsesquioxane has a molecular weight in the range of 550 to 2,500 g/mole.
The silsesquioxanes used in the present invention are commercially available or can be prepared according to methods known to the person skilled in the art. Such methods are e.g. described in Chem. Rev. 1995, 95, 1409-1430.
The silsesquioxanes are preferably present in the radiation-sensitive composition in an amount of 2 to 30 wt.-%, based on the total solids content of the radiation-sensitive layer, an amount of 5 to 15 wt.-% is especially preferred.
According to one embodiment, an IR-sensitive composition of the present invention comprises at least one carboxylic acid of the general formula (A) as an optional additional component
R28—(CR29R30)a—Y2—CH2COOH (VII)
wherein:
a is 0, 1, 2 or 3.
N-aryl-polycarboxylic acids are especially preferred; in particular those of formula (VIIa) below:
wherein Ar represents a mono- or polysubstituted or unsubstituted aryl group and v is an integer of 1 to 5,
and of formula (VIIb)
wherein R33 represents a hydrogen atom or a C1-C6 alkyl group and b and c are each an integer from 1 to 5.
Possible substituents of an aryl group are C1-C3 alkyl groups, C1-C3 alkoxy groups, C1-C3 thioalkyl groups and halogen atoms. The aryl group can comprise 1 to 3 identical or different substituents.
v is preferably 1 and Ar preferably represents a phenyl group.
In formula (VIb) c is preferably 1 and R33 preferably represents a hydrogen atom.
Beispiele fuir solche Polycarbonsäiuren sind:
The most preferred polycarboxylic acid is anilino diacetic acid.
The carboxylic acid is preferably present in the IR-sensitive composition in an amount of from 0 to 10 wt.-%, more preferably 1 to 10 wt.-% and especially preferred 1.5 to 3 wt.-%, based on the total solids content.
Furthermore, the radiation-sensitive composition of the present invention can optionally comprise a binder or binder mixture soluble or swellable in aqueous alkaline developer. Basically all polymers or polymer mixtures known in the technical field of radiation-sensitive compositions can be used as polymeric binders for the radiation-sensitive coating. Linear organic polymers soluble or swellable in water or in aqueous alkaline solutions are especially suitable. Suitable binders are described for example in EP 170 123 A1. Polyvinyl acetals, acrylic acid copolymers, methacrylic acid copolymers, polyurethanes, partially esterified copolymers of maleic acid, novolaks and acidic cellulose derivatives are particularly suitable. It is preferred that the binder comprise acid groups, especially preferred carboxy groups. Acrylic polymers are most preferred. Binders with acid groups preferably have an acid value in the range of 20 to 180 mg KOFUg polymer. Optionally, the binder can comprise groups capable of undergoing a cycloaddition (e.g. photocycloaddition). The amount of binder is not particularly restricted and is preferably in the range of 0 to 90 wt.-%, especially preferred 5 to 60 wt.-%.
The radiation-sensitive composition can also comprise small amounts of a thermopolymerization inhibitor. Suitable examples of inhibitors of an undesired thermopolymerization include e.g. hydroquinone, p-methoxyphenol, di-t-butyl-p-cresol, pyrrogallol, t-butylcatechol, benzoquinone, 4,4′-thio-bis-(3-methyl-6-t-butylphenol), 2,2′-methylene-bis-(4-methyl-6-t-butylphenol) and N-nitrosophenylhydroxylamine salts. The amount of non-absorbable polymerization inhibitor in the radiation-sensitive coating is preferably 0 to 5 wt.-%, based on the dry layer weight, especially preferred 0.01 to 2 wt.-%. Such inhibitors are often introduced into the radiation-sensitive coating via commercial monomers or oligomers and are therefore not expressly mentioned.
Furthermore, the radiation-sensitive composition of the present invention can comprise dyes or pigments for coloring the layer. Examples of colorants include e.g. phthalocyanine pigments, azo pigments, carbon black and titanium dioxide, ethyl violet, crystal violet, azo dyes, anthraquinone dyes and cyanine dyes. The amount of colorant is preferably 0 to 10 wt.-%, based on the dry layer weight, especially preferred 0.5 to 5 wt.-%.
For improving the physical properties of the hardened layer, the radiation-sensitive composition can additionally comprise plasticizers. Suitable plasticizers include e.g. dibutyl phthalate, dioctyl phthalate, didodecyl phthalate, dioctyl adipate, dibutyl sebacate, triacetyl glycerin and tricresyl phosphate. The amount of plasticizer is not particularly restricted, however, it is preferably 0 to 10 wt.-%, based on the dry layer weight, especially preferred 0.25 to 5 wt.-%.
The radiation-sensitive composition can also comprise known chain transfer agents. They are preferably used in an amount of 0 to 15 wt.-%, based on the dry layer weight, especially preferred 0.5 to 5 wt.-%.
Furthermore, the radiation-sensitive composition can comprise leuco dyes such as e.g. leuco crystal violet and leucomalachite green. They are preferably present in an amount of 0 to 10 wt.-%, based on the dry layer weight, especially preferred 0.5 to 5 wt.-%.
Additionally, the radiation-sensitive composition can comprise surfactants. Suitable surfactants include siloxane-containing polymers, fluorine-containing polymers and polymers with ethylene oxide and/or propylene oxide groups. They are preferably present in an amount of 0 to 10 wt.-%, based on the dry layer weight, especially preferred 0.2 to 5 wt.-%.
Exposure indicators, such as e.g. 4-phenylazodiphenylamine, can also be present as optional components of the radiation-sensitive composition; they are preferably present in an amount of 0 to 5 wt.-%, especially preferred 0 to 2 wt.-%, based on the dry layer weight.
The radiation-sensitive elements of the present invention can for example be printing form precursors (in particular precursors of lithographic printing plates), printed circuit boards for integrated circuits or photomasks. The use for the production of printing form precursors is especially preferred.
A dimensionally stable plate or foil-shaped material is preferably used as a substrate in particular in the production of printing form precursors. Preferably, a material is used as dimensionally stable plate or foil-shaped material that has already been used as a substrate for printing matters. Examples of such substrates include paper, paper coated with plastic materials (such as polyethylene, polypropylene, polystyrene), a metal plate or foil, such as e.g. aluminum (including aluminum alloys), zinc and copper plates, plastic films made e.g. from cellulose diacetate, cellulose triacetate, cellulose propionate, cellulose acetate, cellulose acetatebutyrate, cellulose nitrate, polyethylene terephthalate, polyethylene, polystyrene, polypropylene, polycarbonate and polyvinyl acetate, and a laminated material made from paper or a plastic film and one of the above-mentioned metals, or a paper/plastic film that has been metallized by vapor deposition. Among these substrates, an aluminum plate or foil is especially preferred since it shows a remarkable degree of dimensional stability, is inexpensive and furthermore exhibits excellent adhesion to the coating. Furthermore, a composite film can be used wherein an aluminum foil has been laminated onto a polyethylene terephthalate film.
A metal substrate, in particular an aluminum substrate, is preferably subjected to at least one treatment selected from graining (e.g. by brushing in a dry state or brushing with abrasive suspensions, or electrochemical graining, e.g. by means of a hydrochloric acid electrolyte), anodizing (e.g. in sulfuric acid or phosphoric acid) and hydrophilizing.
In order to improve the hydrophilic properties of the surface of the metal substrate that has been grained and optionally anodized in sulfuric acid or phosphoric acid, the metal substrate can be subjected to an aftertreatment with an aqueous solution of sodium silicate, calcium zirconium fluoride, polyvinylphosphonic acid or phosphoric acid. Within the framework of the present invention, the term “substrate” also encompasses an optionally pre-treated substrate exhibiting, for example, a hydrophilizing layer on its surface.
The details of the above-mentioned substrate pre-treatment are known to the person skilled in the art.
For producing a radiation-sensitive element, the radiation-sensitive composition of the present invention is applied to a hydrophilic surface of the substrate by means of common coating processes (e.g. spin coating, dip coating, coating by means of doctor blades). It is also possible to apply the radiation-sensitive composition on both sides of the substrate; however, for the elements of the present invention, it is preferred that the radiation-sensitive coating be only applied to one side of the substrate.
For this purpose, the radiation-sensitive composition comprises one or several organic solvents.
Suitable solvents include low alcohols (e.g. methanol, ethanol, propanol and butanol), glycolether derivatives (e.g. ethylene glycol monomethylether, ethylene glycol dimethylether, propylene glycol monomethylether, ethylene glycol monomethylether acetate, ethylene glycol monoethylether acetate, propylene glycol monomethylether acetate, propylene glycol monoethylether acetate, ethylene glycol monoisopropylether acetate, ethylene glycol monobutylether acetate, diethylene glycol monomethylether, diethylene glycol monoethylether), ketones (e.g. diacetone alcohol, acetyl acetone, acetone, methyl ethyl ketone, cyclohexanone, methyl isobutyl ketone), esters (e.g. methyl lactate, ethyl lactate, acetic acid ethyl ester, 3-methoxypropyl acetate and butyl acetate), aromatics (e.g. toluene and xylene), cyclohexane, γ-butyrolactone, tetrahydrofuran, dimethylsulfoxide, dimethylformamide and N-methylpyrrolidone. The solids content of the radiation-sensitive mixture to be applied depends on the coating method that is used and is preferably 1 to 50 wt.-%.
The additional application of a water-soluble oxygen-impermeable overcoat onto the radiation-sensitive layer can be advantageous. The polymers suitable for such an overcoat include, inter alia, polyvinyl alcohol, polyvinyl alcohol/polyvinyl acetate copolymers, polyvinyl pyrrolidone, polyvinyl pyrrolidone/polyvinyl acetate copolymers, polyvinyl methylethers, ring-opened copolymers of maleic acid anhydride and a comonomer such as methylvinylether, polyacrylic acid, cellulose ether, gelatin, etc.; polyvinyl alcohol is preferred. Preferably, the composition for the oxygen-impermeable overcoat is applied in the form of a solution in water or in a solvent miscible with water; in any case, the solvent is selected such that the radiation-sensitive coating already present on the substrate does not dissolve. The layer weight of the overcoat can e.g. be 0.1 to 6 g/m2, preferably 0.5 to 4 g/m2. However, the printing plate precursors according to the present invention show excellent properties even without an overcoat. The overcoat can also comprise matting agents (i.e. organic or inorganic particles with a particle size of 2 to 20 μm) which facilitate the planar positioning of the film during contact exposure. In order to improve adhesion of the overcoat to the radiation-sensitive layer, the overcoat can comprise adhesion promoters such as e.g. poly(vinylpyrrolidone), poly(ethyleneimine) and poly(vinylimidazole).
Suitable overcoats are described for example in EP 1 000 387 B1.
The thus produced radiation-sensitive elements are image-wise exposed in a manner known to the person skilled in the art with UV/VIS radiation of a wavelength of >300 nm. For this purpose, common lamps, such as carbon arc lamps, mercury lamps, xenon lamps and metal halide lamps, or lasers or laser diodes can be used. UV laser diodes emitting UV radiation in the range of about 405 nm (e.g. 405±10 nm) and frequency-doubled NdYAG lasers emitting at around 532 nm are of particular interest as a radiation source.
If the sensitizer absorbs IR radiation, i.e. noticeably absorbs radiation of a wavelength in the range of more then 750 to 1,200 nm, and preferably shows an absorption maximum in this range in its absorption spectrum, image-wise exposure can be carried out with IR radiation sources. Suitable radiation sources are semi-conductor lasers or laser diodes which emit in the mentioned wavelength range.
After image-wise exposure, the elements are developed in a manner known to the person skilled in the art, using a commercially available aqueous alkaline developer whereby the exposed areas remain on the substrate and the unexposed areas are removed.
After image-wise exposure, i.e. prior to developing, a heat treatment can be carried out at 50 to 180° C., preferably 90 to 150° C. Sometimes it is advantageous to subject the developed element to a heat treatment (150 to 250° C., preferably 170 to 220° C.) or a UV overall exposure or both. The developed elements can be treated with a preservative (“gumming”) using a common method. The preservatives are aqueous solutions of hydrophilic polymers, wetting agents and other additives.
The radiation-sensitive elements of the present invention result in printing plates with excellent abrasion resistance, resulting in high print run length.
The invention will be explained in more detail in the following examples; however, they shall not restrict the invention in any way.
A coating solution was prepared from the following components:
The components listed above were dissolved under stirring in 200 ml of a mixture consisting of
After filtration of the solution, it was applied by means of common processes to an electrochemically grained and anodized aluminum foil that had been subjected to an aftertreatment with an aqueous solution of polyvinylphosphonic acid and the layer was dried for 4 minutes at 90° C. The dry weight of the resulting IR-sensitive layer was about 1.4 g/m2.
Then an oxygen-impermeable layer with a dry layer weight of 2.0 g/m2 was applied by coating with a solution of the following composition:
Drying took place for 5 minutes at 90° C.
The plate precursor produced in this manner was then exposed in a Trendsetter 3244 of the company Creo/Scitex with an 830 nm laser diode (20 W head, 3 W, different drum speeds). An UGRA/FOGRA Postscript 2.0 EPS, which contains different elements for evaluating the quality of the copies, was used for imaging.
The exposed precursor was further processed in a MercuryNews® processor (Kodak Polychrome Graphics LLC) equipped with a preheating section, a pre-wash section, an immersion type developing bath, a section for rinsing with water, a gumming and a drying section. The processor was filled with developer 980 from Kodak Polychrome Graphics LLC. The following parameters were applied for processing the plate precursor: speed 120 cm/min, preheating 630, pre-wash volume 0.5 l/m2 plate, temperature of the developing bath 23±1° C. After this treatment, the exposed areas remained on the plate while the unexposed areas were completely removed by the developer.
The following criteria were used for evaluating the copies obtained after preheating and developing: The reproduction quality of 1 pixel elements, the optical density of checkerboard patterns of the pixel elements and the optical density of a solid element. For determining the contrast and the density of solids and dots, a D19/D 196 apparatus (Gretag/Macbeth Color Data Systems, Great Britain) was used.
The results with respect to energy requirements showed that an exposure energy of 31 mJ/cm2 was sufficient for a good reproduction of solids, while an energy of 40 mj/cm2 was required for 1 pixel elements. The plate exposed with 40 mJ/cm2 was mounted in a sheet-fed offset press and used for printing using an abrasive printing ink (Offset S7184 of Sun Chemical; contains 10% CaCO3). The image areas accepted the printing ink without any problems and the paper copies did not show any toning in the non-image areas. After 220,000 high-quality copies, printing was discontinued; however, the plate could have been used for more prints. Only very few break-outs were observed in the solids and all fine pixel elements were maintained.
The coating solution of Example 1 was modified by adding 0.45 g anilino diacetic acid and leaving out the 2-thio(4-ethenyl)benzyl-5-mercapto- 1,3,4-thiadiazole.
The coating solution and the overcoat solution were applied as described in Example 1. Exposure and developing was carried out as described in Example 1.
The following energy requirements were observed for good prints:
The plate exposed with 78 mJ/cm2 was mounted in a sheet-fed offset press and used for printing using the abrasive printing ink Offset S7184.
The image areas accepted the printing ink without any problems and the paper copies did not show any toning in the non-image areas. After 220,000 high-quality copies, printing was discontinued; however, the plate could have been used for more prints.
Only very few break-outs were observed in the solids and all fine pixel elements were maintained.
An electrochemically grained (in HCl) and anodized aluminum foil was subjected to a treatment with an aqueous solution of polyvinylphosphonic acid (PVPA) and, after drying, coated with the following solution and dried.
The solution was filtered, applied to the lithographic substrate and the coating was dried for 4 minutes at 90° C. The dry layer weight of the photopolymer layer was about 1.6 g/m2.
The resulting plate was provided with an overcoat layer by coating it with the aqueous solution described in Example 1; after drying at 90° C. for 4 minutes, the overcoat layer had a dry layer weight of about 2 g/m2.
The printing plate precursor was exposed to the light of a Ga-doped MH lamp with an energy of 3.4 mJ/cm2 in a vacuum frame using a gray scale having a tonal range of 0.15 to 1.95, wherein. the density increments amounted to 0.15 (UGRA gray scale). Immediately after exposure, the plate was heated in an oven for 2 minutes at 90° C.
Then the exposed plate was treated for 30 seconds with developer 952 of Kodak Polychrome Graphics LLC.
Then the developer solution was again rubbed over the surface for another 30 seconds using a tampon and then the entire plate was rinsed with water. After this treatment, the exposed portions remained on the plate. For the assessment of its photosensitivity, the plate was blackened in a wet state with printing ink.
The following results were obtained:
One printing plate precursor was exposed with 3.4 mJ/m2 and developed as described above, then the resulting printing plate was mounted in a sheet-fed offset press and used for printing with the abrasive printing ink Offset S7184. After 220,000 copies, no abrasion was observed on the plate.
Only very few break-outs were observed in the solids and all fine pixel elements were maintained.
The coating solution of Example 3 was modified by adding 0.9 g PSS-octa(2(4-cyclohexenyl)ethyldimethylsilyloxy substituted (available from Aldrich) and leaving out the 0.7 g methacryl-POSS cage. A printing plate was produced as described in Example 3.
The following results were obtained:
One printing plate precursor was exposed with 3.4 mJ/m2 and developed as described above. Then the resulting printing plate was mounted in a sheet-fed offset press and used for printing with the abrasive printing ink Offset S7184. After 220,000 copies, no abrasion was observed.
Only very few break-outs were observed in the solids and all fine pixel elements were maintained.
Example 1 was repeated, but the coating solution did not contain methacryl-POSS cage. A minimum energy of 33 mJ/cm2 was required for a good reproduction of solids, and 41 mJ/cm2 for 1 pixel elements.
The printing plate produced by exposure with 41 mJ/cm2 was mounted in a sheet-fed offset press and used for printing with the abrasive printing ink Offset S7184. The image areas accepted the printing ink without any problems and the paper copies did not show any toning in the non-image areas.
Printing had to be discontinued after only 150,000 copies because the obtained copies were of poor quality. A high number of break-outs were observed in the solids and the fine elements were affected considerably.
Number | Date | Country | Kind |
---|---|---|---|
10 2004 034 362.4 | Jul 2004 | DE | national |
Filing Document | Filing Date | Country | Kind | 371c Date |
---|---|---|---|---|
PCT/EP05/07686 | 7/14/2005 | WO | 1/11/2007 |