Patent Grant
7968364
The invention generally relates to MEMS switches and, more particularly, the invention relates to contact systems for MEMS switches.
A wide variety of electrical switches operate by moving one member into direct contact with another member. For example, a relay switch may have a conductive cantilever arm that, when actuated, moves to directly contact a stationary conductive element. This direct contact closes an electrical circuit, consequently electrically communicating the arm with the stationary element to complete an ohmic connection. Accordingly, the physical portions of the arm that directly contact each other are known in the art as “ohmic contacts,” or as referred to herein, simply “contacts.”
Contacts often are fabricated by forming an electrically conductive metal on another surface, which may or may not be an insulator. For example, a cantilevered arm may be formed from silicon, while the contact at its end is formed from a conductive metal. When exposed to oxygen, water vapor, and environmental contaminants, however, the metal may react to form an insulative surface contamination layer, such as an insulative nitride layer, insulative organic layer, and/or an insulative oxide layer. As a result, the contact may be less conductive. Larger switches nevertheless generally are not significantly affected by this phenomenon because they often are actuated with a force sufficient to “break or scrub through” the surface contamination layer (e.g., an insulative oxide layer).
Conversely, switches with much smaller actuation forces often are not able to break through this surface contamination layer. For example, electrostatically actuated MEMS switches often have typical contact forces measured in Micronewtons, which can be on the order of 1000 to 10,000 times less than the comparable force used in larger switches, such as reed or electromagnetic relays. Accordingly, the insulative surface contamination layer may degrade conductivity, which, in addition to reducing its effectiveness, reduces the lifetime of the switch.
In accordance with one embodiment of the invention, a method of fabricating a hermetically capped MEMS switch that includes a substrate and a platinum-series contact seals a cap to the substrate over the contact in an oxygenated environment in a process that also passivates the contact. In one embodiment, the contact is oxidized at a first temperature and pressure, and the cap is hermetically sealed at a second, higher temperature and pressure. In another embodiment, the cap is hermetically at a temperature below that at which a passivating dioxide will form, and the contact is later oxides at a higher temperature, consuming oxygen confined within the volume defined by the sealed cap. In a preferred embodiment, the contact is ruthenium and the passivation includes ruthenium dioxide.
The platinum-series based material may include a platinum-series element. Alternatively, the platinum-series based material may be a platinum-series based oxide. In some embodiments, at least one of the contacts has both a platinum-series based element and a conductive passivation. For example, the platinum-series based element may be ruthenium, while the conductive passivation may be ruthenium dioxide.
In accordance with another embodiment of the invention, a capped MEMS apparatus has a substrate, a first contact, and a movable member with a second contact that moves relative to the substrate. The substrate supports the movable member. Moreover, at least one of the contacts has a conductive platinum-series based material that provides an electrical connection when contacting the other electrical contact.
Those skilled in the art should more fully appreciate advantages of various embodiments of the invention from the following “Description of Illustrative Embodiments,” discussed with reference to the drawings summarized immediately below.
In illustrative embodiments, a MEMS switch has a contact formed from a platinum-series based material. For example, the contact may be formed from ruthenium metal (hereinafter “ruthenium” alone), ruthenium dioxide, or both. This type of contact should have material properties that provide favorable resistances and durability, while at the same time minimizing undesirable insulative surface contamination layers that could degrade switch performance. The MEMS switch is capped in a process that employs oxygen, such that the passivation of the switch contact and the capping occur via a continuous process in an oxygen-controlled environment. Details of illustrative embodiments are discussed below.
As known by those skilled in the art, when closed, the switch 16 electrically connects the first set of components 12 with the second set of components 14. Accordingly, when in this state, the system 10 may transmit electronic signals between the first and second sets of components 12 and 14. Conversely, when the switch 16 is opened, the two sets of components 12 and 14 are not electrically connected and thus, cannot electrically communicate through this path.
The stationary member 24 illustratively is fixedly secured to the substrate 18 and, in some embodiments, serves as an actuation electrode to move the movable member 22, when necessary. Alternatively, or in addition, the switch 16 may have one or more other actuation electrodes not shown in the figures. It should be noted, however, that electrostatically actuated switches are but one embodiment. Various embodiments apply to switches using other actuation means, such as thermal actuators and electromagnetic actuators. Discussion of electrostatic actuation therefore is not intended to limit all embodiments.
The movable member 22 has an electrical contact 28A at its free end for alternately connecting with a corresponding contact 28B on a stationary contact beam 29. When actuated, the movable member 22 translates in a direction generally parallel to the substrate 18 to contact the contact 28B on the stationary contact beam 29. During use, the movable member 22 alternatively opens and closes its electrical connection with the stationary contact beam 29. When closed, the switch 16 creates a closed circuit that typically forms a communication path between various elements, such as those discussed above.
The die forming the electronic switch 16 can have a number of other components. For example, the die could also have circuitry (not shown) that controls a number of functions, such as actuation of the movable member 22. Accordingly, discussion of the switch 16 without circuitry is for convenience only.
It should be noted that various embodiments can use a wide variety of different types of switches. For example, the switch 16 could multiplex more than two nodes and thus, be a three or greater position switch. Those skilled in the art should be capable of applying principles of illustrative embodiments to a wide variety of different switches. Discussion of the specific switch 16 in
In accordance illustrative embodiments of the invention, one or both of the two noted contacts 28A and/or 28B is formed from a platinum-series based material (also known as “platinum group” or “platinum metals”). Specifically, as known by those skilled in the art, platinum-series elements include platinum (Pt), ruthenium (Ru), rhodium (Rh), palladium (Pd), osmium (Os), and iridium (Ir). Contacts 28A or 28B having platinum-series based materials therefore comprise at least a platinum-series based element. For example, ruthenium dioxide (RuO2, or RuO2) is considered to be a platinum-series based material because part of it is ruthenium.
In one embodiment, one contact (e.g., contact 28A) is formed from a platinum-series based material, while the other contact (e.g., contact 28B) is formed from another type of material, such as a gold based material. In preferred embodiments, however, both contacts 28A and 28B are formed from a platinum-series based material. In some embodiments, this material simply may be a conductive oxide, such as ruthenium dioxide. In other embodiments, however, one or both of the contacts 28A and 28B have at least two layers; namely, a base layer 30 and a conductive passivation layer 32 (also referred to simply as “passivation layer 32” or more generally as “conductive passivation”). For example, the base layer 30 may be a platinum-series element, such as ruthenium, while the passivation layer 32 is a conductive oxide. Among others, the conductive oxide may be a platinum-series based material, such as ruthenium dioxide. In other embodiments using this two layer approach, however, the conductive oxide is not a platinum-series based material. Moreover, this two layer approach can have additional layers, such as an adhesion layer between the two layers 30 and 32.
Platinum-series based elements provide a number of advantages when used to form contacts 28A and/or 28B. Specifically, in the MEMS context, thin layers of such materials (e.g., on the order of angstroms) provided a relatively low resistivity while being hard enough to withstand repeated contact. During experiments, however, contacts formed from platinum-series elements alone undesirably formed an insulative surface contamination layer. It subsequently was discovered that application of an appropriate conductive oxide both passivated the base layer 30 and substantially mitigated formation of an insulative surface contamination layer. Moreover, the conductive oxide permitted sufficient conductivity. It also was discovered that rather than using a two layer approach, a single conductive oxide comprised of a platinum-series based material also provided satisfactory results. Consequently, when applied as discussed herein, certain materials, such as platinum-series based materials, can be used to form the contacts 28A and/or 28B without the significant risk of formation of an insulative surface contamination layer.
As noted above, the switch 16 in
It is anticipated that the conductive passivation layer 32 may deteriorate or degrade to some extent during the lifetime of the switch 16, or have some kind of imperfection that adversely affects its passivation capabilities. For example, although it serves its purpose as a satisfactory passivation element, the discussed conductive oxide still may have some permeability to oxygen remaining in the chamber 36 from fabrication processes. Specifically, semiconductor packaging processes often seal the chamber 36 in the presence of oxygen. In one such process, glass frit wafer-to-wafer bonding processes may require bonding in the presence of oxygen to facilitate organic burn off of volatile solvents in the glass paste. In addition, if the glass contains lead, oxygen may be required to oxidize any metallic lead to prevent subsequent surface contamination.
As noted above, exposure to these contaminants in some circumstances can cause formation of an insulative surface contamination layer. For example, when at least one of the contacts 28A or 28B is formed from ruthenium, sufficient exposure to oxygen may cause formation of an insulative oxide layer, such as a ruthenium oxide (RuO) layer, or a ruthenium tetraoxide (RuO4, or RuO4) layer.
Accordingly, to further protect the contacts 28A and 28B, illustrative embodiments provide a gettering system 38 for attracting and trapping much of the residual contaminants, such as oxygen, if any, within the hermetically sealed chamber 36. For example, among other ways of gettering, the switch 16 may have a coating of deposited platinum-series metal, such as ruthenium, innocuously located within the chamber 36. To that end,
The switch 16 can be packaged in a number of other types of packages. Discussion of the two types in
Another difference between the switch 16 in
Of course, as noted above, various embodiments apply to many different types of switches. For example, rather than apply to switches having one stationary contact 28B and another moving contact 28A, various embodiments apply to switches having two or more moving contacts.
Rather than having a member that moves only in the plane parallel to the substrate 18, the movable member 22 in this embodiment moves generally perpendicular to the substrate 18, or in an arcuate manner relative to the substrate 18. Such a design often is referred to as a “cantilevered design.” The stationary contact 28B of this embodiment therefore simply is generally planar and positioned on the surface of the substrate 18. The contacts 28A and 28B may be comprised of the same materials as discussed above (although schematically shown as appearing to have only one layer—they still may have two layers, which is similar to other embodiments). In a similar manner, this embodiment has other similar components, such as a movable member 22, stationary member 24, and substrate 18. In a manner similar to other embodiments, this embodiment may be contained in a conventional package, such as one of the packages shown in
It should be noted that for simplicity, the process of
The process begins at step 400, which forms the base structure. For example, the process may begin by depositing and etching various layers of materials on a base substrate. The movable member 22 may or may not be formed at this point. For example, the process may fabricate the movable member 22 and expose its end for depositing contact material in a subsequent step. Alternatively, the process may form a recess or specific area on a sacrificial layer for first depositing contact material in a subsequent step, and then depositing material (on the contact material) that forms the movable member 22 in an even later step.
Accordingly, step 402 then deposits the contact materials; namely, the process deposits platinum-series based material on at least the location designated step 400, and on a location that will form the stationary contact 28B. In illustrative embodiments, the process may deposit ruthenium metal through conventional means, such as with a sputtering or plating mechanism. After it is deposited, conventional wet or dry etch processes pattern the deposited material to ensure that the ruthenium is at the correct contact locations. Alternatively, as noted above, rather than deposit ruthenium metal, this step may deposit and pattern a conductive oxide, such as ruthenium dioxide, in a conventional manner to the relevant location.
The process then continues to step 404, which completes fabrication of the structure and circuitry on the switch die. As noted above, this step may employ conventional surface micromachining technologies, such as plating, deposition, patterning, etching, and release operations. For example, this step may deposit sacrificial oxides and conductive layers to form the movable member 22 and other components, and then release the movable member 22 and other suspended components (if any). In illustrative embodiments, the movable member 22 is primarily formed from gold or a gold alloy.
It then is determined at step 406 if the contacts 28A and/or 28B should be passivated (i.e., protected from the environment of the package chamber 36, which, as noted above, could have residual oxygen or other contaminants). If step 402 deposited a platinum-series metal, such as ruthenium, then the contact 28A and/or 28B should be passivated to minimize formation of an insulative surface contamination layer. In that case, the process continues to step 408, which first cleans the contacts 28A and 28B (e.g., removing any oxidization that occurred to that point), and then forms a conductive oxide on the platinum-series element. For example, the process may form ruthenium dioxide on a ruthenium metal contact 28A and/or 28B, substantially entirely covering its entire area. In some embodiments, however, the entire area of the ruthenium metal contact 28A and/or 28B is not covered (only a portion of it is covered).
Among other ways, the ruthenium contacts 28A and/or 28B may be exposed to a thermal oxidizing environment at an elevated temperature (e.g., 200 degrees C. or greater). Alternatively, ruthenium dioxide may be directly sputtered on a surface using DC magnetron sputtering. Typical sputtering conditions, for example, may be at temperatures of 300° C., 12 mTorr pressure, with an argon/oxygen mix at 14/45 sccm. This should form a uniform a ruthenium dioxide layer that could be patterned as required by the device application. Etching materials may include O2/CF4, O2Cl2, or O2/N2 plasmas. Exposure of ruthenium metal to an oxygen plasma also should result in the selective formation of a conductive ruthenium dioxide passivation layer over the existing patterned ruthenium based metal.
Step 408 may be entirely skipped, however, if step 406 determines that passivation is not necessary. In either case, the process continues to optional step 410, which applies gettering material to the package or the die. For example, as noted above, this gettering material may control free oxygen (among other things), which, in some instances, can form a native, insulating oxide if exposed to the contacts 28A and/or 28B. As noted above, the impact of oxygen on the contacts 28A and 28B should be substantially mitigated if an area within the chamber 36 having a platinum-series “gettering” metal that is significantly greater than the area of the contacts 28A and 28B. In some embodiments, the gettering metal is the same as the metal used on the contacts 28A and/or 28B. Other embodiments, however, use different metals.
The process then concludes at step 412 by hermetically sealing the switch 16 in ambient oxygen levels that are sufficiently low so as not to saturate the gettering system 38 formed by step 410. One of ordinary skill in the art can determine those levels based on a number of factors.
As noted above, steps 410 is optional. If step 410 is skipped, that leaves step 408 (formation of conductive oxide on platinum series element) adjacent to step 412 (hermitically seal switch). As also noted above, some steps may be performed in a different order than is presented in
An exemplary embodiment involves the passivation of a platinum-series metal contact on a substrate (or “base”), while hermetically sealing the contact within a cap that is secured to the substrate by a process that uses oxygen. Exemplary embodiments may have a platinum-series metal contact on a movable beam, or on both a substrate and a beam. For example, the contact may be ruthenium, which is passivated by the formation of ruthenium dioxide, and the hermetic seal may be formed by the use of a glass frit.
The passivation of the ruthenium contact may involve oxygen in a thermal oxidation process. Preferably, the ruthenium oxide formed will be substantially pure ruthenium dioxide. Creating other forms of oxidized ruthenium may detract from desirable properties for a contact. For example, formation of other ruthenium oxides (such as RuO and RuO4) is preferably avoided or minimized, at least because they may not be sufficiently conductive, may not be stable at normal operating temperatures, or may not be sufficiently hard for normal use.
Securing a cap to a substrate by use of a glass frit (such as lead borosilicate glass) also involves oxygen, as is known in the industry. A glass frit may comprise glass beads or particles in a paste containing solvents, usually organic. The glass beads or particles may include lead (Pb). In some embodiments, the solvent burns off at elevated temperatures, allowing the glass particles to fuse into an amorphous material. During the fusing, lead may migrate to the surface of the glass and be oxidized if sufficient oxygen is available, as discussed below.
A glass frit may be cured by a process of organic burn off (“OBO”) in an oxygen environment at a temperature in the range of 200 degrees Celsius to 300 degrees Celsius, for example. The frit paste will sinter at temperatures of about 440 degrees Celsius, and in the process may release some of the lead. For example, as the temperature increases and the glass liquefies, some of the lead may come out of solution and migrate to the surface of the glass where it can interact with the ambient environment.
Free lead particles potentially pose a problem, for example if they could form conductive paths (e.g., short circuits) between conductors in the product. As such, sintering the frit paste in an oxygen environment may be useful if it oxidizes the lead, so that the lead particles are not electrically conductive.
A detailed exemplary embodiment is illustrated in the flowchart 500 of
Alternatively, the glass frit may be applied to the device wafer to be capped. For example, the glass frit may be applied to the device wafer to be capped if there is nothing on the surface of the device wafer that would interfere with screen printing the glass frit, such as if MEMS devices on the device wafer are fabricated in a cavity or otherwise below the surface of the device wafer to which the glass frit is being applied.
The glass frit is then cured 502 in an oxygen environment at a temperature of approximately 200 degrees Celsius to 300 degrees Celsius, to burn off (organic burn off, or “OBO”) solvent. In this process, lead from the glass frit is oxidized to become non-conductive lead dioxide (PbO2).
The cap and device wafer are aligned in a thermocompression wafer bonder at 503. An exemplary thermocompression wafer bonder 600 is schematically illustrated in
The atmosphere surrounding the wafers is purged at 504, and then filled with an ambient gas, such as dry nitrogen. The wafers and chuck assembly may be held within a chamber (not shown). The ambient fill gas may include oxygen, but including oxygen at this stage may risk formation of undesirable ruthenium oxides (i.e., RuO and RuO4). Preferably, the introduction of oxygen into the environment is delayed until the temperature of the wafers is at or above about 200 degrees Celsius.
One or more purging cycles may be applied, as illustrated (701) in
The atmosphere is pressurized to 2 atmospheres at 505, and the temperature of the wafers is increased to greater that about 200 degrees Celsius at 506. As discussed above, preferably the environment of the chamber is substantially free of oxygen while the temperature is below 200 degrees Celsius, so ideally no unstable or non-conductive ruthenium oxides are formed.
When the temperature is above about 200 degrees Celsius, oxygen may be introduced into the chamber at 507. This may not be necessary if oxygen was introduced into the chamber at a previous point (such as 504). The amount of oxygen in the environment is preferably sufficient to oxidize the ruthenium contacts to form ruthenium dioxide, and to complete OBO, burning off any remaining solvents in the glass paste, and to oxidize any metallic lead that precipitates to the surface of the glass when the glass fuses. The environment need not be pure oxygen, but a partial pressure of oxygen facilitates the oxidation of any metallic lead precipitates so that they are not electrically conductive, and the completion of the organic burn-off of any remaining solvents in the glass frit system.
In this environment, ruthenium dioxide will begin to form on the ruthenium contact. The process of forming ruthenium dioxide on the contact is self-limiting, because ruthenium dioxide forms where ruthenium is exposed to oxygen. As ruthenium dioxide forms at the exposed surface of the ruthenium contact, that ruthenium dioxide begins to shield the underlying ruthenium. Formation of additional ruthenium dioxide occurs within the ruthenium contact at the interface of the ruthenium and the previously formed ruthenium dioxide. As such, oxygen from the environment must diffuse through any previously formed ruthenium dioxide to reach that interface. Eventually, the ruthenium dioxide grows thick enough to prevent oxygen from migrating through the ruthenium dioxide to reach the underlying ruthenium. At that point, formation of additional ruthenium dioxide is substantially prevented. Any remaining oxygen in the environment will have no further effect on the contact, and as such may be effectively harmless. In preferred embodiments, the ruthenium oxides formed on the contact are substantially free of oxides other than RuO2, but some amounts of other ruthenium oxides may be acceptable. Preferably, the ruthenium oxides comprise at least fifty percent ruthenium dioxide.
Pressure is applied to the wafers via the chucks at 508. The temperature of the chuck, and thus the wafers, is raised to about 440 degrees Celsius at 509.
The combination of temperature, pressure, and the oxygenated environment will cause the glass frit to sinter over time, bonding the wafers. The temperature of the wafers is lowered to ambient at 510.
In
As illustrated in
Oxygen may be added after the temperature reaches about 200 degrees Celsius. At this temperature, the ruthenium contact is passivated by the formation of ruthenium dioxide as the wafers soak in the elevated temperature environment for about two minutes 722. Such a soak may include a period where the temperature is held steady 722, but may also occur during an uninterrupted rise in temperature (see
In some embodiments, the wafers may be maintained at a temperature (which may be known as an “idle” temperature) of above 200 degrees Celsius, as opposed for example to lowering the temperature to below 200 degrees Celsius prior to beginning the passivation and capping process. In the illustrative example of
Then in
In
The wafers are held under this pressure and temperature for approximately ten minutes 725, during which time the bonding occurs. Some embodiments hold the wafers under this pressure for five minutes. Preferably, the cap is hermetically sealed to the substrate by the bonding process. Thereafter, the temperature is ramped down 726 to about or below 200 degrees Celsius, between about 1800 seconds and 2300 seconds. After the temperature has reached about or below 200 degrees Celsius 727, the gas pressure 703 and chuck pressure 745 are reduced.
The bonded wafers may then be removed from the chamber for further processing, such as die singulation, test, and packaging.
The amount of oxygen, gas pressure, chuck pressure, temperatures, and times will vary depending on each other, and the devices being fabricated. For example, the oxygen concentrations will be determined, at least in part, by the amount or area of ruthenium surfaces, exposed glass frit area, temperature, and dwell time at temperature. Oxygen concentrations from 0.25 percent to 10 percent have been successfully used. Clean dry air (“CDA”; approximately twenty percent oxygen) has also been successfully used.
Also, the pressure of the gas within the chamber may vary as a function of the temperature at which the pressure is measured. Preferably, the pressure at any given temperature is such that, when the temperature of the gas is brought to room temperature (e.g., 25 degrees Celsius), the pressure of the gas is reduced to about 1 atmosphere. A higher pressure may be used if the pressure within the hermetically sealed devices is desired to be higher than 1 atmosphere when the device is at room temperature. Such a pressure may assist in keeping elements from the external environment from seeping into the device. Alternately, lower pressure may be used if the pressure within the hermetically sealed device is desired to be lower than 1 atmosphere when the device is at room temperature. Such a pressure may be useful, for example, for (1) partial vacuum packaging to reduce mechanical damping of the MEMS structures or (2) limiting the volume of gases available to react with a capped MEMS device over its lifetime, or (3) facilitating hemeticity testing (for example, a leaking device would draw in ambient atmosphere and perhaps degrade in performance so that it would fail subsequent mechanical or electrical screening).
In some embodiments that involve the formation of a MEMS beam or cantilever, it may be desirable to limit the time that the MEMS structure is exposed to high temperatures, such as the 440 degree Celsius temperature described above. For example, a MEMS structure 800, including a cantilevered beam 801, is schematically illustrated in
In some illustrative embodiments, the oxygen may be supplied as a plasma. The formation of ruthenium dioxide is an endothermic process, so some energy is supplied, for example, from the elevated chamber or wafer temperature, or from the energy in a plasma. Too little energy may result in the formation of undesirable ruthenium oxides (e.g., RuO or RuO4).
Some embodiments may use anodic bonding, rather than a frit. Anodic bonding does not require oxygen, but could be performed in an oxygen environment to, for example, passivate a contact while bonding or provide an environment suitable to passivate the contact during a thermal cycle subsequent to bonding. Alternate bonding methods may occur without the use of a thermocompression bonder, as illustrated for some embodiments herein.
In an illustrative embodiment, a switch may be hermetically capped using a low temperature process in an oxygen-rich atmosphere. The temperature would preferably be lower than the temperature that would form an undesirable oxide (such as RuO or RuO4), and in any case lower than that required to form a conductive oxide (such as ruthenium dioxide, for example). The device could then be heated to at an elevated temperature, while sealed, allowing oxygen confined within the volume of the cap to form the conductive oxide, such as ruthenium dioxide. Such a hermetic seal may be formed at sufficiently low temperature by anodic bonding or low-temperature metal eutectic bonding, for example.
A flow chart illustrating such a process 900 is presented in
The cap is then hermetically sealed to the substrate 902, so as to cover the switch and the contacts within a cavity formed by the cap and substrate. Because this is occurring in the oxygen-rich environment, there will be some oxygen contained within the cavity.
Next, the temperature within the cavity is raised 903 to a point where the contacts will oxidize with the oxygen within the cavity. Preferably the temperature is raised quickly to a point where the desired oxide is formed, and the formation of undesired oxides is mitigated. For example, if the contact is made of ruthenium, and ruthenium dioxide is formed, the temperature should be raised quickly to about 200 degrees Celsius, for example at a rate of about 100 degrees Celsius per minute. The temperature should be made to pass quickly through temperature ranges in which other oxides (such as RuO or RuO4) would form.
After the contacts are oxidized, the temperature is lowered 904 and the process ends 905.
The exemplary processes described above may be useful for other packaging systems, such as the cavity package 38 in
In general, the processes may be useful for capping or sealing an apparatus that includes surfaces that would benefit from passivation, such as surfaces that may undesirably have a capacity to stick to one another. Embodiments may reduce or eliminate the need for a getter in the package. Also, the process steps described herein are exemplary only. In varying applications, some process steps may be skipped or combined, or their order rearranged.
Accordingly, illustrative embodiments of the invention benefit from the material properties of platinum-series based materials while mitigating the contamination problems that prevented known prior art devices from using such materials. Moreover, various embodiments further protect against possible contamination with a gettering system 38 within the package chamber 36. Among other benefits, these optimizations should improve switch performance and increase switch lifetime.
Although the above discussion discloses various exemplary embodiments of the invention, it should be apparent that those skilled in the art can make various modifications that will achieve some of the advantages of the invention without departing from the true scope of the invention. For example, in some embodiments, only one contact 28A or 28B is formed as discussed above, while the other contact 28B or 28A is formed by conventional means, such as with gold or a gold alloy. In other embodiments, an apparatus may have a plurality of contacts that operate in parallel. Therefore, the embodiments of the invention described above are intended to be merely exemplary; numerous variations and modifications will be apparent to those skilled in the art. All such variations and modifications are intended to be within the scope of the present invention as defined in any appended claims.
This patent application is a continuation-in-part of U.S. patent application Ser. No. 11/538,251, filed Oct. 3, 2006 entitled “MEMS Switch Contact System” and naming Mark Schirmer and John Dixon as inventors (practitioner's file 2550/B31), which claims priority from provisional U.S. patent application No. 60/723,019, filed Oct. 3, 2005 entitled, “MEMS CONTACT SYSTEM USING Pt SERIES METALS AND SURFACE PREPARATION THEREOF,” and naming Mark Schirmer as the sole inventor (practitioner's file 2550/A81), the disclosures of which are incorporated herein, in their entirety, by reference.
| Number | Name | Date | Kind |
|---|---|---|---|
| 2664618 | Kleis | Jan 1954 | A |
| 4674180 | Zavracky et al. | Jun 1987 | A |
| 4764244 | Chitty et al. | Aug 1988 | A |
| 4959515 | Zavracky et al. | Sep 1990 | A |
| 5635750 | Schlaak et al. | Jun 1997 | A |
| 5638946 | Zavracky | Jun 1997 | A |
| 6091125 | Zavracky | Jul 2000 | A |
| 6153839 | Zavracky et al. | Nov 2000 | A |
| 6191671 | Schlaak et al. | Feb 2001 | B1 |
| 6483395 | Kasai et al. | Nov 2002 | B2 |
| 6963117 | Yang et al. | Nov 2005 | B2 |
| 7173203 | Ma | Feb 2007 | B2 |
| 7202764 | Deligianni et al. | Apr 2007 | B2 |
| 7256669 | Morrison, Jr. et al. | Aug 2007 | B2 |
| 7372191 | Ohmori et al. | May 2008 | B2 |
| 20020088112 | Morrison, Jr. et al. | Jul 2002 | A1 |
| 20050007217 | Deligianni et al. | Jan 2005 | A1 |
| 20050062120 | Ma et al. | Mar 2005 | A1 |
| 20060037398 | Rich | Feb 2006 | A1 |
| 20070065295 | Moraja et al. | Mar 2007 | A1 |
| 20080135386 | Bozler et al. | Jun 2008 | A1 |
| Number | Date | Country |
|---|---|---|
| 1 628 138 | Feb 2006 | EP |
| 645681 | Nov 1950 | GB |
| WO 2005006372 | Jan 2005 | WO |
| Number | Date | Country | |
|---|---|---|---|
| 20100068854 A1 | Mar 2010 | US |
| Number | Date | Country | |
|---|---|---|---|
| 60723019 | Oct 2005 | US |
| Number | Date | Country | |
|---|---|---|---|
| Parent | 11538251 | Oct 2006 | US |
| Child | 12544470 | US |