Patent Application
20240321816
The present application relates to method and apparatus for processing integrated circuits in general, and, in particular, to a method and apparatus for debonding temporarily bonded wafers in wafer-level packaging applications.
Three-dimensional (3D) chip technologies have been gaining popularity in the microelectronics industry because of their advantages such as shorter circuit paths, higher performance, less power consumption and faster heat dissipation. With 3D chip technologies, multiple heterogeneous silicon wafers can be stacked vertically to form a 3D integrated circuit. The silicon wafers are relatively thin (50-100 μm) such that they can be interconnected by utilizing through-silicon vias (TSVs).
During the manufacturing of a 3D integrated circuit, a thinning step is required to be performed on each silicon wafer of the 3D integrated circuit in order to reduce the thickness of the silicon wafer. The silicon wafer is typically bonded to a rigid carrier prior to the thinning process. Existing approaches for bonding a silicon wafer to a carrier involve the use of an adhesive placed directly between the silicon wafer and the carrier. After back-grinding and all the required backside processing have been performed on the silicon wafer, the thinned silicon wafer needs to be debonded from the carrier. Wafer debonding is the process of separating the processed silicon wafer from the carrier so that the processed wafer can progress to its intended application.
The present disclosure provides an apparatus and method for debonding a silicon wafer from a carrier during the manufacturing of 3D integrated circuits.
In accordance with one embodiment, a light-absorbing layer is placed on a carrier. A wafer is then attached to the light-absorbing layer of the carrier via an adhesive layer to form a bonded wafer stack. After processing the wafer has been processed, a light pulse from a flashlamp is applied to a non-wafer side of the carrier to heat the light-absorbing layer and the adhesive layer in order to loosen the wafer from the bonded wafer stack. Finally, the wafer is removed from the bonded wafer stack.
All features and advantages of the present invention will become apparent in the following detailed written description.
The invention itself, as well as a preferred mode of use, further objects, and advantages thereof, will best be understood by reference to the following detailed description of an illustrative embodiment when read in conjunction with the accompanying drawings, wherein:
Current techniques for debonding a silicon wafer from a carrier include: (a) using chemical solvents to dissolve the adhesive between the silicon wafer and the carrier, (b) using mechanical means to debond the silicon wafer off the carrier, and (c) heating the adhesive between the silicon wafer and the carrier to a point where the silicon wafer can be separated from the carrier by shearing. However, the usage of harsh chemicals is not very desirable. Also, shearing or high temperature may cause damage to the surface structure of the silicon wafer.
The laser-assisted wafer debonding technique is an attractive alternative due to its ability to debond silicon wafers at room temperature. However, there are also some disadvantages associated with the laser-assisted wafer debonding technique, such as variations in the sensitivity of a laser beam's focal point with variation in the thickness of a wafer-carrier stack, power fluctuations of the laser beam, requirement of special beam focusing objectives, need for scanning optics, and low throughput due to beam width limitations, especially when processing a larger size wafer (>300 mm).
Referring now to the drawings and in particular to
Carrier 210 and light absorbing layer 220 are materials chosen to be thermally stable at an elevated temperature and have coefficients of thermal expansion (CTE) that are closely matched with each other in order to mitigate any kind of cracking or delamination of light absorbing layer 220 from carrier 210 when light absorbing layer 220 is heated.
Carrier 210 may be made of quartz, glass or any rigid material which transmits light emitted by a flashlamp. Quartz has a CTE of 5.5×10−7/K. Corning Eagle XG (a type of glass) has a CTE of about 3.2×10−6/K to 3.5×10−6/K. Light absorbing layer 220 may be made of metal (such as tungsten or molybdenum), metal alloy, or ceramic. Molybdenum has a CTE of 4.8×10−6/K, while tungsten has a CTE of 4.5×10−6/K.
One example of a good carrier-absorbing layer combination is Corning Eagle XG for carrier 210 and 90% tungsten/10% titanium at 200 nm thick for light absorbing layer 220 because the CTE between them is matched to within 1.5×10−6/K.
An adhesive layer, such as an adhesive layer 230 in
Adhesive layer 230 may be a thermoplastic or a cross-linkable material that is thermally or ultra-violet (UV) light cured. Adhesive layer 230 may include a polymer or oligomer dissolved or dispersed in a solvent. The polymer or oligomer is selected from a group consisting of polymers and oligomers of cyclic olefins, epoxies, acrylics, silicones, styrenics, vinyl halides, vinyl esters, polyamides, polyimides, polysulfones, polyethersulfones, cyclic olefins, polyolefin rubbers, polyurethanes, ethylene-propylene rubbers, polyamide esters, polyimide esters, polyacetals, polyazomethines, polyketanils, polyvinyl butyrals, and combinations thereof. The type of solvent used depends on the choice of polymer or oligomer.
The thermoplastic composition of adhesive layer 230 should have a viscosity at least 500,000 Pa-s, preferably from 1,000,000 Pa-s to 3,000,000 Pa-s, at room temperature, and a viscosity of less than 15,000 Pa-s, preferably from 500 Pa-s to 10,000 Pa-s, at temperatures between 160° C. and 500° C.
Adhesive layer 230 may be a nonpolymeric material with the structure of the molecule having less than one repeating subunit. When a nonpolymeric bonding material is used, the melting point of adhesive layer 230 should be below its sublimation point and has the ability to crosslink or further react in order to prevent material sublimation at high temperatures. The thermal decomposition temperature of adhesive layer 230 should be between 220° C. and 450° C.
Next, a wafer, such as a wafer 240 in
Subsequently, the wafer side of bonded wafer stack 200 is subjected to a back-thinning process in order to reduce the thickness of wafer 240, as depicted in block 140. After the thickness of wafer 240 has been reduced, electronic devices and/or electrical components can be built on wafer 240, as shown in block 150. Although the device fabrication step is shown to be performed after the thinning step, it is understood by those skilled in the art that the device fabrication step can be performed before the thinning step or the wafer attachment step (block 130).
Afterwards, wafer 240 can be removed (debonded) from bonded wafer stack 200 by exposing the non-wafer side of transparent carrier 210 to an intense pulse of light from a flashlamp, such as a flashlamp 350 in
It is desirable to have light absorbing layer 220 to absorb as much of the light pulse (which is broadband from about 200 nm to about 1,500 nm) as possible. Increased absorbance of the light pulse from flashlamp 350 that a shorter pulse length can be used at a given intensity. This results in less stress on flashlamp 350 and less total energy deposited into wafer 240 from the debonding process. Molybdenum has an absorbance of about 55-60%, while tungsten has an absorbance of about 50-55%. Light absorbing layer 220 can be made thick enough to not pass the light emission from flashlamp 350 but thin enough to have as little thermal mass as possible during the debonding process. The thickness of light absorbing layer 220 is about 100 nm-300 nm, and preferably about 150 nm-250 nm.
Referring now to
Capacitor bank 320 can be charged by capacitor-bank-charging power supply 310. Charges from capacitor bank 320 are then discharged into flashlamp 350 via IGBT-based switching device 330 while IGBT-based switching device 330 is being switched on-and-off repeatedly by frequency controller 340 during the discharge. Frequency controller 340 controls the gating of IGBT-based switching device 330 that, in turn, controls the switching frequency of the discharge. The repeated on-and-off switching of IGBT-based switching device 330 is intended to modulate the current flow from capacitor bank 320 to flashlamp(s) 350, which in turn switches flashlamp(s) 350 on and off. In other words, the frequency or pulse length of light pulses emitted by flashlamp(s) 350 is dictated by frequency controller 340.
Photodiode 360 within flashlamp control unit 301 needs to be calibrated before operation. Photodiode 360 can be calibrated by using bolometer 370 that is National Institute of Standards and Technology (NIST) traceable. During calibration, both photodiode 360 and bolometer 370 are exposed to a single light pulse emitted from flashlamp 350. Bolometer 370 measures the radiant exposure or energy per area (in unit J/cm2) of the single light pulse, and photodiode 360 measures the instantaneous power density (in unit W/cm2) of the same light pulse. The instantaneous power density signals from photodiode 360 are then integrated by integrator 380 to yield a radiant exposure value of the same single light pulse, and the radiant exposure measurement from bolometer 370 is divided by this radiant exposure value from integrator 380 to generate a calibration factor as follows:
After calibration, the photodiode 360/integrator 380 combination can be utilized to provide radiant exposure information of each light pulse emitted from flashlamp 350. Basically, the radiant exposure information of a light pulse emitted from flashlamp 350 can be calculated by multiplying the calibration factor obtained during calibration with the output value of integrator 380 (which is the radiant exposure value of the light pulse emitted from flashlamp 350 formed by integrating the instantaneous power signals of the light pulse emitted from flashlamp 350 measured by photodiode 360).
Wafer debonding unit 302 includes a wafer feeding robot 352, a debonding vacuum table 354, and a vacuum gripper 356.
Prior to debonding, a dicing tape 410 is mechanically clamped to wafer stack 200 via retaining rings 420 to form a bonded wafer assembly, as shown in
At the separation station, vacuum gripper 356 separates carrier 210 from the bonded wafer assembly, while wafer 240 mounted on dicing tape 410 is being held down by debonding vacuum table 354. Both carrier 210 and wafer 240 on dicing tape 410 are conveyed to a cleaning station to remove any residual adhesive (i.e., adhesive layer 230 from
At this point, wafer 240 is so fragile that the vacuum being applied to wafer 240 should be distributed across wafer 240 so as not to break it during removal. This may be accomplished with multiple suction cups 430 distributed across the surface of wafer 240. Alternatively, the vacuum may be applied by a distributed vacuum, such as a vacuum table with perforated holes. Vacuum table 354 may have a polymer on its surface so that wafer 240 is not damaged during handling.
During the debonding process, apparatus 300 may have 5-lamp drivers per flashlamp using 24 mm diameter and 150 mm long lamps with 150 mm×75 mm exposure area per lamp. The flashlamps may be placed parallel to each other to increase the exposure area in increments of 75 mm. For example two flashlamps provide an exposure area of 150 mm×150 mm, three flashlamps provide an exposure area of 150 mm×225 mm, four flashlamps provide an exposure area of 150 mm×300 mm, etc. The flashlamps are placed in a common optical cavity, and the exposure is uniform to within 3%. Flashlamp drivers contain capacitors and IGBTs. The current from the capacitors is switched by the IGBTs into the flashlamps. Lamp drivers may be placed in parallel with each other to increase the peak current supplied to the flashlamps. A variable of the flashlamp system is the charging voltage of the capacitors, the total capacitance, which is determined by the number of flashlamp drivers, and the length of the pulse of light, which is switched on and off by the IGBTs. All parameters are controlled by a computer. Silicon wafer may be debonded from glass carrier plates at 900-950V at pulse durations of 50-150 microseconds, which corresponds to 2-6 J/cm2 emitted with each pulse. The peak radiant power of flashlamp 350 is greater than 20 KW/cm2, more preferable greater than 30 KW/cm2, and even more preferable greater than 40 KW/cm2.
It is noted that the thinner the wafer, the easier it is for the wafer to be debonded from a carrier plate. This is principally due to the fact that the wafer, is very thermally conductive. Silicon, for example, has a thermal conductivity of about 140 W/cm-K. This is over 100 times greater than the typical carrier plate, which is glass. As such, much of energy from the light absorbing layer is conducted to the wafer through the adhesive layer during the 50-150 microsecond long time the absorber is being irradiated by the pulse of light. When the adhesive layer reaches the debond temperature, it debonds from the carrier. The thinner the wafer, the quicker the adhesive reaches the debond temperature. Thus, a thinner wafer may be debonded with a shorter pulse of light at the same intensity. An advantage of this is that less energy is needed to perform the debond process. Additionally, the lifetime of the flashlamps in the flashlamp system is increased since duration is decreased. Alternatively, the intensity of the emission from the flashlamp may be decreased for a given pulse length. This also reduces the total amount of energy deposited into the wafer.
As has been described, the present invention provides an improved method for debonding a wafer from a carrier. There are several advantages of the present invention over the prior art. The first is that the wafer debonding can be performed with as little a single pulse of light. This means that the time to debond the wafer from the stack is dramatically reduced from several 10s of seconds (or longer) to less than 150 microseconds for a single pulse or less than 10 seconds, or even less than 2 for two pulses. Another advantage over the prior art is that the need for rastering the light emission to scan the entire wafer is greatly reduced or eliminated. This dramatically reduces the complexity of the apparatus by eliminating the need for complex scanning optics. A further advantage over the prior art is that the inhomogeneities in the debonding process from hundreds of pulses are greatly reduced since the entire wafer sees the same time temperature history from one or two pulses of light. The same time temperature history in the debonding process has the implication that the wafer is more cleanly debonded than in the prior art. This further reduces the amount of time it takes to remove any residual bonding adhesive from the wafer and carrier plate at the cleaning station over the prior art.
While the invention has been particularly shown and described with reference to a preferred embodiment, it will be understood by those skilled in the art that various changes in form and detail may be made therein without departing from the spirit and scope of the invention.
The present application is a continuation application of U.S. Ser. No. 17/122,796, filed on Dec. 15, 2020.
| Number | Date | Country | |
|---|---|---|---|
| Parent | 17122796 | Dec 2020 | US |
| Child | 18594007 | US |