Patent Application
20120174404
The invention relates to a method for producing tooth parts from dental-grade metal powder. Within the context of the present invention, tooth parts are understood particularly as bridge structures and caps, along with full prostheses.
Prior Art
In the dental industry, the lost-wax casting process continues to be the most commonly used process for producing tooth parts from metal, in which process a wax mold is modeled on a working model, with the shape of said mold corresponding to the object to be cast. Using this wax mold, a cavity is formed in a casting mold, which is then cast with metal. This method is highly costly and requires a great deal of artisanal skill.
For this reason, a number of methods have already been proposed, which are implemented using not molten metal but metal powder which is sintered. None of these methods has gained acceptance in practical use for a wide variety of reasons.
However, one promising method is disclosed in EP 1 885 278 B1 (Wolz). In this case, a metal layer is deposited by electrophoresis from a suspension fluid onto a model, wherein the deposited metal layer is stabilized by sintering, in that it is either fixed on a firing support, or in that it remains on a plated stump, or is placed in a muffle filled with embedding compound or temperature-resistant powder.
In addition to the production of tooth parts from metal, the production of fully ceramic dental prostheses is known, and makes up approximately 10% of the dental market. One customary method consists in using CAD/CAM techniques to mill a framework out of an isostatically pre-pressed block of ceramic, particularly zirconium oxide. In this case, the patient's teeth or a working model is/are scanned, and the framework is milled on the basis of the scanned model. With this method, tooth parts are also milled from solid metal blocks. One major disadvantage of this method is that the milling of ceramic produces dust, and also places high mechanical demands on the milling machine. As a result, the service life of simple, in other words inexpensive, milling machines is too short. Even more complex milling machines, the investment costs of which frequently exceed the economic capability of an average dental laboratory, require an unjustifiable expenditure on maintenance. For these reasons, many dental laboratories no longer even use milling machines.
Statement of the Problem
The invention specified in claim 1 therefore addresses the problem of allowing the milling machines already existing in dental laboratories to be used to produce tooth parts from metal, the quality of which satisfies all requirements of dental medicine.
Embodiment Example
In what follows, the invention will be specified in greater detail in reference to the production of tooth parts from a CrCo alloy. However, the invention is not restricted to CrCo alloys, and can instead be used with all other NE alloys and noble metal alloys.
The invention starts out with a slip made of CrCo dental-grade metal powder. In EP 1885 278 B1 (Wolz), the production of a dental-grade metal slip is described for the first time. An improved CrCo slip is commercially available under the name WOLCERAM CrCo slip, which is used here. It consists of 98 wt % CrCo powder and 2 wt % water (suspension liquid) with small admixtures of organic compounds and preservative agents. Before this slip is used, a conditioning of the slip is highly recommended, in order to prevent agglomerates. A corresponding device for this purpose is disclosed in German patent DE 10 2005 023 737 B4 (Wolz). After conditioning, a mold made of silicone rubber is filled, in order to produce a round disk having a diameter of 95 mm and a thickness of 20 mm. The slip is solidified to a usable blank (green body) by drying the slip in the mold. To ensure that no air bubbles are present in the slip, it is subjected to pressure treatment at 6 bar, during which air is pressed out of the slip. This is followed by the drying process, in which the mold is dried in a drying cabinet at 65° C. for 7 hours. Drying can also be carried out under a vacuum and/or under compression. It is recommended to design the base of the mold as having a water-absorbent layer (e.g., blotting paper), so that the water is able to escape not only on the surface but also on the bottom side of the slip. The resulting concentration gradient of the water concentration is thereby reduced, preventing the non-aqueous auxiliary agents from emerging on the surface. The result of drying is a disk-shaped green body, which corresponds to the shape of the blanks that are processed in customary CAD/CAM milling machines. From the solid blank (green body) approximately 30 tooth parts are milled out of both sides, and remain attached to one another by connectors. Once the connectors have been removed, 30 tooth parts are left. In contrast to milling from a metal disk, with the present method, the removal of the connectors and the smoothing of the connector sites can be easily carried out, since the material is still relatively soft.
The resulting green tooth parts are then subjected to oxygen-free sintering. For this purpose, they are placed in a sintering furnace, such as is disclosed in the older patent application 10 2009 037 737.9 (application date Aug. 17, 2009). The green CrCo tooth parts are sintered at 1190° C. for a period of 45 min. To expel the oxygen, 2.5 l/min argon is introduced. The sintering results in metallic, shiny tooth parts made of CrCo metal, which can still be faced, as is customary. Of course, the shrinkage that occurs as a result of sintering must be compensated for by means of a corresponding CAM/CAD program.
The sintered product has the following properties. The chemical composition has been determined via emission spectroscopy.
Technical data: Density (g/cm3) 8.3
Standards: ISO 9693:1999; ISO 22674:2006; ISO 10993-5:1999
Because some milling machines operate using water as their coolant, it can be problematic that the raw material is still water soluble. Once the blank has been tempered at 250-400° C. for 2 to 3 hours, however, the material can be milled in the presence of water without problems. The material is then stable in an aqueous environment.