Method for reducing wettability of interconnect material at corner interface and device incorporating same

Abstract

A semiconductor device includes a recess defined in a dielectric layer, the recess having an upper sidewall portion extending to an upper corner of the recess and a lower sidewall portion below the upper sidewall portion. An interconnect structure is positioned in the recess. The interconnect structure includes a continuous liner layer having upper and lower layer portions positioned laterally adjacent to the upper and lower sidewall portions, respectively. The upper layer portion includes an alloy of a first transition metal and a second transition metal and the lower layer portion includes the second transition metal but not the first transition metal. The interconnect structure also includes a fill material substantially filling the recess, wherein the second transition metal has a higher wettability for the fill material than the alloy.

Description

BACKGROUND

The disclosed subject matter relates generally to the field of semiconductor device manufacturing, and more particularly, to a method for reducing wettability of ruthenium liner at corner interface and a device made according to the method.

A conventional integrated circuit device, such as a microprocessor, is typically comprised of many thousands of semiconductor devices, e.g., transistors, formed above the surface of a semi-conductive substrate. For the integrated circuit device to function, the transistors must be electrically connected to one another through conductive interconnect structures. The back end of line (BEOL) is the second portion of integrated circuit fabrication where the individual devices (transistors, capacitors, resistors, etc.) get interconnected with wiring on device. BEOL generally begins when the first layer of metal is deposited on the wafer. It includes contacts, insulating layers (dielectrics), metal levels, and bonding sites for chip-to-package connections. Many modern integrated circuit devices are very densely packed, i.e., there is very little space between the transistors formed above the substrate. Thus, these conductive interconnect structures must be made in multiple layers to conserve plot space on the semiconductor substrate.

The conductive interconnect structures are typically accomplished through the formation of a plurality of conductive lines and conductive plugs, commonly referred to as contacts or vias, formed in alternative layers of dielectric materials formed on the device. As is readily apparent to those skilled in the art, the conductive plugs are means by which various layers of conductive lines, and/or semiconductor devices, may be electrically coupled to one another. The conductive lines that connect the various interconnect structures are commonly formed in trenches defined in the dielectric layers.

A contact is generally used to define an interconnect structure (e.g., using polysilicon or metal) to an underlying polysilicon layer (e.g., source/drain or gate region of a transistor), while a via denotes a metal to metal interconnect structure. In either case, a contact opening is formed in an insulating layer overlaying the conductive member. A second conductive layer is then formed over the contact opening and electrical communication is established with the conductive member.

One technique for reducing the size of the features formed on the semiconductor device involves the use of copper for the lines and interconnections in conjunction with new dielectric materials having lower dielectric constants than previously achievable with common dielectric material choices. Standard dielectric materials such as silicon dioxide, TEOS, and F-TEOS have dielectric constants greater than 3. The new dielectric materials, commonly referred to as low-k dielectrics, have dielectric constants less than 3, and thus, allow greater device densities, due to their more efficient isolation capabilities. One suck low-k dielectric is sold under the name of Black Diamond, by Applied Materials, Inc.

Typical interconnect features include a barrier layer for inhibiting electromigration and a seed layer to provide a starting template for the bulk copper fill needed to complete the interconnect. Due to continuous scaling to smaller dimensions, the fabrication process for BEOL metal features must be tightly controlled to address geometries on a scale of sub-nanometers. Ruthenium (Ru) has been proposed as a seed enhancement layer to improve the copper seed coverage, thereby enhancing the copper fill. A ruthenium layer allows direct copper plating, but copper wettability on ruthenium is so good that there is no copper recess at the interface of copper and ruthenium at the upper outer corners of the metal features. These regions, referred to as “triple points” can have a negative impact on reliability. The copper may be at the same height as the ruthenium liner, or the copper can even creep over the top of the ruthenium and migrate along the interlayer-dielectric interface thus inducing early failures.

This section of this document is intended to introduce various aspects of art that may be related to various aspects of the disclosed subject matter described and/or claimed below. This section provides background information to facilitate a better understanding of the various aspects of the disclosed subject matter. It should be understood that the statements in this section of this document are to be read in this light, and not as admissions of prior art. The disclosed subject matter is directed to overcoming, or at least reducing the effects of, one or more of the problems set forth above.

BRIEF SUMMARY OF EMBODIMENTS

The following presents a simplified summary of only some aspects of embodiments of the disclosed subject matter in order to provide a basic understanding of some aspects of the disclosed subject matter. This summary is not an exhaustive overview of the disclosed subject matter. It is not intended to identify key or critical elements of the disclosed subject matter or to delineate the scope of the disclosed subject matter. Its sole purpose is to present some concepts in a simplified form as a prelude to the more detailed description that is discussed later.

One aspect of the disclosed subject matter is seen in a semiconductor device that includes a recess defined in a dielectric layer, the recess having an upper sidewall portion extending to an upper corner of the recess and a lower sidewall portion below the upper sidewall portion. Additionally, the disclosed semiconductor device further includes an interconnect structure positioned in the recess. The interconnect structure includes, among other things, a continuous liner layer having upper and lower layer portions positioned laterally adjacent to the upper and lower sidewall portions, respectively. The upper layer portion includes an alloy of a first transition metal and a second transition metal and the lower layer portion includes the second transition metal but not the first transition metal. Moreover, the interconnect structure of the disclosed semiconductor device also includes a fill material substantially filling the recess, wherein the second transition metal has a higher wettability for the fill material than the alloy.

Another aspect of the disclosed subject matter is seen in a semiconductor device that includes a recess defined in a dielectric layer, the recess having upper and lower sidewall portions, wherein the upper sidewall portion extends to an upper corner of the recess. The semiconductor device also includes an interconnect structure that is positioned in the recess. The interconnect structure includes, among other things, a barrier layer and a continuous liner layer having upper and lower liner portions that are positioned adjacent to the respective upper and lower sidewall portions, wherein the upper liner portion is a layer of alloyed titanium and ruthenium and the lower liner portion is a layer of ruthenium that does not include titanium. Furthermore, the interconnect structure of the disclosed semiconductor device includes a copper-containing fill material positioned on and in contact with the continuous liner layer and substantially filling the recess.

BRIEF DESCRIPTION OF THE SEVERAL VIEWS OF THE DRAWINGS

The disclosed subject matter will hereafter be described with reference to the accompanying drawings, wherein like reference numerals denote like elements, and:

FIG. 1 is a cross section view of a partially completed interconnect structure;

FIG. 2 is a cross-section view of the structure of FIG. 1 illustrating the formation of a barrier layer;

FIG. 3 is a cross-section view of the structure of FIG. 2 illustrating the formation of a transition metal layer at corners of the interconnect structure;

FIG. 4 is a cross-section view of the structure of FIG. 3 illustrating the formation of a ruthenium layer;

FIG. 5 is a cross-section view of the structure of FIG. 4 illustrating a copper fill process;

FIG. 6 is a cross-section view of the structure of FIG. 5 illustrating a copper anneal process to form alloy regions at the corners; and

FIG. 7 is a cross-section view of the structure of FIG. 6 illustrating a polishing process to remove excess copper and recess the copper at the corners.

While the disclosed subject matter is susceptible to various modifications and alternative forms, specific embodiments thereof have been shown by way of example in the drawings and are herein described in detail. It should be understood, however, that the description herein of specific embodiments is not intended to limit the disclosed subject matter to the particular forms disclosed, but on the contrary, the intention is to cover all modifications, equivalents, and alternatives falling within the spirit and scope of the disclosed subject matter as defined by the appended claims.

DETAILED DESCRIPTION

One or more specific embodiments of the disclosed subject matter will be described below. It is specifically intended that the disclosed subject matter not be limited to the embodiments and illustrations contained herein, but include modified forms of those embodiments including portions of the embodiments and combinations of elements of different embodiments as come within the scope of the following claims. It should be appreciated that in the development of any such actual implementation, as in any engineering or design project, numerous implementation-specific decisions must be made to achieve the developers' specific goals, such as compliance with system-related and business related constraints, which may vary from one implementation to another. Moreover, it should be appreciated that such a development effort might be complex and time consuming, but would nevertheless be a routine undertaking of design, fabrication, and manufacture for those of ordinary skill having the benefit of this disclosure. Nothing in this application is considered critical or essential to the disclosed subject matter unless explicitly indicated as being “critical” or “essential.”

The disclosed subject matter will now be described with reference to the attached figures. Various structures, systems and devices are schematically depicted in the drawings for purposes of explanation only and so as to not obscure the disclosed subject matter with details that are well known to those skilled in the art. Nevertheless, the attached drawings are included to describe and explain illustrative examples of the disclosed subject matter. The words and phrases used herein should be understood and interpreted to have a meaning consistent with the understanding of those words and phrases by those skilled in the relevant art. No special definition of a term or phrase, i.e., a definition that is different from the ordinary and customary meaning as understood by those skilled in the art, is intended to be implied by consistent usage of the term or phrase herein. To the extent that a term or phrase is intended to have a special meaning, i.e., a meaning other than that understood by skilled artisans, such a special definition will be expressly set forth in the specification in a definitional manner that directly and unequivocally provides the special definition for the term or phrase.

Referring now to the drawings wherein like reference numbers correspond to similar components throughout the several views and, specifically, referring to FIGS. 1, the disclosed subject matter shall be described in the context of a method for fabricating an interconnect structure. FIG. 1 is a cross-section view of a partially completed interconnect structure 10. A dielectric layer 20 has been provided on a substrate 25. The dielectric layer may represent an interlayer dielectric layer disposed between a device layer or metallization layer and another metallization layer. In one embodiment, the dielectric layer 20 may have a low dielectric coefficient, commonly referred to as a low-k dielectric. One such suitable low-k dielectric material is Black Diamond, offered by Applied Materials, Inc. A hard mask layer 30 is formed to provide a template for etching a recess 40. In the illustrated embodiment, the recess 40 is a trench in which an interconnect line feature is being formed, however, the methods described herein may also be applied to other types of interconnects, such as via structures or dual damascene trench and via structures, where an underlying metal region is being contacted by the interconnect feature. Hence, the recess 40 may be a trench, a via opening, or a combined trench and via opening.

As illustrated in FIG. 2, a barrier layer 50 is formed to line the recess 40. The barrier layer 50 serves to constrain the copper used to eventually fill the recess 40 so that it does not move into the dielectric layer 20. Exemplary barrier materials include tantalum nitride (TaN), which may be formed by physical vapor deposition (PVD) or atomic layer deposition (ALD) processes known in the art.

As illustrated in FIG. 3, a first transition metal layer 60 is formed on upper corners 70 of the recess 40 above the barrier layer 50. Exemplary transition metals could include any element in the d-block of the periodic table, which includes groups 3 to 12 on the periodic table. In the illustrated embodiment, titanium (Ti) is used to form the first transition metal layer 60. A plasma assisted PVD process may be employed without a bias voltage to form the first transition metal layer 60 on the corners 70. In some embodiments, a CVD process may be employed as an alternative to the PVD process. Because of the aspect ratio of the recess 40, the transition metal layer 60 does not substantially cover the sidewall or bottom portions of the recess 40. Stray particles of the transition metal may be formed on the sidewall or bottom portions, but due to the lack of bias voltage to attract the particles to the bottom, the transition metal layer 60 is concentrated at the corners 70. In one embodiment, the thickness of the transition metal layer 60 is about 5 to 30 angstroms.

A second transition metal layer 80 (i.e., any of the d-block metals) having a copper wettability greater than the first transition metal layer 60 is formed using a chemical vapor deposition process in FIG. 4. In the illustrated embodiment, the second transition metal layer is ruthenium (Ru), but other transition metals having relatively high wettabilities that may be used are osmium, rhodium, palladium, platinum, iridium, and niobium. In one embodiment, the thickness of the second transition metal layer 80 is about 10 to 25 angstroms.

The second transition metal layer 80 fully lines the recess 40, and provides a wettable surface for a subsequent copper fill. In FIG. 5, a copper seed layer (not visible) is formed and the bulk copper fill is performed to form copper fill layer 90.

In FIG. 6, an anneal process is performed to realign the grain boundaries and increase the grain size of the copper layer 90. During the anneal process, the first transition metal layer 60 forms an alloy layer 100 in the corner regions 70 with the second transition metal layer 80. In one embodiment, the anneal may be performed at temperatures between about 100-400 ° C. for about 0.5 to 2.0 hr. Subsequently, a chemical mechanical polishing (CMP) process is performed to remove excess copper fill material 90. During the polishing process the horizontal portions of the alloy layer 100, the barrier layer 50, and the hard mask layer 30 are removed, resulting in the structure shown in FIG. 7.

The alloy layer 100 has a reduced wettability as compared to the second transition metal layer 80. The first transition metal in the alloy layer 100 forms an oxide at the corner interface (e.g., TiO_x). The oxide causes the copper layer 90 to dewet at the corner interface 70. Crevices 110 are generated at the corners 70 due to the stress assisted etch used to perform the CMP process, thereby recessing the copper 90 at the corners 70. The crevices 110 isolate the copper 90 from the triple point of the interconnect structure 10

The use of the second transition metal layer 80 allows an improved copper fill by increasing wettability. The formation of the alloy layer 100 during the copper anneal provides reduced wettability in the corner regions 70 during the CMP process, thereby recessing the copper 90. The recessed copper 90 improves the time-dependent dielectric breakdown (TDDB) reliability of the interconnect structure 10, because the poor copper wettability at the trench edge retards copper diffusion to the dielectric surface, which degrades reliability.

The particular embodiments disclosed above are illustrative only, as the disclosed subject matter may be modified and practiced in different but equivalent manners apparent to those skilled in the art having the benefit of the teachings herein. Furthermore, no limitations are intended to the details of construction or design herein shown, other than as described in the claims below. It is therefore evident that the particular embodiments disclosed above may be altered or modified and all such variations are considered within the scope and spirit of the disclosed subject matter. Accordingly, the protection sought herein is as set forth in the claims below.

Claims

1. A semiconductor device, comprising: a recess defined in a dielectric layer, said recess having an upper sidewall portion extending to an upper corner of said recess and a lower sidewall portion positioned below said upper sidewall portion; andan interconnect structure positioned in said recess, said interconnect structure comprising: a continuous liner layer comprising a sidewall layer portion having an upper sidewall layer portion positioned laterally adjacent to and extending along said upper sidewall portion of said recess and a lower sidewall layer portion positioned laterally adjacent to and extending along said lower sidewall portion of said recess such that an upper end of said lower sidewall layer portion forms an interface with a lower end of said upper sidewall layer portion, wherein said upper sidewall layer portion comprises an alloy of a first transition metal and a second transition metal and said lower sidewall layer portion comprises said second transition metal but not said first transition metal; anda fill material substantially filling said recess, wherein said second transition metal has a higher wettability for said fill material than said alloy.

2. The semiconductor device of claim 1, wherein said continuous liner layer is positioned between said fill material and said dielectric layer.

3. The semiconductor device of claim 1, wherein said interconnect structure further comprises a barrier layer positioned between said continuous liner layer and said dielectric layer.

4. The semiconductor device of claim 3, wherein said barrier layer comprises tantalum nitride.

5. The semiconductor device of claim 3, wherein said continuous liner layer is positioned on and in direct contact with said barrier layer.

6. The semiconductor device of claim 1, wherein said second transition metal comprises ruthenium.

7. The semiconductor device of claim 6, wherein said first transition metal comprises titanium.

8. The semiconductor device of claim 1, wherein said fill material comprises copper.

9. The semiconductor device of claim 1, wherein said dielectric layer comprises a low-k dielectric material.

10. The semiconductor device of claim 1, wherein an upper end of said upper sidewall layer portion is substantially flush with an upper surface of said dielectric layer.

11. The semiconductor device of claim 10, wherein an upper surface of said fill material is substantially flush with said upper end of said upper sidewall layer portion and said upper surface of said dielectric layer.

12. The semiconductor device of claim 1, wherein said upper and lower sidewall portions of said recess comprise a substantially vertically oriented continuous sidewall portion of said recess, said upper and lower sidewall layer portions of said continuous liner layer comprise a substantially vertically oriented continuous sidewall layer portion, and said upper sidewall layer portion is positioned vertically above said lower sidewall layer portion.

13. A semiconductor device, comprising: a recess defined in a dielectric layer, said recess having upper and lower sidewall portions, said upper sidewall portion extending to an upper corner of said recess; andan interconnect structure positioned in said recess, said interconnect structure comprising: a barrier layer;a continuous liner layer comprising a sidewall layer portion having an upper sidewall liner portion positioned adjacent to and extending along said upper sidewall portion of said recess and a lower sidewall liner portion positioned laterally adjacent to and extending along said lower sidewall portion of said recess such that an upper end of said lower sidewall liner portion forms an interface with a lower end of said upper sidewall liner portion, wherein said upper sidewall liner portion is a layer of alloyed titanium and ruthenium and said lower sidewall liner portion is a layer of ruthenium that does not comprise titanium; anda copper-containing fill material positioned on and in contact with said continuous liner layer and substantially filling said recess.

14. The semiconductor device of claim 13, wherein said barrier layer comprises tantalum nitride.

15. The semiconductor device of claim 13, wherein said barrier layer is positioned between said dielectric layer and said continuous liner layer and said continuous liner layer is positioned between said barrier layer and said copper-containing fill material.

16. The semiconductor device of claim 13, wherein a thickness of said upper liner portion adjacent to said upper corner of said recess is greater than a thickness of said lower liner portion.

17. The semiconductor device of claim 13, wherein said dielectric layer comprises a low-k dielectric material.

18. The semiconductor device of claim 13, wherein an upper end of said upper sidewall liner portion is substantially flush with an upper surface of said dielectric layer.

19. The semiconductor device of claim 18, wherein an upper end of said barrier layer and an upper surface of said copper-containing fill material are substantially flush with said upper end of said upper sidewall liner portion and said upper surface of said dielectric layer.

20. The semiconductor device of claim 13, wherein said upper and lower sidewall portions of said recess comprise a substantially vertically oriented continuous sidewall portion of said recess, said upper and lower sidewall liner portions of said continuous liner layer comprise a substantially vertically oriented continuous sidewall liner portion, and said upper sidewall liner portion is positioned vertically above said lower sidewall liner portion.