Claims
- 1. A method of making a porous polishing pad material for a polishing pad, the method comprising electrophoretic deposition by immersing spaced apart electrodes in a bath, and while mixing the bath, impressing the electrodes with controlled electrical conditions, the method further comprising the steps of:immersing spaced apart electrodes in a bath having polymeric particles and water; impressing the electrodes with the controlled electrical conditions that consist of, a controlled voltage difference across the electrodes, and 4 controlled current flow through the electrodes; depositing the polymeric particles on one of the electrodes to form a polymeric mass while generating gaseous bubbles within the polymeric mass, which bubbles open at an exterior surface of the polymeric mass to provide a porous polishing pad material having pores therein that open at an exterior polishing surface on the polishing pad material; and varying one of the controlled electrical conditions over a time duration as a thickness of the polymeric mass increases to increase the lengths of the bubbles transverse to the thickness of the polymeric mass.
- 2. The method as recited in claim 1, wherein the step of impressing the electrodes with controlled electrical conditions further includes the step of, connecting the electrodes to a power supply apparatus that supplies the controlled electrical conditions.
- 3. The method as recited in claim 1, wherein the step of immersing spaced apart electrodes in a bath having polymeric particles and water, further includes the step of immersing the spaced apart electrodes in a bath having abrasive particles; andwherein the step of depositing the polymeric particles on one of the electrodes to form a polymeric mass while generating gaseous bubbles within the polymeric mass, further includes the step of, depositing the polymeric particles on one of the electrodes to form a polymeric mass having abrasive particles within the polymeric mass.
- 4. The method as recited in claim 1, and further comprising the step of: maintaining another of the controlled electrical conditions constant while varying said one of the controlled electrical conditions to increase the lengths of the bubbles as the thickness of the polymeric mass increases.
- 5. The method as recited in claim 4, wherein the step of maintaining another of the controlled electrical conditions constant further includes the step of, maintaining the controlled voltage difference across the electrodes constant while decreasing the controlled current flow through the electrodes over a time duration as the thickness of the polymeric mass increases to increase the lengths of the bubbles transverse to the thickness of the polymeric mass.
- 6. The method as recited in claim 1, wherein the step of varying one of the controlled electrical conditions further includes the step of: decreasing the controlled current flow through the electrodes over a time duration as the thickness of the polymeric mass increases to increase the lengths of the bubbles transverse to the thickness of the polymeric mass.
- 7. The method as recited in claim 6, wherein the step of impressing the electrodes with controlled electrical conditions further includes the step of, connecting the electrodes to a power supply apparatus that supplies the controlled electrical conditions.
- 8. The method as recited in claim 6, wherein the step of immersing spaced apart electrodes in a bath having polymeric particles and water, further includes the step of immersing the spaced apart electrodes in a bath having abrasive particles; andwherein the step of depositing the polymeric particles on one of the electrodes to form a polymeric mass while generating gaseous bubbles within the polymeric mass, further includes the step of, depositing the polymeric particles on one of the electrodes to form a polymeric mass having abrasive particles within the polymeric mass.
- 9. The method as recited in claim 6, and further comprising the step of: maintaining another of the controlled electrical conditions constant while decreasing the controlled current flow through the electrodes over a time duration as the thickness of the polymeric mass increases to increase the lengths of the bubbles transverse to the thickness of the polymeric mass.
- 10. The method as recited in claim 7, wherein the step of maintaining another of the controlled electrical conditions constant further includes the step of, maintaining the controlled voltage difference across the electrodes constant.
- 11. The method as recited in claim 1, wherein the step of varying one of the controlled electrical conditions further includes the step of, increasing the controlled voltage difference across the electrodes over a time duration as the thickness of the polymeric mass increases to increase the lengths of the bubbles transverse to the thickness of the polymeric mass.
- 12. The method as recited in claim 11, wherein the step of impressing the electrodes with controlled electrical conditions further includes the step of, connecting the electrodes to a power supply apparatus that supplies the controlled electrical conditions.
- 13. The method as recited in claim 11, wherein the step of immersing spaced apart electrodes in a bath having polymeric particles and water, further includes the step of immersing the spaced apart electrodes in a bath having abrasive particles; andwherein the step of depositing the polymeric particles on one of the electrodes to form a polymeric mass while generating gaseous bubbles within the polymeric mass, further includes the step of, depositing the polymeric particles on one of the electrodes to form a polymeric mass having abrasive particles within the polymeric mass.
- 14. The method as recited in claim 11, and further comprising the step of: maintaining another of the controlled electrical conditions constant while increasing the controlled voltage difference across the electrodes over a time duration as the thickness of the polymeric mass increases to increase the lengths of the bubbles transverse to the thickness of the polymeric mass.
- 15. The method as recited in claim 14, wherein the step of maintaining another of the controlled electrical conditions constant, further includes the step of, maintaining the controlled current flow through the electrodes constant while increasing the controlled voltage across the electrodes over a time duration as the thickness of thc polymeric mass increases to increase the lengths of the bubbles transverse to the thickness of the polymeric mass.
Parent Case Info
This application is a Continuation-in-part of U.S. application Ser. No. 09/162,595 filed Sep. 29, 1998, now abandoned, which claims the benefit of U.S. Provisional Applications Nos. 60/060,294 and 60/060,295 filed Sep. 29, 1997.
US Referenced Citations (7)
Non-Patent Literature Citations (1)
Entry |
“Development of Highly Homogeneous Pellets Applying Electrophoretic Deposition of Ultrafine Abrasives for Nanometer Grinding”, Junichi Ikeno, Yashuhiro Tani, Hisayosi Sato, Annals of the CIRP Vol. 43.1.1994, pp 319-322. No month avail. |
Provisional Applications (2)
|
Number |
Date |
Country |
|
60/060294 |
Sep 1997 |
US |
|
60/060295 |
Sep 1997 |
US |
Continuation in Parts (1)
|
Number |
Date |
Country |
Parent |
09/162595 |
Sep 1998 |
US |
Child |
09/536189 |
|
US |