Information
-
Patent Grant
-
6815265
-
Patent Number
6,815,265
-
Date Filed
Thursday, July 25, 200222 years ago
-
Date Issued
Tuesday, November 9, 200419 years ago
-
Inventors
-
Original Assignees
-
Examiners
Agents
- McDermott, Will & Emery LLP
-
CPC
-
US Classifications
Field of Search
US
- 257 529
- 257 643
- 257 758
- 438 132
- 438 622
- 438 725
- 438 82
- 438 215
- 438 281
- 438 333
-
International Classifications
-
Abstract
An uppermost interlayer isolation film is provided on a semiconductor substrate. An uppermost wire is provided on the uppermost interlayer isolation film. A silicon oxide film is provided to cover the upper surface and the side wall of the uppermost wire. A nitride film is provided on the uppermost interlayer isolation film to cover the uppermost wire through the silicon oxide film. A polyimide film is provided on the nitride film. A portion of the uppermost interlayer isolation film other than a portion located under the uppermost wire is downwardly scooped. The nitride film covers the scooped portion of the uppermost interlayer isolation film. According to the present invention, a semiconductor device improved to be capable of improving coverage of a silicon nitride passivation film is obtained.
Description
BACKGROUND OF THE INVENTION
1. Field of the Invention
The present invention generally relates to a semiconductor device, and more specifically, it relates to a semiconductor device having a passivation film relieved of stress applied to wiring capacity and a wire. The present invention also relates to a method of fabricating such a semiconductor device.
2. Description of the Background Art
In order to protect a semiconductor device, a passivation film is formed on the surface of the semiconductor device.
In general, a two-layer passivation film of SiO
2
and SiN is employed for relaxing stress applied to wiring capacity and a wire.
A method of fabricating a semiconductor device employing such a two-layer passivation film is now described.
Referring to
FIG. 11
, a fuse
2
is formed on a semiconductor substrate
1
. The fuse
2
is employed for redundancy of a memory cell, for example. The function of this fuse
2
is described later. The fuse
2
is made of polysilicon or Al.
Referring to
FIG. 12
, an uppermost interlayer isolation film
3
is formed on the semiconductor substrate
1
to cover the fuse
2
. An uppermost wire
4
of a bimetal is formed on the uppermost interlayer isolation film
3
.
Referring to
FIG. 13
, a silicon oxide film
5
is formed on the uppermost interlayer isolation film
3
by a plasma method to cover the uppermost wire
4
. The plasma method is employed since the uppermost wire
4
is dissolved due to a high temperature if the silicon oxide film
5
is formed by a method other than the plasma method. Therefore, only the plasma method can be employed for forming the silicon oxide film
5
in this case.
Referring to
FIGS. 13 and 14
, the silicon oxide film
5
is etched back and partially left only on the side walls and the upper surface of the uppermost wire
4
. Thereafter a nitride film
6
is formed on the semiconductor substrate
1
.
Referring to
FIG. 15
, a polyimide film
7
is formed on the nitride film
6
.
Referring to
FIG. 16
, the fuse
2
is cut by laser blowing, and hence the portion of the uppermost interlayer isolation film
3
located on the fuse
2
must be reduced in thickness.
Therefore, a hole
8
for introducing a laser beam is formed to pass through portions of the polyimide film
7
and the nitride film
6
located above the fuse
2
, as shown in FIG.
16
.
Referring to
FIG. 17
, the surface of the uppermost interlayer isolation film
3
is partially etched through the hole
8
for optimizing the thickness of the portion of the uppermost interlayer isolation film
3
located on the fuse
2
. Thereafter the fuse
2
is cut by laser blowing, thereby completing the semiconductor device.
FIG. 18
illustrates a problem caused when the thickness of the portion of the uppermost interlayer isolation film
3
located on the fuse
2
is not optimized. If the thickness of the portion of the uppermost interlayer isolation film
3
located on the fuse
2
is left intact, the laser beam for cutting the fuse
2
is so increased in energy that the same disadvantageously cuts an adjacent fuse
2
a
not to be cut, leading to a failure in formation of the target semiconductor device. Therefore, the thickness of the portion of the uppermost interlayer isolation film
3
located on the fuse
2
must be reduced and optimized.
The conventional semiconductor device including the fuse
2
is fabricated in the aforementioned manner.
Referring again to
FIG. 13
, the nitride film
6
is formed by plasma CVD (chemical vapor deposition), disadvantageously leading to inferior coverage.
When the uppermost wire
4
is formed adjacently to another uppermost wire
4
a
as shown in FIG.
19
and the nitride film
6
is formed by plasma CVD, a cavity
9
is defined due to inferior coverage to disadvantageously reduce the reliability of the semiconductor device.
SUMMARY OF THE INVENTION
The present invention has been proposed in order to solve the aforementioned problem, and an object thereof is to provide a method of fabricating a semiconductor device improved to be capable of forming a nitride film on an uppermost wire with excellent coverage.
Another object of the present invention is to provide a highly reliable method of fabricating a semiconductor device through the same number of steps as the prior art with no requirement for additional steps.
Still another object of the present invention is to provide a method of fabricating a semiconductor device improved to be capable of optimizing the thickness of a portion of an uppermost interlayer isolation film located on a fuse with no requirement for additional steps.
A further object of the present invention is to provide a highly reliable semiconductor device obtained by such a method.
A semiconductor device according to a first aspect of the present invention comprises a semiconductor substrate. An uppermost interlayer isolation film is provided on the aforementioned semiconductor substrate. An uppermost wire is provided on the aforementioned uppermost interlayer isolation film. A silicon oxide film is provided to cover the upper surface and the side wall of the aforementioned uppermost wire. A nitride film is provided on the aforementioned uppermost interlayer isolation film to cover the aforementioned uppermost wire through the aforementioned silicon oxide film. A polyimide film is provided on the aforementioned nitride film. A portion of the aforementioned uppermost interlayer isolation film other than portions located under the aforementioned uppermost wire and on the side wall of the aforementioned silicon oxide film is downwardly scooped. The aforementioned nitride film covers the scooped portion of the aforementioned uppermost interlayer isolation film.
In a method of fabricating a semiconductor device according to a second aspect of the present invention, an uppermost interlayer isolation film of SiO
2
is first formed on a semiconductor substrate. An uppermost wire is formed on the aforementioned uppermost interlayer isolation film. A silicon oxide film is formed on the aforementioned uppermost interlayer isolation film by a plasma method, to cover the aforementioned uppermost wire. The aforementioned silicon oxide film is etched back for downwardly scooping a portion of the aforementioned uppermost interlayer isolation film other than portions located under the aforementioned uppermost wire and on the side wall of the aforementioned silicon oxide film. A nitride film is formed on the aforementioned uppermost interlayer isolation film to cover the surface of the aforementioned scooped portion. A polyimide film is formed on the aforementioned nitride film.
The foregoing and other objects, features, aspects and advantages of the present invention will become more apparent from the following detailed description of the present invention when taken in conjunction with the accompanying drawings.
BRIEF DESCRIPTION OF THE DRAWINGS
FIG. 1
shows a flow according to the present invention and a flow according to the prior art in comparison with each other;
FIGS. 2
to
6
are sectional views showing first to fifth steps in a method of fabricating a semiconductor device according to a first embodiment of the present invention;
FIG. 7
is a plan view of a semiconductor device according to a second embodiment of the present invention;
FIG. 8
illustrates a fuse, a pad and a dicing line in the semiconductor device according to the second embodiment of the present invention;
FIGS. 9 and 10
are first and second diagrams for illustrating a function of a fuse according to a third embodiment of the present invention;
FIGS. 11
to
17
are sectional views showing first to seventh steps in a conventional method of fabricating a semiconductor device;
FIG. 18
illustrates a problem caused when the thickness of a portion of an uppermost interlayer isolation film located on a fuse is not optimized; and
FIG. 19
illustrates a problem in the conventional method of fabricating a semiconductor device.
DESCRIPTION OF THE PREFERRED EMBODIMENTS
Embodiments of the present invention are now described.
First Embodiment
FIG. 1
illustrates a flow according to the present invention and a conventional flow in comparison with each other. In the inventive flow, an oxide film etching step is inserted between a plasma CVD SiO
2
deposition step and a plasma CVD nitride film deposition step, dissimilarly to the conventional flow.
A first embodiment of the present invention is now specifically described with reference to
FIGS. 2
to
6
.
Referring to
FIG. 2
, a fuse
2
is formed on a semiconductor substrate
1
. An uppermost interlayer isolation film
3
of SiO
2
is formed on the semiconductor substrate
1
to cover the fuse
2
. An uppermost wire
4
is formed on the uppermost interlayer isolation film
3
.
Referring to
FIG. 3
, a silicon oxide film
5
is formed on the uppermost interlayer isolation film
3
by plasma CVD, to cover the uppermost wire
4
.
Referring to
FIGS. 3 and 4
, the silicon oxide film
5
is etched back. At this time, the silicon oxide film
5
is so etched back as to downwardly scoop a potion of the uppermost interlayer isolation film
3
other than that located under the uppermost wire
4
. This etching is so performed as to optimize the thickness t of the portion of the uppermost interlayer isolation film
3
located on the fuse
2
. The shapes of the shoulder portions of the silicon oxide film
5
are smoothed due to the effect of this etching.
Referring to
FIG. 5
, a nitride film
6
is deposited on the uppermost interlayer isolation film
3
by plasma CVD, to cover the surface of the scooped portion. At this time, the nitride film
6
is formed on the uppermost interlayer isolation film
3
with excellent coverage due to the smoothed shapes of the shoulder portions of the silicon oxide film
5
. A polyimide film
7
is formed on the nitride film
6
.
Referring to
FIG. 6
, portions of the nitride film
6
and the polyimide film
7
located on the fuse
2
are removed by etching, for forming a hole
3
. The thickness t of the portion of the uppermost interlayer isolation film
3
located on the fuse
2
is optimized, and hence this portion of the uppermost interlayer isolation film
3
may not be etched.
Then, the fuse
2
is laser-blown through the hole
8
, thereby completing a semiconductor device.
Second Embodiment
FIG. 7
is a plan view of a semiconductor device according to a second embodiment of the present invention. The semiconductor device according to this embodiment comprises a chip
10
and a pad
11
. Dicing lines
12
are provided on a semiconductor substrate.
A method of fabricating the semiconductor device according to this embodiment further comprises a step of forming the pad
11
and the dicing lines
12
on the semiconductor substrate. In a step similar to that shown in
FIG. 6
, portions of a nitride film
6
and a polyimide film
7
located on a fuse
2
are removed by etching. At this time, portions of the nitride film
6
and the polyimide film
7
located on the pad
11
and on the dicing lines
12
are removed by etching while simultaneously removing the portions of the nitride film
6
and the polyimide film
7
located on the fuse
2
by etching. Then, an electrode is connected to the pad
11
, and dicing is performed through the dicing lines
12
. The fuse
2
is cut by laser blowing. Thus, a semiconductor chip is completed.
Third Embodiment
FIG. 9
is a diagram for illustrating a function of a fuse according to a third embodiment of the present invention. Referring to
FIG. 9
, extra memory cells are prepared by α when forming a memory cell array having capacity of 32 M.
Referring to
FIG. 10
, it is assumed that a memory cell
13
fails. In this case, a fuse
2
connected to the failing memory cell
13
is cut by laser blowing. A data line is connected to an additionally prepared redundancy memory cell
14
. Thus, the chip is not entirely rendered defective by the failure of the memory cell
13
. Consequently, the yield is effectively improved.
According to the present invention, as hereinabove described, coverage of a silicon nitride passivation film can be improved while the thickness of a portion of an interlayer isolation film located on a fuse can be controlled.
Although the present invention has been described and illustrated in detail, it is clearly understood that the same is by way of illustration and example only and is not to be taken by way of limitation, the spirit and scope of the present invention being limited only by the terms of the appended claims.
Claims
- 1. A method of fabricating a semiconductor device, comprising the sequential steps of:forming an uppermost interlayer isolation film of SiO2 on a semiconductor substrate; forming an uppermost wire, having an upper surface and side surfaces, on an upper surface of said uppermost interlayer isolation film; forming a silicon oxide film on said uppermost interlayer isolation film by a plasma method to cover said uppermost wire; etching said silicon oxide film to form an etched back film of silicon oxide covering the upper surface and side surfaces of said uppermost wire and continuing etching to remove a portion of the upper surface of said uppermost interlayer isolation film not located under said uppermost wire and not under the etched back silicon oxide film; forming a nitride film on said uppermost interlayer isolation film to cover the etched interlayer isolation film; and forming a polyimide film on said nitride film.
- 2. The method of fabricating a semiconductor device according to claim 1, further comprising a step of forming a fuse on said semiconductor substrate in advance of said step of forming said uppermost interlayer isolation film, whereinsaid uppermost interlayer isolation film is formed to cover said fuse.
- 3. The method of fabricating a semiconductor device according to claim 2, further comprising a step of removing portions of said nitride film and said polyimide film located on said fuse by etching.
- 4. The method of fabricating a semiconductor device according to claim 2, comprisingconducting said etching to optimize the thickness of a portion of said uppermost interlayer isolation film located on said fuse.
- 5. The method of fabricating a semiconductor device according to claim 4, further comprising a step of forming a pad and a dicing line on said semiconductor substrate, andfurther comprising etching to simultaneously remove portions of said nitride film and said polyimide film located on said pad, on said fuse and on said dicing line.
Priority Claims (1)
Number |
Date |
Country |
Kind |
2002-025015 |
Feb 2002 |
JP |
|
US Referenced Citations (5)
Number |
Name |
Date |
Kind |
4928161 |
Kobayashi |
May 1990 |
A |
5508540 |
Ikeda et al. |
Apr 1996 |
A |
6291837 |
Nakajima et al. |
Sep 2001 |
B1 |
6294474 |
Tzeng et al. |
Sep 2001 |
B1 |
6372554 |
Kawakita et al. |
Apr 2002 |
B1 |
Foreign Referenced Citations (1)
Number |
Date |
Country |
2000077677 |
Mar 2000 |
JP |