Claims
- 1. A method of fabricating a field effect transistor with an LDD structure comprising the steps of:
- forming a gate insulating film on an active region on a surface of a semiconductor substrate;
- selectively covering said gate insulating film to form a gate electrode including a high melting-point metal silicide film;
- forming a thermal oxide film on a top surface and a side surface of said gate electrode with said active region covered completely by said gate insulating film;
- forming a low-concentration source and drain region in said active region by first ion injection;
- depositing a first insulating film and performing anisotropic etching to form an insulating spacer on said side surface of said gate electrode and expose said top surface of said gate electrode and said low-concentration source and drain region; and
- depositing a second insulating film for covering said top surface of said gate electrode and said low-concentration source and drain region exposed by said anisotropic etching and then forming a high-concentration source and drain region in said active region by second ion injection.
- 2. A method of fabricating a field effect transistor with an LDD structure comprising the steps of:
- forming a device-forming area in a surface portion of a semiconductor substrate to define a first active region and a second active region;
- forming a first gate insulating film and a second gate insulating film respectively on surfaces of said first active region and said second active region;
- selectively covering said first gate insulating film and said second gate insulating film to form a first gate electrode and a second gate electrode each including a high melting-point metal silicide film;
- forming thermal oxide films on top and side surfaces of said first gate electrode and said second gate electrode, with said first active region and said second active region covered completely by said first gate insulating film and said second gate insulating film, respectively;
- forming a low-concentration source and drain region in both said first and second active regions by first ion injection;
- depositing a first insulating film and performing anisotropic etching to form an insulating spacer on said side surfaces of said first and second gate electrodes and expose said top surface of said gate electrodes and said low-concentration source and drain region;
- depositing a second insulating film for covering said top surface of said gate electrodes and said low-concentration source and drain region exposed by said anisotropic etching; and
- covering said second active region with a mask and then performing second ion injection to form a high-concentration source and drain region in said first active region.
- 3. The method according to claim 1, further comprising the steps of:
- coating an amorphous high-melting point silicide film containing stoichiometric silicon rich silicide; and
- patterning said amorphous high-melting point silicide film to form a gate electrode which is polycrystallized at a time of forming a thermal oxide film.
- 4. The method according to claim 2, further comprising the steps of:
- coating an amorphous high-melting point silicide film containing stoichiometric silicon rich silicide; and
- patterning said amorphous high-melting point silicide film to form a gate electrode which is polycrystallized at a time of forming a thermal oxide film.
- 5. The method according to claim 1, wherein said gate electrode is a polycide gate electrode.
- 6. The method according to claim 2, wherein said gate electrodes are a polycide gate electrode.
- 7. The method according to claim 1, wherein said step of selectively covering said gate insulating film to form a gate electrode includes the steps of:
- forming a polycrystalline silicon film doped with phosphorous by chemical vapor deposition;
- forming an amorphous high-melting point silicide film containing stoichiometric silicon rich refractory metal silicide;
- etching said amorphous high-melting point silicide film with a gas mixture of SF.sub.6, HBr and He; and
- etching said polycrystalline silicon film with a gas mixture of CI.sub.2 and HBr.
- 8. The method according to claim 2, wherein said step of selectively covering said first gate insulating film and said second gate insulating film includes the steps of:
- forming a polycrystalline silicon film doped with phosphorous by chemical vapor deposition;
- forming an amorphous high-melting point silicide film containing stoichiometric silicon rich refractory metal silicide;
- etching said amorphous high-melting point silicide film with a gas mixture of SF.sub.6, HBr and He; and
- etching said polycrystalline silicon film with a gas mixture of CI.sub.2 and HBr.
- 9. A method of fabricating a field effect transistor with an LDD structure comprising the steps of:
- forming a gate insulating film on an active region on a surface of a semiconductor substrate;
- selectively covering said gate insulating film to form a gate electrode including a high melting-point metal silicide film;
- forming a thermal oxide film on a top surface and a side surface of said gate electrode with said active region covered completely by said gate insulating film;
- forming a low-concentration source and drain region in said active region by first ion injection;
- depositing a first insulating film on said thermal oxide film and said low-concentration source and drain;
- anisotropically etching said first insulator to form an insulating spacer on said side surface of said gate electrode and expose said top surface of said gate electrode and said low-concentration source and drain region;
- depositing a second insulating film for covering said top surface of said gate electrode and said low-concentration source and drain region exposed by said anisotropic etching; and
- forming a high-concentration source and drain region in said active region by second ion injection.
- 10. The method according to claim 9, further comprising the steps of:
- coating an amorphous high-melting point silicide film containing stoichiometric silicon rich refractory metal silicide; and
- patterning said amorphous high-melting point silicide film to form a gate electrode which is polycrystallized at a time of forming a thermal oxide film.
- 11. The method according to claim 10, wherein said step of selectively covering said gate insulating film to form a gate electrode includes the steps of:
- forming a polycrystalline silicon film doped with phosphorous by chemical vapor deposition;
- forming an amorphous high-melting point silicide film containing stoichiometric silicon rich refractory metal silicide;
- etching said amorphous high-melting point silicide film with a gas mixture of SF.sub.6, HBr and He; and
- etching said polycrystalline silicon film with a gas mixture of CI.sub.2 and HBr.
- 12. A method of fabricating a lightly doped diffusion (LDD) field effect transistor structure comprising the steps of:
- depositing a first insulating film over an entire transistor active region having a gate insulating layer, a silicide gate electrode covered by an oxide film, and a low-concentration source and drain region;
- anisotropically etching said first insulating film to form an insulating spacer on a side surface and a top surface of said silicide gate electrode, and expose said top surface of said silicide gate electrode and said low-concentration source and drain region;
- depositing a second insulating film on said top surface of said silicide gate electrode and said low-concentration source and drain region exposed by said anisotropic etching; and
- forming a high-concentration source and drain region in said transistor active region by ion injection after said step of depositing a second insulating film.
- 13. The method according to claim 1, wherein said second insulating film is deposited by chemical vapor deposition (CVD).
- 14. The method according to claim 2, wherein said second insulating film is deposited by chemical vapor deposition (CVD).
- 15. The method according to claim 9, wherein said second insulating film is deposited by chemical vapor deposition (CVD).
- 16. The method according to claim 12, wherein said second insulating film is deposited by chemical vapor deposition (CVD).
Priority Claims (1)
Number |
Date |
Country |
Kind |
7-075127 |
Mar 1995 |
JPX |
|
Parent Case Info
This is a Continuation of application Ser. No. 08/626,019 filed Apr. 1, 1996 now abandoned.
US Referenced Citations (5)
Non-Patent Literature Citations (2)
Entry |
Wolf et al., "Silicon Processing for the VLSI Era vol. 1: Process Technology", pp. 323-325, Lattice Press, 1986. |
Seiki Ogura et al, "Elimination of Hot Electron Gate Current by the Lightly Doped Drain-Source Structure", International Electron Device Meeting (IEDM) Technical Dsigest, 1981, pp. 651-654. |
Continuations (1)
|
Number |
Date |
Country |
Parent |
626019 |
Apr 1996 |
|