Method of forming a catalyst with inhibited mobility of nano-active material

Information

  • Patent Grant
  • 8557727
  • Patent Number
    8,557,727
  • Date Filed
    Tuesday, December 7, 2010
    13 years ago
  • Date Issued
    Tuesday, October 15, 2013
    10 years ago
Abstract
A method of forming a catalyst, comprising: providing a plurality of support particles and a plurality of mobility-inhibiting particles, wherein each support particle in the plurality of support particles is bonded with its own catalytic particle; and bonding the plurality of mobility-inhibiting particles to the plurality of support particles, wherein each support particle is separated from every other support particle in the plurality of support particles by at least one of the mobility-inhibiting particles, and wherein the mobility-inhibiting particles are configured to prevent the catalytic particles from moving from one support particle to another support particle.
Description
FIELD OF THE INVENTION

The present invention relates to the field of catalysts. More specifically, the present invention relates to a method of forming catalysts where the mobility of the active catalytic particles is inhibited.


BACKGROUND OF THE INVENTION

Catalysts are used to facilitate and speed up reactions. In some applications, it is desirable to utilize small-scale catalyst material, such as catalytic nano-sized particles. Furthermore, it is also oftentimes desirable to use support structures to provide a substructure upon which the catalytic particles can reside.


In FIG. 1A, catalyst 100 comprises a plurality of support particles 110a-d, each having at least one corresponding catalytic particle 120a-d. Although FIGS. 1A-C show only four support particles 110, it is contemplated that the catalyst 100 can comprise any number of support particles 110. The catalytic particles 120a-d can be chemically absorbed or bonded onto the surface of the support particles 110a-d. However, the catalytic particles 120a-d are not permanently fixed to their bonded support particles 110a-d. Rather, they are able to move from one support particle 110 to another. For example, FIGS. 1A-B show catalytic particles 120b and 120c moving from their respective support particles 110b and 110c to adjacent support particles 110a and 110d, respectively, such that catalytic particles 120a and 120b are disposed on support particle 110a and catalytic particles 120c and 120d are disposed on support particle 110d. In high temperature applications, the movement of these catalytic particles is magnified. As seen in FIG. 1C, as catalytic particles 120b and 120c move to neighboring support particles 110a and 110d, they begin to coalesce with other catalytic particles 120a and 120d on those neighboring support particles, resulting in larger catalytic particles 120ab and 120cd.


It is understood that the effectiveness and activity of a catalyst are directly proportional to the size of the catalytic particles on the surface of the support particles. As the catalytic particles coalesce into larger clumps, the catalytic particle sizes increase, the surface area of the catalytic particles decreases, and the effectiveness of the catalyst is detrimentally affected.


SUMMARY OF THE INVENTION

The present invention inhibits this movement of catalytic particles and reduces their coalescence, thereby minimizing their individual size and maximizing their combined surface area. The present invention achieves these results by providing one or more mobility-inhibiting particles between the support particles in order to prevent the catalytic particles from moving from one support particles to another.


In one aspect of the present invention, a method of forming a catalyst is provided. The method comprises providing a plurality of support particles and a plurality of mobility-inhibiting particles. Each support particle in the plurality of support particles is bonded with its own catalytic particle. The plurality of mobility-inhibiting particles is then bonded to the plurality of support particles. Each support particle is separated from every other support particle in the plurality of support particles by at least one of the mobility-inhibiting particles. The mobility-inhibiting particles are configured to prevent the catalytic particles from moving from one support particle to another support particle.


In another aspect of the present invention, a method of forming a catalyst is provided. The method comprises providing a plurality of support particles and a plurality of mobility-inhibiting particles. Each support particle in the plurality of support particles is bonded with its own catalytic particle. The plurality of support particles is dispersed in a dispersion liquid, thereby forming a dispersion of support particles. The plurality of mobility-inhibiting particles is dispersed in a dispersion liquid, thereby forming a dispersion of mobility-inhibiting particles. The dispersion of support particles is mixed with the dispersion of mobility-inhibiting particles, thereby forming a wet mixture. The wet mixture is freeze-dried, thereby forming a dried mixture. The dried mixture is then calcined, thereby forming a cluster of the plurality of support particles and the plurality of mobility-inhibiting particles. Each support particle is separated from every other support particle in the plurality of support particles by at least one of the mobility-inhibiting particles. The mobility-inhibiting particles are configured to prevent the catalytic particles from moving from one support particle to another support particle.


In yet another aspect of the present invention, a catalyst is provided. The catalyst comprises a plurality of support particles. Each support particle in the plurality of support particles is bonded with its own catalytic particle. The catalyst also comprises a plurality of mobility-inhibiting particles bonded to the plurality of support particles. Each support particle is separated from every other support particle in the plurality of support particles by at least one of the mobility-inhibiting particles. The mobility-inhibiting particles are configured to prevent the catalytic particles from moving from one support particle to another support particle.





BRIEF DESCRIPTION OF THE DRAWINGS


FIGS. 1A-C illustrate one embodiment of a catalyst susceptible to the movement and coalescence of its catalytic particles.



FIG. 2 is a flow chart illustrating one embodiment of a method of forming a catalyst in accordance with the principles of the present invention.



FIG. 3 illustrates one embodiment of a particle production system in accordance with the principles of the present invention.



FIG. 4 illustrates another embodiment of a particle production system in accordance with the principles of the present invention.



FIG. 5A illustrates one embodiment of a plurality of support particles with their associated catalytic particles in accordance with the principles of the present invention.



FIG. 5B illustrates one embodiment of a plurality of mobility-inhibiting particles in accordance with the principles of the present invention.



FIG. 6A illustrates one embodiment of a dispersion of support particles with their associated catalytic particles in accordance with the principles of the present invention.



FIG. 6B illustrates one embodiment of a dispersion of mobility-inhibiting particles in accordance with the principles of the present invention.



FIG. 7 illustrates one embodiment of a mixture of the dispersion of support/catalytic particles of FIG. 6A and the dispersion of mobility-inhibiting particles of FIG. 6B in accordance with the principles of the present invention.



FIG. 8 illustrates one embodiment of a cluster of mobility-inhibiting particles bonded between support/catalytic particles in accordance with the principles of the present invention.





DETAILED DESCRIPTION OF THE INVENTION

The following description is presented to enable one of ordinary skill in the art to make and use the invention and is provided in the context of a patent application and its requirements. Various modifications to the described embodiments will be readily apparent to those skilled in the art and the generic principles herein may be applied to other embodiments. Thus, the present invention is not intended to be limited to the embodiment shown but is to be accorded the widest scope consistent with the principles and features described herein.


This disclosure refers to both particles and powders. These two terms are equivalent, except for the caveat that a singular “powder” refers to a collection of particles. The present invention may apply to a wide variety of powders and particles. Powders that fall within the scope of the present invention may include, but are not limited to, any of the following: (a) nano-structured powders (nano-powders), having an average grain size less than 250 nanometers and an aspect ratio between one and one million; (b) submicron powders, having an average grain size less than 1 micron and an aspect ratio between one and one million; (c) ultra-fine powders, having an average grain size less than 100 microns and an aspect ratio between one and one million; and (d) fine powders, having an average grain size less than 500 microns and an aspect ratio between one and one million.



FIG. 2 is a flow chart illustrating one embodiment of a method 200 of forming a catalyst in accordance with the principles of the present invention.


At step 210, a plurality of support particles and mobility-inhibiting particles are provided. Preferably, each support particle is bonded with its own distinct catalytic particle (i.e., a one-to-one ratio between the support particles and the catalytic particles). However, it is contemplated that some support particles can be free of any catalytic particles. The term “support/catalytic particle” is used in this disclosure to refer to a support particle and the catalytic particle bonded to it. The mobility-inhibiting particles are configured to prevent the catalytic particles from moving from one support particle to another support particle. In a preferred embodiment, the mobility-inhibiting particles comprise one or more materials that the catalytic particles do not like to travel to or on, thereby reducing the mobility of the catalytic particles.


In a preferred embodiment, the support particles have a non-catalytic composition, in contrast to the catalytic particles. In this respect, the support particles ideally have a different chemical composition than that of the catalytic particles. Similarly, the mobility-inhibiting particles preferably have a non-catalytic chemical composition that is different from that of both the support particles and the catalytic particles. However, it is contemplated that the particle chemical compositions can vary from embodiment to embodiment. In an exemplary embodiment, the support particles comprise or consist of aluminum oxide and the catalytic particles comprise or consist of a platinum group metal, such as platinum, ruthenium, rhodium, palladium, osmium, or iridium. In some embodiments, the mobility-inhibiting particles comprise or consist of a metal oxide (preferably, a transition metal oxide), including, but not limited to, cerium oxide, lanthanum oxide, and titanium oxide. In other embodiments, the mobility-inhibiting particles comprise or consist of a glass or a ceramic, including, but not limited to, boron nitride, titanium carbide, and titanium diboride. Preferably, the mobility-inhibiting particles do not comprise any precious metals.


In a preferred embodiment, the support particles, the catalyst particles, and the mobility-inhibiting particles are nano-particles. Preferably, the support particles and the mobility-inhibiting particles have a maximum diameter of 500 nanometers and a minimum diameter of 1-5 nanometers, while the catalyst particles have a diameter in the range of 0.5-5 nanometers. In some embodiments, the diameter of the support particles and the mobility-inhibiting particles is in the range of 10-15 nanometers and the diameter of the catalyst particles is in the range of 2-5 nanometers. However, it is contemplated that other particle sizes can be employed.


It is contemplated that the nano-scale structure of the particles can be achieved in a variety of ways. In a preferred embodiment, the support particles and the catalytic particles are vaporized in the hottest region of a plasma gun. The vaporized particles are then subjected to rapid quenching, causing them to condense. As a result of this vaporization and condensation, nano-sized support particles are formed with nano-sized catalytic particles bonded to them.


Examples of particle production systems employing plasma reactors to produce nano-sized particles are disclosed in U.S. patent application Ser. No. 12/151,935, filed on May 8, 2008 and entitled, “HIGHLY TURBULENT QUENCH CHAMBER”, the entirety of which is hereby incorporated by reference as if set forth herein. One such particle production system 300 is presented in FIG. 3. The system 300 comprises a precursor supply device 310 and a working gas supply device 320 both fluidly coupled to a plasma production chamber 330 having an energy delivery zone 335 formed therein. The plasma production chamber 330 is fluidly coupled with an injection port 340 of a constricting quench chamber 345, thereby allowing the energy delivery zone 335 to fluidly communicate with the quench chamber 345. One or more ports 390 also allow fluid communication of the quench chamber 345 with a controlled atmosphere system 370 (indicated by the dotted lines). The quench chamber 345 is also fluidly coupled with an ejection port 365.


Generally, the plasma production chamber 330 operates as a reactor, producing an output comprising particles within a gas stream. Particle production includes the steps of combination, reaction, and conditioning. Working gas is supplied from a gas source to a plasma reactor. Within the plasma reactor, energy is delivered to the working gas, thereby creating a plasma. A variety of different means can be employed to deliver this energy, including, but not limited to, DC coupling, capacitive coupling, inductive coupling, and resonant coupling. One or more material dispensing devices introduce at least one material, preferably in powder form, into the plasma reactor. The combination within the plasma reactor of the plasma and the material(s) introduced by the material dispensing device(s) forms a highly reactive and energetic mixture, wherein the powder can be vaporized. This mixture of vaporized powder moves through the plasma reactor in the flow direction of the working gas. As it moves, the mixture cools and particles are formed therein. The still-energetic output mixture, comprising hot gas and energetic particles, is emitted from the plasma reactor.


In an exemplary embodiment, the plasma production chamber 330 combines precursor material (preferably in powder form) supplied from the precursor supply device 310 and working gas supplied from the working gas supply device 320 within the energy delivery zone 335, where the working gas is energized to form a plasma. The plasma is applied to the precursor material within the energy delivery zone 335 to form an energized, reactive mixture. This mixture comprises one or more materials in at least one of a plurality of phases, which may include vapor, gas, and plasma.


The reactive mixture flows from the energy delivery zone 335 into the constricting quench chamber 345 through the injection port 340. As the hot mixture moves from the energy delivery zone 335, it expands rapidly within the quench chamber 345 and cools. While the mixture flows into the quench chamber 345, the ports 390 supply conditioning fluid along the inner surfaces of the quench chamber 345. The conditioning fluid combines, at least to some extent, with the mixture, and flows from the quench chamber 345 through the ejection port 365.


During a period immediately after entering the quench chamber 345, particle formation occurs. Furthermore, the supply of conditioning fluid along the inner surfaces of the quench chamber 345 works to condition the reactive mixture, to maintain entrainment of the particles therein, and to prevent the depositing of material on the inner surfaces of the quench chamber 345.


Still referring to FIG. 3, the structure of the quench chamber 345 can be formed of relatively thin walled components capable of dissipating substantial heat. For example, the thin-walled components can conduct heat from inside the chamber and radiate the heat to the ambient. The quench chamber 345 comprises a substantially cylindrical surface 350, a cone-like (frusto-conical) surface 355, and an annular surface 360 connecting the injection port 340 with the cylindrical surface 350. The cylindrical surface 350, having a large diameter relative to the size of the injection port 340, provides accommodation for the expansion of the reactive mixture that occurs after the mixture flows into the quench chamber 345. The cone-like surface 355 extends from the cylindrical surface 350, away from the injection port 340 and towards the ejection port 365. The cone-like surface 355 is sufficiently smoothly varying so as to not unduly compress fluid flowing from through the quench chamber 345 to the ejection port 365.


Substantial heat is emitted, mostly in the form of radiation, from the mixture following its entry into the quench chamber 345. The quench chamber 345 is preferably designed to dissipate this heat efficiently. For example, the surfaces of the quench chamber 345 are preferably exposed to a cooling apparatus (not shown).


Still referring to FIG. 3, the controlled atmosphere system 370 preferably comprises a chamber 385 into which conditioning fluid is introduced from a reservoir 375 through a conduit 380. The conditioning fluid preferably comprises argon. However, other inert, relatively heavy gases are equally preferred. Furthermore, the preferable mechanism of providing the conditioning fluid into the quench chamber 345 is the formation of a pressure differential between the quench chamber 345 and the outlet 365. Such pressure differential will draw the conditioning fluid into the quench chamber 345 through the ports 390. Other less preferred methods of providing the conditioning fluid include, but are not limited to, forming positive pressure within the chamber 385.


The frusto-conical shape of the quench chamber 345 can provide a modest amount of turbulence within the quench region, thereby promoting the mixing of the conditioning fluid with the reactive mixture, and increasing the quenching rate beyond prior art systems. However, in some situations, an even greater increase in quenching rate may be desired. Such an increase in quenching rate can be achieved by creating a highly turbulent flow within a region of a quench chamber where the conditioning fluid is mixed with the reactive mixture.



FIG. 4 illustrates a particle production system 400 with a highly turbulent quench chamber 445. The system 400 comprises a precursor supply device 410 a working gas supply device 420 fluidly coupled to a plasma production and reaction chamber 430, similar to plasma production chamber 330 discussed above with reference to FIG. 3. An energy delivery system 425 is also coupled with the plasma production and reactor chamber 430. The plasma production and reactor chamber 430 includes an injection port 440 that communicates fluidly with the constricting quench chamber 445. One or more ports 490 can also allow fluid communication between the quench chamber 445 and a controlled atmosphere system 470, similar to controlled atmosphere system 370 in FIG. 3. The quench chamber 445 is also fluidly coupled to an outlet 465.


Generally, the chamber 430 operates as a reactor, similar to chamber 330 in FIG. 3, producing an output comprising particles within a gas stream. Production includes the basic steps of combination, reaction, and conditioning as described later herein. The system combines precursor material supplied from the precursor supply device 410 and working gas supplied from the working gas supply device 420 within the energy delivery zone of the chamber 430. The system energizes the working gas in the chamber 430 using energy from the energy supply system 490, thereby forming a plasma. The plasma is applied to the precursor material within the chamber 430 to form an energized, reactive mixture. This mixture comprises one or more materials in at least one of a plurality of phases, which may include vapor, gas, and plasma. The reactive mixture flows from the plasma production and reactor chamber 430 into the quench chamber 445 through an injection port 440.


The quench chamber 445 preferably comprises a substantially cylindrical surface 450, a frusto-conical surface 455, and an annular surface 460 connecting the injection port 440 with the cylindrical surface 450. The frusto-conical surface 460 narrows to meet the outlet 465. The plasma production and reactor chamber 430 includes an extended portion at the end of which the injection port 440 is disposed. This extended portion shortens the distance between the injection port 440 and the outlet 465, reducing the volume of region in which the reactive mixture and the conditioning fluid will mix, referred to as the quench region. In a preferred embodiment, the injection port 440 is arranged coaxially with the outlet 465. The center of the injection port is positioned a first distance d1 from the outlet 465. The perimeter of the injection port is positioned a second distance d2 from a portion of the frusto-conical surface 455. The injection port 440 and the frusto-conical surface 455 form the aforementioned quench region therebetween. The space between the perimeter of the injection port 440 and the frusto-conical surface 455 forms a gap therebetween that acts as a channel for supplying conditioning fluid into the quench region. The frusto-conical surface 455 acts as a funneling surface, channeling fluid through the gap and into the quench region.


While the reactive mixture flows into the quench chamber 445, the ports 490 supply conditioning fluid into the quench chamber 445. The conditioning fluid then moves along the frusto-conical surface 455, through the gap between the injection port 440 and the frusto-conical surface 455, and into the quench region. In some embodiments, the controlled atmosphere system 470 is configured to control the volume flow rate or mass flow rate of the conditioning fluid supplied to the quench region.


As the reactive mixture moves out of the injection port 440, it expands and mixes with the conditioning fluid. Preferably, the angle at which the conditioning fluid is supplied produces a high degree of turbulence and promotes mixing with the reactive mixture. This turbulence can depend on many parameters. In a preferred embodiment, one or more of these parameters is adjustable to control the level of turbulence. These factors include the flow rates of the conditioning fluid, the temperature of the frusto-conical surface 455, the angle of the frusto-conical surface 455 (which affects the angle at which the conditioning fluid is supplied into the quench region), and the size of the quench region. For example, the relative positioning of the frusto-conical surface 455 and the injection port 440 is adjustable, which can be used to adjust the volume of quench region. These adjustments can be made in a variety of different ways, using a variety of different mechanisms, including, but not limited to, automated means and manual means.


During a brief period immediately after entering the quench chamber 445, particle formation occurs. The degree to which the particles agglomerate depends on the rate of cooling. The cooling rate depends on the turbulence of the flow within the quench region. Preferably, the system is adjusted to form a highly turbulent flow, and to form very dispersed particles. For example, in preferred embodiments, the turbidity of the flow within the quench region is such that the flow has a Reynolds Number of at least 1000.


Still referring to FIG. 4, the structure of the quench chamber 445 is preferably formed of relatively thin walled components capable of dissipating substantial quantities of heat. For example, the thin-walled components can conduct heat from inside the chamber and radiate the heat to the ambient.


Substantial heat is emitted, mostly in the form of radiation, from the reactive mixture following its entry into the quench chamber 445. The quench chamber 445 is designed to dissipate this heat efficiently. The surfaces of the quench chamber 245 are preferably exposed to a cooling system (not shown). In a preferred embodiment, the cooling system is configured to control a temperature of the frusto-conical surface 455.


Following injection into the quench region, cooling, and particle formation, the mixture flows from the quench chamber 445 through the outlet port 465. Suction generated by a generator 495 moves the mixture and conditioning fluid from the quench region into the conduit 492. From the outlet port 465, the mixture flows along the conduit 492, toward the suction generator 495. Preferably, the particles are removed from the mixture by a collection or sampling system (not shown) prior to encountering the suction generator 495.


Still referring to FIG. 4, the controlled atmosphere system 470 comprises a chamber 485, fluidly coupled to the quench region through port(s) 490, into which conditioning fluid is introduced from a reservoir, such as reservoir 375 from FIG. 3, through a conduit 480. As described above, the conditioning fluid preferably comprises argon. However, other inert, relatively heavy gases are equally preferred. Also, as discussed above, the preferable mechanism of providing the conditioning fluid into the quench chamber 445 is the formation of a pressure differential between the quench chamber 445 and the outlet 465. Such pressure differential will draw the conditioning fluid into the quench chamber 445 through the ports 490. Other methods of providing the conditioning fluid include, but are not limited to, forming positive pressure within the chamber 485.


The angle of the frusto-conical surface affects the angle at which the conditioning fluid is supplied into the quench region, which can affect the level of turbulence in the quench region. The conditioning fluid preferably flows into the quench region along a plurality of momentum vectors. The greater the degree of the angle between the momentum vectors, the higher the level of turbulence that will be produced. In a preferred embodiment, the high turbulent quench chamber comprises a frusto-conical surface that is configured to funnel at least two conditioning fluid momentum vectors into the quench region such that there is at least a 90 degree angle between the two momentum vectors. It is contemplated that other angle degree thresholds may be applied as well. For example, attention may also be paid to the angle formed between at least one of the conditioning fluid momentum vectors and the momentum vector of the reactive mixture. In one embodiment of a highly turbulent quench chamber, a reactive mixture inlet is configured to supply the reactive mixture into the quench region along a first momentum vector, the frusto-conical surface is configured to supply the conditioning fluid to the quench region along a second momentum vector, and the second momentum vector has an oblique angle greater than 20 degrees relative to the first momentum vector.


The size of the quench region also affects the level of turbulence in the quench region. The smaller the quench region, the higher the level of turbulence that will be produced. The size of the quench region can be reduced by reducing the distance between the center of the injection port 440 and the outlet 465.


The high turbulence produced by the embodiments of the present invention decreases the period during which particles formed can agglomerate with one another, thereby producing particles of more uniform size, and in some instances, producing smaller-sized particles. Both of these features lead to particles with increased dispersibility and increased ratio of surface area to volume.


Referring back to the method 200 in FIG. 2, particle production system 200 or 300 (or variations thereof) can be used to provide one or more of the support particles, catalytic particles, and mobility-inhibiting particles in nano-scale form. For example, these particles can be introduced as micron-sized precursor material into the particle production system, where they are vaporized and then condensed to form nano-size particles. In a preferred embodiment, the support/catalytic particles are formed and provided separately from the mobility-inhibiting particles, thereby avoiding any premature interaction (e.g., bonding) between the mobility-inhibiting particles and the support/catalytic particles. Such separation can be achieved in a variety of ways, including, but not limited to, using different particle production systems for both groups, or by using the same particle production system for both groups at different times.



FIG. 5A illustrates one embodiment of a plurality of support particles 510 provided in step 210 of method 200. Each support particle 510 has a catalytic particle 520 bonded to it (preferably to its exterior surface). Although, in some embodiments, certain support particles 510 may be absent a catalytic particle 520. It is contemplated that the size of the catalytic particle 520 on the support particle 510 can be affected by changing the amount of catalytic material provided to the particle production system or by otherwise adjusting the mix ratio of catalytic particles to support particles provided to the particle production system. The larger the concentration of catalytic particles provided to the particle production system, the larger the size of the catalytic particles 520 bonded to the support particles 510.



FIG. 5B illustrates one embodiment of a plurality of mobility-inhibiting particles 530 provided in step 210 of method 200. The stripes on the mobility-inhibiting particles 530 are provided solely for the purpose of helping to distinguish the mobility-inhibiting particles 530 from the support particles 510.


At step 220 of method 200, the support/catalytic particles and the mobility-inhibiting particles are dispersed in liquid. FIG. 6A illustrates one embodiment of a dispersion 625 of support/catalytic particles. A close-up of the dispersion 625 shows the support/catalytic particles being separated by a liquid 615a and being made up of support particles 610 having catalytic particles 620 bonded to them. FIG. 6B illustrates one embodiment of a dispersion 635 of mobility-inhibiting particles 630. A close-up of the dispersion 635 shows the mobility-inhibiting particles 630 being separated by a liquid 615b. Although FIGS. 6A-B show the support/catalytic particles and the mobility-inhibiting particles in separate dispersions 625 and 635, it is contemplated that they can also be dispersed in the same container at the same time to form one dispersion.


The dispersion liquids 615a and 615b can be any liquids configured to disperse the support/catalytic particles and the mobility-inhibiting particles, respectively. In a preferred embodiment, the dispersion liquids comprise or consist of water or any organic liquid, such as glycol ethers. In some embodiments, dispersions 625 and 635 both use the same type of dispersion liquid. In other embodiments, dispersions 625 and 635 use different types of dispersion liquids (e.g., dispersion liquid 615a is water and dispersion liquid 615b is ethylene glycol).


In some embodiments, one or more surfactants or other dispersing aids, such as cationic, anionic, zwitterionic, and/or non-ionic carbon based oligomers and/or polymers, can be added to the dispersion liquid. Certain surfactants can be added to the dispersion in order to adjust its acidity and make it stable. Acids can be added to the dispersion in order to acidify the surface of N-oxide particles. The surfactants are carefully chosen so that they will not be harmful to the catalyst material. In preferred embodiments, no sulfates or phosphates are added to the dispersion. Examples of surfactants that can be added to the dispersion liquid are carboxylic acids, polyamines, and polyethers. It is contemplated that other surfactants or dispersing aids can be used as well.


It is contemplated that the different variations of particle, dispersion liquid, and surfactant concentrations can be employed. In a preferred embodiment, the dispersion comprises a 5-25% by weight concentration of powder, meaning that the support/catalytic particles and the mobility-inhibiting particles each make up approximately 5-25% by weight of their respective dispersions. In a preferred embodiment, the dispersion comprises a 1-10% by weight concentration of surfactant or other dispersing aid. Preferably, the surfactant or other dispersing aid accounts for approximately 5% or less of the dispersion.


At step 230 of method 200, the dispersed support/catalytic particles and mobility-inhibiting particles are mixed to form a mixture. If the support/catalytic particles and the mobility-inhibiting particles were not originally dispersed together, or not subsequently placed into the same container to form a single dispersion, then they are at this time placed into the same container where they can be mixed together. In a preferred embodiment, the mixing is performed by sonication, mechanical mixing, and/or shear mixing. However, it is contemplated that a variety of other agitation methods can be employed in order to perform this mixing.



FIG. 7 illustrates one embodiment of a mixture 745 of the dispersions in one container. The mixture 745 comprises a plurality of support particles 710, each having a catalytic particle 720 bonded to it, and mobility-inhibiting particles 730. The particles are separated by the liquid 715, which can comprise any dispersion liquids and surfactants (or other dispersing aids) used in the prior steps.


At step 240, the dispersion liquid is removed from the mixture to form a dried mixture. It is contemplated that the liquid can be removed in a variety of ways. In one embodiment, the dispersion of particles is freeze-dried. The mixture is poured into a freeze-dry appropriate vessel. It is then frozen with liquid nitrogen or some other medium that is cool enough to freeze the dispersion of particles. In one embodiment, the liquid nitrogen, or other freezing medium, is at approximately −60 degrees Celsius. However, it is contemplated that the liquid nitrogen, or other freezing medium, can be used at other temperatures as well. The mixture is then placed into a vacuum system, where the dispersion of particles remains frozen as the water, or other dispersing liquid, is removed via vacuum pressure. In one embodiment, a vacuum pressure of approximately 10 microns is employed. In other embodiments, a vacuum pressure of between approximately 2 microns and approximately 5 microns is employed.


The vacuum pressure removes the water and any other liquid in the mixture having a higher vapor pressure than water. However, in some embodiments, the surfactant remains with the frozen dispersion of particles. The removal of the water leaves a porous powder structure of the support/catalytic particles and the mobility-inhibiting particles, with the surfactant disposed within the pores. The resulting powder is in an intermediate state, being loosely bonded together, yet dry to the touch, providing mechanical handling ability.


At step 250, the dried mixture is calcined, thereby baking off any surfactant and forming clusters of mobility-inhibiting particles bonded between the support/catalytic particles. In some embodiments, the powder is placed in a crucible. It is contemplated that the crucible can be made of ceramic or a variety of other materials. The crucible is then placed in a calcining furnace, where it is heated at a given temperature for a given time. In some embodiments, the crucible is heated in the calcining furnace at approximately 550 degrees Celsius for approximately 2 hours. However, it is contemplated that other temperatures and heating time can be employed as well. In some embodiments, the crucible is placed in a furnace that has already been preheated to the desired baking temperature. Test results have shown that by preheating the furnace before placing the crucible inside, instead of ramping up the temperature to the desired temperature while the crucible is in the furnace, the dispersion of the metal particles can be maximized. However, it is contemplated that, in some embodiments, the furnace temperature can be ramped up while the crucible is in the furnace. In some embodiments, a ramp rate of 1-50 degrees Celsius is employed to raise the temperature of the furnace while the crucible is inside. In a preferred embodiment, the furnace provides an ambient air environment within which the crucible, and consequently the powder, can be heated. It is contemplated that the environment within the furnace need not comprise air. However, it preferably contains some amount of oxygen.


The calcining of the dried mixture takes it from a Van der Waals or proximity attraction between the particles to an actual covalent bond between the particles, resulting in a surfactant-free agglomeration of the support/catalytic particles and the mobility-inhibiting particles. FIG. 8 illustrates one embodiment of a cluster of mobility-inhibiting particles 830 bonded between support particles 810, which have catalytic particles 820 bonded to them. In some embodiments, the present invention produces clusters in the range of 0.5-50 microns. In some embodiments, the present invention produces clusters in the range of 5-10 microns. However, it is contemplated that other cluster sizes can be produced as well.


In some embodiments, the loading percentages of the powders (support, catalyst, and mobility-inhibiting) are adjusted in order to achieve a desired powder concentration for each particular type of powder in the resulting clusters. In some embodiments, a 0.01-15% loading of catalyst powder is employed. In a preferred embodiment, a 0.5-3% loading of catalyst powder is employed. However, it is contemplated that other loading percentages can be employed as well.


In a preferred embodiment, the support particles, the catalyst particles, and the mobility-inhibiting particles in the resulting clusters are nano-particles. Preferably, the support particles and the mobility-inhibiting particles have a maximum diameter of 500 nanometers and a minimum diameter of between 1-5 nanometers, while the catalyst particles have a diameter in the range of 0.5-5 nanometers. In some embodiments, the diameter of the support particles and the mobility-inhibiting particles is in the range of 5-20 nanometers. In some embodiments, the diameter of the support particles and the mobility-inhibiting particles is in the range of 10-15 nanometers and the diameter of the catalyst particles is in the range of 2-5 nanometers. However, it is contemplated that other particle sizes can be employed.


The introduction and bonding of mobility-inhibiting particles to and between the support/catalytic particles prevents the catalytic particles from moving from one support particle to another, thereby preventing the coalescence of the catalytic particles. As a result, the size of the individual catalytic particles can be minimized and the total catalytic surface area of the cluster can be maximized.


The present invention has been described in terms of specific embodiments incorporating details to facilitate the understanding of principles of construction and operation of the invention. Such reference herein to specific embodiments and details thereof is not intended to limit the scope of the claims appended hereto. It will be readily apparent to one skilled in the art that other various modifications may be made in the embodiment chosen for illustration without departing from the spirit and scope of the invention as defined by the claims.

Claims
  • 1. A method of forming a catalyst, comprising: providing a plurality of support particles and a plurality of mobility-inhibiting particles, wherein each support particle in the plurality of support particles is bonded with its own catalytic particle; andbonding the plurality of mobility-inhibiting particles to the plurality of support particles,wherein each support particle is separated from every other support particle in the plurality of support particles by at least one of the mobility-inhibiting particles,wherein the mobility-inhibiting particles are configured to prevent the catalytic particles from moving from one support particle to another support particle, andwherein providing the plurality of support particles comprises:nano-sizing a precursor support powder that has an average grain size equal to or greater than 1 micron;nano-sizing a precursor catalytic powder that has an average grain size equal to or greater than 1 micron; andbonding the nano-sized catalytic powder to the nano-sized support powder, thereby forming the plurality of support particles with each support particle in the plurality of support particles bonded with its own catalytic particle.
  • 2. The method of claim 1, wherein: nano-sizing the precursor support powder and the precursor catalytic powder comprises applying a plasma stream to the precursor support powder and to the precursor catalytic powder, thereby vaporizing the precursor support powder and the precursor catalytic powder; andbonding the nano-sized catalytic powder to the nano-sized support powder comprises condensing the vaporized support powder and the vaporized catalytic powder, thereby forming the plurality of support particles with each support particle in the plurality of support particles bonded with its own catalytic particle.
  • 3. The method of claim 1, wherein providing the plurality of mobility-inhibiting particles comprises nano-sizing a precursor mobility-inhibiting powder that has an average grain size equal to or greater than 1 micron.
  • 4. The method of claim 3, wherein nano-sizing the precursor mobility-inhibiting powder comprises: applying a plasma stream to the precursor mobility-inhibiting powder, thereby vaporizing the precursor mobility-inhibiting powder; andcondensing the vaporized mobility-inhibiting powder.
  • 5. The method of claim 1, wherein providing the plurality of support particles and the plurality of mobility-inhibiting particles comprises: dispersing the plurality of support particles in a dispersion liquid, wherein each support particle in the plurality of support particles is bonded with its own catalytic particle;dispersing the plurality of mobility-inhibiting particles in a dispersion liquid; andmixing the dispersed support particles with the dispersed mobility-inhibiting particles, thereby forming a mixture of the dispersed support particles and the dispersed mobility-inhibiting particles.
  • 6. The method of claim 5, wherein the dispersion liquid for at least one of the support particles and the mobility-inhibiting particles comprises water.
  • 7. The method of claim 5, wherein the dispersion liquid for at least one of the support particles and the mobility-inhibiting particles comprises an organic liquid.
  • 8. The method of claim 7, wherein the organic liquid is a glycol ether.
  • 9. The method of claim 5, wherein at least one of dispersing the plurality of support particles and dispersing the plurality of mobility-inhibiting particles comprises adding a surfactant to the dispersion liquid.
  • 10. The method of claim 9, wherein the surfactant is selected from the group consisting of a carboxylic acid, a polyamine, and a polyether.
  • 11. The method of claim 5, wherein the dispersed support particles and the dispersed mobility-inhibiting particles are mixed using a sonication process.
  • 12. The method of claim 5, wherein the step of bonding at least one mobility-inhibiting particle to and between each support particle in the plurality of support particles, comprises the step of freeze-drying the mixture of dispersed support particles and dispersed mobility-inhibiting particles, thereby forming a dried mixture of dispersed support particles and dispersed mobility-inhibiting particles.
  • 13. The method of claim 12, wherein the step of bonding at least one mobility-inhibiting particle to and between each support particle in the plurality of support particles comprises the step of calcining the dried mixture of dispersed support particles and dispersed mobility-inhibiting particles.
  • 14. The method of claim 1, wherein the plurality of support particles comprises a plurality of alumina particles.
  • 15. The method of claim 1, wherein the catalytic particles comprise platinum.
  • 16. The method of claim 1, wherein the plurality of mobility-inhibiting particles comprises a different chemical composition than the plurality of support particles.
  • 17. The method of claim 16, wherein the plurality of mobility-inhibiting particles comprises a plurality of ceramic particles.
  • 18. The method of claim 16, wherein the plurality of mobility-inhibiting particles comprises a plurality of metal-oxide particles.
  • 19. The method of claim 1, wherein: each support particle in the plurality of support particles has a diameter between 1 nanometer and 500 nanometers;each catalytic particle has a diameter between 0.5 nanometers and 5 nanometers; andeach mobility-inhibiting particle in the plurality of mobility-inhibiting particles has a diameter between 1 nanometer and 500 nanometers.
  • 20. A method of forming a catalyst, comprising: providing a plurality of support particles and a plurality of mobility-inhibiting particles, wherein each support particle in the plurality of support particles is bonded with its own catalytic particle;dispersing the plurality of support particles in a dispersion liquid, thereby forming a dispersion of support particles;dispersing the plurality of mobility-inhibiting particles in a dispersion liquid, thereby fanning a dispersion of mobility-inhibiting particles;mixing the dispersion of support particles with the dispersion of mobility-inhibiting particles, thereby forming a wet mixture;freeze-drying the wet mixture, thereby forming a dried mixture; andcalcining the dried mixture, thereby forming a cluster of the plurality of support particles and the plurality of mobility-inhibiting particles, wherein each support particle is separated from every other support particle in the plurality of support particles by at least one of the mobility-inhibiting particles, and wherein the mobility-inhibiting particles are configured to prevent the catalytic particles from moving from one support particle to another support particle.
  • 21. The method of claim 20, wherein providing the plurality of support particles and the plurality of mobility-inhibiting particles comprises: nano-sizing a precursor support powder that has an average grain size equal to or greater than 1 micron;nano-sizing a precursor catalytic powder that has an average grain size equal to or greater than 1 micron;bonding the nano-sized catalytic powder to the nano-sized support powder, thereby forming the plurality of support particles with each support particle in the plurality of support particles bonded with its own catalytic particle; andnano-sizing a precursor mobility-inhibiting powder that has an average grain size equal to or greater than 1 micron.
  • 22. The method of claim 21, wherein the steps of nano-sizing the precursor powders comprise: applying a plasma stream to the precursor powders, thereby vaporizing the precursor powders; andcondensing the vaporized powders.
  • 23. The method of claim 20, wherein the dispersion liquid for at least one of the support particles and the mobility-inhibiting particles comprises water.
  • 24. The method of claim 20, wherein the dispersion liquid for at least one of the support particles and the mobility-inhibiting particles comprises an organic liquid.
  • 25. The method of claim 24, wherein the organic liquid is a glycol ether.
  • 26. The method of claim 20, wherein at least one of dispersing the plurality of support particles and dispersing the plurality of mobility-inhibiting particles comprises adding a surfactant to the dispersion liquid.
  • 27. The method of claim 26, wherein the surfactant is selected from the group consisting of a carboxylic acid, a polyamine, and a polyether.
  • 28. The method of claim 20, wherein the step of mixing the dispersion of support particles with the dispersion of mobility-inhibiting particles comprises using a sonication process.
  • 29. The method of claim 20, wherein the plurality of support particles comprises a plurality of alumina particles.
  • 30. The method of claim 20, wherein the catalytic particles comprise platinum.
  • 31. The method of claim 20, wherein the plurality of mobility-inhibiting particles comprises a different chemical composition than the plurality of support particles.
  • 32. The method of claim 31, wherein the plurality of mobility-inhibiting particles comprises a plurality of ceramic particles.
  • 33. The method of claim 31, wherein the plurality of mobility-inhibiting particles comprises a plurality of metal-oxide particles.
  • 34. The method of claim 20, wherein: each support particle in the plurality of support particles has a diameter between 1 nanometer and 500 nanometers;each catalytic particle has a diameter between 0.5 nanometers and 5 nanometers; andeach mobility-inhibiting particle in the plurality of mobility-inhibiting particles has a diameter between 1 nanometer and 500 nanometers.
  • 35. A catalyst comprising: a plurality of support particles, wherein each support particle in the plurality of support particles is bonded with its own catalytic particle; anda plurality of mobility-inhibiting particles bonded to the plurality of support particles,wherein each support particle is separated from every other support particle in the plurality of support particles by at least one of the mobility-inhibiting particles,wherein the mobility-inhibiting particles are configured to prevent the catalytic particles from moving from one support particle to another support particle, andwherein the plurality of support particles comprises a plurality of alumina particles.
  • 36. The catalyst of claim 35, wherein the catalytic particles comprise platinum.
  • 37. The catalyst of claim 35, wherein the plurality of mobility-inhibiting particles comprises a different chemical composition than the plurality of support particles.
  • 38. The catalyst of claim 37, wherein the plurality of mobility-inhibiting particles comprises a plurality of ceramic particles.
  • 39. The catalyst of claim 37, wherein the plurality of mobility-inhibiting particles comprises a plurality of metal-oxide particles.
  • 40. A catalyst comprising: a plurality of support particles, wherein each support particle in the plurality of support particles is bonded with its own catalytic particle; anda plurality of mobility-inhibiting particles bonded to the plurality of support particles,wherein each support particle is separated from every other support particle in the plurality of support particles by at least one of the mobility-inhibiting particles,wherein the mobility-inhibiting particles are configured to prevent the catalytic particles from moving from one support particle to another support particle, andwherein each support particle in the plurality of support particles has a diameter between 1 nanometer and 500 nanometers;each catalytic particle has a diameter between 0.5 nanometers and 5 nanometers; andeach mobility-inhibiting particle in the plurality of mobility-inhibiting particles has a diameter between 1 nanometer and 500 nanometers.
CROSS-REFERENCE TO RELATED APPLICATIONS

This application claims priority to U.S. Provisional Patent Application Ser. No. 61/284,329, filed Dec. 15, 2009 and entitled “MATERIALS PROCESSING,” which is hereby incorporated herein by reference in its entirety as if set forth herein.

US Referenced Citations (345)
Number Name Date Kind
2284554 Beyerstedt May 1942 A
2419042 Todd Apr 1947 A
2519531 Worn Aug 1950 A
2562753 Trost Jul 1951 A
2689780 Rice Sep 1954 A
3001402 Koblin Sep 1961 A
3067025 Chisholm Dec 1962 A
3145287 Siebein et al. Aug 1964 A
3178121 Wallace, Jr. Apr 1965 A
3179782 Matvay Apr 1965 A
3313908 Unger et al. Apr 1967 A
3401465 Larwill Sep 1968 A
3450926 Kieman Jun 1969 A
3457788 Miyajima Jul 1969 A
3537513 Austin Nov 1970 A
3552653 Inoue Jan 1971 A
3617358 Dittrich Nov 1971 A
3667111 Chartet Jun 1972 A
3741001 Fletcher et al. Jun 1973 A
3752172 Cohen et al. Aug 1973 A
3774442 Gustavsson Nov 1973 A
3830756 Sanchez et al. Aug 1974 A
3871448 Vann et al. Mar 1975 A
3892882 Guest et al. Jul 1975 A
3914573 Muehlberger Oct 1975 A
3959420 Geddes et al. May 1976 A
3969482 Teller Jul 1976 A
4008620 Narato et al. Feb 1977 A
4018388 Andrews Apr 1977 A
4139497 Castor et al. Feb 1979 A
4157316 Thompson et al. Jun 1979 A
4171288 Keith et al. Oct 1979 A
4174298 Antos Nov 1979 A
4227928 Wang Oct 1980 A
4248387 Andrews Feb 1981 A
4253917 Wang Mar 1981 A
4284609 deVries Aug 1981 A
4369167 Weir Jan 1983 A
4388274 Rourke et al. Jun 1983 A
4431750 McGinnis et al. Feb 1984 A
4436075 Campbell et al. Mar 1984 A
4458138 Adrian et al. Jul 1984 A
4459327 Wang Jul 1984 A
4505945 Dubust et al. Mar 1985 A
4513149 Gray et al. Apr 1985 A
RE32244 Andersen Sep 1986 E
4723589 Iyer et al. Feb 1988 A
4731517 Cheney Mar 1988 A
4764283 Ashbrook et al. Aug 1988 A
4765805 Wahl et al. Aug 1988 A
4824624 Palicka et al. Apr 1989 A
4855505 Koll Aug 1989 A
4866240 Webber Sep 1989 A
4885038 Anderson et al. Dec 1989 A
4983555 Roy et al. Jan 1991 A
4987033 Abkowitz et al. Jan 1991 A
5015863 Takeshima et al. May 1991 A
5041713 Weidman Aug 1991 A
5043548 Whitney et al. Aug 1991 A
5070064 Hsu et al. Dec 1991 A
5073193 Chaklader et al. Dec 1991 A
5157007 Domesle et al. Oct 1992 A
5230844 Macaire et al. Jul 1993 A
5233153 Coats Aug 1993 A
5338716 Triplett et al. Aug 1994 A
5369241 Taylor et al. Nov 1994 A
5371049 Moffett et al. Dec 1994 A
5372629 Anderson et al. Dec 1994 A
5392797 Welch Feb 1995 A
5439865 Abe et al. Aug 1995 A
5442153 Marantz et al. Aug 1995 A
5460701 Parker et al. Oct 1995 A
5464458 Yamamoto Nov 1995 A
5485941 Guyomard et al. Jan 1996 A
5534149 Birkenbeil et al. Jul 1996 A
5553507 Basch et al. Sep 1996 A
5562966 Clarke et al. Oct 1996 A
5582807 Liao et al. Dec 1996 A
5611896 Swanepoel et al. Mar 1997 A
5630322 Heilmann et al. May 1997 A
5652304 Calderon et al. Jul 1997 A
5723187 Popoola et al. Mar 1998 A
5726414 Kitahashi et al. Mar 1998 A
5749938 Coombs May 1998 A
5776359 Schultz et al. Jul 1998 A
5788738 Pirzada et al. Aug 1998 A
5811187 Anderson et al. Sep 1998 A
5837959 Muehlberger et al. Nov 1998 A
5851507 Pirzada et al. Dec 1998 A
5853815 Muehlberger Dec 1998 A
5858470 Bernecki et al. Jan 1999 A
5905000 Yadav et al. May 1999 A
5935293 Detering et al. Aug 1999 A
5973289 Read et al. Oct 1999 A
5989648 Phillips Nov 1999 A
5993967 Brotzman, Jr. et al. Nov 1999 A
5993988 Ohara et al. Nov 1999 A
6004620 Camm Dec 1999 A
6012647 Ruta et al. Jan 2000 A
6033781 Brotzman, Jr. et al. Mar 2000 A
6045765 Nakatsuji et al. Apr 2000 A
6059853 Coombs May 2000 A
6084197 Fusaro, Jr. Jul 2000 A
6102106 Manning et al. Aug 2000 A
6117376 Merkel Sep 2000 A
6213049 Yang Apr 2001 B1
6214195 Yadav et al. Apr 2001 B1
6228904 Yadav et al. May 2001 B1
6254940 Pratsinis et al. Jul 2001 B1
6261484 Phillips et al. Jul 2001 B1
6267864 Yadav et al. Jul 2001 B1
6322756 Arno et al. Nov 2001 B1
6342465 Klein et al. Jan 2002 B1
6344271 Yadav et al. Feb 2002 B1
6379419 Celik et al. Apr 2002 B1
6387560 Yadav et al. May 2002 B1
6395214 Kear et al. May 2002 B1
6398843 Tarrant Jun 2002 B1
6409851 Sethuram et al. Jun 2002 B1
6413781 Geis et al. Jul 2002 B1
6416818 Aikens et al. Jul 2002 B1
RE37853 Detering et al. Sep 2002 E
6444009 Liu et al. Sep 2002 B1
6475951 Domesle et al. Nov 2002 B1
6506995 Fusaro, Jr. et al. Jan 2003 B1
6517800 Cheng et al. Feb 2003 B1
6524662 Jang et al. Feb 2003 B2
6531704 Yadav et al. Mar 2003 B2
6548445 Buysch et al. Apr 2003 B1
6554609 Yadav et al. Apr 2003 B2
6562304 Mizrahi May 2003 B1
6562495 Yadav et al. May 2003 B2
6569397 Yadav et al. May 2003 B1
6569518 Yadav et al. May 2003 B2
6572672 Yadav et al. Jun 2003 B2
6579446 Teran et al. Jun 2003 B1
6596187 Coll et al. Jul 2003 B2
6603038 Hagemeyer et al. Aug 2003 B1
6607821 Yadav et al. Aug 2003 B2
6610355 Yadav et al. Aug 2003 B2
6623559 Huang Sep 2003 B2
6635357 Moxson et al. Oct 2003 B2
6641775 Vigliotti et al. Nov 2003 B2
6652822 Phillips et al. Nov 2003 B2
6652967 Yadav et al. Nov 2003 B2
6669823 Sarkas et al. Dec 2003 B1
6682002 Kyotani Jan 2004 B2
6689192 Phillips et al. Feb 2004 B1
6699398 Kim Mar 2004 B1
6706097 Zornes Mar 2004 B2
6706660 Park Mar 2004 B2
6710207 Bogan, Jr. et al. Mar 2004 B2
6713176 Yadav et al. Mar 2004 B2
6716525 Yadav et al. Apr 2004 B1
6744006 Johnson et al. Jun 2004 B2
6746791 Yadav et al. Jun 2004 B2
6772584 Chun et al. Aug 2004 B2
6786950 Yadav et al. Sep 2004 B2
6813931 Yadav et al. Nov 2004 B2
6817388 Tsangaris et al. Nov 2004 B2
6832735 Yadav et al. Dec 2004 B2
6838072 Kong et al. Jan 2005 B1
6841509 Hwang et al. Jan 2005 B1
6855410 Buckley Feb 2005 B2
6855426 Yadav Feb 2005 B2
6855749 Yadav et al. Feb 2005 B1
6886545 Holm May 2005 B1
6896958 Cayton et al. May 2005 B1
6902699 Fritzemeier et al. Jun 2005 B2
6916872 Yadav et al. Jul 2005 B2
6919527 Boulos et al. Jul 2005 B2
6933331 Yadav et al. Aug 2005 B2
6972115 Ballard Dec 2005 B1
6986877 Takikawa et al. Jan 2006 B2
6994837 Boulos et al. Feb 2006 B2
7007872 Yadav et al. Mar 2006 B2
7022305 Drumm et al. Apr 2006 B2
7052777 Brotzman, Jr. et al. May 2006 B2
7073559 O'Larey et al. Jul 2006 B2
7081267 Yadav Jul 2006 B2
7101819 Rosenflanz et al. Sep 2006 B2
7147544 Rosenflanz Dec 2006 B2
7147894 Zhou et al. Dec 2006 B2
7166198 Van Der Walt et al. Jan 2007 B2
7166663 Cayton et al. Jan 2007 B2
7172649 Conrad et al. Feb 2007 B2
7172790 Koulik et al. Feb 2007 B2
7178747 Yadav et al. Feb 2007 B2
7208126 Musick et al. Apr 2007 B2
7211236 Stark et al. May 2007 B2
7217407 Zhang May 2007 B2
7220398 Sutorik et al. May 2007 B2
7265076 Taguchi et al. Sep 2007 B2
7307195 Polverejan et al. Dec 2007 B2
7323655 Kim Jan 2008 B2
7384447 Kodas et al. Jun 2008 B2
7417008 Richards et al. Aug 2008 B2
7494527 Jurewicz et al. Feb 2009 B2
7541012 Yeung et al. Jun 2009 B2
7541310 Espinoza et al. Jun 2009 B2
7557324 Nylen et al. Jul 2009 B2
7572315 Boulos et al. Aug 2009 B2
7611686 Alekseeva et al. Nov 2009 B2
7615097 McKechnie et al. Nov 2009 B2
7618919 Shimazu et al. Nov 2009 B2
7622693 Foret Nov 2009 B2
7632775 Zhou et al. Dec 2009 B2
7678419 Kevwitch et al. Mar 2010 B2
7709411 Zhou et al. May 2010 B2
7750265 Belashchenko et al. Jul 2010 B2
7803210 Sekine et al. Sep 2010 B2
7851405 Wakamatsu et al. Dec 2010 B2
7874239 Howland Jan 2011 B2
7897127 Layman et al. Mar 2011 B2
7905942 Layman Mar 2011 B1
8051724 Layman et al. Nov 2011 B1
8076258 Biberger Dec 2011 B1
8080494 Yasuda et al. Dec 2011 B2
8142619 Layman et al. Mar 2012 B2
8294060 Mohanty et al. Oct 2012 B2
20010042802 Youds Nov 2001 A1
20020018815 Sievers et al. Feb 2002 A1
20020068026 Murrell et al. Jun 2002 A1
20020079620 DuBuis et al. Jun 2002 A1
20020100751 Carr Aug 2002 A1
20020102674 Anderson Aug 2002 A1
20020131914 Sung Sep 2002 A1
20020143417 Ito et al. Oct 2002 A1
20020182735 Kibby et al. Dec 2002 A1
20020183191 Faber et al. Dec 2002 A1
20020192129 Shamouilian et al. Dec 2002 A1
20030036786 Duren et al. Feb 2003 A1
20030042232 Shimazu Mar 2003 A1
20030047617 Shanmugham et al. Mar 2003 A1
20030066800 Saim et al. Apr 2003 A1
20030108459 Wu et al. Jun 2003 A1
20030110931 Aghajanian et al. Jun 2003 A1
20030139288 Cai et al. Jul 2003 A1
20030143153 Boulos et al. Jul 2003 A1
20030172772 Sethuram et al. Sep 2003 A1
20030223546 McGregor et al. Dec 2003 A1
20040009118 Phillips et al. Jan 2004 A1
20040023302 Archibald et al. Feb 2004 A1
20040023453 Xu et al. Feb 2004 A1
20040077494 LaBarge et al. Apr 2004 A1
20040103751 Joseph et al. Jun 2004 A1
20040119064 Narayan et al. Jun 2004 A1
20040127586 Jin et al. Jul 2004 A1
20040167009 Kuntz et al. Aug 2004 A1
20040176246 Shirk et al. Sep 2004 A1
20040208805 Fincke et al. Oct 2004 A1
20040213998 Hearley et al. Oct 2004 A1
20040238345 Koulik et al. Dec 2004 A1
20040251017 Pillion et al. Dec 2004 A1
20040251241 Blutke et al. Dec 2004 A1
20050000321 O'Larey et al. Jan 2005 A1
20050000950 Schroder et al. Jan 2005 A1
20050066805 Park et al. Mar 2005 A1
20050077034 King Apr 2005 A1
20050097988 Kodas et al. May 2005 A1
20050106865 Chung et al. May 2005 A1
20050163673 Johnson et al. Jul 2005 A1
20050199739 Kuroda et al. Sep 2005 A1
20050220695 Abatzoglou et al. Oct 2005 A1
20050227864 Sutorik et al. Oct 2005 A1
20050233380 Persiri et al. Oct 2005 A1
20050240069 Polverejan et al. Oct 2005 A1
20050258766 Kim Nov 2005 A1
20050275143 Toth Dec 2005 A1
20060051505 Kortshagen et al. Mar 2006 A1
20060068989 Ninomiya et al. Mar 2006 A1
20060094595 Labarge May 2006 A1
20060096393 Pesiri May 2006 A1
20060105910 Zhou et al. May 2006 A1
20060108332 Belashchenko May 2006 A1
20060153728 Schoenung et al. Jul 2006 A1
20060153765 Pham-Huu et al. Jul 2006 A1
20060159596 De La Veaux et al. Jul 2006 A1
20060166809 Malek et al. Jul 2006 A1
20060222780 Gurevich et al. Oct 2006 A1
20060231525 Asakawa et al. Oct 2006 A1
20070048206 Hung et al. Mar 2007 A1
20070049484 Kear et al. Mar 2007 A1
20070063364 Hsiao et al. Mar 2007 A1
20070084308 Nakamura et al. Apr 2007 A1
20070084834 Hanus et al. Apr 2007 A1
20070087934 Martens et al. Apr 2007 A1
20070163385 Takahashi et al. Jul 2007 A1
20070173403 Koike et al. Jul 2007 A1
20070178673 Gole et al. Aug 2007 A1
20070221404 Das et al. Sep 2007 A1
20070253874 Foret Nov 2007 A1
20070292321 Plischke et al. Dec 2007 A1
20080006954 Yubuta et al. Jan 2008 A1
20080031806 Gavenonis et al. Feb 2008 A1
20080038578 Li Feb 2008 A1
20080057212 Dorier et al. Mar 2008 A1
20080064769 Sato et al. Mar 2008 A1
20080105083 Nakamura et al. May 2008 A1
20080116178 Weidman May 2008 A1
20080125308 Fujdala et al. May 2008 A1
20080138651 Doi et al. Jun 2008 A1
20080175936 Tokita et al. Jul 2008 A1
20080187714 Wakamatsu et al. Aug 2008 A1
20080206562 Stucky et al. Aug 2008 A1
20080207858 Kowaleski et al. Aug 2008 A1
20080274344 Vieth et al. Nov 2008 A1
20080277092 Layman et al. Nov 2008 A1
20080277264 Sprague Nov 2008 A1
20080277267 Biberger et al. Nov 2008 A1
20080277268 Layman Nov 2008 A1
20080277269 Layman et al. Nov 2008 A1
20080277270 Biberger et al. Nov 2008 A1
20080277271 Layman Nov 2008 A1
20080280049 Kevwitch et al. Nov 2008 A1
20080280751 Harutyunyan et al. Nov 2008 A1
20080280756 Biberger Nov 2008 A1
20090010801 Murphy et al. Jan 2009 A1
20090054230 Veeraraghavan et al. Feb 2009 A1
20090088585 Schammel et al. Apr 2009 A1
20090114568 Trevino et al. May 2009 A1
20090162991 Beneyton et al. Jun 2009 A1
20090168506 Han et al. Jul 2009 A1
20090170242 Lin et al. Jul 2009 A1
20090181474 Nagai Jul 2009 A1
20090200180 Capote et al. Aug 2009 A1
20090223410 Jun et al. Sep 2009 A1
20090253037 Park et al. Oct 2009 A1
20090274903 Addiego Nov 2009 A1
20090286899 Hofmann et al. Nov 2009 A1
20100089002 Merkel Apr 2010 A1
20100275781 Tsangaris Nov 2010 A1
20110006463 Layman Jan 2011 A1
20110143041 Layman et al. Jun 2011 A1
20110143915 Yin et al. Jun 2011 A1
20110143916 Leamon Jun 2011 A1
20110143930 Yin et al. Jun 2011 A1
20110143933 Yin et al. Jun 2011 A1
20110144382 Yin et al. Jun 2011 A1
20110152550 Grey et al. Jun 2011 A1
20110158871 Arnold et al. Jun 2011 A1
20110174604 Duesel et al. Jul 2011 A1
20110247336 Farsad et al. Oct 2011 A9
20120045373 Biberger Feb 2012 A1
20120171098 Hung et al. Jul 2012 A1
Foreign Referenced Citations (32)
Number Date Country
56-146804 Nov 1981 JP
61-086815 May 1986 JP
63-214342 Sep 1988 JP
05-228361 Sep 1993 JP
05-324094 Dec 1993 JP
6-272012 Sep 1994 JP
H6-065772 Sep 1994 JP
7031873 Feb 1995 JP
07-256116 Oct 1995 JP
11-502760 Mar 1999 JP
2000-220978 Aug 2000 JP
2004-233007 Aug 2004 JP
2004-249206 Sep 2004 JP
2004-290730 Oct 2004 JP
2005-503250 Feb 2005 JP
2005-122621 May 2005 JP
2005-218937 Aug 2005 JP
2005-342615 Dec 2005 JP
2006-001779 Jan 2006 JP
2006-508885 Mar 2006 JP
2006-247446 Sep 2006 JP
2006-260385 Sep 2006 JP
2007-46162 Feb 2007 JP
493241 Mar 1976 SU
201023207 Jun 2010 TW
WO-9628577 Sep 1996 WO
WO 02092503 Nov 2002 WO
WO 2004052778 Jun 2004 WO
WO 2006079213 Aug 2006 WO
WO-2008130451 Oct 2008 WO
WO-2008130451 Oct 2008 WO
2011081833 Jul 2011 WO
Non-Patent Literature Citations (75)
Entry
“Structure and activity of composite oxide supported platinum-iridium catalysts,” S. Subramanian et al. Applied Catalysis, 74 (1991), pp. 65-81.
A. Gutsch et al., “Gas-Phase Production of Nanoparticles”, Kona No. 20, 2002, pp. 24-37.
Dr. Heike Mühlenweg et al., “Gas-Phase Reactions—Open Up New Roads to Nanoproducts”, Degussa ScienceNewsletter No. 08, 2004, pp. 12-16.
Coating Generation: Vaporization of particles in Plasma Spraying and Splat Formation, M. Vardelle, A. Vardelle, K-I li, P. Fauchais, Universite de Limoges, 123 Avenue A. Thomas 87000, Limoges, F. , Pure & Chem, vol. 68, No. 5, pp. 1093-1099, 1996.
H. Konrad et al., “Nanostructured Cu-Bi Alloys Prepared by Co-Evaporation in a Continuous Gas Flow,” NanoStructured Materials, vol. 7, No. 6, 1996, pp. 605-610.
Kenvin et al. “Supported Catalysts Prepared from Mononuclear Copper Complexes: Catalytic Properties”, Journal of Catalysis, pp. 81-91, (1992).
J. Heberlein, “New Approaches in Thermal Plasma Technology”, Pure Appl. Chem., vol. 74, No. 3, 2002, pp. 327-335.
M. Vardelle et al., “Experimental Investigation of Powder Vaporization in Thermal Plasma Jets,” Plasma Chemistry and Plasma Processing, vol. 11, No. 2, Jun. 1991, pp. 185-201.
National Aeronautics and Space Administration, “Enthalpy”, http://www.grc.nasa.gov/WWW/K-12/airplane/enthalpy.html, Nov. 23, 2009, 1 page.
P. Fauchais et al., “Plasma Spray: Study of the Coating Generation,” Ceramics International, Elsevier, Amsterdam, NL, vol. 22, No. 4, Jan. 1996, pp. 295-303.
P. Fauchais et al., “Les Dépôts Par Plasma Thermique,” Revue Generale De L'Electricitie, RGE. Paris, FR, No. 2, Jan. 1993, pp. 7-12.
P. Fauchais et al, “La Projection Par Plasma: Une Revue,” Annales De Physique, vol. 14, No. 3, Jun. 1989, pp. 261-310.
T. Yoshida, “The Future of Thermal Plasma Processing for Coating”, Pure & Appl. Chem., vol. 66, No. 6, 1994 pp. 1223-1230.
Han et al, Deformation Mechanisms and Ductility of Nanostructured Al Alloys, Mat. Res. Soc. Symp. Proc. vol. 821, Jan. 2004, Material Research Society, http://www.mrs.org/s—mrs/bin.asp?CID=2670&DOC=FILE.PDF., 6 pages.
Nagai, Yasutaka, et al. “Sintering Inhibition Mechanism of Platinum Supported on Ceria-based Oxide and Pt-oxide-support Interaction,”Joumal of Catalysis 242 (2006), pp. 103-109, Jul. 3, 2006, Elsevier.
Derwent English Abstract for publication No. SU 193241 A, Application No. 1973SU1943286 filed on Jul. 2, 1973, published on Mar. 1, 1976, entitled “Catalyst for Ammonia Synthesis Contains Oxides of Aluminium, Potassium, Calcium, Iron and Nickel Oxide for Increased Activity,” 3 pgs.
Young, Lee W., Authorized Officer of the International Searching Authority, International Search Report and Written Opinion mailed Apr. 6, 2011, for PCT Application No. PCT/US 10/59761, 9 pgs.
Bateman, James E. et al., “Alkylation of Porous Silicon by Direct Reaction with Alkenes and Alkynes,” Angew. Chem Int. Ed., Dec. 17, 1998, 37, No. 19, pp. 2683-2685.
Langner Alexander et al., “Controlled Silicon Surface Functionalization by Alkene Hydrosilylation,” J. Am. Chem. Soc., Aug. 25, 2005, 127, pp. 12798-12799.
Liu, Shu-Man et al., “Enhanced Photoluminescence from Si Nano-organosols by Functionalization with Alkenes and Their Size Evolution,” Chem. Mater., Jan. 13, 2006, 18,pp. 637-642.
Fojtik, Anton, “Surface Chemistry of Luminescent Colloidal Silicon Nanoparticles,” J. Phys. Chem. B., Jan. 13, 2006, pp. 1994-1998.
Li, Dejin et al., “Environmentally Responsive “Hairy” Nanoparticles: Mixed Homopolymer Brushes on Silica Nanoparticles Synthesized by Living Radical Polymerization Techniques,” J.Am. Chem. Soc., Apr. 9, 2005, 127,pp. 6248-6256.
Neiner, Doinita, “Low-Temperature Solution Route to Macroscopic Amounts of Hydrogen Terminated Silicon Nanoparticles,” J. Am. Chem. Soc., Aug. 5, 2006, 128, pp. 11016-11017.
Fojtik, Anton et al., “Luminescent Colloidal Silicon Particles,” Chemical Physics Letters 221, Apr. 29, 1994, pp. 363-367.
Netzer, Lucy et al., “A New Approach to Construction of Artificial Monolayer Assemblies,” J. Am. Chem. Soc., 1983, 105, pp. 674-676.
Chen, H.-S. et al., “On the Photoluminescence of Si Nanoparticles,” Mater. Phys. Mech. 4, Jul. 3, 2001, pp. 62-66.
Kwon, Young-Soon et al., “Passivation Process for Superfine Aluminum Powders Obtained by Electrical Explosion of Wires,” Applied Surface Science 211, Apr. 30, 2003, pp. 57-67.
Liao, Ying-Chih et al., “Self-Assembly of Organic Monolayers on Aerosolized Silicon Nanoparticles,” J.Am. Chem. Soc., Jun. 27, 2006, 128, pp. 9061-9065.
Zou, Jing et al., “Solution Synthesis of Ultrastable Luminescent Siloxane-Coated Silicon Nanoparticles,” Nano Letters, Jun. 4, 2004, vol. 4, No. 7, pp. 1181-1186.
Tao, Yu-Tai, “Structural Comparison of Self-Assembled Monolayers of n-Alkanoic Acids on the surfaces of Silver, Copper, and Aluminum,” J. Am. Chem. Soc., May 1993, 115, pp. 4350-4358.
Sailor, Michael et al., “Surface Chemistry of Luminescent Silicon Nanocrystallites,” Adv. Mater, 1997, 9, No. 10, pp. 783-793.
Li, Xuegeng et al., “Surface Functionalization of Silicon Nanoparticles Produced by Laser-Driven Pyrolysis of Silane Followed by HF-HNO3 Etching,” Langmuir, May 25, 2004, pp. 4720-4727.
Carrot, Geraldine et al., “Surface-Initiated Ring-Opening Polymerization: A Versatile Method for Nanoparticle Ordering,” Macromolecules, Sep. 17, 2002, 35, pp. 8400-8404.
Jouet, R. Jason et al., “Surface Passivation of Bare Aluminum Nanoparticles Using Perfluoroalkyl Carboxylic Acids,” Chem. Mater., Jan. 25, 2005, 17, pp. 2987-2996.
Yoshida, Toyonobu, “The Future of Thermal Plasma Processing for Coating,” Pure & Appl. Chem., vol. 66, No. 6, 1994, pp. 1223-1230.
Kim, Namyong Y. et al., “Thermal Derivatization of Porous Silicon with Alcohols,” J. Am. Chem. Soc., Mar. 5, 1997. 119, pp. 2297-2298.
Hua, Fengjun et al., “Organically Capped Silicon Nanoparticles with Blue Photoluminescence Prepared by Hydrosilylation Followed by Oxidation,” Langmuir, Mar. 2006, pp. 4363-4370.
Stiles, A.B., Catalyst Supports and Supported Catalysts, Manufacture of Carbon-Supported Metal Catalysts, pp. 125-132, published Jan. 1, 1987, Butterworth Publishers, 80 Montvale Ave., Stoneham, MA 02180.
Ji, Y. et al. (Nov. 2002) “Processing and Mechanical Properties of Al2O3-5 vol.% Cr Nanocomposites,” Journal of the European Ceramic Society 22(12):1927-1936.
“Platinum Group Metals: Annual Review 1996” (Oct. 1997). Engineering and Mining Journal, p. 63.
Rahaman, R. A. et al. (1995). “Synthesis of Powders,” In Ceramic Processing and Sintering. Marcel Decker, Inc., New York, pp. 71-77.
Ünal, N. et al. (Nov. 2011). “Influence of WC Particles on the Microstructural and Mechanical Properties of 3 mol% Y2O3 Stabilized ZrO2 Matrix Composites Produced by Hot Pressing,” Journal of the European Ceramic Society (31)13: 2267-2275.
U.S. Appl. No. 13/291,983, filed Nov. 8, 2011, for Layman et al.
U.S. Appl. No. 12/152,084, filed May 9, 2008, for Biberger.
U.S. Appl. No. 13/028,693, filed Feb. 16, 2011, for Biberger.
U.S. Appl. No. 12/943,909, filed Nov. 10, 2010, for Layman.
U.S. Appl. No. 12/152,111, filed May 9, 2008, for Biberger et al.
U.S. Appl. No. 12/151,830, filed May 8, 2008, for Biberger et al.
U.S. Appl. No. 12/968,248, filed Dec. 14, 2010, for Biberger.
U.S. Appl. No. 12/968,245, filed Dec. 14, 2010, for Biberger.
U.S. Appl. No. 12/968,241, filed Dec. 14, 2010, for Biberger.
U.S. Appl. No. 12/968,239, filed Dec. 14, 2010, for Biberger.
U.S. Appl. No. 12/969,128, filed Dec. 15, 2010, for Biberger.
U.S. Appl. No. 12/962,463, filed Dec. 7, 2010, for Leamon.
U.S. Appl. No. 12/961,030, filed Dec. 6, 2010, for Lehman.
U.S. Appl. No. 12/961,108, filed Dec. 6, 2010, for Lehman.
U.S. Appl. No. 12/961,200, filed Dec. 6, 2010, for Lehman.
U.S. Appl. No. 12/968,253, filed Dec. 14, 2010, for Biberger.
U.S. Appl. No. 12/968,235, filed Dec. 14, 2010, for Biberger.
U.S. Appl. No. 12/969,306, filed Dec. 15, 2010, for Lehman et al.
U.S. Appl. No. 12/969,447, filed Dec. 15, 2010, for Biberger et al.
U.S. Appl. No. 12/969,087, filed Dec. 15, 2010, for Biberger.
U.S. Appl. No. 12/962,533, filed Dec. 7, 2010, for Yin et al.
U.S. Appl. No. 12/962,523, filed Dec. 7, 2010, for Yin et al.
U.S. Appl. No. 12/001,643, filed Dec. 11, 2007, for Biberger et al.
U.S. Appl. No. 12/474,081, filed May 28, 2009, for Biberger et al.
U.S. Appl. No. 12/001,602, filed Dec. 11, 2007, for Biberger et al.
U.S. Appl. No. 12/001,644, filed Dec. 11, 2007, for Biberger et al.
U.S. Appl. No. 12/969,457, filed Nov. 15, 2010, for Leamon et al.
U.S. Appl. No. 12/969,503, filed Nov. 15, 2010, for Leamon et al.
U.S. Appl. No. 12/954,813, filed Nov. 26, 2010, for Biberger.
U.S. Appl. No. 12/954,822, filed Nov. 26, 2010, for Biberger.
U.S. Appl. No. 13/033,514, filed Feb. 23, 2011, for Biberger et al.
Non-Final Office Action mailed Nov. 8, 2012, for U.S. Appl. No. 12/968,245, filed Dec. 14, 2010, for Biberger et al.; 13 pages.
Non-Final Office Action mailed Nov. 8, 2012, for U.S. Appl. No. 12/968,253, filed Dec. 14, 2010, for Biberger et al., 13 pages.
Related Publications (1)
Number Date Country
20110143926 A1 Jun 2011 US
Provisional Applications (1)
Number Date Country
61284329 Dec 2009 US