METHOD OF FORMING ASYMMETRIC THICKNESS OXIDE TRENCHES

Abstract

We herein describe a method of manufacturing a semiconductor device having one or more trenches with an insulation layer. The one or more trenches with an insulation layer are manufactured using the steps of performing an etching process to form the one or more trenches, forming a first insulation layer on a lower surface and sidewalls of the one or more trenches, depositing a hydrophilic layer over the first insulation layer, depositing a photoresist material in the one or more trenches, wherein depositing a photoresist material comprises exposing the hydrophilic layer on an upper region of a first side of the one or more trenches, performing a wet etch process to etch the insulation layer on the sidewall of the first side of the one or more trenches to a predetermined distance below a surface of the photoresist material, removing the photoresist material, removing the hydrophilic layer, and after performing the wet etch process, removing the photoresist material, and removing the hydrophilic layer, and forming a second insulation layer on the sidewall of the first side of the one or more trenches.

Description

TECHNICAL FIELD

The present disclosure relates to a method of manufacturing a semiconductor device having an insulation layer on selective trench sidewalls.

BACKGROUND

Many applications use fast switching, low loss insulated gate bipolar transistors (IGBTs) or metal oxide semiconductor field-effect transistors (MOSFETs). Trench gate IGBTs with uniform thin oxide have high turn on energy (E_ON) and turn off energy (E_OFF) losses due to high gate collector capacitance (C_GC) and gate emitter capacitance (C_GE)

Asymmetric trench oxide (thin oxide in a portion of one trench sidewall and thick oxide in the remaining areas) to improve performance in trench gate IGBTs and MOSFETs with Silicon and SiC. For example, within IGBTs it is advantageous to provide thick oxide in trench sidewall regions not used as a conduction channel and to provide thin oxide in regions where conduction channels are formed. This reduces the gate collector capacitance (C_GC) and gate emitter capacitance (C_GE)and improves the switching speed. This also reduces the turn on energy loss (E_ON) and the turn off energy loss (E_OFF). In the case of SiC where electric field is 10× higher that silicon, the gate structure also enhance breakdown voltage (BV) capability.

Currently available processes for manufacturing a trench with a non-constant oxide layer are unreliable and result in low yields.

Traditional processing methods rely on using the photolithographic exposure dose to determine etch depth. Due to inherent inaccuracy, the etch depth has the tendency to vary significantly from one site to another across a wafer, from wafer to wafer, and between batches.

“IGBT with superior long-term switching behaviour by asymmetric trench oxide”, Proceedings of the 30th International Symposium on Power Semiconductor Devices & ICs 2018, pp 24-27 relates to an IGBT chip with a trench having an asymmetric thick oxide layer and process for manufacturing the chip.

FIGS. 1(a) and 1(b) illustrate steps of manufacturing trenches with asymmetric insulation layers, according to the state of the art. The manufacturing process starts with a homogenous thick oxide insulation layer, covered by a photoresist material. The photoresist is exposed to remove the photoresist to a desired depth, X. The exposure dose is used to determine the depth X, and thus determines where thin gate oxide will be formed. An etch solution is then used to remove the thick oxide layer over all exposed areas.

This method of manufacture results in large variation of X from wafer to wafer and die to die on a wafer. There is also reduced integrity and stability of the photoresist within the trench during the etch process.

SUMMARY

Aspects and preferred features are set out in the accompanying claims.

According to an embodiment of the present disclosure, there is provided a method of manufacturing a semiconductor device having one or more trenches with an insulation layer, wherein the one or more trenches with an insulation layer are manufactured using the steps of:

• • performing an etching process to form the one or more trenches;
    • forming a first insulation layer on a lower surface and sidewalls of the one or more trenches;
  • depositing a hydrophilic layer over the first insulation layer;
  • depositing a photoresist material in the one or more trenches, wherein depositing a photoresist material comprises exposing the hydrophilic layer on an upper region of a first side of the one or more trenches;
  • performing a wet etch process to etch the insulation layer on the sidewall of the first side of the one or more trenches to a predetermined distance below a surface of the photoresist material;
  • removing the photoresist material;
  • removing the hydrophilic layer; and
  • after performing the wet etch process, removing the photoresist material, and removing the hydrophilic layer; forming a second insulation layer on the sidewall of the first side of the one or more trenches.

Forming a first insulation layer may comprise forming a thick insulation layer, and the hydrophilic layer may be deposited over the thick insulation layer, and forming a second insulation layer may comprise forming a thin insulation layer on the sidewall of the first side of the one or more trenches, wherein the thin insulation layer is thinner than the thick insulation layer.

Alternatively, forming a first insulation layer may comprise forming a thin insulation layer, and forming a second insulation layer may comprise forming a thick insulation layer over the thin insulation layer, wherein the thin insulation layer is thinner than the thick insulation layer.

The presently disclosed method of manufacturing a semiconductor device includes a step of depositing a hydrophilic layer. The hydrophilic layer means that the etchant, in the later step of performing a wet etch, uses capillary action to etch the insulation layer on the sidewalls, below the surface of the photoresist material. The capillary action etches down a channel between the hydrophilic layer and the material (for example, silicon) of the semiconductor device outside the trench. This also allows etching below the surface of the insulation layer, allowing deeper channels to be etched. Furthermore, this helps to achieve uniformity and consistency in both the etching process and the width and depth of the etched portion of the insulation layer. This also increases the controllability of the manufacturing process, in particular the width and depth of the etched portion.

The disclosed manufacturing process includes performing a wet etch that etches down a channel along the sidewall of the trench. This process facilitates the manufacture of devices having trenches with asymmetric or symmetric trench gate regions, having two different insulation layer thicknesses on a sidewall of a trench.

The herein disclosed manufacturing process improves uniformity of channel etch depth and width, and therefore improves electrical performance uniformity from die to die. The disclosed process also has improved process control and yield. The disclosed process results in a reduced number of defects caused by instability of photoresist during wet etch down deep trenches, compared to state-of-the-art methods of manufacturing trenches.

The method may be used to process devices of Silicon, SiC, GaN, and other materials used in semiconductor devices.

The method may be used to manufacture insulated gate bipolar transistors (IGBTs), metal oxide semiconductor field-effect transistors (MOSFETs), MOS-Controlled Thyristors, or other semiconductor power devices.

Depositing a photoresist material may be a two-step process that includes depositing a photoresist material and then exposing the hydrophilic layer on an upper region of a first side of the one or more trenches.

The method may further comprise depositing a filling material after growing the thin insulation layer.

The hydrophilic layer may comprise nitride. The hydrophilic layer may comprise Si_xN_y (silicon nitride) or another material with good wettability or a high degree of wetting. The wettability modulates etch rate down trench side-walls, and enables uniformity of etch distance and repeatability of the process. If wettability is not sufficient, some areas will etch faster than others down the trench walls by the capillary action. A material with high degree of wetting improves the capillary action that etches down a channel. The wettability property of the hydrophilic layer allows accurate control of etch depth and ensures uniformity of the etch process down the etched channel.

The hydrophilic layer may have a thickness between 1000 Å and 2500 Å. The thickness of the hydrophilic layer mains integrity during the wet etch/capillary etch process.

The step of performing a wet etch may be carried out using a buffered oxide etch (BOE). The semiconductor device or wafer may be immersed in the BOE in order to etch the insulation layer along any exposed mesa region and trench sidewalls. Exposure to the bottom of deep trenches is difficult except for very wide trenches. The use of a wet etch means that exposure to the bottom of the trench is not required. The wet etch makes use of capillary action of the etch solution (such as BOE 7:1 HCL) to etch down the exposed sidewall and up the second trench sidewall to a desired distance.

The buffered oxide etch may comprise hydrofluoric (HF) acid. Hydrofluoric acid is a suitable solution for use in semiconductor manufacturing, and provides sufficient etch rate to make the process manufacturable.

Forming a thick insulation layer may comprise thermally growing a thick oxide layer using a local oxidation of silicon process.

Alternatively, forming a thick insulation layer may comprise depositing a thick oxide layer.

Depositing a thick oxide layer may be carried out using Tetraethyl Orthosilicate (TEOS) deposition. TEOS deposition is very conformal.

The thick insulation layer may have a thickness between 1800 Å and 5000 Å.

Growing a thin insulation layer may comprise thermally growing a thin oxide layer at 900° C. to 1100° C.

The thin insulation layer may have a thickness between 500 Å to 1800 Å.

The method may comprise manufacturing one or more trenches with an asymmetric insulation layer. The one or more trenches may have one sidewall with an insulation layer of two different thicknesses, and one sidewall with an insulation layer of constant thickness. The step of performing a wet etch may be used to etch along only one sidewall of the one or more trenches.

Alternatively or additionally, the method may comprise manufacturing one or more trenches with a symmetric insulation layer. The one or more trenches may have both sidewalls each with an insulation layer of two different thicknesses. Depositing a photoresist material may comprise exposing the hydrophilic layer on an upper region of two sides of the one or more trenches. The method may further comprise performing a wet etch process to etch the insulation layer on two sidewalls of the one or more trenches to a predetermined distance below a surface of the photoresist material, and growing a thin insulation layer on the two sidewalls of the one or more trenches.

The method may comprise manufacturing at least two trenches each with an insulation layer. A first trench may be separated from a second trench by a mesa region between the two trenches. The first side of the first trench may be adjacent to the first side of the second trench. Depositing a photoresist material may comprise exposing the hydrophilic layer in the mesa region between the first and second trenches.

The method may further comprise removing the hydrophilic layer in the mesa region between the two trenches. This allows the thick oxide in the mesa region to be removed by etching, as the thick oxide in the mesa region is therefore not protected by the hydrophilic layer. This also removes the hydrophilic layer above the thick oxide on the trench sidewall so that the thick oxide on the sidewall can be etched.

Removing the hydrophilic layer in the mesa region may comprise removing the hydrophilic layer such that a top surface of the hydrophilic layer is recessed relative to a surface of the thick oxide layer.

The method may further comprise performing a wet etch process to etch the insulation layer on the mesa region. This removes the thick insulation layer on the mesa region.

BRIEF DESCRIPTION OF THE DRAWINGS

The present disclosure will be understood, by way of example only, from the detailed description that follows and from the accompanying drawings in which:

FIGS. 1(a) and 1(b) illustrate steps of manufacturing trenches with asymmetric insulation layers, according to the state of the art;

FIGS. 2(a) to 2(j) illustrate steps of manufacturing trenches with asymmetric insulation layers, according to an embodiment of the disclosure;

FIG. 3 illustrates schematically a semiconductor device having trenches manufactured using a method according to an embodiment of the disclosure;

DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

FIGS. 2(a) to 2(j) illustrate steps within the manufacturing process of trenches with asymmetric insulation layers, according to an embodiment of the disclosure.

FIG. 2(a) illustrates the first step of manufacturing two trenches with asymmetric insulation layers, which is as follows:

• • (a) Step 1
    • A thin oxide layer 204 is deposited on a silicon substrate 206. The thin oxide layer has thickness of approximately 500 Å to 1800 Å.

FIG. 2(b) illustrates the second step of manufacturing two trenches, which is as follows:

• • (b) Step 2
    • Photolithography and then a dry etch step using plasma source to form trenches to desired depth z in the silicon substrate 206. In this embodiment, the desired depth z of the trenches is 3 μm to 6 μm.

FIG. 2(c) illustrates the third step of manufacturing two trenches, which is as follows:

• • (c) Step 3
    • A thick oxide layer 204 is thermally grown or deposited on the sidewalls and bottom surface of the trenches. The thick oxide layer 204 may be deposited using TEOS. The thick oxide layer has a thickness of approximately 1800 Å to 5000 Å.
    • A hydrophilic layer 206 such as nitride is deposited over the oxide layer 204. The nitride layer 206 has a thickness of approximately 1000 Å to 2500 Å.

FIG. 2(d) illustrates the fourth step of manufacturing two trenches, which is as follows:

• • (d) Step 4
    • The trenches are filled with a photoresist material 208.
    • The photoresist 208 is deposited such that the hydrophilic layer 206 is exposed on a first side of each trench for which asymmetric oxide will be manufactured, and in the mesa region between trenches.
    • The first side of each trench (the side where the hydrophilic layer 206 is exposed) is the side of the trench that will be manufactured to have a thin oxide layer, whilst the side of each trench that will be manufactured to have thick oxide remains covered by the photoresist.
    • The thickness of the photoresist is 1.0 μm to 1.5 μm for a 1.5 μm width trench.

FIG. 2(e) illustrates the fifth step of manufacturing two trenches, which is as follows:

• • (e) Step 5
    • An etch process is performed on the exposed hydrophilic layer 206. The etch process can be a wet or dry etch, and stops on the thick oxide layer 204 in the mesa region.
    • In embodiments where the hydrophilic layer 206 is nitride, the etch process may be done in plasma ambient (an atmosphere or environment of plasma, created by a mixture of gases) using CF4/HBr chemistry.
    • The hydrophilic layer 206 is etched such that the edges of the hydrophilic layer 206 are recessed relative to the surface of the thick oxide 204.

FIG. 2(f) illustrates the sixth step of manufacturing two trenches, which is as follows:

• • (f) Step 6
    • The whole wafer is immersed in a BOE (buffered oxide etch) such as 7:1 HF. The buffered oxide etchant etches the oxide layer 204 on the exposed mesa region and the trench sidewalls extending down from the exposed mesa region to a desired depth Y below the surface of the trench.
    • The hydrophilic layer 206 creates a capillary action so that the etchant etches the oxide layer 204 along the narrow channel between the hydrophilic layer itself 206 and the silicon 202.
    • The presence of the hydrophilic layer 206 allows control of the etch depth and uniformity of the etch process. The hydrophilic layer 206 reduces defects formed during the etch process.

FIG. 2(g) illustrates the seventh step of manufacturing two trenches, which is as follows:

• • (g) Step 7
    • The photoresist is stripped (removed) using any suitable wet (such as hot phosphoric acid) or dry (such as a mixture of CF4 and HBr gases in a plasma etch chamber) chemistry.

FIG. 2(h) illustrates the eighth step of manufacturing two trenches, which is as follows:

• • (h) Step 8
    • The hydrophilic layer is stripped (removed) using any suitable wet or dry chemistry. This leaves the trenches having only oxide 204 on regions not exposed in Steps 4 and 5.

FIG. 2(i) illustrates the ninth step of manufacturing two trenches, which is as follows:

• • (i) Step 9
    • A thin oxide layer 210 is grown on the exposed silicon in a furnace step at 900° C. to 1100° C. The thin oxide layer grows on the first side of each trench in which the hydrophilic layer was exposed in Step 4, and in the mesa region between the trenches.
    • The thin oxide layer has thickness of approximately 500A to 1800A.

FIG. 2(j) illustrates the tenth step of manufacturing two trenches, which is as follows:

• • (j) Step 10
    • Polysilicon 212 is deposited to fill the trenches. The polysilicon 212 is planarised by etching the top of the polysilicon 212 to level off with the silicon 202 in the mesa region between the trenches.

FIG. 3 illustrates schematically a semiconductor device having trenches manufactured using a method according to an embodiment of the disclosure. In this device, the active gates T1, each have asymmetric trench oxide insulation layers, whilst the dummy (or auxiliary trenches) T2 have symmetric thick oxide insulation layers.

The active trenches T1 shown in this embodiment each have an asymmetric oxide. In this embodiment only the electron conduction channel region has thin oxide 210, and the remaining sidewall and bottom of each of the active trenches T1 have thick oxide 204. The thin oxide 210 in the channel region reduces the input capacitance (C_in) and C_GC. This results in reduced gate charge and faster turn-off and turn-on times, therefore reducing E_ON and E_OFF respectively.

Whilst the auxiliary trenches T2 are shown as having thick oxide insulation 204, alternatively the disclosed method could be used to manufacture a semiconductor device having auxiliary trenches with symmetric thin oxide or having variable oxide thickness.

FIGS. 4(a) to 4(i) shows steps in the manufacturing method of a semiconductor device, according to an embodiment of the disclosure;

FIG. 4(a) illustrates the first step of manufacturing the trenches of the semiconductor device, which is as follows:

• • (a) Step 1
    • Trenches 905 are etched.
    • An initial oxide layer 910 is formed over the trenches. The initial oxide layer 910 is a sacrificial oxidation layer. It is an oxide layer created immediately after silicon etch to create trenches. The main purpose of this layer is to remove surface roughness created by the trench etch process. Traditionally, this oxide is later removed prior to formation of the thin gate oxide.
    • A hydrophilic layer 915 such as nitride is deposited over the initial oxide layer 910. The nitride layer 915 has a thickness of approximately 1000 Å to 2500 Å.
    • A thin oxide layer 920 is deposited using TEOS over the hydrophilic layer 915. The thin oxide layer 920 has thickness of approximately 500 Å to 1800 Å.

FIGS. 4(b) and 4(c) illustrates the second step of manufacturing the trenches of the semiconductor device, which is as follows:

• • (b) Step 2
    • Photolithography is performed to apply a photoresist mask 925 that fills the trenches, where the mask ends in the centre of one trench 930 (for example, the active trench) and at least one other trench 935 (for example, a dummy trench). This leaves half of the active trench and the dummy trench exposed, as well as the mesa region between the trenches. The mask 925 may be applied in a two-step process as shown in which the mask is deposited and then etched to expose the TEOS 920.
    • The photoresist 925 is deposited such that the thin oxide layer 920 is exposed on a first side of each trench for which asymmetric oxide will be manufactured, and in the mesa region 940 between trenches.
    • The first side of each trench (the side where the thin oxide layer 920 is exposed) is the side of the trench that will be manufactured to have a thick oxide layer, whilst the side of each trench that will be manufactured to have thin oxide or oxide of different thickness remains covered by the photoresist.

FIG. 4(d) illustrates the first step of manufacturing the trenches of the semiconductor device, which is as follows:

• • (d) Step 3
    • A wet etch is performed on the thin oxide layer 920. The etch may be performed by immersing the whole wafer in a BOE (buffered oxide etch) such as 7:1 HF. The buffered oxide etchant etches the oxide layer 920 on the exposed mesa region 940, the exposed trench sidewalls and bottom, and the trench sidewalls extending up from the trench bottom to a desired height Y above the bottom surface of the trench.
    • The hydrophilic layer 915 creates a capillary action so that the etchant etches the oxide layer 920 along the narrow channel between the hydrophilic layer 915 itself and the photoresist 925.
    • The presence of the hydrophilic layer 915 allows control of the etch depth and uniformity of the etch process. The hydrophilic layer 915 reduces defects formed during the etch process.

FIG. 4(e) illustrates the first step of manufacturing the trenches of the semiconductor device, which is as follows:

• • (e) Step 4
    • The photoresist is stripped (removed) using any suitable wet or dry chemistry.
    • An etch process is performed to remove the exposed regions of the hydrophilic layer 915. The etch process can be a wet or dry etch, and stops on the initial oxide layer 910.
    • In embodiments where the hydrophilic layer 915 is nitride, the etch process may be done in plasma ambient using CF4/HBr chemistry.

FIG. 4(f) illustrates the first step of manufacturing the trenches of the semiconductor device, which is as follows:

• • (f) Step 5
    • A thick oxide layer 945 is thermally grown or deposited on the sidewalls and bottom surface of the trenches in areas without the hydrophilic layer 915 remaining. The thick oxide layer 945 may be deposited using loyal oxidation of silicon (LOCOS). The thick oxide layer 945 has a thickness of approximately 1800 Å to 5000 Å.

FIG. 4(g) illustrates the first step of manufacturing the trenches of the semiconductor device, which is as follows:

• • (g) Step 6
    • An etch process is performed to remove the remaining regions of the hydrophilic layer 915 and the remaining TEOS 920.

FIG. 4(h) illustrates the first step of manufacturing the trenches of the semiconductor device, which is as follows:

• • (h) Step 7
    • Photolithography is performed to apply a photoresist mask 950 that fills the active trench 930, where the mask leaves the dummy trenches 935 exposed.
    • A wet etch process is performed that strips the dummy trenches 935 to the silicon layer.

FIG. 4(i) illustrates the first step of manufacturing the trenches of the semiconductor device, which is as follows:

• • (i) Step 8
    • A thin oxidation layer 955 is grown on the dummy trenches having a constant thickness on the sidewalls and bottom surfaces. The thin oxide 955 layer may be is grown in a furnace step at 900° C. to 1100° C. The thin oxide layer 955 has thickness of approximately 500 Å to 1800 Å.
    • The photoresist is stripped (removed) using any suitable wet or dry chemistry.
    • Polysilicon 960 is deposited to fill the trenches. The polysilicon 960 is planarised by etching the top of the polysilicon 960 to level off with the silicon in the mesa region between the trenches.

FIG. 5 shows an example of a semiconductor device manufactured using the steps of FIGS. 4(a) to 4(h).

The skilled person will understand that in the preceding description and appended claims, positional terms such as ‘above’, ‘overlap’, ‘under’, ‘lateral’, etc. are made with reference to conceptual illustrations of an apparatus, such as those showing standard cross-sectional perspectives and those shown in the appended drawings. These terms are used for ease of reference but are not intended to be of limiting nature. These terms are therefore to be understood as referring to a device when in an orientation as shown in the accompanying drawings.

It will be appreciated that all doping polarities mentioned above could be reversed, the resulting devices still being in accordance with embodiments of the present invention.

Although the disclosure has been described in terms of preferred embodiments as set forth above, it should be understood that these embodiments are illustrative only and that the claims are not limited to those embodiments. Those skilled in the art will be able to make modifications and alternatives in view of the disclosure, which are contemplated as falling within the scope of the appended claims. Each feature disclosed or illustrated in the present specification may be incorporated in the disclosure, whether alone or in any appropriate combination with any other feature disclosed or illustrated herein.

Claims

1. A method of manufacturing a semiconductor device having one or more trenches with an insulation layer, wherein the one or more trenches with an insulation layer are manufactured using the steps of: performing an etching process to form the one or more trenches;forming a first insulation layer on a lower surface and sidewalls of the one or more trenches;depositing a hydrophilic layer over the first insulation layer;depositing a photoresist material in the one or more trenches, wherein depositing a photoresist material comprises exposing the hydrophilic layer on an upper region of a first side of the one or more trenches;performing a wet etch process to etch the insulation layer on the sidewall of the first side of the one or more trenches to a predetermined distance below a surface of the photoresist material;removing the photoresist material;removing the hydrophilic layer; andafter performing the wet etch process, removing the photoresist material, and removing the hydrophilic layer; forming a second insulation layer on the sidewall of the first side of the one or more trenches.

2. A method according to claim 1, wherein forming a first insulation layer comprises forming a thick insulation layer, and wherein the hydrophilic layer is deposited over the thick insulation layer, andwherein forming a second insulation layer comprises forming a thin insulation layer on the sidewall of the first side of the one or more trenches, wherein the thin insulation layer is thinner than the thick insulation layer.

3. A method according to claim 1, wherein forming a first insulation layer comprises forming a thin insulation layer, and wherein forming a second insulation layer comprises forming a thick insulation layer over the thin insulation layer, wherein the thin insulation layer is thinner than the thick insulation layer.

4. A method according to claim 1, wherein the method further comprises depositing a filling material after growing the thin insulation layer.

5. A method according to claim 1, wherein the hydrophilic layer comprises nitride.

6. A method according to claim 1, wherein the hydrophilic layer has a thickness between 1000 Å and 2500 Å.

7. A method according to claim 1, wherein the step of performing a wet etch is carried out using a buffered oxide etch.

8. A method according to claim 7, wherein the buffered oxide etch comprises hydrofluoric acid.

9. A method according to claim 1, wherein forming a thick insulation layer comprises thermally growing a thick oxide layer using a local oxidation of silicon process.

10. A method according to claim 1, wherein forming a thick insulation layer comprises depositing a thick oxide layer.

11. A method according to claim 10, wherein depositing a thick oxide layer is carried out using Tetraethyl Orthosilicate (TEOS).

12. A method according to claim 1, wherein the thick insulation layer has a thickness between 1800 Å and 5000 Å.

13. A method according to claim 1, wherein growing a thin insulation layer comprises thermally growing a thin oxide layer at 900° C. to 1100° C.

14. A method according to claim 1, wherein the thin insulation layer has a thickness between 500 Å to 1800 Å.

15. A method according to claim 1, wherein the method comprises manufacturing one or more trenches with an asymmetric insulation layer.

16. A method according to claim 1, wherein the method comprises manufacturing one or more trenches with a symmetric insulation layer, and wherein depositing a photoresist material comprises exposing the hydrophilic layer on an upper region of two sides of the one or more trenches, andwherein the method further comprises: performing a wet etch process to etch the insulation layer on two sidewalls of the one or more trenches to a predetermined distance below a surface of the photoresist material; andgrowing a thin insulation layer on the two sidewalls of the one or more trenches.

17. A method according to claim 1, wherein the method comprises manufacturing at least two trenches each with an insulation layer, wherein a first trench is separated from a second trench by a mesa region between the two trenches; and wherein the first side of the first trench is adjacent to the first side of the second trench; andwherein depositing a photoresist material comprises exposing the hydrophilic layer in the mesa region between the first and second trenches.

18. A method according to claim 17, wherein the method further comprises removing the hydrophilic layer in the mesa region between the two trenches.

19. A method according to claim 18, wherein removing the hydrophilic layer in the mesa region comprises removing the hydrophilic layer such that a top surface of the hydrophilic layer is recessed relative to a surface of the thick oxide layer.

20. A method according to claim 17, wherein the method further comprises performing a wet etch process to etch the insulation layer on the mesa region.