Patent Application
20120208342
An aspect of the embodiments discussed herein is directed to a method of manufacturing a semiconductor device including a transistor and a non-volatile memory.
A semiconductor device including a transistor and a non-volatile memory has established product lines, such as a complex programmable logic device (CPLD) and a field programmable gate array (FPGA), and has developed a large market because of its programmable features.
In a semiconductor device including a transistor and a non-volatile memory, for example, besides flash memory cells, high-voltage transistors for flash memory control and low-voltage transistors for high performance logic circuit are integrated on one semiconductor chip. In this case, unlike a single layer gate electrode structure of the high-voltage transistor or the low-voltage transistor, the flash memory cell has a stack gate electrode structure including a floating gate and a control gate laminated to each other.
In general, in the gate electrode of the flash memory cell having a stack gate structure, the floating gate is formed from a first layer conductive film, and the control gate is formed from a second layer conductive film. The gate electrode of a peripheral transistor having a single layer gate structure is formed from the second layer conductive film. In addition, between the floating gate and the control gate, an inter-gate insulating film is formed to insulate between the above two gates for capacitive coupling. This inter-gate insulating film is formed of a multilayer film (such as an ONO film) typically including a silicon oxide film and a silicon nitride film and is not formed in a peripheral transistor forming region. Hence, in a process of manufacturing a semiconductor device including a transistor and a non-volatile memory, before the second layer conductive film is deposited, removing the inter-gate insulating film provided in the peripheral transistor forming region may be performed.
In addition, as the non-volatile memory, besides the above flash memory, a non-volatile memory having a single layer gate structure in which an insulating film (such as an ONO film) is used as a charge storage layer has also been known. In the case of this non-volatile memory, before a gate electrode is formed, the charge storage layer provided in a peripheral transistor forming region may be removed. A high-voltage transistor used for controlling a non-volatile memory has been formed by a manufacturing process similar to that for the flash memory described above.
The prior arts regarding to the manufacturing method how to remove the a multilayer film from the semiconductor substrate are known in the patent documents as follows: Japanese Laid-open Patent Publication No. 02-244628 and M. Hayashi et al., “Deposition species from fluorocarbon film by Ar+ ion beam bombardment”, J. Vac. Sci. Technol. A, Vol. 18, No. 4, July/August 2000, pp. 1881 to 1886.
According to an aspect of an embodiment, a method of manufacturing a semiconductor device includes forming an isolation region defining an active region in a semiconductor substrate, forming a first insulating film over the semiconductor substrate, forming a second insulating film having etching properties different from those of the first insulating film over the first insulating film, selectively removing the second insulating film from a first region over the active region and the isolation region by dry etching using a fluorocarbon-based etching gas, removing a residual film formed by the dry etching over the first insulating film by exposure in an atmosphere containing oxygen; and selectively removing the first insulating film from the first region by wet etching.
The object and advantages of the invention will be realized and attained by means of the elements and combinations particularly pointed out in the claims.
It is to be understood that both the foregoing general description and the following detailed description are exemplary and explanatory and are not restrictive of the invention, as claimed.
As described previously, when the process of manufacturing a semiconductor device including a transistor and a non-volatile memory was investigated by the inventors of the embodiments, it was found that in a semiconductor device manufactured by the process described above, the withstand voltage of a gate insulating film of a peripheral transistor may be degraded.
Preferred embodiments of the present embodiments will be explained with reference to accompanying drawings.
A method of manufacturing a semiconductor device according to a first embodiment will be described with reference to
The structure of the semiconductor device according to this embodiment will be first described with reference to
The semiconductor device according to this embodiment is semiconductor device including a transistor and a non-volatile memory each having a stack structure. As illustrated in
The non-volatile memory (Flash) has, as illustrated in
The low-voltage transistor (LV-Tr) has, as illustrated in
The medium-voltage transistor (MV-Tr) has, as illustrated in
The high-voltage transistor (HV-Tr) has, as illustrated in
The thickness of the gate insulating film of the peripheral transistor is increased in accordance with the withstand voltage of each transistor, that is, the thicknesses of the gate insulating films 54, 56, and 58 are increased in this order.
In this embodiment, although one low-voltage transistor (LV-Tr), one medium-voltage transistor (MV-Tr), and one high-voltage transistor (HV-Tr) are only illustrated, n-type and p-type conduction transistors are practically included in each transistor. In addition, transistors having different threshold voltages may also be used in some cases.
Next, the method of manufacturing a semiconductor device according to this embodiment will be described with reference to
First, the surface of the silicon substrate 10 is thermally oxidized, for example, by a thermal oxidation method, so that a silicon oxide film 12 having a thickness of, for example, approximately 8 nm to 16 nm is formed. The silicon oxide film 12 may be formed on the silicon substrate 10, or the silicon oxide film 12 may be formed over the silicon substrate 10.
Next, a silicon nitride film 14 having a thickness of, for example, 55 nm to 130 nm is formed on the silicon oxide film 12, for example, by a thermal chemical vapor deposition (CVD) method performed at a temperature of 700° C. to 900° C. The silicon nitride film 14 may be formed on the silicon oxide film 12, or the silicon nitride film 14 may be formed over the silicon oxide film 12.
Subsequently, a polysilicon film 16 having a thickness of, for example, 60 nm to 120 nm is formed on the silicon nitride film 14, for example, by a thermal CVD method performed at a temperature of 550° C. to 680° C.
A bottom anti-reflective coating (BARC) film 18 and a photoresist film 20 are then formed on the polysilicon film 16 by a spin coating method.
Subsequently, by photolithography, opening portions exposing regions where the isolation films are to be formed are formed (
Next, by using the photoresist film 20 as a mask, the BARC film 18, the polysilicon film 16, and the silicon nitride film 14 are patterned by dry etching, so that the pattern of the photoresist film 20 is transferred to the polysilicon film 16 and the silicon nitride film 14 (
The polysilicon film 16 is a film to be used as a hard mask when the silicon nitride film 14 is patterned. When the silicon nitride film 14 may be sufficiently patterned only by the photoresist film 20, it is not always necessary to form the polysilicon film 16.
Next, by ashing and a subsequent post-treatment, the BARC film 18 and the photoresist film 20 remaining on the polysilicon film 16 are removed (
Subsequently, the silicon oxide film 12 and the silicon substrate 10 are etched by using the patterned polysilicon film 16 and silicon nitride film 14 as a mask, so that trenches 22 for element isolation are formed in the silicon substrate 10 (
Next, an appropriate post-treatment is performed whenever necessary, so that byproducts generated by the etching and adhering to the surface of the silicon substrate 10 are removed.
For example, by a thermal oxidation method, the silicon substrate 10 is then thermally oxidized using the silicon nitride 14 as a mask, so that a silicon oxide film 24 having a thickness of, for example, 1 nm to 18 nm is formed inside the trench 22.
Subsequently, a silicon oxide film 26 having a thickness of, for example, 250 nm to 750 nm is formed on the entire surface, for example, by a high density plasma (HDP) CVD method performed at a temperature of 250° C. to 600° C. (
Next, the surface of the silicon oxide film 26 is polished by a chemical mechanical polishing (CMP) method until the surface of the silicon nitride film 14 is exposed, so that the surface is planarized. Accordingly, isolation films 28 composed of the silicon oxide film 24 and 26 are formed (
By an appropriate post-treatment, a slurry used for the CMP was then removed.
Subsequently, in a nitrogen atmosphere, for example, a heat treatment is performed at a temperature of 800° C. to 1,100° C.
Next, a photoresist film 30 is formed on the entire surface by a spin coating method and is then patterned by photolithography so as to cover the peripheral circuit region and so as to expose the memory cell region.
Next, by using the photoresist film 30 as a mask, for example, wet etching using an aqueous hydrofluoric acid solution is performed, so that the upper surface of the isolation film 28 is etched by, for example, approximately 10 nm to 80 nm, (
Subsequently, for example, wet etching is performed using an aqueous hydrofluoric acid solution diluted with pure water at a ratio of approximately 10:1 to 200:1, so that a native oxide film (not illustrated) on the silicon nitride film 14 is removed.
Next, for example, wet etching using a phosphoric acid solution at a temperature of 130° C. is performed, so that the silicon nitride film 14 is removed.
For example, by wet etching using an aqueous hydrofluoric acid solution, the silicon oxide film 12 is then removed.
Next, a silicon oxide film having a thickness of, for example, 8 nm to 16 nm is formed on the surface of the silicon substrate 10, for example, by a thermal oxidation method. As a result, a sacrifice oxide film 32 composed of a silicon oxide film for ion implantation is formed (
Subsequently, by photolithography and ion implantation, predetermined wells (not illustrated) are formed in the memory cell region and the high-voltage transistor forming region. For example, double wells in which a p-type well is formed in an n-type well are formed in the memory cell region and an n-type high-voltage transistor forming region, and an n-type well is formed in a p-type high-voltage transistor forming region. The n-type well is formed by performing ion implantation using, for example, phosphorous ions under the conditions in which, for example, the acceleration energy is set to 300 keV to 500 keV, and the dose amount is set to 1×1011 cm−2 to 1×1014 cm−2. The p-type well is formed by performing ion implantation using, for example, boron ions under the conditions in which, for example, the acceleration energy is set to 100 keV to 350 keV, and the dose amount is set to 1×1012 cm−2 to 1×1015 cm−2. An n-type buried layer at the bottom of the double well is formed by performing ion implantation using, for example, phosphorous ions under the conditions in which, for example, the acceleration energy is set to 1.6 MeV to 2.6 MeV, and the dose amount is set to 2×1011 cm−2 to 2×1015 cm2.
Next, in a nitrogen atmosphere, for example, a heat treatment is performed at a temperature of 900° C. to 1,200° C. for 1 second to 15 seconds, so that the implanted impurities are activated.
Subsequently, for example, wet etching is performed using an aqueous hydrofluoric acid solution diluted with pure water at a ratio of approximately 10:1 to 200:1, so that the sacrifice oxide film 32 is removed.
In addition, the thickness of the isolation film 28 is gradually decreased, for example, by the operations of removing the silicon oxide film 12 and the sacrifice oxide film 32. As a result, after the sacrifice oxide film 32 is removed, a recess which is recessed from the surface of the active region is formed at the boundary between the isolation film 28 and the active region.
The tunnel insulating film 34 composed of a silicon oxide film having a thickness of, for example, 3 nm to 15 nm is then formed on the surface of the silicon substrate 10 (
Subsequently, an amorphous silicon film 36 is formed on the entire surface of the silicon substrate 10, for example, by a CVD method so as to have a thickness of, for example, 50 nm to 100 nm and to include phosphorous at a concentration of, for example, 0.2×1019 cm−3 to 10×1019 cm−3 (
A bottom anti-reflective coating (BARC) film 38 and a photoresist film 40 are then formed on the amorphous silicon film 36 by a spin coating method.
Next, the photoresist film 40 in the peripheral circuit region is removed, and an opening portion exposing a predetermined region in the memory cell region is formed in the photoresist film 40 by photolithography (
Next, by using the photoresist film 40 as a mask, for example, anisotropic etching is performed in an inductively coupled plasma etching apparatus, so that the amorphous silicon film 36 is patterned (
Next, by ashing and a subsequent post-treatment, the BARC film 38 and the photoresist film 40 remaining on the amorphous silicon film 36 are removed.
Next, the ONO film 42 having a multilayer structure of a silicon oxide film, a silicon nitride film, and a silicon oxide film is formed on the entire surface of the silicon substrate 10 (
By photolithography and ion implantation, predetermined wells (not illustrated) are then formed in a low-voltage transistor forming region and a medium-voltage transistor forming region. For example, p-type wells are formed in an n-type low-voltage transistor forming region and an n-type medium-voltage transistor forming region, and n-type wells are formed in a p-type low-voltage transistor forming region and a p-type medium-voltage transistor forming region.
Next, a photoresist film 44 is formed on the entire surface of the silicon substrate 10 by a spin coating method and is then patterned by photolithography so as to expose the peripheral circuit region and so as to cover the memory cell region.
Subsequently, by using the photoresist film 44 as a mask, for example, dry etching is performed in a magnetron reactive ion etching (RIE) apparatus, so that the top oxide film and the silicon nitride film, which is an intermediate layer, of the ONO film 42 are etched.
The thicknesses of the individual films forming the ONO film 42 are each very small, such as 10 nm or less. In addition, since the recess is formed at the boundary between the active region and the isolation film, in order to remove a film formed in the recess (inclined portion), an over-etching amount may be increased to a degree of 300% or more. Accordingly, when the individual films forming the ONO film 42 are etched, the selectivity with respect to the underlayer may be sufficiently ensured.
In view of the above point, for example, a mixed gas including some of C4F8, C4F6, Ar, and O2 in combination is used as an etching gas to etch the top oxide film, and etching is performed under conditions in which the selectivity with respect to the silicon nitride film as an underlayer is approximately 6.0 or more. In addition, in order to etch the silicon nitride film, which is the intermediate layer, a mixed gas including some of CH3F, Ar, and O2 in combination is used, and etching is performed under conditions in which the selectivity with respect to the bottom oxide film as an underlayer is approximately 9.0 or more.
Under the above etching conditions using a fluorocarbon-based etching gas, as the etching proceeds, a fluorocarbon film as the residual film formed as a by product is deposited on the surface of the substrate. The fluorocarbon film may be deposited on the substrate, or the fluorocarbon film may be deposited over the substrate.
Next, the fluorocarbon film as the residual film deposited on the surface of the substrate is removed by any one of the following methods. The fluorocarbon film as the residual film may be deposited on the surface of the substrate, or the fluorocarbon film as the residual film may be deposited over the surface of the substrate.
According to a first method, the substrate is exposed to a mixed gas including an Ar gas and an oxygen gas in a magnetron RIE apparatus, so that the fluorocarbon film is removed. When the fluorocarbon formed as a byproduct of etching is irradiated with argon beams, fluorine elements are removed, and as a result, a carbon-rich film is formed. When oxygen is allowed to react with this film, the fluorocarbon film may be removed. This method provides advantage in that the treatment may be sequentially performed in the same apparatus following the etching of the top oxide film and the silicon nitride film of the ONO film 42.
As the particular conditions, for example, the RF power is 100 W to 300 W, the pressure is 40 millitorr to 100 millitorr, the total flow rate of the process gas is 100 sccm to 600 sccm, the gas mixing ratio of Ar: O2 is 100:1 to 100:15, the electrode temperature is 50° C., and the process time is 10 seconds to 60 seconds.
The addition amount of an oxygen gas is set in the range of 0.5% to 25% and preferably in the range of approximately 0.5% to 10% with respect to the total flow rate of the process gas. The reasons for this are that when the addition amount of oxygen is less than 0.5%, an effect of removing a fluorocarbon film may not be sufficiently obtained, and when the addition amount of oxygen is more than 25%, ashing of the photoresist film 44 becomes significant. Since the photoresist film 44 is also used as a mask film in the following wet etching operation for removing the bottom oxide film, the photoresist film 44 may have a sufficient thickness for the following wet etching even after the fluorocarbon film is removed.
According to a second method, chemical dry etching is performed to remove the fluorocarbon film using a mixed gas including an oxygen gas, a CF4 gas, and a forming gas (mixed gas including 3% of hydrogen and 97% of nitrogen, hereinafter referred to as “FG” in some cases) in a downflow etching apparatus. The CF4 gas enhances the reactivity of oxygen radicals to the fluorocarbon film and also functions to promote etching of the fluorocarbon film. In addition, the forming gas functions to increase life of oxygen radicals.
As the particular conditions, for example, the microwave power is 800 W to 1,100 W, the pressure is 150 Pa to 300 Pa, the total flow rate of the process gas is 1,200 sccm to 2,000 sccm, the gas mixing ratio of O2:CF4:FG is 617:374:1 to 61:38:1, and the process time is 10 seconds to 33 seconds.
The addition amount of the CF4 gas is set in the range of 0.05% to 3% and preferably in the range of approximately 0.1% to 1% with respect to the total flow rate of the process gas. The reasons for this are that when the addition amount of the CF4 gas is less than 0.05%, the effect of removing a fluorocarbon film may not be sufficiently obtained since the reactivity of oxygen radicals is too low, and when the addition amount of the CF4 gas is more than 3%, ashing of the photoresist film 44 becomes significant since the reactivity of oxygen radicals is too high.
The purpose and the effect of the operation of removing a fluorocarbon film will be described later.
Next, by using the photoresist film 44 as a mask, for example, wet etching is performed by an aqueous hydrofluoric acid solution diluted with pure water at a ratio of approximately 100:1 to 200:1, so that the bottom oxide film of the ONO film 42 and the tunnel insulating film 34 are removed (
By ashing and a subsequent post-treatment, the photoresist film 44 is then removed.
Next, for example, by a thermal oxidation method, a silicon oxide film 46 having a thickness of, for example, 3 nm to 20 nm is formed on the surface of the silicon substrate 10 in the peripheral circuit region (
Subsequently, a photoresist film 48 is formed on the entire surface by a spin coating method and is then patterned by photolithography so as to expose the low-voltage transistor forming region and the medium-voltage transistor forming region and so as to cover the high-voltage transistor forming region and the memory cell region.
Next, by using the photoresist film 48 as a mask, for example, wet etching is performed by an aqueous hydrofluoric acid solution diluted with pure water at a ratio of approximately 100:1 to 200:1, so that the silicon oxide film 46 in the low-voltage transistor forming region and the medium-voltage transistor forming region is selectively removed (
By ashing and a subsequent post-treatment, the photoresist 48 is then removed.
Subsequently, the silicon substrate 10 is thermally oxidized, so that a silicon oxide film 50 having a thickness of, for example, 1 nm to 12 nm is formed in the low-voltage transistor forming region and the medium-voltage transistor forming region (
Next, a photoresist film 52 is formed on the entire surface by a spin coating method and is then patterned by photolithography so as to expose the low-voltage transistor forming region and so as to cover the medium-voltage transistor forming region, the high-voltage transistor forming region, and the memory cell region.
Next, by using the photoresist film 52 as a mask, for example, wet etching is performed by an aqueous hydrofluoric acid solution diluted with pure water at a ratio of approximately 100:1 to 200:1, so that the silicon oxide film 50 in the low-voltage transistor forming region is selectively removed (
Next, by ashing and a subsequent post-treatment, the photoresist 52 is removed.
Subsequently, the silicon substrate 10 is thermally oxidized, so that the gate insulating film 54 composed of a silicon oxide film having a thickness of, for example, 1 nm to 3 nm is formed in the low-voltage transistor forming region. In this operation, the silicon oxide film 50 is additionally oxidized in the medium-voltage transistor forming region, so that the gate insulating film 56 composed of a silicon oxide film having a thickness of, for example, 2 nm to 15 nm is formed. In addition, the silicon oxide film 46 is further additionally oxidized in the high-voltage transistor forming region, so that the gate insulating film 58 composed of a silicon oxide film having a thickness of, for example, 5 nm to 35 nm is formed. As described above, in the low-voltage transistor forming region, the medium-voltage transistor forming region, and the high-voltage transistor forming region, the three types of gate insulating films 54, 56, and 58 having different thicknesses are formed (
Next, a polysilicon film 60 having a thickness of, for example, 50 nm to 110 nm is formed on the entire surface, for example, by a CVD method.
Subsequently, a silicon nitride film 62 having a thickness of 10 nm to 40 nm provided with an oxide film having a thickness of, for example, 3 nm or less on the topmost surface is formed on the polysilicon film 60, for example, by a CVD method.
A BARC film 64 and a photoresist film 66 are then formed on the silicon nitride film 62 by a spin coating method.
Subsequently, the photoresist film 66 is patterned by photolithography so as to cover the peripheral region and the control gate region in the memory cell region (
Next, by using the photoresist film 66 as a mask, for example, anisotropic etching is performed in an inductively coupled plasma etching apparatus, so that the BARC film 64, the silicon nitride film 62, the polysilicon film 60, the ONO film 42, and the amorphous silicon film 36 are patterned. As a result, the floating gate 68 composed of the amorphous silicon film 36 and the control gate 70 composed of the polysilicon film 60 are formed in the memory cell region.
Next, by ashing and a subsequent post-treatment, the BARC film 64 and the photoresist film 66 remaining on the silicon nitride film 62 are removed (
Subsequently, by a thermal oxidation method, side wall insulating films 72 composed of a silicon oxide film are formed on side wall portions of the floating gate 68 and the control gate 70.
Ion implantation is then performed using the control gate 70 as a mask, so that impurity diffusion regions 74 are formed in the silicon substrate 10 at two sides of the control gate 70.
Next, a silicon nitride film 76 having a thickness of, for example, 30 nm to 150 nm is formed on the entire surface, for example, by a thermal CVD method (
By performing dry etching, the silicon nitride films 76 and 62 are then anisotropically etched until the upper surfaces of the polysilicon film 60 and the control gate 70 are exposed, and side wall insulating films 78 are formed from the silicon nitride film 76 on the side wall portions of the floating gate 68 and the control gate 70 provided with the side wall insulating films 72 (
Subsequently, a silicon oxide film 80 having a thickness of, for example, 15 nm to 40 nm is formed on the entire surface, for example, by a thermal CVD method. The silicon oxide film 80 is a film to be used as a hard mask when the polysilicon film 60 is patterned in a subsequent operation.
A BARC film 82 and a photoresist film 84 are then formed on the silicon oxide film 80 by a spin coating method.
Next, the photoresist film 84 is patterned by photolithography so as to cover the memory cell region and the gate electrode forming regions of the peripheral transistors (low, medium, and high-voltage transistors) (
Subsequently, by using the photoresist film 84 as a mask, for example, anisotropic etching is performed in an inductively coupled plasma etching apparatus, so that the BARC film 82, the silicon oxide film 80, and the polysilicon film 60 are patterned. As a result, the gate electrodes 86 composed of the polysilicon film 60 are formed in the peripheral circuit region.
By ashing and a subsequent post-treatment, the BARC film 82 and the photoresist film 84 remaining on the silicon oxide film 80 are then removed.
Next, for example, by wet etching using an aqueous hydrofluoric acid solution, the silicon oxide film 80 is removed.
Subsequently, ion implantation is performed using the gate electrode 86 as a mask, impurity diffusion regions 88 are formed in the silicon substrate 10 at two sides of the gate electrode 86 (
After a silicon nitride film is deposited, for example, by a thermal CVD method, this silicon nitride film is etched-back, so that side wall insulating films 90 composed of the silicon nitride film are formed on the side wall portions of the gate electrodes 86 and the side wall portions of the floating gate 68 and the control gate 70 on which the side wall insulating films 78 are provided.
Next, ion implantation is performed using the gate electrode 86 and the side wall insulating films 90 as a mask and also using the control gate 70 and the side wall insulating films 78 and 90 as a mask, so that impurity diffusion regions 92 are formed in the silicon substrate 10 at two sides of the gate electrode 86, and so that impurity diffusion regions 94 are formed in the silicon substrate 10 at two sides of the control gate 70.
Subsequently, a thermal treatment is performed in a nitrogen atmosphere to activate implanted impurities, so that the source/drain regions 96 composed of the impurity diffusion regions 88 and 92 are formed in the silicon substrate 10 at two sides of the gate electrode 86, and so that the source/drain regions 98 composed of the impurity diffusion regions 74 and 94 are formed in the silicon substrate 10 at two sides of the control gate 70 (
As a result, there are provided the non-volatile memory including the floating gate 68 formed in the memory cell region and on the silicon substrate 10 with the tunnel insulating film 34 interposed therebetween, the control gate 70 formed on the floating gate 68 with the ONO film 42 interposed therebetween, and the source/drain regions 98 formed in the silicon substrate 10 at the two sides of the control gate 70; the low-voltage transistor formed in the low-voltage transistor forming region and having the gate electrode 86 formed on the silicon substrate 10 with the gate insulating film 54 interposed therebetween and the source/drain regions 96 formed in the silicon substrate 10 at the two sides of the gate electrode 86; the medium-voltage transistor formed in the medium-voltage transistor forming region and having the gate electrode 86 formed on the silicon substrate 10 with the gate insulating film 56 interposed therebetween and the source/drain regions 96 formed in the silicon substrate 10 at the two sides of the gate electrode 86; and the high-voltage transistor formed in the high-voltage transistor forming region and having the gate electrode 86 formed on the silicon substrate 10 with the gate insulating film 58 interposed therebetween and the source/drain regions 96 formed in the silicon substrate 10 at the two sides of the gate electrode 86. The non-volatile memory may be formed on the silicon substrate 10, or the non-volatile memory may be formed over the silicon substrate 10.
Subsequently, after a salicide process and predetermined backend process, such as a multilayer wiring process, are performed, the semiconductor device is formed.
In the method of manufacturing a semiconductor device according to the above embodiment, the purpose and effect of the operation of removing a fluorocarbon film during a process of removing the ONO film 42 in the peripheral circuit region will be described with reference to
In the method of manufacturing a semiconductor device according to this embodiment, the reason the fluorocarbon film is removed during the process of removing the ONO film 42 in the peripheral circuit region is that the fluorocarbon film is responsible for degradation in withstand voltage of the gate insulating film of the high-voltage transistor.
As described above, during the operation of removing the ONO film 42 and the preceding operations, a recess 100 is formed at the boundary between the isolation film 28 and the active region (silicon substrate 10). During the dry etching process in which the top oxide film and the silicon nitride film, which is the intermediate layer, of the ONO film 42 are removed, a fluorocarbon film 102, which is a byproduct of the dry etching, is deposited on an inner wall of the recess 100. Since the fluorocarbon film 102 is liable to be deposited on a side wall portion of the recess 100, it is believed that the thickness of the fluorocarbon film 102 is small at a deep position of the recess 100 (see
When an operation of etching a bottom oxide film 104 is performed under this condition, since the etching rate thereof at a position to which the fluorocarbon film 102 adheres is low, the etching is preferentially advanced at the deep position of the recess 100 (see
When the etching of the bottom oxide film 104 (including the tunnel insulating film 34) is further advanced, the isolation film 28 is also etched at the deep position of the recess 100 at which the etching is already completed, and as a result, the shape of the recess 100 at the deep position becomes steep (FIG. 29C).
This steep shape of the recess 100 is maintained after the gate insulating film 58 is formed by subsequent thermal oxidation. As a result, it is believed that since the electric field concentration occurs when a gate insulating material is formed in the recess 100, the withstand voltage of the gate insulating film 58 of the high-voltage transistor is degraded.
In the gate insulating films 54 and 56 of the low-voltage transistor and the medium-voltage transistor, the degradation in withstand voltage as that observed in the gate insulating film 58 of the high-voltage transistor is not observed. The reason for this is believed that in the low-voltage transistor forming region and the medium-voltage transistor forming region, since the gate insulating films 54 and 56 are formed by re-oxidation after the silicon oxide film 46 is removed, the shape of the recess 100 is smoothed, and the electric field concentration is not likely to occur.
By the operation of removing a fluorocarbon film performed as in this embodiment, the etching of the bottom oxide film is prevented from being locally advanced, and hence a steep recess is prevented from being formed at the deep portion of the recess after the bottom oxide film is removed.
As illustrated in the figures, according to the sample which was processed by the operation of removing a fluorocarbon film, the deep portion (enclosed by a dotted line in the figure) of the recess has a smooth shape as compared to that of the sample which was not processed by the operation of removing a fluorocarbon film.
As illustrated in the figure, the samples which were not processed by the operation of removing a fluorocarbon film had a large variation in withstand voltage of the gate insulating film; however, on the other hand, according to the samples which were processed by the operation of removing a fluorocarbon film according to either the first method or the second method, stable and high withstand voltage of the gate insulating film could be obtained.
As described above, according to this embodiment, when the ONO film in the peripheral circuit region is removed, the operation of removing a fluorocarbon film as the residual film adhering to the surface is performed after the top insulating film and the intermediate layer are removed; hence, the shape of the recess formed at the end portion of the isolation film is prevented from being changed during the subsequent process of removing the bottom insulating film. Accordingly, the electric field concentration on the end portion of the isolation film may be prevented, and as a result, the degradation in withstand voltage of the gate insulating film of the peripheral transistor may be prevented.
A method of manufacturing a semiconductor device according to the second embodiment will be described with reference to
First, the structure of the semiconductor device according to this embodiment will be described with reference to
The semiconductor device according to this embodiment is a semiconductor device including a transistor and a non-volatile memory each having a single layer gate structure in which an ONO film is used as a charge storage layer. As with the semiconductor device according to the first embodiment, the semiconductor device of this embodiment also has a memory cell region in which non-volatile memories (Flash) are formed in a matrix and a peripheral circuit region in which various peripheral transistors, such as a logic transistor forming a logic circuit and a high-voltage transistor driving a non-volatile memory, are formed. As the peripheral transistors, the semiconductor device of this embodiment includes, for example, a low-voltage transistor (LV-Tr) forming a high speed logic circuit, a medium-voltage transistor (MV-Tr) forming an input/output circuit, and a high-voltage transistor (HV-Tr) controlling a non-volatile memory.
As illustrated in
Accordingly, at each intersection between the control gate 70 and a region between adjacent bit lines 108, a non-volatile memory is formed which has the control gate 70, source/drain regions formed from adjacent bit lines 108, and the ONO film 42 used as a charge storage layer. In the region between the control gates 70, a silicon nitride film 76 and a liner film formed of a silicon oxide film 80 are filled as illustrated in
The low-voltage transistor (LV-Tr), the medium-voltage transistor (MV-Tr), and the high-voltage transistor (HV-Tr) formed in the peripheral circuit region are similar to those of the semiconductor device according to the first embodiment, and hence a description thereof is omitted.
Next, the method of manufacturing a semiconductor device according to this embodiment will be described with reference to
In addition, since a manufacturing process of the peripheral transistors is basically equivalent to that of the manufacturing method of the semiconductor device according to the first embodiment, a manufacturing process of the non-volatile memory will be primarily described in this embodiment. The manufacturing process of the peripheral transistors will be described with reference to the figures of the first embodiment whenever necessary.
First, as with the method of manufacturing a semiconductor device according to the first embodiment illustrated in
A sacrifice oxide film 32 composed of a silicon oxide film is then formed, for example, by a thermal oxidation method on the active region of the silicon substrate 10 defined by the isolation film 28 (
Subsequently, predetermined wells (not illustrated) are formed in the memory cell region and the high-voltage transistor forming region by photolithography and ion implantation. For example, double wells in which a p-type well is formed in an n-type well are formed in the memory cell region and an n-type high-voltage transistor forming region, and an n-type well is formed in a p-type high-voltage transistor forming region.
Next, for example, a heat treatment is then performed in a nitrogen atmosphere at a temperature of 900° C. to 1,200° C. for 1 second to 15 seconds, so that implanted impurities are activated.
Next, for example, wet etching is performed using an aqueous hydrofluoric acid solution diluted with pure water at a ratio of approximately 10:1 to 200:1, so that the sacrifice oxide film 32 is removed.
Incidentally, the thickness of the isolation film 28 is gradually decreased, for example, by the operations of removing a silicon oxide film 12 and the sacrifice oxide film 32. Accordingly, after the sacrifice oxide film 32 is removed, a recess which is recessed from the surface of the active region is formed at the boundary between the isolation film 28 and the active region.
Next, the silicon oxide film 42a having a thickness of, for example, 5 nm to 14 nm is formed on the surface of the silicon substrate 10 by a thermal oxidation method. The silicon oxide film 42a may be formed on the silicon substrate 10, or the silicon oxide film 42a may be formed over the silicon substrate 10.
Subsequently, the silicon nitride film 42b having a thickness of, for example, 5 nm to 14 nm is formed on the entire surface of the silicon oxide film 42a, for example, by a thermal CVD method (
A photoresist film 40 is formed on the silicon nitride film 42b by photolithography so as to cover the entire surface of the peripheral circuit region and so as to expose bit line forming regions of the memory cell region (
Next, by ion implantation using the photoresist film 40 as a mask, impurity diffusion regions 110 used as the bit lines 108 and impurity diffusion regions 112 used as pocket regions provided at two ends of the impurity diffusion region 110 are formed in the memory cell region (
By ashing and a subsequent post-treatment, the photoresist film 40 on the silicon nitride film 42b is then removed.
Subsequently, the silicon oxide film 42c is formed on the silicon nitride film 42b. The silicon oxide film 42c is formed, for example, by the operations of thermally oxidizing the silicon nitride film 42b by a thermal oxidation method, and then forming a high temperature oxide (HTO) film by a thermal CVD method.
The laminate film composed of the silicon oxide film 42a/silicon nitride film 42b/silicon oxide film 42c is formed as described above, so that the charge storage layer is formed from the ONO film 42 (
By photolithography and ion implantation, predetermined wells (not illustrated) are then formed in the low-voltage transistor forming region and the medium-voltage transistor forming region. For example, p-type wells are formed in an n-type low-voltage transistor forming region and an n-type medium-voltage transistor forming region, and n-type wells are formed in a p-type low-voltage transistor forming region and a p-type medium-voltage transistor forming region.
Subsequently, as with the method of manufacturing a semiconductor device according to the first embodiment illustrated in
In particular, after a photoresist film 44 exposing the peripheral circuit region and covering the memory cell region is formed, by using this photoresist film 44 as a mask, the silicon oxide film 42c and the silicon nitride film 42b are etched, for example, by dry etching performed in a magnetron reactive ion etching apparatus. Next, a fluorocarbon film which adheres to the surface of the substrate when the silicon oxide film 42c and the silicon nitride film 42b are etched is removed by the first or the second method described in the first embodiment. Next, by using the photoresist film 44 as a mask, for example, wet etching is performed by an aqueous hydrofluoric acid solution diluted with pure water at a ratio of approximately 100:1 to 200:1, so that the silicon oxide film 42a is removed. By ashing and a subsequent post-treatment, the photoresist film 44 is then removed.
By removing the ONO film 42 as described above, the shape of the recess formed at the boundary between the isolation film 28 and the active region is prevented from being changed.
Subsequently, as with the method of manufacturing a semiconductor device according to the first embodiment illustrated in
A polysilicon film 60 having a thickness of, for example, 50 nm to 200 nm is then formed on the entire surface of the silicon substrate 10, for example, by a CVD method. The polysilicon film 60 is formed into the control gate 70 of the non-volatile memory and gate electrodes 86 of the peripheral transistors. The polysilicon film 60 may be formed on the silicon substrate 10, or the polysilicon film 60 may be formed over the silicon substrate 10.
Next, a silicon oxide film 114 having a thickness of, for example, 15 nm to 40 nm is formed on the polysilicon film 60, for example, by a CVD method (
A BARC film 64 and a photoresist film 66 are then formed on the silicon oxide film 114 by a spin coating method.
Subsequently, the photoresist film 66 is patterned by photolithography so as to cover the entire surface of the peripheral circuit region and the control gate forming region of the memory cell region (
Next, by using the photoresist films 66 as a mask, the BARC film 64, the silicon oxide film 114, and the polysilicon film 60 are patterned, for example, by anisotropic etching performed in an inductively coupled plasma etching apparatus, so that the control gate 70 is formed from the polysilicon film 60 in the memory cell region.
Next, by ashing and a subsequent post-treatment, the silicon oxide film 114, the BARC film 64, and the photoresist film 66 remaining on the polysilicon film 60 are removed (
The silicon oxide film 80 having a thickness of, for example, 1 nm to 20 nm and the silicon nitride film 76 having a thickness of, for example, 50 nm to 170 nm are then formed on the entire surface of the silicon substrate 10, for example, by a thermal CVD method (
Subsequently, the silicon nitride film 76 is anisotropically etched by dry etching until the upper surface of the silicon oxide film 80 is exposed, so that the space between the control gates 70 is filled with the silicon oxide film 80 and the silicon nitride film 76 (
As with the method of manufacturing a semiconductor device according to the first embodiment illustrated in
Next, a salicide process and predetermined backend processes, such as a multilayer wiring process, are performed, so that the semiconductor device is formed.
As described above, according to this embodiment, when the ONO film in the peripheral circuit region is removed, after the top insulating film and the intermediate layer are removed, the operation of removing a fluorocarbon film as a residual film adhering to the surface is performed; hence, during a subsequent process of removing the bottom insulating film, the shape of the recess formed at the end portion of the isolation film is prevented from being changed. Accordingly, the electric field concentration on the end portion of the isolation film is prevented, and hence the degradation in withstand voltage of the gate insulating film of the peripheral transistor may be prevented.
A method of manufacturing a semiconductor device according to the third embodiment will be described with reference to
The structure of the semiconductor device according to this embodiment will be described with reference to
The semiconductor device according to this embodiment is a semiconductor device including a transistor and a non-volatile memory having a single layer gate structure in which an ONO film is used as a charge storage layer. As with the semiconductor device according to the first embodiment, the semiconductor device of this embodiment also has a memory cell region in which non-volatile memories (Flash) are formed in a matrix and a peripheral circuit region in which various peripheral transistors, such as a logic transistor forming a logic circuit and a high-voltage transistor driving a non-volatile memory, are formed. As the peripheral transistors, the semiconductor device of this embodiment includes, for example, a low-voltage transistor (LV-Tr) forming a high speed logic circuit, a medium-voltage transistor (MV-Tr) forming an input/output circuit, and a high-voltage transistor (HV-Tr) controlling a non-volatile memory.
As illustrated in
Accordingly, at each intersection between the control gate 70 and a region between adjacent isolation films 28, a non-volatile memory is formed in which the control gate 70, the source/drain regions 98 formed in the silicon substrate 10 and at two sides of the control gate 70, and the ONO film 42 used as a charge storage layer are provided. In the region between the control gates 70, as illustrated in FIG. 37C, a silicon nitride film 76 and a liner film formed of a silicon oxide film 80 are filled.
The low-voltage transistor (LV-Tr), the medium-voltage transistor (MV-Tr), and the high-voltage transistor (HV-Tr) formed in the peripheral circuit region are similar to those of the semiconductor device of the first embodiment, and hence a description thereof is omitted.
Next, the method of manufacturing a semiconductor device according to this embodiment will be described with reference to
In addition, since a manufacturing process of the peripheral transistors is basically equivalent to that of the manufacturing method of the semiconductor device according to the first embodiment, a manufacturing process of the non-volatile memory will be primarily described in this embodiment. The manufacturing process of the peripheral transistors will be described with reference to the figures of the first embodiment whenever necessary.
First, as with the method of manufacturing a semiconductor device according to the first embodiment illustrated in
A sacrifice oxide film 32 composed of a silicon oxide film is then formed on the active region of the silicon substrate 10 defined by the isolation film 28, for example, by a thermal oxidation method (
Subsequently, predetermined wells (not illustrated) are formed in the memory cell region and the high-voltage transistor forming region by photolithography and ion implantation. For example, double wells in each of which a p-type well is formed in an n-type well are formed in the memory cell region and an n-type high-voltage transistor forming region, and an n-type well is formed in a p-type high-voltage transistor forming region.
Next, for example, a heat treatment is performed in a nitrogen atmosphere at a temperature of 900° C. to 1,200° C. for 1 second to 15 seconds, so that implanted impurities are activated.
Next, for example, wet etching is performed using an aqueous hydrofluoric acid solution diluted with pure water at a ratio of approximately 10:1 to 200:1, so that the sacrifice oxide films 32 are removed.
Incidentally, the thickness of the isolation film 28 is gradually decreased, for example, by the operations of removing a silicon oxide film 12 and the sacrifice oxide film 32. Accordingly, after the sacrifice oxide film 32 is removed, a recess which is recessed from the surface of the active region is formed at the boundary between the isolation film 28 and the active region.
Next, the silicon oxide film 42a having a thickness of, for example, 5 nm to 14 nm is formed on the surface of the silicon substrate 10 by a thermal oxidation method. The silicon oxide film 42a may be formed on the silicon substrate 10, or the silicon oxide film 42a may be formed over the silicon substrate 10.
Subsequently, the silicon nitride film 42b having a thickness of, for example, 5 nm to 14 nm is formed on the entire surface of the silicon oxide film 42a, for example, by a thermal CVD method (
Next, the silicon oxide film 42c having a thickness of, for example, 3 nm to 15 nm is formed on the silicon nitride film 42b, for example, by a thermal oxidation method. The silicon oxide film 42c may be formed on the silicon nitride film 42b, or the silicon oxide film 42c may be formed over the silicon nitride film 42b.
The laminate film composed of the silicon oxide film 42a/silicon nitride film 42b/silicon oxide film 42c is formed as described above, so that the charge storage layer is formed from the ONO film 42 (
By photolithography and ion implantation, predetermined wells (not illustrated) are then formed in the low-voltage transistor forming region and the medium-voltage transistor forming region. For example, p-type wells are formed in an n-type low-voltage transistor forming region and an n-type medium-voltage transistor forming region, and n-type wells are formed in a p-type low-voltage transistor forming region and a p-type medium-voltage transistor forming region.
Subsequently, as with the method of manufacturing a semiconductor device according to the first embodiment illustrated in
In particular, after a photoresist film 44 exposing the peripheral circuit region and covering the memory cell region is formed, by using this photoresist film 44 as a mask, the silicon oxide film 42c and the silicon nitride film 42b are etched, for example, by dry etching performed in a magnetron reactive ion etching apparatus. Next, a fluorocarbon film which adheres to the surface of the substrate when the silicon oxide film 42c and the silicon nitride film 42b are etched is removed by the first or the second method of the first embodiment. Next, by using the photoresist film 44 as a mask, for example, wet etching is performed by an aqueous hydrofluoric acid solution diluted with pure water at a ratio of approximately 100:1 to 200:1, so that the silicon oxide film 42a is removed. By ashing and a subsequent post-treatment, the photoresist film 44 is then removed.
By removing the ONO film 42 as described above, the shape of the recess formed at the boundary between the isolation film 28 and the active region is prevented from being changed.
Subsequently, as with the method of manufacturing a semiconductor device according to the first embodiment illustrated in
A polysilicon film 60 having a thickness of, for example, 50 nm to 200 nm is then formed on the entire surface of the silicon substrate 10, for example, by a CVD method. The polysilicon film 60 is formed into the control gate 70 of the non-volatile memory and gate electrodes 86 of the peripheral transistors. The polysilicon film 60 may be formed on the entire surface of the silicon substrate 10, or the polysilicon film 60 may be formed over the entire surface of the silicon substrate 10.
Next, a silicon oxide film 114 having a thickness of, for example, 15 nm to 40 nm is formed on the polysilicon film 60, for example, by a CVD method (
A BARC film 64 and a photoresist film 66 are then formed on the silicon oxide film 114 by a spin coating method.
Subsequently, the photoresist film 66 is patterned by photolithography so as to cover the entire surface of the peripheral circuit region and the control gate forming region of the memory cell region (
Next, by using the photoresist films 66 as a mask, the BARC film 64, the silicon oxide film 114, and the polysilicon film 60 are patterned, for example, by anisotropic etching performed in an inductively coupled plasma etching apparatus, so that the control gate 70 is formed from the polysilicon film 60 in the memory cell region.
Subsequently, ion implantation is performed using the photoresist film 66 and the control gate 70 as a mask, so that impurity diffusion regions 74 used as the source/drain regions 98 are formed.
Next, by ashing and a subsequent post-treatment, the silicon oxide film 114, the BARC film 64, and the photoresist film 66 remaining on the polysilicon film 60 are removed (
The silicon oxide film 80 having a thickness of, for example, 1 nm to 20 nm and the silicon nitride film 76 having a thickness of, for example, 50 nm to 170 nm are then formed on the entire surface of the ONO film 42, for example, by a thermal CVD method (
Subsequently, the silicon nitride film 76 is anisotropically etched by dry etching until the upper surface of the silicon oxide film 80 is exposed, so that the space between the control gates 70 is filled with the silicon oxide film 80 and the silicon nitride film 76 (
As with the method of manufacturing a semiconductor device according to the first embodiment illustrated in
Next, a salicide process and predetermined backend processes, such as a multilayer wiring process, are performed, so that the semiconductor device is formed.
As described above, according to this embodiment, when the ONO film in the peripheral circuit region is removed, after the top insulating film and the intermediate layer are removed, the operation of removing a fluorocarbon film as a residual film adhering to the surface is performed; hence, during a subsequent process of removing the bottom insulating film, the shape of the recess formed at the end portion of the isolation film is prevented from being changed. Accordingly, the electric field concentration on the end portion of the isolation film is prevented, and hence the degradation in withstand voltage of the gate insulating film of the peripheral transistor may be prevented.
In addition to the above embodiments, various modifications may be made.
For example, the case in which the present embodiment is applied when the ONO film used as an inter-gate insulating film or a charge storage layer is removed has been described in the above embodiments; however, the present embodiment is not limited thereto. The present embodiment may be widely applied to a method of manufacturing a semiconductor device which has a lower layer insulating film having etching properties equivalent to those of an isolation region and an upper layer insulating film formed on the lower layer insulating film, in which a manufacturing process using a fluorocarbon-based gas for etching the upper layer insulating film is performed.
In a silicon-based semiconductor device, as the lower layer insulating film, a silicon oxide-based insulating film (silicon oxide film or silicon nitride film) may be used. In addition, as the upper layer insulating film, for example, a single silicon nitride film, a multilayer film of a silicon nitride film and a silicon oxide film, or a high dielectric constant insulating film, such as an alumina (Al2O3) film or a hafnia film (HfO2), may be used.
In addition, as the fluorocarbon-based gas used for etching the upper layer insulating film, a flon gas, such as hydrofluorocarbon (HFC) or fluorocarbon (FC), may also be used as well as the gases described in the above embodiments.
In addition, the structure and the process conditions of the semiconductor device described in the above embodiments have been illustrated by way of example and may be appropriately changed and modified whenever necessary.
In the above embodiments, the case in which the present embodiment is applied to the method of manufacturing a semiconductor device including a transistor and a non-volatile memory has been described by way of example; however, the present embodiment is not only limited to a semiconductor device including a transistor and a non-volatile memory.
As described above, the present embodiment may be widely applied to a method of manufacturing a semiconductor device which has a lower layer insulating film containing etching properties equivalent to those of an isolation region and an upper layer insulating film formed on the lower layer insulating film, in which a manufacturing process using a fluorocarbon-based gas for etching the upper layer insulating film is performed. In particular, when the underlayer for the lower layer insulating film has an operation, the present embodiment may be effectively used.
All examples and conditional language recited herein are intended for pedagogical purposes to aid the reader in understanding the embodiment and the concepts contributed by the inventor to furthering the art, and are to be construed as being without limitation to such specifically recited examples and conditions, nor does the organization of such examples in the specification relate to a illustrating of the superiority and inferiority of the embodiment. Although the embodiments have been described in detail, it should be understood that the various changes, substitutions, and alterations could be made hereto without departing from the spirit and scope of the invention.
| Number | Date | Country | Kind |
|---|---|---|---|
| 2008-041782 | Feb 2008 | JP | national |
This Application is a divisional of U.S. application Ser. No. 12/369,859 filed Feb. 12, 2009, which is based upon and claims the benefit of priority of the prior Japanese Patent Application No. 2008-041782 filed on Feb. 22, 2008, the entire contents of which are incorporated herein by reference.
| Number | Date | Country | |
|---|---|---|---|
| Parent | 12369859 | Feb 2009 | US |
| Child | 13455633 | US |