The invention relates to methodologies and test configurations for testing thermal interface materials and, in particular, to methodologies and test configurations for testing thermal interface materials used for testing integrated circuits.
The high cost associated with manufacturing integrated circuits dictates that defective devices be diagnosed as early as possible in the manufacturing process. For this reason, it is highly advantageous to test integrated circuit devices at the wafer level before further processing and packaging. For testing, the wafers are clamped to a wafer chuck and brought into contact with highly sophisticated probes. Once probe contact is made, the circuits are tested for both functionality and power integrity. However, circuits can be tested at power levels in excess of 400 watts, which consequently generates a tremendous amount of heat build-up in the chips which must be removed by the massive wafer chuck.
After wafer test, the wafers are diced into individual devices also known as chips. The good devices are mounted onto substrates to create modules. The modules then go through additional testing that may include burn in and re-test. The test equipment typically includes a high performance heat sink, test socket and tester electronics. The module is installed in the socket, the heat sink is brought into contact with the chip, the chip is tested, the heat sink is removed and the module is removed from the socket and sorted based on functionality. Some or all of these steps are commonly automated.
In some applications, a Liquid Thermal Interface (LTI) is placed between the chip and heat sink in order to improve thermal contact. There are many different types of LTIs that can be used to improve the thermal contact such as, for example, a mixture of water and other additives (i.e., Propylene Glycol (PG)). Water has excellent thermal performance but at high test temperatures may evaporate before the end of test. Also, water and other substances such as, for example, PG, can corrode the C4 connects. The corrosion or evaporation often happens only on small areas of the device and only on a small number of the total devices tested in a high volume manufacturing environment.
Alternate interface materials can have other disadvantages. Helium is clean and non-corrosive but thermal performance is insufficient. PAO (Poly Alpha Olefin) oil and various types of thermal grease have thermal performance almost as good as water but require cleaning with a solvent after test. Thermal pads have insufficient thermal performance and often leave a residue. Fluorinated fluids may be non-corrosive and clean but have poor thermal performance due to their low thermal conductivity. Liquid metals and soft metals can have very good thermal performance but can oxidize (degrade) over time and repeated reuse, they can damage the heat sinks and can have unreliable thermal contact to the chip. Greases, phase change materials and adhesives can make it difficult to separate the heat sink from the chip after test and leave a residue.
If faults stemming from the improper use of LTI are found after production has started it may be necessary to recall product and develop a new LTI resulting in significant production delays. Thus there is a need for improved methods of evaluating LTI fluids to ensure they will provide reliable service. Accordingly, there exists a need in the art to overcome the deficiencies and limitations described hereinabove.
In a first aspect of the invention, a test methodology comprises applying a thermal interface material between a device and heat sink. Power is applied to the test device. The test methodology further comprises monitoring the device with a plurality of temperature sensors. The test methodology further comprises determining whether any of the plurality of temperature sensors increase above a steady state temperature.
In another aspect of the invention, a test methodology comprises measuring conductivity between two interconnects by applying a voltage between the two interconnects. The test methodology further comprises applying a thermal interface material in contact with at least two interconnects. The test methodology further comprises determining whether there is an increase in current when the thermal interface material is in contact with the two interconnects.
In yet another aspect of the invention, a test methodology comprises placing a quantity of thermal interface material on a device under test. The test methodology further comprises placing a glass slide at a predetermined load on the thermal interface material. The test methodology further comprises determining whether the thermal interface material adequately covers the device under test without running over an edge; and at least one of if the thermal interface material does not adequately cover the device and/or runs over the edge, then clean the glass and the device and reapply a different quantity of the thermal interface material, and repeat the placing the glass and determining steps; and if the thermal interface material adequately covers the device then accept the thermal interface material.
In still yet another aspect of the invention, a test configuration comprises a substrate or card for attaching to a device. The test configuration further comprises a heat sink structured to dissipate heat away from the device. The test configuration further comprises a power supply which powers the device. The test configuration further comprises a plurality of temperature sensors at locations throughout the device under test and which take temperature readings at the locations. The test configuration further comprises a temperature measurement device for determining an evaporation of a thermal interface material between the device under test and the heat sink by sensing a temperature rise above a steady state temperature of one or more of the temperature sensors.
In yet another aspect of the invention, a test configuration comprises a power supply which applies a voltage between interconnects. The test configuration further comprises a current measurement device configured to measure current passing through the interconnects and a thermal interface material which contacts the interconnects. The current measurement device provides an indication of a difference in current between a voltage applied to the interconnects without the thermal interface material and when the thermal interface material is in contact with the interconnects.
The present invention is described in the detailed description which follows, in reference to the noted plurality of drawings by way of non-limiting examples of exemplary embodiments of the present invention.
a shows a configuration using temperature sensors to test a thermal interface material in accordance with aspects of the invention;
b shows a test socket with a module having temperature sensors, with a heat sink in non-thermal contact with the device in accordance with aspects of the invention;
c shows a test socket, where the heat sink is in thermal contact with the module having temperature sensors in accordance with aspects of the invention;
d shows a plurality of temperature sensors in accordance with aspects of the invention;
a and 6b show temperature performance data of different thermal interface materials at several different temperature sensor positions along the device obtained using the methods of the present invention;
c shows temperature performance data of different thermal interface materials as a function of the material thermal conductivity obtained using the methods of the present invention;
d shows the result of a simple model predicting temperature gradients on a product module that may have variable LTI coverage and power;
e shows thermal data measured on production modules;
a and 7b show alternative test configurations to measure conductivity (and observe thermal interface material) in accordance with an additional aspect of the invention;
a-9c show representative devices that used thermal interface materials during testing, in accordance with aspects of the invention;
d shows chip surfaces at different phases of testing;
a and 10b show a test configuration to observe thermal interface material on a surface of the device in accordance with an additional aspect of the invention; and
The invention relates to methodologies and test configurations for testing thermal interface materials and, in particular, to methodologies and test configurations for testing thermal interface materials used for testing integrated circuits. The methodologies herein provide improved techniques for determining evaporation of the thermal interface materials (LTI), as well as corrosion caused by using different LTIs.
At step 105, a heat sink is applied to the device with a predetermined load, and temperature. The load is provided to adequately make contact between the heat sink and device and thermal interface material. In embodiments, the heat sink load and geometry will be similar to the proposed production manufacturing application. In embodiments, temperature, time and force may be, for example, 115° C. for 60 minutes at 10 lb. It is understood, though, that this is merely one non-limiting example, as other examples are provided herein. At step 110, a known power is applied to the device to heat the device to a temperature, e.g., 115° C. At step 115, the method monitors a plurality of temperature sensors that are integrated into or coupled to the test device (or production device, if available) to determine the temperatures at various locations. The method will assume that the temperature sensors will reach a steady state temperature as discussed, for example, with reference to
In embodiments, the temperature sensors can be small resistors which are calibrated in an oven by measuring electrical resistance vs temperature. A straight line is fit to the calibration data. During testing of the LTI, temperature is calculated from the measured resistance. Other types of temperature sensors such as diodes can also be used with the present invention.
At step 120, the process determines if the temperature sensors have reached a steady state. If the temperature sensors have not reached a steady state, at step 122, the process determines if any of the temperature sensors exceed a safe limit, e.g., 140° C. depending on the materials of construction of the test device and the specification for product test. If the temperature is exceeding a safe limit, the test is ended and restarted with new conditions of heat sink temperature, LTI volume and/or power. If the temperature does not exceed a safe limit, the process returns to step 115.
If the steady state is achieved at step 120, the process then proceeds to step 125. At step 125, the method notes the time at which a first temperature sensor increases above a steady state as the first evidence of evaporation of the LTI from the device interface. The test ends if the temperature increases above the steady state; whereas, it will continue until the temperature increases above the steady state.
In embodiments, during manufacturing, the method looks for a change in average vs. change in maximum temperature. In embodiments, temperature readings may be made (monitored) before, during and after power is applied to the chip in order to provide comparison and base line data. However, the present invention should not be limited to any specific time periods for temperatures monitored before, during and after power is applied to the chip; although, in embodiments, the test may be run longer than the anticipated product test time, with the time varying from product to product.
Table 1, below, shows examples of weights, loads, wattage, test time and test temperature.
a-2d show a configuration for implementing a test methodology according to an aspect of the invention. The test methodology using the configuration shown in
More specifically,
The module may also contain an underfill material surrounding the C4 interconnects (not shown) and may be covered with a lid (not shown). In non-limiting embodiments, the device 15 (or chip) can have dimensions 21.3 mm×26.7 mm with C4 interconnects powered up to at least about 340 W. In another illustrative, non-limiting embodiment, the device or chip can have dimensions 23.6 mm×22.0 mm with C4 interconnects powered up to at least about 400 W.
b shows a test socket with the test chip module of
Referring to both
In embodiments, the heat sink 35 may be a water cooled heat-sink with a nickel plated surface to take away heat from the powered device 15. The heat sink 35 may be placed in contact with the device 15 by a heat sink actuator 35a, hinge mounted 35b to a test board 35d. The heat sink actuator 35a may include a spring mechanism 35c to provide a downward pressure on the heat sink 35. The heat sink 35 may include flexible supply tubing or bellows to supply cooling fluid while allowing gimbaling and flexibility (not shown). The heat sink 35 may also include heating elements and temperature sensors to actively control chip temperature. It is understood that
b and 2c further show a plurality of temperature sensors 60 integrated into or coupled to the thermal test device 15 (or actual production device, if available). In embodiments, the temperature sensors 60 can be small resistors or diodes (or combination of resistors and diodes). In other embodiments, it is possible to use the actual production device as a thermal test device because modern microprocessor devices often already have multiple temperature sensors. In a test chip, resistors are designed across the chip to result in a uniform or at least known pattern of power dissipation. It should be understood, though, that the pattern of power dissipation across the product device is not as well known as in the test device. When one area of a product device starts to overheat that area will generally start drawing more current from the rest of the chip resulting in an increase in power density which, in turn, increases temperature. This positive feedback can result in localized thermal runaway and damage to the device. Additionally, the production device may not be available in the time frame of the LTI testing.
c shows a power supply 65 and temperature measurement device 70. In embodiments, the power supply 65 provides power levels in excess of 400 watts, which consequently generates a tremendous amount of heat build-up in the device 15. The temperature measurement device 70 is connected to the temperature sensors 60, for determining the temperature across the device 15. In embodiments, the temperature measurement device 70 monitors the temperature sensors 60, to determine a steady state and an increase in temperature of any of the plurality of temperature sensors 60. More specifically, the temperature measurement device 70 is structured and arranged to determine an evaporation of a thermal interface material 40 between the device 15 and heat sink 35 by sensing a temperature rise above a steady state temperature of one or more of the temperature sensors 60. The temperature measurement device 70 can alert the user of these different states by use of, for example, an alarm, display or other user interface.
The temperature sensors 60 can be provided in a predetermined pattern on the device as shown, for example, in
In embodiments, the test device is installed in the test socket, LTI fluid of known volume is applied and it is contacted by the heat sink in a manner for the production of devices. The test device is connected to the power supply 65 which supplies a known voltage and current. The power in watts is the product of the measured voltage and current. The power supply 65 can include a current measurement device configured to measure current passing through the interconnects and a thermal interface material which contacts the interconnects. In embodiments, the current measurement device provides an indication of a difference in current between a voltage applied to the interconnects without the thermal interface material and when the thermal interface material is in contact with the interconnects.
The temperatures are monitored before, during and after power is applied to the chip using the temperature measurement device 70, connected to the temperature sensors 60. As previously noted, the present invention should not be limited to any specific time periods for temperatures monitored before, during and after power is applied to the chip.
If the device is known from its design to have a uniform power across its area, it is expected to see a fairly uniform temperature gradient across the device. The temperatures should quickly settle in at a steady state value for as long as constant power is applied. Steady state is a temperature increase over time that is inconsequential to the expected product test results. As a practical example, a temperature increase of less then 1° C. in 60 seconds may be considered steady state. The steady state temperature increase is often divided by the power to obtain a thermal characterization parameter that is typically referred to as a thermal resistance; units are C/W or may be further normalized by the device surface area as C sq cm/W. This calculation may be performed for each temperature sensor as well as the average of all temperature sensors. In this methodology, if one corner (or other location) becomes hotter than the others, it can be deduced that there is insufficient LTI at that corner (or other location). Other possibilities that would be investigated are a non-flat heat sink or non uniform heat sink force. After the steady state thermal resistance is determined the test is continued to see if and at what time there will be some evidence of evaporation.
Typical results using the methodologies and configuration described herein are shown in
The data shown in
a is an example of results done for a large number of TIM and LTI candidates measured with one test chip, heat sink and force. It should be understood by those of skill in the art that results will be different with other test chips, heat sinks or forces. Plotted are results from the hottest, coolest and average sensors.
c shows the results of several tests of different LTI materials using the same test chip, heat sink and force. Normalized average thermal resistance (C sq cm/W) is plotted vs the interface resistivity (which is inverse thermal conductivity) in units of C sq cm /W. The data is linear. A simple thermal model predicts that the slope of the line is the average LTI gap thickness of 0.00011cm or 1.1 microns. The y intercept is a prediction of overall heat sink performance with a perfect interface material (infinite thermal conductivity). This type of chart can be used to predict performance of other LTI materials if their thermal conductivity is known or to estimate their thermal conductivity if resistance is known. Helium was found to have worse thermal performance than predicted from this chart because the mean free path approaches the gap size, thus effective thermal conductivity of helium in these small gaps is about 2× lower than bulk published values. This method of analyzing the data also provides a way to estimate the effect of heat sink and device flatness on thermal performance.
d shows the result of a calculation that assumes each quadrant of an idealized chip is independently powered and cooled. Resistance is based on the total power and temperature rise of the hottest, coolest and average sensor. The first five cases assume uniform power in each quadrant. The first case has uniform LTI, as expected the temperature is uniform at 0.09 C/W. In case 2, LTI is removed from one quadrant and its temperature increased to 0.21 C/W. As LTI is removed from the other quadrants, the temperature of those quadrants increases to 0.21 C/W thus increasing the average temperature. The second of the five cases assume uniform LTI coverage and a total chip power of 100 watts. The first of these cases has 25 watts on each core. The next case has 40 watts in one core and 20 watts in each of the other cores resulting in an increased temperature of the 40 watt core. However, the average temperature remains the same. The same trend is seen as the power becomes more and more non uniform. It is known that production chips can occasionally have manufacturing defects where one core draws more power than the others.
e shows data measured on production modules at one point in module test. The device has 9 temperature sensors. The maximum, average and minimum temperature increase is plotted versus total module power for each device (shown as a box with error bars). There is a large variation in chip power for these modules but the average sensor data in general follows a linear trend. An action limit based on average is shown (12). The action limit is 1.5 C at zero power due to the accuracy of the temperature sensors. Modules with an average above the action limit (11) were tested without LTI due to a tool malfunction. Modules 10 have good LTI but are defective chips that allow one core to draw excessive power. This data analysis method suggested by the model of
a shows a test configuration in accordance with an additional aspect of the invention. The method using the configuration of
In the test configuration of
For unacceptable candidates, the current may continue to increase over time due, possibly, to one or more phenomenon. For example, the LTI may become more conductive in the presence of air or due to contamination on the interconnects 20 or device. Alternatively, or in addition, the conductive metal dendrites may grow between adjacent interconnects 20, effectively creating a short circuit. It has also been observed conductivity may increase and decrease over time, which may be due to dislocation of the dendrites, dry out of the LTI and evolution of gas, e.g., Hydrogen will be released from water in the presence of sufficient voltage.
b shows an alternate embodiment where the device 15 is placed on a stage 59, and two adjacent interconnects 20 are contacted by electrical probes 57. The probes 57 are connected to a power supply 65, and current is measured. It should be understood that this embodiment may not use a glass slide, even though direct observation is not quite as clear without the glass slide 80. By way of an example, one probe can be connected to a ground interconnect, while a second probe can be connected to an I/O interconnect. In embodiments, the probes can be connected to other solder connections, such as, for example, dummy C4s (solder connections). Once the probes are applied, the power source can apply about 1V-3V. In this example, about 3 μl of solvent (LTI) can be applied to the device. The device can be monitored with a parameter analyzer such as, for example, an HP 4145B Parameter Analyzer (manufactured by Hewlett Packard™). In embodiments, the HP 4145B Parameter Analyzer can take about 1000 data points/scans, where a single scan is about 55 seconds. In embodiments, a “medium” scan is about 73 seconds (each point average of 16 measurements) and “long” scan is about 323 seconds (each point average of 256 measurements). The results of the scans can be sent to a computing device 100 for storage and future retrieval and/or analysis.
The computing device 100, as should be understood by those of skill in the art can include an operating system, a processor, ROM, RAM and permanent storage such as, for example, an internal hard drive or an external storage such as, for example, a CD ROM, magnetic storage, optical storage of the like. More specifically, the computing device 100 includes a processor, memory, an I/O interface, and a bus. The memory can include local memory employed during actual execution of program code, bulk storage, and cache memories. In addition, the computing device 100 includes random access memory (RAM), a read-only memory (ROM), and an operating system (O/S). The computing device 100 is in communication with the external I/O device/resource and storage system. The processor executes computer program code (e.g., program control), which can be stored in the memory and/or storage system. While executing the computer program code, the processor can read and/or write data to/from memory, storage system, and/or I/O interface. The bus provides a communications link between each of the components in the computing device. The functionality provided by the computing device 100 can be implemented by a computing article of manufacture that includes any combination of general and/or specific purpose hardware and/or computer program code. In each embodiment, the program code and hardware can be created using standard programming and engineering techniques, respectively.
Other materials that exhibit good thermal properties without causing corrosion include, for example, Nerol, Limonene, Pinane and Squalene. These materials may, however, evaporate during the test and/or leave residue on the device under test. For example, as discussed below, Nerol may leave a residue on the device under test, which would require cleaning with solvent. It has been discovered from this test procedure that all materials that had oxygen showed varying amounts of current flow and corrosion. Surprisingly, materials that did not contain oxygen did not allow current flow and had no sign of C4 corrosion.
a shows corrosion residue left after testing a device with water based LTI after some LTI came into contact with the chip C4s during electrical test.
d shows chip surfaces at different phases of testing with different thermal interface materials, including Pentadecane in accordance with aspects of the invention. The testing with the interface material disposed between (in contact with) the chip and heat sink is for 30 min at 85° C. More specifically,
Pentadecane shows many advantages over the remaining materials, one of which is no staining after the uncovered baking in an oven for 20 minutes at 70° C. This is in comparison to PG/Water, Nerol and Farnesol, each of which present issues at the same temperature. For example, as shown by the data of
a and 10b show a test configuration to observe LTI on the surface of the device in accordance with an additional aspect of the invention. In the test configuration of
In embodiments, the LTI 40 is placed on the device 15 and the glass slide 80 is contacted to the device 15 in the same manner and force as the heat sink, for example. In one example, the force of the glass slide on the device may depend on the design of the test equipment. For example, a force can range from about 4 to 45 psi, and more specifically about 10 psi. Looking down through the glass slide 80 will allow an observer to determine (view) the extent of the LTI coverage on the device 15. With some types of LTI, it is common to see the fluid coverage change over time as the fluid migrates across the interface between the device and glass slide 80.
It should be understood that
The terminology used herein is for the purpose of describing particular embodiments only and is not intended to be limiting of the invention. As used herein, the singular forms “a”, “an” and “the” are intended to include the plural forms as well, unless the context clearly indicates otherwise. It will be further understood that the terms “comprises” and/or “comprising,” when used in this specification, specify the presence of stated features, integers, steps, operations, elements, and/or components, but do not preclude the presence or addition of one or more other features, integers, steps, operations, elements, components, and/or groups thereof
The corresponding structures, materials, acts, and equivalents of all means or step plus function elements, if any, in the claims below are intended to include any structure, material, or act for performing the function in combination with other claimed elements as specifically claimed. The description of the present invention has been presented for purposes of illustration and description, but is not intended to be exhaustive or limited to the invention in the form disclosed. Many modifications and variations will be apparent to those of ordinary skill in the art without departing from the scope and spirit of the invention. The embodiments were chosen and described in order to best explain the principles of the invention and the practical application, and to enable others of ordinary skill in the art to understand the invention for various embodiments with various modifications as are suited to the particular use contemplated.